JP2009263629A - グラフトポリエーテルポリオール、その製造方法、ポリウレタン樹脂組成物およびポリウレタン樹脂硬化物 - Google Patents
グラフトポリエーテルポリオール、その製造方法、ポリウレタン樹脂組成物およびポリウレタン樹脂硬化物 Download PDFInfo
- Publication number
- JP2009263629A JP2009263629A JP2009053854A JP2009053854A JP2009263629A JP 2009263629 A JP2009263629 A JP 2009263629A JP 2009053854 A JP2009053854 A JP 2009053854A JP 2009053854 A JP2009053854 A JP 2009053854A JP 2009263629 A JP2009263629 A JP 2009263629A
- Authority
- JP
- Japan
- Prior art keywords
- polyether polyol
- molecular weight
- mol
- graft
- meth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ポリエーテルポリオールに、ポリエーテルポリオールの水酸基1モルに対して0.1モル未満のラジカル反応開始剤の存在下で、(メタ)アクリル酸エステルをグラフト反応させることにより、グラフトポリエーテルポリオールを製造する。このグラフトポリエーテルポリオールと、ポリイソシアネートとを含むポリウレタン樹脂組成物を、反応させて硬化させることにより得られるポリウレタン樹脂硬化物は、柔軟性、耐熱性、耐候性および機械強度に優れる。
【選択図】図1
Description
ポリウレタン樹脂硬化物の成形品には、その目的および用途に応じて、柔軟性、耐熱性、耐候性および機械強度が必要とされる場合がある。
かかる柔軟性、耐熱性、耐候性および機械強度を確保すべく、例えば、ポリオキシプロピレントリオールに、ポリオキシプロピレントリオールの水酸基1モルに対して0.33モルの1,1−ビス(t−ブチルパーオキシ)シクロヘキサンの存在下で、メタクリル酸n−ブチルおよびメタクリル酸−2−エチルヘキシルを反応させてメタクリレートグラフトポリエーテルポリオールを得ることが提案されている(例えば、特許文献1参照。)。
また、ポリオキシプロピレンジオールに、ポリオキシプロピレンジオールの水酸基1モルに対して0.25モルのジ−tert−ブチルパーオキサイドの存在下で、メタクリル酸メチルを反応させてメタクリレートグラフトポリエーテルポリオールを得ることが提案されている(例えば、特許文献2参照。)。
本発明の目的は、柔軟性、耐熱性、耐候性および機械強度に優れるポリウレタン樹脂硬化物を得るための、ポリウレタン樹脂組成物の原料として好適なグラフトポリエーテルポリオールおよびその製造方法を提供することにある。
また、本発明のグラフトポリエーテルポリオールでは、示差屈折率検出器および紫外線検出器を装備したゲルパーミエーションクロマトグラフにより測定され、高分子量側ピークと低分子量側ピークとを有するクロマトグラムから、下記式(1)により求められる値が、0.5以下であることが好適である。
HUV:波長254nmにおいて、紫外線検出器により検出された高分子量側ピークのピーク面積
LUV:波長254nmにおいて、紫外線検出器により検出された低分子量側ピークのピーク面積
HRI:示差屈折率検出器により検出された高分子量側ピークのピーク面積
LRI:示差屈折率検出器により検出された低分子量側ピークのピーク面積
また、本発明のグラフトポリエーテルポリオールでは、前記ポリエーテルポリオールの水酸基価が、110mgKOH/g以下であることが好適である。
また、本発明のポリウレタン樹脂硬化物は、上記したポリウレタン樹脂組成物を硬化させることにより得られることを特徴としている。
また、本発明のグラフトポリエーテルポリオールの製造方法は、ポリエーテルポリオールに、前記ポリエーテルポリオールの水酸基1モルに対して0.1モル未満のラジカル反応開始剤の存在下で、(メタ)アクリル酸エステルをグラフト反応させることを特徴としている。
本発明において、ポリエーテルポリオールは、例えば、2〜8個の活性水素基(水酸基および/またはアミノ基)を有する低分子量ポリオールおよび/または低分子量ポリアミンを開始剤として、これにアルキレンオキサイドを開環付加重合させることにより得ることができる。
なお、開始剤には、1個の活性水素基(水酸基および/またはアミノ基)を有する低分子量モノオールおよび/または低分子量モノアミンを含有させてもよい。低分子量モノオールとしては、例えば、メタノール、エタノール、n−プロパノール、イソプロパノール、n−ブタノール、フェノール、クレゾールなどが挙げられる。低分子量モノアミンとしては、例えば、ブチルアミン、ヘキシルアミン、アニリン、ベンジルアミン、トルイジンなどが挙げられる。
ポリエーテルポリオールは、上記した開始剤に、重合触媒の存在下で、アルキレンオキサイドを重合(アルキレンオキサイドとして、エチレンオキサイドおよびプロピレンオキサイドが併用される場合には、ブロック共重合および/またはランダム共重合)させることにより得られる。また、重合触媒としては、例えば、水酸化カリウム、水酸化ナトリウム、水酸化セシウムなどのアルカリ金属触媒、例えば、亜鉛とコバルトとのシアノ錯体などの複合金属触媒、例えば、窒素−リン二重結合を有するホスファゼンやホスファゼニウムなどのホスファゼニウム触媒(例えば、国際公開2007/026798号に記載されるホスファゼニウム触媒)などが挙げられる。
ポリエーテルポリオールの水酸基価は、例えば、3〜600mgKOH/g、好ましくは、5〜300mgKOH/g、さらに好ましくは、5〜200mgKOH/g、とりわけ好ましくは、5〜110mgKOH/g(あるいは110mgKOH/g以下)である。ポリエーテルポリオールの水酸基価が上記範囲外にあると、得られるグラフトポリエーテルポリオールの粘度が著しく高くなり加工性が低下したり、得られるグラフトポリエーテルポリオールとポリイソシアネートとの反応により得られるポリウレタン樹脂硬化物が十分な柔軟性、耐熱性、耐候性および機械強度を発現できない場合がある。なお、ポリエーテルポリオールの水酸基価は、例えば、JIS K1557−1(2007年版)のアセチル化法やフタル化法に準拠して求めることができる。
パーオキサイド化合物としては、例えば、無機パーオキサイド化合物、有機パーオキサイド化合物が挙げられ、好ましくは、有機パーオキサイド化合物が挙げられ、具体的には、アルキルパーオキサイド化合物が挙げられる。
これらラジカル反応開始剤は、単独使用または2種以上併用することができる。
本発明において、(メタ)アクリル酸エステルは、アクリル酸エステルおよび/またはメタクリル酸エステルであって、例えば、下記一般式(1)で示される(メタ)アクリル酸エステルや、下記一般式(2)で示される水酸基含有(メタ)アクリル酸エステルなどが挙げられる。
一般式(1)において、R2で示される炭化水素基または置換炭化水素基としては、例えば、アルキル基または置換アルキル基が挙げられ、これらの炭素数は、例えば、1〜22、好ましくは、2〜20である。アルキル基または置換アルキル基の炭素数が2未満である場合には、得られるグラフトポリエーテルポリオールの粘度が著しく高くなり加工性が低下する場合がある。
具体的には、アラルキル基としては、例えば、ベンジル、1−または2−フェニルエチル、1−、2−または3−フェニルプロピル、ジフェニルメチル、o、mまたはp−メチルベンジル、o、mまたはp−エチルベンジル、o、mまたはp−イソプロピルベンジル、o、mまたはp−tert−ブチルベンジル、2,3,4−、3,4,5−または2,4,6−トリメチルベンジルなどが挙げられる。好ましくは、ベンジルが挙げられる。
一般式(2)において、R4で示されるアルキレン基の炭素数は、例えば、1〜22、好ましくは、2〜20である。
アルキレン基としては、例えば、メチレン、エチレン、n−プロピレン、イソプロピレン、n−ブチレン、イソブチレン、n−ペンチレン、n−ヘキシレン、n−へプチレン、n−オクチレン、2−エチルへキシレン、n−ノニレン、n−デシレン、n−ウンデシレン、n−ドデシレン、n−トリデシレン、n−テトラデシレン、n−ペンタデシレン、n−ヘキサデシレン、n−ヘプタデシレン、n−オクタデシレン、n−ノナデシレン、n−イコシレン、n−ヘンイコシレン、n−ドコシレンなどが挙げられる。好ましくは、エチレン、2−エチルへキシレンが挙げられる。
これら(メタ)アクリル酸エステルのうち、好ましくは、上記一般式(1)で示される(メタ)アクリル酸エステルが挙げられ、さらに好ましくは、上記一般式(1)で示され、R2における炭素数が2以上のアルキル基である、(メタ)アクリル酸アルキルエステルが挙げられる。
モノマー溶液は、必要により、溶媒(モノマー溶液調製用溶媒)により、これらラジカル反応開始剤および(メタ)アクリル酸エステルを溶解させた溶液として調製することもできる。
グラフト反応において、ポリエーテルポリオール、ラジカル反応開始剤および(メタ)アクリル酸エステルの配合方法としては、例えば、ポリエーテルポリオールに対してモノマー溶液を一括して仕込む一括仕込み法、例えば、ポリエーテルポリオールに対してモノマー溶液を分割して仕込む分割仕込み法、例えば、ポリエーテルポリオールに対してモノマー溶液を滴下する滴下法などが挙げられる。
上記した反応におけるラジカル反応開始剤(純度100%)の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して、0.1モル未満、好ましくは、0.05モル未満、さらに好ましくは、0.025未満、通常、0.0005モル以上である。つまり、ラジカル反応開始剤の配合割合は、ラジカル反応開始剤の分子量およびポリエーテルポリオールの数平均分子量にもよるが、ポリエーテルポリオール100重量部に対して、例えば2.1重量部未満、好ましくは、1.05重量部未満、さらに好ましくは、0.525重量部未満、通常、0.01重量部以上である。
(メタ)アクリル酸エステルのポリエーテルポリオールに対する配合割合が上記した範囲未満であると、グラフトするポリ(メタ)アクリル酸エステルの側鎖の長さが、ポリエーテルポリオールに対して過度に短くなり、ポリウレタン樹脂硬化物の柔軟性、耐熱性、耐候性および機械物性が低下する場合がある。また、(メタ)アクリル酸エステルのポリエーテルポリオールに対する配合割合が上記した範囲を超えると、ポリ(メタ)アクリル酸エステルの側鎖の長さが、ポリエーテルポリオールに対して過度に長くなり、得られたグラフトポリエーテルポリオールは高粘度で加工性が低下する場合がある。
反応条件などは、適宜選択されるが、例えば、滴下法が用いられる場合には、例えば、常圧下において、滴下時間が、例えば、5〜600分、好ましくは、60〜450分、さらに好ましくは、120〜300分である。また、反応温度は、例えば、90〜200℃、好ましくは、100〜180℃、さらに好ましくは、110〜160℃であり、反応時間は、例えば、5〜600分、好ましくは、60〜450分、さらに好ましくは、120〜300分である。
これにより、本発明のグラフトポリエーテルポリオールを得ることができる。
このようにして得られる本発明のグラフトポリエーテルポリオールは、水酸基価が、例えば、1〜600mgKOH/g、好ましくは、2〜300mgKOH/g、さらに好ましくは、2〜200mgKOH/g、とりわけ好ましくは、2〜110mgKOH/gである。水酸基価が上記範囲外であるとグラフトポリエーテルポリオールの粘度が著しく高くなり加工性が低下したり、グラフトポリエーテルポリオールとポリイソシアネートとの反応により得られるポリウレタン樹脂硬化物が十分な柔軟性、耐熱性、耐候性および機械強度を発現できない場合がある。なお、水酸基価は、上記と同様の方法により求められる。
そして、グラフトポリエーテルポリオールを、示差屈折率検出器および紫外線検出器を装備したゲルパーミエーションクロマトグラフにより測定すると、そのクロマトグラムには、通常、グラフトされたポリエーテルポリオールに起因する高分子量側ピークと、グラフトされていないポリエーテルポリオールに起因する低分子量側ピークとが現れる。そして、本発明のポリエーテルポリオールは、そのクロマトグラムから、下記式(3)により求められる値が、好ましくは、0.5以下、さらに好ましくは、0.4以下、通常、0.01以上である。
HUV:波長254nmにおいて、紫外線検出器により検出された高分子量側ピークのピーク面積
LUV:波長254nmにおいて、紫外線検出器により検出された低分子量側ピークのピーク面積
HRI:示差屈折率検出器により検出された高分子量側ピークのピーク面積
LRI:示差屈折率検出器により検出された低分子量側ピークのピーク面積
上記値を求めるには、より具体的には、まず、ポリエーテルポリオールの末端水酸基に、紫外線吸収を有する標識化合物を反応させる。これにより、ポリエーテルポリオールを、波長254nmの紫外線検出器により検出できるように、標識化することができる。標識化合物としては、例えば、p−トルエンスルホニルイソシアネート、フェニルイソシアネート、無水安息香酸などが挙げられる。
そうすると、波長254nmにおいて、紫外線検出器により検出されたクロマトグラムには、高分子量側ピークと、低分子量側ピークとが現れる。紫外線検出器により検出されたクロマトグラムのピーク強度は、標識化合物の数(モル数)に比例する。つまり、高分子量側ピーク面積HUVは、グラフトされたポリエーテルポリオールのモル数に起因するピーク面積であり、低分子量側ピーク面積LUVは、グラフトされていないポリエーテルポリオールのモル数に起因するピーク面積である。
一方、示差屈折率検出器により検出されたクロマトグラムにも、高分子量側ピークと、低分子量側ピークとが現れる。示差屈折率検出器により検出されるピーク強度は、溶出するグラフトポリエーテルポリオールの重量濃度に比例する。
そのため、上記式(3)で示される(HRI/LRI)は、低分子量側ピーク面積LRIを基準とした場合における、高分子側ピーク面積HRIの比率、つまり、グラフトポリエーテルポリオールにおいて、グラフトされていないポリエーテルポリオールに対する、グラフトされているポリエーテルポリオールの重量比率を示す。
R=1−{(HUV/LUV)/(HRI/LRI)} ・・・(4)
よって、上記式(4)により求められるR値を、図1に示す、予め作成した校正曲線に当てはめることにより、ポリエーテルポリオールの主鎖にグラフトしているポリ(メタ)アクリル酸エステルの側鎖の割合、つまり、平均枝分子量を求めることができる。
A:(メタ)アクリル酸エステルのモル数(モル)
B:ラジカル反応開始剤のラジカルのモル数(モル)
MWA:(メタ)アクリル酸エステルの分子量(g/モル)
そして、標品を、上記と同様のゲルパーミエーションクロマトグラフにより測定することにより、上記式(4)で示されるR値を求める。その後、設計枝分子量の逆数および上記式(4)で示されるR値を、図1に示すように、座標上にプロットすることにより、校正曲線を作成することができる。なお、校正曲線は、図1に示すように、設計枝分子量の逆数とR値とが、強い相関性を有している。
次に、本発明のグラフトポリエーテルポリオールを含む、本発明のポリウレタン樹脂組成物について説明する。
本発明のポリウレタン樹脂組成物は、上記したグラフトポリエーテルポリオールと、ポリイソシアネートとを含んでいる。
脂肪族ポリイソシアネートとしては、例えば、ヘキサメチレンジイソシアネート(HDI)、トリメチレンジイソシアネート、テトラメチレンジイソシアネート、ペンタメチレンジイソシアネート、1,2−プロピレンジイソシアネート、1,2−、2,3−または1,3−ブチレンジイソシアネート、2,4,4−または2,2,4−トリメチルヘキサメチレンジイソシアネート、2,6−ジイソシアナトメチルカプロエートなどが挙げられる。
芳香族ポリイソシアネートとしては、例えば、4,4′−、2,4′−または2,2′−ジフェニルメタンジイソシアネートまたはその混合物(MDI)、2,4−または2,6−トリレンジイソシアネートまたはその混合物(TDI)、3,3′−ジメトキシビフェニル−4,4′−ジイソシアネート、1,5−ナフタレンジイソシアネート(NDI)、m−またはp−フェニレンジイソシアネートまたはその混合物、4,4′−ジフェニルジイソシアネート、4,4′−ジフェニルエーテルジイソシアネートなどが挙げられる。
また、本発明のポリウレタン樹脂組成物には、必要により、鎖伸長剤を含ませることができる。
また、鎖伸長剤としては、例えば、水酸基含有ポリアミンなども挙げられる。水酸基含有ポリアミンとしては、例えば、アルカノールアミンが挙げられ、例えば、モノエタノールアミン、ジエタノールアミン、2−アミノメチルプロパノールなどが挙げられる。
ポリウレタン樹脂硬化物は、上記の各成分(すなわち、グラフトポリエーテルポリオール、ポリイソシアネートおよび必要により鎖伸長剤)を、例えば、ワンショット法やプレポリマー法などの合成方法により、製造する。
また、攪拌混合時には、必要により、触媒や、溶媒(ポリウレタン調製用溶媒)を適宜の割合で添加することができる。
溶媒(ポリウレタン調製用溶媒)としては、上記した炭化水素溶媒の他に、例えば、アセトン、メチルエチルケトン(MEK)、メチルイソブチルケトン、シクロヘキサノンなどのケトン、例えば、酢酸メチル、酢酸エチル、酢酸ブチル、酢酸イソブチルなどのアルキルエステル、例えば、エチレングリコールエチルエーテルアセテート、プロピレングリコールメチルエーテルアセテート、3−メチル−3−メトキシブチルアセテート、エチル−3−エトキシプロピオネートなどのグリコールエーテルエステル、例えば、ジエチルエーテル、テトラヒドロフラン、ジオキサンなどのエーテル、例えば、塩化メチル、塩化メチレン、クロロホルム、四塩化炭素、臭化メチル、ヨウ化メチレン、ジクロロエタンなどのハロゲン化脂肪族炭化水素、例えば、N−メチルピロリドン、ジメチルホルムアミド、N,N’−ジメチルアセトアミド(DMAc)、ジメチルスルホキシド(DMF)、ヘキサメチルホスホニルアミドなどの極性非プロトン性溶媒などが挙げられる。
イソシアネート基末端プレポリマーを合成するには、グラフトポリオールの水酸基に対する、ポリイソシアネートのイソシアネート基の当量比(イソシアネート基/水酸基)が、1.0を超過する割合であって、例えば、1.01〜2.10の割合で、同時に配合し、攪拌混合して反応させる。
そして、本発明のポリウレタン樹脂組成物は、各種工業用途に用いられ、例えば、柔軟性、耐熱性、耐候性および機械強度に優れる、塗料、接着剤、シーラント、エラストマーなどとして用いられる。
接着剤は、例えば、一液型または二液型として用いられ、具体的には、繊維、食品包装、合成皮革、木材、ゴム、金属などの接着や前処理(プライマー)として用いられる。
エラストマーとしては、例えば、シート、フィルム、印刷ドクター、硬質ロール、ベアリング、カップリング、ハンマー、防振材、ライナ、ギヤ、ポンプのメンブランリング、ダイヤフラム、エアブレーキ、スクリュー、エアバネ、ブッシュ、ワイパ、パッキング、靴底、ヒールトップ、電線、人工皮革などに用いられる。
(ポリエーテルポリオールの製造)
製造例1
セパラブルフラスコに、グリセリンと、グリセリンの水酸基に対して6モル%の水酸化カリウムとを加え、105℃で3時間減圧脱水し、触媒液を得た。得られた触媒液をオートクレーブに仕込み、オートクレーブ内を減圧した。次いで、オートクレーブの内圧が0.4MPa未満となるように、オートクレーブ内に、目標水酸基価になる所定量のプロピレンオキサイドを逐次装入し、その後、110℃に昇温することにより、グリセリンにプロピレンオキサイドを開環付加重合させた。
このポリエーテルポリオールは、粘度(JIS K1557−5(2007年版)のブルックフィールド形回転粘度計を用いた粘度)が510mPa・s(25℃)であり、水酸基価(JIS K1557−1(2007年版)のフタル化法に準拠した水酸基価)が56.0mgKOH/gであった。
実施例1
攪拌機、窒素導入口、モノマー装入管および水冷コンデンサーを備える2Lセパラブルフラスコに、窒素雰囲気下で、製造例1のポリエーテルポリオール880.0重量部を仕込み、オイルバスにて120℃に加熱した。次いで、メタクリル酸n−ブチル220.0重量部と、ラジカル反応開始剤としてパーヘキサC(S)(1,1−ジ(t−ブチルパーオキシ)シクロヘキサンの70重量%炭化水素溶液、日本油脂社製)30.1重量部(純度換算値:21.07重量部)とを混合したモノマー溶液を、4時間かけて均一な速度でセパラブルフラスコに滴下した。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0921モルであり、メタクリル酸n−ブチルの配合モル数は、ラジカル反応開始剤1モルに対して19.10モルであった。
実施例2
ラジカル反応開始剤の配合量を、15.0重量部(純度換算値:10.50重量部)に変更した以外は、実施例1と同様に処理して、グラフトポリエーテルポリオールを得た。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0457モルであり、メタクリル酸n−ブチルの配合モル数は、ラジカル反応開始剤1モルに対して38.47モルであった。
ラジカル反応開始剤の配合量を、7.5重量部(純度換算値:5.25重量部)に変更した以外は、実施例1と同様に処理して、グラフトポリエーテルポリオールを得た。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0228モルであり、メタクリル酸n−ブチルの配合モル数は、ラジカル反応開始剤1モルに対して76.94モルであった。
攪拌機、窒素導入口、モノマー装入管および水冷コンデンサーを備える1Lセパラブルフラスコに、窒素雰囲気下で、製造例1のポリエーテルポリオール720.0重量部を仕込み、オイルバスにて120℃に加熱した。次いで、メタクリル酸n−ブチル135.0重量部およびアクリル酸n−ブチル45.0重量部と、ラジカル反応開始剤としてパーヘキサC(S)(1,1−ジ(t−ブチルパーオキシ)シクロヘキサンの70重量%炭化水素溶液、日本油脂社製)12.3重量部(純度換算値:8.61重量部)とを混合したモノマー溶液を、4時間かけて均一な速度でセパラブルフラスコに滴下した。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0460モルであり、メタクリル酸n−ブチルおよびアクリル酸n−ブチルのそれぞれの配合モル数は、ラジカル反応開始剤1モルに対して、それぞれ、28.64モルおよび10.59モルであり、これらの合計の配合モル数は、ラジカル反応開始剤1モルに対して、39.23モルであった。
実施例5
ラジカル反応開始剤の配合量を、3.3重量部(純度換算値:2.31重量部)に変更した以外は、実施例4と同様に処理して、グラフトポリエーテルポリオール得た。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0124モルであり、メタクリル酸n−ブチルおよびアクリル酸n−ブチルのそれぞれの配合モル数は、ラジカル重合開始剤1モルに対して、106.06モルおよび39.21モルであり、これらの合計の配合モル数は、ラジカル重合開始剤1モルに対して、145.27モルであった。
ラジカル反応開始剤の配合量を、2.2重量部(純度換算値:1.54重量部)に変更した以外は、実施例4と同様に処理して、グラフトポリエーテルポリオールを得た。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0081モルであり、メタクリル酸n−ブチルおよびアクリル酸n−ブチルのそれぞれの配合モル数は、ラジカル重合開始剤1モルに対して、それぞれ、163.50モルおよび60.45モルであり、これらの合計の配合モル数は、ラジカル重合開始剤1モルに対して、223.95モルであった。
ラジカル反応開始剤の配合量を、1.1重量部(純度換算値:0.77重量部)に変更した以外は、実施例4と同様に処理して、グラフトポリエーテルポリオールを得た。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0040モルであり、メタクリル酸n−ブチルおよびアクリル酸n−ブチルのそれぞれの配合モル数は、ラジカル重合開始剤1モルに対して、それぞれ、327.00モルおよび120.90モルであり、これらの合計の配合モル数は、ラジカル重合開始剤1モルに対して、447.90モルであった。
攪拌機、窒素導入口、モノマー装入管および水冷コンデンサーを備える2Lセパラブルフラスコに、窒素雰囲気下で、製造例1のポリエーテルポリオール800.0重量部を仕込み、オイルバスにて120℃に加熱した。次いで、メタクリル酸n−ブチル100.0重量部およびアクリル酸n−ブチル100.0重量部と、ラジカル反応開始剤としてパーヘキサC(S)(1,1−ジ(t−ブチルパーオキシ)シクロヘキサンの70重量%炭化水素溶液、日本油脂社製)24.8重量部(純度換算値:17.36重量部)とを混合したモノマー溶液を、4時間かけて均一な速度でセパラブルフラスコに滴下した。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0833モルであり、メタクリル酸n−ブチルおよびアクリル酸n−ブチルのそれぞれの配合モル数は、ラジカル反応開始剤1モルに対して、それぞれ10.55モルおよび11.71モルであり、これらの合計の配合モル数は、ラジカル反応開始剤1モルに対して、22.26モルであった。
実施例9
攪拌機、窒素導入口、モノマー装入管および水冷コンデンサーを備える1Lセパラブルフラスコに、窒素雰囲気下で、製造例1のポリエーテルポリオール720.0重量部を仕込み、オイルバスにて120℃に加熱した。次いで、メタクリル酸n−ブチル94.7重量部およびアクリル酸n−ブチル85.3重量部と、ラジカル反応開始剤としてパーヘキサC(S)(1,1−ジ(t−ブチルパーオキシ)シクロヘキサンの70重量%炭化水素溶液、日本油脂社製)1.1重量部(純度換算値:0.77重量部)とを混合したモノマー溶液を、4時間かけて均一な速度でセパラブルフラスコに滴下した。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0040モルであり、メタクリル酸n−ブチルおよびアクリル酸n−ブチルのそれぞれの配合モル数は、ラジカル反応開始剤1モルに対して、それぞれ、229.39モルおよび229.18モルであり、これらの合計の配合モル数は、ラジカル反応開始剤1モルに対して、458.57モルであった。
実施例10
ラジカル反応開始剤の配合量を、0.7重量部(純度換算値:0.49重量部)に変更した以外は、実施例9と同様に処理して、グラフトポリエーテルポリオールを得た。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0027モルであり、メタクリル酸n−ブチルおよびアクリル酸n−ブチルのそれぞれの配合モル数は、ラジカル反応開始剤1モルに対して、344.08モルおよび343.77モルであり、これらの合計の配合モル数は、ラジカル反応開始剤1モルに対して、687.85モルであった。
攪拌機、窒素導入口、モノマー装入管および水冷コンデンサーを備える1Lセパラブルフラスコに、窒素雰囲気下で、製造例1のポリエーテルポリオール720.0重量部を仕込み、オイルバスにて120℃に加熱した。次いで、メタクリル酸シクロヘキシル180.0重量部と、ラジカル反応開始剤としてパーヘキサC(S)(1,1−ジ(t−ブチルパーオキシ)シクロヘキサンの70重量%炭化水素溶液、日本油脂社製)12.3重量部(純度換算値:8.61重量部)とを混合したモノマー溶液を、4時間かけて均一な速度でセパラブルフラスコに滴下した。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0460モルであり、メタクリル酸シクロヘキシルの配合モル数は、ラジカル反応開始剤1モルに対して32.29モルであった。
実施例12
攪拌機、窒素導入口、モノマー装入管および水冷コンデンサーを備える1Lセパラブルフラスコに、窒素雰囲気下で、製造例1のポリエーテルポリオール540.0重量部を仕込み、オイルバスにて120℃に加熱した。次いで、メタクリル酸n−ブチル189.3重量部およびアクリル酸n−ブチル170.7重量部と、ラジカル反応開始剤としてパーヘキサC(S)(1,1−ジ(t−ブチルパーオキシ)シクロヘキサンの70重量%炭化水素溶液、日本油脂社製)6.7重量部(純度換算値:4.69重量部)とを混合したモノマー溶液を、4時間かけて均一な速度でセパラブルフラスコに滴下した。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0332モルであり、メタクリル酸n−ブチルおよびアクリル酸n−ブチルのそれぞれの配合モル数は、ラジカル反応開始剤1モルに対して、それぞれ、74.36モルおよび74.37モルであり、これらの合計の配合モル数は、ラジカル反応開始剤1モルに対して、148.73モルであった。
実施例13
ラジカル反応開始剤の配合量を、2.2重量部(純度換算値:1.54重量部)に変更した以外は、実施例12と同様に処理して、グラフトポリエーテルポリオールを得た。なお、ラジカル反応開始剤の配合モル数は、ポリエーテルポリオールの水酸基1モルに対して0.0108モルであり、メタクリル酸n−ブチルおよびアクリル酸n−ブチルのそれぞれの配合モル数は、ラジカル重合開始剤1モルに対して、それぞれ、229.27モルおよび229.32モルであり、これらの合計の配合モル数は、ラジカル重合開始剤1モルに対して、458.59モルであった。
製造例1により得られたポリエーテルポリオールを、そのまま比較例1のサンプルとして供した。
比較例2
比較例1のポリエーテルポリオール720.0重量部に対して、可塑剤(商品名:ARUFON UP−1021、アクリル系高分子可塑剤、東亞合成社製)180.0重量部を配合して攪拌混合した。得られた組成物を比較例2のポリエーテルポリオールとして供した。
ラジカル反応開始剤の配合量を、60.2重量部(純度換算値:42.14重量部)に変更した以外は、実施例1と同様に処理して、グラフトポリエーテルポリオールを得た。なお、ラジカル反応開始剤の配合モル数は、グラフトポリエーテルポリオールの水酸基1モルに対して0.1838モルであり、メタクリル酸n−ブチルの配合モル数は、ラジカル反応開始剤1モルに対して9.57モルであった。
実施例1〜13および比較例3のグラフトポリエーテルポリオールと、比較例1および2のポリエーテルポリオールとについて、下記の評価項目を、下記の手順に従って評価した。なお、「4) ゲルパーミエーションクロマトグラフ」については、実施例1〜11および比較例3のグラフトポリエーテルポリオールのみを、評価した。その結果を、表1および表2に示す。
1) 外観
室温(25℃)において、目視により観察した。
2) 粘度(25℃)
JIS K1557−5(2007年版)のブルックフィールド形回転粘度計を用いる測定方法に準拠して測定した。
3) 水酸基価
JIS K1557−1(2007年版)のフタル化法に準拠して測定した。
4) ゲルパーミエーションクロマトグラフ
i) R値の算出および校正曲線の作成
下記のゲルパーミエーションクロマトグラフにより、ゲルパーミエーションクロマトグラフィー測定した。
装置:Alliance(Waters社製)
示差屈折率検出器:2410型(Waters社製)
紫外線検出器:996型多波長検出器(測定波長:254nm)
カラム(Plgel GUARD+5μmMixed−C×3本、
PolymerLab社製)
・Plgel GUARD(ガードカラム、50×7.5mm)
・5μmMixed−C(300×7.5mm)
移動相:テトラヒドロフラン(THF)
流速:1(ml/min)
測定温度:40℃
グラフトポリエーテルポリオールを、以下の手順に従って標識化し、その後、これをゲルパーミエーションクロマトグラフィー測定した。
ゲルパーミエーションクロマトグラフィー測定により得られたクロマトグラムは、高分子量側ピークと低分子量側ピークとを有しており、これにより、上記式(3)で示される(HUV/LUV)/(HRI/LRI)の値を算出した。続いて、上記式(4)で示されるRを算出した。
ii) 平均枝分子量の算出
作成した校正曲線に、R値を当てはめることにより、平均枝分子量を算出した。
実施例1〜13および比較例3のグラフトポリエーテルポリオール100重量部、または、比較例1および比較例2のポリエーテルポリオール100重量部に対して、表1および表2に示す配合処方に準じたH6XDI(1,3−ビス(イソシアナトメチル)シクロヘキサン、商品名:タケネート600、三井化学ポリウレタン社製)と、ヘキソエート鉛24%(24%オクチル酸鉛、東栄化工社製)0.02重量部とを配合して、これらを攪拌混合した後、5分間脱泡した。脱泡直後(流動性を有しているうちに)、予め100℃に加熱した金型に、混合物を注入し、これを100℃のオーブンに投入して、15時間、反応させて硬化させた。その後、オーブンから取り出して脱型した後、さらに、室温で7日間養生させることにより、ポリウレタン樹脂硬化物を得た。
実施例1〜13および比較例1〜3から調製されたポリウレタン樹脂硬化物について、下記の評価項目を、下記の手順に従って評価した。その結果を、表1および表2に示す。
1) 硬度(SHORE A)
JIS K7312(1996年版)の「熱硬化性ポリウレタンエラストマー成形物の物理試験方法」の7項の「硬さ試験」の記載およびJIS K6253(2006年版)「加硫ゴム及び熱可塑性ゴムの硬さ試験方法」の5項の「デュロメーター硬さ」の試験タイプAの記載に準拠した測定した。
2) 破断時引裂き応力(引裂き強さ)
JIS K7312(1996年版)の6項の「引裂試験」に準拠し、6.3項の「試験片」に記載の(B)切込みなしアングル形試験片を用いて、破断時引裂き応力(引裂き強さ)を測定した。
3) 破断時伸び(切断時伸び)
JIS K7312(1996年版)の5項の「引張試験」に準拠し、5.3項の「試験片」に記載の4号形ダンベル状試験片を用いて測定し、5.5.2項の「切断時伸び」の記載に準拠して、破断時伸び(切断時伸び)を算出した。
4) 引張応力(50%および100%)
(モジュラス50(M50)およびモジュラス100(M100))
JIS K7312(1996年版)の5項の「引張試験」に準拠し、5.3項の「試験片」に記載の4号形ダンベル状試験片を用いて測定し、5.5.3項の「引張応力」の記載に準拠して、伸び50%時の引張応力であるモジュラス50(M50)と、伸び100%時の引張応力であるモジュラス100(M100)とをそれぞれ算出した。
5) 破断時応力(引張強さ)
JIS K7312(1996年版)の5項の「引張試験」に準拠し、5.3項の「試験片」に記載の4号形ダンベル状試験片を用いて測定し、5.5.1項の「引張強さ」の記載に準拠して、破断時応力(引張強さ)を算出した。
6) 耐熱性
ポリウレタン樹脂硬化物の試験片を80℃のオーブンの中に静置して、5日間放置し、シートの形状変化を観察して下記の基準で評価した。
△:一部が溶融した。
×:溶融した。
7) 耐候性
40mm×40mm×2mmのポリウレタン樹脂硬化物について、ダイプラメタルウエザー(KU−R5NCI、ダイプラ・ウィンテス社製)により、下記の条件にて耐候性試験を実施し、シートの形状変化を観察して下記の基準で評価した。
・照度:80mW/cm2
・温度:60℃
・湿度:50%RH
・シャワー回数:10時間に1回
・試験時間:20時間
・評価基準
A:ブリードアウト、溶融とも確認されず、形状に変化がなかった。
B:ブリードアウト、溶融が確認された。
BMA:メタクリル酸n−ブチル
BA:アクリル酸n−ブチル
CHMA:メタクリル酸シクロヘキシル
Claims (6)
- ポリエーテルポリオールに、前記ポリエーテルポリオールの水酸基1モルに対して0.1モル未満のラジカル反応開始剤の存在下で、(メタ)アクリル酸エステルをグラフト反応させて得られることを特徴とする、グラフトポリエーテルポリオール。
- 示差屈折率検出器および紫外線検出器を装備したゲルパーミエーションクロマトグラフにより測定され、高分子量側ピークと低分子量側ピークとを有するクロマトグラムから、下記式(1)により求められる値が、0.5以下であることを特徴とする、請求項1に記載のグラフトポリエーテルポリオール。
(HUV/LUV)/(HRI/LRI) ・・・(1)
HUV:波長254nmにおいて、紫外線検出器により検出された高分子量側ピークのピーク面積
LUV:波長254nmにおいて、紫外線検出器により検出された低分子量側ピークのピーク面積
HRI:示差屈折率検出器により検出された高分子量側ピークのピーク面積
LRI:示差屈折率検出器により検出された低分子量側ピークのピーク面積 - 前記ポリエーテルポリオールの水酸基価が、110mgKOH/g以下であることを特徴とする、請求項1または2に記載のグラフトポリエーテルポリオール。
- 請求項1〜3のいずれかに記載のグラフトポリエーテルポリオールと、
ポリイソシアネートと
を含むことを特徴とする、ポリウレタン樹脂組成物。 - 請求項4に記載のポリウレタン樹脂組成物を硬化させることにより得られることを特徴とする、ポリウレタン樹脂硬化物。
- ポリエーテルポリオールに、前記ポリエーテルポリオールの水酸基1モルに対して0.1モル未満のラジカル反応開始剤の存在下で、(メタ)アクリル酸エステルをグラフト反応させることを特徴とする、グラフトポリエーテルポリオールの製造方法。