GB1236598A - Treatment of deep-drawing steel - Google Patents

Treatment of deep-drawing steel

Info

Publication number
GB1236598A
GB1236598A GB1585568A GB1585568A GB1236598A GB 1236598 A GB1236598 A GB 1236598A GB 1585568 A GB1585568 A GB 1585568A GB 1585568 A GB1585568 A GB 1585568A GB 1236598 A GB1236598 A GB 1236598A
Authority
GB
United Kingdom
Prior art keywords
cooling
deep
treated
drawing steel
niobium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB1585568A
Inventor
Ian Frank Hughes
Roger Charles Hudd
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Richard Thomas and Baldwins Ltd
Original Assignee
Richard Thomas and Baldwins Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Richard Thomas and Baldwins Ltd filed Critical Richard Thomas and Baldwins Ltd
Priority to GB1585568A priority Critical patent/GB1236598A/en
Publication of GB1236598A publication Critical patent/GB1236598A/en
Expired legal-status Critical Current

Abstract

1,236,598. Heat-treating steel sheet; alloys. RICHARD THOMAS & BALDWINS Ltd. March 27, 1969 [April 2, 1968], No. 15855/68. Heading C7A. [Also in Divisions B3] Deep-drawing steel containing 0À01% to 0À1% carbon, 0 to 0À5% manganese, and 0À02% to 0À5% niobium is solution-treated at 900‹ to 1400‹ C., treated to precipitate niobium carbide as particles not exceeding 2000 Angstroms in average size, cold rolled and annealed. The desired particle size may be achieved by control of the cooling conditions after hot rolling (e.g. by finishing at 800‹-1000‹C., coiling at 400‹-800‹C. and cooling in the coil) or by cooling from the rolling temperature at such a rate that niobium carbide is retained in solution followed by reheating e.g. to 600‹ to 950‹C.
GB1585568A 1968-04-02 1968-04-02 Treatment of deep-drawing steel Expired GB1236598A (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
GB1585568A GB1236598A (en) 1968-04-02 1968-04-02 Treatment of deep-drawing steel

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
GB1585568A GB1236598A (en) 1968-04-02 1968-04-02 Treatment of deep-drawing steel

Publications (1)

Publication Number Publication Date
GB1236598A true GB1236598A (en) 1971-06-23

Family

ID=10066736

Family Applications (1)

Application Number Title Priority Date Filing Date
GB1585568A Expired GB1236598A (en) 1968-04-02 1968-04-02 Treatment of deep-drawing steel

Country Status (1)

Country Link
GB (1) GB1236598A (en)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4178417A (en) * 1977-03-23 1979-12-11 The Japan Steel Works, Ltd. Clad steel
EP0024437A1 (en) * 1979-02-27 1981-03-11 Kawasaki Steel Corporation Process for producing non-aging cold-rolled steel sheets
EP0041354A1 (en) * 1980-05-31 1981-12-09 Kawasaki Steel Corporation Method for producing cold rolled steel sheets having a noticeably excellent formability
FR2689907A1 (en) * 1992-04-13 1993-10-15 Toyo Kohan Co Ltd Process for the production of continuously annealed steel sheet and sheet produced by this process

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4178417A (en) * 1977-03-23 1979-12-11 The Japan Steel Works, Ltd. Clad steel
EP0024437A1 (en) * 1979-02-27 1981-03-11 Kawasaki Steel Corporation Process for producing non-aging cold-rolled steel sheets
EP0024437A4 (en) * 1979-02-27 1981-07-16 Kawasaki Steel Co Process for producing non-aging cold-rolled steel sheets.
EP0041354A1 (en) * 1980-05-31 1981-12-09 Kawasaki Steel Corporation Method for producing cold rolled steel sheets having a noticeably excellent formability
FR2689907A1 (en) * 1992-04-13 1993-10-15 Toyo Kohan Co Ltd Process for the production of continuously annealed steel sheet and sheet produced by this process

Similar Documents

Publication Publication Date Title
GB1276309A (en) Process for heat-treating electromagnetic steel sheets
GB1450131A (en) Method for manufacturing a steel sheet
GB1278869A (en) High-strength low-alloy steels having improved formability
GB1462705A (en) Heat treatment of weld metals
GB1187213A (en) Method of processing Metastable Beta Titanium Alloy
GB1308092A (en) High strength low alloy steels
GB1266941A (en)
GB1236598A (en) Treatment of deep-drawing steel
GB1422766A (en) Processing for high permeability silicon steel
GB1428902A (en) Processing for high permeability silicon steel
GB1334022A (en) Process for continuously annealing steels
JPS56102562A (en) Manufacture of al alloy plate for packing
GB1478739A (en) Processing for high permeability silicon steel
GB1322135A (en) Method of producing a minimum-ridging type
GB1311104A (en) Dynamo steel
GB1308484A (en) Continuous annealing process of cold reduced steel strip for drawing
GB1419552A (en) Steels
GB1338285A (en) High tensile strength low alloy steels
GB1233522A (en)
GB1191317A (en) Weldable High Strength Structural Steel not Embrittled by Stress-Relieving Annealings
GB1443466A (en) Steels
US2405946A (en) Production of non-aging steel
GB1320418A (en) Steels
FR2077581A1 (en) Low carbon steel sheets for car bodies
GB1478740A (en) Processing for high permeability silicon steel