JP2006068671A - セメント質基材の塗装方法 - Google Patents
セメント質基材の塗装方法 Download PDFInfo
- Publication number
- JP2006068671A JP2006068671A JP2004257034A JP2004257034A JP2006068671A JP 2006068671 A JP2006068671 A JP 2006068671A JP 2004257034 A JP2004257034 A JP 2004257034A JP 2004257034 A JP2004257034 A JP 2004257034A JP 2006068671 A JP2006068671 A JP 2006068671A
- Authority
- JP
- Japan
- Prior art keywords
- water
- paint
- weight
- coating
- aqueous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】セメント質下地に対し、水性着色塗料、水性メタリック塗料を順次塗装する塗装方法において、前記水性着色塗料として、合成樹脂エマルション及び着色顔料を必須成分とし、該合成樹脂エマルションの固形分100重量部に対し該着色顔料を1〜500重量部含み、前記水性メタリック塗料との色差△Eが20以下であり、粘度が0.1〜6Pa・s、チクソトロピーインデックスが6.0以下である水性着色塗料を使用し、前記水性着色塗料の単位面積当たりの固形分が30g/m2以上となるように塗装する。
【選択図】なし
Description
1.セメント質下地に対し、水性着色塗料、水性メタリック塗料を順次塗装する塗装方法において、
前記水性着色塗料として、
合成樹脂エマルション及び着色顔料を必須成分とし、該合成樹脂エマルションの固形分100重量部に対し該着色顔料を1〜500重量部含み、
前記水性メタリック塗料との色差△Eが20以下であり、
粘度が0.1〜6Pa・s、チクソトロピーインデックスが6.0以下である水性着色塗料を使用し、
前記水性着色塗料の単位面積当たりの固形分が30g/m2以上となるように塗装することを特徴とするセメント質基材の塗装方法。
2.前記水性着色塗料の塗装をローラブラシを用いて行うことを特徴とする1.記載のセメント質基材の塗装方法。
3.前記水性着色塗料の塗装に先立ち、セメント質下地に対し、
平均粒子径0.1μm以下の水性樹脂を結合剤とし、該水性樹脂を固形分で5〜50重量%含む水性下塗塗料を、単位面積当たりの固形分が10g/m2以上となるように塗装することを特徴とする1.または2.に記載のセメント質基材の塗装方法。
水性着色塗料の塗装に先立ち下塗塗料を塗装すれば、水性着色塗料との相乗効果により、セメント質下地からのアルカリ成分の滲出をより確実に抑制することができる。
具体的に、セメント質下地としては、例えば、コンクリート、モルタル、繊維混入セメント板、セメント珪酸カルシウム板、スラグセメントパーライト板、石綿セメント板、スレート板、ALC板、サイディング板等が挙げられる。このうち、コンクリート、モルタル等の基材は、通常、施工現場で水等と混練したものを硬化させることによって得られる。ALC板、サイディング板等のセメント質建材は、抄造法、押し出し成形法、注型法等の各種方法によって板状に成形されたものである。これら基材の表面は、何らかの表面処理(例えばパテ処理、フィラー処理等)が施されたものでもよく、既に塗膜が形成されたものでもよい。
水性下塗塗料の塗装方法としては、ハケ塗り、スプレー塗装、ローラ塗装等の種々の方法を採用することができる。塗付時には水等で希釈することによって、粘性を適宜調整することもできる。希釈割合は、通常0〜50重量%程度である。塗装後の乾燥は通常、常温で行えばよいが、必要に応じ加熱することもできる。
本発明における水性着色塗料は、その形成塗膜において、後述のメタリック塗料とほぼ同色(共色)の色相を呈するものである。本発明では、かかる水性着色塗料をメタリック塗料の下塗りとして採用することにより、メタリック塗料の彩度や光輝性を保持しつつ、塗膜全体の隠ぺい性を高めることができる。具体的に、水性着色塗料の色相は、水性メタリック塗料との色差が20以下(好ましくは10以下、より好ましくは5以下)となるように設定する。
なお、本発明における色差(△E)は、色差計を用いて測定される値であり、それぞれの塗膜のL*値、a*値、b*値より下記式にて算出することができる。
<式>△E={(L* 1−L* 2)2+(a* 1−a* 2)2+(b* 1−b* 2)2}0.5
(式中、L* 1、a* 1、b* 1はそれぞれ水性着色塗料の塗膜のL*、a*、b*。L* 2、a* 2、b* 2はそれぞれ水性メタリック塗料の塗膜のL*、a*、b*)
水性着色塗料の粘度は、通常0.1〜6Pa・sであるが、好ましくは0.2〜4Pa・s、より好ましくは0.3〜3Pa・sである。また、チクソトロピーインデックスは、通常6.0以下であるが、好ましくは4.0以下、より好ましくは3.0以下である。チクソトロピーインデックスの下限は、通常1.0以上である。
なお、本発明における粘度は、BH型粘度計による20rpmにおける粘度(4回転目の指針値)を測定することにより求められる値である。チクソトロピーインデックス(TI)は、BH型粘度計を用い、下記式により求められる値である。いずれも測定温度は23℃である。
<式>TI=η1/η2
(式中、η1は2rpmにおける粘度(Pa・s:2回転目の指針値)。η2は20rpmにおける粘度(Pa・s:4回転目の指針値))
水性着色塗料における合成樹脂エマルションとしては、少なくとも(メタ)アクリル酸アルキルエステルをモノマー成分として含むモノマー群を共重合して得られる合成樹脂エマルションが好ましく使用できる。
モノマー群における(メタ)アクリル酸アルキルエステルの構成比率は、通常50重量%以上、好ましくは60重量%以上、より好ましくは70重量%以上である。上限は特に限定されないが、通常99.8重量%以下、好ましくは99.5重量%以下、より好ましくは99.2重量%以下である。
合成樹脂エマルションのガラス転移温度は通常−60〜80℃(好ましくは−40〜60℃)程度である。また、合成樹脂エマルションの平均粒子径は、通常0.05〜0.4μm程度である。
着色顔料の混合比率は、上記合成樹脂エマルションの固形分100重量部に対し、通常1〜500重量部、好ましくは5〜200重量部、より好ましくは10〜100重量部である。着色顔料の混合比率がかかる範囲内であれば、水性着色塗料の色相を水性メタリック塗料の共色に調整しつつ、塗膜の隠ぺい性を十分に確保することができる。
親水性有機溶剤の混合比率は、上記合成樹脂エマルションの固形分100重量部に対し、通常0.2〜30重量部、好ましくは1〜20重量部である。
なお、水性着色塗料のpHは、6.0〜8.0であることが望ましい。pHがかかる範囲内であれば、水性着色塗料の粘性調整の点で有利である。
アルミニウム顔料としては、種々の表面処理を施したものも使用できる。例えば、アトマイズドアルミニウム粉及び/またはアルミニウム箔を、脂肪酸、脂肪族アミン、脂肪族アミド、脂肪族アルコール等の粉砕助剤を用いて粉砕した後、さらにクロム酸、リン酸、リン酸塩、リン酸エステル、バナジン酸塩、酸化バナジウム、モリブデン酸塩、シリカ等によって処理を施したもの等が使用できる。このような処理を施したアルミニウム顔料を使用すれば、水との接触による水素ガスの発生を抑制することもできる。
着色顔料としては、通常塗料に使用可能なものであれば特に制限されず、例えば酸化チタン、カーボンブラック、酸化第二鉄(ベンガラ)、黄色酸化鉄、オーカー、群青、コバルトグリーン等の無機系顔料、アゾ系、ナフトール系、ピラゾロン系、アントラキノン系、ペリレン系、キナクリドン系、ジスアゾ系、イソインドリノン系、ベンゾイミダゾール系、フタロシアニン系、キノフタロン系等の有機顔料等が使用できる。これら着色顔料は、所望の色彩に応じて1種または2種以上を適宜使用することができる。
着色顔料の混合比率は、上記合成樹脂エマルションの固形分100重量部に対し通常200重量部以下、好ましくは0.1〜100重量部である。
塗付時には水等で希釈することによって、塗料の粘性を適宜調整することもできる。希釈割合は、通常0〜20重量%程度である。塗装後の乾燥は通常、常温で行えばよいが、必要に応じ加熱することもできる。
塗付時には水等で希釈することによって、塗料の粘性を適宜調整することもできる。希釈割合は、通常0〜20重量%程度である。水性クリヤー塗料を塗装した後の乾燥は通常、常温で行えばよいが、必要に応じ加熱することもできる。
・水性下塗塗料A
容器内に合成樹脂エマルションA(スチレン−ブチルアクリレート−アクリルアミド−(2−ヒドロキシエチルメタクリレート)−グリシジルメタクリレート共重合体、pH7.0、固形分50重量%、ガラス転移温度2℃、平均粒子径0.08μm)を200重量部仕込み、これに2,2,4−トリメチル−1,3−ペンタンジオールモノイソブチレートを5重量部、水を180重量部、シリコーン系消泡剤を1重量部混合し、常法で均一に攪拌することによって水性下塗塗料Aを製造した。この水性下塗塗料Aにおける樹脂量(固形分)は26重量%である。
容器内に合成樹脂エマルションAを100重量部仕込み、これに合成樹脂エマルションB(スチレン−メチルメタクリレート−ブチルアクリレート−アクリルアミド−メタクリル酸共重合体、pH7.2、固形分50重量%、ガラス転移温度5℃、平均粒子径0.2μm)を100重量部、2,2,4−トリメチル−1,3−ペンタンジオールモノイソブチレートを5重量部、水を180重量部、シリコーン系消泡剤を1重量部混合し、常法で均一に攪拌することによって水性下塗塗料Bを製造した。この水性下塗塗料Bにおける樹脂量(固形分)は26重量%である。
表1に示す配合に従い、常法により各原料を均一に混合して水性着色塗料A〜Eを製造した。なお、水性着色塗料の製造においては以下の原料を使用した。
・合成樹脂エマルションC(メチルメタクリレート−スチレン−(2−エチルヘキシルアクリレート)−(2−ヒドロキシエチルメタクリレート)−メタクリル酸共重合体、pH7.0、固形分50重量%、ガラス転移温度16℃)
・合成樹脂エマルションD(メチルメタクリレート−スチレン−(2−エチルヘキシルアクリレート)−メタクリル酸共重合体、pH7.1、固形分50重量%、ガラス転移温度16℃)
・着色顔料A:酸化チタン70重量%分散液
・着色顔料B:カーボンブラック24重量%分散液
・有機溶剤A:トリプロピレングリコールモノメチルエーテル(水への溶解度∞)
・有機溶剤B:トリプロピレングリコールモノブチルエーテル(水への溶解度3g/100g)
・増粘剤A:会合性増粘剤(エチレンオキシドウレタンブロックコポリマー、固形分20重量%)
・増粘剤B:アルカリ可溶性エマルション(固形分20重量%)
・pH調整剤:25重量%アンモニア
・消泡剤:シリコーン系消泡剤
容器内に合成樹脂エマルションCを200重量部仕込み、これにアルミニウム顔料(平均粒子径15μm)を20重量部、トリプロピレングリコールモノメチルエーテルを12重量部、会合性増粘剤を2重量部、シリコーン系消泡剤0.8重量部等を常法にて順次混合・攪拌することによって水性メタリック塗料Aを製造した。
容器内に合成樹脂エマルションCを200重量部仕込み、これにトリプロピレングリコールモノメチルエーテルを12重量部、シリコーン系消泡剤0.8重量部等を常法にて順次混合・攪拌することによって水性クリヤー塗料Aを製造した。
・試験例1
スレート板に対し、水性下塗塗料Aを単位面積当たりの固形分が40g/m2となるようにスプレー塗りし、標準状態(温度23℃・相対湿度50%)で3時間乾燥後、水性着色塗料Aを単位面積当たりの固形分が70g/m2となるようにローラ塗りし、標準状態で24時間乾燥させた。次いで、水性メタリック塗料Aを単位面積当たりの固形分が150g/m2となるようにローラ塗りし、標準状態で24時間乾燥後、水性クリヤー塗料Aを単位面積当たりの固形分が70g/m2となるようにスプレー塗りし、標準状態で14日間乾燥させた。
以上の方法で得られた試験体について、促進耐候性試験機としてスーパーUVテスター(岩崎電気株式会社製)を用い、光照射6時間・結露2時間(計8時間)を1サイクルとして計30サイクルまで試験を行った。このときの試験体表面の状態(艶引け、変色等)を確認し、全く異常がないものを◎、ほとんど異常がないものを○、一部に異常がみられるものを△、全体に異常がみられるものを×とした。
表2に示す組合せにおいて、上記実施例1と同様の方法で試験を行った。
Claims (3)
- セメント質下地に対し、水性着色塗料、水性メタリック塗料を順次塗装する塗装方法において、
前記水性着色塗料として、
合成樹脂エマルション及び着色顔料を必須成分とし、該合成樹脂エマルションの固形分100重量部に対し該着色顔料を1〜500重量部含み、
前記水性メタリック塗料との色差△Eが20以下であり、
粘度が0.1〜6Pa・s、チクソトロピーインデックスが6.0以下である水性着色塗料を使用し、
前記水性着色塗料の単位面積当たりの固形分が30g/m2以上となるように塗装することを特徴とするセメント質基材の塗装方法。 - 前記水性着色塗料の塗装をローラブラシを用いて行うことを特徴とする請求項1記載のセメント質基材の塗装方法。
- 前記水性着色塗料の塗装に先立ち、セメント質下地に対し、
平均粒子径0.1μm以下の水性樹脂を結合剤とし、該水性樹脂を固形分で5〜50重量%含む水性下塗塗料を、単位面積当たりの固形分が10g/m2以上となるように塗装することを特徴とする請求項1または請求項2に記載のセメント質基材の塗装方法。