JP2019108474A - ポリカーボネート樹脂用着色防止剤 - Google Patents
ポリカーボネート樹脂用着色防止剤 Download PDFInfo
- Publication number
- JP2019108474A JP2019108474A JP2017242473A JP2017242473A JP2019108474A JP 2019108474 A JP2019108474 A JP 2019108474A JP 2017242473 A JP2017242473 A JP 2017242473A JP 2017242473 A JP2017242473 A JP 2017242473A JP 2019108474 A JP2019108474 A JP 2019108474A
- Authority
- JP
- Japan
- Prior art keywords
- polycarbonate resin
- coloring inhibitor
- polycarbonate
- coloring
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
したがって、成形加工性に優れ、ポリカーボネート樹脂の着色を抑制するとともに、添加量が多い場合でも着色防止剤のブリードが少ないポリカーボネート樹脂用着色防止剤が求められている。
すなわち、本発明は下記の〔1〕〜〔3〕である。
〔1〕下記式(I)で表されるポリアルキレングリコール誘導体からなるポリカーボネート樹脂用着色防止剤。
RO(CH2CH(CH3)O)l/(CH2CH2O)mH ・・・式(I)
(lはオキシプロピレン基の平均付加モル数であって1〜40を示す。mはオキシエチレン基の平均付加モル数であって1〜20を示す。l/(l+m)は0.3〜0.9あり、m/(l+m)は0.1〜0.7である。オキシアルキレン基の付加状態は、ランダム状である。Rは炭素数12〜24のアルケニル基である。)
〔2〕ポリカーボネート樹脂100質量部に対して、前記〔1〕に記載のポリカーボネート樹脂用着色防止剤を0.01〜10.0質量部を配合してなるポリカーボネート樹脂組成物。
〔3〕前記〔2〕に記載のポリカーボネート樹脂組成物を成型してなる成形体。
本発明の一態様であるポリカーボネート樹脂用着色防止剤は、下記式(I)で示される化合物からなり、オキシプロピレン基及びオキシエチレン基の2種類のオキシアルキレン基と炭素鎖12〜24のアルケニル基を有している。
RO(CH2CH(CH3)O)l/(CH2CH2O)mH ・・・式(I)
(lはオキシプロピレン基の平均付加モル数であって1〜40を示す。mはオキシエチレン基の平均付加モル数であって1〜20を示す。l/(l+m)は0.3〜0.9あり、m/(l+m)は0.1〜0.7である。オキシアルキレン基の付加状態は、ランダム状である。Rは炭素数12〜24のアルケニル基である。)
具体的には例えば、ポリカーボネート樹脂と前記式(I)のポリカーボネート樹脂用着色防止剤、必要に応じて他の着色防止剤を、タンブラーやヘンシェルミキサ−等の各種混合機を用い予め混合した後、バンバリーミキサー、ロール、ブラベンダー、単軸混練押出機、二軸混練押出機、ニーダー等で溶融混練する方法が挙げられる。
また各成分を予め混合せずに、又は一部の成分のみ予め混合して、フィーダーを用いて押出機に供給し溶融混練して、ポリカーボネート樹脂組成物を製造してもよい。更には、一部の成分を予め混合し押出機に供給して溶融混練することで得られるポリカーボネート樹脂組成物をマスターバッチとし、再度、他の成分と混合し溶融混練することによってポリカーボネート樹脂組成物を製造することもできる。
[製造例1]
攪拌装置、温度計および圧力ゲージを備えた5リットル容のオートクレーブに、オレイルアルコール402.7g(1.50モル)、三フッ化ホウ素ジエチルエーテル錯体29.2gを入れ、系内を窒素ガスにて置換した後、プロピレンオキシド1910.8g(32.9モル)とエチレンオキシド603.5g(13.7モル)の混合物を、温度50℃で13.5時間かけて圧入し、さらに0.5時間反応を継続した。その後、オートクレーブより生成物を取り出し、水酸化ナトリウムで中和してpH6〜7とし、窒素をバブリングしながら110℃まで加温後、4kPa以下、110℃で2時間脱水を行った。さらに脱水後生成した塩を濾別し、表1の化合物A−1を得た。
製造例1と同様の手法により、l、mが表1に示した比率となるようにして合成を行い、化合物A’−1を得た。
オレイルアルコールを用いずに、エチレンオキシドとテトラヒドロフランの混合物を仕込み、製造例1と同様の手法により、オキシアルキレン基のモル比が表1に示した比率になるように合成を行い、化合物A’-2を得た。
[試験フィルムの作製]
ポリカーボネート樹脂(ACROS ORGANICS製)50gと製造例1で合成した化合物A0.5g(ポリカーボネート樹脂100質量部に対して1質量部)を1Lメスフラスコへ入れ、ジクロロメタンを標線まで加えた。得られた溶液を1時間ほど室温で放置しポリカーボネート樹脂および化合物Aを溶解させた後、この溶液を4mLホールピペットでシャーレ(直径:60mm)に入れ、30分間室温で乾燥させた。乾燥後、シャーレからポリカーボネート樹脂をはがし取ることにより、厚さ50μmのフィルムを得た。
得られたフィルムの黄色度(Y.I.)を分光測色計(LM−2500c、KONICAMINOLTA製)により3回測定し、その平均値をフィルムのY.I.とした。
得られたフィルムの濁り度(Haze)をHazeMeter(NDH 4000、NUPPON DENSHOKU製)により3回測定し、その平均値をフィルムのHazeとした。
得られたフィルムをステンレス丸棒(Φ0.1mm×100mm)の側面に沿って180度折り曲げる作業を繰り返し行い、50回ごとにフィルムのひび割れの有無を確認した。例えば、折り曲げ50回でひび割れが確認されず、100回でひび割れが確認された場合は、成型加工性の評価は100(回数)とする。3回測定し、その平均値をフィルムの成型加工性(回数)とした。
得られたフィルムを、温度50℃で1日放置した後、目視で表面状態の観察をした。その後、さらに10日放置し表面状態を同様に観察した。
○:浸み出しなし、△:わずかに浸み出しあり、×:浸み出しあり
実施例1と同様の方法で、化合物A’−1及びA’−2を用いてキャストフィルムを作製して、Y.I.の測定、Hazeの測定、成形加工性の評価、ブリード性の評価を行った。結果を表2に示す。
Claims (3)
- 下記一般式(I)で表されるポリアルキレングリコール誘導体からなるポリカーボネート樹脂用着色防止剤。
RO(CH2CH(CH3)O)l/(CH2CH2O)mH ・・・式(I)
(lはオキシプロピレン基の平均付加モル数であって1〜40を示す。mはオキシエチレン基の平均付加モル数であって1〜20を示す。l/(l+m)は0.3〜0.9あり、m/(l+m)は0.1〜0.7である。オキシアルキレン基の付加状態は、ランダム状である。Rは炭素数12〜24のアルケニル基である。) - ポリカーボネート樹脂100質量部に対して、請求項1に記載のポリカーボネート樹脂用着色防止剤を0.01〜10.0質量部を配合してなるポリカーボネート樹脂組成物。
- 請求項2に記載のポリカーボネート樹脂組成物を成型してなる成形体。