JP2007270090A - 潤滑油組成物 - Google Patents
潤滑油組成物 Download PDFInfo
- Publication number
- JP2007270090A JP2007270090A JP2006100963A JP2006100963A JP2007270090A JP 2007270090 A JP2007270090 A JP 2007270090A JP 2006100963 A JP2006100963 A JP 2006100963A JP 2006100963 A JP2006100963 A JP 2006100963A JP 2007270090 A JP2007270090 A JP 2007270090A
- Authority
- JP
- Japan
- Prior art keywords
- isomers
- group
- lubricating oil
- alkyl group
- oil composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ポリαオレフィンを基油として含有し、更に、酸化防止剤としてアルキル基を有する芳香族炭化水素と、ジフェニルアミン類と、アルキル化フェニルαナフチルアミンと、フォスファイトとを含有する潤滑油組成物であって、
前記アルキルを有する芳香族炭化水素の含有量が、ポリαオレフィンとアルキル基を有する芳香族化合物との全容量に対して1〜10体積%であり、且つ、前記ジフェニルアミン類(x)と、アルキル化フェニルαナフチルアミン(y)と、フォスファイト(z)とを、質量比(x:y:z)1:1.5〜2.5:0.3〜0.6で含有することを特徴とする潤滑油組成物である。
【選択図】なし
Description
本発明の潤滑油組成物は基油としてポリαオレフィンを用いる。前記ポリαオレフィンは、合成基油の一種であり、両末端の片側に二重結合を有する炭素数3〜18の直鎖状αオレフィンを重合させ,水素添加処理して得られる無色透明の液体である。ポリαオレフィンは、エステル結合を持たないことから、分子内に酸素原子がなく、極性のない炭素と水素とから構成される化合物である。
本発明の潤滑油組成物は、酸化防止剤は、少なくとも下記の4種の酸化防止剤を有するものである。本発明の潤滑油組成物は、本発明の効果に影響を与えない限り、他の酸化防止剤を含むものであってもよい。
本発明の潤滑油組成物に用いられるアルキル基を有する芳香族炭化水素は、少なくとも1つのアルキル基を有する芳香族炭化水素を意味する。ここで、「芳香族炭化水素」とは、実質的に水素原子と炭素原子とから構成され、ヘテロ原子を含まない化合物を意味する。本発明における芳香族炭化水素を含有すると、ポリαオレフィンに特有のゴムの収縮や硬化を防止することもできる。
これらの中でも炭素数8〜30のアルキル基が好ましく、さらに好ましくは炭素数12〜20のアルキル基である。これらのアルキル基は直鎖でも分岐鎖もよい。
本発明の潤滑油組成物に酸化防止剤として使用されるジフェニルアミン類は、2つのフェニル基を有するアミン化合物であれば特に限定されないが、熱酸化安定性の観点から、下記一般式(2)で表されるアルキル化ジフェニルアミンが好ましい。
本発明の潤滑油組成物に使用されるアルキル化フェニルαナフチルアミンとしては、公知のものを適宜選定して用いることができるが、熱酸化安定性の観点から、下記一般式(3)で表されるアルキル化フェニルαナフチルアミンが特に好ましい。
本発明の潤滑油組成物に使用されるフォスファイトとは、亜リン酸エステルを意味する。本発明におけるフォスファイトとしては、公知のものを特に限定なく用いることができる、例えば、トリス(2−エチルヘキシル−3−メルカプトプロピオネート)フォスファイト、トリフェニルフォスファイト、トリオクタデシルフォスファイト、トリステアリルフォスファイト、トリラウリルトリチオフォスファイト、トリイソオクチルフォスファイト、トリス(ノニルフェニル)フォスファイト、トリクレジルフォスファイト、ジフェニルイソデシルフォスファイトなどの亜燐酸トリアルキルエステル類や、亜燐酸ジアルキルエステル類、亜燐酸モノアルキルエステル類などが挙げられる。このなかでも本発明におけるフォスファイトとしては、トリス(アルキルフェニル)フォスファイトが好ましい。前記トリス(アルキルフェニル)フォスファイトの代表例としては、下記一般式(4)で表される化合物が挙げられる。
本発明の潤滑油組成物において、前記ジフェニルアミン類(x)と、アルキル化フェニルαナフチルアミン(y)と、フォスファイト(z)との質量比(配合比率)(x:y:z)は、1:1.5〜2.5:0.3〜0.6である。ジフェニルアミン類の添加量に対して、アルキル化フェニルαナフチルアミンの添加量が1.5倍未満であると熱酸化防止効果が小さくなり、また、2.5倍を超えても添加量に見合った効果は得られない。更に、ジフェニルアミン類の添加量に対して、フォスファイトの添加量が0.3倍未満であると酸化防止効果が小さく、また、0.6倍を超えても添加量に見合った効果は得られない。以上のように、本発明においては、前記3種の酸化防止剤の質量比(配合比率)が1:1.5〜2.5:0.3〜0.6の範囲内にある場合に効果的な熱酸化防止性が発揮される。
本発明の潤滑油組成物には、さらに各種性能を高める目的で公知の潤滑油に用いられる添加剤を、適宜選定して、単独で、又は2種類以上を組み合わせて使用することができる。前記添加剤としては、例えば、ベンゾトリアゾール系金属不活性剤、エステル系のさび止め剤、スチレンーブタジエン水添加重合体、エチレンプロピレン重合体、ポリイソブチレン、ポリメタクリレートなどの流動点降下剤、ポリアクリレート、ポリジメチルシロキサンなどの消泡剤、エチレンオキシドープロピレンオキシド供重合体などの抗乳化剤などが挙げられる。
上記構成を有する本発明の潤滑油組成物は、高い熱酸化安定性を発揮すると共に、スラッジの低減、ゴムに対する影響の低減、水分混入時の酸化安定性等を達成できるものである。特に、本発明の潤滑油組成物は、高温条件下であっても高い熱酸化防止効果を奏することができることから、例えば、80℃以上の高温部分を有する機械の使用において非常に有効である。また、本発明の潤滑油組成物は寿命が長いことから、本発明の潤滑油組成物の使用用途としては、例えば、スクリューコンプレッサー油、タービン油、油圧作動油等、循環使用される潤滑油が挙げられる。但し、本発明の潤滑油組成物の用途は、これらに限定されるものではない。
(1)RBOT(分)
本実施例においてRBOT(Rotating Bomb Oxidation Test)は、全ての条件についてJIS−K2514(1996)に制定されている回転ボンベ式酸化安定度試験に従っておこなった。係る結果によって得られた時間が長いほど、熱酸化安定性及び水混入時の酸化安定性が優れていることを示す。
本実施例において修正ISOT(Indiana Stirring Oxidation Test)は、JIS−K2514(1996)に制定されている内燃機関用潤滑油酸化安定度試験法に、さらに強制的に10L/hの空気を、試験油に吹き込んで酸化劣化を促進して行った。修正ISOTは、1日ごとに動粘度、酸価、スラッジを測定し、動粘度が50%増加、酸価が2以上、又は、スラッジが10mg/100ml以上のいずれか1項目を越えるまでの日数で評価した。この日数が長い程、熱・酸化安定性、スラッジ低減効果が優れていることを示す。
本実施例においてゴム膨潤試験は下記の測定条件の下、JIS−K6251(1999)に準拠して行った。
試験片材質:NBR(NOK社製、A727)
試験条件:120℃×168時間
評価:質量変化率(%)体積変化率(%)、かたさ変化
尚、上記評価項目の内、特に体積変化率が0〜5%の範囲にあるとシール性が良好であることを示す。また、体積変化率がマイナス値であると、シール性が劣るため好ましくない。
本実施例において抗乳化性試験は、全ての条件についてJISK2520に従っておこなった。尚、下記表1の評価結果の「40−40−0(10min)」は、試験10分後に油層−水層−乳化層の体積比が「40−40−0」であること、即ち、乳化層が存在しないことを示す。
実施例及び比較例において、それぞれ下記表1に示す化合物を混合し各潤滑油組成物を調製し、得られた組成物について上記(1)〜(4)の測定を行った。各実施例及び比較例で用いた基油及び添加剤を下記に示す。
(平均分子量:460、動粘度(40℃):32mm2/s)
B:鉱油
(動粘度(40℃):32mm2/s)
※前記鉱油は、水素化精製基油である。
C:炭素数16のアルキル基を分子内に2つ有するアルキルナフタレン
(アルキル基を有する芳香族炭化水素)
D:ジフェニルアミン類
前記一般式(3)におけるR5,R6が、水素原子、−C4H9、−C8H17のいずれかの組み合わせの混合物
E:アルキル化フェニルαナフチルアミン
前記一般式(4)におけるR7がC8H17の化合物
F:トリス(2,4−t−ブチルフェニル)フォスファイト
G:その他添加剤(さび止め剤、腐食防止剤、消泡剤等)
一方、各比較例の潤滑油組成物は、いずれも抗乳化試験では実施例で同等性能を有し潤滑油としての基本性能は満たしているが、RBOT値、修正ISOT値が各実施例より劣っている。さらに、比較例2の潤滑油組成物は、アルキルナフタレンを含有しない場合、ゴム膨潤性が悪いことがわかる。
Claims (2)
- ポリαオレフィンを基油として含有し、更に、酸化防止剤としてアルキル基を有する芳香族炭化水素と、ジフェニルアミン類と、アルキル化フェニルαナフチルアミンと、フォスファイトとを含有する潤滑油組成物であって、
前記アルキルを有する芳香族炭化水素の含有量が、ポリαオレフィンとアルキル基を有する芳香族化合物との全容量に対して1〜10体積%であり、且つ、前記ジフェニルアミン類(x)と、アルキル化フェニルαナフチルアミン(y)と、フォスファイト(z)とを、質量比(x:y:z)1:1.5〜2.5:0.3〜0.6で含有することを特徴とする潤滑油組成物。 - 前記アルキル基を有する芳香族炭化水素が、アルキルナフタレンであることを特徴とする請求項1に記載の潤滑油組成物。