JP2019515091A - 帯電防止性、光安定性熱可塑性ポリカーボネート成形化合物 - Google Patents
帯電防止性、光安定性熱可塑性ポリカーボネート成形化合物 Download PDFInfo
- Publication number
- JP2019515091A JP2019515091A JP2018556456A JP2018556456A JP2019515091A JP 2019515091 A JP2019515091 A JP 2019515091A JP 2018556456 A JP2018556456 A JP 2018556456A JP 2018556456 A JP2018556456 A JP 2018556456A JP 2019515091 A JP2019515091 A JP 2019515091A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- polymer
- component
- vinyl
- composition according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
A)50重量%〜90重量%、好ましくは60重量%〜80重量%、より好ましくは65重量%〜75重量%の、芳香族ポリカーボネート、芳香族ポリエステルカーボネートおよび芳香族ポリエステルからなる群から選択される少なくとも1種のポリマー、好ましくは芳香族ポリカーボネート、
B)下記を含んでなる5重量%〜40重量%、好ましくは10重量%〜30重量%、より好ましくは15重量%〜25重量%のポリマー:
B.1 下記を含んでなる少なくとも1種のゴム変性ビニル(コ)ポリマー:
B.1.1 B.1に対して、80重量%〜95重量%の、少なくとも1種のビニルモノマー、および
B.1.2 B.1に対して、5重量%〜20重量%の、1種以上のエラストマー性ポリブタジエン含有グラフトベース、(コ)ポリマーであり、
ここで、B.1が
ビニルモノマーB.1.1でグラフトされ、かつビニルモノマーB.1.1からなるビニル(コ)ポリマーの含有物を含有している、ポリブタジエン含有ゴム粒子、および
これらのゴム粒子に結合せず、かつゴム粒子に含まれていないビニルモノマーB.1.1からなるビニル(コ)ポリマーマトリックスを含有しているものであり、
および、場合により、
B.2ビニルモノマーでグラフトされ、好ましくは乳化重合法で製造された追加のゴム粒子であり、かつ
B.2.1 それぞれの場合にB.2に対して、5重量%〜75重量%、好ましくは10重量%〜60重量%、より好ましくは25重量%〜50重量%の、少なくとも1種のビニルモノマー、
B.2.2 それぞれの場合にB.2に対して、25重量%〜95重量%、好ましくは40重量%〜90重量%、より好ましくは50重量%〜75重量%の、1種以上のエラストマー性グラフトベース、
からなるゴム粒子、
C)a)ポリエーテルブロックポリマーおよびポリエーテル系ポリウレタンからなる群から選択される、少なくとも1種のポリエーテル系ポリマーまたはコポリマー、およびb)少なくとも1種のホウ素含有塩を含んでなる、3重量%〜25重量%、好ましくは5重量%〜15重量%、より好ましくは6重量%〜12重量%の混合物、
D)ベンゾトリアゾールおよびトリアジンの物質クラスからなる群から選択される、0重量%〜2重量%、好ましくは0.1重量%〜1.0重量%、より好ましくは0.2重量%〜0.8重量%の、少なくとも1種のUV安定剤、
E)1種以上の追加の、0重量%〜20重量%、好ましくは0.1重量%〜10重量%、より好ましくは0.2重量%〜5重量%の添加剤を含んでなり、
ここで、成分A)〜E)を含んでなる組成物が、1重量%〜5重量%、好ましくは1.5重量%〜4.0重量%、より好ましくは1.7重量%〜3.0重量%のポリブタジエン含有量を有する組成物が、今回、有利な特性を有することが見出された。
A)50重量%〜90重量%の、芳香族ポリカーボネート、芳香族ポリエステルカーボネート、および芳香族ポリエステルからなる群から選択される少なくとも1種のポリマー、
B)下記を含んでなる5重量%〜40重量%のポリマー:
B.1 下記を含んでなる少なくとも1種のゴム変性ビニル(コ)ポリマー:
B.1.1 B.1に対して、80重量%〜95重量%の、少なくとも1種のビニルモノマー、および
B.1.2 B.1に対して、5重量%〜20重量%の、1種以上のエラストマー性ポリブタジエン含有グラフトベース、
ここで、B.1は
ビニルモノマーB.1.1でグラフトされ、かつビニルモノマーB.1.1からなるビニル(コ)ポリマーの含有物を含有している、ポリブタジエン含有ゴム粒子、および
これらのゴム粒子に結合せず、かつゴム粒子に含まれていないビニルモノマーB.1.1からなるビニル(コ)ポリマーマトリックス
を含有しているものであり、
および、場合により、
B.2 ビニルモノマーでグラフトされた追加のゴム粒子であり、かつ
B.2.1 B.2に対して、5重量%〜75重量%の少なくとも1種のビニルモノマー、および
B.2.2 B.2に対して、25重量%〜95重量%の1種以上のエラストマー性グラフトベース、
からなるゴム粒子、
C)a)ポリエーテルブロックポリマーおよびポリエーテル系ポリウレタンからなる群から選択される、少なくとも1種のポリエーテル系ポリマーまたはコポリマー、およびb)少なくとも1種のホウ素含有塩を含んでなる、3重量%〜25重量%の混合物、
D)ベンゾトリアゾールおよびトリアジンの物質クラスからなる群から選択される、0重量%〜2重量%の少なくとも1種のUV安定剤、
E)1種以上の追加の0重量%〜20重量%の添加剤を含んでなり、
ここで、成分A)〜E)を含む組成物が1重量%〜5重量%のポリブタジエン含有量を有する。
B.2.1 グラフトポリマーB.2に対して、25重量%〜50重量%の少なくとも1種のビニルモノマー、と
B.2.2 グラフトポリマーB.2に対して、50重量%〜75重量%の、<−70℃のガラス転移温度および0.2〜0.4μmのメジアン粒径D50を有する、1種以上のエラストマー性グラフトベースと
をグラフトすることによる乳化重合で製造されたものである、実施態様1〜8のいずれかに記載の組成物。
−ポリエーテルブロックポリマーに対して、30重量%〜70重量%程度のポリエチレングリコールブロックおよびポリエーテルブロックポリマーに対して、70重量%〜30重量%の程度のナイロン−12ブロックからなる、69.6重量%〜98.6重量%のポリエーテルブロックポリマー、
−ポリ(メタ)アクリレートおよびポリメチル(メタ)アクリレートからなる群から選択される、1重量%〜30重量%の少なくとも1種の追加のポリマー、および
−ビス(オキサラート)ホウ酸カリウムおよびビス(オキサラート)ホウ酸ナトリウムからなる群から選択される、0.4重量%〜4.0重量%の少なくとも1種の代表。
使用可能な成分Aには芳香族ポリカーボネート、芳香族ポリエステルカーボネート、芳香族ポリエステルまたは上記による1種以上のこれら物質クラスの複数の代表の混合物が含まれている。
Aは、単一結合の、追加のヘテロ原子を含んでいてもよい芳香族管が縮合されていてもよい、C1〜C5アルキレン、C2〜C5アルキリデン、C5〜C6シクロアルキリデン、−O−、−SO−、−CO−、−S−、SO2−、C6〜C12アリーレンであり、あるいは式(II)または(III)の部分である:
xは、各場合で独立して0、1または2であり、
pは1または0であり、かつ
R5およびR6は、各X1に対して独立して選択することができ、各々独立して水素またはC1〜C6アルキル、好ましくは水素、メチルまたはエチルであり、
X1は炭素を表し、かつ
mは4〜7、好ましくは4または5の整数であるが、ただし、少なくとも1個の原子X1上でR5およびR6は同時にアルキルである]。
本発明に従い成分Bとして使用可能なゴム変性ビニル(コ)ポリマーは、成分Bに対して、好ましくは少なくとも70重量%の程度、より好ましくは少なくとも85重量%の程度、さらに好ましくは少なくとも95重量%の程度の、最も好ましい実施態様では100重量%の、好ましくはバルク重合プロセスで調製された、第一ゴム変性ビニル(コ)ポリマーB.1であって、
−ビニルモノマーB.1.1でグラフトされたポリブタジエン含有ゴム粒子から構成された分散相を含有し、ビニルモノマーB.1.1と、ゴム粒子に結合していないゴム粒子に含まれないビニルモノマーB.1.1からなるゴム非含有ビニル(コ)ポリマーマトリックスとからなる、ビニル(コ)ポリマーの含有物を有し、
−ここでビニル(コ)ポリマー含有物を含んでいるゴム粒子は、超遠心分離によって測定した0.3〜10.00μm、好ましくは0.5〜1.5μm、特に0.7〜1.0μmのメジアン粒径D50を有し、
−5重量%〜18重量%、好ましくは7重量%〜15重量%、特に8重量%〜13重量%のポリブタジエン含有量を有する、
第一ゴム変性ビニル(コ)ポリマーB.1を含有している。
B.1.1 ゴム変性ビニル(コ)ポリマーB.1に対して、好ましくは80重量%〜95重量%、より好ましくは83重量%〜93重量%、さらに好ましくは85重量%〜92重量%の少なくとも1種のビニルモノマーの、
B.1.2 <−50℃の、さらに好ましくは<−60℃の、より好ましくは<−70℃のガラス転移温度を有する、ゴム変性ビニル(コ)ポリマーB.1に対して、好ましくは5重量%〜20重量%、より好ましくは7重量%〜17重量%、さらに好ましくは8重量%〜15重量%の1種以上のエラストマー性ポリブタジエン含有グラフトベース
の存在下での重合によって調製される。
B.1.1.1 各場合にB.1.1.1とB.1.1.2の合計に対して、65〜85重量部、より好ましくは70〜80重量部、さらに好ましくは74〜78重量部の、ビニル芳香族および/または環置換ビニル芳香族(スチレン、α−メチルスチレン、p−メチルスチレン、p−クロロスチレンなど)および/または(C1−C8)−アルキル(メタ)アクリレート、例えばメタクリル酸メチル、メタクリル酸エチルなど、および
B.1.1.2 各場合にB.1.1.1とB.1.1.2の合計に対して、15〜35重量部、より好ましくは20〜30重量部、さらに好ましくは22〜26重量部の、シアン化ビニル(アクリロニトリルおよびメタクリロニトリルなどの不飽和ニトリル)、および/または(C1−C8)−アルキル(メタ)アクリレート、例えば、メタクリル酸メチル、アクリル酸n−ブチル、アクリル酸t−ブチル、および/または不飽和カルボン酸の誘導体(例えば無水物およびイミド)、例えば無水マレイン酸、
の混合物である。
B.2.1 グラフトポリマーB.2に対して、5重量%〜75重量%、好ましくは10重量%〜60重量%、より好ましくは25重量%〜50重量%の、少なくとも1種のビニルモノマーの、
B.2.2 グラフトポリマーB.2に対して、25重量%〜90重量%、好ましくは40重量%〜90重量%、より好ましくは50重量%〜75重量%の、1種以上のエラストマー性グラフトベース上に
グラフトすることにより調製された1種以上のグラフトポリマーである。
B.2.1.1 各場合にB.2.1.1とB.2.1.2の合計に対して、50〜90重量部、より好ましくは70〜80重量部の、ビニル芳香族および/または環置換ビニル芳香族(スチレン、α−メチルスチレン、p−メチルスチレン、p−クロロスチレンなど)、および/または(C1−C8)−アルキル(メタ)アクリレート、例えばメタクリル酸メチル、メタクリル酸エチルなど、および
B.1.1.2 各場合にB.2.1.1とB.2.1.2の合計に対して、10〜50重量部、より好ましくは20〜30重量部の、シアン化ビニル(アクリロニトリルおよびメタクリロニトリルなどの不飽和ニトリル)、および/または(C1−C8)−アルキル(メタ)アクリレート、例えば、メタクリル酸メチル、アクリル酸n−ブチル、アクリル酸t−ブチル、および/または不飽和カルボン酸の誘導体(例えば、無水物およびイミド)、例えば無水マレイン酸
の混合物である。
成分Cは、ポリエーテルブロックポリマーおよびポリエーテル系ポリウレタンからなる群から選択される少なくとも1種のポリエーテル系ポリマーまたはコポリマー、および少なくとも1種のホウ素含有塩を含むイオン導電性ポリマーまたはポリマーブレンドである。
−ブロックコポリマーに対して、10重量%〜90重量%、より好ましくは20重量%〜80重量%、さらに好ましくは30重量%〜70重量%程度のポリエチレングリコールブロック、およびブロックコポリマーに対して、10重量%〜90重量%、より好ましくは20重量%〜80重量%、さらに好ましくは30重量%〜70重量%程度のナイロン−12からなる、49.8重量%〜99.8重量%、さらに好ましくは69.6重量%〜98.6重量%、最も好ましくは79重量%〜89重量%のポリエーテルブロックポリマー、
−0重量%〜50重量%、さらに好ましくは1重量%〜30重量%、最も好ましくは10重量%〜20重量%の、ポリ(メタ)アクリレートおよびポリメチル(メタ)アクリレートからなる群からの少なくとも1種の代表から選択される追加のポリマー、より好ましくはポリメチルメタクリレート、および
−0.2重量%〜10重量%、さらに好ましくは0.4重量%〜4.0重量%、最も好ましくは1.0重量%〜3.0重量%の、−COOHおよび−OHから選択される少なくとも2種の反応性基を有する、C2〜C8脂肪族または芳香族成分からなる群から選択される、二座配位子を含有している、ホウ素中心陰イオン複合体のアルカリ金属塩、より好ましくはビス(オキサラート)ホウ酸カリウムおよびビス(オキサラート)ホウ酸ナトリウムからなる群からの代表、特に好ましくはビス(オキサラート)ホウ酸カリウム
を含む。
成分Dとして、ベンゾトリアゾールおよびトリアジン、より好ましくは二量体のベンゾトリアゾールおよび1,3,5−トリアジンの物質クラスからなる群からの少なくとも1種の代表から選択されるUV安定剤を使用することが可能である。
R1、R2、およびR3は独立して、C1〜C8アルキルまたはC1〜C8アリールからなる群から選択される、同一または異なる基であり、
nおよびpは独立して各々、0〜5、好ましくは0、1または2、より好ましくは0または1の整数であり、
mは0〜4、好ましくは0または1、より好ましくは0の整数である、
Rは、炭素、水素および場合により酸素、好ましくはC1〜C10アルキルからなる任意の有機基であり、
R2およびR3は好ましくはメチルかまたはフェニル、より好ましくはフェニルである]
の2−(4,6−ジアリール−1,3,5−トリアジン−2−イル)−5−(アルコキシ)フェノールがUV安定剤として使用される。
組成物は成分Eとして、好ましくは難燃剤(例えば、有機リン化合物またはハロゲン化合物、特にビスフェノールA系オリゴホスフェート)、滴下防止剤(anti-drip agents)(例えば、フッ素化ポリオレフィン、シリコーンおよびアラミド繊維の物質クラスの化合物)、難燃助剤(例えば、ナノスケールの金属酸化物)、煙抑制剤(例えば、ホウ酸亜鉛)、滑剤、および離型剤(例えば、テトラステアリン酸ペンタエリスリトール)、核剤、成分Cとはことなる追加の静電気防止剤および導電添加剤、成分Dとは異なる追加の安定剤(例えば、加水分解、熱老朽化、およびエステル交換反応の安定剤、成分Dとは異なる追加のUV安定剤および酸/塩基消光剤)とは異なるさらなる安定剤、着色剤(例えば、二酸化チタン、アゾ顔料およびカーボンブラックなどの有機または無機の顔料ならびに有機可溶性染料)、流動促進剤、相溶化剤、成分Bとは異なる、コアシェル構造を有しない追加の衝撃改質剤、成分A〜Cとは異なる追加のポリマー成分(例えば、官能性ブレンドパートナー)、ならびにフィラーおよび補強剤(例えば、炭素繊維、滑石、雲母、カオリン、CaCO3)からなる群から選択される、1種以上の追加の添加剤を含んでいてもよい。
本発明による熱可塑性成形化合物は、例えば、それぞれの成分を混合し、生じる混合物を、既知の方法で、従来の装置内、例えば、内部混練機、押出機、および双軸システムで、好ましくは200℃〜320℃、より好ましくは240℃〜300℃の温度で溶融化合および溶融押出しすることにより製造することができる。
30000g/molの重量平均分子量Mw(BPA−PC標準に対して塩化メチレン中のGPCにより決定)を有する、ビスフェノールA系直鎖状ポリカーボネート。
スチレン−アクリロニトリル−コポリマーおよびスチレン−アクリロニトリル−コポリマーマトリックスの含有物を有するポリブタジエン含有ゴム粒子の分散相を含み、バルク重合プロセスによって調製された、アクリロニトリル−ブタジエン−スチレン(ABS)ポリマーであって、23:10:67重量%のA:B:S比およびアセトン不溶性画分として決定された、20重量%のゲル含量を有する、アクリロニトリル−ブタジエン−スチレン(ABS)ポリマー。成分B1中の、遊離(即ちアセトン可溶性)スチレン−アクリロニトリルコポリマーは、165kg/molの重量平均分子量Mw(ポリスチレン標準で溶剤としてのアセトン中でのGPCにより測定)を有する。超遠心分離によって測定したメジアンゴム粒径D50は0.85μmである。10kgのラム負荷で、220℃にてISO 1133(2012年バージョン)によって測定した成分B1のメルトボリュームフローレート(MVR)は6.7ml/10分である。
14:50:36重量%のA:B:S比を有し、25:75重量%のアクリロニトリル:スチレン比を有する80重量%のスチレン−アクリロニトリルコポリマーを有し、かつ110kg/molの重量平均分子量Mw(ポリスチレン標準で溶剤としてのアセトン中でのGPCにより測定)を有する、乳化重合法によって調製した20重量%のアクリロニトリル−ブタジエン−スチレン(ABS)グラフトポリマーからなるABSブレンド物。従って、混合物は23:10:67重量%のA:B:S比を有している。超遠心分離によって測定されたメジアンゴム粒径D50は0.32μmである。ゴム粒子は含有物を含有していない。
ポリブチルアクリレートゴムコアおよびポリメチルメタクリレートシェルを有している37重量%のグラフトポリマーからなるASAブレンド物であって、このグラフトポリマーは乳化重合法によって調製された、70:30重量%のコア/シェル比、および24:76重量%のアクリロニトリル:スチレン比を有する63重量%のスチレン−アクリロニトリルコポリマーを有する。従って、この混合物は、26重量%のアクリル酸ブチルゴム含有量を有している。
15重量%のポリメチルメタクリレート、PEBAに対して50重量%程度のポリエチレングリコールブロックおよび、PEBAに対して50重量%程度のナイロン−12ブロックからなる、83.5重量%のポリエーテルアミドブロックポリマー(PEBA)、および1.5重量%のビス(オキサラート)ホウ酸カリウムを含む混合物。C1は8・107Ωの比表面積抵抗(1993年バージョン中のIEC 60093により測定)を有する。
PEBAに対して、50重量%程度のポリエチレングリコールブロックおよびPEBAに対して、50重量%程度のナイロン−12ブロックからなるポリエーテルアミドブロックコポリマー(PEBA)。これは、WO2012/084848A1の成分Cとして発明に従って、使用されるポリエーテルアミドブロックコポリマーである。C2は3・109Ωの比表面積抵抗(1993年バージョン中のIEC 60093により測定)を有する。
Tinuvin(商標)360(BASF、ルートヴィヒスハーフェン、ドイツ):
2,2’−メチレンビス[6−(2H−ベンゾトリアゾール−2−イル)−4−(1,1,3,3−テトラメチルブチル)フェノール]
Tinuvin(商標)1600(BASF、ルートヴィヒスハーフェン、ドイツ):
Tinuvin(商標)329(バスフ、ルートヴィヒスハーフェン、ドイツ):
2−(2H−ベンゾトリアゾール−2−イル)−4−(1,1,3,3−テトラメチルブチル)フェノール
二酸化チタン顔料:Kronos(商標)2233(Kronos Titan GmbH、レーヴァークーゼン、ドイツ)
Rutile顔料:Heucodur(商標)Yellow 3R(Heubach GmbH、ランゲスハイム、ドイツ)
酸化鉄顔料:Bayferrox(商標)180M(Lanxess AG、ケルン、ドイツ)
カーボンブラック:Elftex(商標)570Pearls(Cabot GmbH、ラインフェルデン、ドイツ)
テトラステアリン酸ペンタエリスリトール
Irgafos(商標)168(BASF、ルートヴィヒスハーフェン、ドイツ):
亜リン酸トリス(2,4−ジ−tert−ブチルフェニル)
Irganox(商標)1076(BASF、ルートヴィヒスハーフェン、ドイツ):
2,6−ジ−tert−ブチル−4−(オクタデカンオキシカルボニルエチル)フェノール
260℃の溶融温度で、50mbar(絶対圧)の減圧を適用してWerner&Pfleiderer ZSK−25二軸押出機内で成分を混合した。破壊試験のための試験片を例外として、260℃の溶融温度、および80℃の成形温度でArburg 270E射出成形機内で成型品を製造した。破壊試験のための試験片は300℃の溶融温度、または同一の加工パラメータで製造した。
Claims (15)
- 下記を含んでなる、組成物:
A)50重量%〜90重量%の、芳香族ポリカーボネート、芳香族ポリエステルカーボネート、および芳香族ポリエステルからなる群から選択される少なくとも1種のポリマー、
B)下記を含んでなる5重量%〜40重量%のポリマー:
B.1 下記を含んでなる少なくとも1種のゴム変性ビニル(コ)ポリマー:
B.1.1 B.1に対して、80重量%〜95重量%の、少なくとも1種のビニルモノマー、および
B.1.2 B.1に対して、5重量%〜20重量%の、1種以上のエラストマー性ポリブタジエン含有グラフトベース、
ここで、B.1は
ビニルモノマーB.1.1でグラフトされ、かつビニルモノマーB.1.1からなるビニル(コ)ポリマーの含有物を含有している、ポリブタジエン含有ゴム粒子、および
これらのゴム粒子に結合せず、かつゴム粒子に含まれていないビニルモノマーB.1.1からなるビニル(コ)ポリマーマトリックス
を含有しているものであり、
および、場合により、
B.2 ビニルモノマーでグラフトされた追加のゴム粒子であり、かつ
B.2.1 B.2に対して、5重量%〜75重量%の、少なくとも1種のビニルモノマー、および
B.2.2 B.2に対して、25重量%〜95重量%の、1種以上のエラストマー性グラフトベース、
からなるゴム粒子、
C)a)ポリエーテルブロックポリマーおよびポリエーテル系ポリウレタンからなる群から選択される、少なくとも1種のポリエーテル系ポリマーまたはコポリマー、およびb)少なくとも1種のホウ素含有塩を含んでなる、3重量%〜25重量%の混合物、
D)ベンゾトリアゾールおよびトリアジンの物質クラスからなる群から選択される、0重量%〜2重量%の少なくとも1種のUV安定剤、
E)1種以上の追加の0重量%〜20重量%の添加剤を含んでなり、
ここで、成分A)〜E)を含んでなる組成物が1重量%〜5重量%のポリブタジエン含有量を有する。 - 成分Aが芳香族ポリカーボネートである、請求項1に記載の組成物。
- 成分B.1がバルク重合法で製造され、かつ成分B.1中にビニル(コ)ポリマー含有物を含有しているゴム粒子が0.5〜1.5μmのメジアン粒径D50を有する、請求項1または2に記載の組成物。
- 成分B.1が8重量%〜13重量%のポリブタジエン含有量を有している、請求項1〜3のいずれか一項に記載の組成物。
- ゴム粒子に結合せず、かつゴム粒子に含まれていない、成分Bの前記ビニル(コ)ポリマーが、140〜200kg/molの重量平均分子量を有する、請求項1〜4のいずれか一項に記載の組成物。
- 成分B.2が、
B.2.1 グラフトポリマーB.2に対して、25重量%〜50重量%の少なくとも1種のビニルモノマーと
B.2.2 グラフトポリマーB.2に対して、50重量%〜75重量%の、<−70℃のガラス転移温度および0.2〜0.4μmのメジアン粒径D50を有する、1種以上のエラストマー性グラフトベースと、
をグラフトすることによる乳化重合で製造されたものである、請求項1〜5のいずれか一項に記載の組成物。 - 前記組成物が、ポリアクリレートゴムおよびシリコーンゴムを含まず、かつグラフトベースとしてそのようなゴムを含有しているグラフトポリマーを含まない、請求項1〜5のいずれか一項に記載の組成物。
- 成分Bが、少なくとも70重量%程度の成分B.1からなる、請求項1〜7のいずれか一項に記載の組成物。
- 成分C)からのポリエーテル系ポリマーが、ブロックコポリマーに対して、30重量%〜70重量%のポリエチレングリコールブロックおよびブロックコポリマーに対して、30重量%〜70重量%程度のポリアミドからなるポリエーテル−アミドブロックコポリマーである、請求項1〜8のいずれか一項に記載の組成物。
- 成分C中のホウ素含有塩が、−COOHおよび−OHから選択される少なくとも2種の反応性基を有するC2〜C8の脂肪族または芳香族成分からなる群から選択される二座配位子を含有する、少なくとも1種のホウ素中心陰イオン複合体のアルカリ金属塩である、請求項1〜9のいずれか一項に記載の組成物。
- 前記ホウ素含有塩が、ビス(オキサラート)ホウ酸カリウムまたはビス(オキサラート)ホウ酸ナトリウムである、請求項9に記載の組成物。
- 成分Cが下記からなる、請求項1〜11のいずれか一項に記載の組成物:
−ポリエーテルブロックポリマーに対して、30重量%〜70重量%程度のポリエチレングリコールブロックおよびポリエーテルブロックポリマーに対して70重量%〜30重量%の程度のナイロン−12ブロックからなる、69.6重量%〜98.6重量%のポリエーテルブロックポリマー、
−ポリ(メタ)アクリレートおよびポリメチル(メタ)アクリレートからなる群から選択される、1重量%〜30重量%の少なくとも1種の追加のポリマー、および
−ビス(オキサラート)ホウ酸カリウムおよびビス(オキサラート)ホウ酸ナトリウムからなる群から選択される、0.4重量%〜4.0重量%の少なくとも1種の代表。 - 成分Dが、二量体のベンゾトリアゾールおよび1,3,5−トリアジンの物質クラスからなる群から選択される、請求項1〜12のいずれか一項に記載の組成物。
- 成型品を製造するための、請求項1〜13のいずれか一項に記載の組成物の使用。
- 請求項1〜13のいずれか一項に記載の組成物から得られる、成型品。