JP2996319B2 - Tissue paper with high moisture content - Google Patents
Tissue paper with high moisture contentInfo
- Publication number
- JP2996319B2 JP2996319B2 JP3347953A JP34795391A JP2996319B2 JP 2996319 B2 JP2996319 B2 JP 2996319B2 JP 3347953 A JP3347953 A JP 3347953A JP 34795391 A JP34795391 A JP 34795391A JP 2996319 B2 JP2996319 B2 JP 2996319B2
- Authority
- JP
- Japan
- Prior art keywords
- paper
- tissue paper
- moisture
- web
- flexibility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【０００１】[0001]
【産業上の利用分野】本発明は、高水分含有性を有する
ティシュペーパーに関し、特に、安全性が高く、柔軟で
肌触りに優れ、かつウェブ屑（紙粉）発生の少ないティ
シュペーパーに関する。The present invention has a high water content.
Regarding tissue paper , in particular, it is highly safe, flexible, has excellent touch, and generates less web dust (paper powder) .
About paper .
【０００２】[0002]
【従来の技術】ティシュペーパーやトイレットペーパー
等の家庭紙、その他の繊維ウェブにおいては、従来か
ら、感触をソフトにする等の目的のために、柔軟剤が使
用される。この柔軟剤は、湿潤紙力増強剤（紙が濡れた
ときの強度を保つ薬剤）の可塑剤として作用するほか、
次のような作用を発現する。2. Description of the Related Art Softeners are conventionally used in household paper such as tissue paper and toilet paper, and other fiber webs, for the purpose of softening the feel. This softener acts as a plasticizer for the wet strength agent (an agent that maintains the strength when the paper gets wet),
The following effects are exhibited.
【０００３】親水性基と親油性基とを持ち、親水性基が
セルロースに吸着し、親油性基が外側に向いて配向す
る。従って、セルロースは、親油性基で包まれた状態と
なり、しなやかになると同時に、表面が平滑になる。そ
して、セルロース間の滑りが良好となり、抵抗が少なく
なって、手触りが滑らかになり柔らかくなる。しかも、
繊維の水素結合を封鎖し、繊維のズレを促進して柔らか
くする。[0003] It has a hydrophilic group and a lipophilic group, the hydrophilic group is adsorbed on cellulose, and the lipophilic group is oriented outward. Therefore, the cellulose is wrapped in a lipophilic group, and becomes supple and, at the same time, has a smooth surface. Then, the sliding between the celluloses becomes good, the resistance is reduced, and the touch becomes smooth and soft. Moreover,
It blocks the hydrogen bonds of the fiber and promotes the fiber displacement to make it softer.
【０００４】このような作用をなす柔軟剤は、上記のテ
ィシュペーパー等の繊維ウェブの原料に混合された状態
で抄造されるか、ウェブの形成後であって乾燥前の湿潤
状態か、抄紙し乾燥したウェブに含浸させて添加される
（以下、これを外添と言う）。[0004] The softening agent having such an action is produced in a state of being mixed with a raw material of a fiber web such as the above-mentioned tissue paper, or in a wet state after forming the web but before drying. It is added by impregnating the dried web (hereinafter referred to as external addition).
【０００５】上記の柔軟剤としては、従来、界面活性
剤，ワックスエマルジョン（ワックスを界面活性剤で乳
化させたもので、ワックスが上記の親油性基の役割をな
す），反応型柔軟剤（セルロースと強固に反応して、脂
肪族ハイドロカーボンを規則正しく繊維の周囲に配向さ
せるもの）が知られている。また、最近、ティシュペー
パーに、ソフトでシルキーなフランネル様の感触を持た
せると共に、高いバルク性をも持たせるために、シリコ
ン系の柔軟剤も開発されている（特開平２−２２４６２
６号，同３−９００号公報参照）。As the above softener, a surfactant, a wax emulsion (a wax emulsified with a surfactant, and the wax plays the role of the lipophilic group), a reactive softener (cellulose) Which strongly reacts with the polymer to regularly orient the aliphatic hydrocarbon around the fiber). Recently, a silicone softener has also been developed to give a tissue paper a soft and silky flannel-like feel and a high bulk property (Japanese Patent Laid-Open No. 22462/1990).
6, 3-900).
【０００６】[0006]
【発明が解決しようとする課題】ところで、食品用，衛
生用，家庭用等の繊維ウェブの場合、食品，粘膜，皮膚
等に接触するため、高い安全性が求められる。しかし、
前述した従来の柔軟剤は、化学合成品であり、高濃度で
の添加は、安全性において懸念がある。By the way, in the case of a fibrous web for food, hygiene, home use, etc., high safety is required because it comes into contact with food, mucous membrane, skin and the like. But,
The above-mentioned conventional softener is a chemically synthesized product, and its addition at a high concentration raises safety concerns.
【０００７】また、従来の柔軟性の作用の発現機構は、
前述したように、親水性基がセルロースに吸着し、親油
性基が外側に向いて配向し、繊維間の水素結合を阻害す
ることにあるため、繊維同士の絡み合いや結合が減少
し、この結果、繊維が脱落し、紙粉，繊維粉等の言わば
ウェブ屑が増加する。更に、外側を向いて配向している
親油性基によって撥水性を帯びて、吸水性が低下し、テ
ィシュペーパーに本来要求される吸水性が損なわれる。[0007] The conventional mechanism of exerting the function of flexibility is as follows.
As described above, since the hydrophilic group is adsorbed on the cellulose and the lipophilic group is oriented outward and inhibits the hydrogen bonding between the fibers, the entanglement and bonding between the fibers are reduced, and as a result, As a result, fibers fall off, and so-called web waste such as paper powder and fiber powder increases. Furthermore, tinged with water repellency by lipophilic groups are oriented facing outward, water absorption is reduced, it is impaired water absorption which is originally required for tissue paper chromatography.
【０００８】以上のような種々の問題に起因して、従来
の柔軟剤においては、その添加量が制限され、ティシュ
ペーパーに対して、より優れた触感や柔軟性を付与する
ことができなかった。[0008] Due to the various problems described above, the amount of conventional softener added is limited, and it has not been possible to impart more excellent tactile sensation and softness to tissue paper. .
【０００９】本発明は、このような問題を解消し、安全
性が高く、柔軟で肌触りにも優れる上、保湿性が有り、
しかもウェブ屑（紙粉）発生の少ない、家庭用として好
適な高水分含有性を有するティシュペーパーを提供する
ことを目的とする。The present invention solves such a problem, has high safety, is flexible and has excellent touch, and has moisture retention.
Moreover, it is an object of the present invention to provide a tissue paper having a high moisture content suitable for household use, which generates little web waste (paper powder).
【００１０】[0010]
【課題を解決するための手段】上記の目的を達成するた
めに、本発明のティシュペーパーは、吸湿性を有する多
価アルコール及び糖類のうち少なくとも一種、または、
吸湿性を有する多価アルコール及び糖類のうち少なくと
も一種並びに保水性を有する糊料を、吸湿・柔軟性等付
与剤として、家庭紙用の繊維ウェブに対し１．０〜１０
０重量％含んでなることを特徴とする。In order to achieve the above object, the tissue paper of the present invention comprises at least one of a polyhydric alcohol and a saccharide having hygroscopicity,
The starch adhesive having at least one and water retention of polyhydric alcohols and saccharides having hygroscopicity, as a hygroscopic, flexibility, etc. imparting agent, to a fibrous web for household paper 1.0-10
Characterized in that it comprises 0 wt%.
【００１１】更に、本発明のティシュペーパーは、上記
の多価アルコール及び糖類、保水性を有する糊料が、食
品または食品添加物であることをも特徴とする。Further, the tissue paper of the present invention is characterized in that the above-mentioned polyhydric alcohol, sugar and water-retaining paste are foods or food additives.
【００１２】本発明のティシュペーパーは、多価アルコ
ール及び糖類、保水性を有する糊料を、繊維ウェブを抄
造する際に乾燥前の湿潤状態で含有させ、あるいは、繊
維ウェブを抄造した後、このウェブに含浸させる外添法
により製造される。[0012] tissue paper of the present invention, polyhydric alcohols and saccharides, the glue charges having water retention, a fibrous web is contained in a wet state before drying in papermaking or after papermaking fiber web, the It is manufactured by an external addition method of impregnating the web.
【００１３】本発明のティシュペーパーに含有される、
吸湿性を有する多価アルコール及び糖類としては、グリ
セリン，Ｄ−ソルビット，マルチトール，還元麦芽糖水
飴，還元澱粉加水分解物等が挙げられる。The tissue paper of the present invention contains
Examples of the polyhydric alcohol and saccharide having hygroscopicity include glycerin, D-sorbitol, maltitol, reduced maltose syrup, reduced starch hydrolyzate, and the like.
【００１４】更に、保水性を有する糊料としては、アル
ギン酸ナトリウム，ポリアクリル酸ナトリウム，メチル
セルロース，アルギン酸プロピレングリコールエステ
ル，繊維素グリコール酸ナトリウム（ＣＭＣ），繊維素
グリコール酸カルシウム，澱粉グリコール酸ナトリウ
ム，澱粉リン酸エステルナトリウム，カゼイン，カゼイ
ンナトリウム等が挙げられる。Further, as the paste having water retention properties, sodium alginate, sodium polyacrylate, methylcellulose, propylene glycol alginate, sodium cellulose glycolate (CMC), calcium cellulose glycolate, sodium starch glycolate, starch Examples include sodium phosphate ester, casein, sodium caseinate and the like.
【００１５】上記の多価アルコール及び糖類、保水性を
有する糊料は、いずれも本発明のティシュペーパーに、
吸湿性，柔軟性，肌触り性等を付与し、もしくは向上さ
せる作用をなすものであり（従って、これらを纏めて
“吸湿・柔軟性等付与剤”と言う）、本発明のティシュ
ペーパーでは、吸湿性を有する薬剤のうちの少なくとも
一種を含有していればよい。ここで、上記吸湿・柔軟性
等付与剤には、塩化ナトリウム、塩化カルシウム、ピロ
リン酸カリウム、メタリン酸ナトリウム、ポリリン酸カ
リウム、ポリリン酸ナトリウム等の吸湿性を有する塩類
を追加しても良い。The above-mentioned polyhydric alcohol, saccharides and water-sizing paste are all used in the tissue paper of the present invention.
Hygroscopic, flexible, impart texture and the like, or are those which form a function of improving (hence, these are collectively referred to as "moisture absorption, flexibility, etc. imparting agent"), tissue of the present invention
The paper only needs to contain at least one of hygroscopic drugs. Here, salts having hygroscopicity, such as sodium chloride, calcium chloride, potassium pyrophosphate, sodium metaphosphate, potassium polyphosphate, and sodium polyphosphate, may be added to the agent for imparting moisture absorption and flexibility.
【００１６】本発明のティシュペーパーにおける上記の
吸湿・柔軟性等付与剤の含有量は、余り少な過ぎれば含
有効果が生じず、逆に余り多過ぎても効果が飽和して不
経済となるため、本発明のティシュペーパーでは、繊維
ウェブの重量に対して、１．０〜１００重量％とする。
すなわち、ティシュペーパーの肌触り性を考慮した場合
には、吸湿・柔軟性等付与剤の含有量が１重量％より少
ないと肌触り性が向上せず、１００重量％より多いと水
分含有性が多過ぎて使用感に劣るため、１．０〜１００
重量％とすることが好ましい。以上の吸湿・柔軟性等付
与剤は、確実な安全性を確保するために、本発明では、
食品または食品添加物から選択したものを使用すること
が好ましい。なお、食品または食品添加物以外のグレー
ド（例えば、化粧品原料基準グレード、日本薬局方グレ
ード、ＪＩＳグレード等）に属する物質であっても、人
体への安全性が高いものであれば、吸湿・柔軟性等付与
剤に使用して差し支えない。If the content of the above-mentioned agent for imparting moisture absorption and flexibility in the tissue paper of the present invention is too small, the content effect does not occur. Conversely, if the content is too large, the effect is saturated and uneconomical. In the tissue paper of the present invention, the content is 1.0 to 100% by weight based on the weight of the fiber web.
In other words, when considering the feel of tissue paper chromatography, the content of moisture and flexibility like imparting agent does not improve the texture of less than 1 wt%, the multi-moisture content of the more than 100 wt% 1.0-100
It is preferable to set the weight%. The above-mentioned agent for imparting moisture absorption and flexibility, in order to ensure certain safety, in the present invention,
It is preferred to use one selected from foods or food additives. Even if the substance belongs to a grade other than food or food additive (for example, cosmetic raw material standard grade, Japanese Pharmacopoeia grade, JIS grade, etc.), if it is highly safe to human body, it will absorb moisture and soften. It may be used as a property imparting agent.
【００１７】また、本発明のティシュペーパーにおいて
は、上記の吸湿・柔軟性等付与剤のほかに、流動パラフ
ィン，スクワラン等の炭化水素類、オリーブ油，ツバキ
油，ヒマシ油，大豆油等の植物油、ミツロウ，カルナウ
バロウ，ラノリン等のロウ類、及びセタノール，ステア
リルアルコール，オレイルアルコール等の高級アルコー
ル類を平滑感、手触り感の向上のために含ませても良
い。この油類の含有量は、余り少なすぎても含有効果が
生じず、逆に余り多過ぎても肌触り感が減じるため、本
発明のティシュペーパーでは、繊維ウェブの重量に対し
て、０．１〜３０重量％とすることが好ましい。In the tissue paper of the present invention, in addition to the above agents for imparting moisture absorption and flexibility, hydrocarbons such as liquid paraffin and squalane, vegetable oils such as olive oil, camellia oil, castor oil and soybean oil, beeswax, carnauba wax, waxes and lanolin, and cetanol, stearyl alcohol, smooth sense of higher alcohols such as oleyl alcohol, even if Mase including in order to improve the touch feeling good
No. The content of this oils also causes no content effect much too small, to reduce even touch feeling much too many Conversely, the tissue paper of the present invention, relative to the weight of the fibrous web, 0.1 It is preferable to set it to 30% by weight.
【００１８】そして、これらの油類と上記の吸湿・柔軟
性等付与剤、あるいは後述する他の配合剤との混合状態
を均一にするためと、疎水性物質の含有により生じるで
あろう吸水性の低下を補うために、ショ糖脂肪酸エステ
ル，ソルビタン脂肪酸エステル，グリセリン脂肪酸エス
テル，ポリオキシエチレンラノリンアルコールエーテ
ル，ポリオキシエチレンアルキルエーテル，ポリオキシ
エチレン脂肪酸エステル等の非イオン系界面活性剤、脂
肪酸塩、アルキルベンゼンスルホン酸塩、ポリオキシエ
チレンアルキルエーテル硫酸塩等の陰イオン系界面活性
剤等の界面活性剤を、必要に応じて、適量配合すること
ができる。Further, in order to make the mixing state of these oils and the above-mentioned moisture-absorbing / flexibility imparting agent, or other compounding agents described later uniform, the water-absorbing property which would be caused by the inclusion of a hydrophobic substance. Non-ionic surfactants such as sucrose fatty acid esters, sorbitan fatty acid esters, glycerin fatty acid esters, polyoxyethylene lanolin alcohol ethers, polyoxyethylene alkyl ethers, polyoxyethylene fatty acid esters, fatty acid salts, An appropriate amount of a surfactant such as an anionic surfactant such as an alkylbenzene sulfonate or a polyoxyethylene alkyl ether sulfate can be blended if necessary.
【００１９】加えて、本発明のティシュペーパーでは、
ソルビン酸，ソルビン酸カリウム，デヒドロ酢酸，デヒ
ドロ酢酸ナトリウム，安息香酸，安息香酸ナトリウム，
パラオキシ安息香酸ブチル，パラオキシ安息香酸イソブ
チル，パラオキシ安息香酸エチル，パラオキシ安息香酸
プロピル，パラオキシ安息香酸イソプロピル等の防腐防
かび剤、前述の従来の柔軟剤をも、適量配合して使用す
ることができる。In addition, in the tissue paper of the present invention,
Sorbic acid, potassium sorbate, dehydroacetic acid, sodium dehydroacetate, benzoic acid, sodium benzoate,
Preservatives and fungicides such as butyl paraoxybenzoate, isobutyl paraoxybenzoate, ethyl paraoxybenzoate, propyl paraoxybenzoate, and isopropyl paraoxybenzoate, and the above-mentioned conventional softeners can also be used in appropriate amounts.
【００２０】以上の本発明のティシュペーパーを製造す
るには、繊維ウェブの抄造中にウェブの形成後であって
乾燥前の湿潤状態でスプレー等により上記の吸湿・柔軟
性等付与剤を含浸させるか、繊維ウェブを抄造し乾燥し
た後、このウェブに上記の吸湿・柔軟性等付与剤を含浸
する外添法が採用される。In order to produce the above-mentioned tissue paper of the present invention, the above-mentioned agent for imparting moisture absorption and flexibility is impregnated by spraying or the like in a wet state after forming the web and before drying during papermaking of the fibrous web. Alternatively, an external addition method is employed in which a fiber web is formed and dried, and then the web is impregnated with the above-described agent for imparting moisture absorption and flexibility.
【００２１】外添を乾燥後に行う場合は、繊維ウェブを
抄造した後に、（例えば加工装置上で）ウェブに吸湿・
柔軟性等付与剤の溶液をスプレーしたり、ウェブをこの
溶液中に浸漬したり、印刷機によりウェブを印刷する等
により、所要量を含浸させればよい。When the external addition is performed after drying, after the fiber web is formed, the web is subjected to moisture absorption (for example, on a processing apparatus).
The required amount may be impregnated by spraying a solution of the flexibility imparting agent , dipping the web in the solution, or printing the web by a printing machine.
【００２２】[0022]
【作用】本発明のティシュペーパーでは、吸湿性を有す
る多価アルコール及び糖類、あるいは保水性を有する糊
料が、含有水分を増加させる作用をなす。この作用によ
り本発明のティシュペーパーが水分を吸収すると、この
水分が、繊維を膨潤させ、かつ繊維の水素結合を緩ませ
て、外力に対する抵抗を少なくする。しかも、この水分
は、繊維と対象物（例えば、皮膚等）との間の潤滑剤と
しても作用する。このような水分の作用により、本発明
のティシュペーパーでは、柔軟性，肌触り性が向上す
る。また、吸湿・柔軟性等付与剤のほかに、必要に応じ
て油類物質を繊維ウェブに対して所定量加えることによ
り、平滑感や手触り性が一層向上する。In the tissue paper of the present invention, a polyhydric alcohol and a saccharide having a hygroscopic property, or a paste having a water retention property have an action of increasing the water content. When the tissue paper of the present invention absorbs moisture by this action, the moisture swells the fibers and loosens the hydrogen bonds of the fibers, thereby reducing resistance to external force. In addition, this moisture also acts as a lubricant between the fibers and the object (for example, skin or the like). By the action of such moisture, the tissue paper of the present invention improves flexibility and softness. In addition to moisture-absorbing and flexibility-imparting agents , if necessary
By adding a predetermined amount of the oily substance to the fibrous web, the smoothness and feel can be further improved.
【００２３】ところで、一般に、紙や不織布の湿度（水
分）は、紙や不織布の吸湿能力と、外気の湿度とによっ
てバランスされる。これに対し、本発明のティシュペー
パーにおいて、保水性を有する糊料を、吸湿性を有する
多価アルコール，糖類と併用する場合、糊料の保水性に
より、空気中の水分が一旦吸収されると、その蒸発速度
が遅くなる。従って、必要に応じて糊料を併用する本発
明のティシュペーパーでは、外気の湿度が大きく変化す
るような気象状態にあっても、湿度変化が緩やかにな
り、上記した柔軟性や肌触り向上等の水分の作用が持続
する。In general, the humidity (moisture) of paper or nonwoven fabric is balanced by the moisture absorption capacity of paper or nonwoven fabric and the humidity of the outside air. In contrast, the tissue paper of the present invention
In par , when a paste having water retention is used in combination with a polyhydric alcohol or saccharide having hygroscopicity, once the moisture in the air is absorbed by the water retention of the paste, the evaporation rate of the paste is reduced. Therefore, in the tissue paper of the present invention using a paste as needed, even in a weather condition in which the humidity of the outside air greatly changes, the humidity change becomes gradual, and the above-described softness and softness are improved. The action of moisture lasts.
【００２４】しかも、上記の糊料を併用する場合、この
糊料の接着作用により繊維同士の接着性が向上してウェ
ブの接着強度が高まり、ウェブ屑の発生が少なくなると
共に、触感（ヌメリ感）も向上する。In addition, when the above-mentioned paste is used in combination, the adhesive action of the paste enhances the adhesiveness between the fibers to increase the adhesive strength of the web, thereby reducing the generation of web waste and providing a tactile (slimy) feeling. ) Also improves.
【００２５】[0025]
【実施例】１）繊維ウェブとして家庭紙を使用した実施
例を説明する。坪量が１３．０ｇ／ｍ2で、縦２００ｍ
ｍ、横２２５ｍｍのティシュペーパー（河野製紙（株）
製商品名“ホワイトティシュ”２００組ボックス入りを
使用）の１組（２枚重ね）の両面に、表１に示す吸湿・
柔軟性等付与剤（単独の溶液または混合したものの溶
液）を、このティシュペーパー１組（２６．０ｇ／
ｍ2、これを１００重量％とする）に対し表１に示す量
になるように、ハンドスプレーで均一に噴霧し、湿潤さ
せた後、全自動定温恒温器により８０±２℃で１時間乾
燥させた（なお、表１において、実施例１〜８は、吸湿
性を有する多価アルコール及び糖類のうち少なくとも一
種、または、吸湿性を有する多価アルコール及び糖類の
うち少なくとも一種並びに保水性を有する糊料を、吸湿
・柔軟性等付与剤として繊維ウェブに所定量含ませた例
であり、また、試験例１〜３は、参考のために、吸湿性
を有する塩類を繊維ウェブに所定量含ませた例であ
る）。これを、調湿箱（温度２０±５℃、湿度６５±５
％）に８時間以上放置し、平衡状態になった後のサンプ
ルについて、表４に示す各種の測定を行い、この結果を
実施例１〜８、試験例１〜３として表４に併せて示し
た。EXAMPLE 1) Implementation using household paper as a fiber web
An example will be described. The basis weight is 13.0 g / m 2 and the height is 200 m
225 mm wide tissue paper (Kono Paper Co., Ltd.)
On both sides of the manufactured product name using the "white tissue" 200 set boxed) of a pair (two-ply), shown to moisture absorption, in Table 1
One set of this tissue paper (26.0 g /
m 2 , which is assumed to be 100% by weight) and uniformly sprayed with a hand spray so that the amount shown in Table 1 is obtained, wetted, and then dried at 80 ± 2 ° C. for 1 hour using a fully automatic constant temperature incubator. (Note that, in Table 1, Examples 1 to 8 show that
At least one of polyhydric alcohols and saccharides
Species or hygroscopic polyhydric alcohols and saccharides
Absorb at least one of them and water-sizing paste
・ Example in which a predetermined amount is included in a fiber web as a flexibility imparting agent
In addition, Test Examples 1-3 are hygroscopic for reference.
In this example, a predetermined amount of salt having
). Place this in a humidity control box (temperature 20 ± 5 ° C, humidity 65 ± 5
%) For at least 8 hours, and various measurements shown in Table 4 were performed on the sample after the equilibrium state was obtained. The results are shown in Table 4 as Examples 1 to 8 and Test Examples 1 to 3. Was.
【００２６】２）なお、本発明における吸湿・柔軟性等
付与剤の効能を確認するために、繊維ウェブとして不織
布を使用した参考例を以下に説明する。目付量が３０ｇ
／ｍ2の不織布（二村化学工業（株）製商品名“太閤Ｔ
ＣＦ＃５０３”を使用）を２００ｍｍ×１６０ｍｍに裁
断し、両面に表２に示す吸湿・柔軟性等付与剤（混合し
たものの溶液）を、この不織布（３０．０ｇ／ｍ2、こ
れを１００重量％とする）に対し表２に示す量になるよ
うに、ハンドスプレーで均一に噴霧し、湿潤させた後、
上記１）の家庭紙を使用する場合の例と同様にして乾燥
し、調湿した後のサンプルについて、表５に示す各種の
測定を行い、この結果を参考例９，１０として表５に併
せて示した。2) Moisture absorption and flexibility in the present invention
Nonwoven as a fibrous web to confirm the effectiveness of the imparting agent
A reference example using a cloth will be described below. The basis weight is 30g
/ M 2 nonwoven fabric (trade name “Taiko T” manufactured by Nimura Chemical Industry Co., Ltd.)
The use) CF # 503 "was cut into 200 mm × 160 mm, shown to moisture absorption, flexibility, etc. imparting agent in Table 2 on both sides (the mixed solution although), the nonwoven (30.0 g / m 2, it 100% by weight) and uniformly sprayed with a hand spray so that the amount shown in Table 2 is obtained, and then wetted.
Various measurements shown in Table 5 were performed on the sample after drying and humidity control in the same manner as in the case of using the household paper of 1) above, and the results are shown in Table 5 as Reference Examples 9 and 10. Shown.
【００２７】３）繊維ウェブとして上記１），２）と同
じ家庭紙または不織布を使用し、本発明の吸湿・柔軟性
等付与剤の代わりに表３に示す薬剤を、表３に示す量に
なるように、上記１），２）と同様にして噴霧した後、
上記１），２）と同様にして乾燥し、調湿したサンプル
を比較例１，２（家庭紙），３，４（不織布）として、
表４，５に示す各種の測定を行い、この結果を併せて示
した。3) The same household paper or nonwoven fabric as in 1) and 2) above was used as the fibrous web, and the agents shown in Table 3 were used instead of the moisture-absorbing / softness imparting agents of the present invention in the amounts shown in Table 3. After spraying in the same manner as in 1) and 2) above,
Samples dried and conditioned in the same manner as in 1) and 2) above were used as Comparative Examples 1 and 2 (household paper), 3 and 4 (non-woven fabric).
Various measurements shown in Tables 4 and 5 were performed, and the results are also shown.
【００２８】また、参考のために、表１〜表３に示す薬
剤を除いて水のみで処理した上記１），２）と同じ家庭
紙または不織布について、ブランク１（家庭紙），２
（不織布）として表４，５に示す各種の測定を行い、こ
の結果を併せて示した。For reference, blanks 1 (household paper) and 2 were prepared using the same household paper or nonwoven fabric as in 1) and 2) above, which were treated with water only, except for the chemicals shown in Tables 1 to 3.
Various measurements shown in Tables 4 and 5 were performed for (nonwoven fabric), and the results are also shown.
【００２９】[0029]
【表１】 [Table 1]
【００３０】[0030]
【表２】 [Table 2]
【００３１】[0031]
【表３】 [Table 3]
【００３２】表１，表２，表３の各薬剤は、次のものを
使用した。 塩化カルシウム；国産化学（株）製商品名“塩化カルシ
ウム（試薬）” ピロリン酸カリウム；国産化学（株）製商品名“ピロリ
ン酸カリウム（試薬）” ソルビット；日研化学（株）製商品名“ソルビトール−
ＦＰ” マルチトール；東京化成工業（株）製商品名“マルチト
ール（試薬）” グリセリン；旭電化工業（株）製商品名“食添グリセリ
ン” 流動パラフィン；エッソ石油（株）製商品名“クリスト
ール７０” アルギン酸ナトリウム；（株）紀文フードケミファ製商
品名“ダックアルギンＮＳＰＭ” ポリオキシエチレンラノリンアルコールエーテル；第一
工業製薬（株）製商品名“ラミゲンＥＴ−７０”（ＨＬ
Ｂ１４） ショ糖脂肪酸エステル；第一工業製薬（株）製商品名
“ＤＫエステルＦ−１４０”（ＨＬＢ１３） ソルビタン脂肪酸エステル；第一工業製薬（株）製商品
名“ソルゲン５０”（ＨＬＢ４．７） パラオキシ安息香酸エステル；上野製薬（株）製商品名
“ネオメッキンス”The following drugs were used as the drugs in Tables 1, 2 and 3. Calcium chloride; Domestic Chemical Co., Ltd. product name "Calcium chloride (reagent)" Potassium pyrophosphate; Domestic Chemical Co., Ltd. product name "potassium pyrophosphate (reagent)"Sorbit; Niken Chemical Co., Ltd. product name " Sorbitol-
FP "Maltitol; Trade name" Maltitol (reagent) "manufactured by Tokyo Kasei Kogyo Co., Ltd. Glycerin; Trade name" Food Glycerin "manufactured by Asahi Denka Kogyo Co., Ltd. Liquid paraffin; Trade name" Cris "manufactured by Esso Oil Co., Ltd. Stall 70 "sodium alginate; trade name" Duck Algin NSPM "manufactured by Kibun Food Chemifa Co., Ltd. polyoxyethylene lanolin alcohol ether; trade name" Lamigen ET-70 "manufactured by Daiichi Kogyo Seiyaku Co., Ltd. (HL
B14) Sucrose fatty acid ester; trade name “DK Ester F-140” manufactured by Daiichi Kogyo Seiyaku Co., Ltd. (HLB13) Sorbitan fatty acid ester; trade name “Solgen 50” (HLB 4.7) manufactured by Daiichi Kogyo Seiyaku Co., Ltd. Paraoxybenzoic acid ester; Ueno Pharmaceutical Co., Ltd. product name "Neoplatins"
【００３３】[0033]
【表４】 [Table 4]
【００３４】[0034]
【表５】 [Table 5]
【００３５】表４，表５中の吸湿量Ｗ％は、８０±２℃
×１時間乾燥後のサンプルの重量をｗ１とし、調湿後の
サンプルの重量をｗ２として、以下の数式１により算出
した数値である。The moisture absorption W% in Tables 4 and 5 is 80 ± 2 ° C.
X The numerical value calculated by the following formula 1 where the weight of the sample after drying for 1 hour is w1 and the weight of the sample after humidity control is w2.
【００３６】[0036]
【数１】Ｗ＝｛（ｗ２−ｗ１）／ｗ１｝×１００## EQU1 ## W = {(w2−w1) / w1} × 100
【００３７】また、表４，表５中の手触りは、パネラー
５人により比較して大変良いものを３点、良いものを２
点、やや良いものを１点、劣るものを０点とし（但し、
同評価のサンプルが幾つ有っても良いとした）、５人の
点数を合計して１２〜１５点を◎、８〜１１点を○、４
〜７点を△、０〜３点を×とした。更に、表５中の皮膚
の保湿性，柔軟感は、常温の水道水及び化粧石鹸にて手
を洗った後、ハンカチにより通常、手を拭くように不織
布のサンプルを用いて手を拭くことを各サンプルについ
て繰り返すことにより、パネラー５人により保湿性，柔
軟感を比較して良いものを２点、やや良いものを１点、
劣るものを０点とし（但し、同評価のサンプルが幾つ有
っても良いとした）、５人の点数を合計して７〜１０点
を○、３〜６点を△、０〜２点を×とした。The feel in Tables 4 and 5 was 3 points for a very good touch and 2 points for a good touch as compared by five panelists.
1 point for poor, 1 point for poor, and 0 for poor
It is assumed that there may be any number of samples of the same evaluation).
7 points were rated as Δ, and 0 to 3 points were rated as x. Furthermore, the moisturizing property and softness of the skin shown in Table 5 are as follows: after washing hands with tap water at room temperature and toilet soap, wipe hands with a non-woven fabric sample as with a handkerchief. By repeating for each sample, two panelists who compare the moisturizing property and softness by five panelists, one point that is slightly better,
Inferior items were scored as 0 (however, there may be any number of samples with the same evaluation). The total score of the five people was 7 to 10 points in total, 3 to 6 points in Δ, and 0 to 2 points. Is indicated by x.
【００３８】また、表４の引張り強度は、ＪＩＳ Ｓ−
３１０４に規定されるティシュペーパーの乾燥時引張り
強度試験に準じて紙の縦方向の強度を測定した結果であ
り、表４，表５中の吸水度は、ＪＩＳ Ｓ−３１０４に
規定されるティシュペーパーの吸水度試験に準じて測定
した結果である。The tensile strength in Table 4 is based on JIS S-
3 is a result of measuring the longitudinal strength of the paper in accordance with the tensile strength test when drying the tissue paper specified in 3104. The water absorption in Tables 4 and 5 indicates the tissue paper specified in JIS S-3104. It is the result of having measured according to the water absorption test.
【００３９】そして、表４の紙粉は、図１に示す装置を
使用して測定した。すなわち、図１において、上部に開
口部２を有する箱１（Ｗ４００×Ｌ３５０×Ｈ３００ｍ
ｍ）の底部に、Ｗ0１００×Ｌ0１００ｍｍの表面を黒く
塗った紙３を置き、この表面に両面テープを隙間無く貼
って紙粉を吸着できるようにし、端部を手で摘んだサン
プル５組を開口部２から箱１中に挿入し、このまま（端
部を手で摘んだまま）箱１内で前後に３０回振った後取
り出し、紙３上への紙粉の付着量を目視により比較し
た。付着量が少ないものを○、やや多いものを△、多い
ものを×とした。The paper dust in Table 4 was measured using the apparatus shown in FIG. That is, in FIG. 1, a box 1 (W400 × L350 × H300 m
At the bottom of m), a paper 3 having a surface of W 0 100 × L 0 100 mm painted black was placed, and a double-sided tape was stuck to this surface without any gap so that paper powder could be adsorbed, and the end was sampled by hand. Five sets are inserted into the box 1 through the opening 2 and shaken back and forth 30 times in the box 1 as it is (with the ends picked up by hand), taken out, and the amount of paper dust adhering to the paper 3 is visually observed. Were compared. A sample having a small amount of adhesion was rated as ○, a sample with a slightly large amount was evaluated as Δ, and a sample with a large amount of adhesion was rated X.
【００４０】表４から明らかなように、本発明のティシ
ュペーパーの実施例によれば、吸湿量，手触り，紙粉発
生の防止性，吸水性，皮膚の保湿性，柔軟感とも、比較
例及び何らの処理をしていないブランクのものに比べ、
極めて良好であることが判る。As is apparent from Table 4, the texture of the present invention
According to an embodiment of Yupepa, moisture absorption, texture, prevention of paper dust generation, water absorption, moisture of skin, both soft feeling, compared with that of the blank that is not a comparative example and any processing,
It turns out that it is very good.
【００４１】[0041]
【発明の効果】以上詳述したように本発明のティシュペ
ーパーによれば、安全な吸湿・柔軟性等付与剤を使用し
ているため、高濃度での含有が可能であり、従来のこの
種ウェブに比べ、はるかに優れた柔軟性、肌触り性を有
するティシュペーパーを提供することができる。しか
も、この吸湿・柔軟性等付与剤として、食品または食品
添加物を使用することにより、更に高い安全性を確保す
ることができる。 As described in detail above, the tissue of the present invention
According to Paper , a safe moisture-absorbing / softness-imparting agent is used, so it can be contained at a high concentration and has far superior flexibility and softness compared to conventional webs of this type. Tissue paper can be provided. Moreover, as the moisture absorption, flexibility, etc. imparting agent, by using a food or food additive, Ru can ensure higher safety.
【００４２】また、本発明のティシュペーパーで使用す
る吸湿・柔軟性等付与剤は、親油性や撥水性を帯びない
ため、優れた吸水性を有することができる。Further, the agent for imparting moisture absorption and flexibility used in the tissue paper of the present invention does not have lipophilicity or water repellency, and therefore can have excellent water absorption.
【００４３】加えて、吸湿・柔軟性等付与剤として保水
性を有する糊料を併用すれば、一旦、吸収された水分の
蒸発速度が遅くなり、水分により優れた作用を長時間持
続することができる。従って、必要に応じて糊料を併用
することにより、外気の湿度変化による影響の少ないウ
ェブを提供することができる。また、本発明のティシュ
ペーパーによれば、ウェブ中の保湿成分が皮膚に転移
し、皮膚を保湿して、より優れた肌触り性、柔軟感を付
与することができる。In addition, if a water-retaining paste is used in combination as a moisture-absorbing / flexibility-imparting agent, the rate of evaporation of the absorbed water becomes slower, and the superior action of the water can be maintained for a long time. it can. Therefore, by using a paste as needed, it is possible to provide a web which is less affected by a change in the humidity of the outside air. In addition, the tissue of the present invention
By the paper lever, moisturizing component in the web is transferred to the skin, the skin moisturizing, better feel resistance, it is possible to impart a flexible feel.
【００４４】更に、本発明のティシュペーパーで使用す
る吸湿・柔軟性等付与剤によれば、繊維同士の絡みつき
を阻害しないばかりか、繊維同士の接着強度を高めるこ
とができ、いわゆるウェブ屑の発生を極めて少なくする
ことができる。Further, according to the agent for imparting moisture absorption and flexibility used in the tissue paper of the present invention, not only does not inhibit the entanglement of the fibers, but also the bonding strength between the fibers can be increased, and so-called web debris is generated. Can be extremely reduced.
【図１】本発明のティシュペーパーの効果を実証するた
めに実施例等で使用したウェブ屑（紙粉）発生状況を観
察するための装置である。FIG. 1 is an apparatus for observing the state of generation of web waste (paper powder) used in Examples and the like to verify the effect of the tissue paper of the present invention.
１ 箱 ２ 開口部 ３ 表面を黒く塗り、隙間無く両面テープを貼った紙 1 Box 2 Opening 3 Paper with black surface and double-sided tape with no gap
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 ＦＩ Ｄ２１Ｈ 17/05 Ｄ２１Ｈ 17/05 17/24 17/24 ──────────────────────────────────────────────────の Continued on the front page (51) Int.Cl. 6 Identification code FI D21H 17/05 D21H 17/05 17/24 17/24
Claims (3)
のうち少なくとも一種、または、吸湿性を有する多価ア
ルコール及び糖類のうち少なくとも一種並びに保水性を
有する糊料を、吸湿・柔軟性等付与剤として、家庭紙用
の繊維ウェブに対し１．０〜１００重量％含んでなるこ
とを特徴とする高水分含有性を有するティシュペーパ
ー。1. A moisture-absorbing / flexibility imparting agent comprising at least one of polyhydric alcohols and saccharides having hygroscopicity, or at least one of polyhydric alcohols and saccharides having hygroscopicity and a paste having water retention. Tissue paper having a high water content, comprising 1.0 to 100% by weight based on a fiber web for household paper.
-
が、グリセリン，Ｄ−ソルビット，マルチトール，還元
麦芽糖水飴または還元澱粉加水分解物であることを特徴
とする請求項１記載の高水分含有性を有するティシュペ
ーパー。2. The high water content according to claim 1, wherein the polyhydric alcohol and the saccharide having hygroscopicity are glycerin, D-sorbitol, maltitol, reduced maltose starch syrup or reduced starch hydrolyzate. Tishpe with
Parper .
または保水性を有する糊料が、食品または食品添加物で
あることを特徴とする請求項１または２記載の高水分含
有性を有するティシュペーパー。3. The tissue paper with high water content according to claim 1, wherein the hygroscopic polyhydric alcohol and sugar or the water-sizing paste are foods or food additives. .