JP2006062942A - 触媒活性の高い細孔分布をもつペロブスカイト型複合酸化物および触媒 - Google Patents
触媒活性の高い細孔分布をもつペロブスカイト型複合酸化物および触媒 Download PDFInfo
- Publication number
- JP2006062942A JP2006062942A JP2004283476A JP2004283476A JP2006062942A JP 2006062942 A JP2006062942 A JP 2006062942A JP 2004283476 A JP2004283476 A JP 2004283476A JP 2004283476 A JP2004283476 A JP 2004283476A JP 2006062942 A JP2006062942 A JP 2006062942A
- Authority
- JP
- Japan
- Prior art keywords
- complex oxide
- perovskite
- elements
- perovskite complex
- rare earth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】細孔半径10〜50nmの細孔の占める細孔容積の合計が0.05cc/g以上である、例えば希土類元素類の1種以上と遷移金属元素の1種以上を含むペロブスカイト型複合酸化物。特に構造式RTO3において、Rは希土類元素類の1種以上で構成され、Tは遷移金属元素の1種以上で構成されるもの、あるいはまた、Rは希土類元素類の1種以上と、アルカリ金属元素およびアルカリ土類金属元素の中から選ばれる1種以上とで構成され、Tは遷移金属元素の1種以上で構成されるものが好適に採用できる。ここで「希土類元素類」とは希土類元素にYを加えた元素群をいう。
【選択図】図1
Description
なお「希土類元素類」とは希土類元素にYを加えた元素群をいう。
硝酸ランタンと硝酸ストロンチウムと硝酸鉄を、ランタン元素とストロンチウム元素と鉄元素のモル比が0.8:0.2:1となるように混合した。この混合物を、ランタン元素とストロンチウム元素と鉄元素の液中モル濃度の合計が0.2mol/Lとなるように水に添加して原料溶液を得た。この溶液を攪拌しながら溶液の温度を25℃に調整し、温度が25℃に到達した段階で、沈殿剤として炭酸アンモニウム溶液を添加しながらpH=8に調整した。その後、反応温度を25℃に保ちながら攪拌を12時間継続することにより、沈殿の生成を十分進行させた。得られた沈殿を濾過して回収した後、水洗し、110℃で乾燥した。得られた粉末を前駆体粉と言う。
次に、この前駆体粉を大気雰囲気下600℃で熱処理して焼成した。得られた焼成体のX線粉末回折(Co−Kα線使用)を行ったところ、図1に示すように、(La0.8Sr0.2)FeO3のペロブスカイト型複合酸化物単相であることが確認された。
硝酸ランタンと硝酸鉄を、ランタン元素と鉄元素のモル比が1:1となるように混合した以外は、実施例1を繰り返した。
得られた焼成体のX線粉末回折を行ったところLaFeO3のペロブスカイト型複合酸化物単相であることが確認された。
このペロブスカイト型複合酸化物の焼成体について、実施例1と同様に細孔分布を求めた。その結果を図3に示す。この細孔分布から細孔半径10〜50nmの細孔の占める細孔容積の合計を求めると0.169cc/gであった。
硝酸ランタンと硝酸ストロンチウムと硝酸マンガンを、ランタン元素とストロンチウム元素とマンガン元素のモル比が0.8:0.2:1となるように混合した以外は、実施例1を繰り返した。
得られた焼成体のX線粉末回折を行ったところ(La0.8Sr0.2)MnO3のペロブスカイト型複合酸化物単相であることが確認された。
このペロブスカイト型複合酸化物の焼成体について、実施例1と同様に細孔分布を求めた。その結果を図4に示す。この細孔分布から細孔半径10〜50nmの細孔の占める細孔容積の合計を求めると0.328cc/gであった。
一般的な複合酸化物の製法の1つである共沈法によってペロブスカイト型複合酸化物を製造した。
沈殿剤として水酸化ナトリウムを添加しながらpHを12に調整した以外は、実施例1と同様に沈殿を生成させ、これを濾過、水洗、乾燥して前駆体粉を得た。この前駆体粉を大気雰囲気下600℃で熱処理して焼成した。しかしながらペロブスカイト型複合酸化物単相とはならず、順次熱処理温度を上昇させたところ、900℃で熱処理した場合には(La0.8Sr0.2)FeO3のペロブスカイト型複合酸化物単相からなる焼成体が得られることがX線粉末回折により確認された。そこでこの比較例では焼成温度を900℃とした。
900℃の焼成温度で得られた(La0.8Sr0.2)FeO3ペロブスカイト型複合酸化物の焼成体について実施例1と同様に細孔分布を求めた。その結果を図5に示す。この細孔分布から細孔半径10〜50nmの細孔の占める細孔容積の合計を求めると0.012cc/gであった。
一般的な複合酸化物の製法の1つであるクエン酸錯体法によってペロブスカイト型複合酸化物を製造した。
実施例2と同様に、硝酸ランタンと硝酸鉄を、ランタン元素と鉄元素のモル比が1:1となるように混合した。この混合物を、ランタン元素と鉄元素の液中モル濃度の合計が0.2mol/Lとなるように水に添加し、更にランタン元素と鉄元素の液中モル濃度の合計に対して1.2倍量のクエン酸を添加して原料溶液を得た。
この原料溶液をロータリー・エバポレーターで減圧しながら80℃の湯浴中で約3時間かけて蒸発乾固させ、クエン酸錯体を作製した。
このペロブスカイト型複合酸化物の焼成体について、実施例1と同様に細孔分布を求めた。その結果を図6に示す。この細孔分布から細孔半径10〜50nmの細孔の占める細孔容積の合計を求めると0.032cc/gであった。
前記実施例1〜3、比較例1,2で得られた各焼成体について、以下のとおりPdを担持し、触媒性能を評価した。
(a)Pd担持:焼成体に、Pdにして含有量が2.0重量%に相当する硝酸パラジウム水溶液を含浸させて原料スラリーとした。この原料スラリーをロータリー・エバポレーターで減圧しながら110℃の油浴中で約3時間かけて蒸発乾固させ、更に大気雰囲気下600℃で熱処理してPd担持ペロブスカイト型複合酸化物を得た。
このPd担持ペロブスカイト型複合酸化物の焼成体について、前記と同様の方法で細孔分布を求めた。結果を図7〜11に示す。これらの細孔分布から細孔半径10〜50nmの細孔の占める細孔容積の合計を求めた。
(b)ペレット作製:Pd担持した焼成体を粉砕して粉末とし、これを錠剤成形機で加圧し、厚さ約2〜3mmの板状にした後、破砕、篩い分けにより1〜2mmのペレット状に整粒した。
(c)触媒活性評価:流通式固定床に上記ペレットを3ccの容積となるように充填した後、空間速度60000/hで表1に示す自動車排気モデルガス(当量点組成)を接触させ、出口においてHC濃度を汎用型ガス分析ユニットFIA−510(株式会社堀場製作所製)で、CO濃度を汎用型ガス分析ユニットVIA−510(株式会社堀場製作所製)でそれぞれ測定した。測定の際は、昇温速度10℃/分で室温から600℃まで昇温しながら、HC,COのそれぞれのガス成分について、その浄化率が50%に達するペレットの温度(以下「T50」という)を求めて活性の指標とした。結果を表2に示す。
Claims (10)
- 細孔半径10〜50nmの細孔の占める細孔容積の合計が0.05cc/g以上であるペロブスカイト型複合酸化物。
- 希土類元素類の1種以上と遷移金属元素の1種以上を含む請求項1に記載のペロブスカイト型複合酸化物。
- 構造式RTO3で表される請求項1に記載のペロブスカイト型複合酸化物。
ただし、Rは希土類元素類の1種以上で構成され、Tは遷移金属元素の1種以上で構成される。 - 構造式RTO3で表される請求項1に記載のペロブスカイト型複合酸化物。
ただし、Rは希土類元素類の1種以上と、アルカリ金属元素およびアルカリ土類金属元素の中から選ばれる1種以上とで構成され、Tは遷移金属元素の1種以上で構成される。 - 用途が排ガス浄化用触媒である請求項1〜4に記載のペロブスカイト型複合酸化物。
- 用途が貴金属元素を担持させる触媒用である請求項1〜4に記載のペロブスカイト型複合酸化物。
- 請求項1〜4に記載のペロブスカイト型複合酸化物を用いた排ガス浄化用触媒。
- 請求項1〜4に記載のペロブスカイト型複合酸化物に貴金属元素を担持させてなる排ガス浄化用触媒。
- 前記貴金属元素がPdである請求項8に記載の排ガス浄化用触媒。
- 細孔半径10〜50nmの細孔の占める細孔容積の合計が0.05cc/g以上である請求項8または9に記載の排ガス浄化用触媒。