Description

この発明は、住宅等の建築物の内装材や造作材、建具等の建築資材、家具什器類、住宅機器や家電製品等の表面化粧に使用するための化粧シート、更に詳しくは、表面は視覚的及び手触り感として凹凸感のある落ち着いた艶消し感があり、しかも、耐摩耗性や耐傷性及び耐有機溶剤性に優れ、艶消し感を長期にわたり維持することのできる耐久性に優れた化粧シートに関する。 The present invention relates to a decorative sheet for use in interior decoration and construction materials for buildings such as houses, building materials such as joinery, furniture fixtures, housing equipment and home appliances, and more specifically, the surface is visually It has a calm and matte feeling with a feeling of unevenness and a feeling of touch, and is excellent in wear resistance, scratch resistance and organic solvent resistance, and has excellent durability that can maintain the matte feeling for a long time Regarding the sheet.

従来、上述した特殊化粧シートは、次に述べるような印刷方法によって製作されている。 Conventionally, the above-described special decorative sheet is manufactured by the printing method as described below.

先ず第１の方法は、基材の上に木目模様を形成し、この木目模様の上に透明又は半透明の艶のある反応性硬化型樹脂塗膜層による表面保護層を形成し、前記表面保護層の上に艶消しインキ組成物による導管溝模様層を形成し、視覚的にエンボス効果を現出させる方法である（例えば、特許文献１参照）。 First, a first method is to form a grain pattern on a base material, and to form a surface protective layer on the grain pattern with a transparent or translucent glossy reactive curable resin coating layer, This is a method of visually forming an embossing effect by forming a conduit groove pattern layer with a matte ink composition on a protective layer (see, for example, Patent Document 1).

次に第２の方法は、化粧用紙上に木目模様層を形成し、この木目模様層上に透明又は半透明の反応性硬化型樹脂による表面保護層を形成し、前記表面保護層上に反応性硬化型インキによる導管溝模様層を形成し、この導管溝模様層を形成しない印刷版により透明又は半透明の表面保護層を前記導管溝模様層に印刷見当を合わせる方法である（例えば、特許文献２参照）。 Next, the second method is to form a grain pattern layer on the decorative paper, form a surface protection layer with a transparent or translucent reactive curable resin on the grain pattern layer, and react on the surface protection layer. In this method, a conduit groove pattern layer is formed by a photocurable ink, and a transparent or translucent surface protective layer is aligned with the conduit groove pattern layer by a printing plate that does not form the conduit groove pattern layer (for example, patent Reference 2).

更に、第３の方法は、着色フィルムに木目模様を印刷し、その上に透明なフィルムを貼り合わせた後、導管溝等の柄模様をエンボス版により表面にエンボス加工して凹部を形成し、更にこの凹部をワイピング手法により谷染めし、透明又は半透明の表面保護層をグラビア方式で全面に形成する方法である。 Further, the third method is to print a wood grain pattern on a colored film, and paste a transparent film thereon, then emboss the pattern pattern such as a conduit groove on the surface with an emboss plate to form a recess, Further, this concave portion is dyed by a wiping method, and a transparent or translucent surface protective layer is formed on the entire surface by a gravure method.

ところで、化粧用シートに対する需要者の要望はますます高度になりつつあり、表面仕上げによって視覚的エンボス効果、又は、実質的に凹凸があり、かつ、導管溝以外の部分においても落ち着いた艶消し仕上げ表面であり、手触り感として木質感を表現するソフトな仕上げが好まれている。 By the way, the demands of customers for cosmetic sheets are becoming more and more sophisticated, and the surface finish has a visual embossing effect, or is substantially uneven, and the matte finish is also calm in parts other than the conduit grooves. A soft finish that expresses the texture of the wood as the feel of the surface is preferred.

また、品質においては、耐摩耗性や耐傷性及び耐有機溶剤性に優れ、かつ、艶消し感を長期にわたり維持することのできる耐久性に優れた化粧シートが要望されている。 Further, in terms of quality, there is a demand for a decorative sheet that is excellent in wear resistance, scratch resistance, and organic solvent resistance, and has excellent durability that can maintain a matte feeling over a long period of time.

一方、従来よりスエード調を現出させるために利用されていたビーズを含む塗料による表面保護層により、耐スクラッチ性が良好な艶消し化粧材も提案されている。また、表面保護層に凹凸を形成する方法としては、通常の熱エンボス法や賦形シート上へのキャスティング法が提案されている（例えば、特許文献３）。
特開昭５２−３８００２号公報特許第２８８４８４２号公報特開平６−７９８３１号公報 On the other hand, a matte cosmetic material having good scratch resistance has been proposed by a surface protective layer made of a paint containing beads, which has been used for producing a suede tone. Further, as a method for forming irregularities on the surface protective layer, a normal hot embossing method and a casting method on a shaped sheet have been proposed (for example, Patent Document 3).
JP-A-52-38002 Japanese Patent No. 2884842 JP-A-6-79831

しかしながら、このような要望を満たすために提案されている第１と第２の方法による化粧シートは、導管模様部等の所望の部分を視覚的または手触り感として凹部に現出できるが、前記導管模様部等の所望の部分以外の手触り感として木質感を表現するソフトな仕上がりには不十分である。 However, the decorative sheet according to the first and second methods proposed to satisfy such a demand can appear in a recess as a visual or touch feeling in a desired portion such as a conduit pattern portion. This is insufficient for a soft finish that expresses a wood texture as a touch feeling other than a desired portion such as a pattern portion.

また、第３の方法による化粧シートは、エンボス版によりエンボス加工して凹部を形成した後、この凹部をワイピング手法によりインキにて谷染めするために、全ての凹部は同一色調になり、意匠性において需要者の要望を満たすことが困難であると共に、他のエンボスされない部分の手触り感は現出できない。 In addition, the decorative sheet according to the third method is embossed with an embossing plate to form a concave portion, and then the concave portion is valley-dyed with ink by a wiping method. In addition, it is difficult to satisfy the demands of the consumer, and the touch feeling of other unembossed parts cannot appear.

また、前述の特許文献３のビーズ顔料を用いたものについても、木目模様層上にビーズ顔料を含有する表面保護層を設け、さらにその表面保護層に木目導管溝などの木目板表面の凹凸を表現する凹凸は、熱エンボス法や賦形シート上へのキャスティング法が提案されているが、加工機としてグラビア印刷機以外に熱エンボス加工機又はキャスティング法の設備が必要となる。 In addition, for those using the bead pigment of Patent Document 3 described above, a surface protective layer containing a bead pigment is provided on the wood grain pattern layer, and the surface protective layer is provided with irregularities on the surface of the wood grain plate such as a wood grain conduit groove. For the unevenness to be expressed, a hot embossing method or a casting method on a shaped sheet has been proposed, but a heat embossing machine or a casting method facility is required in addition to a gravure printing machine as a processing machine.

そこで、この発明は、グラビア印刷方式により、表面が耐摩耗性、耐傷性及び耐有機溶剤性に優れ、天然木を艶消し塗装した手触り感と視覚的に天然木の木質感が得られ、しかも、十分な凹凸感が再現された木目模様のある意匠性に優れたプレコート化粧シートを提供することにある。 Therefore, the present invention has a gravure printing method, the surface is excellent in abrasion resistance, scratch resistance and organic solvent resistance, and a natural wood texture can be obtained visually with a feeling of hand-painted natural wood. An object of the present invention is to provide a pre-coated decorative sheet having an excellent design with a grain pattern in which a sufficient unevenness is reproduced.

上記のような課題を解決するため、請求項１の発明は、印刷シートに設けた印刷層の表面に、透明な樹脂成分を主成分とする保護層が設けられてなる化粧シートにおいて、前記保護層が、印刷シートの印刷層上に設けられた第１保護層と、透明又は半透明の球状粒子を含有し前記第１保護層上の所定部分に設けられた第２保護層とからなり、前記第２保護層は深度が４５〜１２０μｍであるグラビア印刷版により形成され、前記球状粒子の平均粒径が５〜４０μｍであり、この球状粒子の含有量が前記第２保護層の主成分である樹脂組成物１００重量部当たり１０〜１５０重量部であり、第２保護層の光沢度はＪＩＳＺ−８７４１に準じた鏡面光沢度測定法により測定されるグロス値（６０°入射）で２０以下であり、第１保護層の突出した表面の艶が第２保護層表面の艶よりグロス値差で０１〜２０の範囲で低くなっている構成を採用したものである。
In order to solve the above-described problems, the invention of claim 1 is directed to a decorative sheet in which a protective layer mainly composed of a transparent resin component is provided on the surface of a printed layer provided on the printed sheet. The layer comprises a first protective layer provided on the printed layer of the printing sheet, and a second protective layer containing transparent or translucent spherical particles and provided in a predetermined portion on the first protective layer; The second protective layer is formed by a gravure printing plate having a depth of 45 to 120 μm, the average particle diameter of the spherical particles is 5 to 40 μm, and the content of the spherical particles is a main component of the second protective layer. It is 10 to 150 parts by weight per 100 parts by weight of a certain resin composition, and the glossiness of the second protective layer is 20 or less in terms of gloss value (60 ° incidence) measured by a specular glossiness measurement method according to JIS Z-8741. , and the table protruding the first protective layer A configuration is adopted in which the gloss of the surface is lower than the gloss of the surface of the second protective layer by a difference in gloss value in the range of 01 to 20 .

次に、請求項２の発明は、透明又は半透明なフィルムの裏面に印刷層と隠蔽層を順次設けたフィルム又は着色フィルムを用い、このフィルムの表面に透明な樹脂成分を主成分とする保護層が設けられてなる化粧シートにおいて、前記保護層が、第１保護層と、透明又は半透明の球状粒子を含有し前記第１保護層上の所定部分に設けられた第２保護層とからなり、前記第２保護層は深度が４５〜１２０μｍであるグラビア印刷版により形成され、前記球状粒子の平均粒径が５〜４０μｍであり、この球状粒子の含有量が前記第２保護層の主成分である樹脂組成物１００重量部当たり１０〜１５０重量部であり、第２保護層の光沢度はＪＩＳＺ−８７４１に準じた鏡面光沢度測定法により測定されるグロス値（６０°入射）で２０以下であり、第１保護層の突出した表面の艶が第２保護層表面の艶よりグロス値差で０１〜２０の範囲で低くなっている構成を採用したものである。
Next, the invention according to claim 2 uses a film or a colored film in which a printed layer and a concealing layer are sequentially provided on the back surface of a transparent or translucent film, and the surface of the film is mainly composed of a transparent resin component. In the decorative sheet provided with a layer, the protective layer includes a first protective layer and a second protective layer containing transparent or translucent spherical particles and provided in a predetermined portion on the first protective layer. The second protective layer is formed by a gravure printing plate having a depth of 45 to 120 μm, the average particle diameter of the spherical particles is 5 to 40 μm, and the content of the spherical particles is the main content of the second protective layer. It is 10 to 150 parts by weight per 100 parts by weight of the resin composition as a component, and the glossiness of the second protective layer is a gloss value (60 ° incidence) measured by a specular glossiness measurement method according to JIS Z-8741. 20 or less, the first A configuration is adopted in which the gloss of the protruding surface of the protective layer is lower than the gloss of the second protective layer surface by a gloss value difference in the range of 01-20 .

上記請求項１又は２の発明において、印刷層とは、例えば木目模様等の意匠性のある模様が印刷される層をいい、模様は木目に限られず、各種幾何学模様、陰影模様により凹凸や金属表面を表現したもの等各種模様が印刷されたものも含み、更に単一色に印刷された無模様のものも含まれる。 In the first or second aspect of the invention, the printed layer refers to a layer on which a design pattern such as a wood grain pattern is printed. The pattern is not limited to the grain, and various geometric patterns and shading patterns may cause unevenness and It includes those printed with various patterns such as those representing a metal surface, and further includes non-patterns printed in a single color.

上記請求項２の発明において、着色フィルムとは、前者の透明又は半透明なフィルムの裏面に印刷層と隠蔽層を設けることに代えて、フィルム内に予め顔料等の着色剤を練り込んだりフィルムの表面に印刷を行って着色されたフィルムをいう。 In the invention of claim 2, the colored film is a film in which a coloring agent such as a pigment is kneaded in advance in the film instead of providing a printing layer and a concealing layer on the back surface of the former transparent or translucent film. A film colored by printing on its surface.

また、上記請求項１又は２の発明において、透明又は半透明の球状粒子としては、微細な樹脂ビーズや無機ビーズを用いたものがあり、樹脂ビーズとしては、アクリル樹脂ビーズ、ポリウレタン樹脂ビーズ、ポリエチレン樹脂ビーズ、ポリスチレン樹脂ビーズ、メラミン樹脂ビーズ等の透明な有機化合物の樹脂球状ビーズがあり、無機ビーズとしてはアルミナやシリカ粉末、ガラス粒子等の透明無機物の球状粒子ビーズなどがある。 In the invention of claim 1 or 2, transparent or translucent spherical particles include those using fine resin beads or inorganic beads, and the resin beads include acrylic resin beads, polyurethane resin beads, polyethylene There are resin spherical beads of transparent organic compounds such as resin beads, polystyrene resin beads, and melamine resin beads, and inorganic beads include spherical particles of transparent inorganic materials such as alumina, silica powder, and glass particles.

なお、球状粒子として透明又は半透明なものに限ったのは、保護層の下部の印刷層や着色フィルムの色彩に視覚的な影響を与えないようにするためである。 The reason why the spherical particles are limited to transparent or semi-transparent particles is to prevent visual influence on the color of the printed layer or the colored film below the protective layer.

また、第２保護層が設けられる第１保護層上の所定部分とは、化粧シート表面に現そうとする凹凸表現のうち凸部分をいい、例えば、木目模様なら導管溝の凹部、年輪模様の凹部及び微細繊維組織等の凹部を表現するために印刷層の前記模様以外の部分に見当合わせを行って設ける部分である。しかし、この所定部分は必ずしも印刷層の模様と一致させる必要はなく、模様と一致しないランダムな凹凸表現とすることもできる。要するに、印刷層の模様と第２保護層が設けられることによる凹凸とが一致しなくても、見た目の模様と、手触り感（凹凸による）により、リアル感は十分に現出することができる。 Further, the predetermined portion on the first protective layer on which the second protective layer is provided refers to a convex portion of the concavo-convex expression that is to appear on the surface of the decorative sheet. In order to express a concave portion such as a concave portion and a fine fiber structure, it is a portion provided by registering a portion other than the pattern of the printed layer. However, the predetermined portion does not necessarily match the pattern of the print layer, and can be a random uneven expression that does not match the pattern. In short, even if the pattern of the printed layer and the unevenness due to the provision of the second protective layer do not match, the real feeling can be sufficiently revealed by the appearance pattern and the touch feeling (due to the unevenness).

また、上記請求項１又は２の発明において、第１保護層の突出した表面の艶が第２保護層表面の艶より低くなっているとは、第１保護層のうち第２保護層に覆われていない外側に現れた部分である凹部と、第２保護層の表面である凸部の表面の艶に差があり、凹部の艶が凸部より艶消しになっている状態をいい、この状態を得るためには第１保護層と第２保護層において艶消剤を含有しない樹脂の艶差によって、あるいはその塗布量によって艶差を生じさせ、第２保護層は第１保護層より艶を現出させ、又は、第１保護層にのみ艶消剤を含有させるか、或いは第１保護層及び第２保護層の両者に含有させる艶消剤の材料や分量を調整して、第１保護層を第２保護層より艶消し状態とする等の適宜手段にて行うことができる。 In the invention of claim 1 or 2, the fact that the gloss of the protruding surface of the first protective layer is lower than the gloss of the surface of the second protective layer is that the second protective layer of the first protective layer is covered. There is a difference in gloss between the concave portion that appears on the outside that is not covered and the surface of the convex portion that is the surface of the second protective layer, and the gloss of the concave portion is more matte than the convex portion. In order to obtain the state, the first protective layer and the second protective layer have a gloss difference caused by the gloss difference of the resin not containing the matting agent or the amount of the resin applied, and the second protective layer is more glossy than the first protective layer. Or the matting agent is contained only in the first protective layer, or the material and amount of the matting agent contained in both the first protective layer and the second protective layer are adjusted. It can be performed by appropriate means such as making the protective layer matt than the second protective layer.

更に、上記請求項１又は２の発明において、第１保護層および耐傷性を良好にする球状粒子を含有している第２保護層の樹脂に、反応性硬化型樹脂や紫外線・電子線硬化型樹脂を用いることにより耐溶剤性にも優れた品質のシートとなった。
Furthermore, in the invention of claim 1 or 2 , a reactive curable resin or an ultraviolet / electron beam curable resin may be used as the resin for the first protective layer and the second protective layer containing spherical particles for improving scratch resistance. By using the resin, it became a sheet having a superior solvent resistance.

上記第１保護層及び第２保護層の主成分である反応性硬化型樹脂組成物としては、アクリルポリオールまたはポリエステルポリオールとポリイソシアネートからなる生成物、アミノアルキッド樹脂にパラトルエンスルホン酸のような触媒を加えたものを使用する。必要に応じて可塑剤、安定剤、分散剤、艶消し剤、希釈剤を添加してもよいのはもちろんのことである。 Examples of the reactive curable resin composition that is the main component of the first protective layer and the second protective layer include a product comprising an acrylic polyol or a polyester polyol and a polyisocyanate, a catalyst such as paratoluenesulfonic acid on an amino alkyd resin. Use the one with added. Of course, plasticizers, stabilizers, dispersants, matting agents, and diluents may be added as necessary.

ここで、上記請求項１における印刷シートは、不透明な化粧シートを基材とし、この基材上に隠蔽ベタ層と印刷層を設けて形成され、第１保護層がこの印刷層の上に設けられ、透明又は半透明な球状粒子を含有する第２保護層は、第１保護層上の所定の位置に設けられている。 Here, the printed sheet according to claim 1 is formed by using an opaque decorative sheet as a base material and providing a concealed solid layer and a printed layer on the base material, and a first protective layer is provided on the printed layer. The second protective layer containing transparent or translucent spherical particles is provided at a predetermined position on the first protective layer.

また、上記請求項２における印刷シートは、透明又は半透明なフィルムを基材とし、この基材上の裏面に印刷層と隠蔽ベタ層とを順次設けて形成されたフィルムか、又は基材の段階で最初から着色が施されている着色フィルムを用い、その表面には第１保護層がこの印刷層の上に設けられ、透明又は半透明な球状粒子を含有する第２保護層は、第１保護層上の所定の部分に設けられている。 Further, the printed sheet according to claim 2 is a film formed by using a transparent or translucent film as a base material and sequentially providing a printing layer and a concealing solid layer on the back surface of the base material, Using a colored film that has been colored from the beginning in the stage, a first protective layer is provided on the surface of the printed layer, and a second protective layer containing transparent or translucent spherical particles It is provided in a predetermined part on one protective layer.

この発明によると、第１及び第２保護層により、表面が耐摩耗性、耐傷性及び耐有機溶剤性に優れたものとなり、例えば木目模様の印刷層を有する化粧シートに適用すれば、天然木を艶消し塗装した感じの仕上がりとなり、手触り及び視覚的な木質感が天然木に近づき、しかも、第２保護層が無い部分と第２保護層がある部分との視覚的な凹凸感及び手触り感としての段差、及び、さらに球状粒子を含有する第２保護層の球状粒子の突出によって、凹凸の段差が十分得られると共に、種々の寸法の段差のある微細な凹凸ができ、種々の凹凸感が再現された木目模様のある意匠性に優れた木目模様を現出させることができる。 According to the present invention, the first and second protective layers make the surface excellent in wear resistance, scratch resistance and organic solvent resistance. For example, when applied to a decorative sheet having a printed pattern of wood grain, natural wood Finished with a matte finish, the feel and visual wood texture approach that of natural wood, and the visual unevenness and feel between the part without the second protective layer and the part with the second protective layer As a result, and the protrusion of the spherical particles of the second protective layer further containing spherical particles, a sufficient uneven step can be obtained, and fine uneven portions with various size steps can be formed, and various uneven feelings can be obtained. It is possible to bring out a wood grain pattern with a reproducible wood grain pattern and excellent design.

即ち、この発明で得られたシートは、第２保護層に透明又は半透明の球状粒子を含有しているために、落ち着いた艶消表面であり、レンズ効果によりソフトな外観が得られ、更に第２保護層の表面は微細な凹凸があり、材質感の手触り感に酷似し、意匠性の高いシートが得られた。 That is, since the sheet obtained in the present invention contains transparent or translucent spherical particles in the second protective layer, it has a calm matte surface, and a soft appearance is obtained by the lens effect. The surface of the second protective layer had fine irregularities, was very similar to the feel of the material feeling, and a highly designable sheet was obtained.

更に、第２保護層が無い部分が凹部となり、この凹部における第１保護層の突出した表面の艶が第２保護層表面の艶より低くなっていることで、凹部が凸部より艶消し状態となり、凹凸部の艶の差によって、視覚的な凹凸感も得られるようになる。 Furthermore, the portion without the second protective layer becomes a concave portion, and the gloss of the surface of the first protective layer protruding from the concave portion is lower than the gloss of the surface of the second protective layer, so that the concave portion is more matte than the convex portion. Thus, a visual unevenness can be obtained due to the difference in gloss of the uneven portions.

なお、一般的に化粧シートの表面全体の光沢度は、ＪＩＳＺ−８７４１に準じた鏡面光沢度測定法により測定されるグロス値（６０°入射）が４０程度までかそれ以下の値、好ましくは２０以下が、落ち着いた艶消し感があり、本願発明は第２保護層で２０以下とする。又、第１保護層が突出している部分のグロス値と第２保護層のグロス値に差を付けると、視覚的に凹凸感が表現されるが、そのグロス値差が大きすぎるとソフト感が表現できず、そのグロス値差は０１〜２０の範囲とする。 In general, the glossiness of the entire surface of the decorative sheet is a gloss value (60 ° incidence) measured by a specular glossiness measuring method according to JIS Z-8741, up to about 40 or less, preferably 20 or less has a calm matte feeling, and the present invention sets the second protective layer to 20 or less. In addition, if the gloss value of the portion where the first protective layer protrudes is different from the gloss value of the second protective layer, a visually uneven feeling is visually expressed, but if the difference between the gloss values is too large, a soft feeling is generated. can not be expressed, the gloss value difference is in the range of 01 to 20.

更に、第１保護層の効果として、紙等の繊維質基材の場合には塗布した反応性硬化型樹脂により繊維質基材特有の吸収性が場所によって異なる、所謂地合ムラによる第２保護層に含まれる球状粒子が埋没することなく表面から突出する球状粒子が安定して、凹凸による手触り感や艶消し効果の安定性が向上する。また、第１保護層が表面に突出している即ち、第２保護層の無い部分の耐摩耗性や耐傷性及び耐溶剤性である物性を確保している。 Further, as the effect of the first protective layer, in the case of a fibrous base material such as paper, the second protection by so-called unevenness in which the absorbency peculiar to the fibrous base material varies depending on the place by the reactive curable resin applied The spherical particles protruding from the surface are stabilized without burying the spherical particles contained in the layer, and the feeling of touch due to the unevenness and the stability of the matte effect are improved. Moreover, the physical property which is the abrasion resistance of the part which the 1st protective layer protrudes on the surface, ie, does not have the 2nd protective layer, scratch resistance, and solvent resistance is ensured.

以下、この発明の実施の形態を添付図面に基づいて説明する。 Embodiments of the present invention will be described below with reference to the accompanying drawings.

図１に示すように、化粧シート１は、基材に不透明な化粧用紙２を用い、グラビア印刷機によってこの化粧用紙２上に隠蔽ベタ層３と、ニトロセルロース系、ウレタン系、アクリル系、塩化ビニール−酢酸ビニル共重合体、ポリエステル等をバインダーとした通常インキにより、例えば木目模様の印刷層４を設けて印刷シート５を形成する。 As shown in FIG. 1, the decorative sheet 1 uses an opaque decorative paper 2 as a base material, and is covered with a concealing solid layer 3 and a nitrocellulose-based, urethane-based, acrylic-based, chloride, and the like on the decorative paper 2 by a gravure printing machine. For example, a printing layer 4 having a wood grain pattern is provided with a normal ink using a vinyl-vinyl acetate copolymer, polyester or the like as a binder to form a printing sheet 5.

上記化粧用紙２としては、薄葉紙、強化紙、含浸紙、合成紙、着色ポリエステルフィルム、着色塩化ビニルフィルム、着色オレフィン系フィルム、アルミ泊等を挙げることができる。 Examples of the decorative paper 2 include thin paper, reinforced paper, impregnated paper, synthetic paper, colored polyester film, colored vinyl chloride film, colored olefin-based film, and aluminum stay.

なお、この木目模様の印刷層４を形成する着色インキとしては、パール顔料、金属粉末等インキ等による光輝性顔料を含有するインキで形成することにより、木目板の木目固有の光沢、即ち「照り」が表現され、より天然木の木質感が得られる。 The colored ink for forming the printed pattern 4 of the wood grain pattern is formed of an ink containing a bright pigment such as a pearl pigment or a metal powder, so that the luster inherent to the wood grain of the wood grain board, that is, “irradiation” Is expressed, and the wood texture of natural wood is obtained.

更に、前記印刷シート５の表面に、保護層６として、適宜艶消剤を含有する第１保護層７と、適宜艶消剤と球状粒子８を含有する第２保護層９を設けた構造になっている。 Furthermore, the surface of the printing sheet 5 has a structure in which a first protective layer 7 containing an appropriate matting agent and a second protective layer 9 containing an appropriate matting agent and spherical particles 8 are provided as the protective layer 6. It has become.

上記第１保護層７は、印刷シート５の木目模様の印刷層４の上に所定の厚みで印刷されて設けられ、第２保護層９は、導管溝模様部とその他の模様部が形成されない部分を有する所望の木目模様の印刷版を用い、印刷シート５の前記木目模様の印刷層４の木目模様の所定部分に合わせて第１保護層７上に印刷されて設けられている。 The first protective layer 7 is provided by being printed with a predetermined thickness on the wood grain print layer 4 of the printing sheet 5, and the second protective layer 9 is not formed with a conduit groove pattern portion and other pattern portions. A printing plate having a desired grain pattern having a portion is used and printed on the first protective layer 7 in accordance with a predetermined portion of the grain pattern printing layer 4 of the print sheet 5.

上記第１保護層７と第２保護層９は、高強度の塗膜を形成する反応性硬化型樹脂で、アミノアルキッド系樹脂、不飽和ポリエステル系樹脂、エポキシ系樹脂、ウレタン系樹脂、アクリル樹脂等を主成分としており、両者は同一の樹脂であっても異なった樹脂であってもよい。 The first protective layer 7 and the second protective layer 9 are reactive curable resins that form a high-strength coating film, such as amino alkyd resins, unsaturated polyester resins, epoxy resins, urethane resins, and acrylic resins. Etc. as the main components, and both may be the same resin or different resins.

第１保護層には上記樹脂に適宜艶消剤を添加するが、その艶消剤としては、一般的な従来のシリカ、炭酸カルシウム、硫酸バリウム、クレイ、タルク等の無機質微粉末でよい。 A matting agent is appropriately added to the first protective layer in the resin, and the matting agent may be a conventional inorganic fine powder such as silica, calcium carbonate, barium sulfate, clay, and talc.

第２保護層９に関しても、前記樹脂に球状粒子８を添加して形成される。ここでいう球状粒子とは、離心率の小さい楕円体状や、面数の多いか又は角の丸まった多面体状の外形が球状に近い粒子であればよい。この角のない球状粒子であると、グラビア印刷方式による樹脂塗装時にドクターブレードを痛める率も少なく、かつ、得られた化粧シートの表面は引っ掻き傷や擦り傷等の耐傷性及び耐摩耗性に優れ、しかも粒子の脱落に対する耐性が得られて表面形状が変化しにくい。 The second protective layer 9 is also formed by adding spherical particles 8 to the resin. As used herein, the spherical particles may be particles having an elliptical shape with a small eccentricity or a polyhedral shape with a large number of faces or rounded corners that are nearly spherical. When the spherical particles are free of corners, the rate at which the doctor blade is damaged during resin coating by the gravure printing method is low, and the surface of the resulting decorative sheet has excellent scratch resistance and abrasion resistance such as scratches and scratches. In addition, the resistance to particle dropout is obtained, and the surface shape hardly changes.

上記球状粒子８は、アクリル系樹脂、ウレタン系樹脂、アルミナ、メラミン粒子、シリカ等のビーズを用い、その平均粒径が５〜４０μｍの真球が好ましく、第２保護層９は、この球状粒子８の含有量が前記第２保護層９の主成分である樹脂組成物１００重量部当たり１０〜１５０重量部に設定され、この球状粒子８は第２保護層９の表面に一部突出することになる。 The spherical particles 8 are beads of acrylic resin, urethane resin, alumina, melamine particles, silica, etc., and are preferably true spheres having an average particle size of 5 to 40 μm. The second protective layer 9 is made of spherical particles. The content of 8 is set to 10 to 150 parts by weight per 100 parts by weight of the resin composition that is the main component of the second protective layer 9, and the spherical particles 8 partially protrude from the surface of the second protective layer 9. become.

第１保護層及び第２保護層の耐傷性や耐摩耗性をさらに向上させるために、スリップ剤を添加して、樹脂の潤滑性を与えることは有効である。スリップ剤としては、脂肪酸アミド、高級脂肪酸等の脂肪酸誘導体やオレフィンワックス、シリコーンオイルを主成分の樹脂組成物１００重量部当たり０．１〜５重量部程度を適宜選定し添加すればよい。 In order to further improve the scratch resistance and wear resistance of the first protective layer and the second protective layer, it is effective to add a slip agent to give the resin lubricity. As the slip agent, a fatty acid amide, a fatty acid derivative such as a higher fatty acid, olefin wax, or silicone oil may be appropriately selected and added in an amount of about 0.1 to 5 parts by weight per 100 parts by weight of the main resin composition.

また、第２保護層９は、例えば木目模様の場合、導管溝模様部と微細繊維模様部及びその他の模様部が形成されない部分を有する所望の木目模様が設けられ、そのグラビア印刷版深度が４５〜１２０μｍであるグラビア印刷版を用い、印刷シート５の前記木目模様の印刷層４の所定部分に合わせて第２保護層より艶の低い第１保護層７上に印刷されているので、第１保護層と第２保護層の艶差による視覚的凹凸感と、第２保護層９の厚みによって発生した段差とその表面への球状粒子８の突出により、凹凸感が再現された意匠性に優れた木目模様を現出させることができることになる。 Further, in the case of a wood grain pattern, for example, the second protective layer 9 is provided with a desired wood grain pattern having a portion in which a conduit groove pattern portion, a fine fiber pattern portion and other pattern portions are not formed, and the gravure printing plate depth is 45. Since the gravure printing plate having a thickness of ˜120 μm is printed on the first protective layer 7 having a lower gloss than the second protective layer in accordance with a predetermined portion of the print pattern 4 of the wood grain pattern of the printing sheet 5, the first Excellent visual design due to the difference in gloss between the protective layer and the second protective layer, and the design that reproduces the unevenness due to the level difference caused by the thickness of the second protective layer 9 and the protrusion of the spherical particles 8 on the surface. The wood grain pattern can be revealed.

このようにして製作された化粧シート１は、住宅等の建築物の内装材や造作材、建具等の建築資材、家具什器類、住宅機器や家電製品等の表面化粧に使用するものであり、この化粧シート１は、木質感をよりリアルに現出すべく、視覚的な凹凸感及び手触りとしてソフトである凹凸感のある落ち着いた艶消し感を備えており、しかも、耐摩耗性や耐傷性及び耐有機溶剤性に優れ、艶消し感を長期にわたり維持することのできる耐久性に優れている。 The decorative sheet 1 produced in this way is used for surface makeup of interior materials and construction materials of buildings such as houses, building materials such as fittings, furniture fixtures, housing equipment and home appliances, This decorative sheet 1 is provided with a soft matte feeling with a soft texture as a visual concavo-convex sensation and a soft feel as a texture, in addition to wear resistance and scratch resistance. It has excellent resistance to organic solvents and excellent durability that can maintain a matte feeling for a long time.

図２は、透明フィルムを基材とした化粧シートの実施の形態を示すものである。 FIG. 2 shows an embodiment of a decorative sheet using a transparent film as a base material.

図示のように、化粧シート１′は、基材に透明フィルム１０を用い、グラビア印刷機によってこの透明フィルム１０の裏面上にウレタン系樹脂、アクリル系樹脂、塩化ビニール−酢酸ビニル共重合体樹脂、ポリエステル系樹脂等をバインダーとした通常着色インキを適宜選択して形成された木目模様の印刷層４と、隠蔽ベタ層３を設けて印刷フィルム１１を形成し、前記印刷フィルム１１の基材の表面に、保護層６として、艶消剤を含有する第１保護層７と、球状粒子８を含有する第２保護層９を設けた構造になっている。 As shown in the figure, the decorative sheet 1 'uses a transparent film 10 as a base material, and a gravure printing machine uses a urethane resin, an acrylic resin, a vinyl chloride-vinyl acetate copolymer resin, A printing film 11 is formed by providing a woodgrain pattern printing layer 4 and a concealing solid layer 3 formed by appropriately selecting a normal colored ink using a polyester resin as a binder, and the surface of the substrate of the printing film 11 Further, as the protective layer 6, a first protective layer 7 containing a matting agent and a second protective layer 9 containing spherical particles 8 are provided.

上記透明フィルム１０としては、ポリエステルフィルム、塩化ビニルフィルム、オレフィン系フィルム等を挙げることができる。 Examples of the transparent film 10 include a polyester film, a vinyl chloride film, and an olefin film.

上記第１保護層７は、印刷フィルム１１の上に所定の厚みで印刷されて設けられ、第２保護層９は、導管溝模様部と微細繊維組織模様部及びその他の模様部が形成されない部分を有する所望の木目模様の印刷版を用い、印刷フィルム１１の前記木目模様の印刷層４の木目模様の所定部分に第１保護層７上に印刷されて設けられている。 The said 1st protective layer 7 is printed and provided by the predetermined thickness on the printing film 11, and the 2nd protective layer 9 is a part in which a conduit groove pattern part, a fine fiber structure pattern part, and other pattern parts are not formed. A printing plate having a desired grain pattern is used, and is printed on the first protective layer 7 at a predetermined portion of the grain pattern printing layer 4 of the printing film 11.

その他、上記第１保護層７と第２保護層９、及び球状粒子８の構成、材料、厚み、及び印刷手段等は、図１の実施形態とほぼ同様であり説明を省略する。 In addition, the configurations, materials, thicknesses, printing means, and the like of the first protective layer 7, the second protective layer 9, and the spherical particles 8 are substantially the same as those in the embodiment of FIG.

この実施形態の化粧シート１′は、図１の化粧シート１と同様、表面が耐摩耗性、耐傷性及び耐有機溶剤性に優れたものとなり、天然木を視覚的及び手触り感として凹凸のある落ち着いた艶消し塗装した状態と球状粒子によるレンズ効果によって、視覚的にソフト感のある仕上がり表面が得られる。 The decorative sheet 1 ′ of this embodiment has a surface with excellent wear resistance, scratch resistance, and organic solvent resistance, similar to the decorative sheet 1 of FIG. Due to the calm matte paint and the lens effect of spherical particles, a visually soft finish is obtained.

また、このようにして製作された化粧シート１′は、住宅等の建築物の内装材や造作材、建具等の建築資材、家具什器類、住宅機器や家電製品等の表面化粧に使用するものであり、この化粧シート１′は、表面が視覚的及び手触り感として凹凸感のある落ち着いた艶消し感があり、しかも、耐摩耗性や耐傷性及び耐有機溶剤性に優れ、艶消し感を長期にわたり維持することのできる耐久性に優れている。 The decorative sheet 1 ′ thus produced is used for surface makeup of interior materials and construction materials for buildings such as houses, building materials such as fittings, furniture fixtures, housing equipment and home appliances. This decorative sheet 1 ′ has a calm matte feeling with a rough surface as a visual and touch feeling, and is excellent in wear resistance, scratch resistance and organic solvent resistance, and has a matte feeling. Excellent durability that can be maintained over a long period of time.

グラビア印刷方式により、坪量３０ｇ／ｍ^２の薄葉紙に硝化綿系通常インキにて木目柄模様の印刷（下地ベタ版、木肌版、調子版、導管版）を施した。木肌模様版には雲母からなるパール顔料インキを使用した。その上に第１保護層としてアクリルポリオールにポリイソシアネートを添加した２液硬化型アクリルウレタン樹脂を乾燥後のグロス値が１０及び塗布量が３ｇ／ｍ^２になるように全面に塗布し、第２保護層として、導管模様部及び微細繊維組織部が形成されない版深度９０μｍの印刷版により前記模様部に合わせて下記配合の透明樹脂ビーズ入り樹脂塗料を塗布し、乾燥させて巻き取りをした。 With a gravure printing method, printing of a wood grain pattern (basic solid plate, wood plate, tone plate, conduit plate) was performed on a thin paper having a basis weight of 30 g / m ² with nitrified cotton-based normal ink. A pearl pigment ink made of mica was used for the wood pattern. Gloss value of 10 and the coating amount after drying two-component curable acrylic urethane resin obtained by adding polyisocyanate acrylic polyol as the first protective layer was coated on the entire surface so as to 3 g / m ² thereon, a second As a protective layer, a resin coating containing transparent resin beads having the following composition was applied to the pattern portion using a printing plate having a plate depth of 90 μm on which a conduit pattern portion and a fine fiber structure portion were not formed, and the resultant was dried and wound up.

第２保護層部分のグロス値は１８〜２０であり、この化粧紙を巻き取り状態で６０℃に保たれた養生室で３日放置し、各層の密着強化促進、樹脂の硬化促進、ブロッキング防止のための養生を行い、本発明の化粧材である化粧紙を得た。 The gloss value of the second protective layer portion is 18 to 20, and this decorative paper is left in a curing room kept at 60 ° C. in a wound state for 3 days to promote adhesion strengthening of each layer, promote resin hardening, and prevent blocking. The decorative paper for the present invention was obtained.

［透明印刷塗料組成］
（１）透明架橋型アクリル樹脂ビーズ（平均粒径３０μｍ）２５部
（２）バインダー（ポリエステルポリオール樹脂／アクリルポリオール樹脂）２０部
（３）スリップ剤（シリコーンオイル）１部
（４）硬化剤（ヘキサメチレンジイソシアネートプレポリマー）２０部
（５）ブロッキング防止剤（アマイド系ワックス）１部
（６）溶剤（酢酸エチル、酢酸ブチル）５０部 [Transparent printing paint composition]
(1) Transparent cross-linked acrylic resin beads (average particle size 30 μm) 25 parts (2) Binder (polyester polyol resin / acrylic polyol resin) 20 parts (3) Slip agent (silicone oil) 1 part (4) Curing agent (hexa Methylene diisocyanate prepolymer) 20 parts (5) Antiblocking agent (amide wax) 1 part (6) Solvent (ethyl acetate, butyl acetate) 50 parts

グラビア方式両面印刷機にて、厚み０．１ｍｍの透明オレフィンフィルムの裏面に通常のウレタン系インキにて皺溝模様のある皮革模様印刷（柄模様版、下地ベタ版）を施し、フィルムを反転後、第１保護層として、微細な凹凸が処理された艶消し状態の表面には艶消剤が配合された透明なアクリルポリオールにポリイソシアネートを添加した２液硬化型アクリルウレタン系樹脂を乾燥後のグロス値が０１及び塗布量が２ｇ／ｍ^２になる様に全面に塗布し、第２保護層として、皺溝模様が形成されない版深度７０μｍの印刷板により皺溝模様部と印刷見当を合わせ下記配合の透明樹脂ビーズ入り樹脂塗料を塗布し、乾燥して巻き取りをした。 Using a gravure double-sided printing machine, apply a leather pattern print (pattern pattern plate, base solid plate) with a groove pattern on the back of a transparent olefin film with a thickness of 0.1 mm with normal urethane ink, and then turn the film over As a first protective layer, after drying a two-component curable acrylic urethane resin in which a polyisocyanate is added to a transparent acrylic polyol in which a matting agent is blended on a matte surface treated with fine irregularities Apply the entire surface so that the gloss value is 01 and the coating amount is 2 g / m ² , and align the groove pattern part and the printing register as a second protective layer with a printing plate with a plate depth of 70 μm on which the groove pattern is not formed. The blended transparent resin beaded resin paint was applied, dried and wound up.

第２保護層部分のグロス値０６〜０７であり、この化粧シートを２０℃に保たれた養生室に５日間放置し、各層の密着強化促進、樹脂の硬化促進、ブロッキング防止のための養生を行い、本発明の化粧材である化粧シートを得た。 The gloss value of the second protective layer portion is 06 to 07, and this decorative sheet is left in a curing room kept at 20 ° C. for 5 days to promote adhesion strengthening of each layer, curing of resin, and curing for preventing blocking. The decorative sheet as the decorative material of the present invention was obtained.

［透明艶消印刷塗料組成］
（１）透明メラミン樹脂ビーズ（平均粒径１０μｍ）２０部
（２）艶消剤（シリカ平均粒径１．５μｍ）２部
（３）バインダー（アクリルポリオール樹脂）１８部
（４）硬化剤（ヘキサメチレンジイソシアネートプレポリマー）１０部
（５）溶剤（酢酸エチル、酢酸ブチル）４０部 [Transparent matte printing paint composition]
(1) Transparent melamine resin beads (average particle size 10 μm) 20 parts (2) Matting agent (silica average particle size 1.5 μm) 2 parts (3) Binder (acrylic polyol resin) 18 parts (4) Curing agent (hexa Methylene diisocyanate prepolymer) 10 parts (5) Solvent (ethyl acetate, butyl acetate) 40 parts

グラビア印刷方式により、厚み０．１ｍｍの塩化ビニル樹脂フィルム（可塑剤の含有量２０重量部）の裏面に塩化ビニール−酢酸ビニール共重合体インキにて木目模様印刷（柄模様版、下地ベタ版）を施し巻き取りをした。再度グラビア印刷機にて、第１保護層として、表面には艶消剤が添加されたアクリルポリオールにポリイソシアネートを添加した２液硬化型アクリルウレタン系樹脂を乾燥後グロス値が０４及び塗布量が２ｇ／ｍ^２になる様に全面に塗布し、第２保護層として柾目状の導管模様及び微細繊維組織模様部が形成されない版深度６０μｍの印刷版にて下記配合の透明樹脂ビーズ入り樹脂塗料所定の部分に塗布し、乾燥させて巻き取りをした。 By gravure printing method, wood grain pattern printing with a vinyl chloride-vinyl acetate copolymer ink on the back of a 0.1 mm thick vinyl chloride resin film (plasticizer content 20 parts by weight) (pattern pattern plate, solid base plate) And rolled up. In the gravure printing machine again, as a first protective layer, after drying a two-component curable acrylic urethane resin in which a polyisocyanate is added to an acrylic polyol with a matting agent added to the surface, the gloss value is 04 and the coating amount is Apply to the whole surface so as to be ² g / m ² , and a resin coating containing transparent resin beads of the following composition is specified on a printing plate having a plate depth of 60 μm where a grid-like conduit pattern and fine fiber texture pattern part are not formed as the second protective layer It was applied to the part and dried and wound up.

第２保護層部分のグロス値は２０であり、この化粧シートを実施例２と同様に養生室に放置し、本発明の化粧材である化粧シートを得た。 The gloss value of the second protective layer portion was 20, and this decorative sheet was left in the curing room in the same manner as in Example 2 to obtain a decorative sheet which is the decorative material of the present invention.

［透明艶消印刷塗料配合例］
（１）透明架橋型アクリルビーズ（平均粒径１２μｍ）２０部
（２）艶消剤（シリカ平均粒径２μｍ）２部
（３）バインダー（アクリルポリオール樹脂）１８部
（４）硬化剤（キシリレンジイソシアネート）１０部
（５）溶剤（酢酸エチル、酢酸ブチル）４０部 [Transparent matte printing paint formulation example]
(1) Transparent cross-linked acrylic beads (average particle size 12 μm) 20 parts (2) Matting agent (silica average particle size 2 μm) 2 parts (3) Binder (acrylic polyol resin) 18 parts (4) Curing agent (xylylene) Isocyanate) 10 parts (5) Solvent (ethyl acetate, butyl acetate) 40 parts

化粧シートを拡大した縦断面図Longitudinal sectional view of a decorative sheet 化粧シートの他の例を拡大した縦断面図A longitudinal sectional view enlarging another example of a decorative sheet

Explanation of symbols

１化粧シート
２化粧用紙
３隠蔽ベタ層
４木目模様の印刷層
５印刷シート
６保護層
７第１保護層
８球状粒子
９第２保護層
１０透明フィルム
１１印刷フィルム DESCRIPTION OF SYMBOLS 1 Decorative sheet 2 Decorative paper 3 Concealed solid layer 4 Print pattern 5 of wood grain pattern Print sheet 6 Protective layer 7 First protective layer 8 Spherical particle 9 Second protective layer 10 Transparent film 11 Print film

Claims

A decorative sheet in which a protective layer mainly composed of a transparent resin component is provided on the surface of a printing layer provided on the printing sheet, wherein the protective layer is provided on the printing layer of the printing sheet. And a second protective layer that contains transparent or translucent spherical particles and is provided at a predetermined portion on the first protective layer, and the second protective layer is formed by a gravure printing plate having a depth of 45 to 120 μm. The spherical particles have an average particle size of 5 to 40 μm, and the content of the spherical particles is 10 to 150 parts by weight per 100 parts by weight of the resin composition as the main component of the second protective layer; 2 The gloss of the protective layer is 20 or less in terms of gloss value (60 ° incidence) measured by a specular gloss measurement method according to JIS Z-8741, and the gloss of the protruding surface of the first protective layer is the second protection. 01-2 in gloss value difference from the gloss of the layer surface A decorative sheet characterized by being lowered in a range of 0 .

In a decorative sheet formed by using a film or a colored film in which a printing layer and a concealing layer are sequentially provided on the back surface of a transparent or translucent film, and a protective layer mainly composed of a transparent resin component is provided on the surface of the film, the protective layer includes a first protective layer consists of a second protective layer provided as necessary contain transparent or translucent spherical particles predetermined portion of said first protective layer, the second protective The layer is formed by a gravure printing plate having a depth of 45 to 120 μm, the average particle diameter of the spherical particles is 5 to 40 μm, and the content of the spherical particles is a main component of the second protective layer. It is 10 to 150 parts by weight per 100 parts by weight, and the glossiness of the second protective layer is 20 or less in terms of gloss value (60 ° incidence) measured by a specular glossiness measurement method according to JIS Z-8741 . 1 Protective layer protrusion The decorative sheet is characterized in that the gloss of the surface is lower than the gloss of the surface of the second protective layer in the range of 01 to 20 in terms of difference in gloss value .