JP2014129197A - ガラス板接着用の仮止材、及びガラスの加工方法 - Google Patents
ガラス板接着用の仮止材、及びガラスの加工方法 Download PDFInfo
- Publication number
- JP2014129197A JP2014129197A JP2012288400A JP2012288400A JP2014129197A JP 2014129197 A JP2014129197 A JP 2014129197A JP 2012288400 A JP2012288400 A JP 2012288400A JP 2012288400 A JP2012288400 A JP 2012288400A JP 2014129197 A JP2014129197 A JP 2014129197A
- Authority
- JP
- Japan
- Prior art keywords
- glass
- glass plate
- meth
- acrylate
- temporary fixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ガラス板同士を接着する接着層を介して相互に固定された複数枚のガラス板からなるガラス板積層体の形状加工処理に対応するガラス板接着用の仮止材である。この仮止材は(メタ)アクリレート成分、発泡剤及び光開始剤を含む。(メタ)アクリレート成分は、(メタ)アクリレート成分を100重量%としたとき、単官能モノマーが60〜90重量%、オリゴマーが10〜40重量%から構成される。
【選択図】なし
Description
本発明者らの検討によれば、このような形状加工処理における加工品質は、ガラス板積層体におけるガラス板同士を接着する接着層の物理的特性が影響することを見出した。
従って、従来の特許文献2等に開示されているような仮止用の接着剤を使用しても、形状加工処理の際に欠けや割れ等の問題が発生し、安定した加工品質の向上を図ることが困難な場合がある。
すなわち、本発明は以下の構成を有する。
(構成1の発明)
ガラス板同士を接着する接着層を介して相互に固定された複数枚のガラス板からなるガラス板積層体の形状加工処理に対応する、ガラス板接着用の仮止材であって、(メタ)アクリレート成分、発泡剤及び光開始剤を含み、前記(メタ)アクリレート成分は、(メタ)アクリレート成分を100重量%としたとき、単官能モノマーが60〜90重量%、オリゴマーが10〜40重量%から構成されることを特徴とするガラス板接着用の仮止材である。
前記ガラス板接着用の仮止材の粘度が200mPa・s以下であることを特徴とする構成1に記載のガラス板接着用の仮止材である。
(構成3の発明)
前記オリゴマーは、ウレタン(メタ)アクリレートであることを特徴とする構成1又は2に記載のガラス板接着用の仮止材である。
前記発泡剤は、アゾアミド、アゾアルキル、アゾエステルから選ばれる1種類以上の化合物であることを特徴とする構成1乃至3のいずれかに記載のガラス板接着用の仮止材である。
(構成5の発明)
前記単官能モノマーは、芳香族及び脂環式構造の少なくともいずれかを骨格に有することを特徴とする構成1乃至4のいずれかに記載のガラス板接着用の仮止材である。
硬化後の前記仮止材のタイプDのデュロメータ硬さは、65〜85であることを特徴とする構成1乃至5のいずれかに記載のガラス板接着用の仮止材である。
構成1乃至6のいずれかに記載のガラス板接着用の仮止材からなる接着層を介して複数枚のガラス板を積層し固定して、ガラス板積層体を形成する積層工程と、前記ガラス板積層体に対して形状加工処理を施す形状加工処理工程と、前記形状加工処理工程の後の前記ガラス板積層体から前記接着層を剥離する剥離工程とを含むことを特徴とするガラスの加工方法である。
(構成8の発明)
前記ガラス板の厚さは、0.1〜1.0mmであることを特徴とする構成7に記載のガラスの加工方法である。
[ガラス板接着用の仮止材]
まず、本発明に係るガラス板接着用の仮止材の実施の形態について説明する。
本発明に係るガラス板接着用の仮止材は、上記構成1にあるように、ガラス板同士を接着する接着層を介して相互に固定された複数枚のガラス板からなるガラス板積層体の形状加工処理に対応する、ガラス板接着用の仮止材であって、(メタ)アクリレート成分、発泡剤及び光開始剤を含み、前記(メタ)アクリレート成分は、(メタ)アクリレート成分を100重量%としたとき、単官能モノマーが60〜90重量%、オリゴマーが10〜40重量%から構成されることを特徴とするガラス板接着用の仮止材である。
図2に示されるように、ガラス板1同士を接着する接着層2を介して相互に固定された複数枚のガラス板1からなるガラス板積層体10において、本発明に係るガラス板接着用の仮止材は上記接着層2を構成するものである。なお、図2では、10枚のガラス板1を各ガラス板間に接着層2を介して積層したガラス板積層体を示しているが、勿論これは一例であって、一般には数十枚程度のガラス基板を積層することが多い。
当該仮止材は、(メタ)アクリレート成分、発泡剤、及び光開始剤を含有している。そして、該(メタ)アクリレート成分は、(メタ)アクリレート成分を100重量%としたとき、単官能モノマー(単官能(メタ)アクリレートモノマー)が60〜90重量%、オリゴマー(アクリレートオリゴマー)が10〜40重量%から構成される。
なお、単官能モノマーとしては、これらの1種又は2種以上を使用しても良い。
なお、ここで言う重量平均分子量としては、ゲルパーミエーションクロマトグラフィー(GPC)で測定される、標準物質はポリスチレンの場合の重量平均分子量を指す。
上記光開始剤の含有量は、上記(メタ)アクリレート成分100重量%に対して、1〜10重量%程度とすることが適当である。
本発明においてアゾ化合物の種類は特に制約されるものではないが、取り分け、アゾアミド、アゾアルキル、及びアゾエステルから選ばれる1種以上であることが好ましい。
上記スペーサーとしては、アクリル、スチレン、6ナイロン等の粒子が望ましい。
本発明は、上記本発明に係る仮止材を用いたガラスの加工方法についても提供するものである。
本発明に係るガラスの加工方法は、上記本発明に係るガラス板接着用の仮止材からなる接着層を介して複数枚のガラス板を積層し固定して、ガラス板積層体を形成する積層工程と、前記ガラス板積層体に対して形状加工処理を施す形状加工処理工程と、前記形状加工処理工程の後の前記ガラス板積層体から前記接着層を剥離する剥離工程とを含むことを特徴とするものである。
図1は、本発明に係るガラスの加工方法を説明するための模式図である。また、図2は、前述のガラス板積層体の層構成を示す断面図である。また、図3は、本発明に係るガラスの加工方法によって得られる電子機器用カバーガラスの一例の平面図である。
図1(a)に示すように、ラミネーター40を使用して、フロート法やダウンドロー法等で製造された厚さが例えば0.5mm程度のガラス板1を複数枚(例えば数十枚程度)積層(ラミネート)してガラス板積層体10を形成する(積層工程)。各ガラス板間には、上述の本発明に係るガラス板接着用の仮止材を塗布して接着層2(図2参照)を設ける。接着層2の厚さは特に制約されるものではないが、本発明においては例えば10〜100μm程度が好適である。
こうして、ガラス板1同士を接着する接着層2を介して相互に固定された複数枚のガラス板1からなるガラス板積層体10が形成される。
本発明に係る仮止材からなる硬化した接着層を剥離するためには、80℃以上の温水が好適である。浸漬時間は適宜決定することができる。
以上の工程によって、例えば図3に示すような電子機器用カバーガラス3が得られる。
化学強化処理の方法としては、例えば、ガラス転移点の温度を超えない温度領域、例えば摂氏300度以上500度以下の温度で、イオン交換を行う低温型イオン交換法などが好ましい。化学強化処理とは、溶融させた化学強化塩とガラス板とを接触させることにより、化学強化塩中の相対的に大きな原子半径のアルカリ金属元素と、ガラス板中の相対的に小さな原子半径のアルカリ金属元素とをイオン交換し、ガラス板の表層に該イオン半径の大きなアルカリ金属元素を浸透させ、ガラス板の表面に圧縮応力を生じさせる処理のことである。化学強化塩としては、硝酸カリウムや硝酸ナトリウムなどのアルカリ金属硝酸を好ましく用いることができる。化学強化処理されたガラス板は強度が向上し耐衝撃性に優れているので、特にタッチパネル式の電子機器に用いられるカバーガラスには好適である。
(実施例1)
本実施例は、仮止材に関するものである。オリゴマーとしてポリエーテル変性ウレタンアクリレートオリゴマーを25重量%、及び単官能モノマーとしてのシクロヘキシル(メタ)アクリレートを75重量%で、(メタ)アクリレート成分として合計100重量%に混合し、光開始剤として1-ヒドロキシ-シクロヘキシル-フェニル-ケトンを2重量%、発泡剤として2,2'−アゾビス(N−ブチル−2−メチルプロピオンアミド)を10重量%添加し、実施例1の仮止材を作成した。得られた仮止材に対して、粘度、硬度、コーティング性、硬化安定性及びチッピング(加工特性)について評価(又は測定)した。この評価結果について表1に示す。
表1〜3に示す種類の原材料を表1〜3に示す組成で使用したこと以外は実施例1と同様にして仮止材を作成した。なお、実施例2〜15及び比悪例1〜3では、表1〜3のオリゴマー及び単官能モノマーを(メタ)アクリレート成分として合計100重量%に混合し、光開始剤及び発泡剤を表1〜3に示す割合で添加した。得られた仮止材について、実施例1と同様に、粘度、硬度、コーティング性、硬化安定性及び加工特性について評価(又は測定)した。それらの結果を表1〜3に示す。
オリゴマー1:ポリエーテル変性ウレタンアクリレートオリゴマー
オリゴマー2:ポリエステル変性ウレタンアクリレートオリゴマー
オリゴマー3:1,2-ポリブタジエン変性ウレタンメタクリレートオリゴマー
オリゴマー4:脂肪族変性ウレタンアクリレートオリゴマー
光開始剤1:1-ヒドロキシ-シクロヘキシル-フェニル-ケトン
発泡剤1:2,2'−アゾビス(N−ブチル−2−メチルプロピオンアミド)
発泡剤2:2,2'-アゾビス(2-メチルプロピオン酸)ジメチル
発泡剤3:2,2'−アゾビス[N−(2−プロペニル)−2−メチルプロピオンアミド]
発泡剤4:1,2-ジデヒドロ-1-(1-シアノ-1-メチルエチル)セミカルバジド
本実施例は、本発明のガラスの加工方法に関する実施例であり、具体的には携帯機器用カバーガラスの製造に関するものである。
以下の(1)積層工程、(2)形状加工処理工程、(3)剥離工程、(4)化学強化処理工程、を経て本実施例の携帯機器用カバーガラスを製造した。
まず、ラミネーターを用いて、フロート法で製造されたアルミノシリゲートガラスからなる厚さ0.5mmのガラス板を20枚積層した。このアルミノシリケートガラスとしては、SiO2:58〜75重量%、Al2O3:4〜20重量%、Li2O:3〜10重量%、Na2O:4〜13重量%を含有する化学強化用ガラスを使用した。なお、各ガラス板間には、上記実施例1の仮止材を塗布して厚さ50μmの接着層を形成した。こうして、接着層を介して20枚のガラス板を積層したガラス板積層体を作製した。
以上のようにして、ガラス板同士を接着する接着層を介して相互に固定された20枚のガラス板からなるガラス板積層体を作製した。
次に、上記小片化されたガラス板積層体に対して所定の形状加工処理を施した。具体的には、回転砥石などを使用して形状加工処理を行い、製品カバーガラスの外形形状を形成した。
ガラス板積層体の形状加工処理の際に、20μmを超えるチッピングを含む欠けや割れ等の発生はなく、良好で安定した加工品質が得られた。
次に、上記形状加工処理を施したガラス板積層体を、80℃以上の温水を収容した液槽中に5分間浸漬させて、ガラス板積層体から複数の各接着層を剥離した。こうして、積層状態のガラス板は1枚ずつ分離された。
次に、上記剥離工程によって1枚ずつ分離されたガラス板に対して化学強化処理を施した。化学強化は硝酸カリウムと硝酸ナトリウムの混合した化学強化液を用意し、この化学強化溶液を380℃に加熱し、上記ガラス板を約4時間浸漬して化学強化処理を行なった。化学強化を終えたガラス板を硫酸、中性洗剤、純水、純水、IPA、IPA(蒸気乾燥)の各洗浄槽に順次浸漬して、超音波洗浄し、乾燥した。
2 接着層
3 電子機器用カバーガラス
10 ガラス板積層体
20 小片化されたガラス板積層体
30 形状加工されたガラス板積層体
40 ラミネーター
50 ガラス用カッター
51,52 回転砥石
60 液槽
Claims (8)
- ガラス板同士を接着する接着層を介して相互に固定された複数枚のガラス板からなるガラス板積層体の形状加工処理に対応する、ガラス板接着用の仮止材であって、
(メタ)アクリレート成分、発泡剤及び光開始剤を含み、
前記(メタ)アクリレート成分は、(メタ)アクリレート成分を100重量%としたとき、単官能モノマーが60〜90重量%、オリゴマーが10〜40重量%から構成されることを特徴とするガラス板接着用の仮止材。 - 前記ガラス板接着用の仮止材の粘度が200mPa・s以下であることを特徴とする請求項1に記載のガラス板接着用の仮止材。
- 前記オリゴマーは、ウレタン(メタ)アクリレートであることを特徴とする請求項1又は2に記載のガラス板接着用の仮止材。
- 前記発泡剤は、アゾアミド、アゾアルキル、アゾエステルから選ばれる1種類以上の化合物であることを特徴とする請求項1乃至3のいずれかに記載のガラス板接着用の仮止材。
- 前記単官能モノマーは、芳香族及び脂環式構造の少なくともいずれかを骨格に有することを特徴とする請求項1乃至4のいずれかに記載のガラス板接着用の仮止材。
- 硬化後の前記仮止材のタイプDのデュロメータ硬さは、65〜85であることを特徴とする請求項1乃至5のいずれかに記載のガラス板接着用の仮止材。
- 請求項1乃至6のいずれかに記載のガラス板接着用の仮止材からなる接着層を介して複数枚のガラス板を積層し固定して、ガラス板積層体を形成する積層工程と、
前記ガラス板積層体に対して形状加工処理を施す形状加工処理工程と、
前記形状加工処理工程の後の前記ガラス板積層体から前記接着層を剥離する剥離工程と
を含むことを特徴とするガラスの加工方法。 - 前記ガラス板の厚さは、0.1〜1.0mmであることを特徴とする請求項7に記載のガラスの加工方法。