JP2006274385A - 水中で剥離する層状複水酸化物を使用した防錆皮膜組成物およびそれを用いた防錆処理金属材料 - Google Patents
水中で剥離する層状複水酸化物を使用した防錆皮膜組成物およびそれを用いた防錆処理金属材料 Download PDFInfo
- Publication number
- JP2006274385A JP2006274385A JP2005097503A JP2005097503A JP2006274385A JP 2006274385 A JP2006274385 A JP 2006274385A JP 2005097503 A JP2005097503 A JP 2005097503A JP 2005097503 A JP2005097503 A JP 2005097503A JP 2006274385 A JP2006274385 A JP 2006274385A
- Authority
- JP
- Japan
- Prior art keywords
- rust preventive
- water
- layered double
- double hydroxide
- rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】一般式:〔M2+ 1−xM3+ x(OH)2〕〔G・yH2O〕
(式中、M2+はMg,Fe,Zn,Cu又はCoから選ばれた2価金属イオン、M3+はAl,Fe,CrまたはInから選ばれた3価金属イオン、0.2≦x≦0.33,Gは炭素数5までの飽和脂肪族モノカルボン酸のCa,Mg,Zn,Ni,Cu,Co,Mn,Al,Fe、CrまたはCe塩、yは0より大きい実数である。)で示される水中で剥離する層状複水酸化物を使用する防錆皮膜組成物である。
Description
「ナノ粒子の金属酸化物含有皮膜による透明防錆処理剤と防錆効果」 工業材料、2004年10月号(Vol.52、No10)、P36−39。
上述した様に、ナノシート分散ゾルは、単独使用するのみならず顔料、フィラーなどの成分を加えて、着色、隠蔽性付与、防錆性の向上などの効果を高めることができる。添加できる成分としては、特に制約はないが、強酸性物質は素材の層状複水酸化物を溶解させる可能性があるため望ましくない。特に、リン酸亜鉛、あるいはトリポリリン酸アルミニウム系防錆顔料であるK−ホワイト105(テイカ(株)製)を加えることにより防錆性がより向上することが分かった。
酢酸マグネシウム0.28mol/L水溶液へ、予め700℃温度下において20時間熱処理を行ったMg−Al系層状複水酸化物(協和化学社製炭酸型複水酸化物DHT−6)を0.28molを加える。15時間室温にて撹拌後、得られた固体生成物(ゲル状)を遠心分離にて分離後、そのまま90℃乾燥機にて10時間乾燥し、その後粉砕することにより生成物1を得た。
酢酸マグネシウムを酢酸セリウムに変更する以外は実施例1と同様の操作を行い、生成物2を得た。
酢酸亜鉛0.28mol/L水溶液へ、予め600℃温度下において20時間熱処理を行ったZn−Al系層状複水酸化物を0.28molを加える。15時間室温にて撹拌後、得られた反応液をそのまま100℃乾燥機にて20時間乾燥し、その後粉砕することにより生成物3を得た。
合成−1で得た生成物1の粉体を、室温下でイオン交換水に所定量加えて得たナノシート分散ゾルを防錆皮膜組成物(a)として使用した。
合成−2で得た生成物2の粉体を、50℃のイオン交換水に所定量加えて得たナノシート分散ゾルを防錆皮膜組成物(b)として使用した。
合成−3で得た生成物3の粉体を、室温下でイオン交換水/エタノール=0.7/0.3(wt比)に所定量加えて得たナノシート分散ゾルを防錆皮膜組成物(c)として使用した。なお、本ナノシート分散ゾルは、若干白濁状態を示し、ナノシートが一部凝集していることが推測された。
合成−1で得た生成物1の粉体を、室温下でイオン交換水に所定量加え、ナノシート分散ゾルの10wt%液の調整を行い、それをバインダー成分として下記の配合により防錆皮膜組成物(d)および(e)を得た。
合成−1で得た生成物1の粉体を、室温下でイオン交換水に所定量加え、ナノシート分散ゾルの5wt%液の調整を行い、それをバインダー成分として下記の配合により防錆皮膜組成物(f)、(g)および(h)を得た。
防錆試験1:
機内温度35℃に保った塩水噴霧試験機に入れ、5%塩化ナトリウム水溶液を1kg/cm2で8時間および24時間噴霧し、試験板の錆の発生を観察した。
機内温度20℃、相対湿度80%に保った恒温恒湿機に入れ、24時間後の試験板の錆の発生を観察した。
評価結果を表4に示した。表4から明らかなように、本発明にもとづく実施例の防錆性の効果が確認された。実施例7における20℃乾燥皮膜に関しては、水への再分散性が残っており、過酷な防錆試験方法である通常の塩水噴霧試験(防錆試験1)では見かけ上、悪くなっているが、穏和な条件で行った防錆試験2では、明らかな防錆効果が確認された。
Claims (8)
- 一般式:〔M2+ 1−xM3+ x(OH)2〕〔G・yH2O〕
(式中、M2+はMg,Fe,Zn,Cu又はCoから選ばれた2価金属イオン、M3+はAl,Fe,CrまたはInから選ばれた3価金属イオン、0.2≦x≦0.33,Gは炭素数5までの飽和脂肪族モノカルボン酸のCa,Mg,Zn,Ni,Cu,Co,Mn,Al,Fe、CrまたはCe塩、yは0より大きい実数である。)で示される水中で剥離する層状複水酸化物を使用する防錆皮膜組成物。 - M2+がMg2+またはZn2+であり、M3+がAl3+であり、Gが酢酸のMg、CeまたはZn塩である請求項1の層状複水酸化物を使用する防錆皮膜組成物。
- 請求項1または請求項2の層状複水酸物を水および/または水を含有する水溶性溶剤に加え、水および/または水を含有する水溶性溶剤中で層状複水酸化物を剥離、分散させてゾル化(以下、「ナノシート分散ゾル」という。)することを特徴とする防錆皮膜組成物の製造方法。
- 請求項3の方法により得られるナノシート分散ゾルを使用する防錆皮膜組成物。
- 請求項3の方法により得られるナノシート分散ゾルに、防錆顔料または/および微粒子顔料等の粉体顔料成分を加えることを特徴とする防錆皮膜組成物。
- 請求項5における防錆顔料が、リン酸亜鉛またはトリポリリン酸アルミニウム系などのリン酸系防錆顔料であることを特徴とする防錆皮膜組成物。
- 請求項5における微粒子顔料が、酸化チタン、酸化ケイ素、酸化亜鉛、酸化セリウム等の平均粒子径が0.1μm以下の金属酸化物であることを特徴とする防錆皮膜組成物。
- 請求項4ないし請求項5のいずれかにおける防錆皮膜組成物を、金属素材に塗装後、100〜700℃で加熱することを特徴とする防錆皮膜処理金属材料。