JP2003026224A - Packaging body - Google Patents

Packaging body

Info

Publication number
JP2003026224A
JP2003026224A JP2001208632A JP2001208632A JP2003026224A JP 2003026224 A JP2003026224 A JP 2003026224A JP 2001208632 A JP2001208632 A JP 2001208632A JP 2001208632 A JP2001208632 A JP 2001208632A JP 2003026224 A JP2003026224 A JP 2003026224A
Authority
JP
Japan
Prior art keywords
package
portion
contents
bag
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP2001208632A
Other languages
Japanese (ja)
Inventor
Kenji Sasaki
Masatoshi Suzuki
健二 佐々木
正敏 鈴木
Original Assignee
Chubu Nippon Kagaku Kk
Unitika Ltd
ユニチカ株式会社
中部日本化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chubu Nippon Kagaku Kk, Unitika Ltd, ユニチカ株式会社, 中部日本化学株式会社 filed Critical Chubu Nippon Kagaku Kk
Priority to JP2001208632A priority Critical patent/JP2003026224A/en
Publication of JP2003026224A publication Critical patent/JP2003026224A/en
Application status is Pending legal-status Critical

Abstract

PROBLEM TO BE SOLVED: To provide an easily openable packaging body from which a content is taken out without damaging or splashing the content. SOLUTION: A notch 5 is formed on a part of a bag 2. By tearing the bag 2 using the notch as a grip 6, an opening 7 is formed for easily taking out a content 4. As a material for the bag 2, a synthetic resin film having an easy peel characteristic or a linear tearing characteristic is used.

Description

【発明の詳細な説明】 【0001】 【発明の属する技術分野】本発明は、開封が容易で、内容物を簡単に取りだすことができる包装体に関し、特に、電子レンジで好適に使用できる包装体に関する。 BACKGROUND OF THE INVENTION [0001] [Technical Field of the Invention The present invention is easy to open, relates packaging body can be taken out the contents easily, in particular, packaging material can be suitably used in the microwave on. 【0002】 【従来の技術】従来より、例えば、ウエハースやクッキーのような菓子類や、ピザや焼きおにぎりといった冷凍食品の包装体には、合成樹脂フィルムをシールした包装体が使用されている。 2. Description of the Prior Art Conventionally, for example, confectionery or such as wafers and cookies, the package of frozen food such as pizza and grilled rice balls, package sealing the synthetic resin film is used. 合成樹脂フィルムとしては、破袋防止と密封性等を考慮して、延伸されたフイルム基材とシール性のあるシーラントフィルムとを張り合わせた軟質のフィルム状材料が用いられている。 Synthetic Examples of the resin film, in consideration of sealing performance such as breakage prevention, film-like material soft by bonding a sealant film with stretched film substrate and the sealing property is used. 【0003】包装体の包装形態としては、図9に示すようなものがある。 [0003] As the package form of the package, there is shown in FIG. 図9(a)は、一対のフィルムを重ね合わせてその四方を接着部3により接着した四方袋、図9(b)は、一枚のフィルムを折り曲げてその三方を接着部3により接着した三方袋、図9(c)は、一枚のフィルムを筒状にしてその背面と両端を接着部3により接着したピロー袋、図9(d)は、四方袋に自立性を持たせたスタンディングパウチである。 9 (a) is square bag adhered by the adhesive portion 3 and the four sides by superimposing a pair of films, FIG. 9 (b), a three-way adhered to the three-way by adhesion portion 3 by folding one film bag, FIG. 9 (c), pillow bag adhered to the back and both end by adhesive portions 3 and a sheet of film into a tubular shape, FIG. 9 (d) is standing pouch which gave autonomy in four bags it is. 【0004】図9(a)〜(d)に示される包装体1を開封して内容物を取り出すには、図9(e)のように接着部3を剥離するために袋体の表面側と裏面側を引き離す方向に引っ張ってシール部分を破壊して開封する方法や、図9(f)のように接着部3に予め設けられた図9 [0004] To remove the FIG 9 (a) ~ contents were opened package 1 shown in (d) is surface-side of the bag in order to peel the adhesive portion 3 as shown in FIG. 9 (e) and a method of opening by breaking the seal portion by pulling in the direction of separating the back surface side, previously provided in the adhesive portion 3 as shown in FIG. 9 (f) 9
(a)〜(d)に示されるノッチ部11をキッカケにして袋体を引き裂いて開封する方法がとられている。 (A) method to the notch 11 an opportunity to tearing open the pouch shown in ~ (d) are taken. 【0005】しかしながら、このような包装体1の開封方法では、クッキーやウエハースのように壊れやすい菓子類は開封時に破壊されたり飛散して、商品価値が低下するという問題がある。 [0005] However, in such a package 1 of the opening method, fragile confectionery such as cookies and wafers are scattered or destroyed at the time of opening, there is a problem that the commercial value is reduced. また、ピザや焼きおにぎりのようにトレーに入った内容物を取り出す場合には、開封しようとしている部分がトレーに引っかかって包装体1が不完全に開いたり、収納されたトレーが壊れたりするという問題がある。 Further, in the case of taking out the contents of which went into the tray as pizza and grilled rice balls, or open the incomplete package 1 part that you are trying to open is caught in the tray, that or broken housed trays There's a problem. また、これらの開封性を改善する目的で、図9(g)に示すように、包装体1の側部にティアテープ12を挿入あるいは装着して、ノッチ部11からの開封方向を一定に保つ開封方法も提案されている。 Further, in order to improve these openability, as shown in FIG. 9 (g), the tear tape 12 insertion or by mounting on the side of the packaging 1, keeping the opening direction from the notch portion 11 in a fixed opening methods have been proposed. しかし、ティアテープ12を挿入あるいは装着できる包装形態はピロー袋の一部であり、その用途は限定されている。 However, packaging form that can be inserted or mounted tear tape 12 is part of a pillow bag, its use is limited. 【0006】 【発明が解決しようとする課題】本発明は前記問題点を解決し、内容物を破壊したり飛散させることなく容易に開封して、簡単に内容物を取り出すことができる包装体を提供することを目的とする。 [0006] The present invention invention is to solve the above solves the above problems, and opened easily without splashing or destroy the contents, easy wrapping body can be taken out the contents an object of the present invention is to provide. また、電子レンジ調理などのような加熱処理においても好適に使用できる包装体を提供することを目的とする。 Another object is to provide a package which can be suitably used in the heat treatment, such as microwave cooking. 【0007】 【課題を解決するための手段】本発明者らは、前記課題を解決するために鋭意研究を重ねた結果、本発明に至ったものである。 [0007] Means for Solving the Problems The present inventors have found, after intensive studies to solve the above problems, and have reached the present invention. すなわち本発明は、袋体の一部に切り込みが形成され、この切り込みは、前記袋体を引き裂いて開封を容易にするための把手となることを特徴とする包装体を提供することを要旨とするものである。 That is, the present invention is cut into a portion of the bag body is formed, this incision, the gist thereof is to provide a package which is characterized in that a handle for facilitating tearing open the bag body it is intended to. 【0008】このように本発明によれば、切り込みを把手として袋体を引き裂くだけで、袋体および内容物に余分な力をかけることなく容易に包装体を開封でき、内容物の破損や飛散を低減できる。 [0008] According to the present invention, only tear the bag cut as handle, it can open easily package without applying excessive force to the bag and contents, damage and scattering of the contents It can be reduced. そして、この切り込みを袋体を平らに置いたときに上面側となる位置に形成すれば、包装体を台の上に置いたままで、上面側に形成された取り出し口より、内容物を溢すことなく容易に取り出すことができる。 Then, by forming the notch on the upper side and a position when placed flat the bag, while at the package on the table, from the extraction is formed on the upper surface side opening, to overflowing the contents it can be easily taken out without. この切り込みは、複数形成されていてもよい。 The cuts may be formed in plurality. 【0009】また、袋体の一部又は全部が合成樹脂フィルムにて形成されていることが好ましく、このような合成樹脂フィルムとしては、直線引き裂き性を有するフィルムが好適に使用でき、さらにイージーピール性を有するフィルムがより好適に使用できる。 Further, it is preferable that a portion of the bag or the whole is formed of synthetic resin films, as such synthetic resin film, can be suitably used a film having linear tearability, further easy peeling film having sex can be more suitably used. 【0010】また、本発明では、切り込みおよびその周囲の袋体の部分をシールするラベルを設けると、このラベルが切り込みとともに開封時の把手として機能するようになるため、より一層開封しやすくなる。 [0010] In the present invention, the cut and provide a label for sealing a portion of the bag body surrounding, it becomes to function as a handle when opening with incisions this label, it becomes more easily opened. 【0011】また、上記のように構成された包装体は、 [0011] configured package as described above,
加熱により内容物の圧力上昇が生じても、内容物の加熱時の圧力上昇を切り込みから逃すことができるため、例えば、電子レンジなどを用いた加熱調理用としても好適に使用できる。 Even if the pressure increase of the content is caused by heating, it is possible to escape from the notch of the pressure rise during heating of the contents, for example, it can be suitably used for cooking with a microwave oven. 【0012】また、本発明の包装体は、切り込みと袋体における内容物を収納する収納部との間にシール部が設けられていると、内容物を収納する収納部の密封性が確保されるためより好ましい。 Further, packaging of the present invention, the sealing portion between the housing part for storing contents, the cut and the bag is provided, the sealing of the housing part for accommodating the contents is ensured more preferred order. シール部のシール強度は、 Seal strength of the seal portion,
その開封性を考慮すると、袋体を形成するために接着されている接着部の強度よりも低いことが好ましく、このような強度を有するものとしては、シール部にイージーピール性のシーラントフィルムあるいはこのイージーピール性のシーラントフィルムを用いた複合フィルムを用いてシールしたものが挙げられる。 In view of its openability, low it is preferable than the strength of the adhesive portion that is bonded to form a bag body, those having such a strength, a sealant film or this the easy peel properties in the seal portion those sealed using the composite film using an easy peeling property of the sealant film. また、上記のようにシール部が形成された包装体では、内容物の加熱時の圧力上昇によりシール部の少なくとも一部が剥離し、さらにこの上昇した圧力を切り込みから逃すことができるようにすると、電子レンジなどを用いた加熱調理用としても好適に使用できる。 Moreover, in the packaging body seal portion as described above is formed, at least a portion of the seal portion is peeled off by a pressure rise during heating of the contents, further to allow escape from the notch of the increased pressure , it can be suitably used for cooking with a microwave oven. あるいは切り込みから袋体の一部をシール部を通過する所まで引き裂いて加熱処理することができるように構成しても良い。 Or cuts may be configured so that it can be heated by tearing a portion of the bag to where it passes through the seal portion from. 【0013】 【発明の実施の形態】本発明の包装体の一例を図1に示す。 [0013] One example of a package of the embodiment of the present invention is shown in FIG. 図1(a)に示すように、包装体1を形成する袋体2は、一枚のシートを筒状に丸めて背面側で重なる両端および開口となる両側を接着部3で接着したピロー袋となっている。 As shown in FIG. 1 (a), the bag body 2 to form the package 1 is, pillow bag adhered on both sides of the opposite ends and an opening that overlaps with the rear side crumpled one sheet into a tubular shape by an adhesive portion 3 It has become. 【0014】袋体2の前面2a側には、予め切り込み加工が施されて切り込み5が形成されている。 [0014] the front surface 2a side of the bag body 2, five cut in advance notch processing is given are formed. この切り込み5は、図1(b)に示すように、袋体2を引き裂いて開封するときの把手6となるものであり、この把手6を持って引っ張ることで袋体2が引き裂かれ、内容物4の取り出し口となる開口部7が形成される。 The cuts 5, as shown in FIG. 1 (b), is intended to be a handle 6 at the time of tearing open the bag body 2, the bag body 2 is torn by pulling with the handle 6, the contents opening 7 is formed as a take-out opening of the goods 4. このように、 in this way,
本発明の包装体1は、袋体2および内容物4に過剰な力をかけることなく容易に袋体2を開封して内容物4を取り出せるため、内容物4の破損や飛散を低減できる。 Package 1 of the present invention, since retrieve the contents 4 opened easily bag body 2 without applying an excessive force to the bag body 2 and the contents 4, it can be reduced breakage or scattering of the contents 4. 【0015】また、内容物4の取り出し口となる開口部7が、袋体2を平らに置いた時に袋体2の上面2aとなる位置に形成されていると、包装体1を台の上に置いたままで内容物4を容易に取り出せる。 [0015] The opening 7 as the outlet of contents 4 and is formed at a position which becomes an upper surface 2a of the bag body 2 when laid flat bag body 2, on the packaging 1 of table It remains easy to take out the contents of 4 was placed. 特に、内容物4 In particular, the contents of 4
が、スナック菓子のようにその形状が開口部7よりも小さい菓子類である場合には、内容物4を溢すことなく、 But if the shape as snacks is less confectionery than the opening 7 without to overflowing the contents 4,
より簡便に取り出せる。 More easily out of the way. 【0016】切り込み加工により形成される切り込み5 [0016] The cuts cuts are formed by processing 5
の形状は、特に限定されるものではなく、図2(a)に示すように袋体2の前面2aに曲線状の切り込み5が形成されているものだけでなく、図2(b)に示すようにコの字型の切り込み5や、図2(c)のような山形の切り込み5など各種の形状に適用できる。 Shape is not limited in particular, not only those curved cut 5 is formed on the front surface 2a of the bag body 2 as shown in FIG. 2 (a), shown in FIG. 2 (b) of co notch 5 and the shaped as applicable to chevron notch 5 and various shapes as shown in FIG. 2 (c). また、切り込み加工を施す位置も特に限定されるものではなく、上記のように袋体2の前面2aの中央部だけでなく、図2 The position subjected to rebated also is not particularly limited, but only the central portion of the front surface 2a of the bag body 2 as described above, FIG. 2
(d)に示すように袋体2の側部よりとしたものや、図2(e)のように袋体2の側端部に設けたものなど各種のものが適用できる。 Those with from a side portion of the bag body 2 as shown in (d) and can be applied those such as various those provided on the side edge of the bag body 2 as shown in FIG. 2 (e). また、袋体2の引き裂き方向は、 In addition, tear direction of the bag body 2,
上記の図2(a)〜(e)のように、対向する接着部3 As described above in FIG. 2 (a) ~ (e), the opposing adhesive portions 3
の一方から他方に向かう方向だけでなく、図2(f)のように接着部3と平行な方向に引き裂くよう構成してもよい。 While not only the direction toward the other from a may be configured to tear in a direction parallel to the bonding portion 3 as shown in FIG. 2 (f). 【0017】また、切り込み5は複数形成されていてもよく、その数や配置および形状は特に限定されるものではないが、例えば、図2(g)のように袋体2の両端に切り込み5a,5bを形成したものや、図2(h)のように袋体2の前面中央部で切り込み5a,5bを対向させて配置したものや、図2(i)のように袋体2の両側に平行となるよう一対の切り込み5a,5bを形成したものなどが適用できる。 Further, the cut 5 may also be formed with a plurality, but the number and arrangement and shape is not particularly limited, for example, 5a cuts across the bag body 2 as shown in FIG. 2 (g) , and which was formed 5b, 5a cut by the front center portion of the bag body 2 as shown in FIG. 2 (h), and that arranged 5b are opposed to each other, both sides of the bag body 2 as shown in FIG. 2 (i) etc. can be applied that formed a pair of notches 5a, 5b so as to be parallel to. さらに、図2(j),(k)のように、袋体2の前面2aと背面2bにそれぞれ切り込み5a,5bを形成したものであってもよい。 Furthermore, FIG. 2 (j), may be obtained by forming the way, 5a cuts respectively on the front 2a and the back 2b of the bag 2, 5b of (k). 【0018】本発明における袋体2は、その一部またはその全部が合成樹脂フィルムで形成されていることが好ましい。 The bag body 2 in the present invention, it is preferable that a part or the whole is formed of a synthetic resin film. 特に、上記のように切り込み5により形成された把手6を持って袋体2を直線状に引き裂き開口部7を形成するためには、袋体2の少なくとも開口部7が形成される部分を、袋体2を開封する方向に直線引き裂き性を有するフィルムで形成することが好ましい。 In particular, in order to form the opening 7 tear the bag body 2 in a straight line with a handle 6, which is formed by 5 notches as described above, at least a portion of the opening 7 is formed in the bag body 2, it is preferable to form a film having linear tearability in the direction of opening the bag body 2. 【0019】本発明に使用される合成樹脂フィルムとしては、例えば、延伸フィルムからなる基材に未延伸フィルムを積層した複合フィルム、具体的には、二軸延伸を施したポリエステルフィルム、ポリプロピレンフィルム、ナイロンフィルム等からなる基材に、未延伸のシーラントフィルム、一般的にはポリエチレンフィルム、ポリプロピレンフィルム等を貼り合わせた複合フィルムが挙げられる。 [0019] synthetic resin film used in the present invention, for example, a composite film laminated unstretched film on a substrate made of stretched film, particularly, a polyester film subjected to biaxial stretching polypropylene film, a substrate made of a nylon film or the like, the sealant film unstretched, typically include a composite film obtained by bonding polyethylene film, polypropylene film or the like. シーラントフィルムとは、包装体を形成するコアに熱融着させて袋を形成することのできるフィルムを指し、通常は、このフィルムと強度を持たせた延伸フィルム(基材フィルム)とを貼り合わせた複合フィルムが使用され、熱融着により袋体が形成される。 The sealant film, by thermal fusion to the core to form a package refers to a film capable of forming a bag, normally stretched film lamination (the base film) and which gave the film and strength composite films are used, the bag body is formed by heat fusion. 【0020】また、内容物に対して遮光性や保存性、装飾性を高める目的で、アルミ箔やアルミ蒸着を施したフィルムを中間層に配置した三層構造のものや、内容物の保存性を高める目的で、基材にバリアー性を付与したもの、具体的には、基材にポリ塩化ビニリデンをコーティングしたものや透明蒸着を施したもの、バリアー性のあるEVOHやMXD6ナイロンを中間層に設けたもの、 Further, the light-shielding property and storage stability relative to the contents, for the purpose of enhancing the decorative, objects or three-layer structure in which a film subjected to aluminum foil and aluminum vapor-deposited on the intermediate layer, the content storability the purpose of increasing, those imparting barrier properties to a substrate, specifically, those subjected to or transparent deposition those coated with polyvinylidene chloride based materials, the EVOH or MXD6 nylon with barrier property to the intermediate layer one provided,
あるいはこれらのタイプ及びEVOH,PVDC等のようにバリアー性を有するフィルムを中間層に配置した複合フィルムなども適用できる。 Alternatively applicable such composite films arranged a film having a barrier property to the intermediate layer, as such these types and EVOH, PVDC. 【0021】本発明において好適に使用される直線引き裂き性を有する複合フィルムとしては、基材フィルムに直線引き裂き性を有するポリエステルフィルム(例えばユニチカ社製エンブレットPC)やナイロンフィルム(例えばユニチカ社製エンブレムNC)を使用したもの、あるいは中間層に、一軸延伸により直線引き裂き性を付与したポリプロピレンフィルムやポリエチレンフィルムや一定方向に直線引き裂き性を付与した二軸延伸のポリプロピレンフィルムを使用した構成、また、上記の基材フィルムを中間層に使用した構成、さらには、シーラントフィルムにより直線引き裂き性を付与した構成、 Examples of the composite film having a linear tearability, which is suitably used in the present invention, a polyester film having a linear tearability to the substrate film (e.g., manufactured by Unitika Ltd. Emblet PC) and nylon film (e.g., manufactured by Unitika Ltd. Emblem those using NC), or the intermediate layer was used a polypropylene film applied to biaxially oriented linear tearability to the polypropylene film was applied a linear tearability or polyethylene film or a predetermined direction by uniaxial stretching arrangement, also, the configuration with the base film in the intermediate layer, and further include compositions that impart linear tearability by sealant film,
そしてこれらを組み合わせた構成が適用できる。 And it can be configured of a combination of these is applied. 【0022】上記の複合フィルムのうち、特に基材フィルムに直線引き裂き性を有するものを用いると、従来より包装体に使用されている複合フィルムのうち、基材フィルムを直線引き裂き性のあるポリエステルフィルムやナイロンフィルムに置き換えるだけで本発明の包装体に使用できるため、構成の変更や層構成の変更による価格上昇が少なくて済み、有利である。 [0022] Of the above composite film, a polyester film, especially the use of those having linear tearability to the base film, of the composite film which is conventionally used in packaging, with a linearity tear the base film because it can be used in the package of the present invention by simply substituting the or nylon film, requires less price increases due to the change of the changes and the layer structure of the arrangement is advantageous. 【0023】袋体2に切り込み5を形成する切り込み加工は、打ち抜き加工により行われる。 The machining cuts to form a 5 cuts the bag body 2 is carried out by punching. この打ち抜き加工は、複合フィルムを形成する際のラミネート加工を行った後に行うと設備面や応用面で有利であるが、ラミネート加工中の後工程に組み込んだり、袋体2の製袋工程中に組み込んだり、袋体2に内容物4を充填する前工程に組み込んでも工程上のロスが軽減できる。 The punching is advantageous to perform after the lamination for forming the composite film in terms of facilities and applications plane, incorporate the subsequent steps in the lamination, in bag-making step of the bag body 2 incorporating Guests can alleviate Ross on process incorporated before filling the contents 4 to the bag body 2. 【0024】上記のように構成された包装体1には、図3(a)に示すように、切り込み5およびその周囲の袋体2の部分をシールするラベル8を、袋体2に貼り重ねるようにして設けてもよい。 [0024] package 1 configured as described above, as shown in FIG. 3 (a), the label 8 to seal the 5 and part of the bag body 2 around its cut, superimposed bonded to the bag body 2 it may be provided so. このラベル8は剥離性と粘着性を兼ね備えたものであり、開封時には、図3(b) The label 8 is intended that combines tackiness and the peeling resistance, at the time of unsealing, and FIG. 3 (b)
に示すように切り込み5と一体の状態でこの切り込み5 This cut 5 in cuts of 5 and the integral state, as shown in
とともに把手6となり、切り込み5だけを設けた包装体1よりも開封性と密封性とが向上する。 Next handle 6, 5 only provided the opening than the packaging 1 cut and the sealing performance is improved with. 【0025】ラベル8の形状は特に限定されるものではなく、例えば、図4(a)〜(c)に示すように各種の形状に適用できる。 The shape of the label 8 is not particularly limited, for example, can be applied to various shapes as shown in FIG. 4 (a) ~ (c). 図4(a)は図3(a)と同じ円形のものであるが、このラベル8のようにラベル8の全面が袋体2に接着されたものでもよく、図4(b), Although FIG. 4 (a) is of the same circular and FIG. 3 (a), may be those entire labeled 8 as the label 8 is bonded to the bag body 2, FIG. 4 (b), the
(c)のように、ラベル8の一部8aが袋体2に接着され、その他の部分8bは非接着となったラベル8としてもよい。 As in (c), a portion 8a of the label 8 is bonded to the bag body 2, other portions 8b may be a label 8 having a non-adhesive. このようにすれば非接着部をつまんで容易に開封することができる。 Pinch the non-adhesive portion so doing can be easily opened. なお、全面接着されるラベル8およびその一部が接着されるラベル8のいずれの場合もその形状は特に限定されるものではない。 Incidentally, the shape is not limited in particular either case the label 8 which the label 8 and portions thereof are entirely bonded is bonded. 【0026】また、本発明におけるラベル8は、感熱の粘着剤を介して、袋体2に形成された切り込み5を覆うように粘着させたものであるが、この粘着剤はラベル8 Further, the label 8 of the present invention, through the heat-sensitive adhesive agent, but is obtained by the adhesive so as to cover the 5 notches formed in the bag body 2, the adhesive label 8
に塗布しても良く、あるいはラベル8には塗布せずに袋体2のラベル8を貼り着ける部分に直接塗布しても良い。 In may be coated, or the label 8 may be applied directly to the part for attaching the label 8 of the bag body 2 without the coating. 【0027】また、本発明におけるラベル8は、一般の紙ラベルのようなものでも適用できるが、透明のラベル8を使用するとラベル8を通して開封の状態が分かるため改ざん防止に適しており、また、包装体1自体のデザインを損なうことなく貼り着けることができるためより好ましい。 Further, the label 8 of the present invention is not intended as a general paper labels can be applied, is suitable for tamper prevention for the state of the opening is seen through the label 8 Using transparent label 8, also, more preferable in terms of being able to be pasted without compromising the design of the package 1 itself. また、ラベル8にバリアー性を有する素材を組み合わせると、ラベル8を透過して袋体2の内部に酸素や水蒸気が進入するのを遅らせることができる。 Also, the combination of material having barrier properties to the label 8, oxygen and water vapor is transmitted through the label 8 to the inside of the bag body 2 can be delayed from entering. 【0028】ラベル8の装着工程は、切り込み5を形成する切り込み加工を行った後に行うと設備面や応用面で有利であるが、切り込み加工中の後工程に組み込んだり、袋体2の製袋工程中に組み込んだり、あるいは内容物4を充填する前工程に組み込むと、工程上のロスが軽減できるため好ましい。 The mounting process of the label 8 is cut but 5 it is advantageous in terms of facilities and application surface and performed after the rebated to form a, incorporate the subsequent steps in the rebated, bag making the bag body 2 incorporate in the process, or when incorporated into a step prior to filling the contents 4, loss on process is preferred because it can reduce. 【0029】本発明の包装体1には、図5(a), [0029] packaging 1 of the present invention, FIG. 5 (a), the
(b)に示すように、切り込み5と袋体2における内容物4を収納する収納部10との間にシール部9が設けられていると、収納部10の密封性が高まるためより好ましい。 As (b), when the sealing portion 9 between the housing part 10 for accommodating the contents 4 of the notch 5 and the bag body 2 is provided, more preferable because the sealing of the housing portion 10 is increased. このシール部9の形状は特に限定されるものではなく、例えば、図6(a)に示すように図5(a)と同様のもののほかに、図6(b)〜(i)に示すように各種のものが適用できる。 The shape of the seal portion 9 is not particularly limited, for example, in addition to FIGS. 5 (a) and the like as shown in FIG. 6 (a), as shown in FIG. 6 (b) ~ (i) various things can be applied to. すなわち図6(b)〜(e)のように、切り込み5を接着部3とシール部9で囲むように構成したものや、図6(f)〜(h)のように、シール部9をラベルシールと呼ばれる構成としたものでもよい。 That is, as in FIG. 6 (b) ~ (e), 5 and those configured to surround a bonding portion 3 and the sealing portion 9 cuts, as shown in FIG. 6 (f) ~ (h), the seal portion 9 it may be one where the structure referred to as adhesive labels. ラベルシールとは、商品を陳列する際の意匠(デザイン)性を良くする目的で、通常の製袋シールよりもシールする部分を大きくして、その部分に商品名等のデザインを施し、商品性を高めたシール部分のことである。 The label seal, in order to improve the design (design) of when to display the goods, to increase the portion of the seal than the usual bag making seal, subjected to a design such as a trade name in that part, merchantability it is that the seal portion increased.
このようにシール部9をラベルシール部分として用いると、商品性としても優れたものとなる。 When used in this manner the seal portion 9 as a label seal portion, and excellent as a marketability. 【0030】また、上記図6(a)〜(h)では、シール部9の一部と接着部3の一部とが接触するよう構成したが、図6(i),(k)のように、シール部9を接着部3から離して設けたものにも適用できる。 Further, in FIG 6 (a) ~ (h), but a part of the sealing portion 9 and a part of the bonding portion 3 is configured to contact, FIG. 6 (i), as (k) a, it can be applied to those provided apart sealing portion 9 from the adhesive portion 3. 【0031】さらに、図6(j),(k)のように、切り込み5をシール部9(接着部3も含む)で囲む構成以外に、切り込み5を含めてシールする形状も適用でき、 Furthermore, as shown in FIG. 6 (j), (k), the cut 5 in addition to the configuration surrounded by the sealing portion 9 (including the bonding portion 3) can be applied shape seal including 5 cuts,
イージーピール性のシーラントを使用した場合のように、シール部9のシール強力が低い場合に有用である。 As in the case of using the easily peelable sealant is useful where a strong seal of the seal portion 9 is low. 【0032】このようなシール部9を設けた場合に、把手6となる切り込み5を持って袋体2を開封する際に、 [0032] When provided with such a sealing portion 9, when with 5 cuts a handle 6 for opening the bag body 2,
シール部9の開封性を考慮すると、シール部9には、イージーピール性のシーラントフィルムあるいはこのイージーピール性のシーラントフィルムを用いた複合フィルムを用いてシールすることが好ましい。 Considering the opening of the seal portion 9, the seal portion 9, it is preferable to seal with a composite film using the easy peeling property of the sealant film or the easily peelable sealant film. すなわち、袋体2の切り込み5が形成される開封部分、あるいは、それと貼り合せする袋体2の少なくとも一方にイージーピール性のシーラントを有する素材で構成されているものを採用することができる。 That is, the opening portion cuts 5 of the bag body 2 is formed, or may be employed which is composed of material having easy peel properties of the sealant to at least one of the bag body 2 to be bonded therewith. また、切り込み5が形成された部分と内容物4との間のシール部9に、袋体2を形成するフィルムとは別にイージーピール性のシーラントあるいはそれから構成される複合フィルムを挿入してシールすることによっても、シール部9の開封性と内容物4の密封性を確保できる。 Further, to the seal portion 9, by inserting a composite film composed separately of easily peelable sealant or from it and the film forming the bag body 2 seal between the notch 5 is part and contents formed 4 also by, it can ensure sealability openability and contents of the fourth seal portion 9. 【0033】イージーピール性のシーラントについて説明する。 [0033] describes easy peel properties of the sealant. 一般的なシーラント(単層)を使った場合、通常のシール条件ではシール強度が高くでてしまい、開封するのが困難であるが、イージーピール性のあるシーラントはそれ自身が複層になっており、シールした後は、 When using common sealant (single layer), the normal sealing conditions will out high seal strength, but it is difficult to open, sealant with easy peeling property is itself turned multilayer cage, after the seal,
シーラント内部の複層になっていた部分が剥離界面となり、シール強度が低く抑えられる。 Portion that was in double layer inside sealant becomes peeling boundary, the seal strength can be kept low. そのため、通常のシール条件においても開封の際の剥離を容易にすることができる。 Therefore, it is possible to facilitate peeling of during unsealing in normal sealing conditions. また、イージーピール性のシーラントを使わなくても、シーラント部分が多層になった構成(ポリサンド構成、あるいはシーラント部分にコーティングを施した構成)であれば、イージーピール性のシーラントと同じ効果が得られるため、有用である。 Further, without using the easy peel properties of the sealant, with the configuration in which the sealant part has a multilayered (Porisando configuration, or were coated sealant partial configuration), the same effect as easily peelable sealant obtained Therefore, it is useful. 【0034】また、上記の構成以外にも、シール部9のシール強度を袋体2を形成するために接着されている接着部3のシール強度よりも低くすることによっても、密封性と開封性とを向上させることができる。 [0034] In addition to the above configuration, also by lower than the seal strength of the adhesive portion 3 which is bonded to the seal strength of the seal portion 9 forming the bag body 2, sealing properties and openability it can be improved and. 具体的には、シール部9のシール温度の条件を下げて、袋体2の接着部3のシール強度の1/2〜1/3程度のシール強度となるようにする、あるいはシール部9を1.0kg Specifically, by lowering the condition of the sealing temperature of the sealing portion 9, made to be 1 / 2-1 / 3 of about seal strength of the seal strength of the adhesive portion 3 of the bag body 2, or the seal portion 9 1.0kg
/15mm程度の弱接着にすることなどが挙げられる。 / And the like be to 15mm about the weak adhesive.
なお、シール部9のシール強力を下げる方法としては、 As a method of lowering a strong seal of the seal portion 9,
シール温度以外に、シール圧力やシールバーの形状を工夫して行っても、同じ効果が得られるため、有用である。 Besides sealing temperature, it is performed by devising a sealing pressure and seal bar shape, since the same effect can be obtained, is useful. 【0035】なお、上記のように、シール部9にイージーピール性のシーラントフィルムやこのシーラントフィルムを用いた複合フィルムを用いてシールしたり、シール部9のシール強度を接着部3のシール強度よりも低くしたりすると、密封性と開封性は確保できるが、シール部9での破袋し易さが増すことになる。 [0035] Incidentally, as described above, or sealed using a composite film using the easy peeling property of the sealant film or the sealant film on a seal portion 9, the seal strength of the seal portion 9 the seal strength of the adhesive portion 3 When even or low and openability and sealability can be secured, so that the bag breaking ease in the sealing portion 9 is increased. このことを考慮すると、シール部9のシール幅を接着部3のシール幅よりも広くとり、破袋しにくくすることも有用な手段となるため、好ましい。 In view of this, the sealing width of the sealing portion 9 takes wider than the seal width of the adhesive portion 3, since it is also useful means to hardly breakage, preferred. 【0036】なお、本発明の包装体は、一般的な食品包装用の包装体として使用できるだけでなく、野菜等の青果物を包装するMA包装などにも適用でき、工業用や医薬品関係等で使用される包装体としても適用できる。 [0036] It should be noted that the package of the present invention can be used not only as a general packaging material for food packaging, can also be applied to such as MA packaging for packaging fruits and vegetables such as vegetables, used in industrial and pharmaceutical relationships, etc. It can be applied as a packaging material to be. 【0037】また、本発明の包装体1に内容物4を充填して加熱すると、内容物4の加熱時の圧力上昇を切り込み5から逃すことができるため、加熱を必要とする分野で好適に使用できる。 Further, when heated to fill the contents of 4 to package 1 of the present invention, it is possible to escape from 5 cuts the pressure rise during heating of the contents 4, suitably in fields requiring heat It can be used. 例えば、近年使用が増えている電子レンジ調理では、包装体1をそのまま電子レンジ内に入れて加熱処理しても、上昇した内圧は切り込み5から逃げるため、破袋することなく好適に使用できる。 For example, in microwave cooking, which is increasing in recent years use, be heat treated to put the packaging 1 as a microwave oven, to escape from the elevated pressure is cut 5 can be suitably used without breakage. また、切り込み5と袋体2における内容物4を収納する収納部10との間にシール部9が形成されている包装体1 Further, the cut 5 and the packaging body 1 of the seal portion 9 is formed between the housing part 10 for accommodating the contents 4 of the bag 2
は、加熱により内部圧力が高くなるとシール部9のシールが緩み内圧が漏れ、その後、切り込み5より内圧が漏れ、破袋することなく電子レンジ調理できる。 The leak seal loosening the internal pressure of the seal portion 9 the internal pressure is increased by the heating, then cut 5 leak pressure than can microwave cooking without breakage. さらに、 further,
加熱調理後は、切り込み5を把手6として袋体2を引き裂いて開封が容易に行え、しかも内容物4には余分な力がかからないため内容物4を破損したり飛散したりすることなく取り出せる。 After cooking, the cuts 5 tearing open the bag body 2 is easily performed as a handle 6, yet taken out without or scattered damaged the contents 4 for excessive force is not applied to the contents 4. 【0038】なお、上記のように開封する前に電子レンジでの加熱調理を行うだけでなく、加熱調理を行う前に包装体1を開封して加熱調理を行うこともできる。 It should be noted, not only performs the cooking in a microwave oven before opening as described above, it is also possible to perform cooking by opening the package 1 prior to performing the cooking. 例えば、切り込み5と袋体2における内容物4を収納する収納部10との間にシール部9が形成されている包装体1 For example, the cut 5 and the packaging body 1 of the seal portion 9 is formed between the housing part 10 for accommodating the contents 4 of the bag 2
において、切り込み5により形成された把手6を用いて、袋体2をシール部9を通過する所まであるいはそれ以上の所まで開封しておき、加熱調理しても、内部圧力が高くなることなく電子レンジ調理ができる。 In, cut 5 with a handle 6, which is formed by, it leaves open the bag body 2 to up to or more places where passing through the sealing portion 9, even if cooked, without the internal pressure increases You can microwave cooking. 【0039】また、切り込み5と袋体2における内容物4を収納する収納部10との間にシール部9が形成されている包装体1は、内容物4が収納されている部分は密封性が確保されており、保存性に優れ、シール強度もある程度確保されているため、ボイル処理やレトルト処理にも好適に使用できる。 Further, the packaging 1 the sealing portion 9 is formed between the housing part 10 for accommodating the contents 4 of the notch 5 and the bag body 2, the portion content 4 is accommodated in sealability There are reserved, excellent storage properties, because they are also secured sealing strength to some extent, it can be suitably used in the boiling treatment or retort treatment. 【0040】なお、上記の説明では、包装体1の包装形態として、ピロー袋を例に挙げて説明したが、本発明はこれに限定されるものではなく、上記図9に示す四方袋、三方袋、スタンディングパウチなどの各種の包装形態にも適用可能である。 [0040] In the above description, as a package form of the package 1 has been described as a pillow bag as an example, the present invention is not limited thereto, square bag shown in FIG. 9, three-way bags, can also be applied to various packaging forms such as standing pouch. 【0041】 【実施例】次に、実施例に基づき本発明を具体的に説明するが、本発明はこれらの実施例のみに限定されるものではない。 [0041] [Embodiment] Next, a detailed explanation of the present invention based on examples, the present invention is not limited only to these examples. なお実施例における各種物性値の測定は、以下の方法により実施した。 Note Measurements of various physical values ​​in the examples were carried out by the following method. (1)内容物の取り出し易さと使用性の評価:図1と図7に示す袋体2を用いて、この袋体を開封したときの内容物の取り出し易さを内容物が洋菓子である場合とスナック菓子である場合とに分けて、それぞれa〜dのように評価した。 (1) extraction ease of content and use of the rating: when using the bag 2 shown in FIGS. 1 and 7, the contents was taken out easily the contents upon opening the bag body is Pastry and divided into the case of the snack food, and evaluated as respectively to d. また、5人のモニターにより、a〜dの評価方法に基づいて包装体1の使用性を総合的に評価した。 In addition, the five monitors, was comprehensively evaluate the use of the package 1 on the basis of the evaluation method of a~d. 内容物:洋菓子a. Contents: Pastry a. 袋体を開封する際の袋体の切り口と内容物との接触の有無内容物との接触が無い:○(良) 内容物との接触が有る:×(悪) b. There is no contact with the presence or absence contents of the contact between the cut and the contents of the bag body at the time of opening the bag body: ○ (good) contents and the contact is there of: × (evil) b. 開封する際の取り出し口(開口部)の形成し易さ袋体の切り口と内容物とが接触することなく、取り出し口が直線的に形成される:◎(良好) 袋体の切り口と内容物とが接触することなく、取り出し口が形成される:○(良) 袋体の切り口と内容物とが接触して、取り出し口が形成し難い:×(悪) 内容物:スナック菓子c. Opening to the time of take-out port without the cut and the contents of the formation easiness bag body (opening) are in contact, outlet are linearly formed: ◎ (good) cut and the contents of the bag Doo is without contact, outlet is formed: ○ (good) in contact with and the contents of cut of the bag, it is difficult to take out port formed: × (bad) contents: snack c. 内容物の取り出し易さ包装体を台に置いた時に取り出し口が袋体の上面側となる位置に形成されるため、袋体を台に置いたままで内容物を取り出せる:○(良) 包装体を台に置いた時に取り出し口が袋体のサイドに形成されるため、袋体を傾けなければ内容物を取り出せない:×(悪) d. Since port taken out extraction ease package contents when placed on a table is formed at a position which becomes upper side of the bag, take out the contents while placing the bag on a table: ○ (good) package since ports extraction when placed on a table and is formed in the side of the bag, if tilt the bag can not eject the contents: × (bad) d. 内容物の取り出し時のこぼれやすさ内容物を袋体の上面側から取り出すため、包装体を台においたままでも内容物をこぼすことなく取り出せる:○ For retrieving spilled ease contents upon removal of the contents from the upper surface side of the bag, taken out without spilling the contents even while placing the package in a trapezoidal: ○
(良) 内容物を袋体のサイドからの取り出すため、包装体を台に置いたままでは内容物がこぼれやすく、取り出し難い:×(悪) 使用性の評価◎:良好○:良△:普通(2)開封性:図5と図8に示す袋体2を用いて、その開封性を下記のa〜cのように評価した。 (Good) for the out takes of the contents from the side of the bag, easy to spill the contents will remain at the package to the base, it is difficult to take out: × (evil) of usability evaluation ◎: good ○: Good △: Normal (2) openability: using the bag body 2 shown in FIGS. 5 and 8, were evaluated for their openability as a~c below. また、5人のモニターにより、その使用性を総合的に評価した。 In addition, the five monitors, and comprehensive evaluation of its usability. 評価基準: a. Evaluation criteria: a. 袋体を開封する際の袋体の切り口と内容物との接触の有無内容物との接触が無い:○(良) 内容物との接触が有る:×(悪) b. There is no contact with the presence or absence contents of the contact between the cut and the contents of the bag body at the time of opening the bag body: ○ (good) contents and the contact is there of: × (evil) b. 袋体を開封する際の袋体の開封方向の安定性の有無袋体を次の3方向に引っ張って開封した。 Was opened unsealing direction stability of the presence or absence bag body of the bag at the time of unsealing the bag body by pulling the next three directions. 【0042】 開封方向に沿ってまっすぐ開封する。 [0042] straight to open along the opening direction. 開封方向に対してゆっくりと右30度方向に引っ張って開封する。 Slowly it is opened by pulling to the right 30 degrees direction with respect to the unsealing direction. 開封方向に対してゆっくりと左30度方向へ引っ張って開封する。 It is opened by pulling slowly to the left 30 degrees direction with respect to the unsealing direction. 【0043】そして、開封後に形成された取り出し口の開封方向の差により下記のように評価した。 [0043] Then, it was evaluated as follows by the difference in the unsealing direction of the formed outlet after opening. 3方向に差がなく切り口がまっすぐに安定して形成できる:○(良) 3方向に差があり、開封方向の安定性に劣る:×(悪) c. 3 direction difference incision can be straight stably formed without: ○ (good) there is a difference in three directions, poor stability of the unsealing direction: × (bad) c. 開封時におけるシール部での開封のし易さ(あけ易さ)を、シール部のシール強力を測定して、下記のように評価した。 Opening easiness in the seal portion during opening of the (opened ease), by measuring the strength sealing of the sealing portion was evaluated as follows. 【0044】 シール強力が1.0kg/15mm未満:◎ シール強力が1.0kg/15mm以上2.0kg/1 The seal strength is less than 1.0kg / 15mm: ◎ seal strength is 1.0kg / 15mm more than 2.0kg / 1
5mm未満:○ シール強力が2.0kg/15mm以上3.0kg/1 5mm less than: ○ seal strength is 2.0kg / 15mm more than 3.0kg / 1
5mm未満:△ 使用性の評価◎:良好○:良△:普通×:不可(3)シール強力:袋体からシール部(接着部を含む) Less than 5 mm: △ use of rating ◎: good ○: Good △: Average ×: No (3) Seal strength: the seal portion from the bag body (including the adhesive portion)
を長手方向と交差する方向に短冊状(シール幅15m The direction into strips intersecting the longitudinal direction (seal width 15m
m)に切り取り、切り取った短冊片のシール部を摘んでT型とし、この短冊片の両端をテストスピード300m Cut to m), and T-type picking seal portion of the cut-out strips, test speed 300m both ends of the strips
m/minで引っ張って、シール強力を測定した。 Pulling in m / min, to measure the seal strength. (4)密封性:包装体を水面下に浸漬させて1分間保持し、包装体から漏れる泡の有無から包装体の密封性を下記のように評価した。 (4) sealing property: package was held by immersing for 1 minute under water, it was evaluated sealability of the package from the presence of bubbles leaking from the package as described below. 【0045】 包装体1から空気の漏れがない場合:○(密封性有り) 包装体1から空気の漏れがある場合:×(密封性無し) (5)電子レンジ適正:包装体1を電子レンジに入れ、 [0045] If there is no leakage of air from the package 1: ○ case from (sealing property there) packaging body 1 there is a leakage of air: × (no tightness) (5) Microwave Suitable for: microwave oven package 1 put in,
600Wで30秒、1分、3分加熱した。 30 seconds at 600W, 1 minute, and heated for 3 minutes. そして、それぞれの時間におけるシール部の開口の有無を調べ、シール部に開口があるものを○、開口のないものを×で評価した。 Then, it is checked whether the opening of the sealing portion at each time, what opening the seal portion ○, were evaluated as having no opening in ×. 【0046】また、3分間加熱した後の接着部の開口の有無、すなわち破袋の有無を調べた。 [0046] In addition, the presence or absence of the opening of the adhesive part after heating for 3 minutes, ie examined for breakage. そして、破袋のないものを○、破袋しているものを×で表した。 Then, those without breakage ○, expressed in × what is breakage. また、3 In addition, 3
分間加熱した時の切り込み部分での空気の吹き出し状況を調べた。 Was examined blowout situation of air at the cut portion when heated minutes. 空気の吹き出しは水蒸気の吹き出しとして見え、切り込み部分での水蒸気の吹き出しがあるものを○、水蒸気の吹き出しのないものを×で評価した。 Balloon of air is seen as a blow-out of steam, the ones where there is a balloon of water vapor in the cut portion ○, was evaluated by × those that do not balloon of water vapor. 【0047】そして、これらの総合的な判断から、電子レンジ適正が有るものを○、無いものを×で表した。 [0047] and was expressed from these comprehensive judgment, what is a microwave oven properly there ○, those not in ×. 実施例1 図1に示す包装体1を形成するために、厚み12μmのポリエチレンテレフタレート(以下、「PET」と称す。)フィルム(ユニチカ社製、エンブレットPET) In order to form the packaging body 1 shown in Embodiment 1 Figure 1, thickness 12μm polyethylene terephthalate (hereinafter, referred to as "PET".) Film (manufactured by Unitika Ltd., Emblet PET)
と、厚み50μmの直鎖状低密度ポリエチレン(以下、 When, a thickness of 50μm linear low density polyethylene (hereinafter,
「LLDPE」と称す。 It referred to as "LLDPE". )フィルム(東セロ社製、トーセロTUX)とを、接着剤(武田薬品工業社製、タケラック A−515/A−50)を用いてドライラミネーションにより貼り合わせ、ラミネート反を作成した。 ) Film (Tohcello Co., the Tosero TUX) and adhesive (manufactured by Takeda Chemical Industries, Ltd., laminated by dry lamination using TAKELAC A-515 / A-50), was prepared a laminate counter. 【0048】このラミネート反に打ち抜き加工を施して切り込み5を形成し、内容物4を充填して、縦(流れ方向)125mm×横80mmのピロー型の包装体1を作成した。 [0048] to form a 5 cuts subjected to punching to the laminate counter, filled with contents 4, longitudinal created the package 1 of pillow type (flow direction) 125 mm × horizontal 80 mm. 包装体1には、内容物4として円形状の壊れやすい洋菓子(ロッテ社製、登録商標:チョコパイ)を1 The package 1, a circular frangible confectionary (Lotte Ltd., trademark: Choco Pie) as contents 4 1
個充填した。 It was co-filling. 【0049】また、上記と同様にして、縦188mm× [0049] In addition, in the same manner as described above, vertical 188mm ×
横130mmのピロー型の包装体1を作成し、内容物4 Create a package 1 of pillow type of horizontal 130mm, contents 4
として洋菓子の代わりにスナック菓子(カルビー社製、 Snacks instead of the pastry as (Calbee Co., Ltd.,
登録商標:かっぱえびせん)を30g充填した。 Registered trademark: kappa ebisen) was 30g filling. 【0050】そして、上記の試験法に従い、それぞれの包装体1について開封性と内容物の取り出しやすさを調べ、その使用性を評価した。 [0050] Then, according to the above test method, for each of the packaging 1. Examine the extraction ease of opening property and contents were evaluated for their usability. 得られた包装体1の評価を表1に示す。 Evaluation of the resulting package 1 shown in Table 1. 【0051】 【表1】 [0051] [Table 1] 実施例2 ラミネート反を形成するPETフィルムの代わりに、厚みが12μmで、流れ方向に直線引裂き性を有するポリエチレンテレフタレート(以下、「PC」と称す。)フィルム(ユニチカ社製、エンブレットPC)を用いた。 Instead of the PET film to form a second embodiment laminating anti, the thickness was 12 [mu] m, a polyethylene terephthalate having a linear tear property in the flow direction (hereinafter, referred to as "PC".) Film (manufactured by Unitika Ltd., Emblet PC) and Using.
そしてそれ以外は実施例1と同様にして、洋菓子を充填した包装体1とスナック菓子を充填した包装体1を作成した。 And otherwise in the same manner as in Example 1 to prepare a package 1 filled with package 1 and snacks filled with confectionery. 【0052】得られた評価結果を表1に示す。 [0052] obtained evaluation results are shown in Table 1. 実施例3 実施例2で作成した包装体1において、ラミネート反に切り込み加工を施した後、図3(a)に示すように、切り込み5とその周囲の袋体2を覆うように厚み50μm A packaging body 1 prepared in Example 3 Example 2, was subjected to a rebated to laminate counter, as shown in FIG. 3 (a), the cut 5 and the thickness 50μm so as to cover the bag body 2 of the surrounding
のPETフィルム(ユニチカ社製、エンブレット)からなるラベル8を装着し、内容物4として洋菓子を充填した包装体とスナック菓子を充填した包装体を作成した。 PET film (manufactured by Unitika Ltd., Emblet) fitted with a label 8 made to prepare a package filled with packing bodies and snacks filled with confectionery as contents 4.
そして、図3(b)に示すように、ラベル8を把手6として袋体2を引き裂き包装体1の開封を行った。 Then, as shown in FIG. 3 (b), it was opened in the packaging 1. The bag body 2 tearing the label 8 as the handle 6. 【0053】得られた包装体1の評価結果を表1に示す。 [0053] The evaluation results of the obtained packaging body 1 are shown in Table 1. 実施例1は、袋体2を開封する際に、袋体2の切り口と内容物4とが接触することなく容易に開口部を形成できた。 Example 1, when opening the bag body 2, and can be easily formed an opening portion without contact between the cut and the content of 4 of the bag body 2. また、内容物の取り出し位置は、包装体1を台の上に置いたときに上面側に形成されていたため、台に置いた状態で内容物を取り出すことができ、スナック菓子のように袋体2の開口部よりも小さな形状の内容物であっても、サイドからこぼすことなく、簡便に内容物を取りだすことができた。 Further, the take-out position of the contents, because it was formed on the upper surface side when placing the package 1 on the table, it is possible to take out the contents in a state placed on the platform, the bag as snacks 2 even the contents of the smaller shape than the opening of the, without spilling from the side, it was possible to easily take out the contents. 【0054】実施例2は,袋体2を引き裂き性を有するラミネート反にて形成したため、実施例1の効果に比べてさらに開封方向の安定性に優れ、エンドシール部までほぼ直線状に平行に開封が十分に行われて開口部7が形成されていた。 [0054] Example 2, since the formation in a laminate counter with tearability of the bag body 2, further excellent unsealing direction of stability as compared to the effect of Example 1, substantially parallel to the straight line to the end seal portion opening is sufficiently performed by opening 7 has been formed. しかもこの開口部7は図1に示すように袋体2の上面側に形成されていたため、洋菓子のように壊れやすい内容物4であっても破損することなく、また、スナック菓子のような小さな菓子を溢すことなく、 Moreover, this opening 7 because it was formed on the upper surface side of the bag body 2 as shown in FIG. 1, without even fragile contents 4 as confectionery damaged, also small confectionery such as snack without to overflowing the,
容易に取り出すことができた。 It could be easily taken out. 【0055】また、実施例3は、図3に示すように切り込み5にラベル8が設けられていたため、実施例2よりもさらに開封性に優れ、使用性の評価の高いものであった。 [0055] In Example 3, since the label 8 to 5 notches 3 are provided, further excellent unsealing performance than that of Example 2, was higher evaluation of usability. 比較例1 図7(a)に示すように、ラミネート反に打ち抜き加工を行わず、袋体2に切り込み5を形成する代わりに、接着部3にノッチ部11を形成した。 Comparative Example 1 As shown in FIG. 7 (a), without punching the laminate counter, instead of forming a 5 cuts the bag body 2 to form a notch 11 in the bonding part 3. そして、それ以外は実施例1と同様にして包装体1を作成した。 Then, to create a package 1 and otherwise in the same manner as in Example 1. 【0056】そして、図7(b)に示すようにノッチ部11をきっかけにして袋体2の側部を引き裂いて内容物4を取り出した。 [0056] Then, the contents were taken out 4 tearing the sides of the bag body 2 in the wake of the notch portion 11 as shown in FIG. 7 (b). 得られた評価結果を表1に示す。 The obtained evaluation results are shown in Table 1. 【0057】比較例1は、図7(b)に示すように、包装体1の開封を袋体2のサイドを引裂いて行っているため、開封時に袋体2と内容物4とが接触して、内容物4 [0057] Comparative Example 1, as shown in FIG. 7 (b), the opening of the package 1 since the go tear the sides of the bag body 2, the bag body 2 and the contents of 4 contacts upon opening Te, contents 4
を破損したり、切り口を袋体2の側部の途中までしか形成することができず、内容物を取り出せないことがあった。 Damaged and can not be only formed a cut halfway sides of the bag body 2, there can not be extracted the contents. また、内容物4の取り出しは包装体1のサイドから行なうため、袋体2を傾けて内容物を取り出す必要がある。 Further, the extraction of the contents 4 to perform from the side of the packaging 1, it is necessary to take out the contents by inclining the bag body 2. また、包装体1を台に置いた状態で内容物4を取り出すことは難しく、内容物4をこぼしてしまうことがあった。 Further, it is difficult to take out the contents 4 in a state of placing the package 1 on the base, there can thus spilling the contents 4. 比較例2 図5に示したものと同様の構成の包装体、すなわち図8 Package of the same construction as that shown in Comparative Example 2 FIG. 5, namely 8
(a)に示す包装体1を形成するために、厚み15μm In order to form the packaging body 1 (a), the thickness of 15μm
のナイロンフィルム(ユニチカ社製、エンブレムNC) Of nylon film (manufactured by Unitika Ltd., emblem NC)
と、厚み50μmのLLDPEフィルム(東セロ社製、 And, with a thickness of 50μm LLDPE film (Tohcello Co., Ltd.,
トーセロTUXFCS)とを、接着剤(武田薬品工業社製、タケラック A−515/A−50)を用いてドライラミネーションにより貼り合わせ、ラミネート反を作成した。 The Tosero TUXFCS) and adhesive (manufactured by Takeda Chemical Industries, Ltd., laminated by dry lamination using TAKELAC A-515 / A-50), was prepared a laminate counter. 【0058】このラミネート反に打ち抜き加工を施して切り込み5(図5参照)を形成し、内容物4を充填して、縦(流れ方向)250mm×横170mmの四方体型の包装体1を作成した。 [0058] to form a notch subjected to punching to the laminate fabric 5 (see FIG. 5), filled with content 4, the vertical created the package 1 of the four-way type of (flow direction) 250 mm × horizontal 170mm . 接着部3の接着条件は180 Bonding conditions of the adhesive portion 3 180
℃とし、接着部3の幅d1を10mm、シール強力を5.0kg/15mmとした。 ℃ and was the width d1 of the adhesive portion 3 to 10 mm, the sealing strength between 5.0 kg / 15 mm. 【0059】また、シール部9は、シール条件を180 [0059] In addition, the seal portion 9, the sealing conditions 180
℃とし、シール部9の幅d2を10mm、シール強力を5.0kg/15mmとした。 ℃ and was the width d2 of the sealing portion 9 10 mm, the sealing strength between 5.0 kg / 15 mm. 切り込み5と対向する接着部3とシール部9との間隔d3は20mmとした。 Distance d3 between the adhesive portion 3 and the sealing portion 9 which cuts 5 facing was 20 mm. 【0060】なお、接着部3の接着条件およびシール部9の接着条件は、接着に使用する一対のシールバーの上段のシールバーの温度であり、下段のシールバー温度は125℃、シール時間は1秒、シール圧力は1kg/c [0060] The adhesive condition of the adhesive condition and sealing portions 9 of the adhesive portion 3 is the temperature of the upper sealing bar of a pair of seal bars to be used for bonding, the lower seal bar temperature is 125 ° C., sealing time is 1 second, sealing pressure is 1 kg / c
2である。 a m 2. 【0061】内容物4には、トレー13に焼きおにぎりが6個入っている焼きおにぎり(日本水産社製)を用いた。 [0061] The contents of 4, using a rice ball shrink rice balls stamped on the tray 13 is in six (manufactured by Nippon Fisheries Co., Ltd.). そして、上記の試験法に従い、開封性を調べ、また、600Wの電子レンジで加熱処理し、電子レンジへの適正を評価した。 Then, according to the above test method to examine the openability, also heat-treated in a microwave oven of 600W, to evaluate the adequacy of the microwave oven. 【0062】得られた包装体1の評価を表2に示す。 [0062] Evaluation of the resulting package 1 is shown in Table 2. 【0063】 【表2】 [0063] [Table 2] 比較例2は、シール部9のシール強力が5.0kg/1 Comparative Example 2, strong sealing of the sealing portion 9 is 5.0 kg / 1
5mmとシール強力が強かったため、密封性は確保されているものの、切り込み5を把手にしてシール部9を通過して開封するのは困難であった。 5mm and a seal for powerful was strong, although sealability is secured, it is difficult to open through the seal portion 9 with a 5 cut in the handle. 実施例4 接着部3とシール部9のシール強力がともに比較例2の約1/3となるようにシール条件を130℃とした。 The sealing conditions as Example 4 seal bonding portion 3 and the sealing portion 9 powerful are both about 1/3 of the Comparative Example 2 was set to 130 ° C.. そして、それ以外は、比較例2と同様にして、包装体1を作成した。 And, otherwise, in the same manner as in Comparative Example 2 to prepare a package 1. 得られた包装体1の評価を表2に示す。 Evaluation of the resulting package 1 shown in Table 2. 実施例5ラミネート反を作成するに際し、LLDPEの代わりに厚み50μmのイージーピール性のフィルム(東セロ社製、特殊シーラントフィルム トーセロCMPS Upon creating the Example 5 laminate counter, easy peel of the film having a thickness of 50μm, instead of LLDPE (Tohcello Co., special sealant film Tosero CMPS
017C)を用いた。 017C) was used. 袋体2を形成する接着部3の接着強力を0.8kg/15mmとし、シール部9のシール強力を0.8kg/15mmとした。 Strong adhesion of the adhesive portion 3 which forms a bag body 2 and 0.8 kg / 15 mm, and a strong seal of the seal portion 9 and 0.8 kg / 15 mm. そしてそれ以外は比較例2と同様にして包装体1を作成した。 And it was prepared otherwise in the package 1 in the same manner as in Comparative Example 2. 【0064】得られた評価結果を表2に示す。 [0064] obtained evaluation results are shown in Table 2. 実施例6 シール部9に厚み50μmのイージーピール性のフィルム(東セロ社製、特殊シーラントフィルム トーセロC Easy peel of the film having a thickness of 50μm in Example 6 the seal portion 9 (Tohcello Co., special sealant film Tosero C
MPS 017C)を、切り込み5の形成側がイージーピール面となるように挿入した。 The MPS 017C), forming side of the notch 5 is inserted so that the easy-peel surface. このシール部9のシール強力は0.9kg/15mmとした。 Seal strength of the seal portion 9 was 0.9kg / 15mm. そしてそれ以外は比較例2と同様にして包装体1を作成した。 And it was prepared otherwise in the package 1 in the same manner as in Comparative Example 2. 【0065】得られた評価結果を表2に示す。 [0065] obtained evaluation results are shown in Table 2. 実施例7 シール部9のシール強力が比較例2の約1/2となるようにシール条件を150℃とした。 Strong seals Example 7 sealing portion 9 has a 0.99 ° C. The sealing conditions to be about 1/2 of the Comparative Example 2. そしてそれ以外は、 And otherwise,
比較例2と同様にして包装体1を作成した。 It created the package 1 in the same manner as in Comparative Example 2. 【0066】得られた評価結果を表2に示す。 [0066] obtained evaluation results are shown in Table 2. 実施例8 シール部9のシール強力が比較例2の約1/3となるようにシール条件を130℃とした。 Strong seals of Examples 8 sealing portion 9 has a 130 ° C. The sealing conditions to be about 1/3 of the Comparative Example 2. そしてそれ以外は、 And otherwise,
比較例2と同様にして包装体1を作成した。 It created the package 1 in the same manner as in Comparative Example 2. 【0067】得られた評価結果を表2に示す。 [0067] obtained evaluation results are shown in Table 2. 実施例9 シール部9のシール強力が実施例5の約1/2となるようにシール条件を150℃とした。 Strong seals Example 9 sealed portion 9 was 0.99 ° C. The sealing conditions so that about 1/2 of Example 5. そしてそれ以外は、 And otherwise,
実施例5と同様にして包装体1を作成した。 It created the package 1 in the same manner as in Example 5. 【0068】得られた評価結果を表2に示す。 [0068] obtained evaluation results are shown in Table 2. 実施例10 シール部9のシール幅を2倍にした以外は実施例8と同様にして包装体1を作成した。 Created the package 1 except that the seal width of Example 10 seal section 9 doubles in the same manner as in Example 8. 【0069】得られた評価結果を表2に示す。 [0069] The evaluation results obtained are shown in Table 2. 実施例11 電子レンジによる加熱処理を行う前に、あらかじめ切り込み5からなる把手6を持って袋体2をシール部9を通過するところまで開封した。 Before performing the heat treatment according to Example 11 microwave oven opening the bag body 2 to the point where it passes through the seal portion 9 with the handle 6 consisting of pre-cut 5. そしてそれ以外は実施例5 And the embodiment except that 5
と同様にして包装体1の評価を行った。 It was evaluated in the packaging body 1 in the same manner as in. 【0070】得られた評価結果を表2に示す。 [0070] obtained evaluation results are shown in Table 2. 実施例12 比較例2で作成したラミネート反を用いて、図2(h) Using a laminated anti-created in Example 12 Comparative Example 2, FIG. 2 (h)
に示すように袋体2の中央部に切り込み加工を施し一対の切り込み5a,5bを形成した。 A pair of notches 5a subjected to rebated to the central portion of the bag body 2 as shown in, to form 5b. そしてこの切り込み5a,5bおよびその周辺部分を覆うように袋体2の内面側に実施例5で使用したイージーピール性のシーラントからなる複合フィルムを、切り込み5とのシール面がイージーピール面となるように挿入して、図6(i)に示す包装体1を作成した。 And this notch 5a, 5b and a composite film thereof made of easily peelable sealant used in Example 5 on the inner surface side of the bag body 2 so as to cover the peripheral portion, the sealing surface with the cut 5 becomes easy peel surface insert as to prepare a package 1 shown in FIG. 6 (i). そしてそれ以外は比較例2と同様にして包装体1の評価を行った。 And otherwise we evaluated of the package 1 in the same manner as in Comparative Example 2. 【0071】得られた評価結果を表2に示す。 [0071] obtained evaluation results are shown in Table 2. 実施例4 Example 4
は、シール部9のシール強力を比較例2の約1/3としたため、切り込み5を把手にして包装体1を開封する際に、シール部9の開封も行うことができた。 Because it has a strong seal of the seal portion 9 with approximately 1/3 of the Comparative Example 2, upon opening the package 1 by the 5 cut in the handle and can be performed even unsealing of the seal portion 9. また、シール部9を設けることで密封性も付与されていた。 Also it has been granted sealability by providing a seal 9. 但し、 However,
電子レンジ適正については、シール部9と接着部3の強度が同じであるため、シール部9が開口して、切り込みが袋体内部の空気の吹き出し口になる前に接着部3も開口(破袋)してしまい、やや劣るものであった。 The microwave oven proper, since the strength of the seal portion 9 and the adhesive portion 3 are the same, the sealing portion 9 is opened, also the adhesive portion 3 before the incision is outlet air bag body opening (dashed bag), so, were those somewhat inferior. 【0072】実施例5は、シール部9のシール強力が0.8kg/15mmと低いため、実施例4と同様に、 [0072] Example 5, since a strong seal of the seal portion 9 is low and 0.8 kg / 15 mm, in the same manner as in Example 4,
切り込み5を把手にしてシール部9を容易に開封することができた。 A sealing portion 9 which cuts 5 in the handle could be easily opened. なお、電子レンジ適正については、シール部9と接着部3の強度が同じであるため、シール部9が開口して、切り込みが袋体内部の空気の吹き出し口になる前に接着部3も開口(破袋)してしまうため電子レンジの使用は困難であった。 Note that the microwave properly, because the strength of the seal portion 9 and the adhesive portion 3 are the same, the sealing portion 9 is opened, also the adhesive portion 3 before the incision is outlet air bag body opening the use of microwave ovens for results in (breakage) was difficult. 【0073】実施例6は、シール部9のシール強力が0.8kg/15mmと低いため、切り込み5を把手にして、シール部9を容易に開封することができた。 [0073] Example 6, since a strong seal of the seal portion 9 is low and 0.8 kg / 15 mm, and a 5 cut in the handle, it was possible to open the sealing portion 9 easily. また、電子レンジ適正についても、接着部3が5.0kg In addition, for the microwave oven proper, the adhesive part 3 5.0kg
/15mmとシール部9よりもシール強力が強いため、 / 15mm and for strong powerful seal than the seal portion 9,
電子レンジでの1分の加熱によりシール部9のみが開口して、切り込み5が吹き出し口となって袋体内部の空気を抜くことができ、包装体1を破袋させることなく、内容物を加熱することができ、優れた電子レンジ適正を有するものとなった。 Only the seal portion 9 by heating for 1 minute in a microwave oven is opened, the cut 5 becomes the outlet can deflate the bag body portion, the packaging 1 without breakage and the contents can be heated, it was to have a proper excellent microwave. 【0074】実施例7は、シール部9のシール強力を比較例2の約1/2としたため、切り込み5を把手にして、シール部9を開封することができた。 [0074] Example 7, because of the strong seal of the seal portion 9 with about 1/2 of the Comparative Example 2, and the 5 cut in the handle, it was possible to open the sealing portion 9. また、実施例2と同様の開封性を有するとともに、実施例2には備わっていなかった密封性も確保されており、実施例2よりもさらに優れた包装体1が得られた。 Furthermore, addition to the same opening property as in Example 2, the sealing property was not provided in Example 2 is also ensured, even more excellent package 1 than in Example 2 were obtained. また、電子レンジ適正については、シール部9のシール強力が接着部3のシール強力の約1/2と弱いため、電子レンジでの3分以内での加熱により、シール部9のみが開口して切り込み5が吹き出し口となり、包装体1を破袋させることなく内容物を加熱でき、電子レンジで好適に使用できた。 Also, the microwave oven proper, because strong seal of the seal portion 9 is weak and about 1/2 of a strong seal adhesion portion 3, by heating within 3 minutes in a microwave oven, only the seal portion 9 is opened cut becomes 5 outlet, the package 1 can heat the contents without breakage it could be suitably used in a microwave oven. 【0075】実施例8は、シール部9のシール強力を比較例の約1/3とすることで、切り込み5を把手にしてシール部9を開封することができた。 [0075] Example 8, by a strong seal of the seal portion 9 with approximately 1/3 of the Comparative Example, it was possible to open the seal portion 9 with a 5 cut in the handle. また、密封性も確保できた。 In addition, it was also able to ensure sealing performance. また、電子レンジ適正については、シール部9のシール強力が接着部3のシール強力の約1/3と弱いため、電子レンジでの1分以内の加熱によりシール部9のみが開口して切り込み5が吹き出し口となり、包装体1を破袋させることなく、内容物を加熱することができ、電子レンジで好適に使用できるものであった。 Also, the microwave oven proper, because strong seal of the seal portion 9 is weak and about one-third of a strong seal adhesion portion 3, cut open only the seal portion 9 by heating within one minute in a microwave oven 5 becomes that outlet, without breakage of the packaging 1, it is possible to heat the contents was achieved, can be suitably used in a microwave oven. 【0076】実施例9は、シール部9のシール強力を実施例5の約1/2としたため、切り込み5を把手にしてシール部9を開封することができるものであった。 [0076] Example 9, since a strong seal of the seal portion 9 was about 1/2 of Example 5, it was capable of opening the seal portion 9 with a 5 cut in the handle. また、密封性も確保されており、レトルト処理やボイル処理も好適に行えるものであった。 Further, sealability is also ensured, retort treatment or boil treatment was also intended to suitably performed. また、電子レンジ適正については、シール部9のシール強力が接着部3のシール強力の約1/2と弱いため、電子レンジでの1分以内の加熱によりシール部9のみが開口して切り込みが吹き出し口となり、包装体1を破袋させることなく、内容物を加熱することができ、電子レンジで好適に使用できた。 Also, the microwave oven proper, because strong seal of the seal portion 9 is weak and about 1/2 of a strong seal adhesion portion 3, the cut and only the seal portion 9 is opened by heating within one minute in a microwave oven is becomes outlet, without breakage of the packaging 1, it is possible to heat the contents, it could be suitably used in a microwave oven. 【0077】実施例10は、実施例8と同様に、シール部9のシール強力を比較例2の約1/3としたが、シール幅を2倍にしたため、電子レンジでの加熱によるシール部9の開口時間を1分から3分以内とすることができ、実施例8と同様に電子レンジで好適に使用できるものであった。 [0077] Example 10, similarly as in Example 8, was a strong seal of the seal portion 9 with approximately 1/3 of the Comparative Example 2, since the seal width is doubled, the sealing portion by heating in a microwave oven 9 of the opening time can be within 3 minutes minutes 1 was achieved, can be suitably used in the same electronic oven as in example 8. このようにシール部9のシール幅を広くすることで、電子レンジ加熱によるシール部9の開口時間を長くすることができ、さらに耐圧強度も高まるため、 Since By thus widening the sealing width of the sealing portion 9, which can increase the opening time of the seal portion 9 by microwave heating, also increased further pressure resistance,
ボイル処理やレトルト処理を行う際の破袋の危険性を低減でき、幅広い分野で好適に使用できる。 Reduces the risk of breakage when performing boiling treatment or retort treatment, it can be suitably used in a wide range of fields. 【0078】実施例11は、電子レンジによる加熱処理を行う前に、あらかじめ切り込み5からなる把手をもって袋体2をシール部9を通過するところまで開封したため、電子レンジ加熱による内部圧力の上昇を防ぐことができ、従来は破袋して使用できなかった包材に対しても電子レンジで好適に使用できる。 [0078] Example 11, before performing the heat treatment by microwaves, for which opening the bag body 2 to the point where it passes through the seal portion 9 with a handle made of pre-cut 5, prevents an increase in internal pressure due to microwave heating it can conventionally be suitably used in a microwave oven with respect to the packaging material that could not be used to breakage. 【0079】実施例12は、イージーピール性のシーラントからなる複合フィルムを、切り込む5とのシール面がイージーピール面となるように挿入したため、シール部9のシール強力が低くなり、切り込み5を把手にしてシール部9を開封することができ、電子レンジを使っての内容物の加熱を好適に行えるものであった。 [0079] Example 12, since the composite film consisting of easily peelable sealant, sealing of a 5 cutting inserts such that the easy-peel surface, strong sealing of the seal portion 9 is lowered, the 5 cut handle can open a seal 9 in the was achieved, suitably perform the heating of the contents of with the microwave. 【0080】 【発明の効果】本発明によれば、袋体の一部に切り込みが形成され、この切り込みは、前記袋体を切り裂いて開封を容易にするための把手となるよう構成することで、 [0080] According to the present invention, cut in a portion of the bag body is formed, the cut is, by configuring such that a handle for facilitating opening tearing through the bag body ,
袋体と内容物とが接触することなく容易に包装体を開封できる。 It can be opened easily package without contact between the bag and contents. そして、切り込みが、前記袋体の前面(上面側)にある場合、台に置いたままで、内容物を溢すことなく簡便に取りだすことができる。 Then, incision, if the front (upper side) of the bag, while at the platform, the contents can easily take out it without 溢Su. また、加熱による内容物の圧力上昇は、この切り込みによって逃がすことができるため、破袋することがなくなり、例えば電子レンジ調理などの加熱処理にも好適に使用できる。 The pressure increase of the contents by heating, it is possible to escape by this notch, prevents the breakage, for example can be suitably used in the heat treatment, such as microwave cooking. 【0081】従って、本発明の包装体は、ウエハースやクッキーなどのような壊れやすい菓子類、スナック菓子やおかきのような小さな菓子類、あるいはトレー入りの冷凍食品のピザや焼きおにぎり、珍味や土産菓子などの食品用途の包装体として好適に使用できる。 [0081] Thus, the package of the present invention, fragile confectionery, such as wafers, cookies, snacks and small confectionery such as crackers or tray containing the frozen food of pizza and grilled rice balls,, delicacies and souvenirs confectionery It can be suitably used as a packaging material for food applications, such as. また、これらのうち、冷凍食品のように加熱を必要とする場合にも、好適に使用でき、さらに、密封性と耐圧強度がある程度確保されている場合には、真空包装或いは脱気包装された固形あるいは水物のレトルトあるいはボイル殺菌処理にも適用可能である。 Further, among these, in the case that requires heating as frozen foods, it can be preferably used, further, when the sealing performance and pressure resistance is secured to some extent has been vacuum packed or degassing packaging in retort or boiling sterilization solid or anhydride can be applied. また、応用展開して、電子部品等の工業用途(トレー入りも含め)、医薬品の器具用途(手術用の器具セット、トレー入りも含め)などの包装体としても使用できる。 Also, the application and development, (including trays containing) industrial applications such as electronic components, pharmaceuticals instrument applications (instrument set for surgery, including a tray filled) can also be used as a packaging material such as.

【図面の簡単な説明】 【図1】本発明の実施の形態における開封前と開封後の包装体の斜視図である。 Is a perspective view of the package after opening the front opening in the embodiment of the BRIEF DESCRIPTION OF THE DRAWINGS [Figure 1] present invention. 【図2】同実施の形態における切り込みの形状と配置を説明する平面図である。 2 is a plan view illustrating the arrangement and shape of the notch in the embodiment. 【図3】切り込みおよびその周囲を覆うラベルを設けた包装体の開封前と開封後の斜視図である。 [Figure 3] cuts and is a perspective view before and after the opening unsealing of the provided package as label covering the periphery thereof. 【図4】同実施の形態におけるラベルの構成を説明する模式図である。 4 is a schematic view for explaining the label configuration in the embodiment. 【図5】切り込みと内容物を収納する収納部との間にシールを設けた包装体の平面図とA−B線に沿う断面図である。 Is a sectional view taken along the plan view and A-B line of the seal provided the package between the Figure 5 cut and content storage unit for storing a. 【図6】同実施の形態におけるシールの形態を説明する模式図である。 6 is a schematic view illustrating a seal in the form in the embodiment. 【図7】比較例で用いた包装体の開封前と開封後の斜視図である。 7 is a perspective view after opening the front opening of the package used in Comparative Example. 【図8】図5に示す包装体にトレー入りの内容物を収納した包装体の開封前と開封後の断面図である。 8 is a cross-sectional view after opening the front opening of the package accommodating the tray containing the contents of the packaging body shown in FIG. 【図9】従来の包装体の一般的な形態および開封方法を説明する模式図である。 9 is a schematic view illustrating a general form and opening method of the conventional package. 【符号の説明】 1 包装体2 袋体2a 袋体上面2b 袋体背面3 接着部4 内容物5 切り込み6 把手7 開口部8 ラベル9 シール部10 収納部13 トレー [EXPLANATION OF SYMBOLS] 1 package 2 bag 2a bag top 2b bag rear third adhesive portion 4 contents 5 incisions 6 grip 7 opening 8 label 9 sealing portion 10 housing 13 tray

───────────────────────────────────────────────────── フロントページの続き (72)発明者 鈴木 正敏 愛知県名古屋市守山区新守山2010番地Fターム(参考) 3E064 AA09 BA26 BA29 BA30 BA36 BA38 BA54 BB03 BC20 EA30 FA01 HA02 HD02 HE03 HM03 HN05 HP02 HP04 HP05 HT07 3E067 AA11 AB01 AB16 BA12A BB15A BB16A BB18A BB25A BC03A CA30 EA08 EA09 EA11 EB06 EB10 EB11 EB22 EE04 FA01 FC01 GB01 GD10 3E086 AC15 AC16 AC18 AD01 BA04 BA15 BA33 BB90 CA01 ────────────────────────────────────────────────── ─── front page of the continuation (72) inventor Masatoshi Suzuki Nagoya, Aichi Prefecture Moriyama-ku, Shinmoriyama 2010 address F-term (reference) 3E064 AA09 BA26 BA29 BA30 BA36 BA38 BA54 BB03 BC20 EA30 FA01 HA02 HD02 HE03 HM03 HN05 HP02 HP04 HP05 HT07 3E067 AA11 AB01 AB16 BA12A BB15A BB16A BB18A BB25A BC03A CA30 EA08 EA09 EA11 EB06 EB10 EB11 EB22 EE04 FA01 FC01 GB01 GD10 3E086 AC15 AC16 AC18 AD01 BA04 BA15 BA33 BB90 CA01

Claims (1)

  1. 【特許請求の範囲】 【請求項1】 袋体の一部に切り込みが形成され、この切り込みは、前記袋体を引き裂いて開封を容易にするための把手となることを特徴とする包装体。 Claims We claim: 1. A cut part of the bag body is formed, the cut can be packaged body characterized in that a handle for facilitating tearing open the bag body. 【請求項2】 切り込みが包装体を平らに置いたときに上面側となる位置に形成されていることを特徴とする請求項1記載の包装体。 Wherein notches package according to claim 1, characterized in that it is formed on the upper surface side and a position when laid flat the package. 【請求項3】 切り込みが複数形成されていることを特徴とする請求項1または請求項2に記載の包装体。 3. A notch packaging body according to claim 1 or claim 2, characterized in that formed in plural. 【請求項4】 袋体の一部又は全部が合成樹脂フィルムで形成されていることを特徴とする請求項1から請求項3のいずれか1項に記載の包装体。 4. A package as claimed in claim 1 in which a portion of the bag or the whole, characterized in that it is formed of a synthetic resin film to any one of claims 3. 【請求項5】 合成樹脂フィルムが直線引き裂き性を有するフィルムであることを特徴とする請求項4記載の包装体。 5. The package of claim 4, wherein the synthetic resin film is characterized in that it is a film having a linear tearability. 【請求項6】 合成樹脂フィルムがイージーピール性を有するフィルムであることを特徴とする請求項5記載の包装体。 6. The package of claim 5, wherein the synthetic resin film is characterized in that it is a film having easy peel properties. 【請求項7】 切り込み及びその周囲の袋体の部分をシールするラベルを有し、このラベルは切り込みとともに把手となる請求項1から請求項6のいずれか1項に記載の包装体。 7. A notch and has a label which seals the portion of the bag body surrounding the package as claimed in claim 1 the label is to be handle with cuts to any one of claims 6. 【請求項8】 内容物の加熱時の圧力上昇を切り込みから逃すことができることを特徴とする請求項1から請求項7までのいずれか1項に記載の包装体。 8. A packaging according to any one of claims 1, characterized in that it is possible to escape from the notch of the pressure rise during heating of the contents to claim 7. 【請求項9】 切り込みと袋体における内容物を収納する収納部との間にシール部が設けられていることを特徴とする請求項1から請求項8までのいずれか1項に記載の包装体。 9. notch and packaging according to any one of the seal portion is provided between the housing part for accommodating the contents from claim 1, wherein up to claim 8 in bag body. 【請求項10】 シール部のシール強度が、袋体を形成するために接着されている接着部の強度より低いことを特徴とする請求項9記載の包装体。 10. A seal strength of the seal portion, package of claim 9, wherein the lower strength of the adhesive portion that is bonded to form a bag. 【請求項11】 シール部にイージーピール性のシーラントフィルムあるいはこのイージーピール性のシーラントフィルムを用いた複合フィルムを用いてシールしたことを特徴とする請求項9または請求項10に記載の包装体。 11. The packaging body according to claim 9 or claim 10, characterized in that sealed using the composite film using an easy peeling property of the sealant film or the easily peelable sealant film to the seal portion. 【請求項12】 内容物の加熱時の圧力上昇によりシール部の少なくとも一部が剥離し、さらに、この上昇した圧力を切り込みから逃すことができることを特徴とする請求項9から請求項11までのいずれか1項に記載の包装体。 12. At least a portion of the seal portion is peeled off by a pressure rise during heating of the contents, further, from the claims 9 to claim 11, characterized in that it is possible to escape from the notch of the increased pressure package of any one. 【請求項13】 切り込みから袋体の一部をシール部を通過する所まで引き裂いて加熱処理することができるように構成されたことを特徴とする請求項9から請求項1 13. The method of claim part of the bag from the claim 9, characterized in that it is configured to be able to heat treatment tear until it passes through the seal portion from the notch 1
    1までのいずれか1項に記載の包装体。 Packaging according to any one of up to 1.
JP2001208632A 2001-07-10 2001-07-10 Packaging body Pending JP2003026224A (en)