JP2021059625A - スチールコード接着用ゴム組成物及びコンベヤベルト - Google Patents
スチールコード接着用ゴム組成物及びコンベヤベルト Download PDFInfo
- Publication number
- JP2021059625A JP2021059625A JP2019182750A JP2019182750A JP2021059625A JP 2021059625 A JP2021059625 A JP 2021059625A JP 2019182750 A JP2019182750 A JP 2019182750A JP 2019182750 A JP2019182750 A JP 2019182750A JP 2021059625 A JP2021059625 A JP 2021059625A
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- mass
- vulcanization accelerator
- present
- steel cord
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
例えば、特許文献1には、硫黄加硫可能なゴム100重量部に対して、ロジンまたはロジン誘導体を3〜15重量部と、有機コバルト塩をコバルト量として0.2〜1.0重量部と、有機塩素化合物を3〜50重量部とを含有するゴム組成物と、亜鉛メッキスチールコードとを接着する、亜鉛メッキスチールコードとゴムとの接着方法等が記載されている。
そこで、本発明は、耐水接着性に優れる、スチールコード接着用ゴム組成物を提供することを目的とする。なお、本発明において耐水接着性は耐湿接着性を含むものとする。
また、本発明は、耐水接着性に優れるコンベヤベルトを提供することも目的とする。
本発明は上記知見等に基づくものであり、具体的には以下の構成により上記課題を解決するものである。
ホウ素を含む有機酸コバルト塩と、
硫黄とを含有し、
加硫促進剤の含有量が、上記ゴム成分100質量部に対して、0.0〜2.0質量部であり、
下記式(X)の値が0.09〜1.32である、スチールコード接着用ゴム組成物。
式(X)=A+B/C
式(X)において、Aは、上記加硫促進剤の含有量であり、
Bは、上記ゴム成分100質量部に対する上記有機酸コバルト塩中のコバルトの含有量であり、
Cは、上記ゴム成分100質量部に対する上記硫黄の含有量である。
[2] 上記有機酸コバルト塩が、ネオデカン酸ホウ酸コバルトである、[1]に記載のスチールコード接着用ゴム組成物。
[3] 上記加硫促進剤を含有し、上記加硫促進剤が、チアゾール系加硫促進剤である、[1]又は[2]に記載のスチールコード接着用ゴム組成物。
[4] 上記加硫促進剤を含有し、上記加硫促進剤が、ベンゾチアゾリルポリスルフィド系化合物である、[1]〜[3]のいずれかに記載のスチールコード接着用ゴム組成物。
[5] 上記加硫促進剤を含有しない、[1]又は[2]に記載のスチールコード接着用ゴム組成物。
[6] 亜鉛メッキスチールコードを接着させるために使用される、[1]〜[5]のいずれかに記載のスチールコード接着用ゴム組成物。
[7] [1]〜[6]のいずれかに記載のスチールコード接着用ゴム組成物を用いて形成されたコンベヤベルト。
また、本発明のコンベヤベルトは、耐水接着性に優れる。
なお、本明細書において「〜」を用いて表される数値範囲は、「〜」の前後に記載される数値を下限値および上限値として含む範囲を意味する。
本明細書において、特に断りのない限り、各成分はその成分に該当する物質をそれぞれ単独でまたは2種以上を組み合わせて使用することができる。成分が2種以上の物質を含む場合、成分の含有量は、2種以上の物質の合計の含有量を意味する。
本明細書において、特に断りのない限り、各成分はその製造方法について特に制限されない。例えば、従来公知の方法が挙げられる。
本明細書において、耐水接着性がより優れることを、本発明の効果がより優れるということがある。
本発明のスチールコード接着用ゴム組成物(本発明の組成物)は、
ジエン系ゴムを少なくとも含むゴム成分と、
ホウ素を含む有機酸コバルト塩と、
硫黄とを含有し、
加硫促進剤の含有量が、上記ゴム成分100質量部に対して、0.0〜2.0質量部であり、
下記式(X)の値が0.09〜1.32である、スチールコード接着用ゴム組成物である。
式(X)=A+B/C
式(X)において、Aは、上記加硫促進剤の含有量であり、
Bは、上記ゴム成分100質量部に対する上記有機酸コバルト塩中のコバルトの含有量であり、
Cは、上記ゴム成分100質量部に対する上記硫黄の含有量である。
ゴム組成物がジエン系ゴム、有機酸コバルト塩及び硫黄を含有し、加硫促進剤を含有しない、又は、加硫促進剤の含有量が少ない場合、有機酸コバルト塩が硫黄によるジエン系ゴムの加硫における加硫促進剤として機能しうると本発明者は考える。
一方、スチールコードとジエン系ゴムとの接着を向上させるためには、硫黄及び有機酸コバルト塩の含有量を増やすことが考えられる。
しかし、ゴム組成物がジエン系ゴム、有機酸コバルト塩及び硫黄を含有し、加硫促進剤を含有しない、又は、加硫促進剤の含有量が少ない場合において、耐水接着性を向上させるために、硫黄に対する有機酸コバルト塩の含有量の比率には最適な範囲があることを本発明者は知見した。
上記知見をもとに、本発明者は、上記式(X)の値が特定の範囲であるときに、耐水接着性が向上することを見出した。
以下、本発明の組成物に含有される各成分について詳述する。
本発明の組成物は、ジエン系ゴムを少なくとも含むゴム成分を含有する。
本発明の組成物に含有されるジエン系ゴムは、ジエン系モノマーを重合して得られるポリマーであれば特に制限されない。
ジエン系ゴムとしては、例えば、天然ゴム、イソプレンゴム(IR)、芳香族ビニル−共役ジエン共重合体ゴム(例えばスチレンブタジエン共重合体ゴム)、アクリロニトリルブタジエンゴム(NBR)、ブチルゴム(IIR)、ハロゲン化ブチルゴム、クロロプレンゴム(CR)が挙げられる。
上記天然ゴム(NR)は特に制限されない。例えば、従来公知のものが挙げられる。
上記イソプレンゴムはイソプレンのホモポリマーであれば特に制限されない。例えば、従来公知のものが挙げられる。
上記スチレンブタジエン共重合体ゴムは、スチレンとブタジエンとの共重合体であれば特に制限されない。
上記スチレンブタジエン共重合体ゴムの結合スチレン量は、本発明の効果により優れ、後述する上記スチレンブタジエン共重合体ゴムのガラス転移温度が低くなるという観点から、上記スチレンブタジエン共重合体ゴム全量に対して、5〜40質量%であることが好ましく、10〜30質量%がより好ましい。
上記スチレンブタジエン共重合体ゴムのブタジエンによるビニル量(1,2−ビニル結合量)は、本発明の効果により優れ、後述する上記スチレンブタジエン共重合体ゴムのガラス転移温度が低くなるという観点から、スチレンブタジエン共重合体ゴムが有するブタジエンによる繰り返し単位の総量に対して、5〜30質量%であることが好ましく、5〜20質量%がより好ましい。
本発明において、上記スチレンブタジエン共重合体ゴムが有する、上記結合スチレン量と上記ビニル量は、1H−NMRで測定することができる。
スチレンブタジエン共重合体ゴムの重量平均分子量は特に制限されない。例えば、20万〜300万とできる。
本発明において、スチレンブタジエン共重合体ゴムの重量平均分子量は、テトラヒドロフランを溶媒とするゲルパーミエーションクロマトグラフィー(GPC)による測定値をもとにした標準ポリスチレン換算値である。
上記スチレンブタジエン共重合体ゴムは、その製造方法について特に制限されない。例えば、溶液重合によるスチレンブタジエン共重合体ゴム(S−SBR)、乳化重合によるスチレンブタジエン共重合体ゴム(E−SBR)が挙げられる。なかでも、上記スチレンブタジエン共重合体ゴムは、本発明の効果により優れるという観点から、S−SBRを含むことが好ましい。
上記ジエン系ゴムの含有量は、上記ゴム成分100質量部に対して、70〜100質量部が好ましい。
上記ゴム成分が、上記天然ゴム及び上記スチレンブタジエン共重合体ゴムを含む場合、上記天然ゴムの含有量は、本発明の効果により優れるという観点から、上記ゴム成分100質量部に対して、20〜80質量部が好ましく、30〜70質量部がより好ましく、40〜60質量部が更に好ましい。
上記スチレンブタジエン共重合体ゴムの含有量は、上記ゴム成分100質量部から上記天然ゴムの含有量を除いた量とできる。
上記ジエン系ゴムの重量平均分子量は、10万以上であればよい。
本発明において、上記ジエン系ゴムの重量平均分子量は、テトラヒドロフランを溶媒とするゲルパーミエーションクロマトグラフィー(GPC)による測定値をもとにした標準ポリスチレン換算値とすることができる。
本発明の組成物に含有されるホウ素を含む有機酸コバルト塩は、ホウ素を含み、有機酸とコバルトで形成される塩であれば特に制限されない。
上記有機酸コバルト塩を構成する有機酸としては、例えば、カルボキシ基を有する化合物が挙げられる。上記カルボキシ基は有機基に結合することができる。上記有機基は特に制限されない。例えば、炭化水素基が挙げられる。上記炭化水素基としては、例えば、脂肪族炭化水素基、芳香族炭化水素基、これらの組合せが挙げられる。
上記脂肪族炭化水素基は、直鎖状、分岐状、環状、これらの組合せが挙げられる。脂肪族炭化水素基は不飽和結合を有してもよい。
上記有機酸コバルト塩を形成する有機酸がカルボキシ基を有する化合物である場合、上記有機酸コバルト塩が有するカルボキシイオン(−COO-)は、上記有機酸のカルボキシ基に由来することができる。
上記有機酸コバルト塩において、上記カルボキシイオンのような、(酸による)アニオンの対イオンは、有機酸コバルト塩が有するコバルトイオン(例えば、Co2+、Co3+)である。
上記有機酸コバルト塩としては、具体的には例えば、下記式(1)で表されるネオデカン酸ホウ酸コバルトのようなコバルトボロン錯体などが挙げられる。
本発明の組成物は硫黄を含有する。上記硫黄は特に制限されない。例えば、硫黄単体が挙げられる。
本発明の組成物において、上記ゴム成分100質量部に対する、加硫促進剤の含有量は0.0〜2.0質量部である。
本発明の組成物における加硫促進剤は、硫黄による加硫が可能なゴム組成物に使用され得る加硫促進剤であれば特に制限されない。
上記加硫促進剤としては、例えば、アルデヒド−アンモニア系、アルデヒド−アミン系、チオウレア系、グアニジン系、チアゾール系、スルフェンアミド系、チウラム系、ジチオカルバミン酸塩系、キサントゲン酸塩系、これらの混合物が挙げられる。
なお、一般的にチアゾール系以外の加硫促進剤に分類されている加硫促進剤がチアゾール骨格を有する場合、本明細書において、上記のような加硫促進剤を、チアゾール系加硫促進剤に分類するものとする。
チアゾール系加硫促進剤は、チアゾール骨格を有する加硫促進剤であれば特に制限されない。チアゾール系加硫促進剤としては、例えば、ベンゾチアゾール骨格を有するベンゾチアゾール系加硫促進剤が挙げられる。
上記ベンゾチアゾール系加硫促進剤としては、例えば、ベンゾチアゾリルスルフィド基を有する加硫促進剤が挙げられる。
本発明の組成物における加硫促進剤の含有量が上記ゴム成分100質量部に対して0.0質量部を超え2.0質量部以下である場合(つまり本発明の組成物が加硫促進剤を上記含有量で含有する場合)、上記加硫促進剤は、耐水接着性により優れるという観点から、チアゾール系加硫促進剤が好ましく、ベンゾチアゾリルポリスルフィド系化合物がより好ましく、2−メルカプトベンゾチアゾール、ジ−2−ベンゾチアゾリルジスルフィド、及び2−メルカプトベンゾチアゾールの亜鉛塩からなる群から選ばれる少なくとも1種が更に好ましい。
本発明の組成物において、下記式(X)の値は0.09〜1.32である。
式(X)=A+B/C
式(X)において、Aは、上記ゴム成分100質量部に対する上記加硫促進剤の含有量であり、
Bは、上記ゴム成分100質量部に対する上記ホウ素を含む有機酸コバルト塩中のコバルトの含有量であり、
Cは、上記ゴム成分100質量部に対する上記硫黄の含有量である。
式(X)の値が上記の特定範囲を満たすことよって、本発明の組成物は耐水接着性に優れる。
本発明の組成物における加硫促進剤の含有量は、上記ゴム成分100質量部に対して、0.0〜2.0質量部である。
本発明の組成物における加硫促進剤の含有量は、耐水接着性により優れるという観点から、上記ゴム成分100質量部に対して、0〜1.5質量部が好ましく、0〜0.7質量部がより好ましい。
本発明の組成物に含有される、ホウ素を含む有機酸コバルト塩中のコバルトの含有量は、上記ゴム成分100質量部に対して、0.22〜1.22質量部であることが好ましく、0.27〜0.78質量部であることがより好ましい。
本発明の組成物に含有される硫黄の含有量は、本発明の効果により優れ、耐久性に優れるという観点から、上記ゴム成分100質量部に対して、2.1〜8.0質量部であることが好ましく、3.5〜5.0質量部がより好ましい。
本発明の組成物は、変性基を有してもよい液状ポリイソプレン、ロジン類、フェノール樹脂及び塩素化パラフィンからなる群から選ばれる少なくとも1種の化合物Aを更に含有することが好ましい。
本発明の組成物は化合物Aを更に含有することによって耐水接着性により優れる。
化合物Aとしての、変性基を有してもよい液状ポリイソプレンは、変性基を有してもよく、室温(23℃)条件下において液状である、イソプレンによる繰り返し単位を有するポリマーである。
変性基を有してもよい液状ポリイソプレンの骨格は、単独重合体、共重合体のいずれであってもよい。
変性基を有してもよい液状ポリイソプレンの骨格としては、例えば、イソプレンの単独重合体;スチレン−イソプレン共重合体、ブタジエン−イソプレン共重合体のような共重合体が挙げられる。
液状ポリイソプレンが変性基を有する場合としては、例えば、上記骨格が上記変性基によって変性されていてもよい。また、変性基を有する液状ポリイソプレンとしては、例えば、イソプレンと上記変性基を導入しうるモノマーとを少なくとも含む単量体を共重合させた共重合体が挙げられる。
上記変性基としては、例えば、カルボキシ基、ヒドロキシ基、酸無水物基が挙げられる。
なかでも、本発明の効果により優れ、耐久性に優れるという観点から、カルボキシ基、酸無水物基が好ましい。
上記変性基は、上記骨格と直接又は有機基を介して結合できる。上記有機基は特に制限されない。
本発明において、上記液状ポリイソプレンの重量平均分子量は、テトラヒドロフランを溶媒とするゲルパーミエーションクロマトグラフィー(GPC)による測定値をもとにした標準ポリスチレン換算値である。
フェノール樹脂としては、一般にゴム組成物に配合可能なものを使用できる。上記フェノール樹脂は、フェノール類とアルデヒドとの反応によって得られる樹脂及びその変性物を含むことができる。フェノール類としては、例えばフェノール、クレゾール、キシレノールまたはレゾルシン等を例示することができる。また、アルデヒドとしては、例えばホルムアルデヒド、アセトアルデヒドまたはフルフラール等を例示することができる。
なお、本発明の組成物は、フェノール樹脂の硬化剤を含有しないことが好ましい態様の1つとして挙げられる。
本発明の組成物は、ロジン類を更に含有することができる。
ロジン類としては、例えば、ロジン、ロジン誘導体が挙げられる。
ロジンは、一般的に、松脂を蒸留等して得られる天然樹脂である。
ロジンを上記のように製造上の観点から例示すると、ロジンとしては、例えば、ガムロジン、ウッドロジン、トールロジンが挙げられる。
上記ロジンは、本発明の効果により優れるという観点から、(ガムロジン、ウッドロジン、トールロジンのなかでは)ガムロジンが好ましい。
樹脂酸としては、例えば、アビエチン酸、ネオアビエチン酸、パラストリン酸、ピマール酸、イソピマール酸、デヒドロアビエチン酸が挙げられる。
上記各種の樹脂酸は、官能基としてカルボキシ基を有する点で共通する。
なお、上記ガムロジン等のロジンの種類によって、一般的に、上記樹脂酸の構成の比率が異なる。
ロジン誘導体(ロジンの変性体)しては、例えば、上記樹脂酸を、酸変性、(二重結合の)不均化、水素化、二量化、又はエステル化した化合物が挙げられる。
上記ロジン類の軟化点は、本発明の効果により優れるという観点から、40〜130℃であることが好ましく、50〜100℃がより好ましい。
ロジン類の軟化点は、JIS K5902−1969に準じて測定することができる。
上記ロジン類の酸価は、50mgKOH/g以上とすることができる。
上記ロジン類の酸価は、本発明の効果により優れるという観点から、50〜200mgKOH/gであることが好ましく、80〜180mgKOH/gがより好ましい。
ロジン類の酸価は、JIS K2501:2003に準じて測定することができる。
上記ロジン類の分子量は、本発明の効果により優れるという観点から、200〜1000であることが好ましく、250〜400がより好ましい。
ロジン類の分子量は、ゲルパーミエーションクロマトグラフィー(GPC)で測定することができる。
なおロジン類は一般的に混合物であるため、上記ロジン類の分子量は平均値であってもよい。
上記塩素化パラフィンは、塩素を有するパラフィンであれば特に制限されない。例えば、平均で炭素数26の鎖状飽和炭化水素化合物であって、該化合物中の水素原子の全部又は一部が塩素原子で置換されているものが挙げられる。
上記塩素化パラフィンが有する塩素量は、塩素化パラフィン全量に対して、例えば、40〜80質量%が好ましい。
変性基を有してもよい液状ポリイソプレンを少なくとも含むことが好ましく、
変性基を有してもよい液状ポリイソプレンと、
ロジン類、フェノール樹脂及び塩素化パラフィンからなる群から選ばれる少なくとも1種の化合物Bとを含むことがより好ましく、
変性基を有してもよい液状ポリイソプレンと、
ロジン類と、
フェノール樹脂と、
塩素化パラフィンとを含むことが更に好ましい。
本発明の組成物は、更に、カーボンブラックを含有することができる。
上記カーボンブラックは特に制限されない。
なかでも、上記カーボンブラックは、本発明の効果により優れるという観点から、HAF級カーボンブラック、ISAF級カーボンブラックが好ましく、HAF級カーボンブラックがより好ましい。
上記カーボンブラックの窒素吸着比表面積(N2SA)は、本発明の効果により優れるという観点から、60〜120m2/gが好ましく、65〜95m2/gがより好ましい。
カーボンブラックの窒素吸着比表面積は、カーボンブラック表面への窒素吸着量をJIS K 6217−2:2017「第2部:比表面積の求め方−窒素吸着法−単点法」にしたがって測定できる。
上記カーボンブラックの含有量は、本発明の効果により優れるという観点から、上記ゴム成分100質量部に対して、35〜75質量部であることが好ましく、40〜70質量部がより好ましい。
本発明の組成物は、更に、老化防止剤を含有することができる。
老化防止剤は特に制限されない。例えば従来公知の老化防止剤が挙げられる。
上記老化防止剤の含有量の上限は、上記ゴム成分100質量部に対して、5.0質量部以下とできる。
本発明の組成物は更に酸化亜鉛を含有することができる。上記酸化亜鉛は特に制限されない。
上記酸化亜鉛の含有量は、本発明の効果により優れるという観点から、上記ゴム成分100質量部に対して、5.0質量部以上であることが好ましい。
上記酸化亜鉛の含有量の上限は、上記ゴム成分100質量部に対して、20質量部以下とできる。
本発明の組成物をスチールコード(例えば亜鉛メッキスチールコード)とともに用いて、例えば加硫することによって、加硫ゴムとスチールコードとを有する複合体を得ることができる。上記複合体において加硫ゴムとスチールコードとは接着することができる。
上記スチールコードは、本発明の効果により優れ、防錆性に優れるという観点から、亜鉛メッキされたものが好ましい。
上記スチールコード(亜鉛メッキされたスチールコードを含む。以下同様)の例えば素線径又はコード径などは、適宜選択できる。上記スチールコードは、その表面が未処理のものであってもよい。
タイゴムとしては、例えば、コンベヤベルトを例えば端部で接続しうるゴムが挙げられる。タイゴムによる接続によってコンベヤベルトを、長く及び/又はエンドレス化することができる。
次に、本発明のコンベヤベルトについて以下に説明する。
本発明のコンベヤベルトは、本発明のスチールコード接着用ゴム組成物を用いて形成されたコンベヤベルトである。
本発明の組成物は、本発明の効果により優れるという観点から、スチールコードをコートするコートゴム層(例えばクッションゴム及び/又はタイゴム)を形成することが好ましい。
本発明のコンベヤベルトは、更に、カバーゴム層を有することが好ましい態様の1つとして挙げられる。上記カバーゴム層を形成しうるゴム組成物は特に制限されない。
図1は本発明のコンベヤベルトの一例を模式的に表す断面斜視図である。
図1において、コンベヤベルト1は、両表面にカバーゴム層6を有し、カバーゴム層6の間に、スチールコード2とコートゴム層4を有する。コートゴム層4はスチールコード2をコートする。コートゴム層4は本発明のスチールコード接着用ゴム組成物で形成されることが好ましい。
下記第1表の各成分を同表に示す組成(質量部)で用いた。
まず、下記第1表に示す成分のうち硫黄および加硫促進剤を除く成分を、バンバリーミキサーで混合し、次に、得られた混合物に硫黄(および加硫促進剤を含有させる場合は加硫促進剤)を第1表に示す量で加えてこれらをロールを用いて混合して、各組成物を製造した。
上記のとおり製造された各組成物を用いて以下の評価を行った。結果を第1表に示す。
耐水接着性を引抜力で評価した。
・評価方法
デシケータ中に保管して防塵防湿処理を施してある直径4.1mmの亜鉛メッキスチールコードに、上記のとおり製造された各組成物を15mmの厚さに付与して、各組成物とスチールコードとの複合体(スチールコードは組成物中に埋まっている状態)とし、上記複合体をプレス成型機を用いて153℃、面圧2.0MPaの条件下で20分間加圧加硫して、試験体(ゴム/亜鉛メッキスチールコード複合体)を作製した。上記試験体において、ゴム表面からスチールコードが突出している箇所のゴムとスチールコードとの境目を蜜ロウでシールし、温度50℃、相対湿度95%の恒温恒湿槽内で28日間放置した。その後、室温(23℃)条件下で各試験体からスチールコードを引き抜く引き抜き試験を行って、上記引き抜きの際にかかった引抜力を測定した。上記引き抜き試験は、DIN22131に準拠して行った。
本発明において、上記引抜力が65N/mmを超える場合、耐水接着性に優れると評価した。
上記引抜力が65N/mm以下である場合、耐水接着性が劣ると評価した。
上記引抜力が65N/mmより大きいほど、耐水接着性により優れると評価した。
(ジエン系ゴム)
・ジエン系ゴム1(NR):天然ゴム。TSR20
・ジエン系ゴム2(SBR):溶液重合スチレンブタジエン共重合体ゴム。商品名タフデン 2000R(旭化成社製)。ガラス転移温度−70℃。重量平均分子量32万、結合スチレン量27質量%、ビニル量9質量%
・液状ポリイソプレン(LIR−403):クラレ社製LIR−403。重量平均分子量34000。酸無水物基を有するポリイソプレン(下記構造)。室温(23℃)の条件下で液状。
・ロジン類(ガムロジン):中国ロジン WW、荒井化学工業株式会社製。軟化点:65℃、酸価:162mgKOH/g、分子量:289
・塩素化パラフィン:塩素化パラフィン(塩素含有量70質量%)。エンパラ 70S、味の素ファインテクノ社製。
・(比較)有機酸コバルト塩(ナフテン酸コバルト10%):ナフテン酸コバルト。コバルト含有量10質量%。商品名「ナフテン酸コバルト 10%」、DIC CORPORATION社製。
・ステアリン酸:ステアリン酸YR(日油社製)
加硫促進剤の含有量及び式(X)の値が所定の範囲を満たさない比較例3は、耐水接着性が劣った。
所定の有機酸コバルト塩を含有せず、代わりにホウ素を含まない有機酸コバルト塩を含有する比較例4は、耐水接着性が劣った。
2 スチールコード
4 コートゴム層
6 カバーゴム層
Claims (7)
- ジエン系ゴムを少なくとも含むゴム成分と、
ホウ素を含む有機酸コバルト塩と、
硫黄とを含有し、
加硫促進剤の含有量が、前記ゴム成分100質量部に対して、0.0〜2.0質量部であり、
下記式(X)の値が0.09〜1.32である、スチールコード接着用ゴム組成物。
式(X)=A+B/C
式(X)において、Aは、前記加硫促進剤の含有量であり、
Bは、前記ゴム成分100質量部に対する前記有機酸コバルト塩中のコバルトの含有量であり、
Cは、前記ゴム成分100質量部に対する前記硫黄の含有量である。 - 前記有機酸コバルト塩が、ネオデカン酸ホウ酸コバルトである、請求項1に記載のスチールコード接着用ゴム組成物。
- 前記加硫促進剤を含有し、前記加硫促進剤が、チアゾール系加硫促進剤である、請求項1又は2に記載のスチールコード接着用ゴム組成物。
- 前記加硫促進剤を含有し、前記加硫促進剤が、ベンゾチアゾリルポリスルフィド系化合物である、請求項1〜3のいずれか1項に記載のスチールコード接着用ゴム組成物。
- 前記加硫促進剤を含有しない、請求項1又は2に記載のスチールコード接着用ゴム組成物。
- 亜鉛メッキスチールコードを接着させるために使用される、請求項1〜5のいずれか1項に記載のスチールコード接着用ゴム組成物。
- 請求項1〜6のいずれか1項に記載のスチールコード接着用ゴム組成物を用いて形成されたコンベヤベルト。