JP2015232630A - 透過投映スクリーン - Google Patents
透過投映スクリーン Download PDFInfo
- Publication number
- JP2015232630A JP2015232630A JP2014119257A JP2014119257A JP2015232630A JP 2015232630 A JP2015232630 A JP 2015232630A JP 2014119257 A JP2014119257 A JP 2014119257A JP 2014119257 A JP2014119257 A JP 2014119257A JP 2015232630 A JP2015232630 A JP 2015232630A
- Authority
- JP
- Japan
- Prior art keywords
- light
- composite oxide
- projection screen
- chromium
- jis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【課題】明るい使用環境での透過投映像の発色鮮明性と、ホットスポット抑止効果に優れた遮熱性を有する透過投映スクリーンで、ショーウインドー用の投映スクリーン兼遮熱ブラインドを提供する。
【解決手段】熱可塑性樹脂中に光拡散性粒子を含有する光透過性樹脂シートにおいて、光透過性樹脂シートが、金属複合酸化物を含み、マンセル明度0〜4(マンセル表色系)に着色され、400〜750nmの可視光波長域における平均反射率10%以下、750〜1200nmの近赤外線波長域における平均反射率25%以上を発現させた透過投映スクリーン。
【選択図】図3
Description
実施例及び比較例で作成した透過投映スクリーンについて以下の評価を行った。透過投映スクリーンのサイズはたて1.5m×よこ2.0mとして、背面に映像投映装置として液晶式ビデオプロジェクター(セイコーエプソン社製EH−TW500S)を使用した。
<プロジェクター光源の視認性:ホットスポットの有無>
たて1.5m×よこ2.0mの透過投映スクリーンの裏面2mの距離にビデオプロジェクターを配置した。投映映像をシート真正面から観察し、以下の基準で評価した。
1:ホットスポット無:プロジェクター光源位置が認知できない
2:軽微なホットスポットを認める:おぼろにプロジェクター光源位置が認知できる
3:ホットスポット有:プロジェクター光源位置がはっきりと認知できる
<映像の発色鮮明性(コントラスト性)>
1:輝度が高く鮮明
2:輝度が高く不鮮明
3:輝度が低く不鮮明
<可視光透過率>
透過投映スクリーンの可視光透過率を、分光側色計CM−3600d(コニカミノルタ社製)を使用しJIS Z8722に従って測定した。
<マンセル明度>
透過投映スクリーンのマンセル明度(JIS Z8721)をMUNSELL BOOK OF COLOR 標準色見本に照合させた。
<熱線反射効果>
室内でASTM D4803-97法による250W赤外線ランプ照射による昇温曲線を30分間測定し、30分後の温度を求めた。
<遮熱効果>
幅100cm×高さ100cm×奥ゆき100cmの立方体の骨組みをアルミ製L型アングル(幅35mm)で組み立て、立方体骨組の底面を除く全面に透過投映スクリーンを貼付固定し試験箱体を作製した。この試験箱体を正午〜13時の太陽光が直射される環境(埼玉県草加市5月:晴天:気温28℃)での試験箱体内部温度を温度センサー(試験箱体内部中心に温度センサーを床上50cmに宙吊固定)で測定した。
環状オレフィンコポリマーとして、エチレンとノルボルネンとの共重合体(ノルボルネン含有率78質量%):商標「TOPAS」:品番6015:ポリプラスチックス社製:屈折率1.53(ISO489):光線透過率(2mmt)91(ISO13468−2)、光拡散性粒子として、架橋ポリメタクリル酸メチル球状粒子(平均粒子径20μm):商標「テクポリマー」:品番MBX−20:積水化成品工業社製:屈折率1.49を用いた。また、黒色系着色剤として、鉄−クロム複合酸化物及び銅−クロム−マンガン複合酸化物を用い、下記配合1により、165℃の熱ロール条件でカレンダー成形を行い、厚さ0.2mm、可視光透過率50%、マンセル明度3.0、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)7%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)43%を発現するシートを得た。
<配合1>
環状オレフィンコポリマー 100質量部
光拡散性粒子(架橋ポリメタクリル酸メチル球状粒子:20μm) 15質量部
黒色系着色剤(鉄−クロム複合酸化物) 0.4質量部
黒色系着色剤(銅−クロム−マンガン複合酸化物) 0.4質量部
実施例1の配合1を下記配合2に変更し、鉄−クロム−コバルト複合酸化物及び
銅−クロム複合酸化物を用いた以外は実施例1と同様にして、厚さ0.2mm、可視光透過率46%、マンセル明度3.0、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)7%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)45%を発現するシートを得た。
<配合2>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
光拡散性粒子(架橋ポリメタクリル酸メチル球状粒子:20μm) 15質量部
黒色系着色剤(鉄−クロム−コバルト複合酸化物) 0.4質量部
黒色系着色剤(銅−クロム複合酸化物) 0.4質量部
実施例1で用いた環状オレフィンコポリマー、黒色系着色剤として鉄−クロム複合酸化物及び銅−クロム−マンガン複合酸化物を用い、下記配合3により、165℃の熱ロール条件でカレンダー成形を行い、厚さ0.2mmのシートを得た。
<配合3>
環状オレフィンコポリマー 100質量部
黒色系着色剤(鉄−クロム複合酸化物) 0.4質量部
黒色系着色剤(銅−クロム−マンガン複合酸化物) 0.4質量部
次に、実施例1で用いた環状オレフィンコポリマー、実施例1で用いた光拡散性粒子を用い、下記配合4により、165℃の熱ロール条件でカレンダー成形を行い厚さ0.1mmのシートを作成し、165℃の熱ロールを有するラミネーターを用いて上記配合3による0.2mmのシートの片面に積層し、総厚0.3mm、可視光透過率45%、マンセル明度3.5、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)6%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)40%を発現するシートを得た。
<配合4>
環状オレフィンコポリマー 100質量部
光拡散性粒子(架橋ポリメタクリル酸メチル球状粒子:20μm) 15質量部
実施例2で用いた軟質ポリ塩化ビニル樹脂組成物、黒色系着色剤として鉄−クロム−コバルト複合酸化物及び銅−クロム複合酸化物を用い、下記配合5により、165℃の熱ロール条件でカレンダー成形を行い、厚さ0.2mmのシートを得た。
<配合5>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
黒色系着色剤(鉄−クロム−コバルト複合酸化物) 0.4質量部
黒色系着色剤(銅−クロム複合酸化物) 0.4質量部
次に、実施例2で用いた軟質ポリ塩化ビニル樹脂組成物、実施例2で用いた光拡散性粒子を用い、下記配合6により、165℃の熱ロール条件でカレンダー成形を行い厚さ0.1mmのシートを作成し、165℃の熱ロールを有するラミネーターを用いて上記配合5による0.2mmのシートの片面に積層し、総厚0.3mm、可視光透過率42%、マンセル明度3.5、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)6%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)41%を発現するシートを得た。
<配合6>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
光拡散性粒子(架橋ポリメタクリル酸メチル球状粒子:20μm) 15質量部
実施例3の配合4を下記配合7に変更した以外は、実施例3と同様として、総厚0.3mm、可視光透過率35%、マンセル明度2.5、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)6%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)40%を発現するシートを得た。
<配合7>
環状オレフィンコポリマー 100質量部
光拡散性粒子(光半透過性黒色粒子) 15質量部
※黒色色素C.I. Pigment Black7をメタクリル酸メチル樹脂に対して0.3質量%濃
度で含有する可視光透過率が40%の、平均粒子径20μmの光半透過性黒色粒子で、
コントラスト引締効果に寄与する
実施例4の配合6を下記配合8に変更した以外は、実施例4と同様として、総厚0.3mm、可視光透過率33%、マンセル明度2.5、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)6%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)41%を発現するシートを得た。
<配合8>
ポリ塩化ビニル樹脂 100質量部
DOP(可塑剤) 65質量部
エポキシ化大豆油 2質量部
Ba−Zn系複合安定剤 1.5質量部
ステアリン酸バリウム(滑剤) 0.2質量部
ベンゾトリアゾール系紫外線吸収剤 0.3質量部
光拡散性粒子(光半透過性黒色粒子) 15質量部
※黒色色素C.I. Pigment Black7をメタクリル酸メチル樹脂に対して0.3質量%濃
度で含有する可視光透過率が40%の、平均粒子径20μmの光半透過性黒色粒子で、
コントラスト引締効果に寄与する
実施例1〜6のシートと下記ガラス織布とを熱ラミネート法で積層し、ガラス織布の片面に光透過性樹脂シートを有し、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)5〜7%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)40〜45%を発現する各種スクリーンを得た。
<ガラス織布>
375dtexのEガラス(屈折率1.558)無撚扁平マルチフィラメント糸条を経糸及び緯糸として、経糸打込密度32本/inch、緯糸打込密度32本/inchで平織してなる空隙率1.0%未満、質量100g/m2のガラス織布(シランカップリング処理)
実施例1〜12のスクリーンに下記配合9による塗液組成物を100メッシュグラビアロールで塗布し、これを乾燥し数日養生してゾルゲル硬化を完了させ防汚層兼帯電防止層を形成し、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)5〜7%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)40〜45%を発現する各種スクリーンを得た。
<配合9>防汚層兼帯電防止層
シリカゾル(粒子径20〜30nm:固形分48質量%の無機コロイド)100質量部
ビニルトリエトキシシラン(シランカップリング剤) 50質量部
ベンゾトリアゾール化合物(紫外線吸収剤) 1質量部
ポリエチレングリコール型非イオン活性剤(帯電防止剤) 1質量部
希釈剤(水) 100質量部
実施例1において、光拡散性粒子の配合を省略した以外は実施例1と同様として、厚さ0.2mm、可視光透過率56%、マンセル明度2.5、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)7%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)45%を発現するシートを得た。
実施例1において、黒色系着色剤(鉄−クロム複合酸化物)0.4質量部、及び黒色系着色剤(銅−クロム−マンガン複合酸化物)0.4質量部の配合を省略した以外は実施例1と同様として、厚さ0.2mm、可視光透過率79%、マンセル明度8.5、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)5%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)4%のシートを得た。
実施例1において、黒色系着色剤(鉄−クロム複合酸化物)0.4質量部、及び黒色系着色剤(銅−クロム−マンガン複合酸化物)0.4質量部の配合を、黒色系着色剤(カーボンブラック:C.I. Pigment Black7)0.8質量部に置換した以外は実施例1と同様として、厚さ0.2mm、可視光透過率44%、マンセル明度3.0、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)6%、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)8%のシートを得た。
2:熱可塑性樹脂
3:光拡散性粒子
3−1:光半透過性黒色粒子
4:黒色系着色剤(金属複合酸化物)
4−1:黒色系着色剤(カーボンブラック)
5:光透過性織布
Claims (5)
- 熱可塑性樹脂中に平均粒子径5〜30μmの光拡散性粒子を含有する光透過性樹脂シートであって、前記光透過性樹脂シートが金属複合酸化物を含み、マンセル明度0〜4(マンセル表色系)に着色されることで、400〜750nmの可視光波長域における平均反射率(JIS R3106準拠)10%以下、750〜1200nmの近赤外線波長域における平均反射率(JIS R3106準拠)25%以上を発現することを特徴とする透過投映スクリーン。
- 前記金属複合酸化物が、鉄−クロム複合酸化物、鉄−クロム−コバルト複合酸化物、鉄−クロム−コバルト−マンガン複合酸化物、銅−クロム複合酸化物、銅−マグネシウム複合酸化物、銅−クロム−マンガン複合酸化物、銅−ビスマス複合酸化物、マンガン−ビスマス複合酸化物から選ばれた1種以上である請求項1に記載の透過投映スクリーン。
- 前記光拡散性樹脂シートが光透過性織布を芯材に含む請求項1〜3のいずれか1項に記載の透過投映スクリーン。
- 前記光透過性樹脂シートが積層構造を有し、前記光拡散性粒子を含有する層と、前記着色剤を含有する層とに分れている請求項1〜3のいずれか1項に記載の透過投映スクリーン。
- 前記光透過性樹脂シートの表面抵抗値(測定方法:JIS K6911、測定条件:湿度30%RH−温度23℃)が、1.0E+12Ω未満である請求項1〜4のいずれか1項に記載の透過投映スクリーン。