JP2020509612A - 高反射ゲインタイプ太陽電池用封止シート及び用途 - Google Patents
高反射ゲインタイプ太陽電池用封止シート及び用途 Download PDFInfo
- Publication number
- JP2020509612A JP2020509612A JP2019569529A JP2019569529A JP2020509612A JP 2020509612 A JP2020509612 A JP 2020509612A JP 2019569529 A JP2019569529 A JP 2019569529A JP 2019569529 A JP2019569529 A JP 2019569529A JP 2020509612 A JP2020509612 A JP 2020509612A
- Authority
- JP
- Japan
- Prior art keywords
- solar cell
- high reflection
- type solar
- resin
- sealing sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
テスト方法は標準GB/T29848《太陽電池モジュール封止用エチレン−酢酸ビニル共重合体(EVA)シート》における積分球付きの分光光度計方法を参照する。
試験装置:紫外可視光分光光度計。
試験条件:380nm〜1100nm。
2.体積抵抗率
テスト方法は標準GB/T29848《太陽電池モジュール封止用エチレン−酢酸ビニル共重合体(EVA)シート》を参照する。
試料サイズ:100mm*100mm。
試験条件:テスト電圧は1000Vである。
3.架橋度
テスト方法は標準GB/T29848《太陽電池モジュール封止用エチレン−酢酸ビニル共重合体(EVA)シート》を参照する。
試料サイズ:100mm*100mm。
試験条件:テスト電圧は1000Vである。
4.収縮率
テスト方法は標準GB/T29848《太陽電池モジュール封止用エチレン−酢酸ビニル共重合体(EVA)シート》を参照する。
試料サイズ:100mm*100mm。
試験条件:120℃,3min。
5.ガラス/EVA剥離強度
テスト方法は標準GB/T29848《太陽電池モジュール封止用エチレン−酢酸ビニル共重合体(EVA)シート》を参照する。
試料サイズ:300mm*10mm。
延伸速度:100mm/min。
6.定湿熱老化耐性
テスト方法は標準GB/T29848《太陽電池モジュール封止用エチレン−酢酸ビニル共重合体(EVA)シート》を参照する。
試験条件:+85℃、相対湿度85%。
試料の試験前後の黄変度(ΔYI)を国家標準GB2409《プラスチックの黄色度の試験方法》に応じて測定する。
7.最大電力
テスト方法は標準IEC61215《地上用結晶シリコン太陽電池モジュール−設計の評定及びタイプの判定》を参照する。
サンプルサイズ:中来会社(中国語:中来公司)両面発電型太陽セル60枚のモジュール。
試験条件:AM1.5、放射照度1000W/m2、+25℃、50%RH。
封止シートの製造過程は以下のとおりである。
まず、エチレン-酢酸ビニル共重合体(米国デュポン社)85wt%、改質助剤である3−(メタクリロイルクロリド)プロピルトリメトキシシラン(上海淳安国際貿易有限会社)10wt%、耐紫外線助剤である2-(2’-ヒドロキシ-3’-t-ブチル-5’-メチルフェニル)-5-クロロベンゾトリアゾール(済南ボンドケミカルテクノロジー有限会社(中国語:済南邦徳化工技術有限公司))2wt%、熱酸化老化防止剤である2,6-ジ-t-ブチル-4-メチルフェノール(聖和ケミカル有限会社(中国語:聖和化工有限公司))1.5wt%、および開始剤である過酸化ベンゾイル(成都格雷西亜化学技術有限会社)1.5wt%を均一に混合した後、60〜90℃で押し出した。そして、流延製膜法によって厚み450μmの封止層を作製した。
まず、エチレン-オクテン共重合体(米国ダウケミカル社)60wt%、改質助剤である3−(2,3−エポキシプロポキシ)プロピルメチルジエトキシシラン(済南郎化化学工業有限会社(中国語:済南郎化化工有限公司))10wt%及びビニルトリメトキシシラン(済南郎化化学工業有限会社)20wt%、耐紫外線助剤である2,4-ジヒドロキシベンゾフェノン(上海至しん化学工業有限会社)6wt%、熱酸化老化防止剤である9,10-ジヒドロ-9-オキサ-10-ホスファフェナントレン-10-オキサイド(東莞市瓦里西化学工業有限会社(中国語:東莞市瓦里西化工有限公司))3wt%、開始剤である2,5-ジメチル-2,5-ビス(tert-ブチルパーオキシ)-ヘキサン(広州市乾晟貿易有限会社)1wt%を均一に混合した後、80〜120℃で押し出した。そして、流延製膜法によって厚み200μmの封止層を作製した。
まず、エチレン-アクリル酸メチル共重合体(米国デュポンケミカル)70wt%、改質助剤であるビニルトリメトキシシラン(上海淳安国際貿易有限会社)18wt%、耐紫外線助剤である2−[4−[2−ヒドロキシ−3−ドデシルオキシプロピル]オキシ]−2−ヒドロキシフェニル]−4,6−ビス(2,4−ジメチルフェニル−1,3,5−トリアジン(済南ボンドケミカルテクノロジー有限会社)8wt%、熱酸化老化防止剤である2− [4− [2−ヒドロキシ−3−ドデシルオキシプロピル]オキシ] −2−ヒドロキシフェニル] −4,6−ビス(2,4−ジメチルフェニル)−1,3,5−トリアジン(聖和ケミカル有限会社)2.5wt%、開始剤であるo,o−tert−アミル−o−(2−エチルヘキシル)−モノ−パーオキシカーボネート(成都格雷西亜化学技術有限会社)1.5wt%を均一に混合した後、80〜120℃で押し出した。そして、流延製膜法によって厚み200μmの封止層を作製した。
まず、エチレン-プロピレン共重合体(米国ダウケミカル社)65wt%、改質助剤であるビニルトリス(β-メトキシエトキシ)ケイ素(南京ロン・シリコン材料有限会社)20wt%、耐紫外線助剤であるビス(1,2,2,6,6-ペンタメチル-4-ピペリジル)セバケート/モノ(1,2,2,6,6-ペンタメチル-4-ピペリジル)セバケートコンパウンド(済南郎化化学工業有限会社)10wt%、熱酸化老化防止剤であるβ-(3,5-ジ-t-ブチル-4-ヒドロキシフェニル)プロピオン酸n-オクタデカノールエステル(杭州儲源化学工業有限会社(中国語:杭州儲源化工有限公司))2.5wt%、開始剤である2,5-ジメチル-2,5-ビス(ベンゾイルペルオキシ)-ヘキサン(ドイツBASF社)2.5wt%を均一に混合した後、150〜200℃で押し出した。そして、流延製膜法によって厚み500μmの封止層を作製した。
まず、エチレン-ノルボルネン共重合体(米国ダウケミカル社)90wt%、改質助剤である3−(2,3−エポキシプロポキシ)プロピルメチルジエトキシシラン(杭州の江シリコーン化学工業有限会社(中国語:杭州之江有机硅化工有限公司))6wt%、耐紫外線助剤であるポリコハク酸(4−ヒドロキシ−2,2,6,6−テトラメチル−1−ピペリジルエタノール)エステル(台湾永光化学会社)2.5wt%、熱酸化老化防止剤であるトリエチレングリコールエーテル−ジ(3−tert−ブチル−4−ヒドロキシ−5−メチルフェニル)プロピオネート(ドイツBASF社)1wt%、開始剤である2,4,6−トリメチルベンゾイル−ジフェニルホスフィンオキシド(ドイツBASF社)0.5wt%を均一に混合した後に、120℃〜160℃で押出した。そして、流延製膜法によって厚み450μmの封止層を作製した。
市販品の厚み450μmの透明な太陽電池用封止材F406Sを購入した。
実施例1、2、3、4、5で得られた太陽電池用封止シートおよび比較例1の材料について性能検出を行った。結果を表1に示す。
Claims (10)
- 封止層と反射層とからなる高反射ゲインタイプ太陽電池用封止シートであって、
前記封止層は、厚さが200〜500μmであり、60〜90wt%の第1の本体樹脂、0.5〜30wt%の改質助剤、0.1〜10wt%の耐紫外線助剤、0.1〜3wt%の熱酸化老化防止剤及び0.1〜3wt%の開始剤を混合した後、60°C〜200°Cで溶融して流延製膜法によって作製され、
前記反射層は、厚さが5〜200μmであり、60〜85wt%の第2の本体樹脂、3〜30wt%の副樹脂、3〜30wt%の第1のフィラー、0〜20wt%の第2のフィラー、0.5〜10wt%の改質助剤、0.5〜20wt%の希釈剤、0〜1wt%の耐紫外線助剤、0.001〜5wt%の熱酸化老化防止剤及び0.001〜5wt%の開始剤を混合した後、封止層の表面に塗布したのち、30°C〜150°Cでの硬化によって作製され、
前記第1の本体樹脂は、エチレンと、プロピレン、ブテン、ヘプテン、オクテン、ノルボルネン、酢酸ビニル、アクリル酸メチル、及びメタクリル酸メチルから選ばれた一種又は二種のモノマーとを共重合して得られることを特徴とする高反射ゲインタイプ太陽電池用封止シート。 - 前記第2の本体樹脂は、ヒドロキシアクリル樹脂、分子末端に水酸基を有するポリオレフィン樹脂、ポリカーボネートジオール、ポリカプロラクトンジオール、及びポリテトラヒドロフランジオールから選ばれた1種または2種以上を任意の配合比で混合して構成され、
前記副樹脂は、ビスフェノールA型エポキシ樹脂、フェノールエポキシ樹脂、ビスフェノールAエポキシビニルエステル樹脂、フェノールエポキシビニルエステル樹脂、アクリル型ビニルエステル樹脂、及びポリウレタン型ビニルエステル樹脂から選べれた1種又は2種以上を任意の配合比で混合して構成されることを特徴とする請求項1に記載の高反射ゲインタイプ太陽電池用封止シート。 - 前記第1のフィラーは、粒径が1μm〜40μmの範囲であるフレーク状の湿式マイカパウダー、タルク粉末、焼成カオリン、酸化亜鉛およびモンモリロナイトから選ばれた1種又は2種以上0〜40wt%と、粒径が1μm〜50μmの範囲である球状のガラスマイクロビーズ、セラミックマイクロビーズ、アルミナ、マグネシア、窒化ホウ素、及び酸化亜鉛から選ばれた一種0〜40wt%と、粒径が0.2μm〜1.0μmの範囲であるチタン白20〜100wt%とを混合して構成され、
前記第2のフィラーは、粒径が5μm〜100μmの範囲であるポリメチルメタクリレート微粉、ポリアミド微粉、ポリエステル微粉、ポリスチレン微粉、ポリエチレン微粉、及びポリプロピレン微粉から選ばれた1種又は2種以上を任意の配合比で混合して構成されることを特徴とする請求項1に記載の高反射ゲインタイプ太陽電池用封止シート。 - 前記改質助剤は、3−(メタクリロイルクロリド)プロピルトリメトキシシラン、ビニルトリエトキシシラン、ビニルトリメトキシシラン、ビニルトリス(β-メトキシエトキシ)シラン、N-(2-アミノエチル-3-アミノプロピル)トリメトキシシラン、及び、3-(2,3-エポキシプロポキシ)プロピルメチルジエトキシシランから選ばれた1種又は2種以上を任意の配合比で混合して構成されることを特徴とする請求項1に記載の高反射ゲインタイプ太陽電池用封止シート。
- 前記希釈剤は、アルキルアクリレート、エーテルアクリレート、ヒドロキシアクリレート、グリコールジアクリレート、トリヒドロキシトリアクリレート、アクリル酸グリシジル、エトキシ化ビスフェノールAアクリレート、アルキルメタクリレート、エーテルメタクリレート、ヒドロキシメタクリレート、グリコールジメタクリレート、トリヒドロキシトリメタクリレート、メタクリル酸グリシジル、及びエトキシ化ビスフェノールAメタクリレートから選ばれた1種又は2種以上を任意の配合比で混合して構成されることを特徴とする請求項1に記載の高反射ゲインタイプ太陽電池用封止シート。
- 前記反射層のパターンは、規則的に配列され、セル同士の間の間隙の形状に一致になるように維持され、反射層はアニロックスロール(anilox roll)コーティング、マスクコーティング、スプレーコーティング、及び転写印刷などの方式の一種でコーティングされることを特徴とする請求項1に記載の高反射ゲインタイプ太陽電池用封止シート。
- 前記反射層の硬化方式は、熱硬化、放射線硬化、紫外線硬化、及びマイクロ波硬化から選ばれた1種、又は2種以上の組み合わせであることを特徴とする請求項1に記載の高反射ゲインタイプ太陽電池用封止シート。
- 請求項1に記載の高反射ゲインタイプ太陽電池用封止シートの用途であって、前記高反射ゲインタイプ太陽電池用封止シートは、結晶シリコン型太陽電池モジュールを封止するために使用され、セル同士の間の間隙の光線反射率を増加させることによりモジュール電力を増加させることを特徴とする高反射ゲインタイプ太陽電池用封止シートの用途。
- 前記結晶シリコン型太陽電池モジュールは、表裏両面とも発電可能な太陽電池モジュールであることが好ましいことを特徴とする請求項8に記載の用途。
- 前記高反射ゲインタイプ太陽電池用封止シートは、前層封止シートまたは後層封止シートとして使用可能であり、太陽電池モジュールを封止する際には、前板ガラス、前層封止シート、セル、後層封止シート、および後板透明材料を順に積層し、ラミネータに入れ、140℃〜160℃の温度で5〜18分間ラミネートし、
前記後板透明材料は、ガラス又は透明な太陽電池バックシートであることを特徴とする請求項9に記載の用途。