EP0000209A1 - Polarisator für sichtbares Licht bestehend aus einem mit Jod gefärbten Polyvinylalkoholfilm und Verfahren zu seiner Herstellung - Google Patents

Polarisator für sichtbares Licht bestehend aus einem mit Jod gefärbten Polyvinylalkoholfilm und Verfahren zu seiner Herstellung Download PDF

Info

Publication number
EP0000209A1
EP0000209A1 EP78200002A EP78200002A EP0000209A1 EP 0000209 A1 EP0000209 A1 EP 0000209A1 EP 78200002 A EP78200002 A EP 78200002A EP 78200002 A EP78200002 A EP 78200002A EP 0000209 A1 EP0000209 A1 EP 0000209A1
Authority
EP
European Patent Office
Prior art keywords
iodine
polyvinyl alcohol
stained
potassium iodide
bath
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
EP78200002A
Other languages
English (en)
French (fr)
Other versions
EP0000209B1 (de
Inventor
Norman William Schuler
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Polaroid Corp
Original Assignee
Polaroid Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Polaroid Corp filed Critical Polaroid Corp
Publication of EP0000209A1 publication Critical patent/EP0000209A1/de
Application granted granted Critical
Publication of EP0000209B1 publication Critical patent/EP0000209B1/de
Expired legal-status Critical Current

Links

Images

Classifications

    • G—PHYSICS
    • G02—OPTICS
    • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
    • G02B5/00—Optical elements other than lenses
    • G02B5/30—Polarising elements
    • G02B5/3025—Polarisers, i.e. arrangements capable of producing a definite output polarisation state from an unpolarised input state
    • G02B5/3033—Polarisers, i.e. arrangements capable of producing a definite output polarisation state from an unpolarised input state in the form of a thin sheet or foil, e.g. Polaroid

Definitions

  • Linear light polarizers in general owe to the anisotropic character of their transmitting medium their properties of selectively passing radiation vibrating along a given electromagnetic radiation vector and absorting electromagnetic radiation vibrating along a second given electromagnetic radiation vector.
  • Dichroic polarizers are linear polarizers of the absorptive variety since they owe their polarizing capabilities to the vectorial anisotropy of their absorption of incident lightwaves. Light entering a dichrcic medium encounters two different absorption coefficients, one low and one high. The emerging light vibrates predominantly in the direction of low absorption.
  • Polyvinyl alcohol film polarizers generally comprise a plastic support, which may be any suitable isotropic material and is preferably cellulose acetate butyrate.
  • the support gives the film dimensional stability and additionally serves as a cover or protective element. It must naturally be transparent.
  • the most widely used type of synthetic polarizer is the polyvinyl alcohol-iodine complex polarizer. It consists of linear polyiodide contained within a polyvinyl alcohol helix. By orienting the polyvinyl alcohol matrix unidircctionally the transition moments of the absorbers are also so oriented and the material becomes visibly dichroic.
  • iodine stained dichroic light polarizing elements 'involves stretching polyvinyl alcohol and subsequently dyeing the material with a dichroic stain containing iodine and is well known. It is disclosed, for example, in U.S. Patent No. 2,237,567.
  • a cast sheet or film of polyvinyl alcohol is first formed from an aqueous solution of the material.
  • the dried cast sheet is then heated to a temperature at which it can be extended by stretching, preferably in a moist atmosphere.
  • the stretched sheet may be bonded to a supporting sheet, as has been discussed above.
  • a dichroic stain may be applied to one or both surfaces of the sheet..
  • a major improvement comprising forming a protective surface layer on the iodine stained polyvinyl alcohol light polarizer.
  • This surface layer comprises an ester of polyvinyl alcohol, the ester being of a polybasic acid or a derivative of such an acid, particularly an inorganic polybasic acid, and more particularly boric acid, thereby providing a hybrid form of polyvinyl alcohol-polyvinyl borate.
  • the protective layer is preferably formed by treating the stained polarizing element with a berating solution containing free boric acid or a derivative that will react to form the ester.
  • the ester formed on the surface of the light polarizer is believed to be polyvinyl orthoborate.
  • the treatment is said to improve greatly the stability of the light polarizer not only against heat but also against moisture and ultraviolet radiation.
  • the esterification reaction may be accompanied by sore decrease in the degree of molecular orientation and loss of stain in the reacted layer. This in turn may cause a loss in the dichroism of the sheet and a deterioration in transmission running as high as from 5 to 10 percent of incident light.
  • the predominant colour of the sheet also changes toward the blue. Thus the sheet becomes less efficient in its overall blue adsorption.
  • the diminution in the blue dichroic absorption, or darkening, of a borated polarizer can be prevented by eliminating the iodine from so much of the surface layer of the sheet as will be penetrated by the boric acid solution.
  • One way of eliminating this iodine is to wash the sheet with water after staining and before treatment with the borating solution.
  • a superior technique for avoiding the loss of blue absorption involves incorporating a high level of potassium iodide in the borating solution. Apparently this reinforces the dichromophore responsible for absorption in the blue range. After the material has been borated and dried, excellent blue dichromophore stability and a high level of blue absorption is maintained.
  • the purpose behind the invention has been to avoid the aforementioned "red leak" problem that arises in iodine stained polyvinyl alcohol light polarizing elements.
  • a light polarizing element according to the invention comprises a uniaxially stretched film of polyvinyl alcohol stained with iodine and which has a surface layer comprising a polyvinyl borate and potassium iodide and is characterised in that zinc ions have been absorbed into the surface layer after staining.
  • a method according to the invention of preparing a light polarizing element comprises .staining with an iodine solution a uniaxially stretched film of polyvin) 1 alcohol and treating the stained film with an aqueous borating solution containing potassium iodide and is characterised in that zinc ions are incorporated into the polarizing element after the staining.
  • the zinc ions be introduced after the element has been stained with the iodine and preferably they are introduced at the same time as the surface treatment of the element to form the polyvinyl borate.
  • the zinc ions are included in the borating solution.
  • the zinc ions may be provided by any ionisable zinc compound, for instance., zinc salts such as zinc chloride, zinc iodide and zinc sulphate. Most preferably they are provided by incorporating zinc chloride into the borating solution.
  • the borate component of the borating solution may be provided in conventional manner as described above, for example by use of a solution of boric acid.
  • the amount of zinc ion incorporated into the polarizing element must naturally be such as to give the desired reduction or elimination of red leak and the optimum amount can be found by simple experiment. Suitable amounts can be defined as being of the concentration effective to stabilise absorption of red light by the polarizer against degradation on heating.
  • the borating solution prevents the iodine stain from being removed from the sheet during processing. If the iodine stained material is treated merely with a solution containing potassium iodide and zinc chloride and no boric acid, much of the active iodine is removed.
  • the dichroic complex formed by polyvinyl alcohol and iodine occurs in a family of varying chain lengths, for example, triiodide, pentaiodide, etc. Since the spectral position of the absorption peaks depends upon the dichromophore chain lengths it can be seen that there will be an optimum relative concentration of short and long chain units resulting in the highest efficiency for the various segments of the visible region.
  • the presence of zinc ion in the polarizer is thought to retard degradation on heating cf the dichromophore responsible for red absorption. This dichroic red. degradation is apparently increased by the potassium iodide acting in conjunction with the dichromophore responsible for blue absorption.
  • the zinc ion apparently stabilises the red absorption of iedine-stained polarizers and inhibits degradation on heating of the dichronophore responsible for such absorption.
  • a polyvinyl alcohol sheet from 0.038 to 0.051 mm in thickness is stretched unidirectionally by techniques well known to the art to between 3.5 and 4 times its normal dimensions.
  • the stretched polyvinyl alcohol sheet is laminated to one side of a layer of cellulose acetate butyrate which is between 0.127 and 0.343 mm in thickness.
  • the cellulose acetate butyrate sheet may have on its surface opposed to its surface laminated to the stretched polyvinyl alcohol a mar resistent coating as is disclosed, for example, in U.S. Patent No. 3,097,106.
  • the cellulose acetate butyrate may be laminated to the polyvinyl alcohol sheet by any suitable method known to the art and in particular may be laminated by means of any suitable adhesive; but preferably one comprising a solution of polyvinyl alcohol.
  • the cellulose acetate butyrate material may contain isotropic dyes which provide cosmetic properties such as tinting.
  • the exposed side of the stretched polyvinyl alcohol is next passed over the surface of an iodine staining bath and essentially floats along the surface.
  • the bath is preferably a mixture of iodine, potassium iodide and water, which is preferably of the composition described below.
  • Excess iodine stain is wiped off and the sheet is then floated on a borating composition bath containing potassium iodide, boric acid, zinc chloride and water, preferably of the composition described below. It is next wiped dry, baked, and may then be laminated to another sheet of cellulose acetate butyrate to provide total protection on both sides of the polarizer.
  • Figure 1 is a schematic illustration of the process of the present invention and each of Figures 2 to 6 is a curve of optical density of an iodine stained light polarizer versus wavelength.
  • Figure 5 is the curve of a polarizer according to the invention while the others are comparative.
  • a film of polyvinyl alcohol approximately 0.038 mm in thickness is uniaxially stretched to 3.6 times its original dimension.
  • the stretched sheet is then laminated to a sheet of cellulose acetate butyrate upon which is coated a film of polyethyleneglycol dimethylacrylate by the general method described in U.S. Patent No. 3,097,106.
  • the cellulose acetate butyrate is laminated to the polarizer by means of a suitable adhesive, e.g. an adhesive comprising polyvinyl alcohol, methanol, a crossl.inking agent and water and is preferably 0.381 mm in thickness.
  • a roll of this laminated, stretched polyvinyl alcohol-cellulose acetate butyrate material 1 is conducted over a suitable roll 2 and drawn across the surface of an iodine stain bath 3.
  • the polyvinyl alcohol layer is in contact with the surface of the bath and the cellulose acetate butyrate layer is the upper layer and generally held out of contact with the surface of the bath.
  • Rolls 4 are mere guide rolls and do not effect the floating of the layer across the surface of the bath.
  • the temperature of the bath is held at 35°C and the residence time of any given point on the web across the surface of the bath is about 15 seconds.
  • wiper 5 which may be no more than a damp towel and is then directed to bath 6 where, in a manner similar to its treatment in bath 3, it is drawn across the surface of a borating composition.
  • the temperature of the borating bath is about 165°F and the residence time of any given point of the web in the bath is 25 to 30 seconds.
  • a second wiping station 7 which is preferably a porous roll with toweling on the outside and vacuum applied inside the roll. To keep the roll damp a gentle water spray is applied to its outside surface. After being toweled dry the web is directed through oven S where it is exposed to air currents of about 94°C to dry the web. .It is then rerolled at station 9.
  • the exposed samples were analysed on a Cary 14 spectrophotometer to determine the optical density of the light polarizing element as a function of wavelength.
  • the solid line represents the optical density of the sample prior to being exposed to 15 hours of 75°C dry heat and the dashed lines indicate the response of the sample after exposure for 15 hours to 75°C dry heat.
  • the curves labelled d relate to the optical density obtained when the transmission axis of the sample polarizer is crossed with the polarization of the spectrophotometer polarizer and curves labelled d y indicate the response of the sample polarizer when its transmission axis is parallel to the polarization axis of the spectrophotometer polarizer.
  • This film was exposed to a first bath containing iodine and potassium iodide and a second bath in which both the potassium iodide and zinc chloride were omitted.
  • The-first bath accordingly comprised iodine, potassium iodide, and water in a weight ratio of 1/15.82/328 and the second bath comprised boric acid and water in a weight ratio of 1/20.54.
  • the resultant curve is shown in Figure 2.
  • This film was manufactured with a first bath which also comprised iodine, potassium iodide and water in a weight ratio of 1/15.82/328; but the second bath comprised boric acid, zinc chloride and water in a weight ratio of 1 25/1/25.67.
  • the resultant curve is shown in Figure 3.
  • This film was prepared with a first bath which also contained iodine, potassium iodide and water in a weight ratio of 1/15.82/328; but the second bath contained boric acid, potassium iodide and water in a weight ratio of 1/1.56/20.54.
  • the resultant curve is shown in Figure
  • This film was prepared with a first bath which also contained iodine, potassium iodide and water in a weight ratio of 1/15.82/328; but the second bath contained boric acid, potassium iodide, zinc chloride and water in a weight ratio of 1.25/1.95/1/25.67.
  • the resultant curve is shown in Figure 5. This is an example of the invention.
  • Fig. 4 the presence of the potassium iodide has substantially eliminated blue leakage in both the before and after-heated polarizers. However, red absorbance is lower than was noted in Fig. 3.
  • Figure 5 which depicts the optical density versus wavelength of a preferred polarizer of the present invention, demonstrates that by including zinc chloride along with potassium iodide in the berating solution the "blue leak" is substantially reduced and the red response or reduction of the "red leak” is maximised. Note particularly that at 750 nm the optical density of the polarizer of Fig. 5 is over 1.5 while the optical density of the polarizer of Fig. 4 at 750 nm is under 1.
  • Fig. 6 clearly show that it does make a difference when the zinc ion is added. It is not enought that zinc ion is applied at some stage in the manufacture of an iodine stained polarizer, but it must be applied subsequent to the iodine staining step. Comparing Fig. 6, for example, to Fig. 4 one cannot help but appreciate the similarity between the two curves. After the heat'stability treatment they are in fact neatly identical. What can be concluded from this is that the zinc ion, when present in the stain, did not have much of an effect on the optical response of the polarizer. If anything, it lowered the blue absorbance..
  • a highly efficient light polarizing element has been prepared which finds utility not only in conventional situations but in some unconventional situations, where as close to absolute extinction as is possible is required in the crossed position as in, for example, flash blindness goggles, such as might be employed by welders and others exposed to sudden bursts of extremely bright visible radiation which is potentially harmful to the eyes.

Landscapes

  • Physics & Mathematics (AREA)
  • General Physics & Mathematics (AREA)
  • Optics & Photonics (AREA)
  • Polarising Elements (AREA)
  • Manufacture Of Macromolecular Shaped Articles (AREA)
  • Shaping By String And By Release Of Stress In Plastics And The Like (AREA)
  • Coloring (AREA)
EP78200002A 1977-06-29 1978-06-01 Polarisator für sichtbares Licht bestehend aus einem mit Jod gefärbten Polyvinylalkoholfilm und Verfahren zu seiner Herstellung Expired EP0000209B1 (de)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US81099677A 1977-06-29 1977-06-29
US810996 1977-06-29

Publications (2)

Publication Number Publication Date
EP0000209A1 true EP0000209A1 (de) 1979-01-10
EP0000209B1 EP0000209B1 (de) 1982-02-10

Family

ID=25205251

Family Applications (1)

Application Number Title Priority Date Filing Date
EP78200002A Expired EP0000209B1 (de) 1977-06-29 1978-06-01 Polarisator für sichtbares Licht bestehend aus einem mit Jod gefärbten Polyvinylalkoholfilm und Verfahren zu seiner Herstellung

Country Status (5)

Country Link
EP (1) EP0000209B1 (de)
JP (1) JPS6033245B2 (de)
AU (1) AU517329B2 (de)
DE (1) DE2861617D1 (de)
IT (1) IT1097458B (de)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2461570A1 (fr) * 1979-07-16 1981-02-06 Shinetsu Chemical Co Procede de fabrication de films, de feuilles minces ou feuilles, polarisantes
US4564545A (en) * 1983-03-01 1986-01-14 Sumitomo Chemical Company, Limited Light-polarizing plate having excellent durability and production of the same
US6606193B2 (en) * 2000-11-08 2003-08-12 Nitto Denko Corporation Polarizer
US6667787B2 (en) 2000-10-30 2003-12-23 Nitto Denko Corporation Polarizer
WO2004053542A1 (en) * 2002-12-12 2004-06-24 Sumitomo Chemical Company, Limited Method for producing polarizing film
US20090202822A1 (en) * 2006-05-26 2009-08-13 Nitto Denko Corporation Polarizer protective film, polarizing plate, and image display apparatus
US9733405B2 (en) 2013-11-29 2017-08-15 Sumitomo Chemical Company, Limited Polarizer and polarizing plate including same
US20190081424A1 (en) * 2017-09-11 2019-03-14 Woertz Engineering Ag Connection device and electrical tunnel installation
CN114355497A (zh) * 2020-10-14 2022-04-15 恒美光电股份有限公司 一种偏光子及其处理方法和制得的偏光片

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4591512A (en) * 1985-01-25 1986-05-27 Polaroid Corporation Method of making light polarizer
JP2663440B2 (ja) * 1987-06-12 1997-10-15 三菱瓦斯化学株式会社 偏光フィルムの製造方法
JPH02244006A (ja) * 1989-03-17 1990-09-28 Nippon Kayaku Co Ltd 位相差フィルム及びその製造法
JP2003029043A (ja) * 2001-07-19 2003-01-29 Nitto Denko Corp 偏光子の製造方法、偏光子、偏光板および液晶表示装置
JP4043263B2 (ja) 2002-03-18 2008-02-06 日東電工株式会社 偏光子の製造方法、偏光子、偏光板および画像表示装置
KR100916955B1 (ko) 2003-04-21 2009-09-14 닛토덴코 가부시키가이샤 편광자, 그 제조 방법, 편광판, 광학 필름 및 화상 표시장치
JP5996516B2 (ja) 2013-11-29 2016-09-21 住友化学株式会社 偏光子及びそれを含む偏光板
JP5932760B2 (ja) 2013-11-29 2016-06-08 住友化学株式会社 偏光子及びそれを含む偏光板

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CH216195A (de) * 1938-12-09 1941-08-15 Zeiss Ikon Ag Verfahren zur Herstellung von Polarisationsfiltern.
US2328219A (en) * 1938-10-29 1943-08-31 Polaroid Corp Light polarizer and process of manufacture
US2375963A (en) * 1943-05-07 1945-05-15 Polaroid Corp Process of manufacturing lightpolarizing material
USRE23297E (en) * 1950-11-28 Sheetlike light-polarizing complex
DE1258084B (de) * 1956-07-02 1968-01-04 Polaroid Corp Verfahren zur Herstellung gefaerbter, lichtpolarisierender Folien

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
USRE23297E (en) * 1950-11-28 Sheetlike light-polarizing complex
US2328219A (en) * 1938-10-29 1943-08-31 Polaroid Corp Light polarizer and process of manufacture
CH216195A (de) * 1938-12-09 1941-08-15 Zeiss Ikon Ag Verfahren zur Herstellung von Polarisationsfiltern.
US2375963A (en) * 1943-05-07 1945-05-15 Polaroid Corp Process of manufacturing lightpolarizing material
DE1258084B (de) * 1956-07-02 1968-01-04 Polaroid Corp Verfahren zur Herstellung gefaerbter, lichtpolarisierender Folien

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2461570A1 (fr) * 1979-07-16 1981-02-06 Shinetsu Chemical Co Procede de fabrication de films, de feuilles minces ou feuilles, polarisantes
US4564545A (en) * 1983-03-01 1986-01-14 Sumitomo Chemical Company, Limited Light-polarizing plate having excellent durability and production of the same
US6667787B2 (en) 2000-10-30 2003-12-23 Nitto Denko Corporation Polarizer
US6606193B2 (en) * 2000-11-08 2003-08-12 Nitto Denko Corporation Polarizer
WO2004053542A1 (en) * 2002-12-12 2004-06-24 Sumitomo Chemical Company, Limited Method for producing polarizing film
US8012383B2 (en) 2002-12-12 2011-09-06 Sumitomo Chemical Company, Limited Method for producing polarizing film
US20090202822A1 (en) * 2006-05-26 2009-08-13 Nitto Denko Corporation Polarizer protective film, polarizing plate, and image display apparatus
US9733405B2 (en) 2013-11-29 2017-08-15 Sumitomo Chemical Company, Limited Polarizer and polarizing plate including same
US20190081424A1 (en) * 2017-09-11 2019-03-14 Woertz Engineering Ag Connection device and electrical tunnel installation
CN114355497A (zh) * 2020-10-14 2022-04-15 恒美光电股份有限公司 一种偏光子及其处理方法和制得的偏光片

Also Published As

Publication number Publication date
AU517329B2 (en) 1981-07-23
IT1097458B (it) 1985-08-31
AU3627778A (en) 1979-11-22
EP0000209B1 (de) 1982-02-10
JPS5416575A (en) 1979-02-07
DE2861617D1 (en) 1982-03-18
JPS6033245B2 (ja) 1985-08-01
IT7825114A0 (it) 1978-06-29

Similar Documents

Publication Publication Date Title
US4166871A (en) Iodine stained light polarizer
US4591512A (en) Method of making light polarizer
EP0000209A1 (de) Polarisator für sichtbares Licht bestehend aus einem mit Jod gefärbten Polyvinylalkoholfilm und Verfahren zu seiner Herstellung
US4396646A (en) Method of making patterned polarizers
EP0807272B1 (de) K- polarisationsschicht mit hohem wirkungsgrad
US4818624A (en) Stabilized light-polarizing material
US2328219A (en) Light polarizer and process of manufacture
US4992218A (en) Process for producing a polarizing film
JPH11248937A (ja) 偏光ポリビニレンシートの製造方法
US7136225B2 (en) Polarizing plate and method for producing the same
KR20180066100A (ko) 편광자 및 그 제조방법
KR100938786B1 (ko) 편광 필름의 제조 방법
JP3505968B2 (ja) 偏光フィルムの製造方法
CN107065055A (zh) 一种偏光片及其生产工艺
JP3680709B2 (ja) 偏光フィルムの製造方法
JPH07104126A (ja) 偏光フィルムの製造方法
JP3708062B2 (ja) ヨウ素系偏光板及びその製造方法
JPH0823608B2 (ja) 偏光膜の製造法
JPH10170721A (ja) 偏光フィルムの製造方法
JP7162069B2 (ja) 偏光子の製造方法
JPS62240905A (ja) 偏光フイルム
JPH06313808A (ja) 偏光フィルムの製造方法
JPS6136203B2 (de)
US5670092A (en) Polarizing film
JPH0641383A (ja) 偏光フイルム

Legal Events

Date Code Title Description
PUAI Public reference made under article 153(3) epc to a published international application that has entered the european phase

Free format text: ORIGINAL CODE: 0009012

AK Designated contracting states

Designated state(s): BE DE FR GB NL

17P Request for examination filed
GRAA (expected) grant

Free format text: ORIGINAL CODE: 0009210

AK Designated contracting states

Designated state(s): BE DE FR GB NL

REF Corresponds to:

Ref document number: 2861617

Country of ref document: DE

Date of ref document: 19820318

PGFP Annual fee paid to national office [announced via postgrant information from national office to epo]

Ref country code: FR

Payment date: 19970510

Year of fee payment: 20

PGFP Annual fee paid to national office [announced via postgrant information from national office to epo]

Ref country code: BE

Payment date: 19970515

Year of fee payment: 20

PGFP Annual fee paid to national office [announced via postgrant information from national office to epo]

Ref country code: GB

Payment date: 19970520

Year of fee payment: 20

PGFP Annual fee paid to national office [announced via postgrant information from national office to epo]

Ref country code: DE

Payment date: 19970523

Year of fee payment: 20

PGFP Annual fee paid to national office [announced via postgrant information from national office to epo]

Ref country code: NL

Payment date: 19970526

Year of fee payment: 20

BE20 Be: patent expired

Free format text: 980601 *POLAROID CORP.

PG25 Lapsed in a contracting state [announced via postgrant information from national office to epo]

Ref country code: GB

Free format text: LAPSE BECAUSE OF EXPIRATION OF PROTECTION

Effective date: 19980531

PG25 Lapsed in a contracting state [announced via postgrant information from national office to epo]

Ref country code: NL

Free format text: LAPSE BECAUSE OF EXPIRATION OF PROTECTION

Effective date: 19980601

REG Reference to a national code

Ref country code: GB

Ref legal event code: PE20

Effective date: 19980531

NLV7 Nl: ceased due to reaching the maximum lifetime of a patent

Effective date: 19980601

PLBE No opposition filed within time limit

Free format text: ORIGINAL CODE: 0009261

STAA Information on the status of an ep patent application or granted ep patent

Free format text: STATUS: NO OPPOSITION FILED WITHIN TIME LIMIT