JP2017046930A - マルチピースソリッドゴルフボール - Google Patents
マルチピースソリッドゴルフボール Download PDFInfo
- Publication number
- JP2017046930A JP2017046930A JP2015172780A JP2015172780A JP2017046930A JP 2017046930 A JP2017046930 A JP 2017046930A JP 2015172780 A JP2015172780 A JP 2015172780A JP 2015172780 A JP2015172780 A JP 2015172780A JP 2017046930 A JP2017046930 A JP 2017046930A
- Authority
- JP
- Japan
- Prior art keywords
- golf ball
- core
- hardness
- kgf
- piece solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
なお、上記の「中上級者」とは、ヘッドスピード(HS)が大凡40〜50m/sであり、そのうち、中級者が40〜48m/s、上級者が42〜50m/sに相当する。
[1]ゴム製の内層及び外層からなる2層コアと、カバーとを有し、且つ、これらの間に少なくとも1層の中間層を介在させたマルチピースソリッドゴルフボールにおいて、上記内層コアの直径が30mm以上であり、外層コアの表面硬度から内層コアの中心硬度を引いた値がJIS−C硬度で25以上であり、内層コアに対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をA、2層コアに対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をBとするとき、A/B≦1.5の数式を満足すると共に、中間層の材料硬度がカバーの材料硬度よりも硬いことを特徴するマルチピースソリッドゴルフボール。
[2]コア硬度分布において、コア中心のJIS−C硬度を(Cc)、コア中心から5mmの位置のJIS−C硬度を(C5)、コア中心から10mmの位置のJIS−C硬度を(C10)、コア中心から15mmの位置のJIS−C硬度を(C15)、コア表面のJIS−C硬度を(Cs)とするとき、下記式(i)〜(v)
1≦(C10)−(Cc)≦15 ・・・・(i)
(C10)−(Cc)<(Cs)−(C10) ・・・・(ii)
18≦(Cs)−(C10) ・・・・(iii)
(Cs)≧80 ・・・・(iv)
(Cc)≧50 ・・・・(v)
の関係を満足する[1]記載のマルチピースソリッドゴルフボール。
[3]下記式(vi)を満足する[1]又は[2]記載のマルチピースソリッドゴルフボール。
1.5≦[(Cs)−(C10)/(C10)−(Cc)]≦4 ・・・・(vi)
[4]下記式(vii)を満足する[1]、[2]又は[3]記載のマルチピースソリッドゴルフボール。
25≦(Cs)−(Cc)≦45 ・・・・(vii)
[5]下記式(viii)を満足する[1]〜[4]のいずれか1項記載のマルチピースソリッドゴルフボール。
(C10)−(C5)≦(C5)−(Cc)≦(Cs)−(C15)≦(C15)−(C10)
・・・・(viii)
[6]コアに中間層を被覆した球体に対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をCとするとき、A/C≦1.9の数式を満足する[1]〜[5]のいずれか1項記載のマルチピースソリッドゴルフボール。
[7]ゴルフボールに対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をHとするとき、A/H≦2.0、及び、A−H≦2.5の数式を満足する[1]〜[6]のいずれか1項記載のマルチピースソリッドゴルフボール。
[8]ゴルフボールに6864N(700kgf)の荷重をかけたときに、平面に接するゴルフボールの面積である加圧面積(mm2)をPS7、ゴルフボールの直径に沿った断面の円の面積であって、ゴルフボール表面にディンプルが全くない場合の仮想平面積(mm2)をS、及びゴルフボールに対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をHとするとき、
PS7/S/H×100≧5.90(mm-1) ・・・・(ix)
を満足する[1]〜[7]のいずれか1項記載のマルチピースソリッドゴルフボール。
[9]ゴルフボールに1961N(200kgf)の荷重をかけたときに、平面に接するゴルフボールの面積である加圧面積(mm2)をPS2、ゴルフボールの直径に沿った断面の円の面積であって、ゴルフボール表面にディンプルが全くない場合の仮想平面積(mm2)をS、及びゴルフボールに対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をHとするとき、
PS2/S/H×100≧1.70(mm-1) ・・・・(x)
を満足する[1]〜[8]のいずれか1項記載のマルチピースソリッドゴルフボール。
本発明のマルチピースソリッドゴルフボールは、ゴム製の内層及び外層からなる2層コアとカバーとを有し、これらの間に少なくとも1層の中間層を介在させたボール構造を有する。
(C10)−(C5)≦(C5)−(Cc)≦(Cs)−(C15)≦(C15)−(C10)
上記関係を外れると、フルショットした時の低スピン効果が足りなくなり、或いは実打初速が低くなり、狙いの飛距離が得られない場合がある。
中間層の材料硬度は、特に制限はないが、ショアD硬度で好ましくは57〜67、より好ましくは59〜65、さらに好ましくは61〜63である。また、中間層を被覆した球体の表面硬度は、ショアD硬度で好ましくは64〜74、より好ましくは66〜72、さらに好ましくは68〜70である。上記中間層が軟らかすぎると、フルショット時のスピン量が増えすぎてしまい飛距離が出なくなることがある。また、中間層が硬すぎると、繰り返し打撃による割れ耐久性が悪くなり、またはパターやショートアプローチ実施時の打感が硬くなりすぎることがある。
(I)成分:重量平均分子量(Mw)が140,000以上であり、且つ、酸含量10〜15質量%及びエステル含量15質量%以上のオレフィン−不飽和カルボン酸−不飽和カルボン酸エステル3元共重合体、またはその金属中和物
(II)成分:重量平均分子量(Mw)が140,000以上であり、且つ、酸含量10〜15質量%のオレフィン−アクリル酸2元ランダム共重合体、またはその金属中和物
カバー(最外層)の材料硬度は、特に制限はないが、ショアD硬度で、好ましくは34〜58、より好ましくは40〜56、更に好ましくは48〜54である。
PS7/S/H×100≧5.90(mm-1)
PS2/S/H×100≧1.70(mm-1)
仮想球面の全表面積に対して、ディンプルの面積の総和が占める比率)については、70%以上とすることが好ましく、より好ましくは75%以上、更に好ましくは80%以上である。ディンプルの表面占有率SRの上限は、特に限定されないが、99%以下が好ましい。特に、大きさが異なる少なくとも3種類のディンプルを配置することが好ましく、これによって、ゴルフボールの球状表面上に隙間なく均一にディンプルを配置することができる。
仮想球容積に対して、ディンプルの縁に囲まれた平面から下方に形成されるディンプル容
積の総和が占める比率)を0.75%以上にすることが好ましく、より好ましくは0.80%以上、さらに好ましくは1.1%以上である。ディンプルの体積占有率VRの上限は、1.5%以下とすることが好ましく、より好ましくは1.4%以下である。
コアの形成
表1に示すゴム組成の内層コアを同表中に示す加硫温度及び加硫時間にて形成した。次に、表2に示すゴム組成の外層コアを同表中に示す加硫温度及び加硫時間にて被覆形成して各実施例及び比較例の内外層のゴム製のソリッドコアを製造した。
・ポリブタジエンA:JSR社製、商品名「BR01」
・ポリブタジエンB:JSR社製、商品名「BR51」
・アクリル酸亜鉛:日本触媒社製
・有機過酸化物(1):ジクミルパーオキサイド、日油社製、商品名「パークミルD」
・有機過酸化物(2):1,1ジ(t−ブチルパーオキシ)シクロヘキサンとシリカの混合物、日油社製、商品名「パーヘキサC−40」
・「水」:蒸留水、和光純薬工業社製
・老化防止剤:2,2−メチレンビス(4−メチル−6−ブチルフェノール)、大内新興化学工業社製、商品名「ノクラックNS−6」
・硫酸バリウム:商品名「バリコ#300」(ハクスイテック社製)
・酸化亜鉛:商品名「酸化亜鉛3種」(堺化学工業社製)
・ステアリン酸亜鉛:商品名「ジンクステアレートG」(日油社製)
・ペンタクロロチオフェノール亜鉛塩:ZHEJIANG CHO & FU CHEMI社製
上記で得た2層コアの周囲に、表3に示した配合の中間層材料を用いて射出成形法により中間層被覆球体を得た。次に、上記で得た中間層被覆球体の周囲に、同表に示した配合のカバー材料を用いて射出成形法によりカバー(最外層)を形成し、コアの周囲に中間層及びカバー(最外層)を備えたゴルフボールを作製した。
・「T−8295、T−8290」:DIC Bayer Polymer社製の「(商標)パンデックス」、MDI−PTMGタイプ熱可塑性ポリウレタン
・「ハイミラン1706、ハイミラン1557、ハイミラン1605」:三井・デュポンポリケミカル社製のアイオノマー
・「AN4319」:未中和のエチレン−メタクリル酸−エステル成分の3元共重合体(三井・デュポンポリケミカル社製)
・「AN4221C」:未中和のエチレン−アクリル酸2元共重合体(三井・デュポンポリケミカル社製)
・「ハイトレル4001」:東レデュポン社製のポリエーテルエステルエラストマー
・「ポリエチレンワックス」:三洋化成社製、商品名「サンワックス161P」
・「イソシアネート化合物」:4,4'−ジフェニルメタンジイソシアネート
・「ステアリン酸マグネシウム」:日油社製「マグネシウムステアレートG」
・「水酸化カルシウム」:白石カルシウム社製「水酸化カルシウムCLS−B」
・「酸化マグネシウム」:協和化学工業社製「キョーワマグMF150」
・「ポリテールH」:三菱化学社製
直径:ディンプルの縁に囲まれた平面の直径(mm)
SR:ディンプルがないと仮定したゴルフボールの仮想球面の全表面積に対して、ディンプルの面積の総和が占める比率(単位:%)
ディンプルA
図1の断面形状では、最深点の深さLは0.150mmである。
ディンプルB
図2の断面形状のものは、中心地点Cの深さHが0.097mm、最深点の深さDが0.131mm、外周縁Eから中心地点Cまでの距離を100として外周縁から最深点までの位置が39、曲率半径Rは0.5mm、エッジ角A2が10.5°である。
コアの表面は球面であるが、その球面に硬度計の針をほぼ垂直になるようにセットし、JIS K6301−1975規格に従ってJIS−C硬度でコア表面硬度を計測した。
コアの中心及び所定位置における断面硬度については、コアを半球状にカットして断面を平面にして測定部分に硬度計の針を垂直に押し当てて測定した。JIS−C硬度の値で示される。
なお、内層コアの中心及び外層コアの表面のショアD硬度をASTM D2240−95規格に準拠したタイプDデュロメータによっても計測した。
23.9±1℃の温度で、任意の表面5箇所を測定し、その平均値を1個の内層コア、外層コア被覆球体(コア全体)、または中間層被覆球体の測定値とし、測定個数5個の各球体の平均値を求めた。
23.9±1℃の温度で、任意のディンプルのない部分を5箇所測定し、その平均値を1個のボールの測定値とし、測定個数5個のボールの平均値を求めた。
内層コア、外層コア被覆球体(コア全体)、中間層被覆球体又はボールを硬板の上に置き、初期荷重98N(10kgf)を負荷した状態から終荷重1275N(130kgf)に負荷したときまでのたわみ量をそれぞれ計測した。なお、上記のたわみ量は、いずれも23.9℃に温度調整した後の測定値である。
中間層及びカバーの樹脂材料を厚さ2mmのシート状に成形し、2週間以上放置した。その後、ショアD硬度はASTM D2240−95規格に準拠して計測した
中間層被覆球体又はボール(カバー)の表面に対して針を垂直になるように押し当てて計測した。なお、ボール(カバー)の表面硬度は、ボール表面においてディンプルが形成されていない陸部における測定値である。ショアD硬度はASTM D2240−95規格に準拠したタイプDデュロメータによって計測した。
ゴルフボールの加圧面積PSの測定方法は、平面上に感圧紙(富士フィルム社製の圧力測定フィルム・プレスケール中圧用)を敷き、各実施例及び比較例のゴルフボールを設置した。そして、インストロン・コーポレーション製4204型を用いて、これらゴルフボールに6864N(700kgf)、1961N(200kgf)の各荷重をかけ、ゴルフボールとの接触によって感圧紙が発色した部分の面積の総和を測定した。プレスケール圧力画像解析システムFPD−9270(富士フィルム社製)を用いて、発色した部分の面積を求めた。上記の加圧面積は、ゴルフボールの任意の一位置における測定の結果である。
ゴルフ打撃ロボットにドライバー(W#1)をつけてヘッドスピード(HS)45m/sにて打撃した時の飛距離を測定し、下記基準により評価した。クラブはブリヂストン社製「TourStage X−Drive709 D430ドライバー(2013年モデル)」(ロフト9.5°)を使用した。なお、上記のヘッドスピードは中上級者の平均的なヘッドスピードに相当する。
〔判定基準〕
トータル飛距離225.0m以上 ・・・・ ○
トータル飛距離225.0m未満 ・・・・ ×
ゴルフ打撃ロボットにサンドウエッジをつけてヘッドスピード(HS)35m/sにて打撃した時のスピンの量を下記の基準により判断した。
〔判定基準〕
スピン量5900rpm以上 ・・・・ ○
スピン量5900rpm未満 ・・・・ ×
比較例1は、内層コアの直径が小さいものであり、その結果、ドライバー(W#1)打撃時の実打初速が遅くなり、飛距離が出ない。
比較例2は、外層コアの表面硬度が軟らかいものであり、その結果、W#1打撃時の低スピン効果が足りずに飛距離が出ない。
比較例3は、カバーが中間層より硬いものであり、アプローチ時にスピンがかからず、所望のアプローチスピン効果が得られない。
Claims (9)
- ゴム製の内層及び外層からなる2層コアと、カバーとを有し、且つ、これらの間に少なくとも1層の中間層を介在させたマルチピースソリッドゴルフボールにおいて、上記内層コアの直径が30mm以上であり、外層コアの表面硬度から内層コアの中心硬度を引いた値がJIS−C硬度で25以上であり、内層コアに対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をA、2層コアに対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をBとするとき、A/B≦1.5の数式を満足すると共に、中間層の材料硬度がカバーの材料硬度よりも硬いことを特徴するマルチピースソリッドゴルフボール。
- コア硬度分布において、コア中心のJIS−C硬度を(Cc)、コア中心から5mmの位置のJIS−C硬度を(C5)、コア中心から10mmの位置のJIS−C硬度を(C10)、コア中心から15mmの位置のJIS−C硬度を(C15)、コア表面のJIS−C硬度を(Cs)とするとき、下記式(i)〜(v)
1≦(C10)−(Cc)≦15 ・・・・(i)
(C10)−(Cc)<(Cs)−(C10) ・・・・(ii)
18≦(Cs)−(C10) ・・・・(iii)
(Cs)≧80 ・・・・(iv)
(Cc)≧50 ・・・・(v)
の関係を満足する請求項1記載のマルチピースソリッドゴルフボール。 - 下記式(vi)を満足する請求項1又は2記載のマルチピースソリッドゴルフボール。
1.5≦[(Cs)−(C10)/(C10)−(Cc)]≦4 ・・・・(vi) - 下記式(vii)を満足する請求項1、2又は3記載のマルチピースソリッドゴルフボール。
25≦(Cs)−(Cc)≦45 ・・・・(vii) - 下記式(viii)を満足する請求項1〜4のいずれか1項記載のマルチピースソリッドゴルフボール。
(C10)−(C5)≦(C5)−(Cc)≦(Cs)−(C15)≦(C15)−(C10)
・・・・(viii) - コアに中間層を被覆した球体に対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をCとするとき、A/C≦1.9の数式を満足する請求項1〜5のいずれか1項記載のマルチピースソリッドゴルフボール。
- ゴルフボールに対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をHとするとき、A/H≦2.0、及び、A−H≦2.5の数式を満足する請求項1〜6のいずれか1項記載のマルチピースソリッドゴルフボール。
- ゴルフボールに6864N(700kgf)の荷重をかけたときに、平面に接するゴルフボールの面積である加圧面積(mm2)をPS7、ゴルフボールの直径に沿った断面の円の面積であって、ゴルフボール表面にディンプルが全くない場合の仮想平面積(mm2)をS、及びゴルフボールに対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をHとするとき、
PS7/S/H×100≧5.90(mm-1) ・・・・(ix)
を満足する請求項1〜7のいずれか1項記載のマルチピースソリッドゴルフボール。 - ゴルフボールに1961N(200kgf)の荷重をかけたときに、平面に接するゴルフボールの面積である加圧面積(mm2)をPS2、ゴルフボールの直径に沿った断面の円の面積であって、ゴルフボール表面にディンプルが全くない場合の仮想平面積(mm2)をS、及びゴルフボールに対して、初期荷重98N(10kgf)から終荷重1,275N(130kgf)を負荷したときまでのたわみ量(mm)をHとするとき、
PS2/S/H×100≧1.70(mm-1) ・・・・(x)
を満足する請求項1〜8のいずれか1項記載のマルチピースソリッドゴルフボール。