JP2017171800A - ポリエチレンテレフタレート樹脂組成物 - Google Patents
ポリエチレンテレフタレート樹脂組成物 Download PDFInfo
- Publication number
- JP2017171800A JP2017171800A JP2016060482A JP2016060482A JP2017171800A JP 2017171800 A JP2017171800 A JP 2017171800A JP 2016060482 A JP2016060482 A JP 2016060482A JP 2016060482 A JP2016060482 A JP 2016060482A JP 2017171800 A JP2017171800 A JP 2017171800A
- Authority
- JP
- Japan
- Prior art keywords
- polyethylene terephthalate
- terephthalate resin
- liquid crystal
- resin composition
- wholly aromatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ポリエチレンテレフタレート樹脂100重量部、および全芳香族液晶ポリエステル0.1〜40重量部を含有するポリエチレンテレフタレート樹脂組成物であって、該全芳香族液晶ポリエステルは、式[I]で示される繰返し単位を全繰返し単位中25モル%以上含み、かつ、結晶融解温度が270℃以下である、ポリエチレンテレフタレート樹脂組成物を提供する。
【選択図】なし
Description
0.4≦p/q≦2.0
2≦r≦15、および
2≦s≦15]
式[IV]中のAr2が、
PET :ポリエチレンテレフタレート
LCP :全芳香族液晶ポリエステル
BON6:6−ヒドロキシ−2−ナフトエ酸
POB :パラヒドロキシ安息香酸
HQ :ハイドロキノン
TPA :テレフタル酸
実施例において、ポリエチレンテレフタレート樹脂として以下のものを使用した。
PET:ユニチカ社製NEH−2070
トルクメーター付き攪拌装置および留出管を備えた2Lの反応容器にBON6、POB、HQおよびTPAを、下記に示す組成比で、総量5モルとなるように仕込み、次いで酢酸カリウム0.05g(全モノマーに対し67モルppm)および全モノマーの水酸基量(モル)に対して1.025倍モルの無水酢酸を仕込み、次の条件で脱酢酸重合を行った。
POB :276.23g(40モル部)
BON6:376.34g(40モル部)
HQ :55.05g(10モル部)
TPA :83.06g(10モル部)
ポリエチレンテレフタレート樹脂100重量部に対して、合成例1で得られたLCPを表1で示す比率でドライ混合し、2軸押出機((株)池貝製、PCM−30)を用いて、280℃のシリンダ温度にてコンパウンドした。合成例1で得られたLCPはポリエチレンテレフタレート樹脂に容易に相溶した。このようにしてLCPが分散されたポリエチレンテレフタレート樹脂組成物のペレットを得た。
INSTRON5567(インストロンジャパン カンパニイリミテッド社製万能試験機)を用いて、ASTM D638に準じて130℃における引張伸び率を測定した。
前記の成形片を試験片とし、差圧ガス・蒸気透過率測定装置(GTR−30XA2、G2700T・F)を用いて、JIS K7126−1に準拠する下記の条件下で気体透過量を測定し、気体透過係数を算出した。
検出器:ガスクロマトグラフ[熱伝導度検出器(TCD)]
試験差圧:1atm
試験気体:酸素ガス
試験条件:20±2℃、65±5%Rh
透過面積:15.2×10−4m2 (φ4.4×10−2m)
ポリエチレンテレフタレート樹脂は、実施例1と同様の成形を行い、ガスバリア性試験を行った。結果を表1に示す。
ポリエチレンテレフタレート樹脂、LCPを表1に示すような比率に変更したこと以外は、実施例1と同様にしてポリエチレンテレフタレート樹脂組成物のペレットを取得し、ガスバリア性試験を行った。結果を表1に示す。
また、本発明のポリエチレンテレフタレート樹脂組成物は、引張伸び率に優れるため、ブロー成形法による樹脂の成形が可能である。
これに対し、比較例1および2は、引張伸び率がポリエチレンテレフタレート樹脂単独と比較して劣ったものであった。
Claims (6)
- 式[I]〜[IV]で示される繰返し単位の組成比は以下の式を満たす、請求項2に記載のポリエチレンテレフタレート樹脂組成物:
35≦p≦48、
35≦q≦48、
2≦r≦15、および
2≦s≦15。 - 請求項1〜4のいずれかに記載のポリエチレンテレフタレート樹脂組成物から構成される成形品。
- ブロー成形品である、請求項5に記載の成形品。