JP2918296B2 - 自己消火性積層フィルム - Google Patents

自己消火性積層フィルム

Info

Publication number
JP2918296B2
JP2918296B2 JP2156101A JP15610190A JP2918296B2 JP 2918296 B2 JP2918296 B2 JP 2918296B2 JP 2156101 A JP2156101 A JP 2156101A JP 15610190 A JP15610190 A JP 15610190A JP 2918296 B2 JP2918296 B2 JP 2918296B2
Authority
JP
Japan
Prior art keywords
film
laminated film
extinguishing
self
flame
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
JP2156101A
Other languages
English (en)
Other versions
JPH0445928A (ja
Inventor
倫 堀
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sekisui Chemical Co Ltd
Original Assignee
Sekisui Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=15620335&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=JP2918296(B2) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Sekisui Chemical Co Ltd filed Critical Sekisui Chemical Co Ltd
Priority to JP2156101A priority Critical patent/JP2918296B2/ja
Priority to EP91109561A priority patent/EP0461612B1/en
Priority to DE69126236T priority patent/DE69126236T2/de
Priority to US07/714,955 priority patent/US5258226A/en
Publication of JPH0445928A publication Critical patent/JPH0445928A/ja
Application granted granted Critical
Publication of JP2918296B2 publication Critical patent/JP2918296B2/ja
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Description

【発明の詳細な説明】 （産業上の利用分野） 本発明は、炎の中では燃焼するが、火源から離される
と、直ちに自ら消火して燃え拡がることのない自己消火
性積層フィルムに関する。
（従来の技術） 従来、合成樹脂フィルムは、主として包装材料分野で
汎用されて来たが、最近では、電子精密機器、輸送機
器、建材等の分野で用いられるようになって来た。この
ような新規分野では、積層フィルムの難燃化が要求さ
れ、各種の研究が進められており、例えば、少なくとも
２枚のプラスチックフィルムの間に難燃剤を含有した接
着剤層を介在させてなる難燃性積層フィルムが提案され
ている（特開昭53-82887号公報参照）。この技術によれ
ば、多量の難燃剤による接着剤層の接着性の低下を招く
ので、これを防ぐ為に、接着剤層に含有させる難燃剤と
して接着剤に不溶解で、且つ平均粒径が接着剤層厚みの
80％以下の粉体状難燃剤を接着剤100重量部に対し60〜4
00重量部の範囲で添加すると共に、接着剤層の厚みが２
枚のプラスチックフィルムの総厚みに対し20％乃至同一
厚みの範囲とすることも提案されている（特開昭62-240
545号公報参照）。
（発明が解決しようとする課題） しかしながら、前記難燃性積層フィルムに於いては、
何れも、難燃性を付与する為には、多量の難燃剤を含有
させねばならず、然も、該難燃剤は、ハロゲン、燐、硫
黄、アンチモン等の元素を主体とする故に、焼却すると
有害気体を発生し、大気汚染の元凶となり、又、一方で
は燃焼炉の腐食や水質汚染をも惹起するという問題点が
あった。
（課題を解決するための手段） 本発明自己消火性積層フィルムは、上記従来の問題点
を解決する為になされたものであって、２枚以上の合成
樹脂フィルムからなる積層フィルムであって、このう
ち、少なくとも１枚のフィルムは、メルトフローレート
が20（g/10分）以上で、且つ難燃剤を含有する熱可塑性
樹脂製フィルムからなることを特徴とする自己消火性積
層フィルムをその要旨とするものである。
即ち、本発明では、自己消火性積層フィルムを形成す
るフィルムの一として、少量の難燃剤を含有すると共
に、熱によって極めて融け易い特定の熱可塑性樹脂から
なるフィルム（以下「特定のフィルム」という）を採用
することによって、万一火炎に曝されても、逸速くこの
特定のフィルムのみが先に溶融落下し、残りのフィルム
への延焼率を低く抑えることが出来、溶融落下した樹脂
自体も自己消火性を有するので、結局火炎は拡大しない
という従来には見られなかった全く新しい難燃機溝に基
くものである。
但、溶融指数の高い（溶融流れ性のよい）樹脂からな
るフィルムは、一般に機械的強度に乏しく、これ自体で
は所期の物性が得られないので、通常の汎用樹脂からな
るフィルムからなるフィルムと積層することによって、
強度物性と難燃性とを兼備したものとするのである。
本発明で用いられる難燃剤としては、一般的なハロゲ
ン、燐、硫黄を含む有機系難燃剤、金属水酸化物、重炭
酸ナトリウム等の無機系難燃剤が使用可能であるが、そ
の使用量は、前述の通り特定のフィルムのみで済むの
で、フィルムに塗布乃至含有したり、２枚のフィルム間
に介在させる接着剤中に練込んだりする従来一般に使用
される難燃性フィルムでの使用量の半分以下で充分であ
る。
本発明で用いられる特定のフィルムを構成する樹脂と
しては、ポリオレフィン系もしくはポリアミド系樹脂が
好適に用いられ、ポリオレフィン系樹脂としては、ポリ
エチレン、エチレン−酢酸ビニル共重合体、エチレン−
エチルアクリレート共重合体等のエチレン共重合体、ポ
リプロピレン、プロピレンと他のモノマーとの共重合
体、低分子量ポリエチレン、低分子量ポリプロピレン等
が挙げられる。
一方、ポリアミド系樹脂としては、ナイロン６、ナイ
ロン６−６、ナイロン６−10、ナイロン11、ナイロン12
及びこれらの共重合物等が、好適に使用される。尚、こ
れらの樹脂には、高級アルコール、ヒドロキシ安息香酸
エステル等の可塑剤が含まれていてもよい。
何れにしても、特定のフィルムとして用いる樹脂の種
類としては、上記ポリオレフィン系樹脂、ポリアミド系
樹脂のみに限定されない。
又、前記特定のフィルムを構成する樹脂には、必要に
応じて、充填剤、顔料、抗酸化剤等を添加してもよい。
本発明で用いられる特定のフィルムを構成する樹脂
は、そのメルトフローレートが20（g/10分）以上のもの
でなければならず、かかる樹脂は比較的分子量の低いも
のから得られるのであって、20に満たない場合は溶融落
下し難く、又、溶融落下するとしても、その前に他の積
層フィルムに燃え移る危険性があり、所期の機能を発揮
し得ない。
本発明でいうメルトフローレートとは、JIS K 7210
「熱可塑性プラスチックの流れ試験方法」で測定される
値をいい、ポリエチレン系樹脂にあっては、条件４（試
験温度190℃、試験荷重2.16kg/f）、ポリプロピレン系
樹脂及びポリアミド系樹脂にあっては、条件14（試験温
度230℃、試験荷重2.16kg/f）での測定値である。
又、この難燃剤を含有するフィルムは、積層フィルム
全体に対し重量比で50％以上になるよう構成されている
のが好ましく、これに満たない場合は、所期の効果が得
られない場合がある。
本発明で用いられる前記特定のフィルム以外のフィル
ムを構成する樹脂としては、ポリエチレン、エチレン−
酢酸ビニル共重合体、ポリプロピレン、ポリエチレンテ
レフタレート等のポリエステル、ポリアミド等が、好適
に使用され、好ましくは、特定のフィルムと同系統のも
のを選択するのがよい。
本発明自己消火性積層フィルムに於ける特定のフィル
ムは、それ以外のフィルムの片面もしくは両面の何れに
積層されていてもよく、又、２枚の熱可塑性樹脂フィル
ムの間に介在せしめられていてもよい。又、特定のフィ
ルムを、熱可塑性樹脂フィルムに積層する方法として
は、押出コーティング、ホットメルトコーティング、溶
液コーティング等の公知の方法が使用される。
（作用） 本発明白已消火性積層フィルムは、２枚以上の合成樹
脂フィルムからなる積層フィルムであって、このうち、
少なくとも１枚のフィルムは、メルトフローレートが20
（g/10分）以上で、且つ難燃剤を含有する熱可塑性樹脂
製フィルムからなるので、着火した場合には、火炎が拡
大乃至延焼する前に、特定のフィルムが溶出して滴下
し、火源から離れると直ちに消火する。
（実施例） 以下、本発明の実施例を具体的に説明するが、本発明
は実施例に限定されるものではない。
実施例１ エチレン−酢酸ビニル共重合体（商品名「ウルトラセ
ン720」東ソー社製、メルトフローレート150、酢酸ビニ
ル含量28％）95重量部と、難燃剤（商品名「AFR1002」
旭硝子社製、臭素含量66％）５重量部とを、120℃の熱
ロールにより５分間混練して特定のフィルムを構成する
材料を調製した後、厚み20μの２枚の直鎖状低密度ポリ
エチレンフィルムに挟んで、200μのスペーサーを入れ
た120℃のプレス機で熱プレスして、厚みが200μの本発
明積層フィルムを得た。
得られた積層フィルムを、幅20cmのテープ状に切断し
て試験片とし、垂直に垂下して着火試験を行った。
結果は、火源から離すと直ちに消火し、自己消火性を
示した。
実施例２ エチレン−酢酸ビニル共重合体として（商品名「ウル
トラセン530」東ソ−社製、メルトフローレート75、酢
酸ビニル含量６％）を用いたこと以外は実施例１と同様
にして、厚みが200μの本発明積層フィルムを得、着火
試験を行った。
結果は、火源から離すと直ちに消火し、自己消火性を
示した。
比較例１ エチレン−酢酸ビニル共重合体として（商品名「ウル
トラセン541」東ソー社製、メルトフローレート９、酢
酸ビニル含量10％）を用いたこと以外は実施例１と同様
にして、厚みが200μの積層フィルムを得、着火試験を
行った。
結果は、火源から離した後も、滴下しながら最後迄燃
え続けた。
比較例２ エチレン−酢酸ビニル共重合体として（商品名「ウル
トラセン631」東ソー社製、メルトフローレート1.5、酢
酸ビニル含量20％）を用いたこと以外は実施例１と同様
にして、厚みが200μの積層フィルムを得、着火試験を
行った。
結果は、火源から離した後も、滴下しながら最後迄燃
え続けた。
実施例３ 低分子量ポリプロピレン（商品名「ビスコール330−
Ｐ」三洋化成工業社製、メルトフローレート500以上）7
0重量部と、エチレン−酢酸ビニル共重合体（商品名
「ウルトラセン720」東ソー社製、メルトフローレート1
50、酢酸ビニル含量28％）30重量部に、燐酸グァニジン
（商品名「アピノン301」三和ケミカル社製）10重量部
を160℃で加熱混合した後、厚み30μのポリプロピレン
フィルムの片面に、ホットメルトコーターにより、100
μの厚みにコーティングして、厚みが130μの本発明積
層フィルムを得た。
得られた積層フィルムを幅20cmのテープ状に切断して
試験片とし、垂直に垂下して着火試験を行った。
結果は、火源から離すと直ちに消火し、自己消火性を
示した。
実施例４ エチレン−酢酸ビニル共重合体（商品名「ウルトラセ
ン681」東ソー社製、メルトフローレート350、酢酸ビニ
ル含量20％）45重量部に、塩素化ポリエチレン（商品名
「エラスレン301−Ａ」昭和電工社製）５重量部と、ト
ルエン50重量部を混合した後、厚み15μのポリエチレン
テレフタレートフィルムの片面に、ロールコーティング
により、200μの厚みにコーティングし、その上面から
厚み20μの低密度ポリエチレンフィルムを圧着し、100
℃の熱ロールによりプレスして、厚みが235μの積層フ
ィルムを得た。
得られた積層フィルムを幅20cmのテープ状に切断して
試験片とし、垂直に垂下して着火試験を行った。
結果は、火源から離すと直ちに消火し、自己消火性を
示した。
（発明の効果） 本発明の自己消火性積層フィルムは、叙上の通りの構
成とされているので、難燃剤の含有量が少量で済み、廃
薬物の処理が容易であり、自動車内装材、電気用、建築
用、輸送梱包用に使用して好適なものである。

Claims (1)

    (57)【特許請求の範囲】
  1. 【請求項１】２枚以上の合成樹脂フィルムからなる積層
    フィルムであって、このうち、少なくとも１枚のフィル
    ムは、メルトフローレートが20（g/10分）以上で、且つ
    難燃剤を含有する熱可塑性樹脂製フィルムからなること
    を特徴とする自己消火性積層フィルム。
JP2156101A 1990-06-14 1990-06-14 自己消火性積層フィルム Expired - Lifetime JP2918296B2 (ja)