JP4668456B2 - Skin Kiyoshi 拭用 cosmetic paper - Google Patents

Skin Kiyoshi 拭用 cosmetic paper Download PDF

Info

Publication number
JP4668456B2
JP4668456B2 JP2001140933A JP2001140933A JP4668456B2 JP 4668456 B2 JP4668456 B2 JP 4668456B2 JP 2001140933 A JP2001140933 A JP 2001140933A JP 2001140933 A JP2001140933 A JP 2001140933A JP 4668456 B2 JP4668456 B2 JP 4668456B2
Authority
JP
Japan
Prior art keywords
pulp
paper
weight
skin
decorative sheet
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2001140933A
Other languages
Japanese (ja)
Other versions
JP2002330820A (en
Inventor
伸一 武智
正栄 重冨
繁徳 黒木
Original Assignee
大王製紙株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大王製紙株式会社 filed Critical 大王製紙株式会社
Priority to JP2001140933A priority Critical patent/JP4668456B2/en
Publication of JP2002330820A publication Critical patent/JP2002330820A/en
Application granted granted Critical
Publication of JP4668456B2 publication Critical patent/JP4668456B2/en
Application status is Active legal-status Critical
Anticipated expiration legal-status Critical

Description

【0001】 [0001]
【発明の属する技術分野】 BACKGROUND OF THE INVENTION
本願発明は、皮脂吸収作用をもつ皮膚清拭用化粧用紙に関するものである。 The present invention relates to skin Kiyoshi 拭用 decorative paper with sebum absorption.
【0002】 [0002]
【従来の技術】 BACKGROUND OF THE INVENTION
人体の顔面皮膚に分泌される皮脂を吸収して顔面を清拭する化粧用紙として脂取り紙が知られている。 Oil blotting paper is known in the face to absorb the sebum, which is secreted into the human body of facial skin as a cosmetic paper to be cleaned. この脂取り紙は、皮脂吸収性は勿論のこと、それ以外にも、顔面皮膚への肌ざわり感触とか柔軟性といった感覚上の要素も重要である。 The oil-absorbing paper, sebum absorption is of course that, in addition to it, elements on the feeling, such as skin sitting dividing feel Toka flexibility to the facial skin is also important.
【0003】 [0003]
ところで、皮脂吸収作用をもつ皮膚清拭用化粧用紙(いわゆる「脂取り紙」)に柔軟性を付与するために色々な柔軟剤を使用することが考えられるが、従来から一般的な柔軟剤の添加は、紙の繊維間結合を弱め、脂取り紙の基本的機能である皮脂吸収作用を低下させるという問題がある。 Incidentally, it is conceivable to use a variety of softening agents in order to impart flexibility to the skin Qing 拭用 decorative paper with sebum absorption (so-called "oil blotting paper"), a general softening agent conventionally addition, weaken the bonds between the fibers of the paper, there is a problem of lowering the sebum absorption is a fundamental feature of the oil-absorbing paper.
【0004】 [0004]
保湿効果により紙を柔軟化させる天然素材に由来するコラーゲンなどの成分・繊維は非常に高価であり、また、硬化しやすく、その保湿能力が低下するため、効果を持続することが難しい。 Component-fibers such as collagen derived from natural materials to soften the paper by moisturizing effect is very expensive, also cured easily, since the moisturizing ability is lowered, it is difficult to sustain the effect.
【0005】 [0005]
また、天然に置き換え素材としての合成の柔軟剤(たとえば、東邦化学 ソフノン)があるが、合成柔軟剤は有臭性があり、化粧用紙には不適合である。 Further, softener synthesis as a material substituting the natural (e.g., Toho Chemical Sofunon) there is a synthetic softener has odorous property, the decorative sheet is irrelevant.
【0006】 [0006]
一方、紙に柔軟性を付与するための物理的方法として、いわゆる金箔打ち加工法があるが、この方法は、生産性が悪くコスト高になり、消費者に安価な製品を提供できない、という難点がある。 Difficulty Meanwhile, as a physical method for imparting softness to paper, there is a so-called gold leaf beating processing method, the method, the productivity becomes poor cost can not provide an inexpensive product to the consumer, that there is.
【0007】 [0007]
【発明が解決しようとする課題】 [Problems that the Invention is to Solve
本願発明は、すぐれた皮脂吸収性とともに、高度な柔軟性をそなえた皮膚清拭用化粧用紙を低コストに提供しようとなされたものである。 The present invention, together with excellent sebum absorbency, which has been made and to provide a skin Qing 拭用 decorative sheet provided with a high degree of flexibility at low cost.
【0008】 [0008]
【課題を解決するための手段】 In order to solve the problems]
本願発明の皮膚清拭用化粧用紙は、紙の主成分となる繊維原料のほかに、皮脂吸収作用をもつ吸油性填料と、紙に柔軟性を付与する柔軟剤とを基本構成要素としてなる。 Skin Kiyoshi 拭用 decorative sheet of the present invention, in addition to the fiber material as a main component of paper, comprising the oil-absorbing fillers with sebum absorption, and a softener which imparts a softness to the paper as a basic component.
【0009】 [0009]
本願発明の化粧用紙の原料となる繊維としては、木材パルプ繊維、マニラ麻、亜麻、大麻、黄麻、楮、三椏、雁皮等の靱皮繊維、コットン、藁、竹、ケナフ等の非木材パルプ繊維、アクリルやレーヨン等の化学繊維、シルク等の動物繊維が挙げられる。 The fibers as a raw material for cosmetic sheet of the present invention, wood pulp fibers, Manila hemp, flax, hemp, jute, paper mulberry, mitsumata, bast fibers such as Ganpi, cotton, straw, bamboo, non-wood pulp fibers such as kenaf, acrylic chemical fibers and rayon, and animal fibers silk like. 特にマニラ麻、亜麻、大麻、黄麻、楮、三椏、雁皮等の靱皮繊維を原料とする化粧用紙は強度が高く、吸脂能力に優れている。 Particularly Manila hemp, flax, hemp, jute, paper mulberry, mitsumata, decorative paper bast fibers as a raw material, such as Ganpi has high strength and excellent oil absorption ability. これらの繊維は、それぞれ単独で用いられてもよく、また2種以上を混合して用いてもよい。 These fibers may be used alone, or may be used in combination of two or more. 一般公知の抄紙方法で抄紙された化粧用紙の坪量(JISP−8124による。以下、同じ)が8〜30g/m 2であれば、化粧用紙として好適に使用できる。 The basis weight of the decorative paper which is paper in general known papermaking methods (by JISP-8124. Hereinafter, the same) is as long as 8~30g / m 2, can be suitably used as a cosmetic sheet. 上記化粧用紙の坪量が8g/m 2未満であると強度が低く使用時に撚れや破損を生じやすくなり、坪量が30g/m 2を超えるとコストが嵩むだけでなく、また、しなやかさがなくなり、使用感が悪化する。 The decorative strength and basis weight is less than 8 g / m 2 of the sheet becomes prone to twist and breakage during use low basis weight not only costly exceeds 30 g / m 2, also supple is eliminated, a feeling of use is deteriorated.
【0010】 [0010]
脂取り紙用として好適な填料としては、従来公知の吸油性無機填料が使用可能であるが、たとえばスチレンビーズのような有機填料も使うことができる。 Suitable fillers for use oil-absorbing paper, traditionally known oil-absorbing inorganic filler can be used, can also be used e.g. organic fillers such as styrene beads.
【0011】 [0011]
化粧用紙用、特に脂取り紙用として好適な吸油性無機填料としては、クレー、タルク、炭酸カルシウム、ホワイトカーボン、酸化チタン、ヒドロキシアパタイト等があるが、その中で最も好適な無機填料としては本願出願人の先願にかかる特願2000−234908号で開示されている「ヒドロキシアパタイト」含有の無機填料がある。 Cosmetic sheet, a particularly preferred oil-absorbing inorganic filler for the oil-absorbing paper, present clay, talc, calcium carbonate, white carbon, titanium oxide, there is a hydroxyapatite, as the most preferable inorganic filler therein there are applicant "hydroxyapatite" disclosed in such Japanese Patent application No. 2000-234908 the earlier application containing an inorganic filler. ヒドロキシアパタイト[Ca 10 (PO 46 (OH) 2 ]は、人の骨や歯の成分であり、リン酸カリシウムの一種で、工業的には陽イオン、陰イオン、たんぱく質、アミノ酸などに対して優れた吸着性を有する材料として、また、生体への影響が小さいことから、人工歯根など生体適合材として注目されている。 Hydroxyapatite [Ca 10 (PO 4) 6 (OH) 2] is the bones and components of a person's teeth, a kind of phosphoric acid Karishiumu industrially the cationic, anionic, proteins, amino acids with respect to such as a material having excellent adsorptivity Te, in addition, since the effect on the living body is small, it has attracted attention as a biocompatible material such as an artificial tooth root. ヒドロキシアパタイトは、皮脂の中でも、特に酸化された皮脂(過酸化脂質)を効率よく吸着する性質を有するため、これを吸油性填料中に含有させることにより、酸化皮脂を効率よく吸収する化粧用紙が得られる。 Hydroxyapatite is in sebum, since it has the property of particularly efficiently adsorbed sebum oxidized (lipid peroxidation), by containing it in the oil-absorbing fillers, decorative paper to absorb the oxidized sebum efficiently is can get. ヒドロキシアパタイトの含有量は、化粧用紙の主成分である繊維原料に対して1〜100重量%とするのがよい。 The content of hydroxy apatite is preferably set to 1 to 100% by weight relative to the fiber material which is the main component of the decorative sheet. 1%未満だと十分な過酸化脂質吸着効果が得られず、100%以上だと化粧用紙としての十分な紙の強度が得られない。 Not enough lipid peroxide adsorption effect can be obtained with less than 1%, can not be obtained a sufficient strength of the paper as a cosmetic sheet that it 100% or more.
【0012】 [0012]
上記填料中には、さらにタルクを含有させるのが好適である。 The above in filler, it is preferable to further contain talc. タルクの含有量は、化粧用紙の主成分である繊維原料に対して0.5〜90重量%とするのがよい。 The content of talc is preferably set to 0.5 to 90% by weight relative to the fiber material which is the main component of the decorative sheet. また、上記填料は平均粒子径を0.5〜8μmとするのがよい(就中、0.5〜2μmの範囲が、化粧用紙の平滑度を向上させる上で特に好適である)。 Further, the filler is preferably set to 0.5~8μm an average particle diameter (especially, the range of 0.5~2μm are particularly suitable for improving the smoothness of the cosmetic sheet). 更に好適には、2種類以上の填料を組み合わせるのが好適であり、特にヒドロキシアパタイトとタルクの組み合わせは、柔軟性、吸脂性に好適な相乗効果をかもしだす。 More preferably, it is preferable to combine two or more of filler, particularly the combination of hydroxy apatite and talc, engender flexibility, suitable synergistic effect on oil absorption.
【0013】 [0013]
平均粒子径が0.5μm未満の填料は、紙中への歩留まりが悪く、コスト的に不利であり、脂質の除去性に劣る。 Fillers average particle size of less than 0.5μm, the poor yield into the paper, a cost disadvantage, poor removability of the lipid. 平均粒子径が8μmを超えると肌触りが極端に悪化し、粉落ちなどの問題が生じる。 When the average particle diameter is more than 8μm feel is extremely deteriorated, problems such as dusting occurs. 上記のように、填料中にタルクを0.5〜90重量%含有させると、紙の平滑度が向上し、化粧用紙の肌触りがよくなる。 As described above, when talc is contained 0.5 to 90 wt% in filler improves the smoothness of the paper, soft cosmetic sheet is improved. さらに加えて、吸脂時に紙の透明度を向上させる機能がより優れたものとなる。 In addition, it is assumed that function to improve the transparency of the paper when oil absorption is more excellent. また、本願発明の化粧用紙には、保湿剤およびおしろい粉の少なくとも一方を含有させることもできる。 Further, the decorative sheet of the present invention, may contain at least one humectant and face powder powder. 保湿剤やおしろい粉を含有させることにより、皮膚の保護性や化粧の効果により優れた化粧用紙となる。 By containing the moisturizer and face powder powder, an excellent decorative sheet by protective and decorative effect of the skin.
【0014】 [0014]
本願発明の化粧用紙では、上記例示のような填料のほかに、さらに化粧用紙に柔軟性を与付するために多価アルコール系の柔軟剤を添加する。 The decorative sheet of the present invention, in addition to the filler as exemplified above, further addition of softener polyhydric alcohol in order to subject given the flexibility the decorative paper.
【0015】 [0015]
本願発明にかかる化粧用紙は、上記例示の填料や柔軟剤等が、どのような形態で含まれていてもよい。 Cosmetic sheet according to the present invention, the above-exemplified fillers and softening agents and the like, may be included in any form. 内添されていてもよいし、抄紙後の原紙に填料を塗工するようにしてもよい。 It may be internally added, may be coated with a filler to base paper after paper.
【0016】 [0016]
なお、本願発明の化粧用紙は、既知の化粧用紙の抄紙方法に基づいて、抄紙することが可能である。 Incidentally, the decorative sheet of the present invention, based on the papermaking method known cosmetic sheet can be paper. たとえば、填料や柔軟剤等を添加した繊維パルプスラリーを既知の抄紙機によって抄紙して製造することが可能である。 For example, it is possible to produce by papermaking fiber pulp slurry was added filler and softening agent by a known paper machine.
【0017】 [0017]
一方、本願発明の化粧用紙は、次記の疑似吸脂量測定方法による吸脂量が1g/m 2以上であることが望ましい。 On the other hand, cosmetic paper of the present invention, it is desirable oil absorption amount by the quasi oil absorption amount measuring method of the next SL is 1 g / m 2 or more. 吸脂量が1g/m 2未満であると、吸収する皮脂の量が少なすぎて化粧用紙として適さない。 If oil absorption amount is less than 1 g / m 2, is not suitable as a cosmetic sheet is too small the amount of sebum absorbed. 吸脂量が1g/m 2以上であれば、化粧用紙の皮脂吸収量としては十分である。 If oil absorption amount is 1 g / m 2 or more is sufficient as sebum absorption of the cosmetic sheet.
【0018】 [0018]
上記疑似吸脂量測定法は、印刷適性試験機の胴の表面に21cm×25cmの試料片を粘着テープなどで固定して有効面積19cm×18cmとし、上記印刷適性試験機の印刷ロールに油液(ヒマシ油80重量%+ベンジルアルコール20重量%)0.5mlを膜厚4.8μmとなるように均一に塗布した上、上記胴と印刷ロールとのニップ幅を5mmとして転写回転速度30rpmで1回転させて、上記油液を上記試料に転写させる。 The pseudo oil absorption amount measurement method, the effective area 19cm × 18cm sample piece surface to 21cm × 25 cm of the trunk of printability tester fixed with adhesive tape or the like, the hydraulic fluid to the printing roll of the printability tester (castor oil 80 wt% + benzyl alcohol 20% by weight) on which is uniformly applied to the 0.5ml a thickness 4.8 .mu.m, the transfer speed 30rpm a nip width between the cylinder and the printing roll as 5 mm 1 is rotated to transfer the hydraulic fluid in the sample. その後に、転写後の有効面積分の試料片の重量から転写前の有効面積分の紙の重量を差分した値(数1)に基づいて、試料1m 2あたりの吸脂量とする。 Then, based on the value (number 1) obtained by subtracting the weight of the paper of the effective area fraction before transfer from the weight of the effective area fraction sample piece after transfer, the oil absorption amount per sample 1 m 2.
【0019】 [0019]
【数1】 [Number 1]
【0020】 [0020]
また、脂取り紙に代表される、皮脂を吸収させて除去することを目的とする化粧用紙は、使用者が皮脂を拭き取れたことを視覚的に確認できるように、多くの場合、皮脂を吸収すると、吸収部分の透明度が向上する機能を有している。 Further, typified by oil blotting paper, as cosmetic sheet for the purpose of removing by absorbing the sebum can visually confirm that the user has wiped off the sebum often absorb sebum Then, the transparency of the absorption part has a function to improve. 本願発明者らは、かかる機能の良否をパンチ力という数値で表している。 The present inventors have expressed the acceptability of such a function in the numerical value of the punch force. パンチ力は、吸脂前と吸脂後の紙の色差より算出される値であり、パンチ力の数値が高ければ高いほど、吸脂時に透明度が向上することになり使用者の満足感が得られる化粧用紙である。 Punch force is a value calculated from the color difference of the paper after oil absorption before and oil absorption, the higher the value of the punch, obtained satisfaction of the user will be improved transparency when oil absorption it is a cosmetic paper.
【0021】 [0021]
本願発明の化粧用紙は、上記パンチ力が5.0以上であることが好ましい。 Cosmetic sheet of the present invention, it is preferable that the punching force is 5.0 or more. パンチ力が5.0以上あれば、吸脂時に透明性が発現して、吸脂高価を視覚的に確認できる。 If punch is 5.0 or more, it expressed transparency upon oil absorption, can visually confirm the oil absorption expensive. ここで、パンチ力の測定方法は、次記の通りである。 Here, the measurement method of punching power is as follows: Symbol. まず、裏当てに白色板および黒色板を用い、分光白色光度計「EPR−80WX」(東京電色株式会社製)にて、転写前の紙試料の色彩度Lw、Aw、BwおよびLa、Ab、Bbをそれぞれ測定し、両者の色差ΔE 1を(数2)に従って算出する。 First, using a white plate and a black plate to the backing at a spectral white photometer "EPR-80WX" (manufactured by Tokyo Denshoku Co., Ltd.), color saturation Lw paper sample before transfer, Aw, Bw and La, Ab , Bb was measured, to calculate both the color difference Delta] E 1 according to equation (2). それとともに、上記吸脂量の測定と同様に、上記印刷適性試験機の胴の表面に21cm×25cmの試料片を粘着テープなどで固定して有効面積19cm×18cmとし、上記印刷適性試験機の印刷ロールに油液(ヒマシ油80重量%+ベンジルアルコール20重量%)0.5mlを膜厚4.8μmとにるように均一に塗布し、上記胴と印刷ロールとのニップ幅を5mmとして転写回転速度30rpmで1回転させて、上記油液を上記試料に転写させる。 At the same time, similarly to the measurement of the oil absorption amount, and a specimen of 21cm × 25 cm on the surface of the cylinder of the printability tester fixed with adhesive tape or the like as an active area 19cm × 18cm, the printability tester hydraulic fluid to the printing roll (castor oil 80 wt% + benzyl alcohol 20 wt%) 0.5 ml was uniformly coated to resemble a thickness 4.8 .mu.m, the transfer nip width between the cylinder and the printing roll as 5mm by one rotation at a rotational speed 30 rpm, thereby transferring the hydraulic fluid to the sample. 次いで、転写後の紙試料の色差ΔE 2を転写前の紙試料のΔE 1と転写後の紙試料の色差ΔE 2とから(数3)にしたがってパンチ力ΔEを算出する。 Then calculated punch Delta] E color difference Delta] E 2 of the paper sample after transfer from the color difference Delta] E 2 Metropolitan paper sample after transcription and Delta] E 1 of the paper samples prior to transfer in accordance with equation (3).
【0022】 [0022]
【数2】 [Number 2]
ΔEn={(Lw−Lb) 2 +(Aw−Ab) 2 +(Bw−Bb) 2 } /2 ΔEn = {(Lw-Lb) 2 + (Aw-Ab) 2 + (Bw-Bb) 2} / 2
ただし、Lw:白色使用時の明度、Lb:黒色使用時の明度Aw:白色使用時の青〜黄色味、Ab:黒色使用時の青〜黄色味Bw:白色使用時の赤〜緑色味、Bb:黒色使用時の赤〜緑色味【0023】 However, Lw: white when using brightness, Lb: brightness at the time of the black use Aw: white use at the time of the blue to Yellowness, Ab: blue to at the time of the black use Yellowness Bw: white use at the time of the red to Ryokushokumi, Bb : red to Ryokushokumi [0023] at the time of the black use
【数3】 [Number 3]
ΔE=ΔE 1 +ΔE 2 ΔE = ΔE 1 + ΔE 2
ΔE:パンチ力一方、好適には、本願発明の化粧用紙に含有される上記例示の無機填料は、上記のように、タルク0.5〜90重量%とヒドロキシアパタイトとを含有するのが好ましい。 Delta] E: one punch, preferably, the above-exemplified inorganic filler contained in the decorative sheet of the present invention, as described above, preferably contains talc 0.5 to 90 wt% hydroxyapatite. 上記タルクは、平均粒子径が0.5〜8μmのタルクであり、好適には、平均粒子径0.5〜2μmの微粉タルクである。 The talc has an average particle diameter of talc 0.5 to 8 m, preferably a fine powder of talc having an average particle diameter of 0.5 to 2 [mu] m. タルクの平均粒子径は、既知のマイクロトラック法によって測定すればよい。 The average particle diameter of the talc can be measured by known micro track method. また、整粒された市販のタルク(日本タルク株式会社製、SG−2000)等を用いることもできる。 In addition, the sizing has been commercially available talc (Nippon Talc Co., Ltd., SG-2000) can also be used and the like. タルクを含有させることにより、紙の平滑度が向上し、肌触りが良くなり、使用感に優れた化粧用紙となる。 By containing talc, it improves the smoothness of the paper, touch is improved, the decorative sheet excellent in feeling of use.
【0024】 [0024]
かかる化粧用紙は、非常に肌触り感に優れ、かつ酸化皮脂の吸脂性にも優れ、さらに、一般的な化粧用紙、特に脂取り紙の機能である、皮脂を吸収した際に、その吸収部分の透明度が向上するという機能がより優れたものとなる。 Such decorative paper is excellent in touch feeling, and excellent oil absorption of oxidized sebum, further common cosmetic paper, in particular of oil-absorbing paper features, upon absorption of sebum, absorbent portion thereof feature called transparency of is improved becomes more excellent. よって、使用者は、吸脂効果を視覚的に確認でき、満足感が得られるようになる。 Thus, the user can visually can see the oil absorption effect, so that satisfaction is obtained.
【0025】 [0025]
また、本願発明の化粧用紙は、保湿剤やおしろい粉などを含有させることも可能である。 Further, the decorative sheet of the present invention, it is also possible to incorporate such moisturizer and face powder powder. 上記保湿剤としては、ホホバ油、グリセロール、1,3−ブチレングリコール、ヒアルロン酸、コラーゲン等の保湿機能をもった物質が挙げられる。 As the humectant, jojoba oil, glycerol, 1,3-butylene glycol, hyaluronic acid, moisturizing function with a substance such as collagen.
【0026】 [0026]
本願発明の化粧用紙は、着色剤を用いて着色することも可能である。 Cosmetic sheet of the present invention can also be colored with a colorant. 化粧用紙を着色すると、吸脂部分と非吸脂部分とのコントラストがはっきりして、より吸脂効果を視覚によって確認がしやすくなる。 When coloring the decorative paper, clear contrast between the oil absorption portion and the non-oil absorption portion, becomes easier to visually identify more oil absorption effect. 着色剤としては、塩基性染料、酸性染料、直接染料といった公知の染料および顔料を用いることが可能である。 As the colorant, it is possible to use a basic dye, acid dye, known dyes and pigments such as direct dyes. 顔料は、色の滲みが少なく、耐色性に優れている。 Pigment, color bleeding is small, has excellent color fastness. 染料は化粧紙が肌に直接触れるものであることから、食用染料が好ましい。 Since the dyes are those decorative paper is in direct contact with skin, edible dyes are preferred.
【0027】 [0027]
化粧用紙の柔軟性に関する要素として、本願発明者は、紙の坪量及び密度、柔軟剤の種類と添加量が特に重要であると考えるとともに、これらの3要素と、化粧用紙の軟らかさ、パンチ力、皮脂吸収作用及びふきとり適性との関係をみるために、12例の試料を作り、それぞれについて種々のテストを行って、表1のような結果を得た。 As an element relating to the flexibility of the decorative sheet, the present inventor has a basis weight of paper and density, together considered to be particularly the type and amount of softener important, and these three elements, the decorative paper softness, punch force, in order to see the relation between the sebum absorption and wiping suitability, making a sample of 12 patients, conducted various tests for each, to obtain a result shown in Table 1.
【0028】 [0028]
なお、本願発明の化粧用紙では柔軟剤として日新化学研究所 ネオソフターを使用する。 Incidentally, in the decorative sheet of the present invention to use Nisshinkagakukenkyusho Neosofuta as softener.
【0029】 [0029]
<評価基準> <Evaluation Criteria>
本願発明者が、化粧用紙の軟らかさ:紙パルプ技術協会が発行するJAPANTAPPI規格 T498による「ハンドルオメータ法」に基づき測定した。 The inventors of the present application, the softness of the decorative paper was measured on the basis of the due to JAPANTAPPI standard T498 to Technical Association of Pulp and Paper Industry issued "handle O meter method". パンチ力、吸脂量の測定:前段に記載したとおりである。 Punching power, oil absorption amount of measurement: are as described in the previous stage.
【0030】 [0030]
過酸化脂質の吸着率:次記のとおり測定した。 Adsorption rate of lipid peroxide was measured as follows: Symbol. まず、図1のように組立てた装置のカラム1に試料1gを入れ、n−ヘキサン4gで希釈したオリーブ油(和光純薬製)2gをカラム1の上部から流す。 First, the sample was placed 1g of the column 1 of the assembled apparatus shown in FIG. 1, n-hexane 4g olive oil was diluted with water (Wako Pure Chemical) passing 2g from the top of the column 1. このとき、カラム1内をオリーブ油が流れるように吸引しながら行う。 In this case, performed with suction through the column 1 to flow is olive oil. 次いで、カラム上部よりn−ヘキサン100mlを流して流出液を採取する。 Then, collecting the effluent by flowing n- hexane 100ml from the column top. 次いで、その流出液をウォーターバスで蒸発させ、残量約10mlになったところで、ウォータバスより取り出し、該混合液に氷酢酸10mlおよびヨウ化カリウム2gを添加して撹拌する。 Then evaporated and the effluent water bath, upon reaching a remaining amount of about 10ml, taken out from the water bath and stirred with the addition of glacial acetic acid 10ml and potassium iodide 2g to the mixture. 次いで、この混合液中の遊離したヨウ素を、ビュレットを用いて0.01mol/lチオ硫酸ナトリウムにて滴定する。 Then, the liberated iodine this mixed solution, and titrate with 0.01 mol / l sodium thiosulfate using burette. 終点はデンプン指示薬を入れ求める。 The end point is obtained put the starch indicator. 滴定結果より過酸化物価を求め、求められた過酸化物価より過酸化脂質の吸着量を算出する。 Seeking peroxide from titration results, it calculates the amount of adsorbed lipid peroxide from peroxide obtained.
【0031】 [0031]
【表1】 [Table 1]
【0032】 [0032]
表1に記載されている各試料について、柔軟性、パンチ力、吸脂量及びふきとり適性について測定したところ、試料NO. For each sample listed in Table 1, flexibility, punching power, it was measured for the oil absorption amount and wiping suitability, samples NO. 1〜12の各試料のうち、試料NO. Of each sample 1-12, samples NO. 1〜6の各試料は、柔らかさ、パンチ力、吸脂量、ふきとり適性とも目標とする数値又は結果が得られた。 Each sample of 1-6, softness, punch, oil absorption amount, the numerical or results to both wiping suitability target was obtained.
【0033】 [0033]
これに対して、表1に記載されている試料NO. In contrast, the samples are listed in Table 1 NO. 1〜12の各試料のうち、試料NO. Of each sample 1-12, samples NO. 7〜12の各試料は次のような理由で化粧用紙として不適格であった。 Each sample 7-12 was unsuitable as a cosmetic sheet for the following reasons.
【0034】 [0034]
すなわち、試料NO. That is, samples NO. 7の試料は、坪量を小さくしてみたものであるが(5g/m 2 )、使用時に撚れや破れが生じ、又吸脂量も1g/m 2に満たず、化粧用紙としては不適格であった。 7 samples, which is obtained tried to reduce the basis weight (5g / m 2), twisting and tear occurs during use, and the oil absorption amount not less than 1 g / m 2, as a cosmetic sheet not It was eligible.
【0035】 [0035]
試料NO. Sample NO. 8の試料は、試料NO. 8 of the sample, the sample NO. 7の試料とは逆に坪量を大きくしてみたものであるが(33g/m 2 )、必要な柔軟性が得られなかった。 Although the 7 samples in which tried to increase the basis weight in the reverse (33g / m 2), the necessary flexibility is not obtained.
【0036】 [0036]
次に、試料NO. Next, the sample NO. 9の試料は、柔軟剤の添加量を少なくしてみたものであるが、(0.05重量%)、必要な柔軟性に欠けるものであった。 9 samples, which is obtained tried to reduce the amount of softener were those lacking (0.05 wt%), the required flexibility.
【0037】 [0037]
試料NO. Sample NO. 10の試料は、密度を大きくしてみたものであるが(0.85g/cm 3 )、必要な吸脂量が得られなかった。 10 samples, which is obtained try increasing the density (0.85g / cm 3), oil absorption amount is not obtained required.
【0038】 [0038]
試料NO. Sample NO. 11の試料は、多量の柔軟剤を添加してみたものであるが(120重量%)、柔軟性は十分であったが、その逆作用として必要な吸脂量(1.0g/m 2 )とパンチ力が得られなかった。 11 samples, but which was tried by adding a large amount of softener (120 wt%), but the flexibility was sufficient, oil absorption amount required as an adverse (1.0 g / m 2) punch force can not be obtained with.
【0039】 [0039]
次に、試料NO. Next, the sample NO. 12の試料は、密度を小さくしてみたものであるが(0.30g/cm 3 )、必要な吸脂量(1g/m 2 )及びパンチ力が得られなかった。 12 samples, which is obtained tried to reduce the density (0.30g / cm 3), oil absorption amount required (1g / m 2) and the punch force is not obtained. 又、ふきとり適性の点でも良好な結果が得られなかった。 Also, good results in terms of wiping suitability can not be obtained.
【0040】 [0040]
以上の考察にもとずいて、本願発明者は、皮膚清拭用の化粧用紙として好適な数値として坪量の範囲を8〜30g/m 2とし、密度を0.40〜0.75g/cm 3とし、柔軟剤の添加量を繊維原料に対して0.1〜100重量%としたものである。 Te also DOO cerebrospinal above discussion, the present inventor has a range of basis weight as a suitable value as a cosmetic sheet for skin Qing拭用and 8~30g / m 2, a density 0.40~0.75g / cm 3 and then, in which the amount of softener was 0.1 wt% relative to the fiber material.
【0041】 [0041]
【実施例】 【Example】
<実施例1> <Example 1>
針葉樹パルプと広葉樹パルプとの混合パルプ(針葉樹パルプ/広葉樹パルプ:80/20)を原料とし叩解度500mlに調整し、平均粒子径1μmのタルク25重量パーセントおよび平均粒子径3μmのヒドロキシアパタイト5重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量15g/m 2の化粧用紙を得た。 Mixing pulp with softwood pulp and hardwood pulp (softwood pulp / hardwood pulp: 80/20) was adjusted to freeness 500ml as a raw material, talc having an average particle diameter of 1 [mu] m 25% by weight and hydroxyapatite with an average particle diameter of 3 [mu] m 5 wt% the pulp slurry was added to obtain a decorative sheet having a basis weight of 15 g / m 2 and paper making in known paper machine.
【0042】 [0042]
<実施例2> <Example 2>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:50/50)を原料とし叩解度500mlに調整し、平均粒子径3μmのタルク10重量パーセントおよび平均粒子径3μmのヒドロキシアパタイト10重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量15g/m 2の化粧用紙を得た。 Mixing pulp with softwood pulp and Manila hemp pulp (softwood pulp / Manila hemp pulp: 50/50) was adjusted to freeness 500ml as a raw material, talc having an average particle diameter of 3 [mu] m 10 wt% and the average hydroxyapatite particle size 3 [mu] m 10 wt% the pulp slurry was added to obtain a decorative sheet having a basis weight of 15 g / m 2 and paper making in known paper machine.
【0043】 [0043]
<実施例3> <Example 3>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:75/25)を原料とし叩解度500mlに調整し、平均粒子径1μmのタルク50重量パーセントおよび平均粒子径5μmのヒドロキシアパタイト20重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量20g/m 2の化粧用紙を得た。 Softwood pulp and Manila hemp pulp pulp mixed with (softwood pulp / Manila hemp pulp: 75/25) was adjusted to freeness 500ml as a raw material, talc having an average particle diameter of 1 [mu] m 50% by weight and hydroxyapatite with an average particle diameter of 5 [mu] m 20 wt% the pulp slurry was added to obtain a decorative sheet having a basis weight of 20 g / m 2 and paper making in known paper machine.
【0044】 [0044]
<実施例4> <Example 4>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:70/30)を原料とし叩解度500mlに調整し、平均粒子径3μmのタルク30重量パーセントおよび平均粒子径3μmのヒドロキシアパタイト50重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量15g/m 2の化粧用紙を得た。 Mixing pulp with softwood pulp and Manila hemp pulp (softwood pulp / Manila hemp pulp: 70/30) was adjusted to freeness 500ml as a raw material, talc having an average particle diameter of 3 [mu] m 30% by weight and hydroxyapatite 50 having an average particle diameter of 3 [mu] m wt% the pulp slurry was added to obtain a decorative sheet having a basis weight of 15 g / m 2 and paper making in known paper machine.
【0045】 [0045]
<実施例5> <Example 5>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:30/70)を原料とし叩解度500mlに調整し、平均粒子径1μmのタルク10重量パーセントおよび平均粒子径3μmのヒドロキシアパタイト50重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量30g/m 2の化粧用紙を得た。 Softwood pulp and Manila hemp pulp pulp mixed with (softwood pulp / Manila hemp pulp: 30/70) was adjusted to freeness 500ml as a raw material, talc having an average particle diameter of 1 [mu] m 10% by weight and hydroxyapatite 50 having an average particle diameter of 3μm wt% the pulp slurry was added to obtain a decorative sheet having a basis weight of 30 g / m 2 and paper making in known paper machine.
【0046】 [0046]
<実施例6> <Example 6>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:60/40)を原料とし叩解度500mlに調整し、平均粒子径1μmのタルク5重量パーセントおよび平均粒子径5μmのヒドロキシアパタイト5重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量8g/m 2の化粧用紙を得た。 Softwood pulp and Manila hemp pulp and mixed pulp (softwood pulp / Manila hemp pulp: 60/40) was adjusted to freeness 500ml as a raw material, hydroxyapatite talc 5% by weight and an average particle size 5μm average particle diameter of 1 [mu] m 5 wt% the pulp slurry was added to obtain a decorative sheet having a basis weight of 8 g / m 2 and paper making in known paper machine.
【0047】 [0047]
上記実施例1〜6の各化粧用紙における密度、柔軟剤添加量、軟らかさ、パンチ力、吸脂量、肌触り、ふきとり適性等は、表2に示す通りであり、それぞれ本願発明の要件を充足し、総合判定においても良好と認められた。 Density, softeners amount of each cosmetic sheets of Examples 1 to 6, softness, punch, oil absorption amount, texture, wipe suitability are as shown in Table 2, satisfy the requirements of the present invention, respectively , and it was recognized as the better in the overall judgment.
【0048】 [0048]
<比較例1> <Comparative Example 1>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:40/60)を原料とし叩解度500mlに調整し、平均粒子径10μmのタルク0.3重量パーセントおよび平均粒子径5μmのヒドロキシアパタイト5重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量5g/m 2の化粧用紙を得た。 Softwood pulp and Manila hemp pulp pulp mixed with (softwood pulp / Manila hemp pulp: 40/60) was adjusted to freeness 500ml as a raw material, hydroxyapatite talc 0.3% by weight and an average particle size 5μm average particle diameter of 10 [mu] m 5 the pulp slurry was added% by weight, to obtain a decorative sheet having a basis weight of 5 g / m 2 and paper making in known paper machine.
【0049】 [0049]
<比較例2> <Comparative Example 2>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:50/50)を原料とし叩解度500mlに調整し、平均粒子径5μmのタルク1重量パーセントおよび平均粒子径0.3μmのヒドロキシアパタイト0.5重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量33g/m 2の化粧用紙を得た。 Softwood pulp and Manila hemp pulp and mixed pulp (softwood pulp / Manila hemp pulp: 50/50) was adjusted to freeness 500ml as a raw material, hydroxyapatite talc 1% by weight and an average particle size 0.3μm in average particle diameter 5 [mu] m 0 the pulp slurry was added .5% by weight, to obtain a decorative sheet having a basis weight of 33 g / m 2 and paper making in known paper machine.
【0050】 [0050]
<比較例3> <Comparative Example 3>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:90/10)を原料とし叩解度500mlに調整し、平均粒子径0.3μmのタルク5重量パーセントおよび平均粒子径10μmのヒドロキシアパタイト30重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量15g/m 2の化粧用紙を得た。 Mixing pulp with softwood pulp and Manila hemp pulp (softwood pulp / Manila hemp pulp: 90/10) was adjusted to freeness 500ml as a raw material, the average hydroxyapatite Talc 5% by weight and an average particle size 10μm particle size 0.3 [mu] m 30 the pulp slurry was added% by weight, to obtain a decorative sheet having a basis weight of 15 g / m 2 and paper making in known paper machine.
【0051】 [0051]
<比較例4> <Comparative Example 4>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:40/60)を原料とし叩解度500mlに調整し、平均粒子径3μmのタルク150重量パーセントおよび平均粒子径3μmのヒドロキシアパタイト30重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量20g/m 2の化粧用紙を得た。 Mixing pulp with softwood pulp and Manila hemp pulp (softwood pulp / Manila hemp pulp: 40/60) was adjusted to a raw material freeness 500 ml, talc having an average particle diameter of 3 [mu] m 0.99% by weight and hydroxyapatite 30 with an average particle diameter of 3 [mu] m wt% the pulp slurry was added to obtain a decorative sheet having a basis weight of 20 g / m 2 and paper making in known paper machine.
【0052】 [0052]
<比較例5> <Comparative Example 5>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:70/30)を原料とし叩解度500mlに調整し、平均粒子径5μmのタルク10重量パーセントおよび平均粒子径3μmのヒドロキシアパタイト0.3重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量15g/m 2の化粧用紙を得た。 Softwood pulp and Manila hemp pulp and mixed pulp (softwood pulp / Manila hemp pulp: 70/30) was adjusted to freeness 500ml as a raw material, the average hydroxyapatite Talc 10% by weight and an average particle diameter 3μm particle size 5 [mu] m 0.3 the pulp slurry was added% by weight, to obtain a decorative sheet having a basis weight of 15 g / m 2 and paper making in known paper machine.
【0053】 [0053]
<比較例6> <Comparative Example 6>
針葉樹パルプとマニラ麻パルプとの混合パルプ(針葉樹パルプ/マニラ麻パルプ:50/50)を原料とし叩解度500mlに調整し、平均粒子径3μmのタルク100重量パーセントおよび平均粒子径3μmのヒドロキシアパタイト120重量パーセントを添加したパルプスラリーを、既知の抄紙機にて抄紙して坪量15g/m 2の化粧用紙を得た。 Mixing pulp with softwood pulp and Manila hemp pulp (softwood pulp / Manila hemp pulp: 50/50) was adjusted to freeness 500ml as a raw material, talc 100% by weight of the average particle diameter of 3μm and the average particle size 3μm hydroxyapatite 120 weight percent the pulp slurry was added to obtain a decorative sheet having a basis weight of 15 g / m 2 and paper making in known paper machine.
【0054】 [0054]
上記比較例1〜6の各化粧用紙における密度、柔軟剤添加量、軟らかさ、パンチ力、吸脂量、肌触り、ふきとり適性等は表2に示す通りであり、それらの各比較例のものは、いずれかの項目で本願発明の要件を充足せず、その結果、総合判定においても良好な評価を得られなかった。 Density of each decorative sheet of Comparative Example 1-6, softeners amount, softness, punch, oil absorption amount, texture, wipe suitability are as shown in Table 2, those of their respective comparative examples not meet the requirements of the present invention in any of the items, the result could not be obtained a good evaluation in the overall judgment.
【0055】 [0055]
【発明の効果】 【Effect of the invention】
以上の説明から明らかなように、本願発明の皮膚清拭用化粧用紙は、必要な皮脂吸収作用のほか、十分な柔軟性をそなえており、使用感のすぐれたものであり、しかも安価に製造し得る効果がある。 As apparent from the above description, the skin Kiyoshi 拭用 decorative sheet of the present invention, in addition to sebum absorption necessary, equipped with a sufficient flexibility, which has excellent feeling of use, inexpensively manufactured there is an effect that may be.
【0056】 [0056]
【表2】 [Table 2]
【0057】 [0057]
【図面の簡単な説明】 BRIEF DESCRIPTION OF THE DRAWINGS
【図1】過酸化脂質の吸着率の測定に用いた装置図である。 1 is a system diagram used to measure the adsorption rates of lipid peroxidation.
【符号の説明】 DESCRIPTION OF SYMBOLS
1・・・カラム。 1 ... column.

Claims (4)

  1. 繊維原料と、吸油性をもつ填料と、多価アルコール系からなる柔軟剤とを含み、 Includes a fiber material, a filler having an oil absorbing, and a softener consisting of polyhydric alcohol,
    前記填料がヒドロキシアパタイトおよびタルクであり、 The filler is hydroxyapatite and talc,
    JISP−8124による坪量が8〜30g/m 2であり、密度が0.40〜0.75g/cm 3であり、上記柔軟剤の添加量が上記繊維原料に対して0.1〜100重量%であり、 The basis weight by JISP-8124 is 8~30g / m 2, a density of 0.40~0.75g / cm 3, 0.1~100 weight amount of the softening agent relative to the fiber material % der is,
    JAPANTAPPI−T498「ハンドルオメーター法」による柔らかさが30mN未満、下記擬似吸脂量測定法による吸脂量が1g/m 以上であることを特徴とする皮膚清拭用化粧用紙。 JAPANTAPPI-T498 softness by 'handle O meter method "is less than 30 mN, skin Kiyoshi拭用decorative sheet, characterized in that it is oil absorption amount by the following pseudo-oil absorption amount measurement method is 1 g / m 2 or more.
    擬似吸脂量測定法 印刷適性試験機の胴の表面に21cm×25cmの試料片を粘着テープなどで固定して有効面積19cm×18cmとし、上記印刷適性試験機の印刷ロールに油液(ヒマシ油80重量%+ベンジルアルコール20重量%)0.5mlを膜厚4.8μmとなるように均一に塗布した上、上記胴と印刷ロールとのニップ幅を5mmとして転写回転速度30rpmで1回転させて、上記油液を上記試料に転写させる。 On the surface of the body of the pseudo oil absorption amount measurement method printability tester by fixing the sample piece of 21cm × 25 cm adhesive tape or the like as an active area 19cm × 18cm, hydraulic fluid (castor oil printing roll of the printability tester 80 wt% + benzyl alcohol 20% by weight) on which it is uniformly applied to the 0.5ml a thickness 4.8 .mu.m, by one rotation at the transfer speed 30rpm a nip width between the cylinder and the printing roll as 5mm , thereby transferring the hydraulic fluid to the sample. その後に、転写後の有効面積分の試料片の重量から転写前の有効面積分の紙の重量を差分した値(数1)に基づいて、試料1m2あたりの吸脂量とする。 Then, based on the value (number 1) obtained by subtracting the weight of the paper of the effective area fraction before transfer from the weight of the effective area fraction sample piece after transfer, the oil absorption amount per sample 1 m @ 2.
  2. 上記ヒドロキシアパタイトの含有量が上記繊維原料に対して1〜100重量%であることを特徴とする請求項1記載の皮膚清拭用化粧用紙。 Skin Kiyoshi拭用decorative sheet of claim 1, wherein the content of the hydroxyapatite is 1 to 100% by weight relative to the fiber material.
  3. 上記タルクの含有量が上記繊維原料に対して0.5〜90重量%であることを特徴とする請求項1又は2記載の皮膚清拭用化粧用紙。 Skin Kiyoshi拭用decorative sheet according to claim 1 or 2, wherein the content of the talc is 0.5 to 90% by weight relative to the fiber material.
  4. 上記ヒドロキシアパタイト及び/又はタルクの平均粒子径が0.5〜8μmであることを特徴とする請求項2又は3記載の皮膚清拭用化粧用紙。 Skin Kiyoshi 拭用 decorative sheet according to claim 2 or 3, wherein the average particle diameter of the hydroxy apatite and / or talc is 0.5 to 8 m.
JP2001140933A 2001-05-11 2001-05-11 Skin Kiyoshi 拭用 cosmetic paper Active JP4668456B2 (en)