JP2010222354A - 自己結合多成分歯科材料 - Google Patents
自己結合多成分歯科材料 Download PDFInfo
- Publication number
- JP2010222354A JP2010222354A JP2010063379A JP2010063379A JP2010222354A JP 2010222354 A JP2010222354 A JP 2010222354A JP 2010063379 A JP2010063379 A JP 2010063379A JP 2010063379 A JP2010063379 A JP 2010063379A JP 2010222354 A JP2010222354 A JP 2010222354A
- Authority
- JP
- Japan
- Prior art keywords
- paste
- dental material
- material according
- filler
- basic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】第一のペーストおよび第二のペーストを含有する硬化性多成分歯科材料であって、この第一のペーストは、(i)1種以上の酸基を有さないラジカル重合性モノマーおよび(ii)塩基性充填材を含有し、そしてこの第二のペーストは、(iii)1種以上の酸基含有ラジカル重合性モノマーおよび(iv)非塩基性充填材を含有する。この多成分歯科材料は、少なくともペースト(A)または(B)の中に、ラジカル重合のための少なくとも1種の開始剤(v)を含有する。
【選択図】なし
Description
(項目1)
(A)第一のペーストであって、
(i)1種以上の酸基を含まないラジカル重合性モノマーおよび
(ii)充填材
を含有する、第一のペースト、ならびに
(B)第二のペーストであって、
(iii)1種以上の酸基含有ラジカル重合性モノマーおよび
(iv)非塩基性充填材
を含有する、第二のペースト
を含有する硬化性多成分歯科材料であって、該多成分歯科材料は、少なくともペースト(A)または(B)の中に、ラジカル重合のための少なくとも1種の開始剤(v)を含有する、硬化性多成分歯科材料。
塩基性充填材をペースト(A)の中に含有する、上記項目に記載の歯科材料。
1種以上の酸基を有さないラジカル重合性モノマー(vi)をまたペースト(B)の中に含有する、上記項目のいずれかに記載の歯科材料。
非塩基性充填材(ix)をまたペースト(A)の中に含有する、上記項目のいずれかに記載の歯科材料。
自己硬化性であり、そして開始剤(v)、好ましくは過酸化物、特に好ましくは過酸化ベンゾイルを、ペースト(B)の中に含有し、そして活性化剤(vii)、好ましくは塩基性活性化剤、特に好ましくは芳香族アミンをまた、ペースト(A)の中に含有する、上記項目のいずれかに記載の歯科材料。
二重硬化性であり、そしてまた、少なくとも1種の光開始剤(viii)を、少なくともペースト(A)またはペースト(B)の中に含有する、上記項目のいずれかに記載の歯科材料。
前記非塩基性充填材(iv)、および必要に応じて前記非塩基性充填材(ix)もまた、SiO2、中性金属塩およびこれらの組み合わせから選択される、上記項目のいずれかに記載の歯科材料。
前記非塩基性充填材(iv)および/または(ix)が、石英、発熱性シリカ、沈降シリカ、ゾル−ゲルシリカ、石英ガラス、希土類金属の中性フッ化物、好ましくは三フッ化イッテルビウム、およびこれらの組み合わせから選択される、上記項目のいずれかに記載の歯科材料。
前記少なくとも1種の酸基含有ラジカル重合性モノマー(iii)が、少なくとも1つのエチレン性不飽和基および少なくとも1つの酸基を含み、該エチレン性不飽和基が、アクリロイル基、メタクリロイル基、ビニル基およびこれらの組み合わせから選択され、そして該酸基が、カルボン酸基、スルホン酸基、ホスホン酸基、リン酸基およびこれらの組み合わせから選択される、上記項目のいずれかに記載の歯科材料。
前記少なくとも1種の酸基含有ラジカル重合性モノマー(iii)が、ラジカル重合性のリン酸二水素エステルまたはリン酸水素エステルである、上記項目のいずれかに記載の歯科材料。
アクリロイル基および/またはメタクリロイル基から好ましくは選択される少なくとも2つのエチレン性不飽和基を有する、少なくとも1種の酸基を有さないラジカル重合性モノマー(i)および/または(vi)を含有する、上記項目のいずれかに記載の歯科材料。
上記項目のいずれかに記載の硬化性多成分歯科材料のペースト(A)とペースト(B)とを、好ましくは0.4:0.6〜0.6:0.4の範囲の体積比、特に好ましくは、0.46:0.54〜0.54:0.46の範囲の体積比で混合する工程を包含する、使用の準備ができた歯科材料の調製プロセス。
歯科学において使用するための、上記項目のいずれかに記載の硬化性多成分歯科材料。
歯科修復物を歯のエナメル質および/またはぞうげ質に固定するための、上記項目のいずれかに記載の硬化性多成分歯科材料。
第一のレザバおよび第二のレザバを有する二重注射器であって、該二重注射器は、上記項目のいずれかに記載の硬化性多成分歯科材料を収容することを特徴とし、ペースト(A)が該第一のレザバに収容され、そしてペースト(B)が第二のレザバに収容される、二重注射器。
第一のペーストおよび第二のペーストを含有する硬化性多成分歯科材料であって、この第一のペーストは、(i)1種以上の酸基を有さないラジカル重合性モノマーおよび(ii)塩基性充填材を含有し、そしてこの第二のペーストは、(iii)1種以上の酸基含有ラジカル重合性モノマーおよび(iv)非塩基性充填材を含有する。この多成分歯科材料は、少なくともペースト(A)または(B)の中に、ラジカル重合のための少なくとも1種の開始剤(v)を含有する。
(A)第一のペーストであって、
(i)1種以上の酸基を含まないラジカル重合性モノマーおよび
(ii)充填材
を含有する、第一のペースト、ならびに
(B)第二のペーストであって、
(iii)1種以上の酸基含有ラジカル重合性モノマーおよび
(iv)非塩基性充填材
を含有する、第二のペースト
を含有する硬化性多成分歯科材料であって、この多成分歯科材料は、少なくともペースト(A)または(B)の中に、ラジカル重合のための少なくとも1種の開始剤(v)を含有する、硬化性多成分歯科材料によって達成される。
65重量%〜80重量%、特に好ましくは、70重量%〜80重量%の、塩基性充填材(ii)および塩基性充填材(ii)と非塩基性充填材(ix)との組み合わせから選択される充填材、ならびに
20重量%〜35重量%、特に好ましくは、20重量%〜30重量%の、ペースト(A)について上で定義されたマトリックス混合物を含有し、そして
ペースト(B)が、各場合においてペースト(B)の総重量に対して:
60重量%〜70重量%の非塩基性充填材(iv)、および
30重量%〜40重量%の、ペースト(B)について上で定義されたマトリックス混合物を含有する、
歯科材料に関する。
以下に示される組成を有する実施例1および2のペーストを、以下のように調製した。他に記載されない限り、全ての値は、重量(重量部)による。最初に、マトリックス混合物を、個々のモノマーを一緒に攪拌することにより調製した。開始剤、および適用可能な場合には活性化剤を、このモノマー混合物に溶解した。このマトリックス混合物を攪拌装置に導入し、そして均質なペーストが存在するまで、充填材を攪拌した。ぞうげ質接着を決定するために、調製した実施例1および2のペースト(A)およびペースト(B)を、各々1:1で混合した(これらの2つのペーストの密度はおよそ同じであったので、1:1の体積比は、本明細書では、およそ1:1の重量比に対応する。)。
硬い歯の物質への接着を、いわゆるUltradent法を使用して実施した。この目的で、ウシの歯を、ポリエステル樹脂に包埋した。エナメル質への接着が試験されるのかぞうげ質への接着が試験されるのかに依存して、最も上にあるエナメル質層を水を付けた120グリッドの紙やすりで研磨し、そして水を付けた600グリッドの紙やすりで再度研磨した。ぞうげ質への接着の場合には、120グリッドの紙やすりでの研磨を、ぞうげ質表面が露出するまで行った。接着試験のための試験片を調製する前に、歯の表面を水ですすぎ、そして送風機で軽く乾燥させたが、完全には乾燥させなかった。Tetric EvoCeram(Ivoclar Vivadent AG,Liechtenstein製の光重合性析出材料)を含む、予め重合させたコンポジットの、長さ3mmおよび直径2.3mmのブロックを、歯科用重合ランプ(Bluephase,Ivoclar Vivadent AG,400nm〜500nm)での放射(20秒間)により調製した。次いで、成形した立体を、少量の固定コンポジットと一緒に接着表面にコーティングし、そしてぞうげ質の表面に置いた。コンポジット試験片をねじにより歯の表面に固定し、そして過剰なセメントを除去した。
(ペースト(A))
**)94%の充填材、5%のシランおよび1%の水を混合し、そして未反応シランの反応後にエバポレートした。
78.5%のUDMA
21.0%のジメタクリル酸デカンジオール
0.5%の過酸化ベンゾイル
からなる30%のマトリックス混合物、
50%の発熱性シリカAerosil(登録商標)OX−50(Evonik Degussa;粒子サイズ40nm)、
10%の三フッ化イッテルビウム
からなるコンポジットから、このコンポジットをケーキ(厚さ1cm)に100℃で約2時間重合させ、次いでこのケーキを(粉砕後の平均粒子サイズ5μm)に粉砕することにより調製した。
ペースト(A)
固定コンポジットであるKerr Corporation,USA製のMaxcem EliteTMのぞうげ質接着を、上に記載したように試験した。本願の発明者らが知る限り、Maxcem EliteTMは、以下の組成を有する:
ペースト1
充填剤含有量77%
充填剤の組成:
Claims (15)
- (A)第一のペーストであって、
(i)1種以上の酸基を含まないラジカル重合性モノマーおよび
(ii)充填材
を含有する、第一のペースト、ならびに
(B)第二のペーストであって、
(iii)1種以上の酸基含有ラジカル重合性モノマーおよび
(iv)非塩基性充填材
を含有する、第二のペースト
を含有する硬化性多成分歯科材料であって、該多成分歯科材料は、少なくともペースト(A)または(B)の中に、ラジカル重合のための少なくとも1種の開始剤(v)を含有する、硬化性多成分歯科材料。 - 塩基性充填材をペースト(A)の中に含有する、請求項1に記載の歯科材料。
- 1種以上の酸基を有さないラジカル重合性モノマー(vi)をまたペースト(B)の中に含有する、請求項1または2に記載の歯科材料。
- 非塩基性充填材(ix)をまたペースト(A)の中に含有する、請求項1〜3のいずれか1項に記載の歯科材料。
- 自己硬化性であり、そして開始剤(v)、好ましくは過酸化物、特に好ましくは過酸化ベンゾイルを、ペースト(B)の中に含有し、そして活性化剤(vii)、好ましくは塩基性活性化剤、特に好ましくは芳香族アミンをまた、ペースト(A)の中に含有する、請求項1〜4のいずれか1項に記載の歯科材料。
- 二重硬化性であり、そしてまた、少なくとも1種の光開始剤(viii)を、少なくともペースト(A)またはペースト(B)の中に含有する、請求項5に記載の歯科材料。
- 前記非塩基性充填材(iv)、および必要に応じて前記非塩基性充填材(ix)もまた、SiO2、中性金属塩およびこれらの組み合わせから選択される、請求項1〜6のいずれか1項に記載の歯科材料。
- 前記非塩基性充填材(iv)および/または(ix)が、石英、発熱性シリカ、沈降シリカ、ゾル−ゲルシリカ、石英ガラス、希土類金属の中性フッ化物、好ましくは三フッ化イッテルビウム、およびこれらの組み合わせから選択される、請求項7に記載の歯科材料。
- 前記少なくとも1種の酸基含有ラジカル重合性モノマー(iii)が、少なくとも1つのエチレン性不飽和基および少なくとも1つの酸基を含み、該エチレン性不飽和基が、アクリロイル基、メタクリロイル基、ビニル基およびこれらの組み合わせから選択され、そして該酸基が、カルボン酸基、スルホン酸基、ホスホン酸基、リン酸基およびこれらの組み合わせから選択される、請求項1〜8のいずれか1項に記載の歯科材料。
- 前記少なくとも1種の酸基含有ラジカル重合性モノマー(iii)が、ラジカル重合性のリン酸二水素エステルまたはリン酸水素エステルである、請求項9に記載の歯科材料。
- アクリロイル基および/またはメタクリロイル基から好ましくは選択される少なくとも2つのエチレン性不飽和基を有する、少なくとも1種の酸基を有さないラジカル重合性モノマー(i)および/または(vi)を含有する、請求項1〜10のいずれか1項に記載の歯科材料。
- 請求項1〜11のいずれか1項に記載の硬化性多成分歯科材料のペースト(A)とペースト(B)とを、好ましくは0.4:0.6〜0.6:0.4の範囲の体積比、特に好ましくは、0.46:0.54〜0.54:0.46の範囲の体積比で混合する工程を包含する、使用の準備ができた歯科材料の調製プロセス。
- 歯科学において使用するための、請求項1〜11のいずれか1項に記載の硬化性多成分歯科材料。
- 歯科修復物を歯のエナメル質および/またはぞうげ質に固定するための、請求項1〜11のいずれか1項に記載の硬化性多成分歯科材料。
- 第一のレザバおよび第二のレザバを有する二重注射器であって、該二重注射器は、請求項1〜11のいずれか1項に記載の硬化性多成分歯科材料を収容することを特徴とし、ペースト(A)が該第一のレザバに収容され、そしてペースト(B)が第二のレザバに収容される、二重注射器。