JP2005089490A - 再剥離性粘着テープ - Google Patents
再剥離性粘着テープ Download PDFInfo
- Publication number
- JP2005089490A JP2005089490A JP2003320718A JP2003320718A JP2005089490A JP 2005089490 A JP2005089490 A JP 2005089490A JP 2003320718 A JP2003320718 A JP 2003320718A JP 2003320718 A JP2003320718 A JP 2003320718A JP 2005089490 A JP2005089490 A JP 2005089490A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- sensitive adhesive
- adhesive tape
- parts
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
【解決手段】 熱可塑性樹脂を一軸延伸して得た線状体を交差させて形成した布状基材の少なくとも片面に
(A)(a)アルキル基の炭素数が4〜12の(メタ)アクリル酸アルキルエステル65〜99.9重量部、(b)ヒドロキシル基含有単量体0.1〜8重量部、(c)その他の単量体0〜27重量部を乳化重合して得られる、共重合体のガラス転移点が−20〜−75℃の共重合体エマルジョン100重量部(固形分換算)に対し
(B)軟化点が100〜170℃のロジン系粘着付与樹脂1〜30重量部、
(C)リン酸エステル系界面活性剤0.01〜5重量部ならびに
(D)ポリイソシアネート系架橋剤0〜5重量部
を含有する粘着剤組成物層が積層されてなる再剥離性粘着テープ。
【選択図】 図1
Description
また、上記のような要求を満たす粘着テープとしては、例えば、剥離工程前に紫外線等を照射して接着力を低下させるもの、或いは、マイクロカプセル化した発泡剤を粘着剤中に含有させた粘着テープを使用し、剥離工程前に加熱して発泡させることにより接着面積を低減して接着力を低下させるものなどが提案されている。
しかしながら、これらの粘着性を制御する粘着テープはコストの大幅な上昇を招き、加えて紫外線照射装置などの設置による設備コストの増大や、各工程毎の煩雑な工程管理が必要となり、粘着テープ、ひいては最終製品の価格を上昇させる要因となる。
(A)(a)アルキル基の炭素数が4〜12の(メタ)アクリル酸アルキルエステル65〜99.9重量部、(b)ヒドロキシル基含有単量体0.1〜8重量部、(c)その他重合可能な単量体0〜27重量部、{ただし、(a)+(b)+(c)=100重量部}を乳化重合することにより得られる、共重合体のガラス転移点が−20℃〜−75℃の共重合体エマルジョン100重量部(固形分換算)に対し
(B)軟化点が100℃〜170℃のロジン系粘着付与樹脂1〜30重量部、
(C)リン酸エステル系界面活性剤0.01〜5重量部ならびに
(D)ポリイソシアネート系架橋剤0〜5重量部
を含有するエマルジョン型粘着剤組成物層が積層されてなることを特徴とする粘着テープを提供するものである。
また、本発明は、布状基材が線状体を織成、編成、又は、からみ織することによって得られたものである上記の粘着テープ、及び、布状基材が線状体を一方向に並列し、その上に他の線状体を交差するように配列し、その交点を結合することによって得られたものである上記の粘着テープを提供するものである。
さらに、本発明は、線状体がポリオレフィンからなる上記の粘着テープ、布状基材の片面又は両面にポリオレフィンからなる薄層が積層されてなる上記の粘着テープを提供するものである。
また、JIS Z−0237粘着テープ・粘着シート試験方法10.4項に規定される180度引きはがし粘着力の測定によるステンレス板に対する粘着力が、初期値が5〜15N/25mmで、かつ貼り付け3ヶ月経過後の値が初期値の1.0〜1.5倍である請求項1〜5のいずれかに記載の粘着テープ、およびトルエン、キシレン、メチルメタアクリレート、ブチルアクリレート、2−エチルヘキシルアクリレートの含有量がそれぞれ10μg/g(粘着剤1gに対する量)以下の上記の粘着テープを提供するものである。
このような布状基材の厚さは50〜300μmが好ましく、さらに好ましくは80〜200μmである。
また、布状基材3の反対面、図5において上面には、ポリオレフィン層5を積層することができ、図5には記載されていないが、さらに、金属箔層6を積層することも可能である。この場合、金属箔層6は布状基材3の上に接着剤を介して、ポリオレフィン層の下に積層される。
(A)(a)アルキル基の炭素数が4〜12の(メタ)アクリル酸アルキルエステル65〜99.9重量部、(b)ヒドロキシル基含有単量体0.1〜8重量部、(c)その他重合可能な単量体0〜27重量部、{ただし、(a)+(b)+(c)=100重量部}を乳化重合することにより得られる、共重合体のガラス転移点が−20℃〜−75℃の共重合体エマルジョン100重量部(固形分換算)に対し
(B)軟化点が100℃〜170℃のロジン系粘着付与樹脂1〜30重量部、
(C)リン酸エステル系界面活性剤0.01〜5重量部ならびに
(D)ポリイソシアネート系架橋剤0〜5重量部
を含有することを特徴とするエマルジョン型粘着剤組成物層が形成される。
本発明において、(a)アルキル基の炭素数が4〜12の(メタ)アクリル酸アルキルエステルとしては、例えばブチル(メタ)アクリレート、イソブチル(メタ)アクリレート、t−ブチル(メタ)アクリレート、ペンチル(メタ)アクリレート、イソアミル(メタ)アクリレート、ヘキシル(メタ)アクリレート、ヘプチル(メタ)アクリレート、オクチル(メタ)アクリレート、イソオクチル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレート、ノニル(メタ)アクリレート、イソノニル(メタ)アクリレート、デシル(メタ)アクリレート、イソデシル(メタ)アクリレート、ウンデシル(メタ)アクリレート、ドデシル(メタ)アクリレートなどの直鎖または分岐脂肪族アルコールのアクリル酸エステルおよび対応するメタクリル酸エステルなどを挙げることができる。これらは、単独であるいは2種類以上併用して用いることができる。なかでも、ブチル(メタ)アクリレート、2−エチルヘキシル(メタ)アクリレートが好ましい。
スチレン、α−メチルスチレン、4−メチルスチレン、2−メチルスチレン、3−メチルスチレン、4−メトキシスチレン、2−ヒドロキシメチルスチレン、4−エチルスチレン、4−エトキシスチレン、3,4−ジメチルスチレン、3,4−ジエチルスチレン、2−クロロスチレン、3−クロロスチレン、4−クロロ−3−メチルスチレン、4−t−ブチルスチレン、2,4−ジクロロスチレン、2,6−ジクロロスチレン、1−ビニルナフタレンなどの芳香族ビニル単量体;
アクリル酸、メタクリル酸、エチルアクリル酸、イタコン酸、マレイン酸、無水マレイン酸、マレイン酸モノエステル、クロトン酸などのα,β−不飽和カルボン酸単量体;
酢酸ビニルなどのビニル系単量体;
ジビニルベンゼンなどの上記以外の多官能性単量体;
4−(メタ)アクリロイルオキシ−2,2,6,6−テトラメチルピペリジン、4−(メタ)アクリロイルアミノ−2,2,6,6−テトラメチルピペリジン、4−(メタ)アクリロイルオキシ−1,2,2,6,6−ペンタメチルピペリジンなどのピペリジン系モノマー;
そのほかジカプロラクトンなどが挙げられる。
これらは、必要に応じて用いられ、単独であるいは二種以上を併用して使用することができる。
以上の乳化剤は、1種単独であるいは2種以上を併用することができる。
ここで、(B)ロジン系粘着付与樹脂の軟化温度は、100〜170℃、好ましくは105〜160℃、さらに好ましくは110〜150℃である。軟化温度が100℃未満であると、粘着付与樹脂の軟化点、凝集力が向上せず、高温時の粘着保持力が維持できない。一方、軟化温度が170℃を超えるものは、現在のところ、エステル化反応時に粘度が上昇し、作製できない。(B)ロジン系粘着付与樹脂は、1種単独で使用することも、あるいは2種以上を混合して用いることもできる。なお、以上の(B)ロジン系粘着付与樹脂のほかに、必要に応じて、テルペン樹脂系、石油樹脂系、クマロン・インデン樹脂などを配合することもできる。
このような界面活性剤の使用量は、共重合体エマルジョン(固形分換算)100重量部に対して0.01〜5重量部、好ましくは0.02〜4重量部、さらに好ましくは0.03〜3重量部である。ここで、0.01重量部未満では再剥離性が不充分であり、一方、5重量部を超えると経時的に粘着力が低下する。
このような架橋剤の配合量は、共重合体エマルジョン100重量部(固形分換算)に対して0〜5重量部である。架橋剤は、粘着力のコントロールのために用いられるものであり、必要に応じて配合される。5重量部を超えると、粘着力が低下する。好ましくは、0〜3重量部である。
このような粘着剤組成物には、従来公知のキレ−ト化合物、メラミン化合物、エポキシ化合物、アジリジン化合物などの架橋機能を有する化合物、顔料、可塑剤、(B)以外の粘着付与剤、保護コロイド剤、消泡剤、防腐剤、防カビ剤、湿潤剤、アルカリ性化合物、増粘剤、酸化防止剤、紫外線吸収剤、などの添加物を配合することができる。
<初期粘着力>
360番の耐水研磨紙で長さ方向に研磨したSUS304鋼板に粘着テープを貼り付け、試験片とする。23℃、相対湿度50%の雰囲気中に20分静置した上記の試験板を用い、JIS Z−0237粘着テープ・粘着シート試験方法10.4項に規定される180度引きはがし粘着力の測定にて、オートグラフを用い試料幅25mm、引張速度300mm/minで引きはがしたときの抗力を求める。
<経時粘着力>
上記初期粘着力測定と同様にしてSUS304鋼板に粘着テープを貼り付け、試験片とする。23℃、相対湿度50%の雰囲気中に3ヶ月静置した上記の試験板を用い、上記初期粘着力と同様な方法で測定して抗力を求める。
以下に実施例を挙げて説明するが、本発明は本実施例および以下の実施例に限定解釈されるものではない。
エマルジョン型粘着剤;
2−エチルヘキシルアクリレート90重量部、メチルメタアクリレート5重量部、ヒドロキシエチルアクリレート5重量部を主成分とする単量体を乳化重合して共重合体エマルジョンを製造した後、共重合エマルジョン100重量部(固形分換算)に対してロジン系粘着付与樹脂スーパーエステルE726(荒川化学(株)製)を固形分基準で10重量部、リン酸エステル界面活性剤JAS101(竹本油脂(株)製)を固形分基準で0.1重量部を配合し、全固形分55重量%、粘度10,000mPa・sになるように調整した。
a.初期粘着力
360番の耐水研磨紙で長さ方向に研磨したSUS304鋼板に粘着テープを貼り付け、試験片とする。23℃、相対湿度50%の雰囲気中に20分静置した上記の試験板を用い、JIS Z−0237粘着テープ・粘着シート試験方法10.4項に規定される180度引きはがし粘着力の測定にて、オートグラフを用い試料幅25mm、引張速度300mm/minで引きはがしたときの抗力を求める。
上記初期粘着力測定と同様にしてSUS304鋼板に粘着テープを貼り付け、試験片とする。この試験片を23℃、相対湿度50%の雰囲気中に3ヶ月静置したものについて、上記初期粘着力と同様な方法で測定して抗力を求める。初期粘着力に対する比率を求め、評価結果を表1に示した。
上記aの初期粘着力測定で作成した試験片を70℃×3日間養生後、上記aに示した条件で引き剥がし後、SUS表面ののり残り面積を目視で評価した。
◎:のり残り面積20%未満
○:のり残り面積20以上50%未満
×:のり残り面積50%以上
幅5cm、長さ50cmの粘着テープを容量50mlのバイアル瓶に入れ、100℃で30分加熱後、気相部を1ml採取しガスクロ/質量分析(GC/MS)で定量する。
上記基材のコロナ放電処理面に、下記のようにして得られた本発明のエマルジョン型粘着剤を塗布厚み40μmとなるように塗布した。このようにして得られた再剥離性粘着テープについて、実施例1と同様に初期粘着力、経時粘着力、再剥離性を評価した。結果は表1の通りであった。
2−エチルヘキシルアクリレート90重量部、メチルメタアクリレート5重量部、ヒドロキシエチルアクリレート5重量部を主成分とする単量体を乳化重合して共重合体エマルジョンを製造した後、共重合エマルジョン100重量部(固形分換算)に対してロジン系粘着付与樹脂スーパーエステルE726(荒川化学(株)製)を固形分基準で10重量部、リン酸エステル界面活性剤JAS101(竹本油脂(株)製)を固形分基準で0.02重量部、およびポリイソシアネート系架橋剤アクアネート110(日本ポリウレタン(株)製)を0.2重量部を配合し、全固形分55重量%、粘度11,000mPa・sになるように調整した。
2.線状体
3.布状基材
4.粘着剤層
5.ポリオレフィン層
6.金属箔
7.接着剤層
8.剥離剤層
Claims (7)
- 熱可塑性樹脂を一軸延伸して得られた線状体を交差せしめて形成した布状基材の少なくとも片面に
(A)(a)アルキル基の炭素数が4〜12の(メタ)アクリル酸アルキルエステル65〜99.9重量部、(b)ヒドロキシル基含有単量体0.1〜8重量部、(c)その他重合可能な単量体0〜27重量部、{ただし、(a)+(b)+(c)=100重量部}を乳化重合することにより得られる、共重合体のガラス転移点が−20℃〜−75℃の共重合体エマルジョン100重量部(固形分換算)に対し
(B)軟化点が100℃〜170℃のロジン系粘着付与樹脂1〜30重量部、
(C)リン酸エステル系界面活性剤0.01〜5重量部ならびに
(D)ポリイソシアネート系架橋剤0〜5重量部
を含有するエマルジョン型粘着剤組成物層が積層されてなることを特徴とする粘着テープ。 - 布状基材が、線状体を織成、編成、又は、からみ織することによって得られたものである請求項1に記載の粘着テープ。
- 布状基材が、線状体を一方向に並列し、その上に他の線状体を交差するように配列し、その交点を結合することによって得られたものである請求項1に記載の粘着テープ。
- 線状体が、ポリオレフィンからなる請求項1〜3のいずれかに記載の粘着テープ。
- 布状基材の少なくとも片面に、ポリオレフィンからなる薄層が積層されてなる請求項1〜4のいずれかに記載の粘着テープ。
- JIS Z−0237粘着テープ・粘着シート試験方法10.4項に規定される180度引きはがし粘着力の測定によるステンレス板に対する粘着力が、初期値が5〜15N/25mmで、かつ貼り付け3ヶ月経過後の値が初期値の1.0〜1.5倍である請求項1〜5のいずれかに記載の粘着テープ。
- トルエン、キシレン、メチルメタアクリレート、ブチルアクリレート、2−エチルヘキシルアクリレートの含有量がそれぞれ10μg/g(粘着剤1gに対する量)以下の請求項1〜6のいずれかに記載の粘着テープ。