FI75852B - Foernaetningsbar polyetenkomposition, som aer speciellt anvaendbar i en rotationsgjutningsprocess och anvaendning av kompositionen. - Google Patents
Foernaetningsbar polyetenkomposition, som aer speciellt anvaendbar i en rotationsgjutningsprocess och anvaendning av kompositionen. Download PDFInfo
- Publication number
- FI75852B FI75852B FI830437A FI830437A FI75852B FI 75852 B FI75852 B FI 75852B FI 830437 A FI830437 A FI 830437A FI 830437 A FI830437 A FI 830437A FI 75852 B FI75852 B FI 75852B
- Authority
- FI
- Finland
- Prior art keywords
- polyethylene
- weight
- tert
- bis
- curing agent
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K5/00—Use of organic ingredients
- C08K5/36—Sulfur-, selenium-, or tellurium-containing compounds
- C08K5/37—Thiols
- C08K5/372—Sulfides, e.g. R-(S)x-R'
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F255/00—Macromolecular compounds obtained by polymerising monomers on to polymers of hydrocarbons as defined in group C08F10/00
- C08F255/02—Macromolecular compounds obtained by polymerising monomers on to polymers of hydrocarbons as defined in group C08F10/00 on to polymers of olefins having two or three carbon atoms
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K5/00—Use of organic ingredients
- C08K5/49—Phosphorus-containing compounds
- C08K5/51—Phosphorus bound to oxygen
- C08K5/52—Phosphorus bound to oxygen only
- C08K5/524—Esters of phosphorous acids, e.g. of H3PO3
Claims (18)
1. Polyetenkomposition, som är speciellt använd-bar i en rotationsgjutningsprocess, känneteck- n a d därav, att den omfattar polyetylen med en täthet 3 5 av 0,920 - 0,970 g/cm och ett smältindex i omrädet av 10 - 35 dg/min, 0,3 - 1,3 vikt-%, beräknat pä polyety-lenet, av ett bis(tert.-alkylperoxialkyl)bensen, 0,2 - 1,5 vikt-%, beräknat pä polyetylenet, av ett hjälphärd-ningsmedel, vilket valts frän gruppen bestäende av tri- 10 allylcyanurat, triallylisocyanurat och 1,2-polybuta-dien, 0,01 - 0,05 vikt-%, beräknat pä polyetylenet, av en hindrad fenolisk antioxidant, och 0,01 - 0,2 vikt-%, beräknat pä polyetylenet, av en sekundär antioxidant, vilken valts frän gruppen bestäende av di(stearyl)-penta- 15 erytritoldifosfit, tris-di-(tert.-butylfenyl)fosfit, di- lauryltiodipropionat och bis(2,4-di-tert.-butylfenyl)-pentaerytritoldifosfit.
2. Komposition enligt patentkravet 1, k ä n -netecknad därav, att hjälphärdningsmedlet är 20 1,2-polybutadien.
3. Komposition enligt patentkravet 1, k ä n -netecknad därav, att hjälphärdningsmedlet är triallylcyanurat eller triallylisocyanurat.
4. Komposition enligt nägot av patentkraven 25 1-3, kännetecknad därav, att mängden hjälphärdningsmedel är 0,4 - 0,7 vikt-% av polyetylenet.
5. Komposition enligt nägot av patentkraven 1-4, kännetecknad därav, att polyetylenet är en homopolymer av etylen.
6. Komposition enligt nägot av patentkraven 1-4, kännetecknad därav, att polyetylen et är en sampolymer av etylen och ett - C^Q-d-olefin.
7. Komposition enligt nägot av patentkraven 1-5, kännetecknad därav, att polyety- 35 lenet har en täthet av 0,950 - 0,970 g/cm^.
8. Komposition enligt nägot av patentkraven 1-7, kännetecknad därav, att peroxiden är bis(tert.-butylperoxiisopropyl)bensen. 20 7 5 8 5 2
9. Komposition enligt nägot av patentkraven 1-8, kännetecknad därav, att den sekun- dära antioxidanten är di(stearyl)-pentaerytritoldifosfit, tris-di-tert.-butylfenylfosfit, dilauryltiodipropionat 5 eller bis(2,4-di-tert.-butylfenyl)pentaerytritoldifosfit.
10. Komposition enligt nägot av patentkraven 1-9, kännetecknad därav, att mängden peroxid är 0,4 - 0,9 vikt-% av polyetylenet.
11. Komposition enligt patentkravet 1 eller 3, 10 kännetecknad därav, att polyetylenets tät- 3 het är 0,950 - 0,970 g/cm , peroxiden är bis(tert.-butyl-peroxiisopropyl)bensen i en mängd av 0,4 - 0,9 vikt-% av polyetylenet, mängden hjälphärdningsmedel är 0,4 - 0,7 vikt-% av polyetylenet och den sekundära antioxidanten 15 är tris-di-tert.-butylfenylfosfit.
12. Användning av en komposition, vilken omfattar polyetylen med en täthet av 0,920 - 0,970 g/cm3 och ett smältindex i omrädet av 10-35 dg/min, 0,3-1,3 vikt-%, be-räknat pä polyetylenet, av ett bis (tert.-alkylperoxidalkyl)- 20 bensen, 0,2 - 1,5 vikt-%, beräknat pä polyetylenet, av ett hjälphärdningsmedel, vilket valts frän gruppen bestäende av triallylcyanurat, triallylisocyanurat och 1,2-poly-butadien, 0,01 - 0,05 vikt-%, beräknat pä polyetylenet, av en hindrad fenolisk antioxidant och 0,01 - 0,2 vikt-%, 25 beräknat pä polyetylenet, av en sekundär antioxidant, vilken valts frän gruppen bestäende av di(stearyl)-penta-erytritoldifosfit, tris-di(tert.-butylfenyl)fosfit, dilauryltiodipropionat och bis(2,4-di-tert.-butylfenyl)-pentaerytritoldifosfit, i en rotationsgjutningsprocess 30 för framställning av polyetylenprodukter.
13. Användning enligt patentkravet 12, kännetecknad därav, att polyetylenet har en täthet av 0,950 - 0,970 g/cm3.
14. Användning enligt patentkravet 12 eller 13, 35 kännetecknad därav, att hjälphärdnings- medlet är 1,2-polybutadien.