JP2019510185A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2019510185A5 JP2019510185A5 JP2018540828A JP2018540828A JP2019510185A5 JP 2019510185 A5 JP2019510185 A5 JP 2019510185A5 JP 2018540828 A JP2018540828 A JP 2018540828A JP 2018540828 A JP2018540828 A JP 2018540828A JP 2019510185 A5 JP2019510185 A5 JP 2019510185A5
- Authority
- JP
- Japan
- Prior art keywords
- barrier layer
- crucible
- layer
- oxygen
- carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 239000000463 material Substances 0.000 claims 15
- OKTJSMMVPCPJKN-UHFFFAOYSA-N carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims 6
- 229910052799 carbon Inorganic materials 0.000 claims 6
- 229910052760 oxygen Inorganic materials 0.000 claims 6
- 239000001301 oxygen Substances 0.000 claims 6
- MYMOFIZGZYHOMD-UHFFFAOYSA-N oxygen Chemical compound O=O MYMOFIZGZYHOMD-UHFFFAOYSA-N 0.000 claims 6
- GUVRBAGPIYLISA-UHFFFAOYSA-N tantalum Chemical compound [Ta] GUVRBAGPIYLISA-UHFFFAOYSA-N 0.000 claims 4
- 229910052715 tantalum Inorganic materials 0.000 claims 4
- RTAQQCXQSZGOHL-UHFFFAOYSA-N titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 claims 4
- 229910052719 titanium Inorganic materials 0.000 claims 4
- 239000010936 titanium Substances 0.000 claims 4
- 239000007769 metal material Substances 0.000 claims 3
- ZOKXTWBITQBERF-UHFFFAOYSA-N molybdenum Chemical compound [Mo] ZOKXTWBITQBERF-UHFFFAOYSA-N 0.000 claims 3
- 229910052750 molybdenum Inorganic materials 0.000 claims 3
- 239000011733 molybdenum Substances 0.000 claims 3
- GUCVJGMIXFAOAE-UHFFFAOYSA-N niobium Chemical compound [Nb] GUCVJGMIXFAOAE-UHFFFAOYSA-N 0.000 claims 3
- 229910052758 niobium Inorganic materials 0.000 claims 3
- 239000010955 niobium Substances 0.000 claims 3
- 239000000843 powder Substances 0.000 claims 3
- 239000007921 spray Substances 0.000 claims 3
- WFKWXMTUELFFGS-UHFFFAOYSA-N tungsten Chemical compound [W] WFKWXMTUELFFGS-UHFFFAOYSA-N 0.000 claims 3
- 229910052721 tungsten Inorganic materials 0.000 claims 3
- 239000010937 tungsten Substances 0.000 claims 3
- 239000007789 gas Substances 0.000 claims 2
- 238000000034 method Methods 0.000 claims 2
- 238000000465 moulding Methods 0.000 claims 2
- 238000003825 pressing Methods 0.000 claims 2
- 239000003870 refractory metal Substances 0.000 claims 2
- 238000005245 sintering Methods 0.000 claims 2
- 239000002002 slurry Substances 0.000 claims 2
- 239000000956 alloy Substances 0.000 claims 1
- 229910045601 alloy Inorganic materials 0.000 claims 1
- 239000005350 fused silica glass Substances 0.000 claims 1
- 238000004519 manufacturing process Methods 0.000 claims 1
- 229910052751 metal Inorganic materials 0.000 claims 1
- 239000002184 metal Substances 0.000 claims 1
- 239000000203 mixture Substances 0.000 claims 1
- 229910052594 sapphire Inorganic materials 0.000 claims 1
- 239000010980 sapphire Substances 0.000 claims 1
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims 1
- 238000005507 spraying Methods 0.000 claims 1
- 238000007751 thermal spraying Methods 0.000 claims 1
Claims (22)
- タングステン又はモリブデン、あるいはタングステン系又はモリブデン系の材料からなる基礎材料を用いた壁（３）を有するるつぼであって、
前記壁（３）の外側面（６）又は前記壁（３）内に、あるいは、前記壁（３）の外側面及び前記壁（３）内に、前記基礎材料よりも炭素又は酸素あるいは炭素及び酸素に対する親和性の強い金属材料を用いたバリア層（２）が少なくとも部分的に設けられている、るつぼ。 - 前記バリア層（２）は、タンタル、ニオブ、又はチタン、あるいは、タンタル系、ニオブ系、又はチタン系の材料を用いて作成される、請求項１に記載のるつぼ。
- 前記バリア層（２）は、該バリア層（２）とは異なる材料を用いた外側層（５）により覆われる、請求項１又は２に記載のるつぼ。
- 前記外側層（５）に前記るつぼの前記基礎材料を用いてある、請求項３に記載のるつぼ 。
- 前記バリア層（２）は、前記壁（３）の外側１／３に設けられる、請求項１〜４のいずれか１項に記載のるつぼ。
- 前記バリア層（２）は、９０％以上の相対密度をもつ、請求項１〜５のいずれか１項に記載のるつぼ。
- 前記バリア層（２）は、９５％以上の相対密度をもつ、請求項１〜５のいずれか１項に記載のるつぼ。
- 前記バリア層（２）は、９９％以上の相対密度をもつ、請求項１〜５のいずれか１項に 記載のるつぼ。
- 前記バリア層（２）は、２５μｍ〜５００μｍの厚さをもつ、請求項１〜８のいずれか１項に記載のるつぼ。
- 前記バリア層（２）は、１００μｍ〜３００μｍの厚さをもつ、請求項１〜８のいずれ か１項に記載のるつぼ。
- 前記バリア層（２）は、１７５μｍ〜２２５μｍの厚さをもつ、請求項１〜８のいずれ か１項に記載のるつぼ。
- 前記バリア層（２）は、スラリープロセスにより作成された層として設けられる、請求 項１〜１１のいずれか１項に記載のるつぼ。
- 前記バリア層（２）は、溶射層として設けられる、請求項１〜１１のいずれか１項に記載のるつぼ。
- 前記バリア層（２）は、コールドガススプレーにより作成された層として設けられる、 請求項１３に記載のるつぼ。
- 前記バリア層（２）は、前記基礎材料よりも炭素又は酸素あるいは炭素及び酸素に対する親和性の強い金属材料を少なくとも９０重量％含む、請求項１〜１４のいずれか１項に記載のるつぼ。
- 単結晶サファイア又は溶融石英を生成するためのるつぼとして請求項１〜１５のいずれか１項に記載のるつぼ（１）を使用する使用方法。
- 高温用途のるつぼ（１）を製造する方法であって、
耐熱金属粉末を加圧及び焼結して、又は成形して、あるいは、加圧、焼結及び成形して、耐熱金属の基礎材料を用いたブランク材（１０）を作成する工程と、
前記基礎材料よりも炭素又は酸素あるいは炭素及び酸素に対する親和性の強い金属材料を用いたバリア層（２）を、溶射により、又はスラリープロセスにより、前記ブランク材（１０）の外側面（６）に設ける工程とを含む、方法。 - 前記耐熱金属粉末が、モリブデン又はタングステン、これらの合金、又はこれらの粉末 混合物である、請求項１７に記載の方法。
- 前記溶射がコールドガススプレーである、請求項１７又は１８に記載の方法。
- 前記バリア層（２）の前記材料に、タンタル、ニオブ、又はチタン、あるいは、タンタル系、ニオブ系、又はチタン系の材料を使用する、請求項１７〜１９のいずれか１項に記載の方法。
- 前記バリア層（２）とは異なる材料を用いた外側層（５）を前記バリア層（２）に付加する、請求項１７〜２０のいずれか１項に記載の方法。
- 前記外側層（５）に前記るつぼ（１）の前記基礎材料を構成する材料を用いる、請求項 ２１に記載の方法。