FI116138B - Förfarande för tillverkning av mineraliserad Portland-cementklinker - Google Patents
Förfarande för tillverkning av mineraliserad Portland-cementklinker Download PDFInfo
- Publication number
- FI116138B FI116138B FI963418A FI963418A FI116138B FI 116138 B FI116138 B FI 116138B FI 963418 A FI963418 A FI 963418A FI 963418 A FI963418 A FI 963418A FI 116138 B FI116138 B FI 116138B
- Authority
- FI
- Finland
- Prior art keywords
- sulfur
- fluorine
- feedstock
- weight
- containing component
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B7/00—Hydraulic cements
- C04B7/36—Manufacture of hydraulic cements in general
- C04B7/38—Preparing or treating the raw materials individually or as batches, e.g. mixing with fuel
- C04B7/42—Active ingredients added before, or during, the burning process
- C04B7/421—Inorganic materials
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Ceramic Engineering (AREA)
- Inorganic Chemistry (AREA)
- Materials Engineering (AREA)
- Structural Engineering (AREA)
- Organic Chemistry (AREA)
- Curing Cements, Concrete, And Artificial Stone (AREA)
- Furnace Details (AREA)
- Artificial Fish Reefs (AREA)
Claims (7)
1. Metod för att framställa mineraliserad portlandce- mentklinker, där nämnda klinker har en svavelhalt av minst ; 1,5 vikt-% beräknat som S03 och en fluorhalt av minst 0,15 vikt-% beraknat som F, i ett ugnssystem, där räblandningen ‘1' i följd utsättes för förvärmning, kalcinering, bränning • V 35 och slutligen kylning, varvid räblandnings-tillflödes- : : materialets sammansättning är sädan att ett eller bäda av (··.( de följande villkoren uppfylles: 1. svavelhalten Xs är högst 1,2 vikt-% beräknat som • * 116138 12 S03 pä en LOI-fri basis, 2. fluorhalten XF är högst 0,14 vikt-% beräknat pä en LOI-fri basis, och väri en svavelhaltig komponent eller en fluorhaltig 5 komponent eller bäda införes i strömmen av tillflödesmate-rial vid en punkt i processen där temperaturen för strömmen av tillflödesmaterial är högre än 700 °C, mängden svavelhaltig komponent eller fluorhaltig komponent eller bäda är tillräcklig för att tillförsäkra om att den färdiga 10 portlandcementklinkern uppvisar erforderlig svavel- och fluorhalt.
2. Metod enligt patentkrav 1, kännetecknad av att Xs är högst 0,8 vikt-% eller XF är högst 0,10 vikt-% eller bäda. 15
3. Metod enligt patentkrav 1, kännetecknad av att Xs är högst 0,4 vikt-% eller XF är högst 0,06 vikt-% eller bäda.
4. Metod enligt nägot av patentkraven 1-3, kännetecknad 20 av att tillsatsen av svavelhaltig komponent och eller fluorhaltig komponent eller bäda genomföres i den zon där rä-blandnings-tillflödesmaterialet förvärmes.
5. Metod enligt nägot av patentkraven 1-4, kännetecknad '* 25 av att ugnssystemet är sädan som har en särskild kalcine- ’ * ringszon, och att den svavelhaltiga komponenten och/eller ... ’ den fluorhaltiga komponenten tillföres denna kalcinerings- : ·,: zon. 1
6. Metod enligt nägot av patentkraven 1-5, kännetecknad av att den svavelhaltiga produkten tillföres säsom natur-ligt gips, hemihydrat (bassanit), anhydrit, langbeinit, baryter eller andra svavelhaltiga mineral innehällande I kalcium eller magnesium, eller att mineraliseraren är en ; 35 svavelhaltig spillprodukt vald bland sulfater, säsom FGD- : (Flue Gas Desiilphurization)-gips, sulfit- eller sulfid- ,···, haltiga avsvavlingsprodukter, sulfathaltiga industriella .!’! biprodukter, säsom ammonium- eller järnbaserade sulfater, 116138 13 dartim frän ceinentugn, svavelhaltigt bränsle, säsom petkoks eller högsvavligt koi eller oija.
7. Metod enligt nägot av patentkraven 1-5, kännetecknad 5 av att den fluorhaltiga produkten tillföres säsom fluorit, fluorapatit, kryolit eller industriella biprodukter inne-hällande fluor, säsom hexafluorkiselsyra eller silikontet-rafluorid, företrädesvis fluorit. 10 • 3 • · 1 t f t • · t I » k t < ·