JP2007224451A - 樹脂補強織物用ポリエステル繊維 - Google Patents
樹脂補強織物用ポリエステル繊維 Download PDFInfo
- Publication number
- JP2007224451A JP2007224451A JP2006046786A JP2006046786A JP2007224451A JP 2007224451 A JP2007224451 A JP 2007224451A JP 2006046786 A JP2006046786 A JP 2006046786A JP 2006046786 A JP2006046786 A JP 2006046786A JP 2007224451 A JP2007224451 A JP 2007224451A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- fiber
- dtex
- polyester fiber
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】ポリエチレンテレフタレートからなる繊維であって、切断強度が7.0cN/dtex以上、切断伸度が13%以上、0.10cN/dtex荷重下での230℃における熱収縮率が0.1〜5.0%であり、かつ該繊維表面にエポキシ化合物が繊維重量を基準として0.05〜1.0重量%付着していることを特徴とする。さらには、200〜230℃における熱収縮応力のピーク値が0.15cN/dtex以下であることや、単糸繊度が4.5〜6.0dtex、単糸数が190〜250filであることが好ましい。
【選択図】なし
Description
本発明の樹脂補強織物用ポリエステル繊維は、主としてポリエチレンテレフタレートから構成されるが、該ポリエステルには本発明の目的を阻害しない範囲内、例えば全酸成分を基準として10モル%以下、好ましくは5モル%以下の範囲内で第三成分が共重合されたものであってもよい。好ましく用いられる共重合成分としては、例えば、酸成分としてイソフタル酸、ナフタレンジカルボン酸、ジフェニルジカルボン酸、ジフェノキシエタンジカルボン酸、β−ヒドロキシエトキシ安息香酸、p−オキシ安息香酸、アジピン酸、セバシン酸、1,4−シクロヘキサンジカルボン酸等を挙げることができ、また、ジオール成分としてエチレングリコール、プロピレングリコール、テトラメチレングリコール、シクロヘキサン−1,4−ジメタノール、ネオペンチルグリコール、ビスフェノールA、ビスフェノールS等を挙げることができる。さらに、上記ポリエステル中には少量の他の重合体や酸化防止剤、制電剤、顔料、蛍光増白剤その他の添加剤が含有されていてもよい。
ポリマー又は繊維をフェノール/テトラクロロエタン=1/1(容量比)混合溶媒に溶解し、30℃において測定した。
JIS−L1013に準拠して測定した。
繊維を50cm以上の長さに切り取り、一端を固定して他端に0.10cN/dtexとなるように重りを吊り下げる。固定端から50cmの部分に印をつけ、230℃に維持された恒温槽の中で試料を30分間収縮させ、収縮後の長さから収縮率を算出する。
得られた織物をピンテンターを用いてセット荷重9kg、200℃で90秒熱セットした。この熱セット反にイソシアネート系接着剤(大日本インキ(株)製)を塗布(厚み約0.05mm)し、24時間風乾した。このセット反にウレタン樹脂シートを貼り合わせた後、3kg/cm2の荷重下190℃3分間の熱処理を行った。24時間放置後、塩ビと織物間の180°剥離力を引張試験機で測定した。接着力はN/2.5cmの値で示した。
撚糸工程における糸切れ回数が1回/100km未満、または製織時の糸切れが1回/100km未満、または除去困難な粘着性のスカムが発生した、のうちいずれにもあてはまらない場合を○、いずれかの不具合が見られた場合には×とした。
目視で均整性、変色、毛羽、スカム汚れを確認し何れも問題ない場合○、1つでも問題あれば×とした。
固有粘度0.64のポリエチレンテレフタレートチップを65Paの真空度下、100℃で2時間予備結晶化した後、同真空下230℃で固相重合を行い、重合時間を調整することにより表1に示す固有粘度のポリエチレンテレフタレートチップを得た。このチップを溶融押し出し機で溶融し、延伸後の繊度が1100dtexとなるように吐出量を調整しながら孔径0.4mm、孔数192個の紡糸口金より紡糸した。紡出糸を300℃に加熱した口金下の加熱雰囲気中を通過させ、25℃の冷却風で冷却固化し、オイリングローラーで紡糸油剤を付着量が0.30%となるように付着せしめた後、それぞれの紡糸速度で引取った。
繊維の製造条件と物性、及び樹脂補強織物の性能を表1に示す。
実施例1において、紡糸油剤の付着率を0.45%になるように調整し、延伸工程にてエポキシを付着させなかった以外は実施例1と同様にしてポリエステル繊維及び樹脂補強織物を得た。得られた繊維の製造条件と物性、及び樹脂補強織物の性能を表1に併せて示す。
固有粘度0.64のポリエチレンテレフタレートチップを65Paの真空度下、100℃で2時間予備結晶化した後、同真空下240℃で固相重合を行い、固有粘度1.01のポリエチレンテレフタレートチップを得た。このチップを溶融押し出し機で溶融し、延伸後の繊度が1100dtexとなるように吐出量を調整しながら孔径1.0mm、孔数249個の紡糸口金より紡糸した。紡出糸を250℃に加熱した口金下の加熱雰囲気中を通過させ、25℃の冷却風で冷却固化し、オイリングローラーで紡糸油剤を付着量が0.30%となるように付着せしめた後、紡糸速度2100m/分で引取った。
比較例2において、紡糸油剤の付着率を0.45%になるように調整し、延伸工程にてエポキシを付着させなかった以外は比較例2と同様にしてポリエステル繊維及び樹脂補強織物を得た。得られた繊維の製造条件と物性、及び樹脂補強織物の性能を表1に併せて示す。
Claims (4)
- ポリエチレンテレフタレートからなる繊維であって、切断強度が7.0cN/dtex以上、切断伸度が13%以上、0.10cN/dtex荷重下での230℃における熱収縮率が0.1〜5.0%であり、かつ該繊維表面にエポキシ化合物が繊維重量を基準として0.05〜1.0重量%付着していることを特徴とする樹脂補強織物用ポリエステル繊維。
- 200〜230℃における熱収縮応力のピーク値が0.15cN/dtex以下である請求項1記載の樹脂補強織物用ポリエステル繊維。
- 単糸繊度が4.5〜6.0dtex、単糸数が190〜250filである請求項1または2に記載の樹脂補強織物用ポリエステル繊維。
- 請求項1〜3のいずれか1項記載の樹脂補強織物用ポリエステル繊維を用いたベルト用基布。