JP2016540098A5 - - Google Patents
Download PDFInfo
- Publication number
- JP2016540098A5 JP2016540098A5 JP2016542029A JP2016542029A JP2016540098A5 JP 2016540098 A5 JP2016540098 A5 JP 2016540098A5 JP 2016542029 A JP2016542029 A JP 2016542029A JP 2016542029 A JP2016542029 A JP 2016542029A JP 2016540098 A5 JP2016540098 A5 JP 2016540098A5
- Authority
- JP
- Japan
- Prior art keywords
- composition
- peroxide
- antioxidant
- pellet
- molecular weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Links
- 239000003963 antioxidant agent Substances 0.000 claims 25
- 230000003078 antioxidant Effects 0.000 claims 22
- 239000000203 mixture Substances 0.000 claims 22
- 150000002978 peroxides Chemical class 0.000 claims 20
- IJGRMHOSHXDMSA-UHFFFAOYSA-N nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 claims 14
- 239000008188 pellet Substances 0.000 claims 14
- BJELTSYBAHKXRW-UHFFFAOYSA-N 2,4,6-tris(prop-2-enoxy)-1,3,5-triazine Chemical compound C=CCOC1=NC(OCC=C)=NC(OCC=C)=N1 BJELTSYBAHKXRW-UHFFFAOYSA-N 0.000 claims 11
- 229910052757 nitrogen Inorganic materials 0.000 claims 9
- PWWSSIYVTQUJQQ-UHFFFAOYSA-N Distearyl thiodipropionate Chemical compound CCCCCCCCCCCCCCCCCCOC(=O)CCSCCC(=O)OCCCCCCCCCCCCCCCCCC PWWSSIYVTQUJQQ-UHFFFAOYSA-N 0.000 claims 7
- 239000002656 Distearyl thiodipropionate Substances 0.000 claims 7
- 235000019305 distearyl thiodipropionate Nutrition 0.000 claims 7
- 239000007788 liquid Substances 0.000 claims 7
- 238000002844 melting Methods 0.000 claims 7
- 229920000642 polymer Polymers 0.000 claims 6
- 230000000111 anti-oxidant Effects 0.000 claims 3
- -1 polyethylene Polymers 0.000 claims 3
- XOUQAVYLRNOXDO-UHFFFAOYSA-N 2-tert-butyl-5-methylphenol Chemical compound CC1=CC=C(C(C)(C)C)C(O)=C1 XOUQAVYLRNOXDO-UHFFFAOYSA-N 0.000 claims 2
- ODJQKYXPKWQWNK-UHFFFAOYSA-L 3-(2-carboxylatoethylsulfanyl)propanoate Chemical compound [O-]C(=O)CCSCCC([O-])=O ODJQKYXPKWQWNK-UHFFFAOYSA-L 0.000 claims 2
- 239000007983 Tris buffer Substances 0.000 claims 2
- 239000000155 melt Substances 0.000 claims 2
- VNWKTOKETHGBQD-UHFFFAOYSA-N methane Chemical compound C VNWKTOKETHGBQD-UHFFFAOYSA-N 0.000 claims 2
- 125000000325 methylidene group Chemical group [H]C([H])=* 0.000 claims 2
- 150000001451 organic peroxides Chemical class 0.000 claims 2
- ISWSIDIOOBJBQZ-UHFFFAOYSA-N phenol Chemical compound OC1=CC=CC=C1 ISWSIDIOOBJBQZ-UHFFFAOYSA-N 0.000 claims 2
- 150000007970 thio esters Chemical class 0.000 claims 2
- BDLPXCQLOWBOID-UHFFFAOYSA-M 10-methoxy-10-oxo-9-(1,2,2,6,6-pentamethylpiperidin-4-yl)decanoate Chemical compound [O-]C(=O)CCCCCCCC(C(=O)OC)C1CC(C)(C)N(C)C(C)(C)C1 BDLPXCQLOWBOID-UHFFFAOYSA-M 0.000 claims 1
- KKAKGATZLWUOMA-UHFFFAOYSA-N N-(2,2,6,6-tetramethylpiperidin-4-yl)formamide Chemical compound CC1(C)CC(NC=O)CC(C)(C)N1 KKAKGATZLWUOMA-UHFFFAOYSA-N 0.000 claims 1
- 239000004698 Polyethylene (PE) Substances 0.000 claims 1
- 150000001412 amines Chemical class 0.000 claims 1
- 238000009472 formulation Methods 0.000 claims 1
- 229920000573 polyethylene Polymers 0.000 claims 1
- 229940116351 sebacate Drugs 0.000 claims 1
- CXMXRPHRNRROMY-UHFFFAOYSA-L sebacate(2-) Chemical compound [O-]C(=O)CCCCCCCCC([O-])=O CXMXRPHRNRROMY-UHFFFAOYSA-L 0.000 claims 1
- 239000003381 stabilizer Substances 0.000 claims 1
Claims (27)
- 0.6〜66重量パーセント(重量%)のシアヌル酸トリアリル(TAC)及び34〜99.4重量%の抗酸化剤(AO)を含む、予備配合組成物。
- 前記TAC及びAOが、1:100〜3:2のTAC:AO重量比で存在する、請求項1に記載の前記組成物。
- 過酸化物架橋性組成物であって、
(A)過酸化物架橋性ポリマーと、
(B)過酸化物と、
(C)シアヌル酸トリアリル(TAC)と、
(D)1つ以上の抗酸化剤(AO)と、を含み、
前記TACが、0.0005重量%〜0.01重量%の濃度で存在する、前記組成物。 - ペレットの形態である、請求項3に記載の前記組成物。
- 過酸化物架橋性ペレットを作製するための方法であって、
(1)
(A)過酸化物架橋性ポリマーと、
(B)シアヌル酸トリアリル(TAC)及びAOの予備配合物であって、0.6〜66重量%のTAC及び34〜99.4重量%のAOを含むか、または本質的にそれらからなる、予備配合物と、の均質な溶融物を形成するステップと、
(2)100μm未満のメッシュサイズを有するフィルターに、(1)の均質な溶融物を通過させるステップと、
(3)前記(2)の濾過した均質な溶融物からペレットを形成するステップと、
を含む、前記方法。 - 前記ペレットに過酸化物を含浸させるさらなるステップを含む、請求項5に記載の前記方法。
- 過酸化物架橋性組成物であって、
(A)過酸化物架橋性ポリマーと、
(B)0.0005重量%〜0.01重量%の低分子量、または低融点、または液体の窒素塩基と、
(C)1つ以上の抗酸化剤(AO)と、
(D)任意に、過酸化物と、を含む、前記組成物。 - 前記塩基が、TAC及び/もしくはN,N’−1,6−ヘキサンジイルビス(N−(2,2,6,6−テトラメチル−4−ピペリジニル)−ホルムアミドならびに/またはビス(1,2,2,6,6−ペンタメチル−4−ピペリジル)セバケート及びメチル1,2,2,6,6−ペンタメチル−4−ピペリジルセバケートの混合物を含む、請求項7に記載の前記組成物。
- 前記抗酸化剤がDSTDPを含む、請求項7又は8に記載の前記組成物。
- 過酸化物架橋性ペレットを作製するための方法であって、
(1)
(A)過酸化物架橋性ポリマーと、
(B)0.0005重量%〜0.01重量%の低分子量、または低融点、または液体の窒素塩基と、
(C)任意に、抗酸化剤(AO)と、の均質な溶融物を形成するステップと、
(2)100μm未満のメッシュサイズを有するフィルターに、前記(1)の均質な溶融物を通過させるステップと、
(3)前記(2)の濾過した均質な溶融物からペレットを形成するステップと、
を含む、前記方法。 - 前記ペレットに過酸化物を含浸させるさらなるステップを含む、請求項10に記載の前記方法。
- 過酸化物架橋性ペレットを作製するための方法であって、
(1)過酸化物架橋性ポリマーのAOとの溶融物を形成するステップと、
(2)100μm未満のメッシュサイズを有するフィルターに、前記(1)の溶融物を通過させるステップと、
(3)前記(2)の濾過した均質な溶融物からペレットを形成するステップと、
(4)前記ペレットに低分子量または液体の窒素塩基を含浸させるステップと、
を含む、前記方法。 - 前記ペレットは、過酸化物もまた含浸している、請求項12に記載の前記方法。
- 過酸化物架橋性組成物であって、
(A)過酸化物架橋性ポリエチレンと、
(B)0.005重量%〜0.03重量%の、ヒンダードアミン安定剤を含む低分子量、または低融点、または液体の窒素塩基であって、1,400g/モルを超えない分子量、及び95℃を超えない溶融温度を有する低分子量、または低融点、または液体の窒素塩基と、
(C)1つ以上の抗酸化剤(AO)と、
(D)任意に、有機過酸化物と、を含む、前記組成物。 - 前記低分子量、または低融点、または液体の窒素塩基は、1,000g/モルを超えない分子量を有する、請求項14に記載の前記組成物。
- 前記抗酸化剤がチオエステルを含む、請求項14又は15に記載の前記組成物。
- 前記抗酸化剤がヒンダードフェノールを含む、請求項14又は15に記載の前記組成物。
- 前記抗酸化剤がヒンダードフェノール及びチオエステルを含む、請求項14〜17のいずれか一項に記載の前記組成物。
- 前記抗酸化剤が、テトラキス[メチレン(3,5−ジ−tert−ブチル−4−ヒドロキシヒドロ−シナメート)]メタン;4,4’−チオビス(3−メチル−6−tert−ブチルフェノール;及びジステアリルチオジプロピオネート(DSTDP)を含む、請求項1〜4、7〜9及び14〜18のいずれか一項に記載の前記組成物。
- 前記抗酸化剤が、[1,3,5−トリス(4−tert−ブチル−3−ヒドロキシ−2,6−ジメチルベンジル)−1,3,5−トリアジン−2,4,6−(1H,3H,5H)−トリオン];及びジステアリルチオジプロピオネート(DSTDP)を含む、請求項1〜4、7〜9及び14〜16のいずれか一項に記載の前記組成物。
- 0.5重量%〜2.5重量%の有機過酸化物を含む、請求項14〜20のいずれか一項に記載の前記組成物。
- 過酸化物架橋性ペレットを作製するための方法であって、
(1)
(A)過酸化物架橋性ポリマーと、
(B)低分子量、または低融点、または液体の窒素塩基と、
(C)任意に、抗酸化剤(AO)と、の均質な溶融物を形成するステップと、
(2)100μm未満のメッシュサイズを有するフィルターに、前記(1)の均質な溶融物を通過させるステップと、
(3)前記(2)の濾過した均質な溶融物からペレットを形成するステップと、
を含む、前記方法。 - 前記ペレットに過酸化物を含浸させるさらなるステップを含む、請求項22に記載の前記方法。
- 前記抗酸化剤が、テトラキス[メチレン(3,5−ジ−tert−ブチル−4−ヒドロキシヒドロ−シナメート)]メタン;4,4’−チオビス(3−メチル−6−tert−ブチルフェノール;及びジステアリルチオジプロピオネート(DSTDP)を含む、請求項5、6、10〜13、22及び23のいずれか一項に記載の前記方法。
- 前記抗酸化剤が、[1,3,5−トリス(4−tert−ブチル−3−ヒドロキシ−2,6−ジメチルベンジル)−1,3,5−トリアジン−2,4,6−(1H,3H,5H)−トリオン];及びジステアリルチオジプロピオネート(DSTDP)を含む、請求項5、6、10〜13、22及び23のいずれか一項に記載の前記方法。
- 請求項5、6、10〜13及び22〜25のいずれか一項に記載の前記方法によって作製されたシースを備える、ワイヤまたはケーブル。
- 請求項1〜4、7〜9及び14〜21のいずれか一項に記載の前記組成物を含むシースを備える、ワイヤまたはケーブル。