JP2000062081A - Decorative sheet - Google Patents
Decorative sheetInfo
- Publication number
- JP2000062081A JP2000062081A JP10237051A JP23705198A JP2000062081A JP 2000062081 A JP2000062081 A JP 2000062081A JP 10237051 A JP10237051 A JP 10237051A JP 23705198 A JP23705198 A JP 23705198A JP 2000062081 A JP2000062081 A JP 2000062081A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- decorative sheet
- resin
- gloss
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、建築内外装や物品
表面化粧等に使用する化粧シートに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative sheet used for interior and exterior construction of buildings, surface makeup of articles and the like.
【０００２】[0002]
【従来の技術】化粧シートには、基材表面の好ましくな
い色彩や欠陥を隠蔽し、基材上に付与する絵柄の意匠性
を十分に発揮させる為に、基材と絵柄層との間に隠蔽層
を設ける場合が多い。係る隠蔽層としては、二酸化チタ
ン又は酸化亜鉛等の白色顔料を分散した樹脂層や、アル
ミニウム粉又は真鍮粉等の金属粉を分散した樹脂層を、
塗工法や押出成形法で設ける技術が、広く用いられてい
る。2. Description of the Related Art A decorative sheet is provided between a base material and a pattern layer in order to conceal undesired colors and defects on the surface of the base material and to fully exert the design of the design applied to the base material. A hiding layer is often provided. As such a hiding layer, a resin layer in which a white pigment such as titanium dioxide or zinc oxide is dispersed, or a resin layer in which a metal powder such as aluminum powder or brass powder is dispersed,
The technique of providing by a coating method or an extrusion molding method is widely used.
【０００３】ところが、白色顔料を使用した隠蔽層は、
白色顔料の結晶と分散媒樹脂との屈折率差を利用して光
を散乱させるという原理に基づくものであって、本質的
に光の透過を遮断するものではないから、その隠蔽能力
には自ずと限界がある。従って、化粧シートとして実用
上十分な隠蔽性を確保する為には、分散媒樹脂に対して
白色顔料を大量に添加するか、若しくは隠蔽層を十分厚
く、例えば数十μｍ程度に設ける必要が生じる。However, the hiding layer using a white pigment is
It is based on the principle of scattering light by utilizing the difference in the refractive index between the crystals of the white pigment and the dispersion medium resin, and does not essentially block the transmission of light. There is a limit. Therefore, in order to ensure a practically sufficient hiding property as a decorative sheet, it is necessary to add a large amount of white pigment to the dispersion medium resin, or to provide a hiding layer sufficiently thick, for example, about several tens of μm. .
【０００４】しかし、前者は隠蔽層を脆弱化して化粧シ
ートの層間密着強度を低下させたり、隠蔽層用材料の塗
工適性や押出成形適性を低下させることや下地色として
白色だけでは色表現上で不十分である等の問題があり、
後者は材料費が嵩み、化粧材の可撓性を低下させたり、
特に塗工法で設ける場合には、１回の工程で塗工可能な
厚みには限度があるので、複数回に分けて塗工せざるを
得ず、生産性が低下し生産コストが上昇してしまうこと
や金属粉の比重が高いことによって分散不安定となり塗
布工程中でも沈降が起こり易い等の問題点がある。The former, however, weakens the hiding layer to lower the interlayer adhesion strength of the decorative sheet, lowers the coating suitability or extrusion molding suitability of the hiding layer material, and uses white as the base color alone for color expression. There are problems such as
In the latter case, the material cost is high and the flexibility of the decorative material is reduced,
In particular, when the coating method is used, there is a limit to the thickness that can be coated in one step, so there is no choice but to coat it in multiple steps, reducing productivity and increasing production costs. There is a problem in that dispersion and instability occur due to the fact that the metal powder is crushed and the metal powder has a high specific gravity, and sedimentation easily occurs during the coating process.
【０００５】一方、金属粉を使用した隠蔽層は、金属粉
の光反射性を利用して光の透過を遮蔽するものであるか
ら、白色顔料と比較して少量でも十分に高い隠蔽性が得
られる利点がある。ところが、その特有の金属調（メタ
リック調）の光沢や沈んだ色彩の為に、金属感を活かし
た特殊な用途を別とすれば、化粧材として最も一般的な
木目柄や石目柄、抽象柄、無地柄等の落ち着いた意匠感
を得たい場合には、あまり適当でない場合が多い。ま
た、隠蔽性に優れた金属粉は一般に粒径が大きい上に、
分散媒樹脂との接着性にも乏しいので、隠蔽層の凝集力
が低く、化粧材の層間密着強度に劣るという問題点もあ
る。On the other hand, the hiding layer using metal powder is a layer that blocks the transmission of light by utilizing the light reflecting property of the metal powder, and therefore a sufficiently high hiding property can be obtained even in a small amount as compared with the white pigment. There is an advantage. However, because of its unique metallic (metallic) luster and sunk color, except for special uses that take advantage of the metallic feel, the most common wood grain pattern, stone pattern, and abstract pattern as a decorative material. In many cases, it is not very suitable for obtaining a calm design feeling such as patterns and plain patterns. In addition, the metal powder with excellent concealing property generally has a large particle size,
Since the adhesiveness with the dispersion medium resin is also poor, there is also a problem that the cohesive force of the hiding layer is low and the interlayer adhesion strength of the decorative material is poor.
【０００６】これら両者の長所・短所を補い合う目的
で、金属粉を使用した隠蔽層の表面側に、白色顔料を使
用した隠蔽層を設ける形で、両者を積層併用する技術の
提案もある（特開平５−６４８７０号公報参照）。しか
し、この技術によると、隠蔽層を２層に亘り設けるの
で、生産工程が煩雑となるし、隠蔽層が全体として肉厚
となり、層間強度や可撓性の低下の原因ともなる。ま
た、表面側の白色顔料を使用した隠蔽層の厚みにバラツ
キが発生すると、その厚い箇所と薄い箇所とで下地の金
属光沢や沈んだ色彩の現れ方が異なり、意匠上好ましく
ないので、隠蔽層の厚みを高精度に管理せねばならない
等の問題点があった。[0006] For the purpose of compensating the advantages and disadvantages of both of these, there is also a proposal of a technique of laminating and using a concealing layer using a white pigment on the surface side of a concealing layer using a metal powder (special feature: See Kaihei 5-64870). However, according to this technique, since the concealing layer is provided over two layers, the production process becomes complicated, and the concealing layer becomes thick as a whole, which causes a decrease in interlayer strength and flexibility. Further, when the thickness of the hiding layer using the white pigment on the surface side is varied, the thick metal part and the thin part differ in the appearance of the metallic luster of the base and the sunk color, which is not preferable in terms of design. There was a problem that the thickness of the product had to be controlled with high accuracy.
【０００７】また、これらの化粧シートの基材シートと
しては塩化ビニル樹脂フイルムが広く用いられている
が、燃焼時に有害な塩化水素ガスやダイオキシンを発生
させるため、化粧シートは環境問題も抱えている。ま
た、従来化粧シートタイプとしては塩化ビニル樹脂フイ
ルムに柄を印刷した化粧シートと該印刷柄上に透明な塩
化ビニル樹脂フイルムをラミネートしたダブリングタイ
プがあるが、前者は表面の柄が磨耗によって消滅した
り、耐溶剤性が劣るため表面が汚染され易い等の問題が
ある、一方後者は耐磨耗性は向上しているものの、耐溶
剤性が劣ることと２枚の塩化ビニル樹脂フイルムを用い
ている為、高価格となるという問題を抱えているむもの
である。Although vinyl chloride resin film is widely used as a base sheet for these decorative sheets, the decorative sheet also has environmental problems because it produces harmful hydrogen chloride gas and dioxin during combustion. . As a conventional decorative sheet type, there is a decorative sheet in which a pattern is printed on a vinyl chloride resin film and a doubling type in which a transparent vinyl chloride resin film is laminated on the printed pattern, but in the former, the surface pattern disappears due to abrasion. However, there is a problem that the surface is easily contaminated due to poor solvent resistance. On the other hand, although the latter has improved abrasion resistance, it has poor solvent resistance and two vinyl chloride resin films are used. Therefore, there is a problem of high price.
【０００８】[0008]
【発明が解決しようとする課題】本発明は、従来技術に
おける上記した問題点を解決し、簡便且つ安価に安定的
に製造可能であり、優れた隠蔽性を有し、柔らかい光沢
を有し、色相等の意匠上の問題もなく、しかも耐磨耗
性、耐溶剤性、層間強度等の物性にも問題のない化粧シ
ートを提供することを目的とする。DISCLOSURE OF THE INVENTION The present invention solves the above-mentioned problems in the prior art, can be stably produced easily at low cost, has an excellent concealing property, has a soft luster, It is an object of the present invention to provide a decorative sheet that has no design problems such as hue and has no problems with physical properties such as abrasion resistance, solvent resistance and interlayer strength.
【０００９】[0009]
【課題を解決するための手段】本発明の化粧シートは、
少なくとも二酸化チタンを含む着色顔料及び二酸化チタ
ンで部分被覆した雲母チタン微粉末を含有する隠蔽層を
具備してなるものである。The decorative sheet of the present invention comprises:
It comprises a concealing layer containing a coloring pigment containing at least titanium dioxide and titanium mica fine powder partially coated with titanium dioxide.
【００１０】また、本発明の化粧シートは透明又は半透
明基材シートの片面に絵柄層、前記隠蔽層をこの順に積
層し、もう一方の面に艶調整層を設けてなるものであ
る。The decorative sheet of the present invention comprises a transparent or semi-transparent substrate sheet, on one side of which a picture layer and the above-mentioned concealing layer are laminated in this order, and on the other side of which a gloss adjusting layer is provided.
【００１１】また、本発明の化粧シートは前記もう一方
の面に凹凸模様を有してなるものである。The decorative sheet of the present invention has an uneven pattern on the other surface.
【００１２】また、本発明の化粧シートの前記艶調整層
はグロス層とマット層の２層から成り、少なくともその
内の一層は模様状を成しているものである。The gloss adjusting layer of the decorative sheet of the present invention is composed of two layers, a gloss layer and a matte layer, and at least one of them is patterned.
【００１３】また、本発明の化粧シートの前記基材シー
トは塩化ビニル及び塩化ビニリデン樹脂以外の熱可塑性
樹脂又は熱可塑性樹脂エラストマーであることを特徴と
するものである。The base sheet of the decorative sheet of the present invention is characterized in that it is a thermoplastic resin or a thermoplastic resin elastomer other than vinyl chloride and vinylidene chloride resins.
【００１４】[0014]
【発明の実施の形態】図１に示したものは、本発明の化
粧シートの最も典型的な構成の例であって、基材シート
１の裏面に絵柄層２及び隠蔽層３が順次設けられて構成
されており、該隠蔽層３が少なくとも二酸化チタンを含
有した着色顔料及び雲母チタン微粉粉を含有してなるも
のである。そして、基材シート１の表面には前記艶調整
層が設けられ、グロス層とマット層の２層から成り、少
なくともその内の一層は模様状を成しているものであ
る。図１はその一例でマット層４及び模様状グロス層５
（必要に応じて該基材シート１の表面や該マット層４又
は該グロス層５の表面に凹凸６が形成される）が設けら
れてなるものである。1 shows an example of the most typical structure of a decorative sheet of the present invention, in which a pattern layer 2 and a hiding layer 3 are sequentially provided on the back surface of a base sheet 1. The concealing layer 3 contains a coloring pigment containing at least titanium dioxide and titanium mica fine powder. The gloss adjusting layer is provided on the surface of the base material sheet 1, and is composed of two layers, a gloss layer and a matte layer, and at least one of them is patterned. FIG. 1 shows an example of the mat layer 4 and the patterned gloss layer 5.
(Concavities and convexities 6 are formed on the surface of the base material sheet 1 and the surface of the mat layer 4 or the gloss layer 5 if necessary).
【００１５】勿論、本発明の化粧材の形態は上記した形
態に限定されるものではなく、例えば、基材シート１と
絵柄層２の間にプライマー層６や隠蔽層３の上に接着補
助層７を設けても良い（図２）。Of course, the form of the decorative material of the present invention is not limited to the above-mentioned form, and for example, the adhesive auxiliary layer may be formed on the primer layer 6 or the concealing layer 3 between the base sheet 1 and the pattern layer 2. 7 may be provided (FIG. 2).
【００１６】本発明は、本化粧シートにより表面からの
磨耗によつて柄の消失が起こらず、しかも貼り合わされ
る基材表面の汚れや色ムラ、バラツキを隠蔽でき、しか
も他の諸物性、生産性、価格等に優れた艶調整層、絵柄
層及び隠蔽層を有する化粧シートを提供しようとするも
のである。以下、上述の図１、２に示した形態の場合に
関して説明することにする。According to the present invention, the present decorative sheet does not cause the pattern to disappear due to abrasion from the surface, and can conceal stains, color unevenness, and variations on the surfaces of the substrates to be laminated, and other physical properties and production. An object of the present invention is to provide a decorative sheet having a gloss adjusting layer, a pattern layer and a concealing layer which are excellent in properties and price. Hereinafter, the case of the configurations shown in FIGS. 1 and 2 will be described.
【００１７】本発明の化粧シートにおいて、基材シート
１としては透明又は半透明の熱可塑性樹脂、熱可塑性樹
脂エラストマー、生分解性樹脂、セルロース系樹脂、熱
硬化性樹脂シートが使用可能だが、本化粧シートの表面
への熱エンボス加工適性や該化粧シートを基材に貼り合
わせたり、その後のＶカツトや曲面加工等での加工適性
を考慮すると、これら諸加工適性に於いて優れる熱可塑
性樹脂や熱可塑性樹脂エラストマーが好ましく使用でき
る、特に基材への貼り合わせ加工後に、再度熱を受け
て、化粧シートが基材より浮き上がることや熱エンボス
により形成されていた凹凸が消失することなどの少な
い、すなわち該物性面に優れる軟化点８０℃以上のポリ
エチレン、ポリプロピレンなどオレフイン系、アクリル
系、ポリエステル系などの熱可塑性樹脂シート、や熱可
塑性エラストマー樹脂シートが特に好ましく使用でき
る。また、これらの基材シート１に耐候性や難燃性向上
の為、紫外線吸収剤や難燃剤を添加して使用しても良
い。尚、塩化ビニル樹脂や塩化ビニリデン樹脂シートは
耐溶剤性や上記諸物性に劣るばかりでなく、燃焼時に有
害なダイオキシン、塩化水素ガスを発生させる等の問題
がある為、本発明の基材シートとしての使用は好ましく
ない。In the decorative sheet of the present invention, a transparent or translucent thermoplastic resin, a thermoplastic resin elastomer, a biodegradable resin, a cellulosic resin, or a thermosetting resin sheet can be used as the base material sheet 1. Considering the suitability for heat embossing on the surface of the decorative sheet and the suitability for laminating the decorative sheet on a substrate, and subsequent V-cutting or curved surface processing, a thermoplastic resin excellent in these various processing suitability or A thermoplastic resin elastomer can be preferably used, especially after laminating to a substrate, receiving heat again, the decorative sheet is less likely to be lifted from the substrate and the unevenness formed by heat embossing is less likely to disappear. That is, olefin-based, acrylic-based, polyester-based such as polyethylene and polypropylene having a softening point of 80 ° C. or more, which are excellent in the physical properties, A thermoplastic resin sheet, or a thermoplastic elastomer resin sheet is particularly preferably used for. Further, an ultraviolet absorber or a flame retardant may be added to the base sheet 1 for improving weather resistance and flame retardancy. Incidentally, vinyl chloride resin or vinylidene chloride resin sheet is not only inferior in solvent resistance and the above-mentioned various physical properties, but also has a problem of generating harmful dioxin, hydrogen chloride gas during combustion, etc. Is not preferred.
【００１８】本発明の化粧シートにおける絵柄層２は従
来公知の如く、例えば通常の印刷インキや塗料、染顔料
等を使用して、通常の印刷法や塗装法、染色法等で所望
の任意の絵柄状に設けることができるが、絵柄層２の着
色顔料としては、耐候性に優れるペノリン系、キナクリ
ドン系、イソインドリノン系、フタロシアニン系有機顔
料や二酸化チタン、カーボンブラツクなどの無機顔料も
好ましく使用できる。また、絵柄層２の樹脂成分として
は、アクリル樹脂、ウレタン樹脂、ポリエステル樹脂、
ポリアミド樹脂、酢酸ビニル樹脂、エチレン酢酸ビニル
樹脂、ブチラール樹脂等の熱可塑性樹脂、またポリエス
テルポリオール、セルロース樹脂、ポリアクリルポリオ
ール、ポリエーテルポリオールなど水酸基（−ＯＨ）を
有するポリオール樹脂、アミノ基（−ＮＨ2 ）を有する
アミノ樹脂あるいはカルボキシル基（−ＣＯＯＨ）を有
するカルボン酸を有する活性水素を有する樹脂とイソシ
アネート基（−ＮＣＯ）を有するポリイソシアネート樹
脂とを反応させる２液硬化樹脂などが使用できるが、上
層、下層との接着性や層としての柔軟性の点で優れるエ
チレン酢酸ビニル樹脂や上記２液硬化樹脂（ウレタン樹
脂）が好ましく使用できる。As for the pattern layer 2 in the decorative sheet of the present invention, as is conventionally known, for example, a usual printing ink, paint, dye or pigment is used, and any desired printing method, coating method, dyeing method or the like is used. Although it can be provided in the form of a pattern, as the coloring pigment of the pattern layer 2, an organic pigment such as a penolin-based, quinacridone-based, isoindolinone-based, phthalocyanine-based organic pigment or titanium dioxide or carbon black having excellent weather resistance is also preferably used. it can. As the resin component of the pattern layer 2, acrylic resin, urethane resin, polyester resin,
Thermoplastic resins such as polyamide resin, vinyl acetate resin, ethylene vinyl acetate resin, butyral resin, polyester polyol, cellulose resin, polyacryl polyol, polyether polyol, etc. having hydroxyl group (-OH), amino group (-NH) A two-component curing resin in which an amino resin having 2 ) or a resin having active hydrogen having a carboxylic acid having a carboxyl group (—COOH) and a polyisocyanate resin having an isocyanate group (—NCO) are reacted can be used. Ethylene vinyl acetate resin and the above-mentioned two-component curing resin (urethane resin), which are excellent in terms of adhesiveness to the upper and lower layers and flexibility as the layer, can be preferably used.
【００１９】また、隠蔽層３は本発明の化粧シートの構
成中、最も重要な特徴点であって、少なくとも二酸化チ
タンを含有する着色顔料及び二酸化チタンで部分被覆し
た雲母チタン微粉末の両方を含有することを必須要件と
する。なお、二酸化チタンで部分被覆した雲母チタン微
粉末としては二酸化チタンで部分被覆した雲母チタンに
酸化鉄などで処理した着色雲母チタン微粉末をも含んで
おり、適宜、所望の色相に着色する際に好ましく用いる
ことができる。Further, the concealing layer 3 is the most important characteristic point in the constitution of the decorative sheet of the present invention, and contains both the coloring pigment containing at least titanium dioxide and the fine powder of mica titanium partially coated with titanium dioxide. To do is an essential requirement. The mica titanium fine powder partially coated with titanium dioxide also includes colored mica titanium fine powder partially treated with titanium dioxide and treated with iron oxide or the like, and when appropriately colored in a desired hue. It can be preferably used.
【００２０】少なくとも二酸化チタンを含有する着色顔
料及び二酸化チタンで部分被覆した雲母チタン微粉末の
種類は特に限定されず、いずれも従来公知の任意のもの
が適宜使用可能である。二酸化チタンを含有する着色顔
料における二酸化チタンとは、隠蔽層３の分散媒として
使用する通常の結着剤樹脂と比較して高い屈折率を有す
る、それ自体は無色の固体物質を微細な粉末状にした二
酸化チタン（チタン白、チタニウムホワイト）であっ
て、アナターゼ形とルチル形との２種類の内、特に隠蔽
力、耐候性に優れているルチル形の方が好ましく使用で
きる。また、平均粒径は一般に０．１〜０．５μｍ程度
であり、中でも０．２〜０．３μｍ程度のものが最も隠
蔽力に優れることが知られている。なお二酸化チタン以
外の白色顔料すなわち酸化亜鉛（亜鉛華）、塩基性炭酸
鉛（鉛白）、塩基性硫酸鉛、硫化亜鉛、リポトン、チタ
ノツクスなども二酸化チタンに隠蔽性や耐候性は及ばな
いものの併用することは可能である、また、着色顔料と
しては耐候性に優れる前記インキ用着色顔料が好ましく
使用できる。The types of the coloring pigment containing at least titanium dioxide and the titanium mica fine powder partially coated with titanium dioxide are not particularly limited, and any conventionally known one can be appropriately used. Titanium dioxide in the coloring pigment containing titanium dioxide has a high refractive index as compared with a normal binder resin used as a dispersion medium for the hiding layer 3, and is itself a colorless solid substance in the form of fine powder. Among the two types of titanium dioxide (titanium white and titanium white), the rutile type, which has excellent hiding power and weather resistance, can be preferably used. The average particle size is generally about 0.1 to 0.5 μm, and it is known that the average particle size of about 0.2 to 0.3 μm has the best hiding power. In addition, white pigments other than titanium dioxide, such as zinc oxide (zinc white), basic lead carbonate (lead white), basic lead sulfate, zinc sulfide, lipoton, and titanox, are used in combination with titanium dioxide that does not have concealment or weather resistance. It is also possible to use, and as the color pigment, the above-mentioned color pigment for ink having excellent weather resistance can be preferably used.
【００２１】二酸化チタンで部分被覆した雲母チタン微
粉末としては天然雲母を二酸化チタンでコーティングし
て被覆率１５〜５５％としたものであり（粒子系５〜１
３０μｍ）、更に酸化鉄をコーティング処理したものも
含め、使用できる。また雲母を部分被覆している二酸化
チタンとしては前記同様ルチル型、アナターゼ型の２種
類が使用可能だが、耐候性に優れるルチル型二酸化チタ
ンが好ましく使用できる。これらに光が入射した際には
多重反射が起こり、真珠光沢、絹光沢に似た柔らかい光
沢を与え、木目印刷の下地として用いた場合には樹木の
照り感を与えることができるものであり、金属粉を用い
た場合のような強い金属光沢とは異なった柔らかい光沢
を与えるものである。二酸化チタンでコーティングして
被覆率２０％未満である場合や平均粒径が１０μｍ未満
の場合は銀パール光沢とはならず白色顔料光沢となって
しまう傾向があるため、被覆率２０％〜５０％で、平均
粒径が１０μｍ〜１００μｍが好ましく使用できる、な
お、被覆率５０％以上で、平均粒径が１００μｍ以上で
ある場合は、パール光沢が強過ぎて柔らかい光沢とはな
らない、また、塗布液中で沈降したり、塗布表面に筋が
入ったり塗工上のトラブルも起きやすくなるので使用は
好ましくない。The fine mica powder partially coated with titanium dioxide is obtained by coating natural mica with titanium dioxide to give a coverage of 15 to 55% (particle system 5 to 1).
30 μm), and those coated with iron oxide can also be used. As the titanium dioxide partially covering the mica, two types of rutile type and anatase type can be used as described above, but rutile type titanium dioxide excellent in weather resistance can be preferably used. When light is incident on these, multiple reflection occurs, giving a pearly luster, a soft luster similar to silk luster, and when used as a base for wood grain printing, it is possible to give a shiny feeling of trees, It gives a soft luster, which is different from the strong metallic luster as when metal powder is used. When coated with titanium dioxide and the coverage is less than 20%, or when the average particle size is less than 10 μm, the silver pearl luster and the white pigment luster tend to occur, so the coverage is 20% to 50%. The average particle size is preferably 10 μm to 100 μm, and when the coverage is 50% or more and the average particle size is 100 μm or more, the pearl luster is too strong to give a soft luster. It is not preferable to use it because it tends to settle in it, streaks on the surface of the coating, and troubles in coating tend to occur.
【００２２】また、隠蔽層３の厚みは、貼合わせられる
基材の色調、濃度や凸凹の程度と、目的の化粧材に所望
される表面意匠との兼ね合いによって、必要最低限の厚
みが決定される。一般的には、必要とする隠蔽性の程度
にもよるが概ね３０μｍ以下で十分であり、通常は１〜
１５μｍ程度で十分満足すべき隠蔽性が得られる。Further, the thickness of the concealing layer 3 is determined to be the minimum necessary thickness in consideration of the color tone, the density and the degree of unevenness of the substrate to be laminated and the surface design desired for the intended decorative material. It Generally, depending on the degree of concealment required, a thickness of about 30 μm or less is sufficient, and usually 1 to
A satisfactory hiding property can be obtained at about 15 μm.
【００２３】また、基材シート１の表面には前記艶調整
層が設けられ、グロス層とマット層の２層から成り、少
なくともその内の一層は模様状を成しているものであ
る。マット層４としては艶消効果を出すために適量の艶
消剤すなわちマイカ、シリカ、アルミナ、炭酸カルシウ
ム、珪藻土、珪砂、シラスバルーンなどを適宜のビヒク
ルすなわちウレタン樹脂、アクリル樹脂、ポリエステ
ル、ポリスチレン、ポリビニルブチラール、エチレン酢
酸ビニル、エチレンビニルアルコール樹脂などの熱可塑
性樹脂やアミノ樹脂、セルロース系樹脂、ポリオール樹
脂とイソシアネート化合物によるアクリルウレタン樹
脂、ポリエステルウレタン樹脂、ポリエーテルウレタン
樹脂などの１種または２種以上の混合樹脂に混練した塗
料、塗液を塗布して設けられるが塗布方法はグラビア印
刷などや各種コート方式が用いられる、また模様状グロ
ス層５としてはマツト層４に用いたビヒクルすなわち上
記各種樹脂と同じものがが主体として用いられる（艶消
し剤は混ぜられたとしてもごく微量）。 特に耐溶剤性
に優れるアクリルウレタン樹脂、ポリエステルウレタン
樹脂、ポリエーテルウレタン樹脂などが好ましく使用で
きる、また表面の磨耗性向上のためには耐磨耗性に優れ
る球形状アルミナ微粉末が艶消し剤をも兼ね、好ましく
使用できる、また、表面汚染性を向上させるために、該
グロス層５やマツト層４にフッ素系樹脂やシリコーン系
樹脂を適宜添加することも好ましく使用できる、また、
難燃剤や紫外線吸収剤等を添加することも好ましく使用
できる。これらマツト層４と模様状グロス層５の光沢の
差によって裏面の絵柄層、隠蔽層を引き立てるという意
匠効果を発揮するものである。と同時にこれらの層に上
記各種材料を添加することによつて各種機能、物性効果
を奏するものである。Further, the gloss adjusting layer is provided on the surface of the base material sheet 1, and it comprises two layers of a gloss layer and a mat layer, and at least one of them has a pattern. As the matte layer 4, an appropriate amount of a matting agent, ie, mica, silica, alumina, calcium carbonate, diatomaceous earth, silica sand, shirasu balloon, etc., for producing a matting effect, is used as an appropriate vehicle, that is, urethane resin, acrylic resin, polyester, polystyrene, polyvinyl. One or more of thermoplastic resins such as butyral, ethylene vinyl acetate, ethylene vinyl alcohol resin, amino resins, cellulosic resins, acrylic urethane resins based on polyol resins and isocyanate compounds, polyester urethane resins, polyether urethane resins, etc. It is provided by coating a mixed resin with a kneaded paint or coating liquid, but the coating method is gravure printing or various coating methods, and the patterned gloss layer 5 is the vehicle used for the mat layer 4, that is, the various resins described above. The same thing Used as the body (trace amounts as matting agent was mixed). In particular, acrylic urethane resin, polyester urethane resin, polyether urethane resin, etc., which have excellent solvent resistance, can be preferably used, and spherical alumina fine powder, which has excellent abrasion resistance, is used as a matting agent to improve the abrasion resistance of the surface. In addition, it can be preferably used, and it is also preferable to appropriately add a fluorine resin or a silicone resin to the gloss layer 5 or the mat layer 4 in order to improve surface contamination.
It is also preferable to add a flame retardant or an ultraviolet absorber. The difference in gloss between the matte layer 4 and the patterned gloss layer 5 exerts a design effect of complementing the pattern layer and the concealing layer on the back surface. At the same time, various functions and physical properties are obtained by adding the above-mentioned various materials to these layers.
【００２４】また前記プライマー層６は基材シート１と
絵柄層２及び隠蔽層３の間に層間密着力向上のために設
けるがプライマー樹脂を塗布によって設けるが更にコロ
ナ処理を基材シート１に併用しても良い、該プライマー
樹脂としてはウレタン樹脂、アクリル樹脂、ポリエステ
ル、ポリスチレン、ポリビニルブチラール、エチレン酢
酸ビニル、エチレンビニルアルコール樹脂などの熱可塑
性樹脂やアミノ樹脂、セルロース系樹脂、ポリオール樹
脂とイソシアネート化合物によるアクリルウレタン樹
脂、ポリエステルウレタン樹脂、ポリエーテルウレタン
樹脂などの１種または２種以上の混合樹脂等が使用でき
る。The primer layer 6 is provided between the base sheet 1 and the pattern layer 2 and the concealing layer 3 for improving the interlayer adhesion, but a primer resin is applied by coating, but a corona treatment is also used for the base sheet 1. The primer resin may be a thermoplastic resin such as urethane resin, acrylic resin, polyester, polystyrene, polyvinyl butyral, ethylene vinyl acetate, ethylene vinyl alcohol resin, amino resin, cellulose resin, polyol resin and isocyanate compound. Acrylic urethane resin, polyester urethane resin, polyether urethane resin, etc. may be used alone or in combination of two or more.
【００２５】また、前記接着補助層７は隠蔽層３上に設
けて、本発明の化粧シートを作成するが、木質板、金属
板、プラスチック等の基材へ貼り合わせるに際して、該
基材にエマルジョンなどの接着剤を塗布し、その接着面
に対して本発明の化粧シートの前記接着補助層面７を重
ねて貼り合わせを行うが、該隠蔽層３と該基材の接着層
の層間密着力向上のために設けてなるものである。接着
補助層７としては前記プライマー層６のプライマー樹脂
と同様ものが使用できる。The adhesive auxiliary layer 7 is provided on the concealing layer 3 to prepare the decorative sheet of the present invention. When the adhesive auxiliary layer 7 is attached to a base material such as a wooden board, a metal plate or a plastic, the emulsion is applied to the base material. The adhesive auxiliary layer surface 7 of the decorative sheet of the present invention is laminated on the adhesive surface of the present invention and the resulting adhesive sheet is laminated to improve the interlayer adhesion between the hiding layer 3 and the adhesive layer of the base material. It is provided for. The same adhesive resin as the primer resin of the primer layer 6 can be used as the adhesion auxiliary layer 7.
【００２６】[0026]
【実施例】＜実施例１＞厚さ１００μｍの透明ポリオレ
フィン系樹脂フィルムの裏面をコロナ処理後、通常のウ
レタン系グラビア印刷インキにて木目柄の絵柄を施し、
該絵柄面に、ウレタン系ビヒクル１００重量部あたり二
酸化チタン４０重量部及びキナクリドン系顔料３０重量
部を添加、更にルチル型二酸化チタン被覆率２８％の雲
母チタン（イリオジン１０１：メルク社製）を３０重量
部を添加した隠蔽性インキを使用してグラビア印刷法に
より乾燥後の塗布量７ｇ／ｍ2 にベタ印刷して隠蔽層を
形成し、反対面にウレタン系ビヒクル１００重量部あた
り、球形状アルミナ１０重量部及び炭酸カルシウム４０
重量部を添加したマツトインキを乾燥後の塗布量３ｇ／
ｍ2 ベタ（全面）印刷し、マツト層を形成した、次にウ
レタン系ビヒクル１００重量部あたり球形状アルミナ１
重量部を添加したグロスインキを乾燥後の塗布量２ｇ／
ｍ2 柄印刷し、模様状グロス層を形成して化粧シートを
作製した。この化粧シートの隠蔽層面を、２液硬化型ウ
レタン系接着剤が施されたＭＤＦ（中密度木質板）基材
面に重ね貼付して化粧板を作製した。このＭＤＦ（中密
度木質板）基材面には色差６の色ムラのある基材であつ
たが、この化粧シートを、貼つて化粧板となつたものか
らは上記色ムラは全く感じられなかった。[Examples] <Example 1> After a corona treatment was applied to the back surface of a transparent polyolefin resin film having a thickness of 100 μm, a wood grain pattern was applied using a normal urethane gravure printing ink.
40 parts by weight of titanium dioxide and 30 parts by weight of quinacridone pigment were added to 100 parts by weight of the urethane-based vehicle, and 30 parts by weight of mica titanium having a rutile-type titanium dioxide coating rate of 28% (Iriodin 101: manufactured by Merck) was added to the pattern surface. Part of the hiding ink was solid-printed by a gravure printing method at a coating amount of 7 g / m 2 after drying to form a hiding layer. On the opposite side, 100 parts by weight of the urethane-based vehicle was used to form spherical alumina 10 parts. Parts by weight and calcium carbonate 40
Matt ink added with 1 part by weight of coating amount after drying 3 g /
m 2 solid printing (overall surface) printing to form a matte layer, then spherical alumina 1 per 100 parts by weight of urethane vehicle
Coating amount after drying of gloss ink with 2 parts by weight added
An m 2 pattern was printed to form a patterned gloss layer to prepare a decorative sheet. The concealing layer surface of this decorative sheet was laminated on the surface of the MDF (medium density wooden board) substrate on which the two-component curing type urethane adhesive had been applied to produce a decorative board. This MDF (medium density wooden board) substrate had a color difference of 6 with a color unevenness, but the above-mentioned color unevenness was not felt at all when the decorative sheet was pasted to form a decorative board. It was
【００２７】なお、上記実施例１において、隠蔽性イン
キの雲母チタンの代わりにアルミニウム粉を使用したと
ころ隠蔽性は満足したが、色調はやや黒ずみ、金属光沢
が強過ぎ、意匠的に満足すべきものではなかった。In Example 1, when aluminum powder was used in place of the mica titanium of the hiding ink, the hiding property was satisfactory, but the color tone was slightly dark, the metallic luster was too strong, and the design should be satisfactory. Was not.
【００２８】[0028]
【発明の効果】本発明の化粧シートは、前記材料を使用
し、及び層構成を成すことによって、貼合わせられる基
材のもつ色調ムラ、濃度を隠蔽することができ、印刷
柄、艶調整層と相まって、柔らかい光沢を持つ意匠効果
を奏するものであり、同時に、表面の耐磨耗性、耐溶剤
性及び曲面、Ｖカツト加工適性に優れ、また、燃焼時に
有害な塩化水素ガスやダイオキシンを発生しないという
優れた利点を有するものである。INDUSTRIAL APPLICABILITY The decorative sheet of the present invention is capable of concealing uneven color tone and density of a substrate to be laminated by using the above-mentioned materials and forming a layer structure, and a printed pattern and a gloss adjusting layer. In addition, it has a design effect with a soft luster, and at the same time has excellent surface abrasion resistance, solvent resistance and curved surface, and V cut processing suitability, and also generates harmful hydrogen chloride gas and dioxin during combustion. It has an excellent advantage that it does not.
【図１】本発明の化粧シートの実施の形態を示す側断面
図である。FIG. 1 is a side sectional view showing an embodiment of a decorative sheet of the present invention.
【図２】本発明の化粧シートの実施の形態を示す側断面
図である。FIG. 2 is a side sectional view showing an embodiment of a decorative sheet of the present invention.
１ 基材シート ２ 絵柄層 ３ 隠蔽層 ４ マツト層 ５ 模様状グロス層 ６ プライマー層 ７ 接着補助層 1 Base sheet 2 pattern layers 3 Concealment layer 4 mat layers 5 patterned gloss layer 6 Primer layer 7 Adhesion auxiliary layer
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 2E110 AA26 AA57 AB22 AB23 BA05 BA12 BB02 BB23 GA03Z GA07Z GA23X GA32X GA32Z GB43Z GB44Z GB52Z 4F100 AA21A AC10A AK03B AK11 AK21 AK24 AK28 AK41 AK46 AK61 AL09B AR00A AR00C AR00D AR00E AT00B BA02 BA04 BA05 BA07 BA10A BA10D BA10E CA13 CA13A DB16A DB20A DE01A GB07 HB00C HB00E HB21D JB07 JB16B JK06 JK09 JL01 JN01B JN02 JN02A JN21 JN21E JN26 JN26D ─────────────────────────────────────────────────── ─── Continued front page F-term (reference) 2E110 AA26 AA57 AB22 AB23 BA05 BA12 BB02 BB23 GA03Z GA07Z GA23X GA32X GA32Z GB43Z GB44Z GB52Z 4F100 AA21A AC10A AK03B AK11 AK21 AK24 AK28 AK41 AK46 AK61 AL09B AR00A AR00C AR00D AR00E AT00B BA02 BA04 BA05 BA07 BA10A BA10D BA10E CA13 CA13A DB16A DB20A DE01A GB07 HB00C HB00E HB21D JB07 JB16B JK06 JK09 JL01 JN01B JN02 JN02A JN21 JN21E JN26 JN26D
Claims (5)
び二酸化チタンで部分被覆した雲母チタン微粉末を含有
する隠蔽層を具備してなることを特徴とする化粧シー
ト。1. A decorative sheet comprising a color pigment containing at least titanium dioxide and a masking layer containing fine titanium mica powder partially coated with titanium dioxide.
層、前記隠蔽層をこの順に積層し、もう一方の面に艶調
整層を設けてなることを特徴とする請求項１に記載の化
粧シート。2. A transparent or semi-transparent substrate sheet, wherein a picture layer and said hiding layer are laminated in this order on one side, and a gloss adjusting layer is provided on the other side. Makeup sheet.
を特徴とする請求項１〜２に記載の化粧シート。3. The decorative sheet according to claim 1 or 2, wherein the other surface has an uneven pattern.
から成り、少なくともその内の一層は模様状であること
を特徴とする請求項１〜３に記載の化粧シート。4. The decorative sheet according to claim 1, wherein the gloss adjusting layer is composed of two layers, a gloss layer and a mat layer, and at least one of the layers is patterned.
リデン樹脂以外の熱可塑性樹脂又は熱可塑性樹脂エラス
トマーであることを特徴とする請求項１〜４に記載の化
粧シート。5. The decorative sheet according to claim 1, wherein the base sheet is a thermoplastic resin other than vinyl chloride and vinylidene chloride resins or a thermoplastic resin elastomer.