JP2016194163A - 金属被覆鉄ストリップ - Google Patents
金属被覆鉄ストリップ Download PDFInfo
- Publication number
- JP2016194163A JP2016194163A JP2016131466A JP2016131466A JP2016194163A JP 2016194163 A JP2016194163 A JP 2016194163A JP 2016131466 A JP2016131466 A JP 2016131466A JP 2016131466 A JP2016131466 A JP 2016131466A JP 2016194163 A JP2016194163 A JP 2016194163A
- Authority
- JP
- Japan
- Prior art keywords
- strontium
- calcium
- concentration
- coating
- iron strip
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
亜鉛: 40〜60質量%;
ケイ素: 0.3〜3質量%;及び
マグネシウム: 0.3〜10質量%。
(a)熱処理炉中で鉄ストリップを熱処理する工程;及び
(b)溶融浴中でそのストリップを熱浸漬被覆し、そのことにより鉄ストリップの上に合金の被覆を形成する工程;
を包含し、この方法は、溶融浴中の(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムの濃度が少なくとも2ppmに制御することにより特徴付けられる。
(a)熱処理炉中で鉄ストリップを熱処理する工程;及び
(b)溶融浴中でそのストリップを熱浸漬被覆し、鉄ストリップの上に金属合金の被覆を形成する工程;
を包含する方法を提供する。
(a)被覆の耐腐食性に貢献する少なくとも0.5質量%及び10質量%未満のマグネシウム、
(b)被覆のスパングル寸法を最小にする二ホウ化チタン、及び
(c)上述の表面欠陥の数を最小にする50ppmを上回り0.2質量%未満のストロンチウム及びカルシウムを併せた量、
を含むAl−Zn−Si−Mg被覆合金である。
なお、本発明は以下の態様を含む。
・態様1
ストリップの少なくとも片面上に金属合金の被覆を有する鉄ストリップであって、該金属合金は主要元素としてアルミニウム、亜鉛、ケイ素、及びマグネシウムを含み、ストロンチウム及び/又はカルシウム及び不可避的な不純物及び要すれば意図的な合金化元素として存在するその他の元素をも含み、マグネシウムの濃度は少なくとも1重量%であり、(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が50ppmを上回る、鉄ストリップ。
・態様2
前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が0.2重量%未満である態様1記載の鉄ストリップ。
・態様3
前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が150ppm未満である態様1又は2記載の鉄ストリップ。
・態様4
前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が100ppm未満である先行態様のいずれか記載の鉄ストリップ。
・態様5
前記マグネシウムの濃度が10重量%未満である先行態様のいずれか記載の鉄ストリップ。
・態様6
前記マグネシウムの濃度が5重量%未満である先行態様のいずれか記載の鉄ストリップ。
・態様7
前記マグネシウムの濃度が3重量%未満である先行態様のいずれか記載の鉄ストリップ。
・態様8
前記マグネシウムの濃度が少なくとも0.5重量%である先行態様のいずれか記載の鉄ストリップ。
・態様9
前記マグネシウムの濃度が少なくとも1重量%及び5重量%未満である先行態様のいずれか記載の鉄ストリップ。
・態様10
前記マグネシウムの濃度が1.5重量%及び3重量%の間である先行態様のいずれか記載の鉄ストリップ。
・態様11
前記アルミニウム、亜鉛、ケイ素、及びマグネシウムの合金がここに定義される二ホウ化チタン変性合金である先行態様のいずれか記載の鉄ストリップ。
・態様12
前記アルミニウム、亜鉛、ケイ素、及びマグネシウムの合金がインジウム、スズ、ベリリウム、チタン、銅、ニッケル、コバルト、及びマンガンのいずれか一種以上を含有する先行態様のいずれか記載の鉄ストリップ。
・態様13
前記アルミニウム、亜鉛、ケイ素、及びマグネシウムの合金が、例えば溶融浴中における汚染によるような痕跡量にて存在するものとは異なる、意図的な合金の要素としてバナジウム及び/又はクロムを含有しない先行態様のいずれか記載の鉄ストリップ。
・態様14
前記鉄の濃度が1重量%未満である先行態様のいずれか記載の鉄ストリップ。
・態様15
前記被覆が、ここで定義される小さいスパングルを有する先行態様のいずれか記載の鉄ストリップ。
・態様16
前記ストリップがその片面又は両面に被覆されている先行態様のいずれか記載の鉄ストリップ。
・態様17
前記被覆がストリップのその面又は各面上に80g/m 2 未満の被覆質量の金属合金を有する先行態様のいずれか記載の鉄ストリップ。
・態様18
前記被覆がストリップのその面又は各面上に20ミクロメートル未満の平均被覆厚さを有する先行態様のいずれか記載の鉄ストリップ。
・態様19
鉄ストリップの少なくとも片面上に金属合金の被覆を形成する方法であって、該金属合金は主要元素としてアルミニウム、亜鉛、ケイ素、及びマグネシウムを含み、ストロンチウム及び/又はカルシウム及び不可避的な不純物及び要すれば意図的な合金化元素として存在するその他の元素をも含み、マグネシウムの濃度は少なくとも0.5重量%であり、(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が50ppmを上回り、該方法は引き続いて鉄ストリップを熱処理炉及び金属合金を含む溶融浴に通過させ、そして:
(a)熱処理炉中で鉄ストリップを熱処理する工程;及び
(b)溶融浴中でそのストリップを熱浸漬被覆し、鉄ストリップの上に金属合金の被覆を形成する工程;
を包含する方法。
・態様2016年7月26日 前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が0.2重量%未満である態様19記載の方法。
・態様21
前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が150ppm未満である態様19又は20記載の方法。
・態様22
前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が100ppm未満である態様19〜21のいずれか記載の方法。
・態様23
前記工程(b)が、ストリップのその面又は各面上に80g/m 2 未満の被覆質量の被覆を形成する工程を包含する態様19〜22のいずれか記載の方法。
・態様24
前記工程(b)が、ストリップのその面又は各面上に20ミクロメートル未満の平均被覆厚の被覆を形成する工程を包含する態様19〜23のいずれか記載の方法。
・態様25
前記工程(b)が、ここで定義される小さいスパングルを有する被覆を形成する工程を包含する態様19〜23のいずれか記載の方法。
・態様26
態様1〜18のいずれか一つに定義された金属合金被覆鉄ストリップから作成された冷間形成された製品。
Claims (26)
- ストリップの少なくとも片面上に金属合金の被覆を有する鉄ストリップであって、該金属合金は主要元素としてアルミニウム、亜鉛、ケイ素、及びマグネシウムを含み、ストロンチウム及び/又はカルシウム及び不可避的な不純物及び要すれば意図的な合金化元素として存在するその他の元素をも含み、マグネシウムの濃度は少なくとも1質量%であり、(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が50ppmを上回る、鉄ストリップ。
- 前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が0.2質量%未満である請求項1記載の鉄ストリップ。
- 前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が150ppm未満である請求項1又は2記載の鉄ストリップ。
- 前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が100ppm未満である先行請求項のいずれか記載の鉄ストリップ。
- 前記マグネシウムの濃度が10質量%未満である先行請求項のいずれか記載の鉄ストリップ。
- 前記マグネシウムの濃度が5質量%未満である先行請求項のいずれか記載の鉄ストリップ。
- 前記マグネシウムの濃度が3質量%未満である先行請求項のいずれか記載の鉄ストリップ。
- 前記マグネシウムの濃度が少なくとも0.5質量%である先行請求項のいずれか記載の鉄ストリップ。
- 前記マグネシウムの濃度が少なくとも1質量%及び5質量%未満である先行請求項のいずれか記載の鉄ストリップ。
- 前記マグネシウムの濃度が1.5質量%及び3質量%の間である先行請求項のいずれか記載の鉄ストリップ。
- 前記アルミニウム、亜鉛、ケイ素、及びマグネシウムの合金がここに定義される二ホウ化チタン変性合金である先行請求項のいずれか記載の鉄ストリップ。
- 前記アルミニウム、亜鉛、ケイ素、及びマグネシウムの合金がインジウム、スズ、ベリリウム、チタン、銅、ニッケル、コバルト、及びマンガンのいずれか一種以上を含有する先行請求項のいずれか記載の鉄ストリップ。
- 前記アルミニウム、亜鉛、ケイ素、及びマグネシウムの合金が、例えば溶融浴中における汚染によるような痕跡量にて存在するものとは異なる、意図的な合金の要素としてバナジウム及び/又はクロムを含有しない先行請求項のいずれか記載の鉄ストリップ。
- 前記鉄の濃度が1質量%未満である先行請求項のいずれか記載の鉄ストリップ。
- 前記被覆が、ここで定義される小さいスパングルを有する先行請求項のいずれか記載の鉄ストリップ。
- 前記ストリップがその片面又は両面に被覆されている先行請求項のいずれか記載の鉄ストリップ。
- 前記被覆がストリップのその面又は各面上に80g/m2未満の被覆質量の金属合金を有する先行請求項のいずれか記載の鉄ストリップ。
- 前記被覆がストリップのその面又は各面上に20ミクロメートル未満の平均被覆厚さを有する先行請求項のいずれか記載の鉄ストリップ。
- 鉄ストリップの少なくとも片面上に金属合金の被覆を形成する方法であって、該金属合金は主要元素としてアルミニウム、亜鉛、ケイ素、及びマグネシウムを含み、ストロンチウム及び/又はカルシウム及び不可避的な不純物及び要すれば意図的な合金化元素として存在するその他の元素をも含み、マグネシウムの濃度は少なくとも0.5質量%であり、(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が50ppmを上回り、該方法は引き続いて鉄ストリップを熱処理炉及び金属合金を含む溶融浴に通過させ、そして:
(a)熱処理炉中で鉄ストリップを熱処理する工程;及び
(b)溶融浴中でそのストリップを熱浸漬被覆し、鉄ストリップの上に金属合金の被覆を形成する工程;
を包含する方法。 - 前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が0.2質量%未満である請求項19記載の方法。
- 前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が150ppm未満である請求項19又は20記載の方法。
- 前記(i)ストロンチウム又は(ii)カルシウム又は(iii)ストロンチウム及びカルシウムを併せた濃度が100ppm未満である請求項19〜21のいずれか記載の方法。
- 前記工程(b)が、ストリップのその面又は各面上に80g/m2未満の被覆質量の被覆を形成する工程を包含する請求項19〜22のいずれか記載の方法。
- 前記工程(b)が、ストリップのその面又は各面上に20ミクロメートル未満の平均被覆厚の被覆を形成する工程を包含する請求項19〜23のいずれか記載の方法。
- 前記工程(b)が、ここで定義される小さいスパングルを有する被覆を形成する工程を包含する請求項19〜23のいずれか記載の方法。
- 請求項1〜18のいずれか一つに定義された金属合金被覆鉄ストリップから作成された冷間形成された製品。