DE60321771D1 - Strontiumfeldspat-aluminiumtitanat für hochtemperaturanwendungen - Google Patents
Strontiumfeldspat-aluminiumtitanat für hochtemperaturanwendungenInfo
- Publication number
- DE60321771D1 DE60321771D1 DE60321771T DE60321771T DE60321771D1 DE 60321771 D1 DE60321771 D1 DE 60321771D1 DE 60321771 T DE60321771 T DE 60321771T DE 60321771 T DE60321771 T DE 60321771T DE 60321771 D1 DE60321771 D1 DE 60321771D1
- Authority
- DE
- Germany
- Prior art keywords
- feldspat
- strontium
- high temperature
- aluminum titanate
- temperature applications
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
- C04B35/63—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B using additives specially adapted for forming the products, e.g.. binder binders
- C04B35/632—Organic additives
- C04B35/636—Polysaccharides or derivatives thereof
- C04B35/6365—Cellulose or derivatives thereof
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
- C04B35/46—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxides or titanates
- C04B35/462—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxides or titanates based on titanates
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
- C04B35/16—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay
- C04B35/18—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay rich in aluminium oxide
- C04B35/195—Alkaline earth aluminosilicates, e.g. cordierite or anorthite
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
- C04B35/46—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxides or titanates
- C04B35/462—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxides or titanates based on titanates
- C04B35/478—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on titanium oxides or titanates based on titanates based on aluminium titanates
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
- C04B35/63—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B using additives specially adapted for forming the products, e.g.. binder binders
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
- C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
- C04B35/63—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B using additives specially adapted for forming the products, e.g.. binder binders
- C04B35/632—Organic additives
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B38/00—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof
- C04B38/0006—Honeycomb structures
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N3/00—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust
- F01N3/02—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for cooling, or for removing solid constituents of, exhaust
- F01N3/021—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for cooling, or for removing solid constituents of, exhaust by means of filters
- F01N3/022—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for cooling, or for removing solid constituents of, exhaust by means of filters characterised by specially adapted filtering structure, e.g. honeycomb, mesh or fibrous
- F01N3/0222—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for cooling, or for removing solid constituents of, exhaust by means of filters characterised by specially adapted filtering structure, e.g. honeycomb, mesh or fibrous the structure being monolithic, e.g. honeycombs
-
- F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING
- F01—MACHINES OR ENGINES IN GENERAL; ENGINE PLANTS IN GENERAL; STEAM ENGINES
- F01N—GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR MACHINES OR ENGINES IN GENERAL; GAS-FLOW SILENCERS OR EXHAUST APPARATUS FOR INTERNAL COMBUSTION ENGINES
- F01N3/00—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust
- F01N3/08—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous
- F01N3/10—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust
- F01N3/24—Exhaust or silencing apparatus having means for purifying, rendering innocuous, or otherwise treating exhaust for rendering innocuous by thermal or catalytic conversion of noxious components of exhaust characterised by constructional aspects of converting apparatus
- F01N3/28—Construction of catalytic reactors
- F01N3/2803—Construction of catalytic reactors characterised by structure, by material or by manufacturing of catalyst support
- F01N3/2825—Ceramics
- F01N3/2828—Ceramic multi-channel monoliths, e.g. honeycombs
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
- C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
- C04B2111/00793—Uses not provided for elsewhere in C04B2111/00 as filters or diaphragms
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
- C04B2235/3206—Magnesium oxides or oxide-forming salts thereof
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
- C04B2235/3213—Strontium oxides or oxide-forming salts thereof
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3217—Aluminum oxide or oxide forming salts thereof, e.g. bauxite, alpha-alumina
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3231—Refractory metal oxides, their mixed metal oxides, or oxide-forming salts thereof
- C04B2235/3232—Titanium oxides or titanates, e.g. rutile or anatase
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/327—Iron group oxides, their mixed metal oxides, or oxide-forming salts thereof
- C04B2235/3272—Iron oxides or oxide forming salts thereof, e.g. hematite, magnetite
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3418—Silicon oxide, silicic acids, or oxide forming salts thereof, e.g. silica sol, fused silica, silica fume, cristobalite, quartz or flint
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
- C04B2235/3427—Silicates other than clay, e.g. water glass
- C04B2235/3463—Alumino-silicates other than clay, e.g. mullite
- C04B2235/3481—Alkaline earth metal alumino-silicates other than clay, e.g. cordierite, beryl, micas such as margarite, plagioclase feldspars such as anorthite, zeolites such as chabazite
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/30—Constituents and secondary phases not being of a fibrous nature
- C04B2235/44—Metal salt constituents or additives chosen for the nature of the anions, e.g. hydrides or acetylacetonate
- C04B2235/449—Organic acids, e.g. EDTA, citrate, acetate, oxalate
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
- C04B2235/52—Constituents or additives characterised by their shapes
- C04B2235/5292—Flakes, platelets or plates
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
- C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
- C04B2235/54—Particle size related information
- C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
- C04B2235/5436—Particle size related information expressed by the size of the particles or aggregates thereof micrometer sized, i.e. from 1 to 100 micron
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
- C04B2235/72—Products characterised by the absence or the low content of specific components, e.g. alkali metal free alumina ceramics
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
- C04B2235/74—Physical characteristics
- C04B2235/77—Density
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
- C04B2235/80—Phases present in the sintered or melt-cast ceramic products other than the main phase
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
- C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
- C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance
- C04B2235/9607—Thermal properties, e.g. thermal expansion coefficient
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02T—CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION
- Y02T10/00—Road transport of goods or passengers
- Y02T10/10—Internal combustion engine [ICE] based vehicles
- Y02T10/12—Improving ICE efficiencies
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10S—TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10S55/00—Gas separation
- Y10S55/30—Exhaust treatment
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Ceramic Engineering (AREA)
- Manufacturing & Machinery (AREA)
- Materials Engineering (AREA)
- Structural Engineering (AREA)
- Organic Chemistry (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Inorganic Chemistry (AREA)
- Combustion & Propulsion (AREA)
- General Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Health & Medical Sciences (AREA)
- Toxicology (AREA)
- Filtering Materials (AREA)
- Compositions Of Oxide Ceramics (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US10/098,711 US6620751B1 (en) | 2002-03-14 | 2002-03-14 | Strontium feldspar aluminum titanate for high temperature applications |
PCT/US2003/007503 WO2003078352A1 (en) | 2002-03-14 | 2003-03-12 | Strontium feldspar aluminum titanate for high temperature applications |
Publications (1)
Publication Number | Publication Date |
---|---|
DE60321771D1 true DE60321771D1 (de) | 2008-08-07 |
Family
ID=27804293
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
DE60321771T Expired - Lifetime DE60321771D1 (de) | 2002-03-14 | 2003-03-12 | Strontiumfeldspat-aluminiumtitanat für hochtemperaturanwendungen |
Country Status (10)
Country | Link |
---|---|
US (1) | US6620751B1 (de) |
EP (1) | EP1483221B1 (de) |
JP (1) | JP4350523B2 (de) |
KR (1) | KR100931755B1 (de) |
CN (1) | CN1313416C (de) |
AU (1) | AU2003220183A1 (de) |
DE (1) | DE60321771D1 (de) |
TW (1) | TWI303241B (de) |
WO (1) | WO2003078352A1 (de) |
ZA (1) | ZA200406908B (de) |
Families Citing this family (77)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6897175B2 (en) * | 2001-10-09 | 2005-05-24 | General Electric | Catalyst and method for the alkylation of hydroxyaromatic compounds |
JP3489030B1 (ja) * | 2002-04-26 | 2004-01-19 | 勉 福田 | チタン酸アルミニウム系焼結体の製造方法 |
JP4750415B2 (ja) * | 2002-07-31 | 2011-08-17 | コーニング インコーポレイテッド | チタン酸アルミニウムベースのセラミック製品 |
JP4324799B2 (ja) * | 2002-11-01 | 2009-09-02 | オーセラ株式会社 | チタン酸アルミニウムマグネシウム焼結体の製造方法 |
GB0304939D0 (en) | 2003-03-05 | 2003-04-09 | Johnson Matthey Plc | Light-duty diesel engine and a particulate filter therefor |
WO2005005019A1 (ja) | 2003-07-11 | 2005-01-20 | Ohcera Co., Ltd. | 排ガス浄化ハニカムフィルタ及びその製造方法 |
WO2005009922A1 (ja) * | 2003-07-25 | 2005-02-03 | Ngk Insulators, Ltd. | セラミックス多孔質体及びその透過性能評価方法 |
US7442425B2 (en) | 2003-09-30 | 2008-10-28 | Corning Incorporated | High porosity honeycomb and method |
US6942713B2 (en) * | 2003-11-04 | 2005-09-13 | Corning Incorporated | Ceramic body based on aluminum titanate |
US7122612B2 (en) | 2004-02-27 | 2006-10-17 | Corning Incorporated | Porous ceramic filters with catalyst coatings |
US7259120B2 (en) * | 2004-04-21 | 2007-08-21 | Corning Incorporated | Aluminum titanate ceramic articles and methods of making same |
US20060021308A1 (en) * | 2004-07-29 | 2006-02-02 | Merkel Gregory A | Mullite-aluminum titanate body and method for making same |
US20060078479A1 (en) * | 2004-10-07 | 2006-04-13 | Caterpillar Inc. | Filter assembly for an exhaust treatment device |
WO2006044268A1 (en) | 2004-10-13 | 2006-04-27 | Dow Global Technologies Inc. | Catalysed diesel soot filter and process for its use |
US20070259769A1 (en) * | 2005-02-22 | 2007-11-08 | Ellison Adam J G | Aluminum titanate ceramic articles and methods of making same |
KR100752520B1 (ko) | 2005-03-07 | 2007-08-29 | (주)케이에이치 케미컬 | 내부식성 세라믹 재료 및 이를 사용한 필터, 이들의제조방법 |
CN101213156B (zh) * | 2005-05-31 | 2014-07-16 | 康宁股份有限公司 | 包含成孔剂组合的形成钛酸铝陶瓷的批料混合物和生坯,以及它们的制造和烧制方法 |
CN100344583C (zh) * | 2005-08-17 | 2007-10-24 | 华东师范大学 | 一种烧结微纤结构化微米尺度颗粒的多孔复合材料及制造方法 |
US7700163B2 (en) * | 2005-10-27 | 2010-04-20 | Corning Incorporated | Microwave process for porous ceramic filters with passivation and catalyst coatings |
DE102006035052A1 (de) * | 2005-11-17 | 2007-05-24 | Robert Bosch Gmbh | Filterelement und Filter zur Abgasnachbehandlung |
US20070254798A1 (en) * | 2006-03-31 | 2007-11-01 | Addiego William P | Peroxide containing compounds as pore formers in the manufacture of ceramic articles |
US7744669B2 (en) * | 2006-07-14 | 2010-06-29 | Corning Incorporated | Plugging material for aluminum titanate ceramic wall flow filter manufacture |
US8298311B2 (en) * | 2006-11-15 | 2012-10-30 | Corning Incorporated | Filters with controlled submicron porosity |
US8974724B2 (en) * | 2006-11-29 | 2015-03-10 | Corning Incorporated | Aluminum titanate batch compositions and method |
US20080138273A1 (en) * | 2006-12-11 | 2008-06-12 | Yi Jiang | Wall flow reactor for hydrogen production |
DE102006062141A1 (de) * | 2006-12-22 | 2008-06-26 | Dow Wolff Cellulosics Gmbh | Celluloseetherhaltige Additive für die Keramikextrusion |
CN101553445B (zh) | 2006-12-27 | 2012-09-19 | 日立金属株式会社 | 钛酸铝质陶瓷蜂窝状结构体的制造方法 |
EP1941940A1 (de) * | 2007-01-03 | 2008-07-09 | Ford Global Technologies, LLC | Poröses Substrat zur Verwendung als Partikelfilter für katalytisch oder nicht katalytisch Rußregenerationsverfahren |
CN101687719A (zh) * | 2007-03-20 | 2010-03-31 | 康宁股份有限公司 | 用于陶瓷过滤器的低收缩性堵塞混合物,堵塞的蜂窝体过滤器及其制造方法 |
EP2150512B1 (de) * | 2007-05-31 | 2016-01-06 | Corning Inc. | Aluminiumtitanatkeramik grünkörper mit einem porenbildungsformer und verfahren zur herstellung von keramikartikel |
CN101801879A (zh) * | 2007-07-31 | 2010-08-11 | 康宁股份有限公司 | 应用于陶瓷蜂窝体的组合物 |
US7867932B2 (en) * | 2007-08-28 | 2011-01-11 | Corning Incorporated | Refractory glass ceramics |
WO2009061397A2 (en) * | 2007-11-05 | 2009-05-14 | Corning Incorporated | Low expansion cement compositions for ceramic monoliths |
WO2009073092A2 (en) | 2007-11-30 | 2009-06-11 | Corning Incorporated | Compositions for applying to honeycomb bodies |
WO2009076985A1 (en) * | 2007-12-17 | 2009-06-25 | Imerys Services | Ceramic honeycomb structures |
CN101925538A (zh) * | 2008-01-21 | 2010-12-22 | 住友化学株式会社 | 钛酸铝镁的制备方法 |
WO2009122532A1 (ja) | 2008-03-31 | 2009-10-08 | イビデン株式会社 | ハニカム構造体 |
WO2009122534A1 (ja) * | 2008-03-31 | 2009-10-08 | イビデン株式会社 | ハニカム構造体 |
US8729436B2 (en) * | 2008-05-30 | 2014-05-20 | Corning Incorporated | Drying process and apparatus for ceramic greenware |
US8101117B2 (en) * | 2008-05-30 | 2012-01-24 | Corning, Incorporated | Controlled gas pore formers in extruded ware |
CN102171164B (zh) | 2008-08-28 | 2014-11-12 | 康宁股份有限公司 | 蜂窝状基材中的孔径分布控制 |
US7914718B2 (en) * | 2008-08-28 | 2011-03-29 | Corning Incorporated | Gas pore former in cellular monoliths |
JP5294057B2 (ja) * | 2008-10-02 | 2013-09-18 | 日立金属株式会社 | チタン酸アルミニウム質セラミックハニカム構造体の製造方法 |
US8138108B2 (en) * | 2009-02-27 | 2012-03-20 | Corning Incorporated | Aluminum titanate-containing ceramic-forming batch materials and methods using the same |
US8051703B2 (en) * | 2009-02-27 | 2011-11-08 | Corning Incorporated | Methods for using a fluid stream to test a honeycomb body |
US9227878B2 (en) | 2009-04-30 | 2016-01-05 | Corning Incorporated | Selected binders for the extrusion of ultra-thin wall cellular ceramics |
US8377836B2 (en) * | 2009-05-22 | 2013-02-19 | Corning Incorporated | Methods of making ceramic bodies using catalyzed pore formers and compositions for making the same |
US8056401B2 (en) * | 2009-05-26 | 2011-11-15 | Corning Incorporated | In-line moisture-content measurement of ceramic materials in ceramic article manufacturing |
US20100301515A1 (en) * | 2009-05-29 | 2010-12-02 | Thomas William Brew | Honeycomb Extrusion Die Apparatus And Methods |
US20110045233A1 (en) * | 2009-08-20 | 2011-02-24 | Sandra Lee Gray | Dimensional control during firing to form aluminum titanate honeycomb structures |
US20110151181A1 (en) * | 2009-12-21 | 2011-06-23 | Geo2 Technologies, Inc. | Fiber Enhanced Porous Substrate |
EP2540370B1 (de) * | 2010-02-22 | 2018-04-04 | Hitachi Metals, Ltd. | Keramikwabenstruktur |
US8641942B2 (en) | 2010-05-12 | 2014-02-04 | Corning Incorporated | Laser scanning systems and methods for measuring extruded ceramic logs |
EP2390307A1 (de) | 2010-05-27 | 2011-11-30 | Corning Incorporated | Verarbeitung poröser Keramik mittels geprilltem Wachs und nichtionischem Tensid |
CN103153465B (zh) * | 2010-10-04 | 2015-11-25 | 大塚化学株式会社 | 排气净化过滤器及其制造方法 |
US20120133065A1 (en) | 2010-11-30 | 2012-05-31 | Stephen John Caffrey | Real-time, closed-loop shape control of extruded ceramic honeycomb structures |
US9908260B2 (en) | 2013-05-20 | 2018-03-06 | Corning Incorporated | Porous ceramic article and method of manufacturing the same |
US9376347B2 (en) | 2013-05-20 | 2016-06-28 | Corning Incorporated | Porous ceramic article and method of manufacturing the same |
US9623360B2 (en) | 2013-05-20 | 2017-04-18 | Corning Incorporated | Porous ceramic article and method of manufacturing the same |
US10472291B2 (en) * | 2013-10-15 | 2019-11-12 | Corning Incorporated | Crosslinked starches for pore forming in ceramics |
FR3031975B1 (fr) * | 2015-01-23 | 2019-07-05 | Commissariat A L'energie Atomique Et Aux Energies Alternatives | Procede de preparation d'un materiau a base d'aluminosilicate, et procede de preparation d'un materiau composite a matrice en aluminosilicate |
MX2017015281A (es) | 2015-05-29 | 2018-08-15 | Corning Inc | Obstrucción de filtro tipo panal y aparato para obstrucción de filtro tipo panal. |
CN109219589B (zh) | 2016-05-31 | 2022-04-26 | 康宁股份有限公司 | 多孔制品及其制造方法 |
WO2018089596A1 (en) | 2016-11-10 | 2018-05-17 | Corning Incorporated | Composite ceramic materials, articles, and method of manufacture |
US11661379B2 (en) | 2017-07-21 | 2023-05-30 | Corning Incorporated | Methods of extracting volatiles from ceramic green bodies |
WO2019023186A1 (en) | 2017-07-24 | 2019-01-31 | Corning Incorporated | ANTIOXIDANTS IN CERAMIC BODIES IN GREEN CONTAINING DIFFERENT OILS FOR IMPROVED COOKING |
MX2020001622A (es) | 2017-08-11 | 2020-08-20 | Corning Inc | Mezclas por lotes de cerámica cruda que comprenden una emulsión inversa y métodos para formar un cuerpo de cerámica. |
WO2019089731A1 (en) | 2017-10-31 | 2019-05-09 | Corning Incorporated | Batch compositions comprising spheroidal pre-reacted inorganic particles and spheroidal pore-formers and methods of manufacture of honeycomb bodies therefrom |
CN111712474A (zh) | 2017-12-19 | 2020-09-25 | 康宁股份有限公司 | 包含稳定化乳液的生坯陶瓷混合物及形成陶瓷体的方法 |
CN108484161B (zh) * | 2018-06-20 | 2020-11-03 | 上海定向材料科技有限公司 | 一种钛酸铝复合材料及其制备方法 |
US11698017B2 (en) | 2018-07-20 | 2023-07-11 | Corning Incorporated | System and method for detecting defects in a honeycomb body |
WO2020150039A1 (en) | 2019-01-14 | 2020-07-23 | Corning Incorporated | Green ceramic batch mixtures comprising an inverse emulsion and methods for forming a ceramic body |
CN114555540B (zh) | 2019-08-13 | 2024-06-21 | 康宁股份有限公司 | 用于堵塞蜂窝体的胶结剂混合物及其制造方法 |
WO2022026236A1 (en) | 2020-07-30 | 2022-02-03 | Corning Incorporated | Aluminum titanate-feldspar ceramic bodies, batch mixtures, and methods of manufacture |
US20230278933A1 (en) | 2020-08-25 | 2023-09-07 | Corning Incorporated | Cement mixtures for plugging honeycomb bodies and methods of making the same |
WO2024097046A1 (en) | 2022-10-31 | 2024-05-10 | Corning Incorporated | Higher temperature extrusion of ceramic precursor paste |
WO2024097048A1 (en) | 2022-10-31 | 2024-05-10 | Corning Incorporated | Method of inducing a reduced wall drag state in a high wall drag ceramic precursor paste |
Family Cites Families (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH02229763A (ja) | 1989-03-02 | 1990-09-12 | Kitagawa Iron Works Co Ltd | 鋳ぐるみ用セラミックス及び鋳ぐるみ体 |
CA2167991C (en) * | 1995-01-25 | 1999-12-14 | Kazuhiko Kumazawa | Honeycomb regenerator |
JP3555382B2 (ja) * | 1997-04-22 | 2004-08-18 | 松下電器産業株式会社 | 排ガスフィルターとその製造方法及びこの排ガスフィルターを備えたディーゼルエンジン |
CN1235133A (zh) * | 1998-05-11 | 1999-11-17 | 佟定远 | 一种应用于制造铝低压铸造机升液管的高强耐热陶瓷材料 |
CN1156412C (zh) * | 2000-07-13 | 2004-07-07 | 胡勇波 | 复合材料蜂窝陶瓷及其制造方法 |
JP3600933B2 (ja) * | 2000-11-08 | 2004-12-15 | オーセラ株式会社 | チタン酸アルミニウム系焼結体の製造方法 |
-
2002
- 2002-03-14 US US10/098,711 patent/US6620751B1/en not_active Expired - Lifetime
-
2003
- 2003-03-12 KR KR1020047014476A patent/KR100931755B1/ko active IP Right Grant
- 2003-03-12 AU AU2003220183A patent/AU2003220183A1/en not_active Abandoned
- 2003-03-12 JP JP2003576362A patent/JP4350523B2/ja not_active Expired - Fee Related
- 2003-03-12 WO PCT/US2003/007503 patent/WO2003078352A1/en active Application Filing
- 2003-03-12 DE DE60321771T patent/DE60321771D1/de not_active Expired - Lifetime
- 2003-03-12 CN CNB038060671A patent/CN1313416C/zh not_active Expired - Lifetime
- 2003-03-12 EP EP03716479A patent/EP1483221B1/de not_active Expired - Lifetime
- 2003-03-13 TW TW092105978A patent/TWI303241B/zh not_active IP Right Cessation
-
2004
- 2004-08-31 ZA ZA2004/06908A patent/ZA200406908B/en unknown
Also Published As
Publication number | Publication date |
---|---|
TWI303241B (en) | 2008-11-21 |
KR100931755B1 (ko) | 2009-12-14 |
JP4350523B2 (ja) | 2009-10-21 |
TW200413076A (en) | 2004-08-01 |
AU2003220183A1 (en) | 2003-09-29 |
KR20040099329A (ko) | 2004-11-26 |
CN1642872A (zh) | 2005-07-20 |
EP1483221B1 (de) | 2008-06-25 |
CN1313416C (zh) | 2007-05-02 |
EP1483221A4 (de) | 2006-08-16 |
EP1483221A1 (de) | 2004-12-08 |
JP2005519834A (ja) | 2005-07-07 |
WO2003078352A1 (en) | 2003-09-25 |
US6620751B1 (en) | 2003-09-16 |
ZA200406908B (en) | 2005-08-31 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
DE60321771D1 (de) | Strontiumfeldspat-aluminiumtitanat für hochtemperaturanwendungen | |
DE60229169D1 (de) | Kühlvorrichtung | |
NO20034498L (no) | Hoyekspanderende pakning | |
DE50303143D1 (de) | Wärmekraftmaschine | |
DE50209166D1 (de) | Innenkühlbare Schraube | |
DE60335973D1 (de) | Metallische Flachdichtung | |
DE60317389D1 (de) | Abkühlungssystem für eng zusammengestellten Speichervorrichtungen | |
NO20051998D0 (no) | Torke prosess | |
NO20022806L (no) | Grusoppblåst isolasjonspakning | |
NO20031285L (no) | Isolasjons-omlöps-overgangsskjöt | |
DE60323899D1 (de) | Startvorrichtung | |
DE60305826D1 (de) | Verbrennungsmotor-Anlassersystem | |
NO20032504D0 (no) | Tetningsblanding | |
DE50302271D1 (de) | Kondensor | |
DE60334519D1 (de) | Kühlvorrichtung | |
DE60302581T2 (de) | Kühlelement | |
DE50301221D1 (de) | Kühlelement für Gase | |
DE60218800D1 (de) | Hochtemperaturdichtung | |
DE60304875D1 (de) | Motorkühlsysteme | |
DE50202991D1 (de) | Hochtemperaturfestes Klebemittel | |
NO20051512D0 (no) | Hoy strekkbar termisk insulator | |
DE602004006365D1 (de) | Hochspannungskondensator für Magnetron | |
FI20022004A (fi) | Vesipohjainen jäähdytysneste moottorisovellutuksiin | |
NO20021945L (no) | Kjöleanordning | |
ITVR20030088A1 (it) | Procedimento per la realizzazione di fasce anti-implosione per cinescopi |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
8364 | No opposition during term of opposition |