JP4206027B2 - タッチパネル用光透過性ハードコートフィルム - Google Patents
タッチパネル用光透過性ハードコートフィルム Download PDFInfo
- Publication number
- JP4206027B2 JP4206027B2 JP2003364587A JP2003364587A JP4206027B2 JP 4206027 B2 JP4206027 B2 JP 4206027B2 JP 2003364587 A JP2003364587 A JP 2003364587A JP 2003364587 A JP2003364587 A JP 2003364587A JP 4206027 B2 JP4206027 B2 JP 4206027B2
- Authority
- JP
- Japan
- Prior art keywords
- hard coat
- refractive index
- light
- film
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
代表的なアナログタイプのタッチパネルは、ガラスの表面に第1の透明導電膜が積層され、第1の透明導電膜の表面にマイクロドットスペーサーが形成され、その第1の透明導電膜に空間を設けて第2の透明導電膜が積層され、さらに第2の透明導電膜の表面に透明フィルムが積層されている構造を有しており、透明フィルムの表面を指やペンなどで触ると、スペーサーのない部分で2枚の透明導電膜を接触させることにより入力位置を記録させることができる。
このアナログタイプのタッチパネルは、通常、表面にマイクロドットスペーサーが形成された第1の透明導電膜が積層されたガラスと、第2の透明導電膜が積層された透明フィルムを透明導電膜同士面で、空間を設けて2枚の透明導電膜を積層することにより、製造できる。
しかし、タッチパネル用のITO膜とPETフィルムとの積層物は、全光線透過率がクリアハードコートPETフィルムと比較して低く、透過色も黄色をしているため、視認性、操作性、高級感が十分ではないという問題点があった。
また、ガラス板、ポリカーボネート板、ポリエチレンテレフタレート板などの透明基板、アクリル樹脂などからなるハードコート層、ZrO2、TiO2、Al2O3などからなる屈折率が1.50〜2.50の高屈折率層、SiO2、MgF2などからなる屈折率が1.35〜1.60の低屈折率層、透明導電体層を積層した透明タッチパネルが開示されている(特許文献1参照)。しかし、この透明タッチパネルは、視認性、操作性がある程度改善されているが、まだ十分とは言えず、透過色が黄色をしているという問題点があった。
しかし、この透明タッチパネルは、透過光が無着色か僅かに黄色味を帯びているものであり、タッチパネルに望まれる青色ではなかった。
このため、全光線透過率が高く、青色の透過色を生じることができるタッチパネル用光透過性ハードコートフィルムが望まれていた。
また、本発明は、上記タッチパネル用光透過性ハードコートフィルムにおいて、前記光透過性ハードコート層が防眩性光透過性ハードコート層であるタッチパネル用光透過性ハードコートフィルムを提供するものである。
また、本発明は、上記タッチパネル用光透過性ハードコートフィルムにおいて、高屈折率層において、アンチモンドープ酸化錫の含有量が全金属酸化物の合計量の20〜90質量%であるタッチパネル用光透過性ハードコートフィルムを提供するものである。
以下、本発明を詳細に説明する。
本発明において、光透過性基材フィルム1としては、種々のプラスチックシート、フィルムが使用できる。光透過性基材フィルム1の具体例としては、例えばポリエチレン樹脂、ポリプロピレン樹脂などのポリオレフィン樹脂、ポリエチレンテレフタレート樹脂、ポリエチレンナフタレート樹脂、ポリブチレンテレフタレート樹脂などのポリエステル樹脂、ポリ塩化ビニル樹脂、ポリスチレン樹脂、ポリウレタン樹脂、ポリカーボネート樹脂、ポリアミド樹脂、ポリイミド樹脂、フッ素系樹脂などの各種合成樹脂のフィルムが挙げられ、特に、高強度であり安価であることから、ポリエチレンテレフタレート樹脂などのポリエステル樹脂より成るフィルムが好ましい。光透過性基材フィルム1は、単層であってもよいし、同種又は異種の2層以上の多層であってもよい。
光透過性基材フィルム1の厚みは、特に制限ないが、通常10〜350μmが好ましく、25〜300μmがより好ましく、50〜250μmが特に好ましい。
電離放射線硬化型化合物の硬化物からなる光透過性ハードコート層2は、電離放射線硬化型化合物を含有する硬化性組成物を塗布して電離放射線を照射して硬化させて形成できる。
電離放射線硬化型化合物の硬化物からなる光透過性ハードコート層2の厚さは、特に制限ないが、1〜50μmが好ましく、2〜30μmがより好ましく、3〜20μmが特に好ましい。
電離放射線硬化型化合物の硬化物からなる光透過性ハードコート層2の硬さは、スチールウール硬度で200g/cm2以上の荷重をかけた場合であっても傷が付かないことが好ましい。
電離放射線硬化型化合物としては、不飽和モノマー、オリゴマー、樹脂又はそれらを含む組成物などが挙げられる。その具体例としては、多官能アクリレート、ウレタンアクリレートやポリエステルアクリレート等の2官能基以上を有する多官能の電離放射線硬化型のアクリル系化合物が挙げられ、ウレタンアクリレートやポリエステルアクリレートが好ましい。多官能アクリレートとしては、エチレングリコールジ(メタ)アクリレート、プロピレングリコールジ(メタ)アクリレート、ブチレングリコールジ(メタ)アクリレート、ネオペンチルグリコールジ(メタ)アクリレート、ヘキサンジオールジ(メタ)アクリレート、トリメチロールエタントリ(メタ)アクリレート、トリメチロールプロパントリ(メタ)アクリレート、ペンタエリスリトールトリ(メタ)アクリレート、ペンタエリスリトールテトラ(メタ)アクリレート、ジペンタエリスリトールペンタ(メタ)アクリレート、ジペンタエリスリトールヘキサ(メタ)アクリレート、グリセロールトリ(メタ)アクリレート、トリアリル(メタ)アクリレート、ビスフェノールAエチレンオキシド変性ジ(メタ)アクリレート等が挙げられる。
ポリエステルアクリレートは、例えば多価カルボン酸と多価アルコールの縮合によって得られる両末端に水酸基を有するポリエステルオリゴマーの水酸基を(メタ)アクリル酸でエステル化することにより、又は多価カルボン酸にアルキレンオキシドを付加して得られるオリゴマーの末端の水酸基を(メタ)アクリル酸でエステル化することにより得られる。
電離放射線硬化型化合物は、1種単独で使用してもよいし、2種以上を組合せて用いてもよい。
光重合開始剤は、1種単独で使用してもよいし、2種以上を組合せて用いてもよい。
電離放射線硬化型化合物と光重合開始剤の配合割合は、通常電離放射線硬化型化合物100質量部に対し光重合開始剤が0.01〜20質量部が好ましく、0.1〜10質量部が特に好ましい。
本発明において、オリゴマー型光重合開始剤を用いれば重合開始剤に由来するガスの発生がほとんど防止できる。
また、硬化性組成物には、光安定剤、紫外線吸収剤、触媒、着色剤、帯電防止剤、滑剤、レベリング剤、消泡剤、重合促進剤、酸化防止剤、難燃剤、赤外線吸収剤、界面活性剤、表面改質剤等の添加成分を含ませることは任意である。
本発明においては、上記硬化性組成物は、光透過性基材フィルムの表面に塗布され、希釈剤を含む場合は乾燥した後に電離放射線を照射されて、硬化されハードコート層を形成する。
光透過性ハードコート層の厚みは、特に制限ないが、通常1〜50μmが好ましく、2〜30μmがより好ましく、3〜20μmが特に好ましい。
上記硬化性組成物の光透過性基材フィルムへの塗布方法は、例えば、バーコート法、ナイフコート法、ロールコート法、ブレードコート法、ダイコート法、グラビアコート法、カーテンコート法など従来公知の方法が挙げられる。
高屈折率層3には、アンチモンドープ酸化錫と、酸化ジルコニウム又は酸化チタンのいずれか一方又は両者の金属酸化物を含有する。これらの金属酸化物を含有することにより、屈折率を1.65〜1.90の範囲とすることができる。アンチモンドープ酸化錫は、低屈折率層4との接着性を向上させることができる。
アンチモンドープ酸化錫としては、ドープされたアンチモンの含有量は、1〜20質量%が好ましい。アンチモンドープ酸化錫の含有量は、アンチモンドープ酸化錫と、酸化ジルコニウム及び/又は酸化チタンの金属酸化物の合計量の20〜90質量%が好ましく、25〜70質量%がより好ましく、30〜65質量%が特に好ましい。アンチモンドープ酸化錫が上記範囲よりも少ないと、低屈折率層4との接着性を向上させる効果が低く、上記範囲を超えると全光線透過率が低くなる。
アンチモンドープ酸化錫、酸化ジルコニウム及び酸化チタンの平均粒子径は、10〜500nmが好ましく、50〜150nmが特に好ましい。
高屈折率層3は、前記(A)層の形成に用いられる電離放射線硬化性化合物と同様な電離放射線硬化型化合物に金属酸化物としてアンチモンドープ酸化錫と、酸化ジルコニウム及び/又は酸化チタンを混合した硬化性組成物を塗布して電離放射線を照射して硬化させて形成できる。
シロキサン系硬化性化合物としては、ケイ素アルコキシドなどが好ましい。ケイ素アルコキシドとしては、テトラメトキシシラン、テトラエトキシシラン、メチルトリメトキシシラン、メチルトリエトキシシラン、ジメチルジメトキシシラン、γ−グリシドキシプロピルトリメトキシシラン、ビニルトリメトキシシラン、これらの部分加水分解物などが挙げられる。ケイ素アルコキシドは、空気中の水分などにより加水分解が起こり、脱水縮合により架橋されて、シロキサン系硬化性化合物の硬化物となる。
シロキサン系硬化性化合物は、コロイド粒子の形態で用いることが好ましい。コロイド粒子の平均粒子径は、1〜100nmが好ましい。
本発明のタッチパネル用光透過性ハードコートフィルムの(C)層の低屈折率層4の表面には、好ましくは光透過性導電層5が積層されて用いられる。
光透過性導電層5は、好適にはITO膜などが挙げられる。ITOは、インジウムと錫の酸化物の合金であり、ITO膜は、ITOをスパッタリングにより形成できる。
光透過性導電層5の厚さは、10〜40nmが好ましく、20〜30nmが特に好ましい。
光透過性ハードコート層6は、(A)の電離放射線硬化型化合物の硬化物と同様なもので構成されていてもよい。
光透過性ハードコート層6の厚さは、特に制限ないが、2〜20μmが好ましく、3〜18μmがより好ましく、4〜15μmが特に好ましい。
光透過性ハードコート層6の硬さは、スチールウール硬度で200g/cm2以上の荷重をかけた場合であっても傷が付かないことが好ましい。
本発明の光透過性ハードコートフィルムは、全光線透過率が87.0%以上が好ましく、88.0以上が特に好ましい。
本発明の光透過性ハードコートフィルムの透過光の日本工業規格Z8729号に定めるa*b*表色系のクロマティクネス指数b*値は、0.5〜4.0が好ましく、1.0〜2.0がより好ましく、1.3〜2.0が特に好ましい。
本発明の光透過性ハードコートの透過光の色彩は、青色又は緑色の青色系色などであるが、青色が好ましい。
光透過性ハードコート層形成用の硬化性組成物1の調製
紫外線硬化型化合物としてのウレタンアクリレートと光重合開始剤の混合物(荒川化学工業(株)製、商品名「ビームセット575CB」)100質量部に希釈剤としてトルエン150質量部を加えて調製した溶液を光透過性ハードコート層形成用の硬化性組成物1とする。
光透過性ハードコート層形成用の硬化性組成物2の調製
紫外線硬化型化合物としてのウレタンアクリレート(荒川化学工業(株)製、商品名「ビームセット577」)98質量部に、光重合開始剤(チバ・スペシャルティ・ケミカルズ(株)製、商品名「イルガキュア907」)2質量部を添加して得られる混合液に、希釈剤としてトルエン150質量部を加えて調製した溶液を光透過性ハードコート層形成用の硬化性組成物2とする。
防眩性光透過性ハードコート層形成用の硬化性組成物3の調製
紫外線硬化型化合物としてのポリエステルアクリレート(大日精化工業(株)製、商品名「セイカビームEXF−01L(NPI)」)98質量部に、ポリエステルアクリレートとシリカゲルの混合物(大日精化工業(株)製、商品名「セイカビームEXF−01L(BS)」、シリカゲル含有量10質量%)20質量部、及び光重合開始剤(チバ・スペシャルティ・ケミカルズ(株)製、商品名「イルガキュア907」)2質量部を添加して得られる混合液に、イソブタノール180質量部を加えて調製した溶液を防眩性光透過性ハードコート層形成用の硬化性組成物3とする。
紫外線硬化型化合物としてのウレタンアクリレート、光重合開始剤及び酸化ジルコニウムの混合物(JSR(株)製、商品名「デソライトKZ7252C」、固形分45質量%、固形分に占める酸化ジルコニウム68質量%)100質量部、アンチモンドープ酸化錫の10質量%イソブタノール分散体(大日本インキ化学工業(株)製、商品名「TA−01D」)180質量部の混合液にイソブタノール2870質量部を加えて調製した溶液を高屈折率層形成用の硬化性組成物4(固形分濃度2.0質量%)とする。アンチモンドープ酸化錫の含有量は、アンチモンドープ酸化錫と酸化ジルコニウムの合計量に対して37質量%であった。
高屈折率層形成用の硬化性組成物5の調製
アンチモンドープ酸化錫のイソブタノール分散体「TA−01D」を450質量部、イソブタノールを3950質量部とした以外は、高屈折率層形成用の硬化性組成物4と同様に調製して高屈折率層形成用の硬化性組成物5(固形分濃度2.0質量%)を調製した。
アンチモンドープ酸化錫の含有量は、アンチモンドープ酸化錫と酸化ジルコニウムの合計量に対して60質量%であった。
紫外線硬化型化合物としてのポリエステルアクリレートと光重合開始剤の混合物(大日精化工業(株)製、商品名「セイカビームEXF−01L(NS)」)100質量部、アンチモンドープ酸化錫のイソブタノール分散体(大日本インキ化学工業(株)製、商品名「TA−01D」)3000質量部の混合液にイソブタノール16900質量部を加えて調製した溶液を高屈折率層形成用の硬化性組成物6(固形分濃度2.0質量%)とする。該硬化性組成物中に含まれる金属酸化物はアンチモンドープ酸化錫のみである。
高屈折率層形成用の硬化性組成物7の調製
ウレタンアクリレート、光重合開始剤及び酸化チタンの混合物(日本化薬(株)製、商品名「KAYANOVA MHR−101」、固形分20質量%、固形分に占める酸化チタン65質量%)100質量部、アンチモンドープ酸化錫のイソブタノール分散体(大日本インキ化学工業(株)製、商品名「TA−01D」)100質量部の混合液にイソブタノール1300質量部を加えて調製した溶液を高屈折率溶液7(固形分濃度2.0質量%)とする。アンチモンドープ酸化錫の含有量は、アンチモンドープ酸化錫と酸化チタンの合計量に対して43質量%であった。
シロキサン系硬化性化合物の分散液(コルコート(株)製、商品名「コルコートP」、シロキサン系化合物の濃度2質量%、分散媒:イソブタノール、コロイド粒子の平均粒子径:約6nm)100質量部にイソブタノール900質量部を加えて調製した溶液を低屈折率層形成用の硬化性組成物8(固形分濃度2.0質量%)とする。
ハードコートフィルム1
光透過性基材フィルムとしてのポリエチレンテレフタレート樹脂フィルム(商品名「PET188A4300」、東洋紡績(株)製、厚さ188μm)に硬化性組成物1をマイヤーバー#10にて、乾燥、硬化後の厚さが4μmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、光透過性ハードコート層を形成した。続いて、ポリエチレンテレフタレート樹脂フィルムの光透過性ハードコート層が設けられている面の反対面に硬化性組成物2をマイヤーバー#10にて、乾燥膜厚4μmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(100mJ/cm2)、光透過性ハードコート層を設け、ハードコートフィルム1を得た。
光透過性基材フィルムとしてのポリエチレンテレフタレート樹脂フィルム(商品名「PET188A4300」、東洋紡績(株)製、厚さ188μm)に硬化性組成物1をマイヤーバー#10にて、乾燥、硬化後の厚さが4μmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、光透過性ハードコート層を設けた。続いて、ポリエチレンテレフタレート樹脂フィルムの光透過性ハードコート層が設けられている面の反対面に硬化性組成物3をマイヤーバー#10にて、乾燥膜厚4μmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(100mJ/cm2)、防眩性光透過性ハードコート層を設けて、ハードコートフィルム2を得た。
ハードコートフィルム1の硬化性組成物2を硬化して得られた光透過性ハードコート層上に硬化性組成物4をマイヤーバー#10にて、乾燥、硬化後の厚さが70nmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、高屈折率層を形成した。続いて、その高屈折率層上に硬化性組成物8をマイヤーバー#12にて、乾燥膜厚15nmになるように塗布し、130℃にて1分間乾燥して低屈折率層を形成してタッチパネル用光透過性ハードコートフィルムを得た。そして、低屈折率層上に膜厚25nmになるようにITO膜を蒸着加工した。
ハードコートフィルム1の硬化性組成物2を硬化して得られた光透過性ハードコート層上に硬化性組成物5をマイヤーバー#10にて、乾燥、硬化後の厚さが70nmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、高屈折率層を形成した。続いて、その高屈折率層上に硬化性組成物8をマイヤーバー#12にて、乾燥膜厚15nmになるように塗布し、130℃にて1分間乾燥して低屈折率層を形成してタッチパネル用光透過性ハードコートフィルムを得た。そして、低屈折率層上に膜厚25nmになるようにITO膜を蒸着加工した。
ハードコートフィルム1の硬化性組成物2を硬化して得られた光透過性ハードコート層上に硬化性組成物7をマイヤーバー#10にて、乾燥、硬化後の厚さが70nmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、高屈折率層を形成した。続いて、その高屈折率層上に硬化性組成物8をマイヤーバー#12にて、乾燥膜厚15nmになるように塗布し、130℃にて1分間乾燥して低屈折率層を形成してタッチパネル用光透過性ハードコートフィルムを得た。そして、低屈折率溶液塗工面に膜厚25nmになるようにITO膜を蒸着加工した。
ハードコートフィルム2の防眩性光透過性ハードコート層上に硬化性組成物4をマイヤーバー#10にて、乾燥、硬化後の厚さが70nmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、高屈折率層を形成した。続いて、その高屈折率層上に硬化性組成物8をマイヤーバー#12にて、乾燥膜厚15nmになるように塗布し、130℃にて1分間乾燥して低屈折率層を形成してタッチパネル用光透過性ハードコートフィルムを得た。そして、低屈折率層上に膜厚25nmになるようにITO膜を蒸着加工した。
ハードコートフィルム1の硬化性組成物2を硬化して得られた光透過性ハードコート層上に硬化性組成物4をマイヤーバー#12にて、乾燥、硬化後の厚さが100nmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、高屈折率層を形成した。続いて、その高屈折率層上に硬化性組成物8をマイヤーバー#12にて、乾燥膜厚15nmになるように塗布し、130℃にて1分間乾燥して低屈折率層を形成してタッチパネル用光透過性ハードコートフィルムを得た。そして、低屈折率層上に膜厚25nmになるようにITO膜を蒸着加工した。
ハードコートフィルム1の硬化性組成物2を硬化して得られた光透過性ハードコート層上に硬化性組成物4をマイヤーバー#8にて、乾燥、硬化後の厚さが50nmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、高屈折率層を形成した。続いて、その高屈折率層上に硬化性組成物8をマイヤーバー#12にて、乾燥膜厚15nmになるように塗布し、130℃にて1分間乾燥して低屈折率層を形成してタッチパネル用光透過性ハードコートフィルムを得た。そして、低屈折率層上に膜厚25nmになるようにITO膜を蒸着加工した。
ハードコートフィルム1の硬化性組成物2を硬化して得られた光透過性ハードコート層上に硬化性組成物4をマイヤーバー#10にて、乾燥、硬化後の厚さが70nmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、高屈折率を形成した。続いて、その高屈折率層上に硬化性組成物8をマイヤーバー#16にて、乾燥膜厚20nmになるように塗布し、130℃にて1分間乾燥して低屈折率層を形成してタッチパネル用光透過性ハードコートフィルムを得た。そして、低屈折率層上に膜厚25nmになるようにITO膜を蒸着加工した。
ハードコートフィルム1の硬化性組成物2を硬化して得られた光透過性ハードコート層上に硬化性組成物4をマイヤーバー#16にて、乾燥、硬化後の厚さが200nmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、高屈折率層を形成した。続いて、その高屈折率層上に硬化性組成物8をマイヤーバー#16にて、乾燥膜厚30nmになるように塗布し、130℃にて1分間乾燥して低屈折率層を形成し、さらに低屈折率層上に膜厚25nmになるようにITO膜を蒸着加工して、光透過性ハードコートフィルムを得た。
ハードコートフィルム1の硬化性組成物2を硬化して得られた光透過性ハードコート層上に膜厚25nmになるようにITO膜を蒸着加工して、光透過性ハードコートフィルムを得た。
(比較例3)
ハードコートフィルム1の硬化性組成物2を硬化して得られた光透過性ハードコート層上に硬化性組成物6をマイヤーバー#10にて、乾燥、硬化後の厚さが70nmになるように塗布し、70℃にて1分間乾燥後、紫外線を照射して(1000mJ/cm2)、高屈折率を形成した。続いて、その高屈折率層上に硬化性組成物8をマイヤーバー#10にて、乾燥膜厚10nmになるように塗布し、130℃にて1分間乾燥して低屈折率層を形成し、さらに低屈折率層上に膜厚25nmになるようにITO膜を蒸着加工して、光透過性ハードコートフィルムを得た。この光透過性ハードコートフィルムの高屈折率層に含まれる金属酸化物はアンチモンドープ酸化錫のみである。
実施例及び比較例の光透過性ハードコートフィルムの性状を表1及び表2に示した。
(1)全光線透過率及びヘイズ
光線透過率測定器(日本電色工業(株)製、商品名「NDH2000」)を用いて測定した。
(2)色彩(a*値、b*値)
色差計(日本電色工業(株)製、商品名「SQ2000」)を用いて、色彩の計算を行った。光源として日本工業規格Z8720に規定される標準の光D65を採用し、2度視野の条件で測定を行った。
(3)スチールウール硬度
低屈折率層の表面にスチールウールを200g/cm2の圧力をかけて10回往復擦り付け、表面を目視で観察し、以下に示す基準で評価した。
○:傷がみられない。
×:傷がみられる。
(4)高屈折率層の屈折率の測定
固形分濃度を10質量%に調製した硬化性組成物を、マイヤーバー#10にてガラス板上に塗布し、70℃で1分間乾燥した後、紫外線を照射して(1000mJ/cm2)、高屈折率層を形成し、薄膜測定装置(Filmetrics社製、商品名「F20」)を用いて屈折率を測定した。
(5)低屈折率層の屈折率の測定
固形分濃度を2質量%に調製した硬化性組成物を、マイヤーバー#20にてガラス板上に塗布し、130℃で1分間加熱して低屈折率層を形成し、高屈折率層と同様に、薄膜測定装置を用いて屈折率を測定した。
2 光透過性ハードコート層
3 高屈折率層
4 低屈折率層
5 光透過性導電層
6 光透過性ハードコート層
Claims (4)
- 光透過性基材フィルムの一方の面に、(A)電離放射線硬化型化合物の硬化物からなる光透過性ハードコート層、(B)金属酸化物としてアンチモンドープ酸化錫と、酸化ジルコニウム又は酸化チタンのいずれか一方又は両者の金属酸化物を含有した電離放射線硬化型化合物の硬化物からなる層であり、屈折率が1.65〜1.90の範囲にある厚さ30〜160nmの高屈折率層、及び(C)シロキサン系硬化性化合物の硬化物からなる層であり、屈折率が1.40〜1.55の範囲にある厚さ10〜50nmの低屈折率層を順次積層していることを特徴とするタッチパネル用光透過性ハードコートフィルム。
- 前記光透過性基材フィルムの(A)の電離放射線硬化型化合物の硬化物からなる光透過性ハードコート層が設けられている面の反対面に光透過性ハードコート層を有する請求項1に記載のタッチパネル用光透過性ハードコートフィルム。
- 前記光透過性ハードコート層が防眩性光透過性ハードコート層である請求項1又は2に記載のタッチパネル用光透過性ハードコートフィルム。
- 高屈折率層において、アンチモンドープ酸化錫の含有量が全金属酸化物の合計量の20〜90質量%である請求項1〜3のいずれかに記載のタッチパネル用光透過性ハードコートフィルム。