JP2017083737A - 光伝送体及びその製造方法 - Google Patents
光伝送体及びその製造方法 Download PDFInfo
- Publication number
- JP2017083737A JP2017083737A JP2015213791A JP2015213791A JP2017083737A JP 2017083737 A JP2017083737 A JP 2017083737A JP 2015213791 A JP2015213791 A JP 2015213791A JP 2015213791 A JP2015213791 A JP 2015213791A JP 2017083737 A JP2017083737 A JP 2017083737A
- Authority
- JP
- Japan
- Prior art keywords
- optical transmission
- core material
- transmission body
- shape
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
また、上記コア材の曲げ剛性が、上記クラッド材の曲げ剛性よりも大きいことが考えられる。
また、上記光伝送体が、上記コア材の形状保持力で所定の屈曲形状に保持されていることが考えられる。
また、上記コア材が、熱硬化性成分と、光硬化性成分とを含んでいることが考えられる。
また、上記コア材が、少なくとも、ポリマーポリオール、ヒドロキシ基反応性多官能化合物、ウレタン(メタ)アクリレート、及び、光重合硬化剤が硬化したものを有していることが考えられる。
また、本発明による光伝送体の製造方法は、チューブ状クラッド材と、該クラッド材に収容され該クラッド材よりも屈折率の高いコア材とからなる光伝送体の製造方法において、上記チューブ状クラッド材の内部に、流動状態のコア材材料を充填し、加熱によって上記コア材材料を硬化し、非流動化した上記コア材を有する光伝送体を所定の形状に仮固定し、光を照射することによって上記コア材材料を更に硬化することで、上記コア材の曲げ剛性が、上記クラッド材の曲げ剛性よりも大きいものとし、光伝送体を所定の形状に保持するものである。
E=(4L3/3πd4)×(F/Y)
E:曲げ弾性率(MPa)
L:支点間距離(mm)
d:試験片の外径(mm)
F/Y:荷重−たわみ曲線の直線部分の勾配(N/mm)
コア材3を構成する材料としては、ポリマーポリオールとしてポリオキシプロピレントリオールとポリオキシプロピレンジオールを使用し、ヒドロキシ基反応性多官能化合物としてヘキサメチレンジイソシアネートを使用し、ウレタンアクリレートとしてウレタンアクリレートオリゴマーを使用し、光重合硬化剤としてヒドロキシアルキルフェノン系光重合材を使用する。ここで、各コア材材料の比率は、重量比で、ポリマーポリオール:ヒドロキシ基反応性多官能化合物:ウレタンアクリレート:光重合硬化剤=100:100:95:5とした。又、クラッド材2を構成する材料としては、テトラフルオロエチレン−ヘキサフルオロプロピレン−ビニリデンフルオライド共重合体を使用する。なお、微粒子は、コア材、クラッド材ともに使用していない。上記のクラッド材2の材料を押出成形し、外径3.0mm、肉厚0.2mmの円筒チューブ形状のクラッド材2を得る。このクラッド材2を直径400mmのボビンに巻回した状態で、クラッド材2内に上記コア材3を構成する材料を混合して充填し、100℃で加熱してコア材3に1段階目の硬化処理を施す。このようにして、内側からコア材3、クラッド材2が形成された光伝送体1の形状になる。更に、この両端を切断して150mmの長さとした後、光伝送体1の長さ方向中央部に、光伝送体直径の10倍の直径を有すマンドレルを配置して180度に曲げ、その状態で高圧水銀灯により10秒間光を照射し、コア材3の2段階目の硬化処理を施す。このようにして、所定の屈曲形状に保持された光伝送体1を得た。
上記実施例1において、クラッド材2をテトラフルオロエチレン−ヘキサフルオロプロピレン−ビニリデンフルオライド共重合体のうち高融点品とした他は、上記実施例1と同様にして光伝送体2を得た。
上記実施例1において、クラッド材2の外径を5.0mm、肉厚0.25mmとした他は、上記実施例1と同様にして光伝送体1を得た。
上記実施例1において、クラッド材2を構成する材料として、FEPを使用した他は、上記実施例1と同様にして光伝送体1を得た。
上記実施例1において、各コア材材料の比率を、重量比で、ポリマーポリオール:ヒドロキシ基反応性多官能化合物:ウレタンアクリレート:光重合硬化剤=120:120:38:2とした他は、上記実施例1と同様にして光伝送体1を得た。
1段階目の熱硬化処理の各光伝送体を150mmの長さに切断した後、光伝送体1の長さ方向中央部に、光伝送体の直径の10倍の直径を有すマンドレルを配置して180度に曲げ、その状態で高圧水銀灯により10秒間光を照射し、コア材3の2段階目の硬化処理を施す。2段階目硬化後、光伝送体の両端の間隔(幅)を測定する。その間隔がマンドレルの直径の2倍以内であった場合を合格とする。具体的には、実施例1,2及び比較例1〜3については、直径30mmのマンドレルを使用して、光伝送体両端の間隔60mm以内を合格とし、実施例3については、直径50mmのマンドレルを使用して、光伝送体両端の間隔100mm以内を合格とする。
実施例2及び比較例3の光伝送体による試料について、150mmの長さのものを直線状態に配設して、端面における照度の測定を行った。光源としての緑色LEDを原点とし、光源と反対側の端面から出射される光を照度計で測定して比較検証をした。この際、光伝送体側面からの光を拾わないよう、光源と反対側の端面近傍の側面を覆うようにして、光伝送体に発泡樹脂シートを取り付けた。
併せて、光伝送体全体としての曲げ弾性率を測定した。曲げ弾性率は、上記実施例1〜3及び比較例1〜3と同様にして作成し、長さ150mmの直線形状で2段階目硬化を行った光伝送体を用い、JIS−K6911−1995に準拠した3点曲げ試験に基づき測定を行い、次式によって計算した。
E=(4L3/3πd4)×(F/Y)
E:曲げ弾性率(MPa)
L:支点間距離(mm)
d:試験片の外径(mm)
F/Y:荷重−たわみ曲線の直線部分の勾配(N/mm)
なお、支点間距離は50mm、ヘッドスピードは2mm/minとした。
2 クラッド材
3 コア材
5 光源
Claims (6)
- チューブ状クラッド材と、該クラッド材に収容され該クラッド材よりも屈折率の高いコア材とからなる光伝送体において、上記コア材の曲げ剛性が、上記クラッド材の曲げ剛性の1/2よりも大きいことを特徴とする光伝送体。
- 上記コア材の曲げ剛性が、上記クラッド材の曲げ剛性よりも大きいことを特徴とする請求項1記載の光伝送体。
- 上記光伝送体が、上記コア材の形状保持力で所定の屈曲形状に保持されていることを特徴とする請求項2記載の光伝送体。
- 上記コア材が、熱硬化性成分と、光硬化性成分とを含んでいることを特徴とする請求項3記載の光伝送体。
- 上記コア材が、少なくとも、ポリマーポリオール、ヒドロキシ基反応性多官能化合物、ウレタン(メタ)アクリレート、及び、光重合硬化剤が硬化したものを有していることを特徴とする請求項4記載の光伝送体。
- チューブ状クラッド材と、該クラッド材に収容され該クラッド材よりも屈折率の高いコア材とからなる光伝送体の製造方法において、上記チューブ状クラッド材の内部に、流動状態のコア材材料を充填し、加熱によって上記コア材材料を硬化し、非流動化した上記コア材を有する光伝送体を所定の形状に仮固定し、光を照射することによって上記コア材材料を更に硬化することで、上記コア材の曲げ剛性が、上記クラッド材の曲げ剛性よりも大きいものとし、光伝送体を所定の形状に保持する光伝送体の製造方法。