JP2012180408A - ゴム組成物及びそれを用いたタイヤ - Google Patents
ゴム組成物及びそれを用いたタイヤ Download PDFInfo
- Publication number
- JP2012180408A JP2012180408A JP2011042762A JP2011042762A JP2012180408A JP 2012180408 A JP2012180408 A JP 2012180408A JP 2011042762 A JP2011042762 A JP 2011042762A JP 2011042762 A JP2011042762 A JP 2011042762A JP 2012180408 A JP2012180408 A JP 2012180408A
- Authority
- JP
- Japan
- Prior art keywords
- group
- rubber composition
- conjugated diene
- mass
- rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(A)(a−1)共役ジエン系重合体の重合活性末端に、加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基と、充填材表面へのポリマー濃縮能のある基とを有する変性剤Kの少なくとも1種を反応させてなる変性共役ジエン系重合体10〜100質量%と、(a−2)天然ゴム及び/又はジエン系合成ゴム90〜0質量%とからなるゴム成分と、その100質量部に対して、(B)無機充填材5〜200質量部を含み、かつ(C)前記無機充填材と結合可能な原子又は官能基と、チオエステル基及び/又はジチオエステル基と、を少なくとも有するシランカップリング剤を、前記(B)成分中の無機充填材に対して1〜25質量%の割合で含むことを特徴とするゴム組成物、及び該ゴム組成物を部材に用いてなるタイヤである。
【選択図】なし
Description
しかしながら、シリカは、その表面官能基であるシラノール基の水素結合により粒子同士が凝集する傾向にあり、ゴム中へのシリカ粒子の分散が不十分になるため、通常は、シリカ表面のシラノール基がアルコキシシランと縮合反応することを利用して種々のアルコキシシランが、シリカ表面処理剤あるいはカップリング剤として用いられている。例えば、最近シランカップリング剤として、アシルチオアルキルトリアルコキシシランなどの保護化メルカプトシランが開発されている(例えば、特許文献3参照)。この保護化メルカプトシランは、ゴム組成物中へのシリカの分散性を良くし、作業性を向上させると共に、転がり抵抗性能も向上させる作用を有している。
[1](A)(a−1)共役ジエン系重合体の重合活性末端に、加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基と、充填材表面へのポリマー濃縮能のある基とを有する変性剤Kの少なくとも1種を反応させてなる変性共役ジエン系重合体10〜100質量%と、(a−2)天然ゴム及び/又はジエン系合成ゴム90〜0質量%とからなるゴム成分と、その100質量部に対して、(B)無機充填材5〜200質量部を含み、かつ(C)前記無機充填材と結合可能な原子又は官能基と、チオエステル基及び/又はジチオエステル基と、を少なくとも有するシランカップリング剤を、前記(B)成分中の無機充填材に対して1〜25質量%の割合で含むことを特徴とするゴム組成物、
[2](a−1)変性共役ジエン系重合体の25℃におけるバウンドラバー量が、40質量%以上である上記[1]に記載のゴム組成物、
<バウンドラバー量の測定方法>
[変性共役ジエン系重合体100質量部と湿式シリカ(BET法比表面積:205±10m2/g)60質量部とを混練室内容積2リットルの密閉式混練装置を使用して、{(混練されているゴム組成物の体積/混練室内容積)×100}が60%にて混練りし、最高混練温度160℃に達した時点で、当該ゴム混練り物を密閉式混練装置から排出して、バウンドラバー量測定用ゴム組成物Mを得る。このゴム組成物M0.2gを1mm角に裁断して質量を測定した後、トルエン25mL中に加えて、25℃にて48時間放置した後、ガラス繊維フィルターでろ過し、トルエン不溶分を分離した後、分離したトルエン不溶分を25℃にて真空乾燥した後秤量し、下記式によりバウンドラバー量(%)を求める。
バウンドラバー量(%)={(トルエン不溶分の質量―ゴム組成物M中の湿式シリカの質量)/(ゴム組成物Mの質量―ゴム組成物M中の湿式シリカの質量)}×100
但し、シリカのBET法比表面積は、ISO 5794/1に準拠して測定する。]
[3]変性剤Kにおいて、加水分解処理後の塩基性官能基にプロトンが結合した化合物の共役酸のpKa値(酸解離定数Kaの逆数の対数値)が4以上である上記[1]又は[2]に記載のゴム組成物、
[4]変性剤Kが、充填材表面へのポリマー濃縮能のある基として、加水分解によりシラノール基を生成するケイ素含有基を有する上記[1]〜[3]のいずれかに記載のゴム組成物、
[5]加水分解によりシラノール基を生成するケイ素含有基が、ケイ素原子に直接結合するヒドロカルビロキシ基及び/又はハロゲン原子を有するケイ素含有基である上記[1]〜[4]のいずれかに記載のゴム組成物、
[7](a−1)変性共役ジエン系重合体が、共役ジエン系重合体の重合活性末端に変性剤Kを反応させた後、加水分解処理して得られたものである上記[1]〜[6]のいずれかに記載のゴム組成物、
[8](a−1)変性共役ジエン系重合体が、共役ジエン系重合体の重合活性末端に変性剤Kを反応させた後、加水分解処理の前又は後に、縮合促進剤の存在下に縮合反応処理して得られたものである上記[7]に記載のゴム組成物、
[9](a−1)変性共役ジエン系重合体が、重合末端に、シラノール基と塩基性官能基とを持つ変性基を有する上記[1]〜[8]のいずれかに記載のゴム組成物、
[10]加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基が、加水分解処理前において、保護された第1アミノ基又は保護された第2アミノ基である上記[1]〜[9]のいずれかに記載のゴム組成物、
[11]加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基を加水分解処理した後の塩基性官能基が、第1アミノ基又は第2アミノ基である上記[1]〜[9]のいずれかに記載のゴム組成物、
[12](C)シランカップリング剤における無機充填材と結合可能な官能基が、アルコキシシリル基である上記[1]〜[11]のいずれかに記載のゴム組成物、
[13](C)シランカップリング剤が、下記一般式(1)及び/又は(2)で表される化合物である上記[1]〜[12]のいずれかに記載のゴム組成物、
m、n、u、v、wはそれぞれ独立して1≦m≦20、0≦n≦20、0≦u≦3、0≦v≦2、0≦w≦1であり、かつ(u/2)+v+2w=2又は3である。
A部が複数である場合、複数のA部におけるZa u、Zb v及びZc wそれぞれにおいて、同一でも異なっていても良く、Bが複数である場合、複数のB部におけるZa u、Zb v及びZc wそれぞれにおいて、同一でも異なっても良い。]
[14]一般式(2)で表されるシランカップリング剤が、下記式(2−a)、(2−b)及び(2−c)で表される化合物の中から選ばれる少なくとも一種である上記[13]に記載のゴム組成物、
[16](a−1)変性共役ジエン系重合体が、変性芳香族ビニル−共役ジエン共重合体である上記[1]〜[15]のいずれかに記載のゴム組成物、
[17]重合活性末端を有する共役ジエン系重合体が、有機アルカリ金属化合物を重合開始剤とし、共役ジエン化合物一種以上、又は共役ジエン化合物一種以上と芳香族ビニル化合物とをアニオン重合させて得られたものである上記[1]〜[16]のいずれかに記載のゴム組成物、
[18]縮合促進剤を乾式配合してなる上記[1]〜[17]のいずれかに記載のゴム組成物、
[19]上記[1]〜[18]のいずれかに記載のゴム組成物を部材に用いたことを特徴とするタイヤ、及び
[20]部材がトレッドである上記[19]に記載のタイヤ、
を提供するものである。
本発明のゴム組成物は、(A)(a−1)共役ジエン系重合体の重合活性末端に、加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基と、充填材表面へのポリマー濃縮能のある基とを有する変性剤Kの少なくとも1種を反応させてなる変性共役ジエン系重合体10〜100質量%と、(a−2)天然ゴム及び/又はジエン系合成ゴム90〜0質量%とからなるゴム成分と、その100質量部に対して、(B)無機充填材5〜200質量部を含み、かつ(C)前記無機充填材と結合可能な原子又は官能基と、チオエステル基及び/又はジチオエステル基と、を少なくとも有するシランカップリング剤を、前記(B)成分中の無機充填材に対して1〜25質量%の割合で含むことを特徴とする。ここで、チオエステル基及びジチオエステル基は、いずれもチオカルボン酸エステル基であり、チオエステル基とは、チオ酸(S−酸)のエステル基をいい、ジチオエステル基とは、ジチオ酸のエステル基をいう。
((a−1)変性共役ジエン系重合体)
本発明のゴム組成物における(A)ゴム成分の一つを構成する(a−1)変性共役ジエン系重合体は、共役ジエン系重合体の重合活性末端に、加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基と、充填材表面へのポリマー濃縮能のある基とを有する変性剤Kの少なくとも1種を反応させてなる重合体である。
当該変性共役ジエン系重合体の製造に用いられる重合活性末端を有する共役ジエン系重合体は、共役ジエン化合物、又は芳香族ビニル化合物と共役ジエン化合物とを、有機アルカリ金属化合物を重合開始剤としてアニオン重合により重合したものであることが好ましい。
重合方法については特に制限はなく、溶液重合法、気相重合法、バルク重合法のいずれも用いることができるが、特に溶液重合法が好ましい。また、重合形式は、回分式及び連続式のいずれであっても良い。
また、芳香族ビニル化合物としては、例えばスチレン、α−メチルスチレン、1−ビニルナフタレン、3−ビニルトルエン、エチルビニルベンゼン、ジビニルベンゼン、4−シクロへキシルスチレン、2,4,6−トリメチルスチレン等が挙げられる。これらは単独で用いても良く、二種以上を組み合わせて用いても良いが、これらの中で、スチレンが特に好ましい。
これらの重合活性末端を有する共役ジエン系重合体は、該重合活性末端に、変性剤Kを反応させて、末端に所定の変性基を形成させるには、前記共役ジエン系重合体は、少なくとも10%のポリマー鎖がリビング性又は擬似リビング性を有するものであることが好ましい。
上述のアニオン重合の開始剤として用いられる有機アルカリ金属化合物としては、有機リチウム化合物が好ましい。有機リチウム化合物としては、特に制限はないが、ヒドロカルビルリチウム及びリチウムアミド化合物が好ましく用いられ、前者のヒドロカルビルリチウムを用いる場合には、重合開始末端にヒドロカルビル基を有し、かつ他方の末端が重合活性末端である共役ジエン系重合体が得られる。また、後者のリチウムアミド化合物を用いる場合には、重合開始末端にリチウムアミド化合物由来の窒素含有基を有し、他方の末端が重合活性末端である共役ジエン系重合体が得られる。
具体的には、反応に不活性な有機溶媒、例えば脂肪族、脂環族、芳香族炭化水素化合物等の炭化水素系溶媒中において、共役ジエン化合物又は共役ジエン化合物と芳香族ビニル化合物を、前記リチウム化合物を重合開始剤として、所望により、用いられるランダマイザーの存在下にアニオン重合させることにより、目的の重合活性末端を有する共役ジエン系重合体が得られる。
また、有機リチウム化合物を重合開始剤として用いた場合には、前述のランタン系列希土類金属化合物を含む触媒を用いた配位重合に比べ、活性末端を有する共役ジエン重合体のみならず、活性末端を有する共役ジエン−芳香族ビニル共重合体も効率よく得ることができる。
また、溶媒中の単量体濃度は、好ましくは5〜50質量%、より好ましくは10〜30質量%である。尚、共役ジエン化合物と芳香族ビニル化合物を用いて共重合を行う場合、仕込み単量体混合物中の芳香族ビニル化合物の含量は55質量%以下の範囲が好ましい。
この有機アルカリ金属化合物を重合開始剤としてアニオン重合させることにより得られる重合活性末端を有する共役ジエン系重合体としては、共役ジエン化合物一種以上と芳香族ビニル化合物との共重合体が好ましく、スチレン−ブタジエン共重合体がより好ましい。
このランタン系列希土類元素化合物を含む重合開始剤を用いて配位重合させることにより得られる重合活性末端を有する共役ジエン系重合体としては、共役ジエン化合物一種以上の単独重合体又は共重合体が好ましく、ポリブタジエンがより好ましい。
本発明において、(a−1)成分である変性共役ジエン系重合体は、前述のようにして得られた重合活性末端を有する共役ジエン系重合体の該重合活性末端に、変性剤Kを反応させることにより、得られた重合体である。
当該変性剤Kとしては、加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基と、充填材表面へのポリマー濃縮能のある基とを有する化合物が用いられる。
この変性剤Kとしては、加水分解処理後の塩基性官能基にプロトンが結合した化合物の共役酸のpKa値(酸解離定数Kaの逆数の対数値)が4以上であることが好ましい。
本発明に係る(C)シランカップリング剤のチオエステル基及びジチオエステル基は加水分解性であるので、塩基性官能基にプロトンが結合した化合物の共役酸のpKa値が4以上であると、(C)シランカップリング剤のカップリング反応を更に促進するので好ましい。
変性剤Kを加水分解した後の塩基性官能基にプロトンが結合した化合物の共役酸のpKa値は、「化学便覧基礎編改訂5版」に記載されたデータを用いる。但し、「化学便覧基礎編改訂5版」に記載のない化合物については、水溶液中、温度25℃で平沼産業(株)製自動滴定装置COM−1600にてpKa値を測定する。
換言すれば、当該変性剤Kにおいて、加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基が、加水分解処理前において、保護された第1アミノ基又は保護された第2アミノ基であることが好ましく、保護された第1アミノ基であることが更に好ましい。
なお、一般式(3)のAにおける、炭素数1〜20のヒドロカルビロキシ基及びハロゲン原子から選ばれる官能基の内、炭素数1〜20のヒドロカルビロキシ基が好ましい。また、R13O及びR14O、並びにAにおける炭素数1〜20のヒドロカルビロキシ基及びハロゲン原子の合計の10%以上が、加水分解処理により、Si原子と共にシラノール基を生成することが好ましい。
すなわち、当該変性共役ジエン系重合体が重合末端にシラノール基を有することにより、ゴム組成物中の無機充填材が特にシリカである場合、該シリカとの反応性がより高くなり、ゴム組成物中のシリカの分散性が向上し、ゴム組成物の低発熱性が向上するという大きな効果を奏する。また、シラノール基は揮発性有機化合物(VOC)を発生しないので、作業環境上好ましい。
前記一般式(3)のAにおける、ヘテロ原子含有官能基を含んでも良い炭素数1〜20のヒドロカルビル基は、炭素数1〜20のアルキル基若しくはアルケニル基、炭素数6〜20のアリール基、炭素数7〜20のアラルキル基等が挙げられ、炭素数1〜10のアルキル基が好ましく、炭素数1〜6のアルキル基がより好ましく、メチル基、エチル基、n−プロピル基、イソプロピル基、n−ブチル基、イソブチル基、sec−ブチル基、tert−ブチル基などが挙げられる。ここで、ヘテロ原子としては、酸素原子、窒素原子及び/又は硫黄原子が好ましく、ヘテロ原子含有官能基としては、エポキシ基、エステル基、エーテル基、保護された第1アミノ基、保護された第2アミノ基、第3アミノ基、チオエステル基(S−酸エステル基及びO−酸エステル基の双方を含む。)、ジチオエステル基、チオエーテル基などが挙げられる。
前記一般式(3)のAにおける、炭素数1〜20のヒドロカルビロキシ基としては、炭素数1〜20のアルコキシ基若しくはアルケニロキシ基、炭素数6〜20のアリーロキシ基、炭素数7〜20のアラルキロキシ基等が挙げられるが、これらの中で、良好な反応性を有する観点から、炭素数1〜10のアルコキシ基が好ましい。このアルコキシ基を構成するアルキル基は、直鎖状、枝分かれ状、環状のいずれであっても良い。このようなアルコキシ基としては、例えばエトキシ基、n−プロポキシ基、イソプロポキシ基、n−ブトキシ基、イソブトキシ基、sec−ブトキシ基、tert−ブトキシ基、各種ペントキシ基、各種ヘキソキシ基、各種ヘプトキシ基、各種オクトキシ基、各種デシロキシ基、シクロペチロキシ基、シクロヘキシロキシ基などを挙げることができ、これらの中で、反応性の観点から、炭素数2〜6のアルコキシ基が好ましく、特にエトキシ基が好ましい。A1、A2及びA3は同一であっても異なっていても良い。
また、前記一般式(3)のAにおけるハロゲン原子としては、例えば塩素原子や臭素原子が挙げられる。
炭素数2〜6のアルカンジイル基は、直鎖状、枝分かれ状のいずれであっても良く、例えばエチレン基、1,3−プロパンジイル基、1,2−プロパンジイル基、各種ブタンジイル基、各種ペンタンジイル基、各種ヘキサンジイル基などを挙げることができるが、これらの中で直鎖状のもの、例えばエチレン基、1,3−プロパンジイル基、1,4−ブタンジイル基、1,5−ペンタンジイル基、1,6−ヘキサンジイル基などが挙げられ、特に1,3−プロパンジイル基が好ましい。
前記一般式(3)で表される変性剤Kの具体例は、有機金属化合物を重合開始剤とするアニオン重合で得られる、重合活性末端を有する共役ジエン系重合体の変性剤として好適に用いられる。
本発明において、(a−1)成分の変性共役ジエン系重合体は、好適には、前述したアニオン重合により得られた、重合活性末端を有する共役ジエン系重合体の該活性末端に、前述した変性剤Kを反応させた後、水の存在下、酸性、中性又はアルカリ性の条件で加水分解処理して得られるが、所望により、共役ジエン系重合体の重合活性末端に変性剤Kを反応させた後、水の存在下、酸性、中性又はアルカリ性の条件で加水分解処理する前又は後に、縮合促進剤の存在下に縮合反応処理して得られたものであっても良い。
前記の変性剤Kを反応させる変性反応工程、その後加水分解処理する加水分解工程及び所望により縮合反応処理する縮合反応工程を以下に詳述する。
《変性反応工程》
この変性反応工程においては、重合活性末端有する共役ジエン系重合体の該活性末端に、上述の一般式(3)により表わされる変性剤Kを、該共役ジエン系重合体の活性末端に対して、好ましくは化学量論的量又はそれより過剰に加え、該重合体の活性末端と反応させる。
本発明における変性反応工程は、通常、重合反応と同じ温度、圧力条件で実施される。
この加水分解工程においては、変性反応工程又は所望による縮合反応工程終了後、水の存在下、酸性、中性又はアルカリ性の条件で加水分解反応が行われる。これにより、変性共役ジエン系重合体に結合した加水分解性官能基が効率よく加水分解され、シラノール基と、塩基性官能基とが変性共役ジエン系重合体の末端に生成する。
この加水分解反応に用いる水の量は、開始剤のLiなどのモル量より過剰なモル量、例えば2〜4倍のモル量であることが好ましい。加水分解時間は、通常10分〜数時間程度である。
なお、アルカリ性条件で加水分解反応を行う場合には、塩基性化合物として、水酸化ナトリウム、水酸化カリウムなどの水酸化アルカリ金属、好ましくは水酸化ナトリウムを加えることが望ましく、酸性条件で加水分解反応を行う場合には、酸性化合物として、塩酸、硫酸、硝酸などの無機酸、酢酸、ギ酸などのカルボン酸、四塩化ケイ素などを加えることが望ましい。
上述のように、(a−1)変性共役ジエン系重合体が、重合末端に、シラノール基と塩基性官能基とを持つ変性基を有することが好ましい。
本発明においては、共役ジエン系重合体の重合活性末端に変性剤Kを反応させた後、加水分解処理の前又は後に、縮合促進剤の存在下に縮合反応処理する縮合反応工程を設けることができる。
縮合反応で用いる縮合促進剤は、変性反応後、及び縮合反応開始前に添加することが好ましい。変性反応前に添加した場合、活性末端との直接反応が起こり、活性末端に所望の変性基が導入されない場合がある。また、縮合反応開始後に添加した場合、縮合促進剤が均一に分散せずその触媒性能が低下する場合がある。
縮合促進剤の添加時期としては、変性反応工程と加水分解工程との間に縮合反応工程を設ける場合には、通常変性反応開始5分〜5時間後、好ましくは変性反応開始15分〜1時間後である。加水分解工程後に縮合反応工程を設ける場合には、通常加水分解反応開始5分〜5時間後、好ましくは10分〜2時間後である。
前記金属元素を含む縮合促進剤としては、Ti、Sn、Bi、Zr及びAlの中から選ばれる少なくとも一種を含み、かつ前記金属のアルコキシド、カルボン酸塩又はアセチルアセトナート錯塩であるものが好適である。
具体的には、テトラキス(2−エチル−1,3−ヘキサンジオラト)チタン、テトラキス(2−メチル−1,3−ヘキサンジオラト)チタン、テトラキス(2−プロピル−1,3−ヘキサンジオラト)チタン、テトラキス(2−ブチル−1,3−ヘキサンジオラト)チタン、テトラキス(1,3−ヘキサンジオラト)チタン、テトラキス(1,3−ペンタンジオラト)チタン、テトラキス(2−メチル−1,3−ペンタンジオラト)チタン、テトラキス(2−エチル−1,3−ペンタンジオラト)チタン、テトラキス(2−プロピル−1,3−ペンタンジオラト)チタン、テトラキス(2−ブチル−1,3−ペンタンジオラト)チタン、テトラキス(1,3−ヘプタンジオラト)チタン、テトラキス(2−メチル−1,3−ヘプタンジオラト)チタン、テトラキス(2−エチル−1,3−ヘプタンジオラト)チタン、テトラキス(2−プロピル−1,3−ヘプタンジオラト)チタン、テトラキス(2−ブチル−1,3−ヘプタンジオラト)チタン、テトラキス(2−エチルヘキソキシ)チタン、テトラメトキシチタン、テトラエトキシチタン、テトラ−n−プロポキシチタン、テトライソプロポキシチタン、テトラ−n−ブトキシチタン、テトラ−n−ブトキシチタンオリゴマー、テトライソブトキシチタン、テトラ−sec−ブトキシチタン、テトラ−tert−ブトキシチタン、ビス(オレエート)ビス(2−エチルヘキサノエート)チタン、チタンジプロポキシビス(トリエタノールアミネート)、チタンジブトキシビス(トリエタノールアミネート)、チタントリブトキシステアレート、チタントリプロポキシステアレート、チタントリプロポキシアセチルアセトネート、チタンジプロポキシビス(アセチルアセトネート)、チタントリプロポキシ(エチルアセトアセテート)、チタンプロポキシアセチルアセトネートビス(エチルアセトアセテート)、チタントリブトキシアセチルアセトネート、チタンジブトキシビス(アセチルアセトネート)、チタントリブトキシエチルアセトアセテート、チタンブトキシアセチルアセトネートビス(エチルアセトアセテート)、チタンテトラキス(アセチルアセトネート)、チタンジアセチルアセトネートビス(エチルアセトアセテート)、ビス(2−エチルヘキサノエート)チタンオキサイド、ビス(ラウレート)チタンオキサイド、ビス(ナフテネート)チタンオキサイド、ビス(ステアレート)チタンオキサイド、ビス(オレエート)チタンオキサイド、ビス(リノレート)チタンオキサイド、テトラキス(2−エチルヘキサノエート)チタン、テトラキス(ラウレート)チタン、テトラキス(ナフテネート)チタン、テトラキス(ステアレート)チタン、テトラキス(オレエート)チタン、テトラキス(リノレート)チタン、チタンジ−n−ブトキサイド(ビス−2,4−ペンタンジオネート)、チタンオキサイドビス(ステアレート)、チタンオキサイドビス(テトラメチルヘプタンジオネート)、チタンオキサイドビス(ペンタンジオネート)、チタンテトラ(ラクテート)などが挙げられる。
なかでも、テトラキス(2−エチル−1,3−ヘキサンジオラト)チタン、テトラキス(2−エチルヘキソキシ)チタン、チタンジ−n−ブトキサイド(ビス−2,4−ペンタンジオネート)が好ましい。
(b)ジルコニウムのアルコキシド
(c)ジルコニウムのカルボン酸塩
(d)アルミニウムのアルコキシド
(e)アルミニウムのカルボン酸塩
また、縮合反応を有機溶媒中に水が液滴として分散している系又は水溶液中で行っても良い。
縮合反応時の温度は20〜180℃が好ましく、さらに好ましくは30〜170℃、特に好ましくは50〜170℃である。縮合反応時の温度を前記範囲にすることによって、縮合反応を効率よく進行完結することができ、得られる変性共役ジエン系重合体の経時変化によるポリマーの老化反応などによる品質の低下などを抑えることができる。
縮合反応時の反応系の圧力は、好ましくは0.01〜20MPa、より好ましくは0.05〜10MPaである。
縮合反応の形式については特に制限はなく、バッチ式反応器を用いても、多段連続式反応器などの装置を用いて連続式で行っても良い。また、この縮合反応と脱溶媒を同時に行っても良い。
その後、水蒸気を吹き込んで溶媒の分圧を下げるスチームストリッピング等の脱溶媒処理や真空乾燥処理を経て当該変性共役ジエン系重合体が得られる。
前記変性反応工程において、共役ジエン系重合体の重合末端に変性剤Kを反応させて導入された変性基においては、前述した加水分解工程や、スチームストリッピングなどの水蒸気を用いる脱溶媒処理工程において、シラノール基が生成すると共に、第1アミノ基又は第2アミノ基などの塩基性官能基が生成する。
このような加水分解による、シラノール基やアミノ基などの保護基を脱離させる操作は、変性反応工程終了から、脱溶媒して乾燥ポリマーとなるまでのいずれの段階で行っても良い。
このようにして得られた(a−1)成分の変性共役ジエン系重合体は、重合末端に変性剤として、塩基性官能基を有すると共に、充填材表面へのポリマー濃縮能のあるシラノール基などを有するケイ素含有基が導入されたものとなる。
バウンドラバー量(%)は以下のようにして測定される。
変性共役ジエン系重合体100質量部と湿式シリカ(BET法比表面積:205±10m2/g、東ソウ・シリカ株式会社製、商品名「ニプシルAQ」)60質量部とを混練室内容積2リットルの密閉式混練装置を使用して、{(混練されているゴム組成物の体積/混練室内容積)×100}が60%にて混練りし、最高混練温度160℃に達した時点で、当該ゴム混練り物を排出して、バウンドラバー量測定用ゴム組成物Mを得る。
このゴム組成物M0.2gを1mm角に裁断して質量を測定した後、トルエン25mL中に加えて、25℃にて48時間放置した後、ADVANTEC社製ガラス繊維フィルターでろ過し、トルエン不溶分を分離した後、分離したトルエン不溶分を25℃にて真空乾燥した後秤量し、下記式によりバウンドラバー量を求める。
バウンドラバー量(%)={(トルエン不溶分の質量―ゴム組成物M中の湿式シリカの質量)/(ゴム組成物Mの質量―ゴム組成物M中の湿式シリカの質量)}×100
なお、シリカのBET法比表面積は、ISO 5794/1に準拠して測定する。
本発明のゴム組成物における(A)ゴム成分のもう一つの成分を構成する(a−2)天然ゴム及び/又はジエン系合成ゴムにおいて、ジエン系合成ゴムとしては、例えばポリブタジエン、ポリイソプレン、ポリブタジエン−ポリイソプレン共重合体、スチレン−ブタジエン共重合体、スチレン−イソプレン共重合体、スチレン−イソプレン−ブタジエン三元共重合体、エチレン−プロピレン−ジエン三元共重合体、ブチルゴム、ハロゲン化ブチルゴム等が挙げられる。
この(a−2)成分は、一種を単独で用いても良く、二種以上を組み合わせて用いても良い。
なお、(A)ゴム成分において、(a−2)成分である天然ゴム及び/又はジエン系合成ゴムを必須成分として用いる場合は、(a−1)成分10〜95質量%と(a−2)成分90〜50質量%とからなることが好ましく、(a−1)成分30〜95質量%と(a−2)成分70〜5質量%とからなることがより好ましく、(a−1)成分50〜95質量%と(a−2)成分50〜5質量%とからなることが更に好ましい。
本発明のゴム組成物においては、(B)成分として無機充填材を含有する。この(B)成分の無機充填材は、本発明の効果を好適に発揮させる観点から、ゴム成分100質量部に対して、5〜200質量部を含むことを要し、10〜200質量部を含むことが好ましく、10〜150質量部を含むことが更に好ましく、10〜120質量部を含むことが特に好ましい。
本発明のゴム組成物においては、無機充填材として、シリカや、シリカ以外の無機系補強性充填材を用いることができる。
本発明において、無機充填材として用いるシリカとしては市販のあらゆるものが使用でき、なかでも湿式シリカ、乾式シリカ、コロイダルシリカを用いるのが好ましく、湿式シリカを用いるのが特に好ましい。シリカのBET法比表面積としては100m2/g以上のものが好ましく、より好ましくは150m2/g以上、特に好ましくは170m2/g以上である。このようなシリカとしては東ソーシリカ社製、商品名「ニプシルAQ」(BET法比表面積 =205m2/g)、「ニプシルKQ」、デグッサ社製商品名「ウルトラジルVN3」(BET法比表面積 =175m2/g)等の市販品を用いることができる。
シリカ以外の無機系補強性充填材としては、下記一般式(5)で表される化合物を用いることができる。
dM3・xSiOy・zH2O ・・・(5)
ここで、一般式(5)中、M3は、アルミニウム、マグネシウム、チタン、カルシウム、及びジルコニウムからなる群から選ばれる金属、これらの金属の酸化物又は水酸化物、及びそれらの水和物、又はこれらの金属の炭酸塩から選ばれる少なくとも一種であり、d、x、y及びzは、それぞれ1〜5の整数、0〜10の整数、2〜5の整数、及び0〜10の整数である。
尚、一般式(5)において、x、zがともに0である場合には、該無機化合物はアルミニウム、マグネシウム、チタン、カルシウム及びジルコニウムから選ばれる少なくとも1つの金属、金属酸化物又は金属水酸化物となる。
前記一般式(5)で表わされる無機充填材としては、γ−アルミナ、α−アルミナ等のアルミナ(Al2O3)、ベーマイト、ダイアスポア等のアルミナ一水和物(Al2O3・H2O)、ギブサイト、バイヤライト等の水酸化アルミニウム[Al(OH)3]、炭酸アルミニウム[Al2(CO3)2]、水酸化マグネシウム[Mg(OH)2]、酸化マグネシウム(MgO)、炭酸マグネシウム(MgCO3)、タルク(3MgO・4SiO2・H2O)、アタパルジャイト(5MgO・8SiO2・9H2O)、チタン白(TiO2)、チタン黒(TiO2n-1)、酸化カルシウム(CaO)、水酸化カルシウム[Ca(OH)2]、酸化アルミニウムマグネシウム(MgO・Al2O3)、クレー(Al2O3・2SiO2)、カオリン(Al2O3・2SiO2・2H2O)、パイロフィライト(Al2O3・4SiO2・H2O)、ベントナイト(Al2O3・4SiO2・2H2O)、ケイ酸アルミニウム(Al2SiO5 、Al4・3SiO4・5H2O等)、ケイ酸マグネシウム(Mg2SiO4、MgSiO3等)、ケイ酸カルシウム(Ca2・SiO4等)、ケイ酸アルミニウムカルシウム(Al2O3・CaO・2SiO2等)、ケイ酸マグネシウムカルシウム(CaMgSiO4)、炭酸カルシウム(CaCO3)、酸化ジルコニウム(ZrO2)、水酸化ジルコニウム[ZrO(OH)2・nH2O]、炭酸ジルコニウム[Zr(CO3)2]、各種ゼオライトのように電荷を補正する水素、アルカリ金属又はアルカリ土類金属を含む結晶性アルミノケイ酸塩などが使用できる。また、前記一般式(5)中のM3がアルミニウム金属、アルミニウムの酸化物又は水酸化物、及びそれらの水和物、又はアルミニウムの炭酸塩から選ばれる少なくとも一つである場合が好ましい。
一般式(5)で表されるこれらの無機化合物は、単独で使用しても良いし、2種以上を混合して使用しても良い。これらの無機系補強性充填材の平均粒径は、混練作業性、耐摩耗性及びウェットグリップ性能のバランスなどの観点から、0.01〜10μmの範囲が好ましく、0.05〜5μmの範囲がより好ましい。
本発明においては、無機充填材としては、特にシリカが好適である。
本発明のゴム組成物は、所望により、上述の無機充填材に加えてカーボンブラックを含有しても良い。このカーボンブラックとしては、特に制限はなく、例えばGPF、FEF、SRF、HAF、N339、IISAF、ISAF、SAF等が用いられ、窒素吸着比表面積(N2SA、JIS K 6217−2:2001に準拠して測定する)が20〜250m2/gであることが好ましい。このカーボンブラックは1種を単独で用いても良く、2種以上を組み合わせて用いても良い。
本発明において、カーボンブラックは、無機充填材には含まれない。
本発明のゴム組成物が充填材全量中、(B)無機充填材として、好ましくはシリカ5〜95質量%と、カーボンブラック95〜5質量%と、を含むことにより、低発熱性及び耐摩耗性の向上したゴム組成物となる。
本発明のゴム組成物において、(C)成分として用いるシランカップリング剤は、前述した(B)無機充填材と結合可能な原子又は官能基、及びチオエステル基及び/又はジチオエステル基(すなわち保護されたメルカプト基)を少なくとも有する化合物である。
前記の無機充填材と結合可能な官能基としては、アルコキシシリル基を好ましく挙げることができる。
このような(C)シランカップリング剤としては、例えば下記の(C−1)化合物及び/又は(C−2)化合物を用いることができる。
当該(C−1)化合物としては、下記一般式(1)
で表されるシランカップリング剤が用いられる。
また、R4で表される炭素数1〜18の二価の炭化水素基としては、例えば炭素数1〜18のアルキレン基、炭素数2〜18のアルケニレン基、炭素数5〜18のシクロアルキレン基、炭素数6〜18のシクロアルキルアルキレン基、炭素数6〜18のアリーレン基、炭素数7〜18のアラルキレン基を挙げることができる。前記アルキレン基及びアルケニレン基は、直鎖状、枝分かれ状のいずれであっても良く、前記シクロアルキレン基、シクロアルキルアルキレン基、アリーレン基及びアラルキレン基は、環上に低級アルキル基などの置換基を有していても良い。
このR4としては、炭素数1〜6のアルキレン基が好ましく、特に直鎖状アルキレン基、例えばメチレン基、エチレン基、トリメチレン基、テトラメチレン基、ペンタメチレン基、ヘキサメチレン基を好ましく挙げることができる。
これらのシランカップリング剤の中で、下記式(1−a)
本発明におけるゴム組成物に、当該(c−1)シランカップリング剤を用いることにより、ゴム加工時の作業性に優れると共に、低発熱及び耐摩耗性の良好なタイヤを与えることができる。
当該(c−2)化合物としては、下記一般式(2)
m、n、u、v、wはそれぞれ独立して1≦m≦20、0≦n≦20、0≦u≦3、0≦v≦2、0≦w≦1であり、かつ(u/2)+v+2w=2又は3である。
A部が複数である場合、複数のA部におけるZa u、Zb v及びZc wそれぞれにおいて、同一でも異なっていても良く、Bが複数である場合、複数のB部におけるZa u、Zb v及びZc wそれぞれにおいて、同一でも異なっても良い。]
で表されるシランカップリング剤が用いられる。
で示される構造を有する化合物の中から選ばれる少なくとも一種を挙げることができる。
前記式(2−a)で表されるシランカップリング剤としては、Momentive Performance Materials社が、商標「NXT Low−V Silane」として、また、式(2−b)で表されるシランカップリング剤としては、Momentive Performance Materials社が、商標「NXT Ultra Low−V Silane」として、さらに、化学式(2−c)で表されるシランカップリング剤としては、Momentive Performance Materials社が、商標、「NXT Z」として上市している。
また、作業中における揮発性有機化合物(VOC)の発生をできるだけ抑制して、加工性の良好なゴム組成物を得る場合には、当該(C)成分のシランカップリング剤として、前記VOCの発生がないか、発生があっても極めて少ないものが好ましい。
このようなシランカップリング剤としては、前述した式(2−b)及び式(2−c)で表される(c−2)化合物を挙げることができる。
当該縮合促進剤の内容については、前述した変性共役ジエン系重合体の製造方法における縮合反応において説明したとおりであり、特にチタン原子を含む縮合促進剤が好ましい。
当該縮合促進剤をゴム組成物の調製時に添加する場合には、第1混練段階において、他成分と、通常20〜185℃程度、好ましくは60〜175℃の温度で混練りすることが好ましい。
ゴム組成物における当該縮合促進剤の含有量は、ゴム成分100質量部当たり、シリカとシラノールの反応性の観点から0.1〜10質量部であることが好ましく、0.5〜5質量部であることがより好ましい。
本発明のゴム組成物は、硫黄架橋性であることが好ましく、加硫剤として硫黄が好適に用いられる。その使用量としては、(A)ゴム成分100質量部に対し、硫黄分(硫黄及び硫黄供与剤の硫黄分の合計量)を0.1〜10質量部配合することが好ましい。この範囲であれば、加硫ゴム組成物の必要な弾性率及び強度を確保すると共に低燃費性を得ることができるからである。この観点から、硫黄分を0.2〜8質量部配合することがさらに好ましい。
本発明のタイヤは、前述した本発明のゴム組成物を部材に用いたことを特徴とする。部材としては、トレッド、ベーストレット、サイドウォール、サイド補強ゴム及びビードフィラーを好ましく挙げることができ、これらのいずれかに、本発明のゴム組成物を用いることができるが、トレッドに用いることが好ましく、特にキャップトレッドに用いることが好ましい。
本発明のゴム組成物をトレッドに用いたタイヤ、特に空気入りタイヤは、転がり抵抗が低く低燃費性に優れると共に、耐摩耗性に優れる。なお、本発明のタイヤに充填する気体としては、通常の或いは酸素分圧を変えた空気、又は窒素等の不活性ガスが挙げられる。本発明のゴム組成物をトレッドに用いる場合は、例えばトレッド用部材に押出し加工され、タイヤ成形機上で通常の方法により貼り付け成形され、生タイヤが成形される。この生タイヤを加硫機中で加熱加圧して、タイヤが得られる。
<変性共役ジエン系重合体についての測定>
(1)重量平均分子量(Mw)
GPC[東ソー製、HLC−8020]により検出器として示差屈折計を用いて測定し、単分散ポリスチレンを標準としたポリスチレン換算で示した。なお、カラムはGMHXL[東ソー製]で、移動相はテトラヒドロフランである。
(2)変性SBRのスチレン含有量(質量%)
270MHZ 1H−NMRによって求めた。
(3)ブタジエン部分中のビニル結合含有量(質量%)
フーリエ変換赤外分光光度計(商品名「FT/IR−4100」、日本分光社製)を使用し、特開2005−015590号公報に記載されたフーリエ変換赤外分光法によって、ブタジエン部分中のビニル結合含有量(%)を測定した。
アルコキシシリル基及びハロゲン原子の加水分解量については、エトキシシリル基の例で説明する。1H−NMRにおいて、変性された重合体のSiOCH2CH3に特徴づけられる3.6−3.7ppm付近の多量バンドと、ベース部分の数平均分子量から計算を行い、重合体のアルコキシシラン量M(%)を算出した。GPCの注入サンプル量対比のベース同等成分のピーク面積から、GPCでの未カップリング成分の比率RGPC%を計算した。カップリングなどの後反応成分を減ずるために、前記M(%)とRGPC%との差を求め、これを、シラノール生成数を100として、計算した。シラノール生成率に用いる数平均分子量は、Mark−Houwink式で校正したGPCから求めた数平均分子量を適用した。
(5)バウンドラバー量(%)
上述の方法により、各変性共役ジエン系重合体のバウンドラバー量(%)を測定した。
<変性剤Kについての測定>
(6)pKa値の測定
上述のように、pKa値の数値は、「化学便覧基礎編改訂5版」に記載されたデータを用いた。但し、「化学便覧基礎編改訂5版」に記載のない化合物については、水溶液中、温度25℃で平沼産業(株)製自動滴定装置COM−1600にてpKa値を測定した。
(7)加硫ゴム組成物の動的損失正接(tanδ)
粘弾性測定装置(レオメトリックス社製)を使用し、温度60℃、歪み5%、周波数15Hzでtanδを測定した。比較例1又は9のtanδを100として下記式にて指数表示した。指数値が小さい程、低発熱性であり、ヒステリシスロスが小さいことを示す。
動的損失正接(tanδ)指数={(供試加硫ゴム組成物のtanδ)/(比較例1又は9の加硫ゴム組成物のtanδ)}×100
(9)加硫ゴム組成物の耐摩耗性
JIS K 6264:2005に準拠し、ランボーン型摩耗試験機を用いて、室温におけるスリップ率が25%の摩耗量を測定し、比較例1又は9の摩耗量の逆数を100として下記式にて指数表示した。指数の大きいほど、耐摩耗性に優れていることを示す。
耐摩耗性指数={(比較例1又は9の加硫ゴム組成物の摩耗量)/(供試加硫ゴム組成物の摩耗量)}×100
窒素雰囲気下、攪拌機を備えたガラスフラスコ中のジクロロメタン溶媒400ml中にアミノシラン部位として36gの3−アミノプロピルメチルジエトキシシラン(Gelest社製)を加えた後、さらに保護部位として塩化トリメチルシラン(Aldrich社製)48ml、トリエチルアミン53mlを溶液中に加え、17時間室温下で攪拌し、その後反応溶液をエバポレーターにかけることにより溶媒を取り除き、反応混合物を得、さらに得られた反応混合物を5mm/Hg条件下で減圧蒸留することにより、130〜135℃留分として有機シラン化合物[N,N−ビス(トリメチルシリル)−3−ジエトキシ(メチル)シリル−1−プロパンアミン]を40g得た。
変性剤K−A: N−メチル−N−トリメチルシリル−3−ジエトキシ(メチル)シリル−1−プロパンアミン:化学式(3−a)
変性剤K−B:N−トリメチルシリル−N−グリシジル−3−ジエトキシ(メチル)シリル−1−プロパンアミン:化学式(3−b)
変性剤K−C: N,N−ビス(トリメチルシリル)−3−ジエトキシ(メチル)シリル−1−プロパンアミン:化学式(3−c)
変性剤K−D: プロピル(ジメチル)エトキシシラン:化学式(4−a)
変性剤K−E: N−メチル−N−トリメチルシリル−3−ジメチル(エトキシ)シリル−1−プロパンアミン:化学式(4−b)
変性剤K−F: 3−トリメチルシリルオキシプロピル(ジエトキシ)メチルシラン:化学式(4−c)
変性剤K−G: N−[3−(ジエトキシ)メチルシリルプロピル]−N−フェニルアセトアミド:化学式(4−d)
変性剤K−H: メチルトリエトキシシラン:化学式(4−e)
なお、第1表において、「<<」はpKa値がK−GのpKa値(0.61)よりはるかに小さいことを表す。
<活性末端を有するSBRの製造>
乾燥し、窒素置換した800mLの耐圧ガラス容器に、1,3−ブタジエンのシクロヘキサン溶液及びスチレンのシクロヘキサン溶液を、1,3−ブタジエン60g及びスチレン15gとなるように加え、2,2−ジテトラヒドロフリルプロパン0.70mmolを加え、さらにn−ブチルリチウム(BuLi)0.70mmolを加えた後、50℃の温水浴中で1.5時間重合反応を行なった。この際の重合転化率は、ほぼ100%であった。
<変性反応工程>
次に、重合反応系に変性剤K−AであるN−メチル−N−トリメチルシリル−3−ジエトキシ(メチル)シリル−1−プロパンアミンのリチウム(Li)対比等モルとなる量を加えて、さらに50℃で30分間変性反応を行った。
<加水分解工程及びその後の工程>
その後、重合反応系に、1モル/リットルの水酸化ナトリウム(NaOH)水溶液を少しずつ加え、pH10.5になった段階で、水をリチウム(Li)対比3倍のモル量加え、30分間撹拌した。次に、重合反応系に、2,6−ジ−tert−ブチル−p−クレゾール(BHT)のイソプロパノール溶液を加えて重合反応を停止させた。その後、水蒸気を吹き込んで溶媒の分圧を下げて(スチームストリッピング)脱溶媒した後、真空乾燥して変性SBR−Aを得た。
製造例1において、変性剤K−Aの代わりに、変性剤K−BであるN−トリメチルシリル−N−グリシジル−3−ジエトキシ(メチル)シリル−1−プロパンアミンを用いた以外は、製造例1と同様にして、変性SBR−Bを製造した(製造例2)。
同様にして、変性剤K−Aの代わりに、変性剤K−CであるN,N−ビス(トリメチルシリル)−3−ジエトキシ(メチル)シリル−1−プロパンアミンを用いて変性SBR−Cを製造した(製造例3)。
製造例4 変性SBR−C−2の製造
製造例3の変性反応工程(変性剤K−C)に続いて、縮合促進剤としてテトラキス(2−エチル−1,3−ヘキサンジオラト)チタン1.50gを加え、更に15分間攪拌した。その後、製造例3と同様にして加水分解工程及びその後の工程を経て、変性SBR−C−2を得た。
変性剤K−Aの代わりに、変性剤K−Dであるプロピル(ジメチル)エトキシシランを用いて変性SBR−Eを製造し(比較製造例1)、変性剤K−Aの代わりに、変性剤K−EであるN−メチル−N−トリメチルシリル−3−ジメチル(エトキシ)シリル−1−プロパンアミンを用いて変性SBR−Eを製造し(比較製造例2)、変性剤K−Aの代わりに、変性剤K−Fである3−トリメチルシリルオキシプロピル(ジエトキシ)メチルシランを用いて変性SBR−Fを製造し(比較製造例3)、変性剤K−GであるN−[3−(ジエトキシ)メチルシリルプロピル]−N−フェニルアセトアミドを用いて変性SBR−Gを製造し(比較製造例4)、変性剤K−Hであるメチルトリエトキシシランを用いて変性SBR−Hを製造した(比較製造例5)。
以上のようにして得られた変性SBR−A乃至変性SBR−Hの重量平均分子量、スチレン含有量及びブタジエン部分のビニル結合含有量並びにシラノール生成率及びバウンドラバー量を第5表及び第6表に示す。
製造例1〜4及び比較製造例1〜5で得られた変性SBR−A〜変性SBR−C−2及び変性SBR−D〜Hを用い、第2表、第3表及び第4表の配合処方に従い、実施例1〜7及び比較例1〜9の16種類のゴム組成物を調製した。
次に、これら16種類のゴム組成物を空気入りタイヤのキャップトレッド(トレッドの踏面側)に配設して、それぞれタイヤサイズ215/45ZR17の乗用車用空気入りタイヤを常法に従って製造し、それら16種類の空気入りタイヤのキャップトレッドからtanδ測定用サンプル及び耐摩耗性測定用サンプルを切り出して、動的損失正接(tanδ)及びランボーン型摩耗試験による摩耗量を上記の方法で測定した。tanδ及び耐摩耗性の評価結果は第5表及び第6表に示す。
1)変性共役ジエン系重合体: 製造例1〜4及び比較製造例1、2、4で得られた変性SBR−A〜変性SBR−C−2及び変性SBR−D、E、G
2)ポリイソプレンゴム: JSR株式会社製、商品名「IR2200」
3)軟化剤: 三共油化工業株式会社製、商品名「A/Oミックス」
4)シリカ: 東ソー・シリカ(株)、商品名「ニプシルAQ」
5)カーボンブラック: ISAF、旭カーボン(株)製、商品名「ノクラック6C」
6)シランカップリング剤: 第5表及び第6表に示すシランカップリング剤
7)老化防止剤6C: N−(1,3−ジメチルブチル)−N’−フェニル−p−フェニレンジアミン:大内新興化学工業(株)製、商品名「ノクラック6C」
8)縮合促進剤: 第5表に示すように、実施例4のゴム組成物に第1混練段階でテトラキス(2−エチル−1,3−ヘキサンジオラト)チタンを2質量部配合した。
9)加硫促進剤DPG: 1,3−ジフェニルグアニジン:大内新興化学工業(株)製、商品名「ノクセラーD」
10)加硫促進剤DM: ジベンゾチアゾリルジスルフィド:大内新興化学工業(株)製、商品名「ノクセラーDM」
11)加硫促進剤CZ: N−シクロヘキシル−2−ベンゾチアゾリルスルフェンアミド:大内新興化学工業社製、商品名「ノクセラーCZ」
1)変性共役ジエン系重合体: 製造例1〜2及び比較製造例5で得られた変性SBR−A〜B及び変性SBR−H
2)天然ゴム: RSS#3
3)〜4)は、第2表と同じ
5)シランカップリング剤: 第5表及び第6表に示すシランカップリング剤
6)老化防止剤6C: N−(1,3−ジメチルブチル)−N’−フェニル−p−フェニレンジアミン:大内新興化学工業(株)製、商品名「ノクラック6C」
7)加硫促進剤DPG: 1,3−ジフェニルグアニジン:大内新興化学工業(株)製、商品名「ノクセラーD」
8)加硫促進剤DM: ジベンゾチアゾリルジスルフィド:大内新興化学工業(株)製、商品名「ノクセラーDM」
9)加硫促進剤CZ: N−シクロヘキシル−2−ベンゾチアゾリルスルフェンアミド:大内新興化学工業社製、商品名「ノクセラーCZ」
1)変性共役ジエン系重合体: 比較製造例3で得られた変性SBR−F
2)〜9)は、第4表と同じ
NXT: Momentive Performance Materials社製、商品名「NXT」(登録商標)
S2.5: デグサ社製、商品名「Si75」(登録商標)、化学名:ビス(3−トリエトキシシリルプロピル)ポリスルフィドの混合物(一分子中のSの数が平均2.4)
NXT: Momentive Performance Materials社製、商品名「NXT」(登録商標)
NXT Z: Momentive Performance Materials社製、商品名「NXT Z」(登録商標)
Claims (20)
- (A)(a−1)共役ジエン系重合体の重合活性末端に、加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基と、充填材表面へのポリマー濃縮能のある基とを有する変性剤Kの少なくとも1種を反応させてなる変性共役ジエン系重合体10〜100質量%と、(a−2)天然ゴム及び/又はジエン系合成ゴム90〜0質量%とからなるゴム成分と、その100質量部に対して、(B)無機充填材5〜200質量部を含み、かつ(C)前記無機充填材と結合可能な原子又は官能基と、チオエステル基及び/又はジチオエステル基と、を少なくとも有するシランカップリング剤を、前記(B)成分中の無機充填材に対して1〜25質量%の割合で含むことを特徴とするゴム組成物。
- (a−1)変性共役ジエン系重合体の25℃におけるバウンドラバー量が、40質量%以上である請求項1に記載のゴム組成物。
<バウンドラバー量の測定方法>
変性共役ジエン系重合体100質量部と湿式シリカ(BET法比表面積:205±10m2/g)60質量部とを混練室内容積2リットルの密閉式混練装置を使用して、{(混練されているゴム組成物の体積/混練室内容積)×100}が60%にて混練りし、最高混練温度160℃に達した時点で、当該ゴム混練り物を密閉式混練装置から排出して、バウンドラバー量測定用ゴム組成物Mを得る。このゴム組成物M0.2gを1mm角に裁断して質量を測定した後、トルエン25mL中に加えて、25℃にて48時間放置した後、ガラス繊維フィルターでろ過し、トルエン不溶分を分離した後、分離したトルエン不溶分を25℃にて真空乾燥した後秤量し、下記式によりバウンドラバー量(%)を求める。
バウンドラバー量(%)={(トルエン不溶分の質量―ゴム組成物M中の湿式シリカの質量)/(ゴム組成物Mの質量―ゴム組成物M中の湿式シリカの質量)}×100
但し、シリカのBET法比表面積は、ISO 5794/1に準拠して測定する。 - 変性剤Kにおいて、加水分解処理後の塩基性官能基にプロトンが結合した化合物の共役酸のpKa値(酸解離定数Kaの逆数の対数値)が4以上である請求項1又は2に記載のゴム組成物。
- 変性剤Kが、充填材表面へのポリマー濃縮能のある基として、加水分解によりシラノール基を生成するケイ素含有基を有する請求項1〜3のいずれかにに記載のゴム組成物。
- 加水分解によりシラノール基を生成するケイ素含有基が、ケイ素原子に直接結合するヒドロカルビロキシ基及び/又はハロゲン原子を有するケイ素含有基である請求項1〜4のいずれかに記載のゴム組成物。
- 加水分解により、ヒドロカルビロキシ基及び/又はハロゲン原子の10%以上がシラノール基を生成する請求項5に記載のゴム組成物。
- (a−1)変性共役ジエン系重合体が、共役ジエン系重合体の重合活性末端に変性剤Kを反応させた後、加水分解処理して得られたものである請求項1〜6のいずれかに記載のゴム組成物。
- (a−1)変性共役ジエン系重合体が、共役ジエン系重合体の重合活性末端に変性剤Kを反応させた後、加水分解処理の前又は後に、縮合促進剤の存在下に縮合反応処理して得られたものである請求項7に記載のゴム組成物。
- (a−1)変性共役ジエン系重合体が、重合末端に、シラノール基と塩基性官能基とを持つ変性基を有する請求項1〜8のいずれかに記載のゴム組成物。
- 加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基が、加水分解処理前において、保護された第1アミノ基又は保護された第2アミノ基である請求項1〜9のいずれかに記載のゴム組成物。
- 加水分解処理後の官能基が塩基性官能基であるもの、及び加水分解により脱保護可能な基でプロトンが保護されてなる塩基性官能基の中から選ばれる少なくとも一種の官能基を加水分解処理した後の塩基性官能基が、第1アミノ基又は第2アミノ基である請求項1〜9のいずれかに記載のゴム組成物。
- (C)シランカップリング剤における無機充填材と結合可能な官能基が、アルコキシシリル基である請求項1〜11のいずれかに記載のゴム組成物。
- (C)シランカップリング剤が、下記一般式(1)及び/又は(2)で表される化合物である請求項1〜12のいずれかに記載のゴム組成物。
m、n、u、v、wはそれぞれ独立して1≦m≦20、0≦n≦20、0≦u≦3、0≦v≦2、0≦w≦1であり、かつ(u/2)+v+2w=2又は3である。
A部が複数である場合、複数のA部におけるZa u、Zb v及びZc wそれぞれにおいて、同一でも異なっていても良く、Bが複数である場合、複数のB部におけるZa u、Zb v及びZc wそれぞれにおいて、同一でも異なっても良い。] - (B)無機充填材がシリカである請求項1〜14のいずれかに記載のゴム組成物。
- (a−1)変性共役ジエン系重合体が、変性芳香族ビニル−共役ジエン共重合体である請求項1〜15のいずれかに記載のゴム組成物。
- 重合活性末端を有する共役ジエン系重合体が、有機アルカリ金属化合物を重合開始剤とし、共役ジエン化合物一種以上、又は共役ジエン化合物一種以上と芳香族ビニル化合物とをアニオン重合させて得られたものである請求項1〜16のいずれかに記載のゴム組成物。
- 縮合促進剤を乾式配合してなる請求項1〜17のいずれかに記載のゴム組成物。
- 請求項1〜18のいずれかに記載のゴム組成物を部材に用いたことを特徴とするタイヤ。
- 部材がトレッドである請求項19に記載のタイヤ。