JP2017080937A - ユニフォーム衣料用難燃防水性布帛 - Google Patents
ユニフォーム衣料用難燃防水性布帛 Download PDFInfo
- Publication number
- JP2017080937A JP2017080937A JP2015209418A JP2015209418A JP2017080937A JP 2017080937 A JP2017080937 A JP 2017080937A JP 2015209418 A JP2015209418 A JP 2015209418A JP 2015209418 A JP2015209418 A JP 2015209418A JP 2017080937 A JP2017080937 A JP 2017080937A
- Authority
- JP
- Japan
- Prior art keywords
- fabric
- flame
- flame retardant
- base fabric
- fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
また、本発明では、ビニロン繊維を構成するポリマーを必要に応じてアセタール化してもよく、こうすることで耐水性、耐熱水性の向上が期待できる。アセタール化は、通常、ポリマー内部、ポリマー間又はその両者において行い、このときのアセタール化度としては、10〜40モル%程度が好ましい。
難燃ビニロン繊維(ユニチカトレーディング社製「ミューロンFR」、LOI値35、単糸繊度1.5dtex、平均繊維長38mm)と綿繊維(単糸繊度1.7dtex、平均繊維長35mm)とを、ビニロン繊維75質量部、綿繊維25質量部の割合で混紡し、太さ30番手双糸の混紡糸を得た。この混紡糸を経緯糸に用い、エアージェット織機(石川製作所社製)にて綾組織の生機を製織した。製織後、生機を糊抜き、精練、シルケットし、さらに染色した後、巾出しを極力抑えながら仕上げ剤を使用せずに仕上げセットした。以上のようにして基布を得た。
張力を掛けて基布を仕上げセットしたこと、並びに基布及び樹脂層に張力を掛けてドライラミネーションしたこと以外は、実施例1と同様に行い、難燃防水性布帛を得た。
実施例1において、難燃剤をそれぞれ含有しない接着剤溶液及び樹脂層用溶液を用いたこと以外は、実施例1と同様に行い、布帛を得た。
接着層の厚みを45μmに代えて5μm(比較例2)、120μm(実施例3)としたこと以外は、実施例1と同様に行い、各々布帛を得た。
樹脂層におけるポリウレタン樹脂と難燃剤との含有比率(ポリウレタン樹脂:難燃剤)を、1:10に変更したこと以外は、実施例1と同様に行い、布帛を得た。
Claims (3)
- 基布、接着層及びラミネート層がこの順で積層されてなる難燃防水性布帛であって、前記基布は難燃ビニロン繊維とセルロース繊維とを混率(難燃ビニロン繊維/セルロース繊維)90/10〜10/90の割合で含有し、さらに前記接着層及びラミネート層は共に難燃剤を含有し、布帛全体として耐水圧が50kPa以上の範囲にあることを特徴とするユニフォーム衣料用難燃防水性布帛。
- 前記接着層及びラミネート層が共にポリカーボネート系ポリウレタン樹脂から構成されていることを特徴とする請求項1記載のユニフォーム衣料用難燃防水性布帛。
- 前記布帛全体の洗濯収縮率が5%以下であることを特徴とする請求項1又は2記載のユニフォーム衣料用難燃防水性布帛。