JP2010031356A - 高亜鉛含有鉄鉱石を用いた還元鉄製造方法 - Google Patents
高亜鉛含有鉄鉱石を用いた還元鉄製造方法 Download PDFInfo
- Publication number
- JP2010031356A JP2010031356A JP2009106320A JP2009106320A JP2010031356A JP 2010031356 A JP2010031356 A JP 2010031356A JP 2009106320 A JP2009106320 A JP 2009106320A JP 2009106320 A JP2009106320 A JP 2009106320A JP 2010031356 A JP2010031356 A JP 2010031356A
- Authority
- JP
- Japan
- Prior art keywords
- zinc
- iron ore
- iron
- dust
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】亜鉛を0.01mass%以上、鉄を50mass%以上含有する高亜鉛含有鉄鉱石を含有する鉄鉱石と、炭素系固体還元材とを混合した混合原料4を移動型炉床3上に積載し、炉床3上部から熱供給して混合原料4を還元し、混合原料4を溶融しないかまたは一部のみ溶融させて、還元鉄を得ることを特徴とする高亜鉛含有鉄鉱石を用いた還元鉄製造方法を用いる。高亜鉛含有鉄鉱石の配合量が鉄鉱石の10mass%以上であること、混合原料4を塊成化して、炉床3上に積載すること、炉床3上に炭材を積載した上に、混合原料4を積層すること、混合原料4を1250℃以上で加熱することが好ましい。
【選択図】図1
Description
(1)、亜鉛を0.01mass%以上、鉄を50mass%以上含有する高亜鉛含有鉄鉱石を含有する鉄鉱石と、炭素系固体還元材とを混合した混合原料を移動型炉床上に積載し、該炉床上部から熱供給して前記混合原料を還元し、前記混合原料を溶融しないかまたは一部のみ溶融させて、還元鉄を得ることを特徴とする高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
(2)、高亜鉛含有鉄鉱石の配合量が鉄鉱石の10mass%以上であることを特徴とする(1)に記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
(3)、混合原料を塊成化して、炉床上に積載することを特徴とする(1)または(2)に記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
(4)、炉床上に炭材を積載した上に、混合原料を積層することを特徴とする(1)ないし(3)のいずれかに記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
(5)、混合原料を1250℃以上で加熱することを特徴とする(1)ないし(4)のいずれかに記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
(6)、(1)ないし(5)のいずれかに記載の還元鉄製造方法において移動型炉床炉で発生したダストの少なくとも一部を回収し、該ダストを前記移動型炉床上に積載し、該炉床上部から熱供給して、前記移動型炉床炉で発生するダストから粗酸化亜鉛を得ることを特徴とする高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
(7)、混合原料中の鉄鉱石の平均亜鉛濃度が0.005mass%以上であることを特徴とする(6)に記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
(8)、(1)ないし(5)のいずれかに記載の還元鉄製造方法において、高亜鉛含有鉄鉱石を含有する鉄鉱石と、亜鉛含有ダストと、炭素系固体還元材と、造滓材とを混合した混合原料を移動型炉床上に積載し、該炉床上部から熱供給して、前記移動型炉床炉で発生するダストから粗酸化亜鉛を得ることを特徴とする高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
(9)、混合原料中の平均亜鉛濃度が0.45mass%以上であることを特徴とする(8)に記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
2 炉体
2a 予熱帯
2b 還元帯
2d 冷却帯
3 回転炉床
4 混合原料
5 バーナー
6 装入装置
7 排出装置
8 冷却装置
11 鉱石ホッパー
12 石炭ホッパー
14 混合機
15 回転炉床炉
16 還元鉄排出口
17 排ガスダクト用バグフィルター
18 粉体搬送用ローリー
19 吸引ファン
20 煙突
21 回収ダスト搬送コンベアー
21a 第1回収ダスト搬送コンベアー
21b 第2回収ダスト搬送コンベアー
22 第1回収ダスト貯蔵ホッパー
23 ダストヤード
Claims (9)
- 亜鉛を0.01mass%以上、鉄を50mass%以上含有する高亜鉛含有鉄鉱石を含有する鉄鉱石と、炭素系固体還元材とを混合した混合原料を移動型炉床上に積載し、該炉床上部から熱供給して前記混合原料を還元し、前記混合原料を溶融しないかまたは一部のみ溶融させて、還元鉄を得ることを特徴とする高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
- 高亜鉛含有鉄鉱石の配合量が鉄鉱石の10mass%以上であることを特徴とする請求項1に記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
- 混合原料を塊成化して、炉床上に積載することを特徴とする請求項1または請求項2に記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
- 炉床上に炭材を積載した上に、混合原料を積層することを特徴とする請求項1ないし請求項3のいずれかに記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
- 混合原料を1250℃以上で加熱することを特徴とする請求項1ないし請求項4のいずれかに記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
- 請求項1ないし請求項5のいずれかに記載の還元鉄製造方法において移動型炉床炉で発生したダストの少なくとも一部を回収し、該ダストを前記移動型炉床上に積載し、該炉床上部から熱供給して、前記移動型炉床炉で発生するダストから粗酸化亜鉛を得ることを特徴とする高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
- 混合原料中の鉄鉱石の平均亜鉛濃度が0.005mass%以上であることを特徴とする請求項6に記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
- 請求項1ないし請求項5のいずれかに記載の還元鉄製造方法において、高亜鉛含有鉄鉱石を含有する鉄鉱石と、亜鉛含有ダストと、炭素系固体還元材と、造滓材とを混合した混合原料を移動型炉床上に積載し、該炉床上部から熱供給して、前記移動型炉床炉で発生するダストから粗酸化亜鉛を得ることを特徴とする高亜鉛含有鉄鉱石を用いた還元鉄製造方法。
- 混合原料中の平均亜鉛濃度が0.45mass%以上であることを特徴とする請求項8に記載の高亜鉛含有鉄鉱石を用いた還元鉄製造方法。