JP2006027676A - Easy-to-open package - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a package that is excellent in seal stability compared to a cohesion breakage type sealant in terms of the face-to-face seal of a film package, ensures both easy-to-open performance and sealing performance, and is easy to take its content out of it. <P>SOLUTION: The package 100 is formed from a laminated film 110. The seal layer of the laminated film 110 comprises a co-extrusion layer peelable between layers, the co-extrusion layer including a support layer formed from polypropylene as its main component, and a peelable layer formed from a resin composition of polypropylene and polyethylene as its main component. An opening area 150 is defined in the surface of the package 100 by providing a cut line 111 in the surface of the package 100. The laminated film 110 is torn from the opening area 150 along virtual line 160. The laminated film 110 is cut off as it is in such a manner as to be peeled at a lateral seal 132 interlaminarly. Consequently, a large opening 110a' is defined in it. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

  The present invention relates to a package in which the contents to be stored can be easily taken out.

  As a means of opening pillow packaging bags often used for snacks, etc., hold the vertical seal part of the package and the opposite side with your fingers and pull it in the direction perpendicular to the horizontal seal part to peel off the entire horizontal seal part. Opening is usually performed. In addition, it has been widely practiced to improve the openability by forming notches such as so-called I notches and V notches in the peripheral seal portion.

  On the other hand, for example, as an easy-opening means such as a lid for a jelly container, a method using an easy peel film as a seal layer (sealant layer) has been widely used. It has been studied to apply an easy-opening property to the heat seal portion of the film package in a so-called “face-to-face seal” state, which is also applied to the film package.

  In this case, in the film package, since all the seal parts including the opening part are easy-open seals, it is necessary to manage the seal strength higher than that of the container lid. For example, a film package is more likely to be deformed by internal and external pressure than a rigid container, and a bag breakage is likely to occur during packaging, distribution, and storage, and therefore the required level of pressure resistance of the seal portion is high. For example, when the contents are wet tissue or the like, it is necessary to prevent drying during long-term storage when not opened, and high moisture resistance is required. Moreover, since the contents may not be used up at once after opening, the sealing properties other than the required opening need to be maintained to some extent even after opening. As described above, in the face-to-face sealing of the film packaging body, the inherently contradictory performances of moderately easy opening and sealing properties are required to be higher than those of the container lid material, and the strength of the peripheral seal portion is more strict. Need to control.

  The easy peel mechanism of the seal layer includes cohesive peeling, delamination, and interfacial peeling, but in the face-to-face seal of the film package, since stable seal strength is required as described above, conventionally, A cohesive peel type sealant which is generally said to be excellent in seal stability is mainly used.

  As such a cohesive failure type sealant, for example, in Patent Document 1 below, a layer made of a polyolefin resin or a polyolefin copolymer resin (first layer), a polypropylene resin (resin A) ), A layer (second layer) composed of a resin composition composed of a polystyrene resin (resin B) and a graft polymer (resin C) having a structure in which polystyrene is grafted on polypropylene is disclosed. In addition, it is disclosed that the resin composition used as the second layer is used as a sealant material that exhibits easy-openability due to cohesive failure in sealing with an adherend using a polypropylene resin.

On the other hand, for example, a package that contains moisture-containing contents such as a portable wet tissue has a required performance of facilitating the removal of the contents while being compact for convenience of carrying. As such a package, for example, in Patent Document 2 below, a makeup is provided in which a bag body is cut and an opening is formed, and a lid member that can be peeled off with an adhesive is provided thereon. An encapsulating bag such as a fiber material for use is described, and a film packaging body having an opening and capable of resealing the opening is disclosed.
JP 2002-361798 A Japanese Utility Model Publication No. 59-99974

  In the conventional sealing layer by cohesive peeling as described in Patent Document 1, the sealing stability in the face-to-face seal of the film package is still insufficient. In particular, in the case of polypropylene-based easy peel sealants that have excellent heat resistance, strong film stiffness, and capable of high-speed filling and packaging, the cohesive peel type has a very narrow range of sealing conditions that can provide moderately easy opening. There are problems that the conditions are too weak and the sealing properties are insufficient, or the sealing conditions are too strong and the easy-opening properties are often insufficient.

  On the other hand, in the case of the package 300 as shown in Patent Document 2, there is a problem that it is difficult to take out the contents because there is a limit to the size of the opening that can be formed. In particular, when it is desired to reduce the size of the package so that it is convenient to carry, such as a portable wet tissue, there is a limit to increasing the opening area, and this problem becomes significant.

  The present invention has been made in view of the problems as described above, and the object thereof is to provide better sealing stability than a cohesive failure type sealant in face-to-face sealing of a film package, and provide easy-opening and sealing properties. The object is to provide a compatible package. Moreover, it is providing the package which can enlarge the opening area for taking out the contents from a package using such a face-to-face seal.

  More specifically, this invention provides the easy-open packaging body which consists of the following structures.

  (1) A package comprising two or more laminated films each having a heat-resistant base material layer and a heat-sealable seal layer, wherein the seal layers are heat-sealed, and the seal layer comprises: The co-extruded layer is peelable between layers, and the co-extruded layer is mainly composed of a support layer mainly composed of polypropylene and disposed on the substrate layer side, and a resin composition composed of polypropylene and polyethylene. An easy-open packaging body that forms a multilayer including a release layer disposed in an inner layer.

  According to the easy-open packaging body of the present invention, since a co-extruded layer that can be peeled between polypropylene-based layers is used as the sealing layer that provides easy-opening properties, only the innermost peeling layer peels off during peeling. . Thereby, in the face-to-face sealing of the film package, a more stable sealing strength can be obtained than before, and both easy opening and sealing can be achieved under a wider range of sealing conditions (temperature, pressure, time).

  The heat-resistant “base material layer” is a layer that becomes the outermost layer at the time of heat sealing and has heat resistance higher than the heat sealing temperature. For example, stretched polyester, stretched polyamide, stretched polypropylene, etc. are uniaxial or biaxial. And a film stretched and oriented. A heat-sealable “seal layer” is a layer that becomes the innermost layer during heat sealing and can be thermally welded at a temperature lower than the heat sealing temperature. In addition, the “support layer” in the co-extruded layer is a layer remaining on the base layer side when the heat seal portion is peeled off, and the “release layer” in the co-extruded layer is when the heat seal portion is peeled off. It is a layer peeled away from the support layer.

  (2) The easy-open packaging body according to (1), wherein the support layer polypropylene is a homopolymer and the release layer polypropylene is a random polymer.

  According to this aspect, when the polypropylene of the support layer is a homopolymer with high crystallinity, the stiffness of the film inherent to the polypropylene can be obtained, which can be suitable for high-speed filling. Furthermore, by making the release layer polypropylene into a random polymer with low crystallinity, the compatibility between the support layer and the release layer can be appropriately adjusted, and easy opening by delamination, that is, appropriate interlayer adhesion strength can be obtained. . Moreover, since the polypropylene of the release layer is a random polymer containing ethylene, compatibility with polyethylene, which is another component of the release layer, increases, so that the release layer can be made uniform and the release layer cohesively breaks. Can be prevented.

  The homopolymer of propylene is a propylene homopolymer. The random polymer of propylene is a polymer in which copolymer monomers such as ethylene and 1-ptene are randomly incorporated into the propylene chain.

  (3) The easy-open packaging body according to (1) or (2), wherein the laminated film has a seal strength of 4 N / 15 mm or more and 7 N / 15 mm or less.

  According to this aspect, by setting the seal strength to 4 N / 15 mm or more, sufficient hermeticity can be obtained, and bag breakage during production, distribution, and storage of the film package can be prevented. Further, for example, when the content is a wet tissue or the like, it is possible to maintain moisture resistance and prevent the content from being dried. Moreover, moderate easy opening property can be provided by making seal strength into 7 N / 15mm or less.

The above-mentioned seal strength is, for example, a measured value under conditions of a seal time of 0.5 seconds, a seal pressure of 0.98 MPa / cm ² , and a tensile speed of a test piece of 300 mm / min. The sealing temperature is 140 to 160 ° C. In addition, although it does not specifically limit as a sealing machine, For example, well-known heat seal testers like test sealer TP-701-C (brand name: Tester Sangyo Co., Ltd. product) can be used.

  (4) The easy-open packaging body according to any one of (1) to (3), wherein the packaging body is a pillow packaging body.

  Normally, the pillow package is difficult to open unless there is a trigger for opening such as a notch, but in this respect, the present invention can be easily opened by hand without the need for a notch.

  (5) Upper and lower horizontal seal portions and vertical seal portions are formed in the pillow package by the heat seal, and an opening region for taking out contents from the pillow package is formed in the laminated film. A cut line is provided as described above, and a cover material that can be peeled off from the laminated film is adhered to the surface of the laminated film so as to cover the opening region. The tear opening means for guiding tearing of the laminated film is formed so that a continuous opening is formed from the opening region to the lateral seal portion from the opening region. Sex packaging.

  According to this aspect, when the lid member is peeled off, the opening region is cut along the cut line by the adhesive on the back surface of the lid member and lifted up, and separated from the lid member together. As a result, the area surrounded by the cut line becomes an opening, and an outlet for the contents is formed. And further, if the tear from the opening region is continued along the tear guiding means, a continuous opening is formed from the opening region to the lateral seal portion, and the lateral seal portion has an easy-opening property. The tearing part can be removed as it is. Therefore, a large opening area can be obtained also in the pillow package, and the contents can be easily taken out, improving convenience.

  The “opening region” formed by the cut line forms an opening from which the contents can be taken out at the time of opening. For this reason, it is preferable that the cut line is not closed, such as a shape that triggers opening, for example, a U-shape. Further, the cut line may be a continuous line or a perforation.

  As the “tear-inducing means”, in addition to using a stretched film described later, for example, a continuous line or a perforation may be formed in at least a part of the laminated film. In this case, it may be formed so as to penetrate the laminated film, or may be formed in a so-called “half cut” state in which a cut line is formed so as not to penetrate in the thickness direction of the laminated film. Good.

  (6) The easy-open packaging body according to (5), wherein the tear induction means is formed by setting the stretch direction of the stretched film constituting the laminated film as the tear direction.

  According to this aspect, since a stretched film may be used as a part of the laminated film, a step of physically forming the tearing induction means becomes unnecessary. The stretched film is preferably a highly oriented uniaxial or biaxially stretched film, and more preferably a so-called easily tearable (straight cut) uniaxially stretched film. Such a film is conventionally well-known and a commercial item can be used suitably.

  (7) The easy-open packaging body according to any one of (1) to (6), wherein the content contained in the packaging body is a portable wet tissue.

  According to this aspect, the portable wet tissue is usually stored in the pillow package, and it is necessary to easily remove the wet tissue from the pillow package, and since it is a small package, a particularly large opening is provided. is necessary. In this respect, among the easy-open packaging bodies according to the present invention, a large opening can be formed, and the wet tissue can be easily taken out, particularly if the packaging body is the above-described packaging body (5) or (6). Further, since the sealing property is sufficient, it is possible to provide a package that can prevent the contents from drying and can withstand long-term distribution and storage.

  (8) The easy-open packaging body according to (7), wherein the lateral seal portion is a face seal having a seal width of 2 mm or more.

  According to this aspect, in the case of a small pillow package like the above-described portable wet tissue, the width of the upper and lower seal portions is reduced. Therefore, in order to obtain a reliable sealing performance, a face seal having a seal width of 2 mm or more may be performed instead of a line seal. In the case of such a face seal, the seal strength is usually very high. However, if the easy-open packaging body of the present invention, even if the face seal is 2 mm or more, the easy-openability of the seal portion is improved. Since it can be obtained, a large opening can be easily formed.

  ADVANTAGE OF THE INVENTION According to this invention, in the face-to-face sealing of a film packaging body, it can provide the packaging body which is excellent in seal stability compared with the cohesive failure type sealant, and can make easy openability and sealing performance compatible. In addition, by using this, the opening area for taking out the contents from the package can be increased, and a package suitable for portable wet tissue can be provided.

  Hereinafter, an example of an embodiment of the present invention will be described based on the drawings. In the following description of the embodiment, the same constituent elements are denoted by the same reference numerals, and the description thereof is omitted or simplified.

<Overall configuration of easy-open packaging>
1 to 3 are diagrams showing an example of an embodiment of the easy-open packaging body according to the present invention, FIG. 1 is a perspective view showing an outline of the easy-open packaging body, and FIG. 2 is a view of the laminated film in FIG. FIG. 3 is an enlarged cross-sectional view, and FIG. 3 is an enlarged view of the vicinity of the horizontal seal portion in the AA ′ cross-sectional view of FIG.

  As shown in FIG. 1, this package 100 is a pillow package composed of a laminated film 110 made of a flexible packaging material. Reference numerals 131 and 132 in FIG. 1 are upper and lower horizontal seal portions, respectively, and a vertical seal (back seal) portion (not shown) is provided at the center portion on the back side in FIG.

  A cut line 111 is formed in a U-shape on the upper surface side of the laminated film 110 of the package 100 as shown in FIG. The U-shaped cutting line 111 provides an opening region 150 inside the U-shape. The opening region 150 becomes a portion that is later cut and raised by the peeling of the lid member 120. And the cover material 120 which has the tongue piece part 121 is adhere | attached so that the opening area | region 150 may be covered. An adhesive layer (not shown) is provided on a portion excluding the tongue piece 121 on the lower surface side of the lid member 120. And the laminated film 110 and the lid | cover material 120 are adhere | attached so that peeling is possible through this adhesive layer. Here, “adhesion” refers to a state where re-peeling and resealing are possible.

  Two parallel tear guiding means 160 are provided on the upper surface of the laminated film 110, extending from both end points of the U-shaped cut line 111 to the lateral seal portion 132. In this embodiment, the tearing induction means 160 is described as a virtual line. Actually, the stretching direction of the stretched film constituting the laminated film 110 coincides with the direction of the virtual line. The orientation is the tearing induction means 160.

<Configuration of laminated film>
As the laminated film 110 constituting the package 100, a laminated film having a base material layer and a seal layer is used. FIG. 2 shows an example of the configuration of the laminated film 110. This laminated film 110 is laminated | stacked by the dry lamination method through the adhesive agent in order of the base material layer A / intermediate layer B / sealing layer C from the outer layer.

Sealing layer C is further supported layer C _1, which is arranged in the intermediate layer B side becomes coextruded film consisting of a release layer C ₂ Metropolitan disposed innermost surface. And as shown in FIG. 3, in the horizontal seal | sticker part 132 of the package 100, the two laminated | multilayer film 110 are heat-welded by heat sealing. That is, the innermost layer of the peeling layer C ₂ facing each other are integrally joining surface disappears by welding.

  As a structure of the laminated | multilayer film 110, a conventionally well-known structure can be used and it does not specifically limit. For example, in order from the outer layer side, a two-layer structure of base material layer / sealing layer, a three-layer structure of base material layer / intermediate layer / sealing layer, base material layer / first intermediate layer / second intermediate layer / sealing layer A four-layer configuration can be exemplified. The laminating method may be a dry laminating method of laminating via an adhesive, or laminating by extrusion coating with polyethylene or polypropylene.

<Base material layer A and intermediate layer B>
Examples of the base material layer A (outermost layer) include known stretched films such as stretched polyester, stretched polyamide, and stretched polypropylene. Further, as the intermediate layer B, a barrier layer such as paper, non-woven fabric, and aluminum foil can be appropriately combined in addition to the stretched film. The stretched film may be stretched uniaxially or biaxially.

<Sealing layer C>
In the present invention, the seal layer C is composed of a co-extruded layer that can be peeled between the layers. The co-extruded layer is disposed on the base material layer A side, and includes a support layer C ₁ mainly composed of polypropylene, polypropylene, and It is characterized in that a multilayer including a release layer C ₂ mainly composed of a resin composition made of polyethylene and disposed in the innermost layer of the laminated film is formed.

  The entire sealing layer C is composed of a co-extruded layer that can be peeled between layers. The thickness of the sealing layer C is preferably 25 μm to 40 μm.

Support layer C _1, the polypropylene as a main component, it is preferable preferably a polypropylene homopolymer. The thickness of the support layer C ₁ is preferably 80% of the total sealing layer C is 90%, and preferably specifically a 35μm from 20.

Peeling layer C ₂ is the resin composition comprising polypropylene and polyethylene as a main component, it is preferred as the polypropylene is a random polymer. The thickness of the support layer C ₂ is preferably 10% of the total sealing layer C is 20%, it is preferable specifically a 10μm from 5 [mu] m.

  The coextruded layer having the above-described configuration may be formed by coextrusion coating, or the coextruded film may be laminated with an adhesive, polysandrami, or the like. A commercially available film may be used as the coextruded film. Examples of such a co-extruded film for delamination include Aroma TP6 (trade name: Showa Denko Plastic Products). Note that the sealing layer C is not limited to the two-layer configuration as shown in FIG. 2 and may have a configuration of three or more layers.

<Cutting line and opening area>
The cut line 111 may be provided so as to generate the opening region 150, and the shape and length of the cut line 111 are not particularly limited. In addition, the size of the opening region 150 serving as the take-out port can be appropriately selected according to the size of the package 100 and the size and shape of the contents to be taken out. For example, when the contents are portable wet tissue, the size of the opening region 150 is preferably about 5 × 20 mm to 40 × 60 mm.

  Further, in this embodiment, the cut line 111 is a continuous line formed so as to penetrate the film 110, but the cut line 111 does not necessarily have to be a continuous line and is formed in a perforated shape. Also good.

<Tearing induction means>
As described above, in this embodiment, the tearing induction means 160 is described as a virtual line, and actually, the stretching direction of the stretched film constituting the laminated film 110 coincides with the direction of the virtual line. The orientation of the stretched film is the tearing induction means 160. Specifically, for example, the base layer A in FIG. 2 may be a stretched film, preferably a highly oriented uniaxial or biaxially stretched film, and in particular, so-called easily tearable (straight cut). A uniaxially stretched film is more preferable. A conventionally well-known commercial item can be used for these stretched films.

  The tear guiding means 160 is not limited to the above-described stretching orientation, and for example, a cut line may be formed on the laminated film 110. In this case, the cut line may be formed so as to penetrate the laminated film 110 and may be in a so-called half-cut state. However, in order to maintain the sealing performance of the entire packaging body, the half-cut state It is preferable that The half cut can be formed only on the base material layer A, for example, by a known method such as laser light irradiation or mechanical cutting blade processing.

<Cover material>
The lid member 120 is preferably a sheet having a predetermined rigidity, and examples thereof include a laminated film of OPP 20 μm / PET 70 μm. Moreover, a well-known hot melt etc. can be used as an adhesive layer.

<Action>
Next, the effect | action of this package 100 is demonstrated using FIGS. 4-7. FIG. 4 is a perspective view showing a state in which peeling of the lid member 120 in FIG. 1 is started, and FIG. 5 is a perspective view showing a state in which the cover 120 is torn to the middle of the lateral seal portion 132 along the tear guiding means after peeling. 6 is a cross-sectional view taken along line AA ′ in FIG. 5 and is an enlarged view of the vicinity of the lateral seal portion, and FIG. 7 is a perspective view showing a state in which the tearing portion is removed.

  First, as shown in FIG. 4, in the package 100, the lid member 120 is peeled from the tongue piece 121 side of the lid member 120 along the direction of the arrow. Then, the opening area 150 is adhered by the adhesive layer on the back surface side of the lid member 120, and the opening area 150 of the laminated film 110 is cut along the cut line 111 and lifted. Thereby, the opening part 110a is formed in the upper surface of the laminated | multilayer film 110, and it will be in the state which can visually recognize the contents.

  Next, as shown in FIG. 5, when the cover member 120 is further peeled off, it is laminated along two parallel imaginary lines 160 formed following both end portions of the U-shaped cut line 111. The film 110 is torn and reaches the horizontal seal portion 132 as it is.

In this case, the lateral seal part 132, since the sealing layer C is seal layer delamination type, as shown in FIG. 6, the upper surface in a part of the peeling layer C ₂ (FIG. 6 was applied in the lateral seal portion 132 The release layer C ₂ ) on the side becomes the root portion 180, and the support layer C ₁ and the release layer C ₂ are peeled from each other at the release surface 170. As a result, the portion of the laminated film 110 that covers the horizontal seal portion 132 can be easily cut out, and finally, as shown in FIG. 7, a larger opening portion 110a is formed from the opening region 150 to the horizontal seal portion 132. 'Can be formed.

  The sealing strength of the lateral seal portion 132 is preferably 4N / 15 mm or more and 7N / 15 mm or less. If the seal strength is less than 4 N / 15 mm, there is a risk that seal omission may occur and the sealing performance may be reduced, or defective products such as bag breakage may occur due to external pressure during distribution storage. On the other hand, when the seal strength exceeds 7 N / 15 mm, it is not preferable because easy-openability cannot be obtained and a tearing portion remains. In addition, according to the easy-open packaging body of this invention, said value can be obtained on wider sealing conditions (temperature, time, pressure) compared with the conventional cohesive peeling type sealing layer. Therefore, management of sealing conditions is easy, and as a result, the incidence of defective products such as missing seals and difficulty in opening can be significantly reduced.

  As described above, the package 100 can form a larger opening than the conventional one, and in addition, since the seal portion is easy to open, the laminated film at the torn portion can be easily removed. Can do. Therefore, contents that are difficult to remove from the package, such as wet tissue, have little space between the packaging bag and the contents, and the friction is large, so that the contents are difficult to pull out, or small such as screws and confectionery A plurality of products are accommodated, and the product is suitably used as a package when it is desired to take out a large number of items at once.

  Note that the package 100 may be used as it is, or the package 100 may be further accommodated in an outer container. According to this, even if it is a case where the opening part of the package 100 is exposed after opening, the contents can be protected again by the exterior container.

Hereinafter, the present invention will be described in more detail with reference to Examples and Comparative Examples.
<Example 1>
A laminated film having the following specifications, PET 12 μm / ink / adhesive / aluminum foil 6 μm / adhesive / easy peel film (I) 35 μm was produced.
Here, as easy peel film (I) 35μ, delamination type allomer TP6 (trade name: manufactured by Showa Denko Plastic Products Co., Ltd.) was used. Allomer TP6 is a co-extruded film made of homopolypropylene 28μ / (random polypropylene + polyethylene) 7μ.

<Comparative Example 1>
A laminated film having the following specifications, PET 12 μm / ink / adhesive / aluminum foil 6 μm / adhesive / easy peel film (II) 30 μm was produced.
Here, as the easy peel film (II) 30 μm, a cohesive peeling type trefan 9151 (trade name: manufactured by Toray Synthetic Co., Ltd.) was used. The trefan 9151 is a coextruded film made of random polypropylene 24 μ / (polypropylene + polyethylene) 6 μ.

<Comparative example 2>
A laminated film having the following specifications, PET 12 μ / ink (pattern release varnish) / adhesive / aluminum foil 6 μ / adhesive / CPP 30 μ was produced.

<Comparative Example 3>
A laminated film having the following specifications, uniaxially stretched OPP 20 μm / ink / adhesive / aluminum foil 6 μm / adhesive / easy peel film (III) 30 μm was produced.
Here, the easy peel film (III) 30 μm is a cohesive peeling type, and is a film composed of polyethylene 25 μm / ethylene copolymer 5 μm.

<Test Example 1>
The laminated films of Example 1 and Comparative Examples 1 and 2 were heated under the conditions of a sealing time of 0.5 seconds, a sealing pressure of 0.98 MPa / cm ² , a test piece tensile speed of 300 mm / min, and a sealing temperature of 100 ° C. to 170 ° C. Sealing was performed, and the sealing strength was measured by 90-degree T-shaped peeling. The results are shown in Table 1 and FIG. The numerical unit in Table 1 is N / 15 mm. In addition, it measured using test sealer TP-701-C (brand name: Tester Sangyo Co., Ltd. product) as a heat seal tester sealing machine.

  From the results of Table 1 and FIG. 8, in Example 1 using the delamination type easy peel film, the seal strength is 4 N / 15 mm or more and 7 N / 15 mm or less between the seal temperatures of 140 ° C. and 160 ° C. It can be seen that the range of the seal temperature that can achieve the seal strength (4N / 15mm or more and 7N / 15mm or less) that can simultaneously achieve easy opening and sealing is as wide as about 20 ° C.

  On the other hand, in Comparative Example 1 using the cohesive peeling type easy peel film, the sealing strength at a sealing temperature of 140 ° C. is as low as less than 4 N / 15 mm, and the sealing performance is insufficient. In addition, the seal strength at a seal temperature of 160 ° C exceeds 7N / 15mm, the easy-openability is insufficient, and the seal temperature range that can achieve the seal strength that can achieve easy-openability and sealability at the same time is only 150 ° C. Thus, it can be seen that it is narrower than Example 1. Further, in Comparative Example 2 using a pattern release varnish (a configuration in which the ink layer is peeled off), the seal strength at 120 ° C. has already exceeded 7 N / 15 mm, and the CPP has been completely broken in the peeled state. The easy-openability was not obtained.

<Test Example 2>
A pillow package was prepared using the laminated films of Example 1 and Comparative Examples 1 and 3, and the seal strength of the transverse seal portion was measured, and the hand feeling when peeled by hand and the peeled state were evaluated. The results are summarized in Table 2 (Example 1) and Table 3 (Comparative Example 1).

  The pillow package is in the form of a gusset, length 104 mm x width 42 mm (with the gusset portion extended) x height 18.5 mm, seal width 8 mm for the vertical seal, and seal width for the top and bottom horizontal seals 9 mm (face seal) was prepared, and the test pieces were sampled by providing slits in the form of 10 mm wide strips in the lateral seal portion on the upper surface of the bag as shown in FIG. In addition, as shown in FIG. 9, the test piece 112 is sampled on the side where the vertical seal 190 is not tilted (the horizontal seal is performed in the state of two upper and lower laminated films), and the test piece 113 is formed by the vertical seal 140. Sampling was performed at two locations on the side where the body fell (horizontal sealing was performed in the state of two upper and lower laminated films and a vertical sealing portion). Of the left and right test pieces 112 and 113, the higher value was taken as the seal strength. The numerical value is an average of n = 4.

  From the results of Tables 2 and 3, in Example 1 using the delamination type easy peel film, the hand feeling is good and the peeled state is stable in a wide range of seal temperature from 120 ° C to 150 ° C. In addition, no sealing failure or breakage was observed.

  On the other hand, in Comparative Example 1 using the cohesive peeling type easy peel film, the seal strength is insufficient at 120 ° C. or lower, while the hand feeling is poor at 130 ° C. or higher and good easy-openability is obtained. I couldn't. Further, in Comparative Example 3 using the same cohesive peeling type easy peel film, the hand feeling when peeling by hand was good, but the sealing strength was insufficient at any sealing temperature.

  INDUSTRIAL APPLICABILITY The present invention can be suitably used as an easy-open packaging body for easily taking out the contents to be stored, for example, a portable wet tissue packaging body.

It is a perspective view which shows one Embodiment of the package body of this invention. It is an expanded sectional view of the laminated film in FIG. FIG. 2 is a cross-sectional view taken along line X-X ′ in FIG. 1, and is an enlarged view near a horizontal seal portion. It is a perspective view which shows the state which peeled the cover material in FIG. It is a perspective view which shows the state which torn the laminated | multilayer film to the middle of the horizontal seal part in FIG. FIG. 6 is a cross-sectional view taken along line X-X ′ in FIG. 5, and is an enlarged view in the vicinity of a lateral seal portion. It is a perspective view which shows the state which removed the tearing part in FIG. It is a graph which shows the measurement result of the seal strength of Test Example 1 in an Example. It is a graph which shows the sampling method of Test Example 2 in an Example.

Explanation of symbols

DESCRIPTION OF SYMBOLS 100 Package 110 Laminated film 110a, 110a 'Opening part 111 Cut line 112, 113 Test piece 120 Cover material 121 Tongue piece part 131, 132 Horizontal seal part 140 Vertical seal part 150 Opening area 160 Virtual line 170 Peeling surface 180 Root cut part

Claims (8)

A package comprising two or more laminated films each having a heat-resistant base material layer and a heat-sealable seal layer, wherein the seal layers are heat-sealed,
The seal layer is composed of a co-extruded layer that can be peeled between layers, and the co-extruded layer is mainly composed of a resin layer composed mainly of polypropylene and a support layer disposed on the base material layer side, and polypropylene and polyethylene. The easy-open packaging body which forms the multilayer containing the peeling layer arrange | positioned at the innermost layer of a laminated | multilayer film.   The easy-open packaging body according to claim 1, wherein the polypropylene of the support layer is a homopolymer, and the polypropylene of the release layer is a random polymer.   The easy-open packaging body according to claim 1 or 2, wherein a sealing strength of the laminated film is 4 N / 15 mm or more and 7 N / 15 mm or less.   The easily openable package according to any one of claims 1 to 3, wherein the package is a pillow package. By the heat seal, upper and lower horizontal seal portions and vertical seal portions are formed in the pillow package,
The laminated film is provided with a score line so as to form an opening region for taking out contents from the pillow package,
A cover material that can be peeled off from the laminated film is adhered to the surface of the laminated film so as to cover the opening region,
Tear guiding means for guiding tearing of the laminated film so as to tear the laminated film from the opening region and to form a continuous opening from the opening region to the lateral seal portion by peeling off the lid material The easy-open packaging body according to claim 4, wherein is formed.   The easy-open packaging body according to claim 5, wherein the tear induction means is formed by setting the stretch direction of the stretched film constituting the laminated film as the tear direction.   The easy-open packaging body according to claim 5 or 6, wherein the contents contained in the packaging body is a portable wet tissue.   The easy-open packaging body according to claim 7, wherein the lateral seal portion is a face seal having a seal width of 2 mm or more.