JPH0687201A - Decorative film - Google Patents
Decorative filmInfo
- Publication number
- JPH0687201A JPH0687201A JP23868592A JP23868592A JPH0687201A JP H0687201 A JPH0687201 A JP H0687201A JP 23868592 A JP23868592 A JP 23868592A JP 23868592 A JP23868592 A JP 23868592A JP H0687201 A JPH0687201 A JP H0687201A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- pattern
- film
- ink
- pattern printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、窓ガラスや、金属板な
どに貼着して装飾を施す表面材として用いられる化粧フ
ィルムに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative film used as a surface material which is attached to a window glass or a metal plate for decoration.
【０００２】[0002]
【従来の技術】例えば、窓ガラスや透明プラスチック
板、または金属板などに貼着する化粧フィルムは、光を
透過できる透明または半透明のフィルムに印刷模様やエ
ンボス模様が施された化粧フィルムが用いられる。この
ような化粧フィルムは、例えば特公昭５８−１４３１２
号公報や特公平１−３５７０８号公報に明示されている
化粧シートなどがある。これら従来の化粧シートは、木
目模様が施された化粧シートで、この木目を表現するた
めに、エンボス模様で導管部分を形成し、印刷模様でそ
の模様を強調させるとともに、エンボス面にコーティン
グを施し、このエンボスによる凹部内にインキを充填さ
せた構成となっている。2. Description of the Related Art For example, as a decorative film attached to a window glass, a transparent plastic plate, a metal plate, or the like, a decorative film having a printed pattern or an embossed pattern on a transparent or translucent film capable of transmitting light is used. To be Such a decorative film is disclosed, for example, in Japanese Examined Patent Publication No. 58-14312.
There is a decorative sheet and the like which are specified in Japanese Patent Publication No. Hei 1-35708. These conventional decorative sheets are decorative sheets with a wood grain pattern.In order to express this wood grain, the conduit portion is formed with an embossed pattern, the printed pattern is emphasized, and the embossed surface is coated. The ink is filled in the concave portion formed by this embossing.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、上記の
ような従来の化粧シートでは、特公昭５８−１４３１２
号公報や特公平１−３５７０８号公報に記載されている
ものは、エンボス面の全面にトップコート層としてコー
ティングを施すので、導管部分となるエンボスの凹凸模
様がはっきり形成されないという欠点があり、また、エ
ンボスによる凹部内にインキを充填させているので、模
様における色変化はあるが、質感がないという欠点があ
る。However, in the conventional decorative sheet as described above, Japanese Patent Publication No. 58-14312 is used.
In Japanese Patent Laid-Open Publication No. Hei 1-35708 and Japanese Patent Publication No. 1-35708, since the entire surface of the embossed surface is coated as a top coat layer, there is a drawback that the embossed pattern of the embossing that forms the conduit portion is not clearly formed. Since the ink is filled in the concave portion by embossing, there is a drawback that the pattern has a color change but no texture.
【０００４】そこで本発明は、上記問題点を解消するた
めに、印刷による模様とエンボスによる立体感を向上さ
せ、よりリアル感のある化粧フィルムを提供することを
目的としている。In order to solve the above problems, it is an object of the present invention to provide a decorative film having a more realistic appearance by improving the three-dimensional effect of the pattern and embossing by printing.
【０００５】[0005]
【課題を解決するための手段】次に、上記の目的を達成
するための手段を、実施例に対応する図面を参照して説
明する。この発明の化粧フィルム１は、透明若しくは半
透明の熱可塑性樹脂よりなる基材フィルム２の表面２ａ
に、エンボスによる凹凸模様を形成し、該凹凸模様の凹
部４内にインキ３を充填するとともに、前記凹凸模様の
凸部５のみにコーティングを施し、コート層６を形成さ
せ、かつ、該コート層６の表面６ａに硬化性樹脂をバイ
ンダーとしたインキで模様印刷層７を形成したことを特
徴としている。また、この発明の化粧フィルムは、上記
コート層６を着色された着色コート層６としてもよく、
さらに、上記コート層６の表面に形成される模様印刷層
７のインキを前記コート層６とは異なる光沢のインキを
用いて形成させてもよい。さらに、前述した基材フィル
ム２の裏面２ｂに模様印刷層８を形成して化粧フィルム
３１としたり、前記基材フィルム２の裏面２ｂに、模様
印刷層８と透明若しくは半透明層１２、模様印刷層８と
不透明な隠蔽層９、模様印刷層８と金属蒸着フィルム
層、が形成されたことを特徴としたり、前記凹部４内に
充填されるインキ３がマット剤を含有した艶消し半透明
インキ又は艶消し着色インキである化粧フィルム２１，
３１，４１としてもよい。Means for achieving the above object will be described below with reference to the drawings corresponding to the embodiments. The decorative film 1 of the present invention comprises a surface 2a of a base film 2 made of a transparent or translucent thermoplastic resin.
A concave-convex pattern is formed by embossing, ink 3 is filled in the concave-convex pattern 4 of the concave-convex pattern, and only the convex part 5 of the concave-convex pattern is coated to form a coat layer 6; The pattern printing layer 7 is formed on the surface 6a of 6 with an ink containing a curable resin as a binder. Further, in the decorative film of the present invention, the coating layer 6 may be the colored coating layer 6,
Further, the ink of the pattern printing layer 7 formed on the surface of the coat layer 6 may be formed using an ink having a gloss different from that of the coat layer 6. Furthermore, the pattern printing layer 8 is formed on the back surface 2b of the base film 2 to form the decorative film 31, or the back surface 2b of the base film 2 is printed with the pattern printing layer 8 and the transparent or semitransparent layer 12 and the pattern printing. Layer 8 and opaque concealing layer 9, pattern printing layer 8 and metal vapor-deposited film layer are formed, and the matte semi-transparent ink in which the ink 3 filled in the recess 4 contains a matting agent Or a decorative film 21, which is a matte colored ink,
It may be 31, 41.
【０００６】[0006]
【作用】透明若しくは半透明の熱可塑性樹脂よりなる基
材フィルム２の表面２ａに、エンボスによる凹凸模様を
形成する。次に、この凹凸模様の凹部４内にインキ３を
充填するとともに、前記凹凸模様の凸部５のみにコーテ
ィングを施し、コート層６を形成させる。そして、コー
ト層６の表面６ａに硬化性樹脂をバインダーとしたイン
キで模様印刷層７を形成し、化粧フィルム１を得る。前
記コート層６を着色された着色コート層６として形成し
たり、上記コート層６の表面６ａに形成される模様印刷
層７のインキを前記コート層６とは異なる光沢のインキ
を用いれば、前記化粧フィルムと異なる化粧フィルムが
得られる。さらに、前記基材フィルム２の裏面２ａに
は、模様印刷層８を形成させたり、模様印刷層８と透明
若しくは半透明層１２とを形成したり、模様印刷層８と
不透明な隠蔽層９とを形成したり、模様印刷層８と金属
蒸着フィルム層とを形成してもよく、また、前記凹凸模
様の凹部４内に充填されるインキ３を、マット剤を含有
した艶消し半透明インキ又は艶消し着色インキとすれ
ば、各種化粧フィルム２１，３１，４１を得ることがで
きる。Function: An embossed pattern is formed on the surface 2a of the base film 2 made of a transparent or translucent thermoplastic resin. Next, the ink 3 is filled in the concave portions 4 having the concave-convex pattern, and only the convex portions 5 having the concave-convex pattern are coated to form the coat layer 6. Then, the pattern printing layer 7 is formed on the surface 6a of the coat layer 6 with the ink using the curable resin as a binder, and the decorative film 1 is obtained. If the coating layer 6 is formed as a colored coating layer 6 or the ink of the pattern printing layer 7 formed on the surface 6a of the coating layer 6 is an ink having a gloss different from that of the coating layer 6, A decorative film different from the decorative film can be obtained. Further, on the back surface 2a of the base film 2, a pattern printing layer 8 is formed, a pattern printing layer 8 and a transparent or semitransparent layer 12 are formed, and a pattern printing layer 8 and an opaque concealing layer 9 are formed. May be formed, or the pattern printing layer 8 and the metal vapor deposition film layer may be formed, and the ink 3 filled in the concave portions 4 of the uneven pattern may be a matte semi-transparent ink containing a matting agent or If the matte colored ink is used, various decorative films 21, 31, 41 can be obtained.
【０００７】[0007]
【実施例】次に、本発明の実施例を詳述する。 Ｉ．第１実施例 図１は本発明の第１の実施例に係わる化粧フィルムの断
面図である。本実施例の化粧フィルム１は、まず、熱可
塑性樹脂フィルムである厚さ１５０μの透明な塩化ビニ
ル樹脂フィルムを基材フィルム２とし、この基材フィル
ム２の表面２ａに、オーク材の柾目の導管模様をエンボ
ス加工にて凹凸模様を形成させる。次に、体質顔料で艶
消しされたインキを、メジュームを８０、黒を６、赤を
２黄を３、硬化剤を９の割合で調色し、このインキ３を
前記凹凸模様の凹部４内にワイピング法によって充填さ
せる。EXAMPLES Next, examples of the present invention will be described in detail. I. First Embodiment FIG. 1 is a sectional view of a decorative film according to a first embodiment of the present invention. In the decorative film 1 of this example, first, a transparent vinyl chloride resin film having a thickness of 150 μ, which is a thermoplastic resin film, is used as the base film 2, and the surface 2a of the base film 2 has oak-shaped perforated conduits. The pattern is embossed to form an uneven pattern. Next, an ink mattized with an extender pigment is toned with a ratio of 80 for medium, 6 for black, 3 for red and 3 for red, and 9 for curing agent. To be filled by the wiping method.
【０００８】次に、１５０メッシュで深さ６０μの格子
型のミル押しで成型されたメッシュロールにて、ウレタ
ン樹脂をバインダーとするとともに、クリヤーを７３、
マットを１８、硬化剤を９の割合とした七分艶の透明コ
ーティング液を前記凹凸模様の凸部５のみにコーティン
グし、コート層６を形成させる。そして、ウレタン樹脂
などの硬化性樹脂をバインダーとし、体質顔料で艶消し
されるとともに、前記凹凸模様の凹部４内に充填したイ
ンキ３と同系色でやや弱い色のインキ、すなわちメジュ
ームを７６、黒を５、赤を２、黄を８、硬化剤を９の割
合で調色された艶消しインキを用いて、オーク柾目の導
管の模様でグラビア製版した導管版にて前記コート層６
の表面６ａに印刷し、模様印刷層７を形成して、化粧フ
ィルム１とする。Then, using a mesh roll formed by pressing a 150-mesh, 60-μ deep grid-type mill, the urethane resin was used as a binder and the clear was 73,
A transparent coating liquid having a matte of 18 and a hardening agent of a ratio of 9 is used to coat only the convex portions 5 of the concavo-convex pattern to form a coat layer 6. Then, using a curable resin such as urethane resin as a binder, the ink is matt with an extender pigment, and is an ink of a similar color to the ink 3 filled in the concave portion 4 of the uneven pattern, that is, a slightly weaker color, that is, a medium of 76, black. 5, a red 2, yellow 8 and a curing agent 9 were used to prepare a matte ink.
The pattern printing layer 7 is formed by printing on the surface 6a of the above, and the decorative film 1 is obtained.
【０００９】この化粧フィルム１によれば、コート層６
の表面６ａに形成された模様印刷層７を艶消しのインキ
で形成させたので、この模様印刷層７が光沢のあるコー
ト層６よりも視覚的に凹陥感をもたせることができ、ま
た、この模様印刷層７のインキを凹凸模様の凹部４内に
充填されたインキ３と異なる色合いとしたので、異なる
色の凹模様が形成される立体感を表現でき、導管部分に
目止めを施したようなリアルな木目模様を表現したフィ
ルムが得られる。また、この化粧フィルム１を図２に示
すようにベニヤ合板１０などに接着剤を用いて貼着すれ
ば、リアル感のある化粧合板１１が得られる。According to this decorative film 1, the coat layer 6
Since the pattern printing layer 7 formed on the surface 6a of the above is formed by the matte ink, the pattern printing layer 7 can give a more visually depressed feeling than the glossy coat layer 6, and Since the ink of the pattern printing layer 7 has a different shade from the ink 3 filled in the concave and convex portions 4, it is possible to express a three-dimensional effect in which concave patterns of different colors are formed, and it seems that the conduit portion is sealed. You can get a film that expresses a realistic grain pattern. If this decorative film 1 is attached to a veneer plywood 10 or the like with an adhesive as shown in FIG. 2, a decorative plywood 11 having a realistic appearance can be obtained.
【００１０】II．第２実施例 次に、第２の実施例について説明する。図３は本発明の
第２の実施例に係わる化粧フィルムの断面図である。こ
の第２の実施例の化粧フィルム２１は、まず、熱可塑性
樹脂フィルムである厚さ８０μのライトブラウン色の塩
化ビニル樹脂フィルムの一方の面に梨地加工を施し、他
方の印刷適正を有する面にオーク柾模様の色変化版で印
刷し、次いでこのオーク柾模様の木肌版で印刷して、こ
のフィルムに模様印刷層８を形成させる。上記色変化版
は、メジュームを８６、黒を０．５、赤を３．５、黄を
１０の割合に調色したインキを用い、木肌版は、メジュ
ームを８９．５、黒を３、赤を１．５、黄を６の割合に
調色したインキとする。II. Second Example Next, a second example will be described. FIG. 3 is a sectional view of a decorative film according to the second embodiment of the present invention. The decorative film 21 of the second embodiment is obtained by first applying satin finish to one surface of a light brown vinyl chloride resin film having a thickness of 80 μ, which is a thermoplastic resin film, and then applying the matte finish to the other surface having printability. The pattern printing layer 8 is formed on this film by printing with a color changing plate of the oak pattern and then printing with a wood surface plate of the oak pattern. The color-change plate uses an ink toned with a ratio of 86 for medium, 0.5 for black, 3.5 for red, and 10 for yellow. The wood-skin plate has 89.5 for medium, 3 for black, and red. Is 1.5 and yellow is 6 tones.
【００１１】次に、熱可塑性樹脂フィルムである厚さ８
０μの透明な塩化ビニル樹脂フィルムを基材フィルム２
とし、この基材フィルム２の裏面２ｂに、模様印刷層８
が形成された前記フィルムをラミネート貼着させるとと
もに、この基材フィルム２の表面２ａにオーク柾の導管
の凹凸模様をエンボスによって形成させる。この基材フ
ィルム２の裏面２ｂに貼着されるフィルムは隠蔽層９と
なる。次に、体質顔料で艶消しされたインキを、メジュ
ームを８０、黒を６、赤を２黄を３、硬化剤を９の割合
で調色し、このインキ３を前記エンボスによって形成さ
れた凹凸模様の凹部内にワイピング法によって充填させ
る。Next, a thickness of 8 which is a thermoplastic resin film.
Base film 2 of 0μ transparent vinyl chloride resin film
The pattern printing layer 8 is formed on the back surface 2b of the base film 2.
The film on which the film is formed is laminated and attached, and the concavo-convex pattern of a conduit of oak is formed on the surface 2a of the base film 2 by embossing. The film attached to the back surface 2b of the base film 2 serves as the hiding layer 9. Next, an ink mattized with an extender pigment was toned with a ratio of 80 for medium, 6 for black, 3 for red and 3 for red, and 9 for curing agent. The concave portion of the pattern is filled by the wiping method.
【００１２】次に、１５０メッシュで深さ６０μの格子
型のミル押しで成型されたメッシュロールにて、ウレタ
ン樹脂をバインダーとするとともに、クリヤーを６０、
マットを１７、黒を２、赤を３、黄を９、硬化剤を９の
割合とした七分艶の着色透明コーティング液を、前記凹
凸模様の凸部５のみにコーティングし、コート層６を形
成させる。そして、ウレタン樹脂などの硬化性樹脂をバ
インダーとし、体質顔料で艶消しされるとともに、メジ
ュームを７６、黒を５、赤を２、黄を８、硬化剤を９の
割合で調色された艶消しインキを用いて、オーク柾目の
導管の模様でグラビア製版した導管版にて前記コート層
６の表面６ａに印刷し、模様印刷層７を形成して、化粧
フィルム２１とする。Next, with a mesh roll formed by pressing a 150-mesh, 60-μ deep grid-type mill, the urethane resin was used as a binder and the clear was 60,
Matte 17, black 2, red 3, yellow 9 and hardener 9 in a ratio of 9% of a transparent transparent coating liquid is coated only on the convex portion 5 of the uneven pattern to form the coating layer 6. Let it form. Then, a curable resin such as urethane resin is used as a binder, and is matted with an extender pigment. At the same time, the medium is 76, black is 5, red is 2, yellow is 8, and a curing agent is toned at a ratio of 9. An erase ink is used to print on the surface 6a of the coat layer 6 with a conduit plate that is gravure-made in the pattern of oak-grained conduits to form a pattern-printed layer 7 to form a decorative film 21.
【００１３】この実施例の化粧フィルム２１によれば、
前述した第１の実施例と同様に、コート層６の表面６ａ
に形成された模様印刷層７を艶消しのインキで形成させ
たので、この模様印刷層７が光沢のあるコート層６より
も視覚的に凹陥感をもたせることができ、また、この模
様印刷層７のインキを凹凸模様の凹部４内に充填された
インキ３と異なる色合いとしたので、異なる色の凹模様
が形成される立体感を表現でき、導管部分に目止めを施
したようなリアルな木目模様を表現したフィルムが得ら
れる。また、基材フィルム２の裏面２ｂに着色されたフ
ィルム、すなわち隠蔽層９を形成させるとともに、基材
フィルム２と隠蔽層９の間に模様印刷層８を形成させた
ので、深みのある模様が表現でき、よりリアル感のある
フィルムを得ることができる。According to the decorative film 21 of this embodiment,
Similar to the above-described first embodiment, the surface 6a of the coat layer 6
Since the pattern printing layer 7 formed in 1) is formed with a matte ink, the pattern printing layer 7 can have a more visually depressed feeling than the glossy coat layer 6. Since the ink of No. 7 has a different color shade from the ink 3 filled in the concave and convex portions 4 of concave and convex pattern, it is possible to express a three-dimensional effect in which concave patterns of different colors are formed, and it is realistic that the conduit portion is sealed. A film expressing a grain pattern can be obtained. In addition, since the colored film, that is, the hiding layer 9 is formed on the back surface 2b of the base film 2, and the pattern printing layer 8 is formed between the base film 2 and the hiding layer 9, a deep pattern is formed. It is possible to express and obtain a more realistic film.
【００１４】なお、上記各実施例の他に、例えば、第１
の実施例のような凹凸模様の凸部分にコート層を形成さ
せたのち、このコート層よりも艶のある硬化性樹脂イン
キを用いてコート層の表面に絵柄を印刷して、模様印刷
層を形成させてもよい。この場合、コート層が、その表
面の模様印刷層より光沢が低いので、この模様印刷層よ
りも凹陥状に見え、さらに、凹凸模様の凹部が形成され
ていることから、このフィルムでは凹部が二重に表現さ
れるようになる。In addition to the above embodiments, for example, the first
After forming a coat layer on the convex portion of the uneven pattern as in the example of 1., a pattern is printed on the surface of the coat layer using a curable resin ink that is glossier than this coat layer to form a pattern printing layer. It may be formed. In this case, since the coating layer has a lower gloss than the pattern printing layer on the surface thereof, it looks more concave than the pattern printing layer, and since the concave and convex portions are formed, this film has two concave portions. It will be expressed heavily.
【００１５】また、第２の実施例のような凹凸模様の凸
部分に着色コート層を形成させたのち、この着色コート
層よりも艶のある硬化性樹脂インキを用いて着色コート
層の表面に絵柄を印刷し、模様印刷層を形成させてもよ
い。この場合も、着色コート層が、その表面の模様印刷
層より光沢が低いので、この模様印刷層よりも凹陥状に
見え、さらに、凹凸模様の凹部が形成されていることか
ら、このフィルムでは凹部が二重に表現されるようにな
る。Further, after a colored coat layer is formed on the convex portion of the uneven pattern as in the second embodiment, the surface of the colored coat layer is coated with a curable resin ink which is glossier than the colored coat layer. A pattern may be printed to form a pattern printing layer. In this case as well, the gloss of the colored coating layer is lower than that of the pattern printing layer on the surface of the colored coating layer, so that it looks more concave than that of the pattern printing layer. Will be double expressed.
【００１６】さらに、上述した第１の実施例の化粧フィ
ルム１などの裏面、すなわち基材フィルム２の裏面２ｂ
に、図４に示すようなグラビア印刷などの印刷による模
様印刷層８を形成したり、またこの模様印刷層を形成し
たのち、図５に示すように、この模様印刷層８を覆うよ
うに透明なフィルムなどによる透明層１２や、ハーフミ
ラー材質の金属蒸着フィルム層などを形成してもよい。
このような化粧フィルム３１，４１では、基材フィルム
裏面２ｂの模様印刷層８により、深みのある表現が可能
となるとともに、金属蒸着フィルム層によって光が反射
して表面より見える模様に陰影や立体感などの模様が浮
きでたりなど、複雑な模様を醸しだすことができる。Further, the back surface of the decorative film 1 or the like of the first embodiment described above, that is, the back surface 2b of the base material film 2.
Then, a pattern printing layer 8 is formed by printing such as gravure printing as shown in FIG. 4, or after this pattern printing layer is formed, as shown in FIG. 5, it is transparent so as to cover the pattern printing layer 8. The transparent layer 12 made of a film or the like, or the metal vapor deposition film layer made of a half mirror material may be formed.
In such decorative films 31 and 41, the pattern printing layer 8 on the back surface 2b of the base film enables a deeper expression, and the metal vapor deposition film layer reflects light so that the pattern can be seen from the front surface with a shadow or a three-dimensional shape. It is possible to create complex patterns such as feeling patterns.
【００１７】[0017]
【発明の効果】以上説明したように本発明による化粧フ
ィルムでは、基材フィルムの表面に形成される凹凸模様
の凸部のみにコート層を形成させ、このコート層の表面
にさらに模様印刷層を形成させたので、視覚的に深みが
増加し、模様が立体的に表現されるフィルムになるとと
もに、これらコート層と、このコート層の表面の模様印
刷層、及び凹凸模様の凹部内に充填される、各インキの
光沢の度合いをそれぞれ変えることで、視覚的に凹陥状
をもたせることができ、リアル感のある化粧フィルムを
得ることができるという効果がある。また、上記各部分
の色合いをそれぞれ異なるように設定すれば、異なる色
の凹模様が形成される立体感を表現でき、例えば導管部
分に目止めを施したようなリアルな木目模様を表現した
フィルムを得ることができるという効果がある。さら
に、基材フィルムの裏面に模様印刷層を形成させると、
深みのある模様が表現でき、よりリアル感のある化粧フ
ィルムを得ることができる。また、基材フィルムの裏面
に、模様印刷層を形成するとともに、この模様印刷層を
覆うように透明フィルムによる透明層を形成したり、ハ
ーフミラーなどの金属蒸着フィルムを貼着して金属蒸着
フィルム層を形成させれば、深みのある表現が可能とな
るとともに、金属蒸着フィルム層などによって光が反射
して表面より見える模様に陰影や立体感などの模様が浮
きでたりなど、複雑な模様を醸しだすことができるとい
う効果がある。As described above, in the decorative film according to the present invention, the coating layer is formed only on the convex portions of the uneven pattern formed on the surface of the base film, and the pattern printing layer is further formed on the surface of the coating layer. Since it is formed, the depth is visually increased, and the film becomes a three-dimensional pattern, and at the same time, these coat layers, the pattern print layer on the surface of this coat layer, and the recesses of the uneven pattern are filled. By changing the degree of gloss of each ink, it is possible to visually give a concave shape, and it is possible to obtain a realistic decorative film. Also, by setting the shades of the above parts differently, it is possible to express a three-dimensional effect in which concave patterns of different colors are formed, and for example, a film that expresses a realistic wood grain pattern such as a pipe part with a seal. There is an effect that can be obtained. Furthermore, when a pattern printing layer is formed on the back surface of the base film,
A deep pattern can be expressed, and a more realistic makeup film can be obtained. In addition, a pattern printing layer is formed on the back surface of the base film, and a transparent layer made of a transparent film is formed so as to cover the pattern printing layer, or a metal deposition film such as a half mirror is attached to the metal deposition film. By forming a layer, it is possible to create a deeper expression and to create complex patterns such as patterns such as shadows and three-dimensional effects that are visible on the surface due to light being reflected by the metal deposition film layer. The effect is that it can be brought out.
【図１】本発明による化粧フィルムの第１の実施例を示
す断面図FIG. 1 is a sectional view showing a first embodiment of a decorative film according to the present invention.
【図２】同実施例による化粧フィルムを用いた化粧合板
を示す断面図FIG. 2 is a sectional view showing a decorative plywood using a decorative film according to the same example.
【図３】本発明による化粧フィルムの第２の実施例を示
す断面図FIG. 3 is a sectional view showing a second embodiment of the decorative film according to the present invention.
【図４】本発明による化粧フィルムの他の実施例を示す
断面図FIG. 4 is a sectional view showing another embodiment of the decorative film according to the present invention.
【図５】本発明による化粧フィルムの他の実施例を示す
断面図FIG. 5 is a sectional view showing another embodiment of the decorative film according to the present invention.
１，２１，３１，４１…化粧フィルム ２…基材フィルム ２ａ…表面 ２ｂ…裏面 ３…インキ ４…凹部 ５…凸部 ６…コート層（着色コート層） ６ａ…コート層の
表面 ７…模様印刷層 ８…模様印刷層 ９…隠蔽層 １２…透明層1, 21, 31, 41 ... Decorative film 2 ... Base film 2a ... Front surface 2b ... Back surface 3 ... Ink 4 ... Recessed portion 5 ... Convex portion 6 ... Coat layer (colored coat layer) 6a ... Coat layer surface 7 ... Pattern printing Layer 8 ... Pattern printing layer 9 ... Concealing layer 12 ... Transparent layer
Claims (8)
なる基材フィルムの表面に、エンボスによる凹凸模様を
形成し、該凹凸模様の凹部内にインキを充填するととも
に、前記凹凸模様の凸部のみにコーティングを施し、コ
ート層を形成させ、かつ、該コート層の表面に硬化性樹
脂をバインダーとしたインキで模様印刷層を形成したこ
とを特徴とする化粧フィルム。1. An uneven pattern by embossing is formed on the surface of a substrate film made of a transparent or translucent thermoplastic resin, and ink is filled in the concave part of the uneven pattern, and only the convex part of the uneven pattern is formed. A decorative film, characterized in that a coating layer is applied to form a coating layer, and a pattern printing layer is formed on the surface of the coating layer with an ink containing a curable resin as a binder.
であることを特徴とする請求項１記載の化粧フィルム。2. The decorative film according to claim 1, wherein the coating layer is a colored coating layer.
刷層のインキを前記コート層とは異なる光沢のインキを
用いて形成させたことを特徴とする請求項１又は請求項
２記載の化粧フィルム。3. The makeup according to claim 1 or 2, wherein the ink of the pattern printing layer formed on the surface of the coat layer is formed by using an ink having a gloss different from that of the coat layer. the film.
形成したことを特徴とする請求項１乃至請求項３のいず
れかに記載の化粧フィルム。4. The decorative film according to claim 1, wherein a pattern printing layer is formed on the back surface of the base film.
透明若しくは半透明層とを形成したことを特徴とする請
求項１乃至請求項３のいずれかに記載の化粧フィルム。5. The decorative film according to claim 1, wherein a pattern printing layer and a transparent or semi-transparent layer are formed on the back surface of the base film.
不透明な隠蔽層とを形成したことを特徴とする請求項１
乃至請求項３のいずれかに記載の化粧フィルム。6. A pattern printing layer and an opaque concealing layer are formed on the back surface of the base film.
To the decorative film according to claim 3.
金属蒸着フィルム層とが形成されたことを特徴とする請
求項１乃至請求項３のいずれかに記載の化粧フィルム。7. The decorative film according to claim 1, wherein a pattern printing layer and a metal vapor deposition film layer are formed on the back surface of the base film.
剤を含有した艶消し半透明インキ又は艶消し着色インキ
であることを特徴とする請求項１乃至請求項３のいずれ
かに記載の化粧フィルム。8. The makeup according to claim 1, wherein the ink filled in the recess is a matte translucent ink or a matte colored ink containing a matting agent. the film.