JP2007019000A - 透明導電膜形成用組成物、透明導電膜及びディスプレイ - Google Patents
透明導電膜形成用組成物、透明導電膜及びディスプレイ Download PDFInfo
- Publication number
- JP2007019000A JP2007019000A JP2006083606A JP2006083606A JP2007019000A JP 2007019000 A JP2007019000 A JP 2007019000A JP 2006083606 A JP2006083606 A JP 2006083606A JP 2006083606 A JP2006083606 A JP 2006083606A JP 2007019000 A JP2007019000 A JP 2007019000A
- Authority
- JP
- Japan
- Prior art keywords
- conductive film
- transparent conductive
- binder component
- meth
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【課題】優れた帯電防止効果を有し、膜の可視光透過率が非常に高く且つ透過画像の色相が自然であり、平滑性、耐擦傷性にも優れた透明導電膜を形成し得る組成物、そのような透明導電膜並びにそのような透明導電膜を表示面に有するディスプレイを提供すること。
【解決手段】バインダー成分及び該バインダー成分中に分散した導電性粉体からなり、該バインダー成分は酸性官能基を有するアクリレート化合物又はメタクリレート化合物を含む活性エネルギー線硬化性バインダー成分であり、該導電性粉体は水酸化錫粉体又はドーパントとしてP、Al、In、Zn及びSbの少なくとも一種を含む水酸化錫粉体である透明導電膜形成用組成物、そのような組成物から得られる透明導電膜、並びにそのような透明導電膜を表示面に有するディスプレイ。
【選択図】図1
Description
一般式(I)
CH2=C(R1)−C(O)−O−R2−P(O)(OR3)−OH
一般式(II)
CH2=C(R1)−C(O)−O−R2−P(O)(OH)−O−R2−C(O)−C(R1)=CH2
(上記式中、R1は水素原子又はメチル基を示し、R2はアルキレンオキサイド基又はポリアルキレンオキサイド基を示し、R3は水素原子、フェニル基、アルキル基又はアルキル フェニル基を示す。)
酸性官能基を有するメタアクリレートとしてモノ(2−メタクリロイルポリエチレンオキサイド)アシッドフォスフェート(ホスマーPE、ユニケミカル株式会社製商品名)を使用した。この酸性官能基を有するメタアクリレート0.1部、トリメチロールプロパントリアクリレート19.9部、及びポリエステルアクリレート10部からなるバインダー成分を、水酸化錫粉体70部、溶剤としてのイソブタノール150部及びガラスビーズ250部とともに容器に入れ、ペイントシェカーで、粒ゲージにより分散状態を確認しながら、5時間練合した。練合後、光開始剤として2−ベンジル−2−ジメチルアミノ−1−(4−モルホリノフェニル)−ブタノン−1を3部加えて、完全に溶解させた後、ガラスビーズを取り除いて粘稠な液状物を得た。その後、ロールコーターを用いてその粘稠な液状物を膜厚75μmのPETフィルム(東洋紡A4300、光透過率91%、ヘイズ0.7%)上に塗布し、有機溶媒を蒸発させた後、高圧水銀灯にて500mJ/cm2の紫外 線を照射して厚み5μmの透明硬化被膜を作製した。
実施例1で使用したのと同じ酸性官能基を有するメタアクリレート7.5部及びトリメチロールプロパントリアクリレート7.5部からなるバインダー成分を、水酸化錫粉体85部、溶剤としてのジアセトンアルコール150部及びガラスビーズ250部とともに容器に入れ、ペイントシェカーで、粒ゲージにより分散状態を確認しながら、5時間練合した。練合後、実施例1と同様にして、厚み5μmの透明硬化被膜を作製した。
酸性官能基を有するメタアクリレートとして、エチレンオキサイド変性コハク酸メタクリレート(ライトエステルHO−MS、共栄社化学株式会社製商品名)を使用した。この酸性官能基を有するメタアクリレート14部、トリメチロールプロパントリアクリレート6部及びポリエステルアクリレート10部からなるバインダー成分を、水酸化錫粉体70部、溶剤としての酢酸ブチル150部及びガラスビーズ250部とともに容器に入れ、ペイントシェカーで、粒ゲージにより分散状態を確認しながら、5時間練合した。練合後、実施例1と同様にして、厚み5μmの透明硬化被膜を作製した。
実施例1で使用したのと同じ酸性官能基を有するメタアクリレート7.5部、及びトリメチロールプロパントリアクリレート7.5部からなるバインダー成分を、ドーパントとしてリンを含む水酸化錫粉体85部、溶剤としてのエチルアルコール100部、アセトン50部及びガラスビーズ250部とともに容器に入れ、ペイントシェカーで、粒ゲージにより分散状態を確認しながら、5時間練合した。練合後、実施例1と同様にして、厚み5μmの透明硬化被膜を作製した。
実施例1で使用したのと同じ酸性官能基を有するメタアクリレート7.5部及びトリメチロールプロパントリアクリレート52.5部からなるバインダー成分を、水酸化錫粉体40部、溶剤としてのイソプロピルアルコール120部及びメチルエチルケトン30部を用いた以外は実施例1と同様にして厚み5μmの透明硬化被膜を作製した。
実施例3で使用したのと同じ酸性官能基を有するメタアクリレート14部、ジペンタエリスリトールヘキサアクリレート76部からなるバインダー成分を、水酸化錫粉体10部、溶剤としての酢酸ブチル150部を用いた以外は実施例1と同様にして厚み5μmの透明硬化被膜を作製した。
バインダー成分としてのアクリルレジン溶液(ダイヤナールLR−90、固形分30%、三菱レイヨン株式会社製)100部を、ITO粉体70部、溶剤としてのシクロヘキサノン150部及びガラスビーズ250部とともに容器に入れ、ペイントシェカーで、粒ゲージにより分散状態を確認しながら、5時間練合した。練合後、ガラスビーズを取り除き、粘稠な液状物を得た。その後、ロールコーターを用いてその粘稠な液状物を膜厚75μmのPETフィルム(東洋紡A4300、光透過率91%、ヘイズ0.7%)上に塗布し、有機溶媒を蒸発させた後、60℃で10分間乾燥させて厚み5μmの透明硬化被膜を作製した。
水酸化錫粉体70部の代わりに酸化錫粉体70部を用いた以外は実施例1と同様にして厚み5μmの透明硬化被膜を作製した。
水酸化錫粉体10部の代わりに酸化錫粉体10部を用いた以外は実施例6と同様にして厚み5μmの透明硬化被膜を作製した。
透明硬化被膜面を目視で評価した際に、
○:スジ・ムラなどが確認できない極めて平滑な面
△:スジ・ムラなど凹凸面が若干確認できる面
×:スジ・ムラなど凹凸面が確認できる面
透明硬化被膜面をスチールウール(#0000)1000g荷重にて10往復擦傷した時に、
○:キズなし
△:キズ多少有り
×:キズあり
Claims (10)
- バインダー成分及び該バインダー成分中に分散した導電性粉体からなり、該バインダー成分は酸性官能基を有するアクリレート化合物又はメタクリレート化合物を含む活性エネルギー線硬化性バインダー成分であり、該導電性粉体は水酸化錫粉体であることを特徴とする透明導電膜形成用組成物。
- バインダー成分及び該バインダー成分中に分散した導電性粉体からなり、該バインダー成分は酸性官能基を有するアクリレート化合物又はメタクリレート化合物を含む活性エネルギー線硬化性バインダー成分及びその他の活性エネルギー線硬化性バインダー成分からなり、該導電性粉体は水酸化錫粉体であることを特徴とする透明導電膜形成用組成物。
- バインダー成分及び該バインダー成分中に分散した導電性粉体からなり、該バインダー成分は酸性官能基を有するアクリレート化合物又はメタクリレート化合物を含む活性エネルギー線硬化性バインダー成分であり、該導電性粉体はドーパントとしてP、Al、In、Zn及びSbの少なくとも一種を含む水酸化錫粉体であることを特徴とする透明導電膜形成用組成物。
- バインダー成分及び該バインダー成分中に分散した導電性粉体からなり、該バインダー成分は酸性官能基を有するアクリレート化合物又はメタクリレート化合物を含む活性エネルギー線硬化性バインダー成分及びその他の活性エネルギー線硬化性バインダー成分からなり、該導電性粉体はドーパントとしてP、Al、In、Zn及びSbの少なくとも一種を含む水酸化錫粉体であることを特徴とする透明導電膜形成用組成物。
- P、Al、In、Zn及びSbの少なくとも一種のドーパントの量が、(ドーパント+Sn)に対して0.1〜20at%であることを特徴とする請求項3又は4記載の透明導電膜形成用組成物。
- 活性エネルギー線硬化性バインダー成分の酸価が0.1〜200mgKOH/gであることを特徴とする請求項1〜5の何れかに記載の透明導電膜形成用組成物。
- 導電性粉体/バインダー成分の質量比が5/95〜95/5の範囲内であることを特徴とする請求項1〜6の何れかに記載の透明導電膜形成用組成物。
- 請求項1〜7の何れかに記載の透明導電膜形成用組成物を塗布又は印刷し、活性エネルギー線を照射し、硬化させて得られるものであることを特徴とする透明導電膜。
- 表面抵抗値が107〜1011Ω/□であり、光透過率が85%以上であり、ヘイズが2 %以下である請求項8記載の透明導電膜。
- 表示面に請求項8又は9記載の透明導電膜を有することを特徴とするディスプレイ。