JP2019022987A - 多層熱回復物品、ワイヤスプライス及びワイヤハーネス、並びに多層熱回復物品用接着剤の製造方法 - Google Patents
多層熱回復物品、ワイヤスプライス及びワイヤハーネス、並びに多層熱回復物品用接着剤の製造方法 Download PDFInfo
- Publication number
- JP2019022987A JP2019022987A JP2018166438A JP2018166438A JP2019022987A JP 2019022987 A JP2019022987 A JP 2019022987A JP 2018166438 A JP2018166438 A JP 2018166438A JP 2018166438 A JP2018166438 A JP 2018166438A JP 2019022987 A JP2019022987 A JP 2019022987A
- Authority
- JP
- Japan
- Prior art keywords
- adhesive
- resin composition
- heat recovery
- multilayer heat
- base material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】本発明の一態様に係る多層熱回復物品は、円筒状の基材層と、この基材層の内周面に積層される接着剤層とを備える多層熱回復物品であって、上記接着剤層が、ポリアミドを主成分とする樹脂組成物で形成され、上記樹脂組成物が電離性放射線の照射により架橋され、上記接着剤層の150℃での剪断粘度が、剪断速度0.01s−1で300Pa・s以上であり、剪断速度100s−1で200Pa・s以下である。
【選択図】図1
Description
本発明の一実施形態に係る多層熱回復物品は、円筒状の基材層と、この基材層の内周面に積層される接着剤層とを備える多層熱回復物品であって、上記接着剤層が、ポリアミドを主成分とし無機フィラーを実質的に含まない樹脂組成物で形成され、上記樹脂組成物が電離性放射線の照射により架橋され、上記接着剤層の150℃での剪断粘度が、剪断速度0.01s−1で300Pa・s以上であり、剪断速度100s−1で200Pa・s以下である。
以下、本発明の各実施形態について図面を参照しつつ詳説する。
図1〜図3の多層熱回復物品1は、例えば絶縁電線同士の接続部分、配線の端末、金属管等の保護、絶縁、防水、防食等のための被覆として使用される。この多層熱回復物品1は、円筒状の基材層10と、この基材層10の内周面に積層される接着剤層11とを備える。
基材層10は、加熱されることで縮径するチューブとして形成される。基材層10は、ポリエチレン、ポリエステル、ポリアミド又はフッ素樹脂を含有するとよい。これらの樹脂は、単独で使用しても、複数を併用してもよい。基材層10は、例示した樹脂を含有することで、適切な熱収縮性を備えることができ、また例示した樹脂が安価に入手できるため製造コストを抑制できる。
酸化防止剤としては、例えばフェノール系化合物、アミン系化合物、ヒンダードアミン系化合物、ヒンダードフェノール系化合物、サリチル酸誘導体、ベンゾフェノン系化合物、ベンゾトリアゾール系化合物等が挙げられ、特に架橋抑制効果に優れたヒンダードアミン系化合物が好適に使用される。これら酸化防止剤を用いることにより、耐銅害性をさらに向上できる。なお、酸化防止剤としては、上述した以外に硫黄系化合物及び亜リン酸エステル系化合物等を単独又は併用で用いることができる。
酸化防止剤として用いるフェノール系化合物としては、ペンタエリスリトールテトラキス[3−3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオネート]、テトラキス−[メチレン−3−(3′5′−ジ−tert−ブチル−4′−ヒドロキシフェニル)プロピオネート]メタン、トリエチレングリコール−ビス[3−(3−tert−ブチル−5−メチル−4−ヒドロキシフェニル)プロピオネート]、6−(4−ヒドロキシ−3,5−ジ−tert−ブチル・アニリノ)−2,4−ビス・オクチル−チオ−1,3,5−トリアジン等を挙げることができる。
酸化防止剤として用いるアミン系化合物としては、4,4’(α、αージメチルベンジル)ジフェニルアミン、2,2,4−トリメチル−1,2−ジヒドロキノリンの重合物、6−エトキシ−2,2,4−トリメチル−1,2−ジヒドロキノリン、N−(1,3−ジメチルブチル)−N’−フェニル−1,4−フェニレンジアミン、N−イソプロピル−N’−フェニル−1,4−フェニレンジアミン等を挙げることができる。
難燃剤としては、塩素化パラフィン、塩素化ポリエチレン、塩素化ポリフェニル、パークロルペンタシクロデカン等の塩素系難燃剤、1,2−ビス(2,3,4,5,6−ペンタブロモフェニル)エタン、エチレンビスペンタブロモベンゼン、エチレンビスペンタブロモジフェニル、テトラブロモエタン、テトラブロモビスフェノールA、ヘキサブロモベンゼン、デカブロモビフェニルエーテル、テトラブロモ無水フタール酸、ポリジブロモフェニレンオキサイド、ヘキサブロモシクロデカン、臭化アンモニウム等の臭素系難燃剤、トリアリルホスフェート、アルキルアリルホスフェート、アルキルホスフェート、ジメチルホスフォネート、ホスフォリネート、ハロゲン化ホスフォリネートエステル、トリメチルホスフェート、トリブチルホスフェート、トリオクチルホスフェート、トリブトキシエチルホスフェート、オクチルジフェニルホスフェート、トリクレジルホスフェート、クレジルフェニルホスフェート、トリフェニルホスフェート、トリス(クロロエチル)ホスフェート、トリス(2−クロロプロピル)ホスフェート、トリス(2,3−ジクロロプロピル)ホスフェート、トリス(2,3−ジブロモプロピル)ホスフェート、トリス(ブロモクロロプロピル)ホスフェート、ビス(2,3ジブロモプロピル)2,3ジクロロプロピルホスフェート、ビス(クロロプロピル)モノオクチルホスフェート、ポリホスホネート、ポリホスフェート、芳香族ポリホスフェート、ジブロモネオペンチルグリコール、トリス(ジエチルホスフィン酸)アルミ等のリン酸エステル又はリン化合物、ホスホネート型ポリオール、ホスフェート型ポリオール、ハロゲン元素含有ポリオール等のポリオール類、メラミンシアヌレート、トリアジン、イソシアヌレート、尿素、グアニジン等の窒素化合物、シリコーン系ポリマー、フェロセン、フマール酸、マレイン酸等のその他の化合物などが挙げられる。これらの中でも、臭素系難燃剤、塩素系難燃剤等のハロゲン系難燃剤が好ましい。臭素系難燃剤及び塩素系難燃剤は単独で使用しても2種以上を併用してもよい。
銅害防止剤としては、3−(N−サリチロイル)アミノ−1,2,4−トリアゾール、デカメチレンジカルボン酸ジサリチロイルヒドラジド、2,3−ビス[3−(3,5−ジ−tert−ブチル−4−ヒドロキシフェニル)プロピオニル]プロピオノヒドラジド等を挙げることができる。基材層10に銅害防止剤を含有させることによって、銅害を防止することができる。基材層10及び接着剤層11に酸化防止剤を含有させる場合は、基材層10に銅害防止剤を含有させなくとも構わない。このように、高価な銅害防止剤を含有させないことによって、多層熱回復物品1の製造コストを抑えることができる。
接着剤層11は、被着部分と基材層10との密着性を高め、防水性等を向上させるためのものである。接着剤層11は、ポリアミドを主成分とし無機フィラーを実質的に含まない樹脂組成物で形成される。この接着剤層11は、電離性放射線の照射により架橋されている。また、この接着剤層11を形成する樹脂組成物は、酸化防止剤を含むことが好ましい。また、接着剤層11を形成する樹脂組成物は、超低密度ポリエチレン又はエチレン共重合体を含んでもよい。さらに、接着剤層11を形成する樹脂組成物は、必要に応じて他の添加剤を添加してもよい。そのような添加剤としては、例えば酸化防止剤、銅害防止剤、粘度特性改良剤、劣化抑制剤、難燃剤、滑材、着色剤、熱安定剤、紫外線吸収剤、粘着剤等が挙げられる。
上記接着剤層11を形成する樹脂組成物は、少なくとも主成分であるポリアミドが電離性放射線の照射により架橋されている。架橋されたポリアミドはネットワークを形成し、接着剤層11に、上述のように剪断速度が大きいとき剪断粘度が小さくなるチキソトロピーを付与する。
原料ポリアミドのMFRが上記下限未満の場合、架橋しても流動性が大き過ぎるため、接着剤層11が基材層10から流出するおそれや、接着剤層11を安定して押出成形するのが困難となるおそれがある。原料ポリアミドのMFRが上記上限を超える場合、当該多層熱回復物品1を使用するときの基材層10の熱収縮時の接着剤層11の流動性が不足し、当該多層熱回復物品1の被着体への密着が不十分となるおそれがある。ここで、MFRは、樹脂の流動性を表す指標である。なお、MFRとは、JIS−K6760(1997)で規定された押出し形プラストメータを用いて測定される値を意味し、ポリアミドについては温度120℃、荷重2.16kgの条件で測定される値であり、他の樹脂については、温度190℃、荷重2.16kgの条件で測定される値である。
接着剤層11を形成する樹脂組成物は、樹脂成分として、上記架橋により得られるチキソトロピーを向上させるために、超低密度ポリエチレン(VLDPE)を含んでもよい。超低密度ポリエチレンは比重が0.91g/cm3以下のポリエチレンである。
上記超低密度ポリエチレンの含有量が上記下限未満の場合、接着剤層11のチキソトロピー向上効果が不十分となるおそれがある。また、上記超低密度ポリエチレンの含有量が上記上限を超える場合、接着剤層11の粘度が高くなり過ぎて当該多層熱回復物品1の被着体への密着が不十分となるおそれがある。
接着剤層11を形成する樹脂組成物は、樹脂成分として、上記架橋により得られるチキソトロピーを向上させるために、エチレン共重合体を含んでも良い。エチレン共重合体の具体例としては、エチレン−酢酸ビニル共重合体(EVA)、エチレン−ブテン共重合体(EBA)、エチレン−オクテン共重合体、エチレン−エチルアクリレート共重合体、エチレン−ブチルアクリレート共重合体などが挙げられる。エチレン共重合体として特にエチレン−酢酸ビニル共重合体が好ましい。
上記エチレン共重合体の中で特に好ましい、エチレン−酢酸ビニル共重合体のMFRの下限としては、1g/10分が好ましく、5g/10分がより好ましい。一方、上記エチレン−酢酸ビニル共重合体のMFRの上限としては、2,000g/10分が好ましく、1,000g/10分がより好ましく、500g/10分がさらに好ましい。上記エチレン−酢酸ビニル共重合体のMFRが上記下限未満の場合、樹脂組成物の加熱時の流動性が不十分となるおそれがある。また、上記エチレン−酢酸ビニル共重合体のMFRが上記上限を超える場合、樹脂組成物の粘度が低くなりやすく、大きな電離性放射線の吸収線量が必要となり不経済となるおそれがある。
接着剤層11の酸化防止剤には基材層10と同様の酸化防止剤を用いることができる。
酸化防止剤には、電離性放射線の照射による樹脂組成物の架橋を抑制する作用もある。この接着剤層11における酸化防止剤の含有量の下限としては、上記樹組成物中の樹脂成分100質量部に対して1質量部が好ましく、2質量部がより好ましい。一方、酸化防止剤の含有量の上限としては、上記樹組成物中の樹脂成分100質量部に対して20質量部が好ましく、15質量部がより好ましい。酸化防止剤の含有量が上記下限未満であると、接着剤層11及び基材層10が酸化し易くなり、多層熱回復物品1が劣化するおそれや、電離性放射線の照射により材料深部まで一様な架橋をすることが困難となるおそれがある。
また、酸化防止剤の含有量が上記上限を超えても、接着剤層11及び基材層10の酸化防止効果の向上が得られず、架橋によるチキソトロピーの付与を阻害するおそれがある。
銅害防止剤としては、基材層10の銅害防止剤と同様のものを挙げることができる。基材層10及び接着剤層11に酸化防止剤を含有させる場合は、接着剤層11に銅害防止剤を含有させなくてもよい。
劣化抑制剤は、当該多層熱回復物品1が被着される被着体の劣化を抑制するためのものである。典型的には、劣化抑制剤は、絶縁電線の被覆層あるいは当該多層熱回復物品1の接着剤層11に含まれる塩基性成分に起因する絶縁層の割れの発生を抑制するためのものである。この劣化抑制剤は、粘度特性改良剤としての役割をも果たし得る。劣化抑制剤としては、被着体が劣化する要因に応じて選択すればよいが、例えば塩基性成分に起因する被着体の劣化を抑制する場合、塩基性成分による脱塩酸反応が生じることを抑制する化合物、又は塩酸反応により生成した塩化水素、塩化物イオン等を捕捉もしくは中和することができる化合物を使用することができる。このような劣化抑制剤としては、例えば活性白土、ハイドロタルサイト、リンを有する酸化防止剤(酸価10mgKOH/g以上)等を挙げることができる。これらの劣化抑制剤を接着剤層11に含有させることで、例えば窒素含有化合物を吸着し、アニオンを取り込み、脱塩酸反応により生じた塩化水素を捕捉する等して接着剤層11の塩基性成分に起因する被着体の劣化を抑制できる。
多層熱回復物品1は、例えば以下の工程により製造することができる。
(1)基材層10を形成するための基材層樹脂組成物を調製する工程
(2)接着剤層11を形成するための接着剤樹脂組成物を製造する工程
(3)基材層樹脂組成物及び接着剤樹脂組成物を溶融押出成機を用いて押出成形することで多層押出成形品を形成する工程
(4)多層押出成形品を拡径させて多層熱回復物品1とする工程
基材層樹脂組成物は、樹脂成分、必要に応じて添加剤を例えば溶融混合機により混合することで調製できる。溶融混合機としては、公知のもの、例えばオープンロール、バンバリーミキサー、加圧ニーダー、単軸混合機、多軸混合機等を使用できる。
接着剤製造工程は、接着剤樹脂組成物を調整する工程と、接着剤樹脂組成物に電離性放射線を照射する工程とを備える。
接着剤樹脂組成物は、ポリアミドを主成分として含む。また、接着剤樹脂組成物は、樹脂成分として、上記ポリアミドに加えて、超低密度ポリエチレン又はエチレン共重合体を含み得る。そして、この接着剤樹脂組成物は、上記樹脂成分と酸化防止剤及び必要に応じた添加剤とを例えば溶融混合機により混合することで調製できる。溶融混合機としては、基材層樹脂組成物を調製する場合と同様のものを使用できる。
接着剤樹脂組成物に照射する電離性放射線としては、例えば電子線、ガンマ線等が挙げられるが、設備の準備が比較的容易な電子線が好適である。
多層押出成形品は、基材層樹脂組成物と接着剤樹脂組成物とを公知の溶融押出成形機を用いて、基材層樹脂組成物及び接着剤樹脂組成物を同時に押出成形することで、基材層10に対応する外層の内周面に接着剤層11に対応する内層が積層されたものとして形成される。多層押出成形品は、基材層樹脂組成物の構成材料を架橋することにより、耐熱性を向上させてもよい。架橋方法としては、例えば電離性放射線の照射による架橋、化学架橋、熱架橋等の方法が挙げられる。
多層押出成形品の拡径は、多層押出成形品を融点以上の温度に加熱した状態で内部に圧縮空気を導入する等の方法により所定の内径となるように膨張させた後、冷却して形状を固定させることで行われる。このような多層押出成形品の拡径は、例えば多層押出成形品の内径が2倍〜4倍程度となるように行われる。このようにして多層押出成形品を拡径させて形状固定したものが当該多層熱回復物品1となる。
当該多層熱回復物品1は、接着剤層11に電離性放射線により架橋されたポリアミドを含むので、接着剤層11が、基材層10の熱収縮の前後には流動せず、基材層10の熱収縮中には十分な流動性を呈して被着体に密着できる。
当該多層熱回復物品1は、例えば導体を被覆する絶縁層がポリエチレン(PE)であるPE電線又はPEケーブル、絶縁層がポリビニルクロライド(PVC)であるPVC電線又はPVCケーブル等のワイヤの保護、絶縁、防水、防食等のために使用することができる。具体的には、多層熱回復物品1は、ワイヤスプライス及びワイヤハーネスに適用することができる。
ワイヤ20は、PE電線若しくはPVC電線等の絶縁電線又はケーブルである。ワイヤ20としては、例えば最外層に位置する絶縁層がポリビニルクロライドを主成分とするものが使用される。絶縁層におけるポリビニルクロライドの含有量は、例えば50質量%以上95質量%以下である。このようなワイヤスプライスにおいて、チューブ1aは、接続部分の保護、絶縁、防水、防食等に寄与することができる。
今回開示された実施の形態はすべての点で例示であって制限的なものではないと考えられるべきである。本発明の範囲は、上記実施形態の構成に限定されるものではなく、特許請求の範囲によって示され、特許請求の範囲と均等の意味及び範囲内での全ての変更が含まれることが意図される。
剪断粘度は、回転式レオメーター(アントンパール株式会社の「MCR302」)を用い、治具PP−12を使用して温度150℃で測定した。剪断粘度は、剪断速度0.001s−1から1000s−1まで、剪断速度を変えて測定した。なお、剪断速度は、回転子の形状及び回転速度により定められ、回転式レオメーターが自動的に設定するようになっている。
垂れ落ち性試験の方法としては、まず、厚さ1mmのシート状とした接着剤を5mm×40mmに切断し、質量を測定する。この切断したシート状接着剤Aを、図8に示すように、四枚のガラス板Pにより四方から挟み込む。次に、この試料を150℃の恒温槽内で中空に鉛直方向に保持し、24時間放置した後にガラス板から接着剤Aが垂れ落ちているかどうかを確認し、さらに72時間後、つまり合計96時間放置した後にガラス板から垂れ落ちた接着剤Aの質量を計測して垂れ落ち率(元のシート状接着剤の質量に対する垂れ落ちた接着剤質量の割合)を算出する。
防水性試験は、上記各接着剤を用いた多層熱回復物品を使用して作製したワイヤスプライスを水中に入れ、多層熱回復物品におけるPVC電線1本が延出する一方の端から200kPaの空気を30秒間吹き込み、PVC電線が4本延出する他方の端からバブルが発生するかを確認することで行った。防水性試験では、バブルが発生しなかったものを「A」、バブルが発生したものを「B」として評価した。
このようにして作製したワイヤスプライスでは、多層熱回復物品の一方の端からPVC電線が1本延出し、他方の端からPVC電線が4本延出している。
1a チューブ
10,10A 基材層
11,11A 接着剤層
2 ワイヤスプライス
20 ワイヤ
21 導体線
3 ワイヤハーネス
30 ワイヤ
31 多ピンコネクタ
A シート状接着剤
P ガラス板
Claims (9)
- 円筒状の基材層と、この基材層の内周面に積層される接着剤層とを備える多層熱回復物品であって、
上記接着剤層が、ポリアミドを主成分とする樹脂組成物で形成され、
上記樹脂組成物が電離性放射線の照射により架橋され、
上記接着剤層の150℃での剪断粘度が、剪断速度0.01s−1で300Pa・s以上であり、剪断速度100s−1で200Pa・s以下である多層熱回復物品。 - 上記樹脂組成物が、超低密度ポリエチレンを20質量%以上含有する請求項1に記載の多層熱回復物品。
- 上記樹脂組成物が、エチレン共重合体を20質量%以上含有する請求項1又は請求項2に記載の多層熱回復物品。
- 上記樹脂組成物が、難燃剤をさらに含有する請求項1、請求項2又は請求項3に記載の多層熱回復物品。
- 導体及びその外側に積層される絶縁層を有するワイヤを複数本と、
上記複数本のワイヤの導体同士が接続された部分に被着されたチューブとを備えるワイヤスプライスであって、
上記チューブが、請求項1から請求項4のいずれか1項に記載の多層熱回復物品を熱収縮させたものであるワイヤスプライス。 - 導体及びその外側に積層される絶縁層を有するワイヤを複数本と、
上記複数本のワイヤに被着されたチューブとを備えるワイヤハーネスであって、
上記チューブが、請求項1から請求項4のいずれか1項に記載の多層熱回復物品を熱収縮させたものであるワイヤハーネス。 - ポリアミドを主成分とする樹脂組成物で形成される多層熱回復物品用接着剤の製造方法であって、
上記樹脂組成物に電離性放射線を照射する工程を備え、
上記接着剤の150℃での剪断粘度が、剪断速度0.01s−1で300Pa・s以上であり、剪断速度100s−1で200Pa・s以下となるよう上記電離性放射線の照射量を調節する多層熱回復物品用接着剤の製造方法。 - 上記樹脂組成物の電離性放射線吸収線量が、90kJ/kg以上である請求項7に記載の多層熱回復物品用接着剤の製造方法。
- 上記電離性放射線が電子線である請求項7又は請求項8に記載の多層熱回復物品用接着剤の製造方法。