JP2008513251A - スリップ・コート組成物および重合性積層体 - Google Patents
スリップ・コート組成物および重合性積層体 Download PDFInfo
- Publication number
- JP2008513251A JP2008513251A JP2007532365A JP2007532365A JP2008513251A JP 2008513251 A JP2008513251 A JP 2008513251A JP 2007532365 A JP2007532365 A JP 2007532365A JP 2007532365 A JP2007532365 A JP 2007532365A JP 2008513251 A JP2008513251 A JP 2008513251A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- blend
- polyethylene
- polyethylene resin
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】(A)基板、および(B)該基板の少なくとも一部分を被覆する滑り層(slip layer)を含む重合性積層体であって、前記滑り層が(i)ポリエチレン・ブレンド、(ii)前記ポリエチレン・ブレンド100重量部当たり、プロピレン・モノマーから誘導されるプロピレン単位を有する約2.5〜約15重量のプロピレン・ポリマーまたはプロピレン・モノマー、および(iii)前記ポリエチレン・ブレンド100重量部当たり、約4.5〜約20重量の動的加硫化ゴムを含む重合性積層体。
【選択図】図1
Description
概略的に述べると、本発明は、(A)基板、および(B)該基板の少なくとも一部分を被覆する滑り層(slip layer)を含む重合性積層体であって、前記滑り層が実質的に(i)ポリエチレン・ブレンド、(ii)前記ポリエチレン・ブレンド100重量部当たり、プロピレン・モノマーから誘導されるプロピレン単位を有する約2.5〜約15重量のプロピレンのポリマーまたはコポリマー、および(iii)前記ポリエチレン・ブレンド100重量部当たり、約4.5〜約20重量の動的加硫化ゴムからなる重合性積層体であり、ここで前記ブレンドが、(a)前記ブレンドの総重量に基づいて、110,000〜約140,000の重量平均分子量および約12未満のポリ分散性(polydispersity)を有する第1ポリエチレン樹脂の約3〜約97重量%、(b)前記ブレンドの総重量に基づいて、50,000〜109,999までの重量平均分子量および約12未満のポリ分散性を有する第2ポリエチレン樹脂の約3〜約97重量%、および(c)前記ブレンドの総重量に基づいて、20,000〜49,999までの重量平均分子量および約12未満のポリ分散性を有する第3ポリエチレン樹脂の約0〜約40重量%を含み、ただし、前記ブレンドが前記ブレンドの総重量に基づいて、前記第1ポリエチレンおよび第2ポリエチレンの混成物の60%以上を含む、ことを特徴とする重合性積層体を提供する。
本発明の積層体は、第1ポリマー層および第2ポリマー層を含む。この第1ポリマー層は比較的低い摩擦係数を有する。1つの態様において前記積層体は、スリップ・コート(slip coat)を形成する第1層およびスリップが搭載された基板を形成する第2層を含む天候シールの少なくとも一部分を形成する。
ポリマー性積層体用のスリップ・コートとして先行技術で用いられてきた比較ポリマー性ブレンドを試料1〜3のように調製した。特に試料1は、約22重量%の高分子量ポリエチレン樹脂、約56重量%の中分子量ポリエチレン樹脂、および約22重量%の低分子量ポリエチレン樹脂をブレンドすることにより調製した。このブレンドは、また約7重量%のカーボンブラック/ポリエチレン濃縮物も含む。この比較例は米国特許第5,110,685号で開示されたものに類似している。
さらに7つのポリマー性ブレンドを調製し、これらのブレンドの押出プロフィールを様々な物理および性能特性について試験した。表IIに示すように、様々なポリエチレン成分(例えば、高、中、および低分子量ポリエチレン樹脂)の比率を変化させた。ブレンドにおける他の全ての構成は一定にした。各ポリエチレン樹脂について表IIで与えられた値は、組成物のポリエチレン・ブレンド成分の重量%に基づいている。全ポリマー性ブレンドには、約62重量%のポリエチレン・ブレンド、7重量%のカーボンブラック/ポリエチレン濃縮物、および27重量%の熱可塑性加硫化物が含まれた。前記カーボンブラック/ポリエチレン濃縮物は、試料1〜5で用いたものと同一であった。TPVIIと命名される熱可塑性加硫化物は、ケイ素−ヒドリド硬化系を用いて硬化された。具体的には、この処方は、200重量%の油伸展オレフィン性エラストマー性コポリマー(この量には100重量部のゴムおよび100重量部の油が含まれる)、50重量部の熱可塑性ポリプロピレン・ホモポリマー、168全重量部のパラフィン油(ゴムを含む100重量部を含む160重量部)、42重量部の粘土、2重量部の水素化ケイ素、0.004017重量部の白金触媒、1重量部のステアリン酸カルシウム、および0.5重量部の抗酸化剤を含んだ。前記エラストマー性コポリマーは、商品名VISTALONTM1696(エクソンモービル社)のポリ(エチレン−co−ポリプレン−co−5−ビニル−2−ノルボルネン)であった。前記熱可塑性ポリプロピレン・ホモポリマーは、約0.6〜1.0の溶融指標を特徴とする、商品名EQUISTARTM51S07A、前記水素化ケイ素は、商品名2−5084(ダウ社)、前記白金触媒は商品名UCT300触媒(ユナイティド・ケミカル・テクノロジーズ社)、前記抗酸化剤は商品名IRGANOXTM1010のものであった。
11 本体
12、13 自動車ドアの上部
14 U字型溝部
15、16 本体11の両側部
17、18 両側部(15および16)の下端部
20 窓ガラス
21、22 スリップ・コート(slip-coating)
31、32 天候シール
33、34 垂直部
35、36 上方突出部
35’ 突出端(35)の低部
36’ 突出部(36)の低部
37、38 下方ガラス当接突出部
40 自動車のドアパネルの部分
41、42 自動車のドアパネルの部分(40)の水平な下壁
42、43 外部ドアパネルの壁
44 ドアパネル(40)の内壁
45、46 スリップ・コート
47、48 スリップ・コート
50 補助天候シール
60 天候シール
61 基板
62 基板(61)の下部
63、64 貫通路
70 ガラス窓
Claims (18)
- (A)基板、および
(B)該基板の少なくとも一部分を覆う滑り層であって、実質的に
(i)ポリエチレン・ブレンドであって、
(a)前記ブレンドの総重量に基づいて約3〜約97重量%の、110,000〜約140,000の重量平均分子量および約12未満のポリ分散性を有する第1ポリエチレン樹脂、
(b)前記ブレンドの総重量に基づいて約3〜約97重量%の、50,000〜約109,999の重量平均分子量および約12未満のポリ分散性を有する第2ポリエチレン樹脂、および
(c)前記ブレンドの総重量に基づいて約0〜約40重量%の、20,000〜49,999の重量平均分子量および約12未満のポリ分散性を有する第3ポリエチレン樹脂、
を含み、但し、前記ブレンドの総重量に基づいて60重量%以上の混合された前記第1ポリエチレン樹脂および前記第2ポリエチレン樹脂を含むポリエチレン・ブレンド、
(ii)前記ポリエチレン・ブレンドの100重量部あたり、約2.5〜約15重量部のプロピレン・モノマーから誘導されるプロピレン単位を有するプロピレンのポリマーまたはコポリマー、および
(iii)前記ポリエチレン・ブレンドの100重量部あたり、約4.5〜約20重量部の動的加硫化ゴム、
からなる滑り層、
を含むポリマー性積層体。 - 前記ポリエチレン・ブレンドが、
(a)約10〜約60重量%の前記第1ポリエチレン樹脂、
(b)約10〜約80重量%の前記第2ポリエチレン樹脂、および
(c)約3〜約30重量%の前記第3ポリエチレン樹脂、
を含み、ここで重量%が前記ポリエチレン・ブレンドの総重量に基づくことを特徴とする請求項1に記載のポリマー性積層体。 - 前記ポリエチレン・ブレンドが、
(a)約15〜約50重量%の前記第1ポリエチレン樹脂、
(b)約15〜約70重量%の前記第2ポリエチレン樹脂、および
(c)約5〜約25重量%の前記第3ポリエチレン樹脂、
を含み、ここで重量%が前記ポリエチレン・ブレンドの総重量に基づくことを特徴とする請求項1に記載のポリマー性積層体。 - 前記滑り層が実質的に、ポリエチレン・ブレンド100重量部に基づいて、
(i)前記ポリエチレン・ブレンド、
(ii)約4〜約12重量部の前記プロピレンのポリマーまたはコポリマー、
(iii)約6〜約18重量部の前記動的加硫化ゴム、
(iv)0〜約30重量部の重点剤、
(v)0〜約20重量部の滑り助剤、
(vi)0〜約20重量部の油、
(vii)0〜約10重量部の重合性加工添加剤、
(viii)0〜約10重量部の安定性増強剤、および
(ix)0〜10重量部の低密度ポリエチレン、
からなることを特徴とする請求項1に記載のポリマー性積層体。 - 前記滑り層が実質的に、ポリエチレン・ブレンド100重量部に基づいて、
(i)前記ポリエチレン・ブレンド、
(ii)約6〜約10重量部の前記プロピレンのポリマーまたはコポリマー、
(iii)約8〜約16重量部の前記動的加硫化ゴム、
(iv)約1〜約20重量部の重点剤、
(v)約1〜約15重量部の滑り助剤、
(vi)約2〜約18重量部の油、
(vii)約0.5〜約7重量部の重合性加工添加剤、
(viii)約0.1〜約5重量部の安定性増強剤、および
(ix)0.1〜7重量部の低密度ポリエチレン、
からなることを特徴とする請求項1に記載のポリマー性積層体。 - 前記第1ポリエチレン樹脂が2.00〜5.00dl/gの実質粘度を有し、前記第2ポリエチレン樹脂が1.00〜1,99dl/gの実質粘度を有し、前記第3ポリエチレン樹脂が約0.10〜0.99dl/gの実質粘度を有することを特徴とする請求項1に記載のポリマー性積層体。
- 前記第1ポリエチレン樹脂が2.20〜4.50dl/gの実質粘度を有し、前記第2ポリエチレン樹脂が1.20〜1,90dl/gの実質粘度を有し、前記第3ポリエチレン樹脂が約0.40〜0.95dl/gの実質粘度を有することを特徴とする請求項1に記載のポリマー性積層体。
- 前記第1ポリエチレン樹脂がASTM D−1238に従って2.16kg荷重で1.0〜約12dg/分の溶融指標を有し、前記第2ポリエチレン樹脂がASTM D−1238に従って2.16kg荷重で1.1〜14dg/分の溶融指標を有し、前記第3ポリエチレン樹脂がASTM D−1238に従って2.16kg荷重で約15〜50dg/分の溶融指標を有することを特徴とする請求項1に記載のポリマー性積層体。
- 前記第1ポリエチレン樹脂が約0.93g/ccより大きな密度を有し、前記第2ポリエチレン樹脂が約0.93g/ccより大きな密度を有し、前記第3ポリエチレン樹脂が約0.93g/ccより大きな密度を有することを特徴とする請求項1に記載のポリマー性積層体。
- 前記可塑性樹脂が結晶または結晶性のポリプロピレンであり、前記動的加硫化ゴムがエチレン、プロピレン、および1種以上のジエンを含むことを特徴とする請求項1に記載のポリマー性積層体。
- 前記熱滑り助剤が、シロキサン・ポリマー類、脂肪酸類、脂肪酸トリグリセリド類、脂肪酸アミド類、エステル類、フルオロポリマー類、グラファイト、モリブデン、シリカ、ボロンニトリド、炭化ケイ素、およびこれらの混合物からなる群から選択されることを特徴とする請求項1に記載のポリマー性積層体。
- 前記動的加硫化ゴムが粒子の形態であり、この粒子の50%以上が約5ミクロン未満の平均直径を有し、このゴムがその15重量%以下が抽出可能な硬化度を有することを特徴とする請求項1に記載のポリマー性積層体。
- 前記ジエンが5−エチリデン−2−ノルボルネンを含むことを特徴とする請求項10に記載のポリマー性積層体。
- 前記ジエンが5−ビニル−2−ノルボルネンを含むことを特徴とする請求項10に記載のポリマー性積層体。
- 前記ゴムがケイ素含有硬化剤により動的加硫化されることを特徴とする請求項14に記載のポリマー性積層体。
- 請求項1のポリマー性積層体を含む天候シール。
- 積層体を製造するプロセスであって、
(I)基板を形成する熱加工可能な組成物を提供する工程、
(II)スリップ・コートを形成するための熱加工可能な組成物を調製する工程であって、
(a)熱可塑性加硫化物を形成するために、ゴムおよびプロピレンのポリマーまたはコポリマーを含むブレンド内の該ゴムを動的加硫化する工程、および
(b)前記ゴムを動的加硫化する工程後、前記熱可塑性加硫化物にポリエチレン・ブレンドを添加する工程であって、該ポリエチレン・ブレンドが、実質的に
(i)前記ブレンドの総重量に基づいて約3〜約97重量%の、110,000〜約140,000の重量平均分子量および約12未満のポリ分散性を有する第1ポリエチレン樹脂、
(ii)前記ブレンドの総重量に基づいて約3〜約97重量%の、50,000〜約109,999の重量平均分子量および約12未満のポリ分散性を有する第2ポリエチレン樹脂、および
(iii)前記ブレンドの総重量に基づいて約0〜約40重量%の、20,000〜49,999の重量平均分子量および約12未満のポリ分散性を有する第3ポリエチレン樹脂、
からなり、前記ポリエチレン・ブレンドが、前記ブレンドの総重量に基づいて60重量%以上の混合された前記第1ポリエチレン樹脂および前記第2ポリエチレン樹脂を含むことを特徴とする工程、および
(III)前記基板を形成用の組成物および前記スリップ・コート形成用の組成物を共押出して、基板および該基板の少なくとも一部分を覆うスリップ・コートを含む積層体を形成する工程、
を含む積層体を製造するプロセス。 - 実質的に
(i)ポリエチレン・ブレンドであって、
(a)前記ブレンドの総重量に基づいて約3〜約97重量%の、110,000〜約140,000の重量平均分子量および約12未満のポリ分散性を有する第1ポリエチレン樹脂、
(b)前記ブレンドの総重量に基づいて約3〜約97重量%の、50,000〜約109,999の重量平均分子量および約12未満のポリ分散性を有する第2ポリエチレン樹脂、および
(c)前記ブレンドの総重量に基づいて約0〜約40重量%の、20,000〜49,999の重量平均分子量および約12未満のポリ分散性を有する第3ポリエチレン樹脂、
を含み、かつ、前記第1ポリエチレン樹脂および前記第2ポリエチレン樹脂を、その合計量において、前記ブレンドの総重量に基づいて60重量%以上含むことを特徴とする前記ブレンド、および
(ii)プロピレンのポリマーまたはコポリマー、および
(iii)動的加硫化ゴム、
からなるスリップ・コート用組成物。