JP2008040309A - 位相差フィルム、偏光板及び液晶表示装置 - Google Patents
位相差フィルム、偏光板及び液晶表示装置 Download PDFInfo
- Publication number
- JP2008040309A JP2008040309A JP2006216738A JP2006216738A JP2008040309A JP 2008040309 A JP2008040309 A JP 2008040309A JP 2006216738 A JP2006216738 A JP 2006216738A JP 2006216738 A JP2006216738 A JP 2006216738A JP 2008040309 A JP2008040309 A JP 2008040309A
- Authority
- JP
- Japan
- Prior art keywords
- film
- liquid crystal
- retardation
- retardation film
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】少なくとも一種のアクリル系ポリマーを含むセルロースアシレートフィルムからなる支持体及び少なくとも一層の光学異方性層を有する位相差フィルムであって、正面レターデーションReと厚さ方向のレターデーションRthが下記式[1]を満たし、且つその波長分散性が下記式[2]を満たし、正面レターデーションReと厚さ方向のレターデーションRthが下記式[3]を満たし、且つその波長分散性が下記式[4]を満たす。[1]0≦Re(630)≦10かつ|Rth(630)|≦25[2]|Re(400)−Re(700)|≦10かつ−35≦Rth(400)−Rth(700)≦60[3]0≦Re(550)≦10かつ100≦Rth(550)≦300[4]1.04≦Rth(450)/Rth(550)≦1.30
【選択図】なし
Description
さらには、屈折率異方性の絶対値が特定の範囲にある光学異方性層を採用することにより、塗布ムラを改善する方法が特許文献6に開示されている。
しかしながら、以上の方法は、液晶表示装置の表示特性を満足できるレベルではなかった。
また、本発明は、液晶表示装置、特にVAモードの液晶表示装置の黒表示時における斜め方向から観察した際の光漏れや色味変化の軽減に寄与するとともに、簡易な方法で安定的に製造可能な、位相差フィルム、及び偏光板を提供することを課題とする。
また、本発明は、正面方向から観察した場合の表示特性が良好であるとともに、斜め方向から観察した場合の表示特性も良好である、具体的には、黒表示時において斜め方向から観察した場合の光漏れ及び色味変化が軽減された、液晶表示装置、特にVAモードの液晶表示装置を提供することを課題とする。
(1) 支持体及び少なくとも一層の光学異方性層を有する位相差フィルムであって、
前記支持体は、少なくとも一種のアクリル系ポリマーを含むセルロースアシレートフィルムからなり、正面レターデーションReと厚さ方向のレターデーションRthが下記式[1]を満たし、且つその波長分散性が下記式[2]を満たし;及び
前記位相差フィルムの正面レターデーションReと厚さ方向のレターデーションRthが下記式[3]を満たし、且つその波長分散性が下記式[4]を満たす位相差フィルム:
[1]0≦Re(630)≦10かつ|Rth(630)|≦25
[2]|Re(400)−Re(700)|≦10かつ−35≦Rth(400)−Rth(700)≦60
[3]0≦Re(550)≦10かつ100≦Rth(550)≦300
[4]1.04≦Rth(450)/Rth(550)≦1.30
式中、Re(λ)は、Re(λ)=(nx−ny)×dで表され、波長λnmにおける正面レターデーション値(単位:nm)を表し、Rth(λ)はRth(λ)={(nx+ny)/2−nz}×dで表され、波長λnmにおける膜厚方向のレターデーション値(単位:nm)を表し、nxはフィルム面内の遅相軸方向の屈折率であり、nyはフィルム面内の進相軸方向の屈折率であり、nzはフィルムの厚み方向の屈折率であり、dはフィルムの厚さ(nm)である。
(2) 前記支持体の波長分散性が、下記式[5]を満たす、(1)の位相差フィルム:
[5]|Re(400)−Re(700)|≦10かつ0≦Rth(400)−Rth(700)≦60 。
(3) 波長分散性が、下記式[6]を満たす、(1)又は(2)の位相差フィルム:
[6]1.06≦Rth(450)/Rth(550)≦1.30 。
(4) 前記光学異方性層の少なくとも一層が、円盤状液晶性化合物の少なくとも一種を含有する重合性液晶組成物を、該円盤状液晶化合物の分子をホメオトロピック配向させ、ネマチック液晶相の状態で重合により固定して形成された層である(1)〜(3)のいずれかの位相差フィルム。
(5) 前記光学異方性層の少なくとも一層が、棒状液晶性化合物の少なくとも一種を含有する重合性液晶組成物を、該棒状液晶性化合物の分子をコレステリック液晶相の状態で固定して形成した層である(1)〜(3)のいずれかの位相差フィルム。
(6) 前記光学異方性層の少なくとも一層が、ポリマー層である(1)〜(3)のいずれかの位相差フィルム。
(7)前記ポリマー層が、ポリアミド、ポリイミド、ポリエステル、ポリエーテルケトン、ポリアミドイミド及びポリエステルイミドからなる群から選ばれる少なくとも一種類のポリマーを含む(6)の位相差フィルム。
(8) 前記光学異方性層の少なくとも一層が、含フッ素化合物を含む(1)〜(7)のいずれかの位相差フィルム。
(9) 前記支持体が、アシル置換度2.70〜3.00のセルロースアシレートを含有するセルロースアシレートフィルムからなる(1)〜(8)のいずれかの位相差フィルム。
(10) 前記アクリル系ポリマーの重量平均分子量が、500以上10,000未満である(1)〜(9)のいずれかの位相差フィルム。
(11) 前記アクリル系ポリマーが、水酸基を主鎖及び/又は側鎖に有するアクリル系ポリマーである(1)〜(10)のいずれかの位相差フィルム。
(12) 前記支持体が、可塑剤を含むセルロースアシレートフィルムからなる(1)〜(11)のいずれかの位相差フィルム。
(13) 前記支持体の膜厚が10〜60μmである(1)〜(12)のいずれかの位相差フィルム。
(14) 偏光膜と、該偏光膜の両面に設けられた保護フィルムを有し、該保護フィルムの少なくとも一方が(1)〜(13)のいずれかの位相差フィルムである偏光板。
(15) さらに、第二の位相差フィルムを有し、前記第二の位相差フィルムの正面レターデーション及び厚さ方向のレターデーションが下記式[7]を満たし、且つ第二の位相差フィルムの波長分散が下記式[8]を満たす(14)の偏光板:
[7]70≦Re(550)≦180かつ30≦Rth(550)≦140
[8]0.7≦Re(450)/Re(550)≦1.0 。
(16) (1)〜(13)のいずれかの位相差フィルム及び/又は(14)又は(15)の偏光板を含む液晶表示装置。
(17) 互いの吸収軸が直交している二枚の偏光板、及び
該二枚の偏光板の間に、一対の基板と、該一対の基板間に挟持された、液晶分子が外部電界が印加されていない非駆動状態において前記一対の基板に対して略垂直な方向に配向する液晶層とを有する液晶セルを、有する液晶表示装置であって、
さらに、(1)〜(13)のいずれかの位相差フィルムを含むか、前記偏光板が(14)又は(15)の偏光板である、液晶表示装置。
(18) 前記液晶表示装置が、さらに第二の位相差フィルムを有し、該第二の位相差フィルムは高分子延伸フィルムからなり、正面レターデーション及び厚さ方向のレターデーションが下記式[7]を満たす、(16)又は(17)の液晶表示装置:
[7]70≦Re(550)≦180かつ30≦Rth(550)≦140 。
(19) 前記液晶表示装置が、さらに第二の位相差フィルムを有し、該第二の位相差フィルムの波長分散が、下記式[8]を満たす、(16)〜(18)のいずれかの液晶表示装置:
[8]0.7≦Re(450)/Re(550)≦1.0 。
(20) 前記液晶表示装置が、さらに第二の位相差フィルムを有し、該第二の位相差フィルムが、セルロースアシレートフィルム、ノルボルネン系フィルム、ポリカーボネート系フィルム、ポリアリレート系フィルム、ポリエステル系フィルム及びポリサルフォン系フィルムのいずれかからなる、(16)〜(19)のいずれかの液晶表示装置。
(21) 前記液晶表示装置が、さらに第二の位相差フィルムを有し、該第二の位相差フィルムが、その面内遅相軸を、前記二枚の偏光板のいずれか一方の吸収軸と直交させて配置されている、(16)〜(20)のいずれかの液晶表示装置。
特に、本発明の位相差フィルム及び偏光板は、液晶表示装置(特にVAモードの液晶表示装置)の黒表示における斜めの漏れ光及び色味変化の双方の軽減に寄与し、正面方向のみならず斜め方向の表示特性の改善に寄与する。
また、従来の液晶表示装置では、液晶セルを正確に光学的に補償するためには、複数の位相差フィルムを、それらの面内遅相軸と偏光板の吸収軸との角度を厳密に調整しながら積層する工程が必要であった。しかしながら、本発明の位相差フィルムではかかる工程を経なくてもよく、例えば、長尺の支持体に連続的に光学異方性層を形成して作製することが可能であり、また、本発明の偏光板の作製時にも、長尺の偏光膜を連続的に積層して作製することが可能である。さらに光学異方性層を塗布により形成する場合に、光学特性の確保のために層厚を厚くする必要がなく、塗布時のムラ等の問題が生じ難く、安定的に作製することが可能である。
さらに、本発明によれば、正面方向から観察した場合の表示特性が良好であるとともに、斜め方向から観察した場合の表示特性も良好である、具体的には、黒表示時において斜め方向から観察した場合の光漏れ及び色味変化が軽減された、液晶表示装置、特にVAモードの液晶表示装置を提供することができる。
Re(λ)=(nx−ny)×d
(式中、nxはフィルム面内における遅相軸方向の屈折率であり、nyはフィルム面内の進相軸方向の屈折率であり、nzはフィルムの厚み方向の屈折率であり、dはフィルムの厚さ(nm)である。)
Rth=((nx+ny)/2−nz)×d
(式中、nxはフィルム面内の遅相軸方向の屈折率であり、nyはフィルム面内の進相軸方向の屈折率であり、nzはフィルムの厚み方向の屈折率であり、dはフィルムの厚さ(nm)である。)
本発明は、Re及びRthの絶対値が小さい、所定のセルロースアシレートフィルムからなる支持体と、光学異方性層とを組合せた位相差フィルムに関する。具体的には、支持体の正面レターデーションと厚さ方向のレターデーションRthが下記式[1]を満たし、且つ前記支持体の波長分散性が下記式[2]を満たし、さらに光学異方性層と組み合わせることにより、位相差フィルム全体としては、正面レターデーションReと厚さ方向のレターデーションRthが下記式[3]を満たし、且つ波長分散性が下記式[4]を満たす位相差フィルムに関する。
[1]0≦Re(630)≦10かつ|Rth(630)|≦25
[2]|Re(400)−Re(700)|≦10かつ−35≦Rth(400)−Rth(700)≦60
[3]0≦Re(550)≦10かつ100≦Rth(550)≦300
[4]1.04≦Rth(450)/Rth(550)≦1.30
[支持体]
本発明の位相差フィルムの支持体には、少なくとも一種のアクリル系ポリマーを含有するセルロースアシレートフィルムが用いられる。セルロースアシレートフィルムは、一般的に、可視光領域に吸収が無く、光透過率が80%以上であり、複屈折性に基づくレターデーションが小さい観点から好ましい。さらに、セルロースアシレートフィルムは、偏光膜に直接貼り合せて偏光板と一体型にでき、また偏光膜の保護膜としての機能にも優れているの観点からも好ましい。
前記支持体のRe及びRthは、下記式[1]’を満たすのが好ましく、下記式[1]”を満たすのがさらに好ましい。
[1]’ 0≦Re(630)≦5かつ|Rth(630)|≦20nm
[1]” 0≦Re(630)≦2かつ|Rth(630)|≦15nm
また、前記支持体の波長分散性は、下記式[2]’を満足するのが好ましく、下記式[2]”を満たすのがさらに好ましい。
[2]’ |Re(400)−Re(700)|≦5かつ−10≦Rth(400)−Rth(700)≦50
[2]” |Re(400)−Re(700)|≦3かつ0≦Rth(400)−Rth(700)≦45
前記セルロースアシレートフィルムは、セルロースアシレートを含有する組成物から形成することができる。前記セルロースアシレートの原料となるセルロースとしては、綿花リンタや木材パルプ(広葉樹パルプ、針葉樹パルプ)などがあり、何れの原料セルロースから得られるセルロースアシレートでも使用でき、場合により混合して使用してもよい。これらの原料セルロースについての詳細な記載は、例えばプラスチック材料講座(17)繊維素系樹脂(丸澤、宇田著、日刊工業新聞社、1970年発行)や発明協会公開技報2001−1745(7頁〜8頁)に記載のセルロースを用いることができ、本発明で用いるセルロースアシレートフィルムに対してはいずれの方法も好ましく採用できる。
前記セルロースアシレートフィルムの作製に用いられるセルロースアシレートはセルロースの水酸基がアシル化されたものであり、例えば、アシル基の炭素原子数2〜22のアセチル基で置換されたセルロースアシレートを用いるのが好ましい。本発明で用いるセルロースアシレートにおいて、セルロースの水酸基への置換度については特に限定されないが、セルロースの水酸基に置換する酢酸及び/又は炭素原子数3〜22の脂肪酸の結合度を測定し、計算によって置換度を得ることができる。測定方法としては、ASTMのD−817−91に準じて実施することができる。
具体的には、アシル基としては、アセチル基、プロピオニル基、ブタノイル基、へプタノイル基、ヘキサノイル基、オクタノイル基、デカノイル基、ドデカノイル基、トリデカノイル基、テトラデカノイル基、ヘキサデカノイル基、オクタデカノイル基、イソブタノイル基、tert−ブタノイル基、シクロヘキサンカルボニル基、オレオイル基、ベンゾイル基、ナフチルカルボニル基、シンナモイル基が好ましく、アセチル基、プロピオニル基、ブタノイル基、ドデカノイル基、オクタデカノイル基、tert−ブタノイル基、オレオイル基、ベンゾイル基、ナフチルカルボニル基、シンナモイル基がより好ましく、アセチル基、プロピオニル基、ブタノイル基がさらに好ましい。
本発明に、支持体として用いるセルロースアシレートフィルムは、少なくとも一種のアクリル系ポリマーを含有する。なお、本明細書において「アクリル系ポリマー」とは、アクリル酸及びその誘導体(アクリル酸エステルのみならずヒドロキシ基等の置換基を有するアクリル酸やアクリル酸エステルを含む)をモノマーとするホモポリマー及びコポリマー、ならびにメタクリル酸及びその誘導体(メタクリル酸エステルのみならずヒドロキシ基等の置換基を有するメタクリル酸やメタクリル酸エステルを含む)をモノマーとするホモポリマー及びコポリマーの総称である。
前記アクリル系ポリマーは、セルロースアシレートフィルム中に添加することにより、該フィルムの光学異方性を低下させる。本発明には、重量平均分子量が500以上10,000未満(より好ましくは500〜5,000)のアクリル系ポリマーを用いるのが好ましい。重量平均分子量が前記範囲であると、セルロースエステルとの相溶性が良好で、且つ製膜中において蒸発及び揮発が生じ難い。特に、(メタ)アクリル酸もしくは(メタ)アクリル酸エステル系ポリマー、芳香環を側鎖に有するアクリル系ポリマー又はシクロヘキシル基を側鎖に有するアクリル系ポリマーは、上記分子量であると、上記に加え、得られるセルロースアシレートフィルムが透明性に優れ、透湿度も極めて低く、従って偏光板用保護フィルムとしても優れた性能を示す。
ポリマーを構成するモノマー単位としては:例えば、アクリル酸メチル、アクリル酸エチル、アクリル酸プロピル(i−、n−)、アクリル酸ブチル(n−、i−、s−、t−)、アクリル酸ペンチル(n−、i−、s−)、アクリル酸ヘキシル(n−、i−)、アクリル酸ヘプチル(n−、i−)、アクリル酸オクチル(n−、i−)、アクリル酸ノニル(n−、i−)、アクリル酸ミリスチル(n−、i−)、アクリル酸シクロヘキシル、アクリル酸(2−エチルヘキシル)、アクリル酸ベンジル、アクリル酸フェネチル、アクリル酸(ε−カプロラクトン)、アクリル酸(2−ヒドロキシエチル)、アクリル酸(2−ヒドロキシプロピル)、アクリル酸(3−ヒドロキシプロピル)、アクリル酸(4−ヒドロキシブチル)、アクリル酸(2−ヒドロキシブチル)、アクリル酸(2−メトキシエチル)、アクリル酸(2−エトキシエチル)、アクリル酸フェニル、アクリル酸(2又は4−クロロフェニル)、アクリル酸(2又は3又は4−エトキシカルボニルフェニル)、アクリル酸(o又はm又はp−トリル)、アクリル酸ベンジル、アクリル酸フェネチル、アクリル酸(2−ナフチル)、アクリル酸シクロヘキシル、アクリル酸(4−メチルシクロヘキシル)、アクリル酸(4−エチルシクロヘキシル)、アクリル酸−p−ヒドロキシメチルフェニル、アクリル酸−p−(2−ヒドロキシエチル)フェニル等、;メタクリル酸エステルとして、上記アクリル酸エステルをメタクリル酸エステルに変えたもの;不飽和酸として、例えば、アクリル酸、メタクリル酸、無水マレイン酸、クロトン酸、イタコン酸等を挙げることができる。上記モノマーで構成されるポリマーはコポリマーでもホモポリマーでもよい。
側鎖に水酸基を有するアクリル系ポリマーとしては、アクリル酸エステルのエステル部に水酸基を有する化合物と、メタクリル酸エステル(エステル部に水酸基を有しない化合物)との共重合体が特に好ましい。
セルロースアシレートフィルムは、Re及びRthの値が、一般的に、短波長側よりも長波長側が大きい波長分散特性となる傾向にある。
本発明において支持体として用いるセルロースアシレートフィルムは、その波長分散性の指標となり得る|Re(400)−Re(700)|の値が、上記式[2]を満足し、好ましくは上記式[2]’を満足し、さらに好ましくは上記式[2]”を満足する。
上記波長分散を達成する為に、波長分散を調整する添加剤を加えてもよい。波長分散調整剤としては、通常、200〜400nmの紫外領域に吸収を持つ化合物が用いられる。例えば、該化合物をセルロースアシレート固形分に対して0.01〜30質量%添加することによって、セルロースアシレートフィルムのRe及び/又はRthの波長分散を調整することができる。波長分散を調整する化合物はセルロースアシレートに十分均一に相溶し、且つ、紫外領域の吸収帯範囲は200〜400nmが好ましく、220〜395nmがより好ましく、240〜390nmがさらに好ましい。
本発明に支持体として使用可能なセルロースアシレートフィルムには、可塑剤を添加することが、フィルムの脆性を改良する点で好ましい。具体的にはフィルム裁断時のクラックの発生等を防ぐことができる。可塑効果のある化合物としては、リン酸エステル、カルボン酸エステル、アミド、エーテル、ウレタンなどの官能基を有する化合物が好ましい。これらの好ましい化合物の例としては以下のものが挙げられるが、これらに限定されるものではない。
リン酸エステルとしては、トリフェニルホフェート、ビフェニルジフェニルホフェート、トリクレジルホスフェート、クレジルジフェニルホスフェート、オクチルジフェニルホスフェート、トリオクチルホスフェート、トリブチルホスフェート、レゾルシノールビスジフェニルフォスフェート、1,3−フェニレンビスジキシレニルフォスフェート、ビスフェノールAビスジフェニルフォスフェートなどを挙げることができる。
カルボン酸エステルとしては、トリメチロールプロパントリベンゾエート、トリメチロールプロパントリシクロヘキシルカルボキシレート、ペンタエリスリトールテトラブチレート、グリセリントリブチレート、トリアセチン、トリブチリン、トリプロピオニンなどの多価アルコールのカルボン酸エステル;コハク酸ジブチル、アジピン酸ジフェニル、フタル酸ジブチル、フタル酸ジアリール、フタル酸ジメチル、フタル酸ジエチル、フタル酸ジ−2−メトキシエチル、フタル酸ジオクチル、フタル酸ジ−2−エチルヘキシルフタレート、トリメリット酸トリメチル、ピロメリット酸テトラエチルなどの飽和、不飽和多価カルボン酸エステル;メチルメタクリレートやエチルアクリレートのオリゴマー;などを挙げることができる。
またオキシ酸のエステルとして、クエン酸トリエチル、クエン酸アセチル・トリエチル、酒石酸ジブチル、ジアセチル酒石酸ジブチル、ブチルフタリルブチルグリコレート、エチルフタリルエチルグリコレート、メチルフタリルエチルグリコレート、ブチルフタリルブチルグリコレートなどのグリコール酸、サリチル酸、クエン酸、リンゴ酸、酒石酸などのオキシ酸のエステルを挙げることができる。
アミドとしては、N−フェニル−ベンゼンカルボンアミド,N−フェニル−p−トルエンスルホンアミド、N−エチルトルエンスルホンアミドなどのカルボン酸アミドやスルホン酸アミドを挙げることができる。
その他、p−トルエンスルホン酸o−クレジルなどのようなスルホン酸エステル、トルエンジイソシアネートとエタノールやヘキシルアルコールなどのアルコールとの反応によるウレタンなどを挙げることができる。
ビスフェノールAのグリシジルエーテルなどのようなエーテルオリゴマーや、トルエンジイソシアネートと2価のアルコールと1価のアルコール混合物との反応によるウレタンオリゴマーなどの低分子量のオリゴマーも好ましい例として挙げられる。
その他、トリチルアルコールなども好ましい例として挙げられる。
これらの可塑効果を示す化合物の添加量は、セルロースアシレート100質量部に対して、5〜30質量部が好ましく、10〜25質量部がさらに好ましい。
本発明の位相差フィルムは、少なくとも一層の光学異方性層を前記支持体上に有する。所定の光学特性を有する前記支持体と積層することによって、上記光学特性を満足する本発明の位相差フィルムとなる限り、基本的にその材料及び形態については特に制限されない。例えば、ポリマーフィルム(好ましくは、複屈折ポリマーフィルムからなる位相差膜)であってもよいし、支持体上に高分子化合物を含有する層を形成後に加熱延伸して得られる膜であってもよいし、及び液晶性組成物を所定の液晶相とした後、その状態に固定して形成された層であってもよい。また、それぞれを積層してもよい。
前記光学異方性層は、重合性液晶性組成物を所定の液晶相とした後、その配向状態を重合により固定して形成した層であるのが好ましい。
その一態様としては、円盤状液晶性化合物の少なくとも一種を含有する重合性液晶組成物を、該円盤状液晶化合物の分子をホメオトロピック配向させ、ネマチック液晶相の状態で重合により固定して形成された層が挙げられる。また他の態様として、棒状液晶性化合物の少なくとも一種を含有する重合性液晶組成物を、該棒状液晶性化合物の分子をコレステリック液晶相の状態で固定して形成した層が挙げられる。
前記光学異方性層の形成に利用可能な円盤状液晶性化合物としては、
円盤状液晶性化合物の重合については、例えば、特開平8−27284号公報に記載の方法を採用できる。
一般式(VI)
D(−L−P)n
(一般式(VI)中、Dは円盤状コアであり、Lは二価の連結基であり、Pは重合性基であり、nは4〜12の整数である。)
前記光学異方性層を形成する際に、液晶性化合物(特に円盤状液晶性化合物)を配向させるため、又は光学特性を面内で均一にするために、少なくとも一種の含フッ素化合物を層形成用の組成物中に含有させるのが好ましい。含フッ素化合物は、含フッ素界面活性剤であるのが好ましい。含フッ素化合物は、低分子化合物でも高分子化合物でもよく、例えば、低分子化合物については、特開2005−128050号公報に例示の化合物が好ましい。
なお、アルキル基の炭素数は、置換基の炭素原子を含まない。以下、他の基の炭素数についても同様である。
Lとしては、単結合、−O−、−CO−、−NR4−、−S−、−SO2−、アルキレン基、又はアリーレン基を含むことが好ましく、−CO−、−O−、−NR4−、アルキレン基、又はアリーレン基を含んでいることが特に好ましい。
Lが、アルキレン基を含む場合、アルキレン基の炭素数は、好ましくは1〜10、より好ましくは1〜8、特に好ましくは1〜6である。特に好ましいアルキレン基の具体例として、メチレン、エチレン、トリメチレン、テトラブチレン、ヘキサメチレン基等が挙げられる。
Lが、アリーレン基を含む場合、アリーレン基の炭素数は、好ましくは6〜24、より好ましくは6〜18、特に好ましくは6〜12である。特に好ましいアリーレン基の具体例として、フェニレン、ナフタレン基等が挙げられる。
Lが、アルキレン基とアリーレン基を組み合わせて得られる2価の連結基(即ちアラルキレン基)を含む場合、アラルキレン基の炭素数は、好ましくは7〜34、より好ましくは7〜26、特に好ましくは7〜16である。特に好ましいアラルキレン基の具体例として、フェニレンメチレン基、フェニレンエチレン基、メチレンフェニレン基等が挙げられる。
Lとして挙げられた基は、適当な置換基を有していてもよい。このような置換基としては先にR1〜R3における置換基として挙げた置換基と同様なものを挙げることができる。
以下にLの具体的構造を例示するが、本発明はこれらの具体例に限定されるものではない。
また、上記した通り、前記光学異方性層は、棒状液晶性化合物の少なくとも一種を含有する重合性液晶組成物を、該棒状液晶性化合物の分子をコレステリック液晶相の状態で固定して形成した層であるのも好ましい。前記棒状液晶性化合物としては、三次元架橋が可能な反射波長が紫外線領域にあるツイスト配向した重合性のカイラルネマチック(コレステリック)液晶層に用いられる液晶モノマー分子(重合性液晶分子)が挙げられる。また、前記重合性液晶組成物としては、例えば、特開平7−258638号公報や特表平10−508882号公報で開示されているような液晶性モノマーとキラル化合物の混合物がある。前記重合性液晶組成物に利用可能な重合性棒状液晶化合物の具体例には、下記化合物A〜Kが含まれる。これらの化合物は混合してもよく、例えば、下記化合物A〜化合物Jの化合物から選択される2種類以上や、下記化合物Kの範囲に含まれる化合物を2種類以上混合して使用することができる。なお、下記化合物Kにおいて、式中Xは整数を示すが、Xは2〜5の整数であることが好ましい。
前記光学異方性層を、液晶性化合物を含有する液晶組成物から形成する場合は、配向させた液晶性化合物の分子を、その配向状態を維持して固定化することが好ましい。固定化は、液晶性化合物の分子に導入した重合性基の重合反応により実施することが好ましい。重合反応には、熱重合開始剤を用いる熱重合反応と光重合開始剤を用いる光重合反応とが含まれるが、光重合反応がより好ましい。光重合開始剤としては、例えば、α−カルボニル化合物(米国特許第2367661号、同2367670号の各明細書記載に記載のもの)、アシロインエーテル(米国特許第2448828号明細書に記載のもの)、α−炭化水素置換芳香族アシロイン化合物(米国特許第2722512号明細書に記載のもの)、多核キノン化合物(米国特許第3046127号、同2951758号の各明細書に記載のもの)、トリアリールイミダゾールダイマーとp−アミノフェニルケトンとの組み合わせ(米国特許第3549367号明細書に記載のもの)、アクリジン化合物及びフェナジン化合物(特開昭60−105667号公報、米国特許第4239850号明細書に記載のもの)及びオキサジアゾール化合物(米国特許第4212970号明細書に記載のもの)を採用することができる。
光学異方性層の厚さは、0.1〜10μmであることが好ましく、0.5〜5μmであることがより好ましい。
前記光学異方性層を形成する際に、液晶性化合物の分子を配向させるために、配向膜を用いることが好ましい。さらに電場の付与、磁場の付与あるいは光照射により配向機能が生じる配向膜も知られている。配向膜に使用するポリマーの種類は、液晶性化合物の分子の配向様式(例えば、平均傾斜角)に応じて決定することができる。例えば、液晶性化合物を水平に配向させるためには配向膜の表面エネルギーを低下させないポリマー(通常の配向用ポリマー)を用いる。具体的なポリマーの種類については液晶セル又は光学補償シートについての公知の文献に記載されている事項を広く採用することができる。特に、ラビング処理の方向に対して直交する方向に液晶性化合物の分子を配向あせる場合には、例えば、特開2002−62427号公報に記載の変性ポリビニルアルコール、特開2002−98836号公報に記載のアクリル酸系コポリマー、特開2002−268068号公報に記載のポリイミド、ポリアミック酸を好ましく用いることができる。いずれの配向膜においても、光学異方性層と配向膜(結果的には光学異方性層と支持体)との密着性を向上させるには、配向膜中には重合性基を有するポリマーを含有させることが好ましい。重合性基は、側鎖に重合性基を有する繰り返し単位を導入するか、あるいは、環状基の置換基として導入することができる。界面で液晶性化合物と化学結合を形成する配向膜を用いることがより好ましく、かかる配向膜としては、例えば、特開平9−152509号公報に記載されているものが採用できる。
前記光学異方性層は、延伸又は未延伸のポリマーフィルムからなるポリマー層や、ポリマー組成物を支持体表面に適用して形成したポリマー層であってもよい。さらに前記支持体上にポリマー層を形成した後、全体として延伸処理を施して、支持体及び位相差フィルムとして必要とされる条件を満足する光学特性を発現させてもよい。前記ポリマー層の形成に用いるポリマー材料については特に制限はないが、成膜後にフィルム面の法線方向に対する面内方向の屈折率が大きくなる各種ポリマー材料が好ましい。また、ポリマー層を形成する過程で重合が進行させて、かかる場合は、該ポリマーを与え得る重合可能な低分子化合物等を用いるのが好ましい。具体的には特開平2000−190385号公報や、特開平2004−226945で開示されている材料が使用可能である。例えば、少なくとも1種類以上の芳香族環を有するポリアミド、ポリイミド、ポリアミック酸、ポリエステル、ポリエーテルケトン、ポリアリールエーテルケトン、ポリアミドイミド、ポリエステルイミドあるいはポリエステルアミド等の各種のポリマー、又はこれらのポリマーを与えうる重合可能な低分子化合物を挙げることができる。これらは単独で用いてもよいし、混合して用いてもよい。
なお、前記ポリアミック酸を用いる場合、溶液塗布、乾燥した後、熱処理によりイミド化することが好ましい。
また、本発明は、直線偏光膜(本明細書において単に「偏光膜」という場合は、「直線偏光膜」をいうものとする)と、該偏光膜の保護膜として、本発明の位相差フィルムを有する偏光板にも関する。本発明の位相差フィルムは、支持体として所定のセルロースアシレートフィルムを有するので、該セルロースアシレートフィルムの裏面(光学異方性層が形成されていない側の表面)を直接、偏光膜の表面と貼り合せることができる。例えば、長尺状のセルロースアシレートフィルムを連続的に供給し、該フィルムの表面に、重合性液晶組成物又はポリマー層形成用組成物等を塗布し、光学異方性層を形成して、長尺状の位相差フィルムを作製し、さらに長尺状の偏光膜と貼り合せることで、連続的に偏光板を安定的に作製することができる。
本発明で採用する偏光膜は、特に制限されず、公知のものを広く採用することができる。例えば、ポリビニルアルコールや部分ホルマール化ポリビニルアルコール、エチレン・酢酸ビニル共重合体部分ケン化物等の親水性ポリマーからなるフィルムに、ヨウ素及び/又はアゾ系やアントラキノン系、テトラジン系等の二色性染料などからなる二色性物質を吸着させて、延伸配向処理したもの等を用いることができる。本発明では、特開2002−131548号公報に記載の延伸方法を用いることが好ましく、特に、偏光膜の吸収軸が長手方向に対して実質的に直交する、幅方向一軸延伸型テンター延伸機を用いることが好ましい。
保護フィルムとして、本発明の位相差フィルム以外保護フィルムを用いる場合、該保護フィルムの種類は特に限定されず、セルロースアセテート、セルロースアセテートブチレート、セルロースプロピオネート等のセルロースエステル類、ポリカーボネート、ポリオレフィン、ポリスチレン、ポリエステル等を用いることができる。保護フィルムは、通常、ロール形態で供給され、長尺の偏光膜に対して、長手方向が一致するようにして連続して貼り合わされることが好ましい。ここで、保護フィルムの配向軸(遅相軸)はいずれの方向であってもよいが、操作上の簡便性から、保護フィルムの配向軸は、長手方向に平行であることが好ましい。また、保護フィルムの遅相軸(配向軸)と偏光膜の吸収軸(延伸軸)の角度も特に限定的でなく、偏光板の目的に応じて適宜設定できる。
本発明の偏光板は、偏光膜及び保護膜(少なくとも一方は本発明の位相差フィルム)を含む。本発明の偏光板の光学的性質及び耐久性(短期、長期での保存性)は、市販のスーパーハイコントラスト品(例えば、株式会社サンリッツ社製HLC2−5618等)と同等以上の性能を有することが好ましい。具体的には、可視光透過率が42.5%以上で、偏光度({(Tp−Tc)/(Tp+Tc)}1/2 ≧ 0.9995(ただし、Tpは平行透過率、Tcは直交透過率)であり、温度60℃、湿度90%RH雰囲気下に500時間及び80℃、ドライ雰囲気下に500時間放置した場合のその前後における光透過率の変化率が絶対値に基づいて3%以下、さらには1%以下、偏光度の変化率は絶対値に基づいて1%以下、さらには0.1%以下であることが好ましい。
[7]70≦Re(550)≦180かつ30≦Rth(550)≦140
[8]0.7≦Re(450)/Re(550)≦1.0
なお、第二の位相差フィルムは、その面内遅相軸が、偏光膜の吸収軸と直交する配置で積層するのが好ましい。
第二の位相差フィルムの詳細については、以下の[液晶表示装置]欄で説明する。
本発明は、本発明の位相差フィルム又は偏光板を有する液晶表示装置にも関する。本発明の液晶表示装置は、駆動電圧が印加されていない又は印加電圧未満の電圧が印加されている非駆動状態において、液晶セル中の液晶性分子が基板に対して垂直に配向する垂直配向型、例えば、VAモード、MVAモード、PVAモード、CPAモード、SUVIVALモード等の液晶セルを含んでいるのが好ましい。以下、図1及び2を用いて、本発明の液晶表示装置の一態様について説明する。図1は本発明の液晶表示装置の、図2は本発明で使用可能な偏光板の構成の一例の模式図を示したものである。図1では、電界効果型液晶素子として負の誘電異方性を有するネマチック液晶を用いてアクティブ駆動を行った例である。
[第二の位相差フィルム]
本発明の液晶表示装置、特に垂直配向型の液晶表示装置には、本発明の位相差フィルムである第一位相差フィルムとともに、第二位相差フィルムを用いるのが好ましい。ここで、第二の位相差フィルムの正面レターデーション及び厚さ方向のレターデーションが下記式[6]を満たし、及び/又は、第二の位相差フィルムの波長分散が、下記式[7]を満たすことが好ましい。
[7]70≦Re(550)≦180かつ30≦Rth(550)≦140
[8]0.7≦Re(450)/Re(550)≦1.0
本発明で用いることができる第二の位相差フィルムは、光学的に一軸でも二軸性でもよい。また、本発明で用いることができる第二の位相差フィルムは、高分子フィルムであっても、重合性液晶組成物から形成された層であってもよく、所望の諸特性が得られるものであれば特に制約はない。採用する高分子としては、均一な二軸配向が達成できるものであれば特に制限はないが、例えば、ノルボルネン系高分子、ポリカーボネート系高分子、ポリアリレート系高分子、ポリエステル系高分子、ポリサルフォン等の芳香族系高分子、トリアセチルセルロース等、溶液流延法や押出し成形方式等で製膜できるものが挙げられる。二軸性の光学異方性層は、押出し成形方式や流延製膜方式等の適宜な方式で製造したフィルムを、例えば、ロールによる縦延伸方式、テンターによる横延伸方式や二軸延伸方式などにより、延伸処理することにより形成することができる。
また、Re(450)/Re(550)で表される波長分散性は、好ましくは0.73〜0.95であり、より好ましくは0.75〜0.90である。
(1)シートを、一定温度に加熱されたロール(加熱ロール)に通して所望の温度に調整する。
(2)次いで、温度を調整したシートを、回転速度の比較的遅い第一ロールから回転速度のより速い第二ロールの順に通過させることにより延伸する。第一ロールの回転速度と第二ロールの回転速度との速度比を制御することにより延伸倍率を1〜4倍の範囲で調整することができる。なお、加熱ロール、第一ロール、及び第二ロールの間に、赤外線ヒータなどを設置して、シートの温度を一定に保持するのが好ましい。
(3)延伸されたフィルムを、冷却ロールに通して冷却する。
(4)冷却された延伸フィルムを巻き取りロールで巻き取って回収する。巻取りによるフィルム同士のブロッキングを防止する目的で、延伸フィルムと同程度の幅のマスキングフィルムを重ねて一緒に巻き取ってもよいし、延伸フィルムの少なくとも一方の端、好ましくは両方の端に、弱い粘着力の幅細のテープ等を貼り付けながら一緒に巻き取ってもよい。
上記方法の工程(1)で、加熱ロールを通過させるシートは、その温度が加熱ロールよりも高い状態、すなわち押出機等によって成形された直後の状態のものであってもよい。また、高い延伸倍率にすることができることから、加熱ロールよりも低い温度のもの、室温(例えば、25〜30℃)のものであってもよい。好ましくは、室温のものである。このように低い温度のシートは、シートを成形した後に、一旦冷却し、ロールに巻き取り回収することによって得ることができる。また、延伸速度は、好ましくは5〜1000mm/秒、より好ましくは10〜750mm/秒である。延伸速度が上記範囲にあると、延伸制御が容易となり、さらに表面精度やレターデーションの面内バラツキをより小さくすることが可能となる。
本発明において、液晶セルはVertically Alignedモード(VAモード)であるのが好ましい。VAモードの液晶セルは、外部電界が印加されていない非駆動状態において、液晶分子が液晶セルの基板に対して略垂直な方向に配向している。このような液晶セルは、例えば、対向面がラビング処理された上下電極基板の間に誘電異方性が負の液晶分子を封入してなる。
より具体的には、Δn=0.0813、及びΔε=−4.6程度の液晶分子を用い、液晶分子の配向方向を示すダイレクタ、いわゆるチルト角が約89°の液晶セルを作製することができる。この時、液晶層の厚さdは、例えば、3.5μmにすることができる。液晶層の厚さd(nm)と、屈折率異方性Δnとの積Δn・dの大きさにより白表示時の明るさが変化する。最大の明るさを得るためには、液晶層の厚さdは2〜5μm(2000〜5000nm)の範囲であるのが好ましく、Δnは、0.060〜0.085の範囲であるのが好ましい。ここで、屈折率異方性Δnは、Δn=Rth/膜厚(nm)である。
で表される。
<液晶セルの作製>
(垂直配向液晶セルの作製)
ポリビニルアルコール3質量%水溶液に、オクタデシルジメチルアンモニウムクロライド(カップリング剤)を1質量%添加した。これを、ITO電極付きのガラス基板上にスピンコートし、160℃で熱処理した後、ラビング処理を施して、垂直配向膜を形成した。ラビング処理は、2枚のガラス基板において反対方向となるように実施した。セルギャップ(d)が約5.0μmとなるように2枚のガラス基板を向かい合わせた。セルギャップに、エステル系とエタン系を主成分とする液晶性化合物(Δn:0.06)を注入し、垂直配向液晶セルを作製した。Δnとdとの積は300nmであった。
支持体1を下記記載の方法により作製した。
(ポリマー1の作製)
下記組成物を四つ口フラスコ(投入口、温度計、環流冷却管、窒素導入口、攪拌機を装着)に投入し、徐々に80℃まで昇温し、攪拌しながら5時間重合を行い、重合終了後ポリマー溶液を多量のメタノールに投入して沈殿させ、さらにメタノールで洗浄し、精製して乾燥し重量平均分子量3,000(GPCにて測定)のポリマー1(アクリレート系ポリマー)を得た。
メチルアクリレート 10質量部
2−ヒドロキシエチルアクリレート 1質量部
アゾビスイソブチロニトリル(AIBN) 1.5質量部
トルエン 30質量部
下記ドープ組成物を加圧密閉容器に投入し、70℃まで加熱しして容器内圧力を1気圧以上とし、撹拌しながらセルロースエステルを完全に溶解させた。ドープ温度を35℃まで下げて一晩静置し、このドープを安積濾紙(株)製の安積濾紙No.244を使用して濾過した後、さらに一晩静置し脱泡した。次いで日本精線(株)製のファインメットNM(絶対濾過精度100μm)、ファインポアNF(絶対濾過精度50μm、15μm、5μmの順に順次濾過精度を上げて使用)を使用して濾過圧力1.0×106Paで濾過し製膜に供した。
セルローストリアセテート(置換度2.83) 100質量部
上記合成のポリマー1 15質量部
下記UV剤(1) 0.8質量部
下記UV剤(2) 0.2質量部
メチレンクロライド 475質量部
エタノール 50質量部
また、得られたフィルムの面内レターデーションRe(630)は2nm、厚み方向のレターデーションRth(630)は−7nmで、|Re(400)−Re(700)|は3nmであり、且つRth(400)−Rth(700)は−25nmであった。
支持体2を下記記載の方法により作製した。
(ポリマー2の作製)
下記組成物を使用し、ポリマー1と同様にして、ポリマー2(アクリレート系ポリマー)を合成した。ポリマー2の重量平均分子量は2,000であった。
メチルメタクリレート 6質量部
エチルメタクリレート 5質量部
2−ヒドロキシエチルアクリレート 1質量部
アゾビスイソブチロニトリル(AIBN) 2質量部
トルエン 30質量部
ドープ組成物のポリマー1をポリマー2に置き換えた以外は、支持体1と同様にして支持体2を作製した。
作製した支持体2の膜厚は80μmであった。
また、得られたフィルムの面内レターデーションRe(630)は2nm、厚み方向のレターデーションRth(630)は−5nmで、|Re(400)−Re(700)|は2nmであり、且つRth(400)−Rth(700)は−20nmであった。
支持体膜厚を40μmに変更した以外は、支持体2と同様にして支持体3を作製した。
得られたフィルムの面内レターデーションRe(630)は2nm、厚み方向のレターデーションRth(630)は−5nmであり、|Re(400)−Re(700)|は2nmであり、且つRth(400)−Rth(700)は−20nmであった。
支持体4を下記記載の方法により作製した。
下記ドープ組成物を下記の組成物に変更した以外は、支持体1と同様にして支持体4を作製した。
(ドープ組成物)
セルローストリアセテート(置換度2.90) 100質量部
上記合成のポリマー1 10質量部
トリフェニルホスフェート 4質量部
ビフェニルジフェニルホスフェート 2質量部
上記UV剤(1) 0.8質量部
上記UV剤(2) 0.2質量部
メチレンクロライド 475質量部
エタノール 50質量部
作製した支持体4の膜厚は80μmであった。
得られたフィルムの面内レターデーションRe(630)は3nm、厚み方向のレターデーションRth(630)は−5nmで、|Re(400)−Re(700)|は2nmであり、且つRth(400)−Rth(700)は−13nmであった。
支持体5を下記記載の方法により作製した。
(支持体5の製膜)
下記ドープ組成物を下記の組成物に変更した以外は、支持体1と同様にして支持体5を作製した。
(ドープ組成物)
セルローストリアセテート(置換度2.92) 100質量部
UMM−1001(アクリル系ポリマー) 20質量部
下記UV剤(3) 1.4質量部
メチレンクロライド 475質量部
エタノール 50質量部
得られたフィルムの面内レターデーションRe(630)は2nm、厚み方向のレターデーションRth(630)は5nmで、|Re(400)−Re(700)|は1nmであり、且つRth(400)−Rth(700)は20nmであった。
支持体1の表面をケン化後、このフィルム上に下記の組成の配向膜塗布液をワイヤーバーコーターで20ml/m2塗布した。60℃の温風で60秒、さらに100℃の温風で120秒乾燥し、膜を形成した。次に、形成した膜にフィルムの遅相軸方向と平行の方向にラビング処理を施して配向膜を形成した。
配向膜塗布液の組成
―――――――――――――――――――――――――――――――――――
下記の変性ポリビニルアルコール 10質量部
水 371質量部
メタノール 119質量部
グルタルアルデヒド 0.5質量部
化合物B 0.2質量部
―――――――――――――――――――――――――――――――――――
光学異方性層塗布液
―――――――――――――――――――――――――――――――――――
下記の円盤状液晶性化合物 1.8g
エチレンオキサイド変性トリメチロールプロパントリアクリレート
(V#360、大阪有機化学(株)製) 0.2g
光重合開始剤(イルガキュアー907、チバガイギー社製) 0.06g
増感剤(カヤキュアーDETX、日本化薬(株)製) 0.02g
含フッ素ポリマー(下記の化合物A) 0.01g
メチルエチルケトン 3.9g
―――――――――――――――――――――――――――――――――――
次に、光学異方性層塗布液の塗布量を変更した以外は、第一の位相差フィルム1と同様にして、第一の位相差フィルム2〜5を作製した。得られた第一位相差フィルムの光学異方性層の厚さは、順に3.6μm、2.2μm、0.8μm、5.0μmであった。作製した位相差フィルムの光学特性は、表1に示す。
次に、支持体として市販のセルロースアセテートフィルム(フジタックTD80UF、富士写真フイルム(株)製、Re(630)=3nm、Rth(630)=45nm、Re(400)−Re(700)=−5nm、Rth(400)−Rth(700)=−13nm)を使用し、塗布膜厚を調整した以外は、第一の位相差フィルム1と同様にして、第一の位相差フィルム6を作製した。
作製した位相差フィルムの光学特性は、表1に示す。
両端に重合可能なアクリレート基を有すると共に、中央部のメソゲンとアクリレートとの間にスペーサを有する棒状液晶性化合物を75重両部、光重合開始剤(Chiba Speciality Chemicals製、イルガキュアIrg184)を1質量部、溶剤としてのメチルエチルケトン25質量部を混合し、さらにカイラル剤として両末端に重合可能なアクリレート基を有するカイラル剤を10質量部加えて光学異方性層塗布液を調製した。
次に、支持体2を使用した以外は、第一の位相差フィルム7と同様にして、第一の位相差フィルム8を作製した。作製した位相差フィルムの光学特性は、表1に示す。
次に、支持体3を使用した以外は、第一の位相差フィルム7と同様にして、第一の位相差フィルム9を作製した。作製した位相差フィルムの光学特性は、表1に示す。
次に、支持体4を使用した以外は、第一の位相差フィルム7と同様にして、第一の位相差フィルム10を作製した。作製した位相差フィルムの光学特性は、表1に示す。
次に、支持体5を使用した以外は、第一の位相差フィルム7と同様にして、第一の位相差フィルム11を作製した。作製した位相差フィルムの光学特性は、表1に示す。
次に、支持体として市販のセルロースアセテートフィルム(フジタックTD80UF、富士写真フイルム(株)製)を使用し、塗布膜厚を調整した以外は、第一の位相差フィルム7と同様にして、第一の位相差フィルム12を作製した。
2,2’−ビス(3,4−ジカルボキシフェニル)ヘキサフルオロプロパンと、2,2’−ビス(トリフルオロメチル)−4,4’−ジアミノビフェニルとから合成された重量平均分子量(Mw)120,000のポリイミドを、シクロヘキサノンに溶解して15重量%のポリイミド溶液を調製した。そして、支持体4の上に前記ポリイミド溶液を塗工した。そして、この塗工膜を100℃で10分乾燥処理した結果、厚み5μmのポリイミドフィルムが形成された。このようにして、位相差フィルム13を製作した。位相差フィルムの光学特性を表1に示す。
4,4’−ビス(3,4−ジカルボキシフェニル)−2,2−ジフェニルプロパン二無水物と、2,2’−ジクロロ−4,4’−ジアミノビフェニルとから合成された重量平均分子量(Mw)3万のポリイミドを、シクロペンタノンに溶解して20重量%のポリイミド溶液を調製した。そして、支持体4の上に前記ポリイミド溶液を塗工した。そして、この塗工膜を130℃で5分熱処理した結果、厚み8μmの透明で平滑なポリイミドフィルムが形成された。このようにして、位相差フィルム14を製作した。位相差フィルムの光学特性を表1に示す。
位相差フィルム13に使用したポリイミドを支持体4の上に塗工した、この塗工膜を100℃で10分乾燥処理した。次いで、前記ポリイミド塗工膜と支持体の積層体を、延伸前の積層体の長さに対して10%の二軸延伸を160℃で行い、支持体上に厚み4μmのポリイミド二軸延伸フィルムが形成された。このようにして、位相差フィルム135を製作した。位相差フィルムの光学特性を表1に示す。
次に、支持体として市販のセルロースアセテートフィルム(フジタックTD80UF、富士写真フイルム(株)製)を使用し、塗布膜厚を調整した以外は、第一の位相差フィルム13と同様にして、第一の位相差フィルム16を作製した。
上記の第一の位相差フィルム1〜12とフジタックTD80UFを、偏光膜の両面にポリビニルアルコール系接着剤を用いてロールtoロールで貼り付け、一体型偏光板を作製した。各フィルムの積層角度は表示装置を上から見た時の左右の方向を基準(0°)にすると、図2に示すように、偏光膜吸収軸104(図1では15)の軸角度は90°、保護フィルム遅相軸102及び106の角度は90°に設定した。作製した下側偏光板を、光学異方性層(図1では10)が上側液晶セル基板(図1では8)に接するように、液晶表示装置に組み込んだ。
保護フィルム(図2では105)として、市販のセルロースアセテートフィルム(フジタックTD80UF、富士写真フイルム(株)製、Re値が3nm、Rth値が50nm)を用いた。また、上側偏光板(図1では1)と上側液晶セル基板(図1では5)との間に、延伸フィルムからなる一軸の位相差フィルムとしてポリカーボネートフィルム(商品名:ピュアエースWR(帝人(株))1枚配置した。このとき、位相差フィルムの面内の遅相軸が上側偏光板の透過軸と一致するように構成した。
ポリカーボネートフィルムの光学特性は、Reが155nm、Rthが78nm、Re(450)/Re(550)=0.8であった。即ち、第二の位相差フィルムに要求される光学特性を満足していた。
以上のようにして作製した液晶表示装置において、装置正面からの方位角方向45度、極角方向60度における黒表示時の光漏れ及び正面からの色味変化を目視により以下の基準で評価した。
A:光漏れを感じない
B:微かに光漏れする
C:弱く光漏れする
D:強く光漏れする
A:着色を感じない
B:微かに着色する
C:弱く着色する
D:強く着色する
トムソン打抜機の18cm×16cmのゴム製マット上に、フィルムサンプルを5枚重ねて置いて打ち抜き、4隅から内側に入る最も長いクラックの長さを測定し、打ち抜き加工適性で脆性を評価した。2mm以下を○、2〜3mm以下を△、3mmを越えるものを×で示す。
一方、フィルム4〜6は、上記式[3]及び/又は上記式[4]を満足していないため、これを第一の位相差フィルムとして用いた比較例では、斜め方向において、黒表示時の光漏れ及び色味変化が観察された。また、フィルム12も、上記式[4]を満足していないため、これを第一の位相差フィルムとして用いた比較例では、斜め方向において、黒表示時の光漏れ及び色味変化が観察された。
2 上側偏光板吸収軸の方向
3 第二の位相差フィルム
4 第二の位相差フィルム遅相軸の方向
5 液晶セル上電極基板
6 上基板配向制御方向
7 液晶分子
8 液晶セル下電極基板
9 下基板配向制御方向
10 第一の位相差フィルム
14 下側偏光板
15 下側偏光板吸収軸の方向
101 偏光板保護フィルム
102 偏光板保護フィルム遅相軸の方向
103 偏光板偏光膜
104 偏光膜吸収軸の方向
105 偏光板保護フィルム
106 偏光板保護フィルム遅相軸の方向
Claims (21)
- 支持体及び少なくとも一層の光学異方性層を有する位相差フィルムであって、
前記支持体が、少なくとも一種のアクリル系ポリマーを含むセルロースアシレートフィルムからなり、正面レターデーションReと厚さ方向のレターデーションRthが下記式[1]を満たし、且つその波長分散性が下記式[2]を満たし;及び
前記位相差フィルムの正面レターデーションReと厚さ方向のレターデーションRthが下記式[3]を満たし、且つその波長分散性が下記式[4]を満たす位相差フィルム:
[1]0≦Re(630)≦10かつ|Rth(630)|≦25
[2]|Re(400)−Re(700)|≦10かつ−35≦Rth(400)−Rth(700)≦60
[3]0≦Re(550)≦10かつ100≦Rth(550)≦300
[4]1.04≦Rth(450)/Rth(550)≦1.30
式中、Re(λ)は、Re(λ)=(nx−ny)×dで表され、波長λnmにおける正面レターデーション値(単位:nm)を表し、Rth(λ)はRth(λ)={(nx+ny)/2−nz}×dで表され、波長λnmにおける膜厚方向のレターデーション値(単位:nm)を表し、nxはフィルム面内の遅相軸方向の屈折率であり、nyはフィルム面内の進相軸方向の屈折率であり、nzはフィルムの厚み方向の屈折率であり、dはフィルムの厚さ(nm)である。 - 前記支持体の波長分散性が、下記式[5]を満たす、請求項1に記載の位相差フィルム:
[5]|Re(400)−Re(700)|≦10かつ0≦Rth(400)−Rth(700)≦60 。 - 波長分散性が、下記式[6]を満たす、請求項1又は2に記載の位相差フィルム:
[6]1.06≦Rth(450)/Rth(550)≦1.30 。 - 前記光学異方性層の少なくとも一層が、円盤状液晶性化合物の少なくとも一種を含有する重合性液晶組成物を、該円盤状液晶化合物の分子をホメオトロピック配向させ、ネマチック液晶相の状態で重合により固定して形成された層である請求項1〜3のいずれか1項に記載の位相差フィルム。
- 前記光学異方性層の少なくとも一層が、棒状液晶性化合物の少なくとも一種を含有する重合性液晶組成物を、該棒状液晶性化合物の分子をコレステリック液晶相の状態で固定して形成した層である請求項1〜3のいずれか1項に記載の位相差フィルム。
- 前記光学異方性層の少なくとも一層が、ポリマー層である請求項1〜3のいずれか1項に記載の位相差フィルム。
- 前記ポリマー層が、ポリアミド、ポリイミド、ポリエステル、ポリエーテルケトン、ポリアミドイミド及びポリエステルイミドからなる群から選ばれる少なくとも一種類のポリマーを含む請求項6に記載の位相差フィルム。
- 前記光学異方性層の少なくとも一層が、含フッ素化合物を含む請求項1〜7のいずれか1項に記載の位相差フィルム。
- 前記支持体が、アシル置換度2.70〜3.00のセルロースアシレートを含有するセルロースアシレートフィルムからなる請求項1〜8のいずれか1項に記載の位相差フィルム。
- 前記アクリル系ポリマーの重量平均分子量が、500以上10,000未満である請求項1〜9のいずれか1項に記載の位相差フィルム。
- 前記アクリル系ポリマーが、水酸基を主鎖及び/又は側鎖に有するアクリル系ポリマーである請求項1〜10のいずれか1項に記載の位相差フィルム。
- 前記支持体が、可塑剤を含むセルロースアシレートフィルムからなる請求項1〜11のいずれか1項に記載の位相差フィルム。
- 前記支持体の膜厚が、10〜60μmである請求項1〜12のいずれか1項に記載の位相差フィルム。
- 偏光膜と、該偏光膜の両面に設けられた保護フィルムとを有し、該保護フィルムの少なくとも一方が請求項1〜13のいずれか1項に記載の位相差フィルムである偏光板。
- さらに、第二の位相差フィルムを有し、前記第二の位相差フィルムの正面レターデーション及び厚さ方向のレターデーションが下記式[7]を満たし、且つ第二の位相差フィルムの波長分散が下記式[8]を満たす請求項14に記載の偏光板:
[7]70≦Re(550)≦180かつ30≦Rth(550)≦140
[8]0.7≦Re(450)/Re(550)≦1.0 。 - 請求項1〜13のいずれか1項に記載の位相差フィルム及び/又は請求項14もしくは15に記載の偏光板を含む液晶表示装置。
- 互いの吸収軸が直交している二枚の偏光板、及び
該二枚の偏光板の間に、一対の基板と、該一対の基板間に挟持された、液晶分子が外部電界が印加されていない非駆動状態において前記一対の基板に対して略垂直な方向に配向する液晶層とを有する液晶セルを、有する液晶表示装置であって、
請求項1〜13のいずれか1項に記載の位相差フィルムをさらに含む、又は前記偏光板が請求項14もしくは15に記載の偏光板である、液晶表示装置。 - 前記液晶表示装置が、さらに第二の位相差フィルムを有し、該第二の位相差フィルムは高分子延伸フィルムからなり、正面レターデーション及び厚さ方向のレターデーションが下記式[7]を満たす、請求項16又は17に記載の液晶表示装置:
[7]70≦Re(550)≦180かつ30≦Rth(550)≦140 。 - 前記液晶表示装置が、さらに第二の位相差フィルムを有し、該第二の位相差フィルムの波長分散が、下記式[8]を満たす、請求項16〜18のいずれか1項に記載の液晶表示装置:
[8]0.7≦Re(450)/Re(550)≦1.0 。 - 前記液晶表示装置が、さらに第二の位相差フィルムを有し、該第二の位相差フィルムが、セルロースアシレートフィルム、ノルボルネン系フィルム、ポリカーボネート系フィルム、ポリアリレート系フィルム、ポリエステル系フィルム及びポリサルフォン系フィルムのいずれかからなる、請求項16〜19のいずれか1項に記載の液晶表示装置。
- 前記液晶表示装置が、さらに第二の位相差フィルムを有し、該第二の位相差フィルムが、その面内遅相軸を、前記二枚の偏光板のいずれか一方の吸収軸と直交させて配置されている、請求項16〜20のいずれか1項に記載の液晶表示装置。