JP2014058685A - 接着剤 - Google Patents
接着剤 Download PDFInfo
- Publication number
- JP2014058685A JP2014058685A JP2013236549A JP2013236549A JP2014058685A JP 2014058685 A JP2014058685 A JP 2014058685A JP 2013236549 A JP2013236549 A JP 2013236549A JP 2013236549 A JP2013236549 A JP 2013236549A JP 2014058685 A JP2014058685 A JP 2014058685A
- Authority
- JP
- Japan
- Prior art keywords
- polyol
- curing agent
- xdi
- derivative
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】硬化剤は、30〜90重量%のキシリレンジイソシアネート誘導体と、10〜70重量%のヘキサメチレンジイソシアネート誘導体とを含む。本発明の硬化剤、および、その硬化剤を含む二液硬化型ポリウレタン組成物によれば、密着性、耐酸・アルカリ性、耐溶剤性、耐汚染性および耐候性をバランスよく向上させることができる。そのため、本発明の硬化剤、および、その硬化剤を含む二液硬化型ポリウレタン組成物は、塗料、インキ、接着剤などの各種産業分野において、好適に用いられる。
【選択図】なし
Description
実施例1
タケネートD−110N(XDIのトリメチロールプロパン変性体、三井化学ポリウレタン社製)75重量部(固形分換算値)、タケネートD−165N(HDIのビウレット変性体、三井化学ポリウレタン社製)25重量部を混合し、硬化剤を得た。
表1に示す処方にて配合した以外は、実施例1と同様の方法により、実施例2〜4および比較例1〜5の硬化剤を調製した。なお、配合部数は、すべて固形分換算値である。
D−165N:ヘキサメチレンジイソシアネートのビウレット変性体(NCO基含有率:23.3重量%、固形分濃度:100重量%、粘度(25℃):2300mPa・s、三井化学ポリウレタン社製)
D−170N:ヘキサメチレンジイソシアネートの三量体(NCO基含有率:20.7重量%、固形分濃度:100重量%、粘度(25℃):2000mPa・s、三井化学ポリウレタン社製)
評価
1)塗膜の作製
実施例1〜4および比較例1〜5により得られた硬化剤と、オレスターQ612(スチレン−メチルメタアクリレート−2−ヒドロキシエチル(メタ)アクリレート共重合体、水酸基価:25mgKOH/g、固形分濃度:50重量%、溶剤:MIBK/酢酸ブチル=8/2(重量比)、三井化学社製)に、酸化チタンを固形分あたり50重量%配合した主剤とを混合し、二液硬化型ポリウレタン組成物を得た。次いで、得られた二液硬化型ポリウレタン組成物を、各種のプラスチックテストピース、または、金属製テストピース(SPCC−SB(冷間圧延鋼板)、厚さ0.8mm)の表面に、バーコーターにて、乾燥後の厚みが15〜20μmとなるようにそれぞれ塗布し、23℃、RH50%で1週間放置し、塗膜を形成した。このようにして得られた塗膜を、以下の各試験に用いた。
上記の1)塗膜の作製において、プラスチックテストピースとして、ポリメチルメタクリレート(PMMA)製、アクリロニトリル−ブタジエン−スチレン共重合体(ABS)製、ポリカーボネート(PC)製のプラスチックテストピースをそれぞれ用いて、上記の1)塗膜の作製に従って塗膜を形成した。
上記の1)塗膜の作製において、金属製テストピースを用いて、上記の1)塗膜の作製に従って塗膜を形成した。
塗膜に、5重量%濃度の塩酸(5%HCl)、および、5重量%濃度の水酸化ナトリウム水溶液(5%NaOH)をそれぞれスポットし、乾燥しないようにシャーレで覆い、24時間後に薬品を除去した跡を目視により観察した。その結果を表1に示す。
塗膜に、エタノール(EtOH)に浸したガーゼを用いて、ラビング試験(100回、往復)を行った後、目視により観察した。その結果を表1に示す。
塗膜に、マジックインキ(青)でマークを付け、24時間後にエタノールで拭き取り、痕跡を目視により観察した。その結果を表1に示す。
塗膜に、促進耐候性試験機(デューパネル光コントロールウエザーメーター、スガ試験機社製)により、連続200時間紫外線を照射し、紫外線照射前後の塗膜のE値を、分光式色彩計(日本電色社製)で測定した。紫外線照射前後のE値の差(ΔE)を算出して、塗膜の黄変度合を評価した。その結果を表1に示す。
△:黄変がやや確認された。(1<ΔE<3)
×:黄変が確認された。(3<ΔE)
Claims (3)
- 硬化剤とポリオール成分とを含む二液硬化型ポリウレタン組成物からなる接着剤であって、
前記硬化剤は、
硬化剤およびポリオール成分を使用時に配合し、混合撹拌して塗布する二液硬化型ポリウレタン組成物の硬化剤であって、
30〜90重量%のキシリレンジイソシアネート誘導体と、10〜70重量%のヘキサメチレンジイソシアネート誘導体とを含み、
前記キシリレンジイソシアネート誘導体が、キシリレンジイソシアネートとトリメチロールプロパンとの反応により得られるキシリレンジイソシアネートのポリオール変性体であり、
前記ヘキサメチレンジイソシアネート誘導体が、ヘキサメチレンジイソシアネートのビウレット変性体、および/または、ヘキサメチレンジイソシアネートの三量体である
ことを特徴とする、接着剤。 - 前記ポリオール成分が、アクリルポリオールを含むことを特徴とする、請求項1に記載の接着剤。
- 前記ポリオール成分の水酸基価が、5〜200mgKOH/gであることを特徴とする、請求項1または2に記載の接着剤。