JP2010185088A - エラストマー複合物、エラストマー配合物及びエラストマー複合物の製造方法 - Google Patents
エラストマー複合物、エラストマー配合物及びエラストマー複合物の製造方法 Download PDFInfo
- Publication number
- JP2010185088A JP2010185088A JP2010126642A JP2010126642A JP2010185088A JP 2010185088 A JP2010185088 A JP 2010185088A JP 2010126642 A JP2010126642 A JP 2010126642A JP 2010126642 A JP2010126642 A JP 2010126642A JP 2010185088 A JP2010185088 A JP 2010185088A
- Authority
- JP
- Japan
- Prior art keywords
- elastomer
- composite
- carbon black
- particulate filler
- elastomer composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】エラストマー複合物であって、エラストマーと、該エラストマー中に分散された微粒子状充填剤とを含み、しかも該微粒子状充填剤が、43から45mL/100gのCDBP(ストラクチャー値)及び260から264m2/gのBET(表面積値)を有し、ダイCを用いてのASTM−D624試験方法により測定される場合の少なくとも160N/mmの引裂き強さを達成するために、十分な量の少なくとも1種のカーボンブラックを含み、前記エラストマー複合物は、エラストマーラテックスを含む第1流体の連続流を混合帯域に供給し、そして微粒子状充填剤を含む第2流体の連続流を加圧下で該混合帯域に供給して混合物を形成させ、しかも該混合帯域内の第1流体と第2流体の混合が、該エラストマーラテックスを該微粒子状充填剤で完全に凝固させるのに十分に強力であることを含む方法により形成される、エラストマー複合物。
【選択図】なし
Description
本明細書に開示されたエラストマー複合物を生成させるための好ましい方法及び装置は、共通に譲渡された米国特許の第6,075,084号明細書、第6,048,923号明細書及び第6,040,364号明細書に記載されており、しかしてそれらの各々の全開示は、これにより、あらゆる目的のために参照することによって本明細書に組み込まれる。かかる方法は、本明細書においていくつかの場合連続湿式混合及び凝固と称される。エラストマー複合物を生成させるための好ましい方法は、エラストマーラテックスを含む第1流体の連続流を凝塊反応器の混合帯域(該凝塊反応器は、該混合帯域から排出端まで延在する細長い凝塊帯域を画定する)に供給し、そして微粒子状充填剤を含む第2流体の連続流を加圧下で該凝塊反応器の該混合帯域に供給して該エラストマーラテックスとの混合物を形成させることを含む。この混合物は連続流として凝塊反応器の排出端まで進み、そして微粒子状充填剤はエラストマーラテックスを凝固するのに効果がある。一層特定的には、第2流体は、凝塊反応器の排出端の前にてエラストマーラテックスを微粒子状充填剤で実質的に完全に凝固させるのに十分に強力に、混合帯域内の第1流体と反対方向にて供給される。エラストマー複合物の実質的に連続的な流れが、排出端から排出される。上記に記されたように、これらの方法は、下記においていくつかの場合連続湿式混合及び凝固と称される。
CDBP≦(BET÷2.9)−X (1)
(ここで、Xは0より大きいか又は等しい)を満たす表面積値及びストラクチャー値を有するカーボンブラックを含むエラストマー複合物が提供される。好ましくはXは0であり、そしてXが0である場合、式(1)はまた、本明細書において「CDBP≦(BET÷2.9)」と表され得る。
CDBP≦(BET÷2.9)−X (2)
(ここで、Xは好ましくは約5である)を満たす表面積値及びストラクチャー値を有するカーボンブラックを含むエラストマー複合物が、本明細書に開示される。一層好ましいものは、Xが約10である式(2)を満たす表面積値及びストラクチャー値を有するカーボンブラックである。式(2)を満たすカーボンブラックは、式(1)を満たすカーボンブラックの部分群である、ということが認識される。更なる適当な超高表面積/ローストラクチャーは、本開示の恩恵が与えられると、当業者に明らかであろう。
ASTM−D1415試験方法に従って測定して約65より大きいショアーA硬度、
ASTM−D412試験方法に従って測定して30メガパスカルより大きい引張り強さ、及び
ASTM−D412試験方法に従って測定して少なくとも約600%の破断点伸び
を達成するために、エラストマー中の選択された濃度にて有効な又は十分な少なくとも1種のカーボンブラックを含む。
次の例の各々について、フィールドラテックスからの天然ゴム、Cabot Corporationから入手できるBP1100カーボンブラック、及び芳香族油を含むエラストマー複合物を製造した。該天然ゴムフィールドラテックスの性質は、下記の表1に与えられている。
実施例1〜3のエラストマー複合物を製造するために、米国特許第6,048,923号明細書に記載された手順と同様である次の手順を用いた。
カーボンブラックの袋を乾式粉砕し、そして引き続いて掻き混ぜ機を備えたカーボンブラックスラリータンク中で水と混合して16.8wt%カーボンブラックスラリーを形成させた。次いで、この粗製スラリーを、該スラリーが約780kg/hrの流量にて混合帯域中に噴流として導入されるように、約3000psigの操作圧にてホモジナイザーに供給して、微粉砕カーボンブラックスラリーを生成させた。
最初にタンクに装填されたラテックスを、凝塊反応器の混合帯域にポンプ輸送した。所望の最終カーボンブラック充填レベルを得るために、ラテックス流量を調節した。430から600kg/hrの間のラテックス流量が、80と95phrの間のカーボンブラック充填レベルをもたらした(より高いラテックス流量がより低いカーボンブラック充填レベルをもたらす)。酸化防止剤及び油は、ラテックス中に添加しなかった。
カーボンブラックスラリーとラテックスを、該ラテックスを該カーボンブラックスラリー中に連行させることにより混合した。連行中に、カーボンブラックはラテックス中に親密に混入され、そしてこの混合物は凝固した。軟らかくて湿ったスポンジ状の「蠕虫」形態の凝塊が、凝塊反応器から出た。
凝塊反応器から排出された湿潤団粒を、脱水押出機(The French Oil Machinery Company,7インチ直径)でもって、10〜25%の湿分に脱水した。該押出機において、該湿潤団粒は圧縮され、そして水が該団粒から絞り出されそして該押出機のスロットバレルに通された。
脱水された団粒を連続式混合機中に落下させ、しかしてそこで該団粒を素練りし、そして油及び酸化防止剤と混合した。生成物出口温度は160℃未満であり、そして湿分含有率は約2%であった。
以下に、本願発明に関連する発明の実施形態について列挙する。
実施形態1
エラストマー複合物であって、エラストマーと、該エラストマー中に分散された微粒子状充填剤とを含み、しかも該微粒子状充填剤が、式CDBP≦(BET÷2.9)を満たすストラクチャー値及び表面積値を有する少なくとも1種のカーボンブラックを含むエラストマー複合物。
実施形態2
少なくとも60phrの微粒子状充填剤を含む、実施形態1に記載のエラストマー複合物。
実施形態3
少なくとも60phrの、式CDBP≦(BET÷2.9)を満たすカーボンブラックを含む、実施形態1に記載のエラストマー複合物。
実施形態4
微粒子状充填剤が、式CDBP≦(BET÷2.9)を満たさないストラクチャー値及び表面積値を有する少なくとも1種の追加の充填剤物質を更に含む、実施形態1に記載のエラストマー複合物。
実施形態5
エラストマーが、天然ゴム、ブタジエン、スチレン、イソプレン、イソブチレン、2,3−ジアルキル−1,3−ブタジエン(ここで、アルキル基はC1からC3のアルキルである)、アクリロニトリル、エチレン又はプロピレンのホモポリマー、コポリマー又はターポリマーから選択される、実施形態1に記載のエラストマー複合物。
実施形態6
エラストマーが、天然ゴムを含む、実施形態1に記載のエラストマー複合物。
実施形態7
オゾン亀裂防止剤、酸化防止剤、可塑剤、加工助剤、樹脂、難燃剤、エキステンダー油、滑剤及びそれらの組合わせから選択された少なくとも1種の添加剤を更に含む、実施形態1に記載のエラストマー複合物。
実施形態8
エラストマー複合物が、ダイCを用いてのASTM−D624試験方法により測定される場合の少なくとも約160N/mmの引裂き強さを有する、実施形態1に記載のエラストマー複合物。
実施形態9
エラストマー複合物であって、汎用ゴムと、該汎用ゴム中に分散された微粒子状充填剤とを含み、しかも該微粒子状充填剤が、ダイCを用いてのASTM−D624試験方法により測定される場合の少なくとも約160N/mmの引裂き強さを達成するために、該汎用ゴム中の有効な少なくとも1種のカーボンブラックの量を含むエラストマー複合物。
実施形態10
エラストマー複合物であって、エラストマーと、該エラストマー中に分散された微粒子状充填剤とを含み、しかも該エラストマー複合物が
ASTM−D1415試験方法に従って測定して約65より大きいショアーA硬度、
ASTM−D412試験方法に従って測定して30メガパスカルより大きい引張り強さ、及び
ASTM−D412試験方法に従って測定して少なくとも約600%の破断点伸び
を有し、該微粒子状充填剤は、式CDBP≦(BET÷2.9)を満たすストラクチャー値及び表面積値を有するカーボンブラックを含むエラストマー複合物。
実施形態11
ASTM D−624試験方法により測定される場合の少なくとも160N/mmの引裂き強さを有する、実施形態10に記載のエラストマー複合物。
実施形態12
エラストマー複合物であって、汎用ゴムと、該汎用ゴム中に分散された微粒子状充填剤とを含み、しかも該微粒子状充填剤が、
ASTM−D1415試験方法に従って測定して約65より大きいショアーA硬度、
ASTM−D412試験方法に従って測定して30メガパスカルより大きい引張り強さ、及び
ASTM−D412試験方法に従って測定して少なくとも約600%の破断点伸び
を達成するために、該汎用ゴム中の有効な少なくとも1種のカーボンブラックの量を含むエラストマー複合物。
実施形態13
カーボンブラックが、式CDBP≦(BET÷2.9)を満たすストラクチャー値及び表面積値を有する、実施形態12に記載のエラストマー複合物。
実施形態14
エラストマーが、ダイCを用いてのASTM−D624試験方法により測定される場合の少なくとも約160N/mmの引裂き強さを有する、実施形態12に記載のエラストマー複合物。
実施形態15
微粒子状充填剤が、式CDBP≦(BET÷2.9)−X(ここで、Xは約5である)を満たすストラクチャー値及び表面積値を有する少なくとも1種のカーボンブラックを含む、実施形態1に記載のエラストマー複合物。
実施形態16
微粒子状充填剤が、式CDBP≦(BET÷2.9)−X(ここで、Xは約10である)を満たすストラクチャー値及び表面積値を有する少なくとも1種のカーボンブラックを含む、実施形態1に記載のエラストマー複合物。
実施形態17
エラストマー配合物であって、少なくとも1種のエラストマー物質と配合されたエラストマー複合物を含み、しかも該エラストマー複合物が、第1エラストマーと、第1エラストマー中に分散された微粒子状充填剤とを含み、該微粒子状充填剤は、式CDBP≦(BET÷2.9)−Xを満たすストラクチャー値及び表面積値を有する少なくとも1種のカーボンブラックを含むエラストマー配合物。
実施形態18
エラストマー物質が、第1エラストマーとは異なるエラストマーを含む、実施形態17に記載のエラストマー配合物。
実施形態19
配合する前のエラストマー複合物が、ダイCを用いてのASTM−D624試験方法により測定される場合の少なくとも約160N/mmの引裂き強さを有する、実施形態17に記載のエラストマー配合物。
実施形態20
配合する前のエラストマー複合物が、
ASTM−D1415試験方法に従って測定して約65より大きいショアーA硬度、
ASTM−D412試験方法に従って測定して30メガパスカルより大きい引張り強さ、及び
ASTM−D412試験方法に従って測定して少なくとも約600%の破断点伸び
を有する、実施形態17に記載のエラストマー配合物。
実施形態21
エラストマーと、該エラストマー中に分散された微粒子状充填剤とを含むエラストマー複合物を製造する方法であって、
エラストマーラテックスを含む第1流体の連続流を混合帯域に供給し、そして
微粒子状充填剤を含む第2流体の連続流を加圧下で該混合帯域に供給して混合物を形成させ、しかも該混合帯域内の第1流体と第2流体の混合が、該エラストマーラテックスを該微粒子状充填剤で実質的に完全に凝固させるのに十分に強力である
ことを含み、しかも該微粒子状充填剤が、式CDBP≦(BET÷2.9)−Xを満たすストラクチャー値及び表面積値を有する少なくとも1種のカーボンブラックを含む方法。
実施形態22
エラストマー複合物が、ダイCを用いてのASTM−D624試験方法により測定される場合の少なくとも160N/mmの引裂き強さを有する、実施形態21に記載の方法。
実施形態23
エラストマー複合物をエラストマー物質と配合してエラストマー配合物を形成させることを更に含む、実施形態21に記載の方法。
実施形態24
エラストマー複合物をエラストマー物質と配合することが、該エラストマー複合物を該エラストマー物質と乾式混合することを含む、実施形態23に記載の方法。
実施形態25
エラストマー物質が、追加の充填剤を含む、実施形態23に記載の方法。
実施形態26
エラストマー複合物を追加の充填剤と配合することを更に含む、実施形態21に記載の方法。
実施形態27
エラストマー複合物が、ダイCを用いてのASTM−D624試験方法により測定される場合の少なくとも160N/mmの引裂き強さを有する、実施形態21に記載の方法。
実施形態28
エラストマー複合物が、
ASTM D1415試験方法により測定される場合の少なくとも65のショアーA硬度、
ASTM D412試験方法により測定される場合の少なくとも30メガパスカルの引張り強さ、及び
ASTM D412試験方法により測定される場合の少なくとも600%の伸び
を有する、実施形態21に記載の方法。
実施形態29
微粒子状充填剤が、約43から45mL/100gのCDBP値及び約260から264m2/gのBET値を有する少なくとも1種のカーボンブラックを含む、実施形態1に記載のエラストマー複合物。
実施形態30
少なくとも1種のカーボンブラックが、エラストマー複合物中のエラストマーの重量を基準として約50から110phrの充填レベルにて存在する、実施形態29に記載のエラストマー複合物。
Claims (13)
- エラストマー複合物であって、エラストマーと、該エラストマー中に分散された微粒子状充填剤とを含み、しかも該微粒子状充填剤が、43から45mL/100gのCDBP(ストラクチャー値)及び260から264m2/gのBET(表面積値)を有する少なくとも1種のカーボンブラックを含み、そのエラストマー複合物が、ダイCを用いてのASTM−D624試験方法により測定される場合の少なくとも160N/mmの引裂き強さを達成するために、十分な量の少なくとも1種のカーボンブラックを含み、前記エラストマー複合物は、エラストマーラテックスを含む第1流体の連続流を混合帯域に供給し、そして微粒子状充填剤を含む第2流体の連続流を加圧下で該混合帯域に供給して混合物を形成させ、しかも該混合帯域内の第1流体と第2流体の混合が、該エラストマーラテックスを該微粒子状充填剤で完全に凝固させるのに十分に強力であることを含む方法により形成される、エラストマー複合物。
- 少なくとも60phrの、微粒子状充填剤を含む、請求項1に記載のエラストマー複合物。
- 微粒子状充填剤が、式CDBP≦(BET÷2.9)−X(ここで、Xは5である)を満たさないストラクチャー値及び表面積値を有する少なくとも1種の追加の充填剤物質を更に含む、請求項1に記載のエラストマー複合物。
- エラストマーが、天然ゴム、又は、ブタジエン、スチレン、イソプレン、イソブチレン、2,3−ジアルキル−1,3−ブタジエン(ここで、アルキル基はC1からC3のアルキルである)、アクリロニトリル、エチレン又はプロピレンのホモポリマー、コポリマー又はターポリマーから選択される、請求項1に記載のエラストマー複合物。
- オゾン亀裂防止剤、酸化防止剤、可塑剤、加工助剤、樹脂、難燃剤、エキステンダー油、滑剤及びそれらの組合わせから選択された少なくとも1種の添加剤を更に含む、請求項1に記載のエラストマー複合物。
- 少なくとも1種のカーボンブラックが、エラストマー複合物中のエラストマーの重量を基準として50から110phrの充填レベルにて存在する、請求項1に記載のエラストマー複合物。
- エラストマー配合物であって、少なくとも1種のエラストマー物質と配合されたエラストマー複合物を含み、しかも該エラストマー複合物が、第1エラストマーと、第1エラストマー中に分散された微粒子状充填剤とを含み、該微粒子状充填剤は、43から45mL/100gのCDBP(ストラクチャー値)及び260から264m2/gのBET(表面積値)を有する少なくとも1種のカーボンブラックを含み、その第1エラストマー複合物が、ダイCを用いてのASTM−D624試験方法により測定される場合の少なくとも160N/mmの引裂き強さを達成するために、十分な量の少なくとも1種のカーボンブラックを含む、エラストマー配合物。
- エラストマー物質が、第1エラストマーとは異なるエラストマーを含む、請求項7に記載のエラストマー配合物。
- エラストマーと、該エラストマー中に分散された微粒子状充填剤とを含むエラストマー複合物を製造する方法であって、エラストマーラテックスを含む第1流体の連続流を混合帯域に供給し、そして微粒子状充填剤を含む第2流体の連続流を加圧下で該混合帯域に供給して混合物を形成させ、しかも該混合帯域内の第1流体と第2流体の混合が、該エラストマーラテックスを該微粒子状充填剤で実質的に完全に凝固させるのに十分に強力であることを含み、しかも該微粒子状充填剤が、43から45mL/100gのCDBP(ストラクチャー値)及び260から264m2/gのBET(表面積値)を有する少なくとも1種のカーボンブラックを含む方法。
- エラストマー複合物をエラストマー物質と配合してエラストマー配合物を形成させることを更に含む、請求項9に記載の方法。
- エラストマー複合物をエラストマー物質と配合することが、該エラストマー複合物を該エラストマー物質と乾式混合することを含む、請求項10に記載の方法。
- エラストマー物質が、追加の充填剤を含む、請求項9に記載の方法。
- エラストマー複合物を追加の充填剤と配合することを更に含む、請求項9に記載の方法。