JP2006283071A - 加工性の良好な合金化溶融亜鉛メッキ高強度鋼板の製造方法 - Google Patents
加工性の良好な合金化溶融亜鉛メッキ高強度鋼板の製造方法 Download PDFInfo
- Publication number
- JP2006283071A JP2006283071A JP2005101738A JP2005101738A JP2006283071A JP 2006283071 A JP2006283071 A JP 2006283071A JP 2005101738 A JP2005101738 A JP 2005101738A JP 2005101738 A JP2005101738 A JP 2005101738A JP 2006283071 A JP2006283071 A JP 2006283071A
- Authority
- JP
- Japan
- Prior art keywords
- steel sheet
- rolling
- mass
- less
- workability
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 質量%で、C:0.05〜0.20%、Mn:1.0〜3.0%、Si:0.3〜1.8%、P:0.05%以下、S:0.03%以下、sol.Al:0.005〜1.0%、N:0.01%以下を含み、残部はFeおよび不可避的不純物から成る鋼片を熱延、酸洗、冷延後、750〜900℃にて焼鈍し、350℃以下まで50℃/秒以上で冷却し、酸洗後、途中の調質圧延をかけることなく、NiまたはNi−Feをプレメッキし、5℃/秒以上で430〜500℃まで加熱後亜鉛メッキ浴中で亜鉛メッキし、460〜550℃で5〜40秒の合金化加熱処理を行い、最終の調質圧延を0.2〜1%の伸び率でかけることにより加工性の良好な合金化溶融亜鉛メッキ高強度鋼板を製造する。
【選択図】 図1
Description
(1)質量%で、C:0.05〜0.20%、Mn:1.0〜3.0%、Si:0.3〜1.8%、P:0.05%以下、S:0.03%以下、sol.Al:0.005〜1.0%、N:0.01%以下を含み、残部はFeおよび不可避的不純物から成る鋼片を熱延、酸洗、冷延後、750〜900℃にて焼鈍し、350℃以下まで50℃/秒以上で冷却し、酸洗後、途中の調質圧延をかけることなく、NiまたはNi−Feをプレメッキし、5℃/秒以上で430〜500℃まで加熱後亜鉛メッキ浴中で亜鉛メッキし、460〜550℃で5〜40秒の合金化加熱処理を行い、最終の調質圧延を0.2〜1%の伸び率でかけることを特徴とする加工性の良好な合金化溶融亜鉛メッキ高強度鋼板の製造方法。
(2)前記組成に加え、さらに、下記(a)〜(e)群のうちから選ばれた1群または2群以上を含有することを特徴とする上記(1)に記載の加工性の良好な合金化溶融亜鉛メッキ高強度鋼板の製造方法。
(a)群:Cr、Moのうちの1種または2種を合計で、0.05〜1.0質量%
(b)群:Bを0.005質量%以下
(c)群:Ti、Nb、Vのうち1種または2種以上を合計で0.005〜0.2質量%
(d)群:Cu、Ni、Snのうち1種または2種以上を合計で、0.02〜2.0質量%
(e)群:Ca、REMのうちの1種または2種を合計で、0.01質量%以下
溶鋼は通常の高炉法で溶製されたものの他、電炉法のようにスクラップを多量に使用したものでもよい。スラブは、通常の連続鋳造プロセスで製造されたものでもよいし、薄スラブ鋳造で製造されたものでもよい。スラブは一旦冷却してから、熱延前の加熱炉で加熱しても良いし、冷却途中で高温まま加熱炉に入れる、所謂HCRやDRでも良い。
Claims (2)
- 質量%で、
C:0.05〜0.20%、
Mn:1.0〜3.0%、
Si:0.3〜1.8%、
P:0.05%以下、
S:0.03%以下、
sol.Al:0.005〜1.0%、
N:0.01%以下
を含み、残部はFeおよび不可避的不純物から成る鋼片を熱延、酸洗、冷延後、750〜900℃にて焼鈍し、350℃以下まで50℃/秒以上で冷却し、酸洗後、途中の調質圧延をかけることなく、NiまたはNi−Feをプレメッキし、5℃/秒以上で430〜500℃まで加熱後亜鉛メッキ浴中で亜鉛メッキし、460〜550℃で5〜40秒の合金化加熱処理を行い、最終の調質圧延を0.2〜1%の伸び率でかけることを特徴とする加工性の良好な合金化溶融亜鉛メッキ高強度鋼板の製造方法。 - 前記組成に加え、さらに、下記(a)〜(e)群のうちから選ばれた1群または2群以上を含有することを特徴とする請求項1に記載の加工性の良好な合金化溶融亜鉛メッキ高強度鋼板の製造方法。
(a)群:Cr、Moのうちの1種または2種を合計で、0.05〜1.0質量%
(b)群:Bを0.005質量%以下
(c)群:Ti、Nb、Vのうち1種または2種以上を合計で0.005〜0.2質量%
(d)群:Cu、Ni、Snのうち1種または2種以上を合計で、0.02〜2.0質量%
(e)群:Ca、REMのうちの1種または2種を合計で、0.01質量%以下