JP2016148003A - 接着性樹脂組成物、積層フィルム、包装材料及び包装容器 - Google Patents
接着性樹脂組成物、積層フィルム、包装材料及び包装容器 Download PDFInfo
- Publication number
- JP2016148003A JP2016148003A JP2015026903A JP2015026903A JP2016148003A JP 2016148003 A JP2016148003 A JP 2016148003A JP 2015026903 A JP2015026903 A JP 2015026903A JP 2015026903 A JP2015026903 A JP 2015026903A JP 2016148003 A JP2016148003 A JP 2016148003A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- layer
- adhesive
- ethylene
- resin composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
<1> エチレン重合体及びエチレン・酢酸ビニル共重合体の少なくとも一方の樹脂Aと、前記樹脂Aに非相溶な樹脂Bと、粘着付与樹脂と、を含有し、JIS−K6760に準拠して測定した2mm厚での引張強度が2MPa以上15MPa以下であり、JIS−K6760に準拠して測定した2mm厚での伸びが50%以上500%以下である接着性樹脂組成物である。
<2> 前記粘着付与樹脂は、芳香族炭化水素樹脂、水素化石油樹脂、及び脂肪族炭化水素樹脂から選択される少なくとも一種である前記<1>に記載の接着性樹脂組成物である。
<3> 前記芳香族炭化水素樹脂が、テルペン系樹脂、ロジン系樹脂、及びスチレン系樹脂を含む前記<2>に記載の接着性樹脂組成物である。
<4> 前記粘着付与樹脂は、水素化石油樹脂及びテルペン系樹脂から選択される少なくとも一種である前記<1>に記載の接着性樹脂組成物である。
<5> 前記水素化石油樹脂が、芳香族系石油樹脂の不飽和二重結合の少なくとも一部が水素化された脂環族炭化水素樹脂である前記<2>〜前記<4>のいずれか1つに記載の接着性樹脂組成物である。
<6> 前記水素化石油樹脂は、芳香族系石油樹脂の不飽和二重結合の一部が水素化された脂環族炭化水素樹脂である前記<5>に記載の接着性樹脂組成物である。
<7> 前記水素化石油樹脂は、軟化点が120℃以上である前記<2>〜前記<6>のいずれか1つに記載の接着性樹脂組成物である。
<8> 前記樹脂Aがエチレン・酢酸ビニル共重合体であり、前記樹脂Bがブテン重合体である前記<1>〜前記<7>のいずれか1つに記載の接着性樹脂組成物である。
<10> 前記第2樹脂層が、エチレン重合体及びブテン重合体を含む前記<9>に記載の積層フィルムである。
<11> 前記第2樹脂層の厚みLA及び前記第1樹脂層の厚みLBは、LA≦LB<20μmの関係を満たす前記<9>又は前記<10>に記載の積層フィルムである。
<12> 支持体と、前記<9>〜前記<11>のいずれか1つに記載の積層フィルムと、を有する包装材料である。
<13> 前記積層フィルムは、共押出により前記支持体の上に層状に成形されている前記<12>に記載の包装材料である。
<14> 少なくとも最表面が樹脂である容器の開口部に接着して前記開口部を閉塞する蓋材である前記<12>又は前記<13>に記載の包装材料である。
<15> 開口した収容部を有し、少なくとも最表面が樹脂である収納容器と、支持体及び前記<9>〜前記<11>のいずれか1つに記載の積層フィルムを有し、前記収納容器の開口部に前記積層フィルムの第1樹脂層を接着させて前記開口部を閉塞する蓋材と、を備えた包装容器である。
<16> 前記収納容器の少なくとも蓋材と接する最表面が、ポリエステルである前記<15>に記載の包装容器である。
また、本発明によれば、少なくとも表面材質が樹脂である容器(樹脂製容器)に接着して被収容物の保管又は運搬等に必要とされる密封性(接着性)と、開封時には容易にかつ滑らかに開封し得る易開封性(易剥離性)と、を兼ね備えた包装材料及び包装容器が提供される。
本発明の接着性樹脂組成物は、少なくとも、エチレン重合体及びエチレン・酢酸ビニル共重合体の少なくとも一方の樹脂Aと、樹脂Aに非相溶な樹脂Bと、粘着付与樹脂と、を含有し、JIS−K6760に準拠して測定した2mm厚での引張強度を2MPa以上15MPa以下の範囲とし、JIS−K6760に準拠して測定した2mm厚での伸びを50%以上500%以下の範囲とする。
本発明の接着性樹脂組成物は、必要に応じて、さらに他の成分を含んでいてもよい。
しかしながら、密封性及び易開封性のバランスについては、未だ両者をともに成り立たせる技術が確立されるに至っていない。このような状況のもと、凝集剥離による剥離機構を採用した場合に、接着強度を保ちつつも容易かつ滑らかに剥離し得るとの知見を得た。
かかる知見に基づき、本発明では、第1の樹脂Aとしてエチレン重合体又はエチレン・酢酸ビニル共重合体の一方又は両方と、第2の樹脂Bとして樹脂Aに非相溶な樹脂と、粘着付与樹脂と、を組み合わせ、かつJIS−K6760に準拠して測定した2mm厚での引張強度が2MPa以上15MPa以下(好ましくは4MPa以上10MPa以下)であり、JIS−K6760に準拠して測定した2mm厚での伸びが50%以上500%以下(好ましくは80%以上490%以下、更に好ましくは100%以上450%以下、最も好ましくは150%以上450%以下)である組成とすることで、各層間における接着強度を確保しつつも、この接着強度より弱い力で凝集破壊される層を得ることができる。これにより、容器内に被収容物を収容して密封する際には、樹脂製容器と蓋材の間において強固な接着性を確保する一方、蓋材を樹脂製容器から剥がして開封する際には、蓋材を容易にかつ滑らかに剥がすことができるものとなる。
本発明の接着性樹脂組成物を用いることで、被収容物の保管又は運搬等に必要とされる密封性(接着性)と、開封時に容易にかつ滑らかに開封し得る易開封性(易剥離性)と、を兼ね備えた包装材料を提供することができる。
本発明の接着性樹脂組成物は、エチレン重合体及びエチレン・酢酸ビニル共重合体の少なくとも一方を含有する。エチレン重合体及びエチレン・酢酸ビニル共重合体は、それぞれ1種単独で含む場合に限られず、複数種を混合して併用してもよい。
また、エチレン重合体の190℃、2160g荷重におけるメルトフローレート(MFR;JIS−K7210(1999年)に準拠)は、成形加工性、及び樹脂材料(例えば樹脂容器、具体的には、例えばポリエステル又はポリエステル製容器)との接着強度の点で、0.1g/10分以上100g/10分以下が好ましく、より好ましくは1g/10分以上80g/10分以下であり、さらに好ましくは3g/10分以上60g/10分以下である。
エチレン・酢酸ビニル共重合体において、エチレンに由来の構造単位の含有比率としては、全構造単位に対して、70質量%以上95質量%以下が好ましく、85質量%以上95質量%以下がより好ましい。
また、エチレン・酢酸ビニル共重合体において、酢酸ビニル(VA)由来の構造単位の含有比率としては、全構造単位に対して、4質量%以上20質量%以下が好ましく、5質量%以上15質量%以下がより好ましい。VA由来の構造単位の含有比率が4質量%以上であると、低温シール性の点で好ましい。
接着性樹脂組成物中における、エチレン重合体及びエチレン・酢酸ビニル共重合体の含有量としては、接着性樹脂組成物の全固形分に対して、50質量%以上90質量%以下が好ましく、55質量%以上80質量%以下がより好ましい。
本発明の接着性樹脂組成物は、樹脂Aに非相溶な樹脂Bの少なくとも一種を含む。
「樹脂Aに非相溶」とは、樹脂Aと樹脂Bとを混合した後に、樹脂Aと樹脂Bとの境界が確認できる状態を意味する。樹脂Aと樹脂Bとの境界は、接着性樹脂組成物を用いて層状の薄片(厚み:0.05μm〜0.1μm)を作製し、オスミウム又はルテニウムにて染色した後、走査型電子顕微鏡などでモルフォロジー(微細構造)を観察することにより確認することができる。
樹脂Bの接着性樹脂組成物中における含有量としては、接着性樹脂組成物の全固形分に対して、10質量%以上50質量%以下が好ましく、15質量%以上45質量%以下がより好ましく、15質量%以上35質量%以下が更に好ましい。樹脂Bの含有量が10質量%以上であると、接着性樹脂組成物の強度、特に層などの成形物を成形した際の成形物の強度を降下させる側に調節することができる。また、樹脂Bの含有量が50質量%以下であると、成形加工性及び経済性の点で有利である。
本発明の接着性樹脂組成物は、粘着付与樹脂の少なくとも一種を含有する。粘着付与樹脂を含有することで、被着体である樹脂材料(例えば樹脂容器、具体的には、例えばポリエステル(好ましくはPET)又はポリエステル製容器)との接着強度に優れたものとなる。
中でも、被着体である樹脂材料(例えば樹脂容器、具体的には、例えばポリエステル(好ましくはPET)又はポリエステル製容器)との接着強度に優れたものとなる点から、水素化石油樹脂は、芳香族系石油樹脂の不飽和二重結合の一部が水素化(すなわち部分水添)された部分水添石油樹脂である脂環族炭化水素樹脂が好ましい。
ロジン系樹脂の具体例としては、上市されている市販品として、エステルガムシリーズ(例えば、エステルガムAA−L、エステルガムAAV、エステルガムAT等;荒川化学社製)、ペンセルシリーズ(例えば、ペンセルA、ペンセルAZ、ペンセルC等;荒川化学社製)などが挙げられる。
スチレン系樹脂の具体例としては、上市されている市販品として、例えば、YSレジンSX(ヤスハラケミカル社製)等が挙げられる。
中でも、上記と同様の理由から、軟化点は、100℃以上が好ましく、110℃以上がより好ましい。特に水素化石油樹脂は、軟化点が120℃以上であるのが好ましい。
粘着付与樹脂の軟化点は、JIS K2207(2006年)に準拠して、軟化点試験方法(環球法)に基づいて測定された値を用いることができる。
接着性樹脂組成物は、上記の成分以外の他の成分として、防曇剤、滑剤、アンチブロッキング剤、酸化防止剤、熱安定剤、光安定剤、耐候安定剤、紫外線吸収剤などの高分子分野で一般に用いられる添加剤をさらに含有してもよい。
他の成分は、接着性樹脂組成物による効果を損なわない範囲で含有することができる。
接着性樹脂組成物は、例えば、上記した成分を同時に又は逐次的にドライブレンド又はメルトブレンドすることによって調製することができる。これらの成分の混合順序には、特に制限はない。
前記ドライブレンドには、ヘンシェルミキサー、タンブラーミキサーなどの各種ミキサーを用いることができる。
前記メルトブレンドには、一軸又は二軸押出機、バンバリーミキサー、ロール、ニーダーなどの混練装置を用いることができる。混練装置による溶融混練は、例えば、160℃〜230℃の温度で行える。
本発明の積層フィルムは、少なくとも、既述の本発明の接着性樹脂組成物を含む第1樹脂層と、低密度ポリエチレン並びにエチレン・α,β−不飽和カルボン酸共重合体及びエチレン・α,β−不飽和カルボン酸エステル共重合体(以下、総じて「エチレン・α,β−不飽和カルボン酸系共重合体」ともいう。)の少なくとも1つを含む第3樹脂層と、第1樹脂層と第3樹脂層との間に配置され、JIS−K6760に準拠して測定した2mm厚での伸びが前記接着性樹脂組成物より小さい樹脂組成物を含む第2樹脂層と、を有している。
本発明の積層フィルムにおける第3樹脂層は、低密度ポリエチレン又はエチレン・α,β−不飽和カルボン酸系共重合体を含むことで、第2の樹脂層に比べて引張強度が強く、かつ支持体への接着性を有することで、後述するように例えばアルミ材料を備えた包装材料とした場合にアルミ材料に対する接着性に優れたものとなり、第2樹脂層との間の接着にも優れている。
本発明における第1樹脂層(以下、接着性層ともいう)は、既述の本発明の接着性樹脂組成物を用いて形成された層である。接着性層は、既述のように、エチレン重合体及びエチレン・酢酸ビニル共重合体の一方又は両方(樹脂A)と、前記樹脂Aに非相溶な樹脂Bと、粘着付与樹脂と、を含有し、JIS−K6760に準拠して測定した2mm厚での引張強度が2MPa以上15MPa以下(好ましくは4Mpa以上10Mpa以下)であり、JIS−K6760に準拠して測定した2mm厚での伸びが50%以上500%以下(好ましくは80%以上490%以下、更に好ましくは100%以上450%以下、最も好ましくは150%以上450%以下)である樹脂組成物を含むことで、被着体である樹脂材料(例えば少なくとも最表面が樹脂である容器、具体的には、例えばポリエステル(好ましくはPET)又はポリエステル製容器)との接着性に優れている。
接着性層におけるエチレン重合体、エチレン・酢酸ビニル共重合体(樹脂A)、樹脂Aに非相溶な樹脂B、及び粘着付与樹脂の詳細については、接着性樹脂組成物の説明において既述した通りであり、好ましい態様も同様である。
接着性層の伸びが第2樹脂層の伸びより大きいことで、積層フィルムを被着体から剥離する際、層間の界面剥離を招来せず、第2樹脂層での凝集破壊による凝集剥離に伴う剥離が可能になる。これにより、積層フィルムの被着体からの剥離を、容易かつ滑らかに行えるようになる。
なお、伸び率(%)は、所定量の接着性樹脂組成物を加圧プレスして2mm厚のプレスシートを作製し、JIS−K6760に準拠した方法により測定される。
なお、引張強度は、伸び率と同様に、所定量の接着性樹脂組成物を加圧プレスして2mm厚のプレスシートを作製し、JIS−K6760に準拠した方法により測定される値である。
接着性層の厚みは、積層フィルムを積層方向と平行に裁断した裁断面を光学顕微鏡等で拡大して観察し計測することで求められる。
第3樹脂層は、低密度ポリエチレン、エチレン・α,β−不飽和カルボン酸共重合体、及びエチレン・α,β−不飽和カルボン酸エステル共重合体の少なくとも1つを含有し、第2樹脂層及びアルミ材料などの支持体に対する接着性を有している。中でも、特にエチレン・α,β−不飽和カルボン酸共重合体又はエチレン・α,β−不飽和カルボン酸エステル共重合体を含有する場合が好ましい。また、第3樹脂層は、必要に応じて、他の成分を含む態様も好ましい。
なお、下記α,β−不飽和カルボン酸エステルのα,β−不飽和カルボン酸についても同様である。
α,β−不飽和カルボン酸エステルの例としては、アクリル酸アルキルエステル(例えば、アクリル酸メチル、アクリル酸エチル、アクリル酸イソプロピル、アクリル酸イソブチル、アクリル酸ノルマルブチル、アクリル酸2−エチルヘキシル等)、メタクリル酸アルキルエステル(例えば、メタクリル酸メチル、メタクリル酸エチル、メタクリル酸イソプロピル、メタクリル酸イソブチル、メタクリル酸ノルマルブチル、メタクリル酸2−エチルヘキシル等)などが挙げられる。
これらモノマーは、1種単独で又は2種以上組み合わせて共重合されてもよい。
この引張強度は、所定量の接着性樹脂組成物を加圧プレスして2mm厚のプレスシートを作製し、JIS−K6760に準拠した方法により測定される。
第3樹脂層の厚みは、積層フィルムを積層方向と平行に裁断した裁断面を光学顕微鏡等で拡大して観察し計測することで求められる。
本発明の積層フィルムは、上記の第3樹脂層と第1樹脂層(接着性層)との間に、第2樹脂層を有している。本発明の積層フィルムは、第2樹脂層を設けて第3樹脂層/第2樹脂層/第1樹脂層(接着性層)の3層を有する積層構造に構成し、第2樹脂層又は接着性層にて凝集破壊による凝集剥離する態様が好ましい。
第2樹脂層の樹脂は、第2樹脂層の伸びが接着性層の伸びよりも小さくなるように選択される。中でも、剥離時の感触(剥離感)がより滑らかで、剥離面の粗れが少ない点から、第2樹脂層の強度を接着性層の強度より弱くしておき、中間層をなす第2樹脂層にて凝集破壊して剥離する態様に構成されることがより好ましい。
なお、エチレン重合体及びブテン重合体は、既述の接着性樹脂組成物にて説明したエチレン重合体、ブテン重合体とそれぞれ同義であり、それぞれの好ましい態様も同様である。
上記のうち、第2樹脂層及び接着性層は、第2樹脂層の厚みをLAとし、接着性層の厚みをLBとした場合、下記の関係(1)を満たすことがより好ましく、下記の関係(2)を満たすことが更に好ましい。
LA≦LB<20μm …(1)
LA≦LB<15μm …(2)
この引張強度は、既述の第1樹脂層及び接着性層と同様の方法で測定される。
伸び率(%)は、引張強度と同様にJIS−K6760に準拠した方法で測定される。
本発明の包装材料は、支持体と、既述の本発明の積層フィルムと、を備えており、支持体に積層フィルムの第3樹脂層を直接又は他の層を介して配設することで構成される。
支持体としては、特に制限はなく、紙、アルミニウム板(例えばアルミ箔)、ポリエステル(例えばポリエチレンテレフタレート)の板状材(シート又はフィルム)、アルミ蒸着ポリエステル(例えばアルミ蒸着ポリエチレンテレフタレート)の板状材(シート又はフィルム)、シリカ蒸着ポリエステル(例えばシリカ蒸着ポリエチレンテレフタレート)の板状材(シート又はフィルム)、ポリオレフィン(例えば、ポリエチレン、ポリプロピレン、ポリスチレン)の板状材(シート又はフィルム)、アルミ蒸着ポリオレフィン(例えばアルミ蒸着ポリプロピレン)の板状材(シート又はフィルム)などが挙げられる。これらの支持基体は、単層構造のみならず、2層以上の積層構造であってもよい。
積層フィルムは、具体例として、紙/ポリオレフィン層/アルミ箔/第3樹脂層/第2樹脂層/第1樹脂層(接着性層)等の構造に構成されてもよい。
本発明においては、経済性の点で、共押出により支持体上に積層フィルム成形する方法が好ましい。
包装容器としては、開口した収容部を有し、少なくとも最表面が樹脂である収納容器と、支持体及び本発明の積層フィルムを有し、少なくとも最表面が樹脂である収納容器の開口部に積層フィルムの第1樹脂層を接着させて開口部を閉塞する蓋材と、を備えた包装容器であってもよい。
また、メルトフローレート(MFR)は、JIS K7210−1999に準拠して190℃、2160g荷重にて測定した。
原料として、以下の材料を準備した。
[エチレン重合体]
・低密度ポリエチレン(1):密度916kg/m3、MFR(190℃、2160g荷重):7.2g/10分
(以下、LDPE(1)と略記する)
・低密度ポリエチレン(2):密度915kg/m3、MFR(190℃、2160g荷重):23g/10分
(以下、LDPE(2)と略記する)
・低密度ポリエチレン(3):密度915kg/m3、MFR(190℃、2160g荷重):70g/10分
(以下、LDPE(3)と略記する)
・低密度ポリエチレン(4):密度915kg/m3、MFR(190℃、2160g荷重):35g/10分
(以下、LDPE(4)と略記する)
・低密度ポリエチレン(5):密度915kg/m3、MFR(190℃、2160g荷重):45g/10分
(以下、LDPE(5)と略記する)
・エチレン・酢酸ビニル共重合体(1):酢酸ビニル10質量%、MFR(190℃、2160g荷重):9g/10分
(以下、EVA(1)と略記する)
・エチレン・酢酸ビニル共重合体(2):酢酸ビニル10質量%、MFR(190℃、2160g荷重):19g/10分
(以下、EVA(2)と略記する)
・ポリブテン:ホモタイプ、MFR(190℃、2160g荷重):1.8g/10分
(以下、PBと略記する)
・エチレン・メタクリル酸共重合体:エチレン含量:91質量%、メタクリル酸含量:9質量%、MFR(190℃、2160g荷重):8g/10分
(以下、酸ポリマーと略記する)
・粘着付与樹脂(1):完全水添石油樹脂(水添脂環族炭化水素樹脂;商品名:アルコンP−115(環球法軟化点:115℃)、荒川化学社製)
・粘着付与樹脂(2):部分水添石油樹脂(水添脂環族炭化水素樹脂;商品名:アルコンM−135(環球法軟化点:135℃)、荒川化学社製)
・粘着付与樹脂(3):ピネン重合体(商品名:YSレジンPX1150N、環球法軟化点;115℃)、ヤスハラケミカル社製)
−第3樹脂層形成用の樹脂の準備−
上記の酸ポリマー(エチレン・メタクリル酸共重合体)を、第3樹脂層形成用の樹脂(エチレン・α,β−不飽和カルボン酸共重合体)として準備した。
表1に示す配合にしたがって、材料を計量(仕込み量を10kgとした)し、溶融押出機(先端ダルメージフライトスクリュー、スクリュ径:φ65mm、L/D(=スクリュ長/スクリュ直径):28)の投入口へ投入した。各樹脂には、ペレットを用いた。そして、溶融押出機の加工温度を180℃に調節して溶融混練し、接着性層形成用の樹脂組成物を調製した。
なお、引張強度、伸びの測定は、以下の方法にて行った。
調製した接着性層形成用の樹脂組成物をそれぞれ約60g計量し、加圧プレス法により2mm厚のプレスシートを作製した。そして、JIS−K6760に準拠した方法により引張強度と伸びを測定した。測定結果を表1に示す。
表2に示す配合にしたがって、材料を計量(仕込み量を10kgとした)し、溶融押出機(先端ダルメージフライトスクリュー、スクリュ径:φ65mm、L/D(=スクリュ長/スクリュ直径):28)の投入口へ投入した。各樹脂には、ペレットを用いた。そして、溶融押出機の加工温度を180℃に調節して溶融混練し、第2樹脂層形成用の樹脂組成物を調製した。
なお、引張強度及び伸びの測定は、上記の「第1樹脂層(接着性層)形成用の樹脂組成物の調製」における場合と同様の方法で行った。
65mmφラミネーター(ダイ幅:900mm幅)を用いて、79.1g/m2の片アート紙(三菱製紙社製)とアルミ箔としてUACJ社製1N30との間に厚み15μmの低密度ポリエチレン(1)を挟み込むようにして、加工温度320℃でサンド加工し、片アート紙/低密度ポリエチレン(15μm)/アルミ箔の積層構造を有する支持体を作製した。
<溶融押出条件>
・各層の溶融押出温度:260℃(第3樹脂層)、260℃(第2樹脂層)、240℃(接着性層)
・アダプター温度:250℃
・ダイ温度:250℃
・ライン速度:30m/分
上記で作製した評価サンプルの各々について、以下の評価を行った。評価結果を表3に示す。
上記で作製した各評価サンプルを、接着性層において接するようにA−PET支持体(PR東プラ社製、厚み:500μm)の上に置き、下記の条件にてヒートシールした。
<シール条件>
・シール装置:ヒートシールバー(10mm幅)
・シール温度:130℃
・シール時間:1秒
・シール圧:0.2MPa(実圧)
さらに、剥離時に接着層における凝集破壊の発生の有無を確認した。
また、測定の際、糸曳きの発生の有無を評価した。糸曳きの評価は、下記の基準にしたがって行った。
<基準>
A:糸曳きはみられない。
B:糸曳き及び毛羽立ちの発生は僅かである。
C:糸曳きの発生が明らかに認められる。
上記の「(1)剥離強度、凝集破壊、及び糸曳き」と同様に、各評価サンプルを、接着性層において接するようにA−PET支持体(PR東プラ社製、厚み:500μm)の上に置き、ヒートシールした。次いで、評価サンプルが支持体にヒートシールされた積層物を15mm幅の短冊に切り出し、A−PET支持体から評価サンプルを、剥離強度の測定と同程度(約300mm/分)の速度にて手動で引き剥がした。引き剥がした際の滑らかさを、以下の基準にしたがって評価し、剥離感を評価する指標とした。
なお、基準は、(良好)A > B > C(不良)の順で評価した。
<基準>
A:ジッピングを伴う剥離現象がなく、滑らかに剥離する。
B:ジッピングを伴う剥離現象が一部で発生するが、ほぼ滑らかに剥離する。
C:ジッピングを伴う剥離現象が発生し、ほぼ全面に界面剥離が起きている。
実施例1において、接着性層の配合を配合3に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表3に示す。
実施例1において、第2樹脂層を層2に代え、かつ接着性層の配合を配合3に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表3に示す。
実施例1において、第2樹脂層を層2に代え、かつ接着性層の配合を配合4に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表3に示す。
実施例1において、第2樹脂層を層5に代え、かつ接着性層の配合を配合3に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表3に示す。
実施例1において、第2樹脂層を層6に代え、かつ接着性層の配合を配合3に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表3に示す。
実施例1において、第2樹脂層を層6に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表3に示す。
実施例1において、第2樹脂層を層5に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表3に示す。
実施例1において、第2樹脂層を層4に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表4に示す。
実施例1において、第2樹脂層を層3に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表4に示す。
実施例1において、接着性層の配合を配合1に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表4に示す。
実施例1において、第2樹脂層を層2に代え、かつ接着性層の配合を配合3に代えると共に、第1樹脂層、第2樹脂層、接着性層の厚みをそれぞれ15μm、15μm、15μmに変更したこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表4に示す。
実施例1において、第2樹脂層を層2に代え、かつ接着性層の配合を配合3に代えると共に、第1樹脂層、第2樹脂層、接着性層の厚みをそれぞれ10μm、25μm、10μmに変更したこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表4に示す。
実施例1において、第2樹脂層を層7に代え、かつ接着性層の配合を配合7に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表4に示す。
実施例1において、第2樹脂層を層3に代え、かつ接着性層の配合を配合8に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表4に示す。
実施例1において、接着性層の配合を配合6に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表5に示す。
実施例1において、接着性層の配合を配合5に代えたこと以外は、実施例1と同様にして、評価サンプルを作製し、測定及び評価を行った。結果を表5に示す。
これに対して、伸びが50%以上500%以下の範囲外である接着層を用いた比較例では、高い剥離強度を保ちつつ、かつ接着性層自体が高強度になりすぎるため、接着性層での凝集剥離が行えずに界面剥離となり、結果、良好な剥離感が得られなかった。また、剥離時の糸曳き現象も防ぐことができなかった。
Claims (16)
- エチレン重合体及びエチレン・酢酸ビニル共重合体の少なくとも一方の樹脂Aと、前記樹脂Aに非相溶の樹脂Bと、粘着付与樹脂と、を含有し、JIS−K6760に準拠して測定した2mm厚での引張強度が2MPa以上15MPa以下であり、JIS−K6760に準拠して測定した2mm厚での伸びが50%以上500%以下である接着性樹脂組成物。
- 前記粘着付与樹脂は、芳香族炭化水素樹脂、水素化石油樹脂、及び脂肪族炭化水素樹脂から選択される少なくとも一種である請求項1に記載の接着性樹脂組成物。
- 前記芳香族炭化水素樹脂が、テルペン系樹脂、ロジン系樹脂、及びスチレン系樹脂を含む請求項2に記載の接着性樹脂組成物。
- 前記粘着付与樹脂は、水素化石油樹脂及びテルペン系樹脂から選択される少なくとも一種である請求項1に記載の接着性樹脂組成物。
- 前記水素化石油樹脂が、芳香族系石油樹脂の不飽和二重結合の少なくとも一部が水素化された脂環族炭化水素樹脂である請求項2〜請求項4のいずれか1項に記載の接着性樹脂組成物。
- 前記水素化石油樹脂は、芳香族系石油樹脂の不飽和二重結合の一部が水素化された脂環族炭化水素樹脂である請求項5に記載の接着性樹脂組成物。
- 前記水素化石油樹脂は、軟化点が120℃以上である請求項2〜請求項6のいずれか1項に記載の接着性樹脂組成物。
- 前記樹脂Aがエチレン・酢酸ビニル共重合体であり、前記樹脂Bがブテン重合体である請求項1〜請求項7のいずれか1項に記載の接着性樹脂組成物。
- 請求項1〜請求項8のいずれか1項に記載の接着性樹脂組成物を含む第1樹脂層と、
JIS−K6760に準拠して測定した2mm厚での伸びが、前記接着性樹脂組成物より小さい樹脂組成物を含む第2樹脂層と、
低密度ポリエチレン、エチレン・α,β−不飽和カルボン酸共重合体、及びエチレン・α,β−不飽和カルボン酸エステル共重合体の少なくとも1つを含む第3樹脂層と、
をこの順に有する積層フィルム。 - 前記第2樹脂層が、エチレン重合体及びブテン重合体を含む請求項9に記載の積層フィルム。
- 前記第2樹脂層の厚みLA及び前記第1樹脂層の厚みLBは、LA≦LB<20μmの関係を満たす請求項9又は請求項10に記載の積層フィルム。
- 支持体と、請求項9〜請求項11のいずれか1項に記載の積層フィルムと、を有する包装材料。
- 前記積層フィルムは、共押出により前記支持体の上に層状に成形されている請求項12に記載の包装材料。
- 少なくとも最表面が樹脂である収納容器の開口部に接着させて前記開口部を閉塞する蓋材である請求項12又は請求項13に記載の包装材料。
- 開口した収容部を有し、少なくとも最表面が樹脂である収納容器と、
支持体及び請求項9〜請求項11のいずれか1項に記載の積層フィルムを有し、前記収納容器の開口部に前記積層フィルムの第1樹脂層を接着させて前記開口部を閉塞する蓋材と、
を備えた包装容器。 - 前記収納容器の少なくとも蓋材と接する最表面が、ポリエステルである請求項15に記載の包装容器。