DE60018316D1 - Nanokomposite hergestellt durch Onium-Ionen interkalierten Ton und zähe mit Anhydrid gehärtete Epoxidharze - Google Patents
Nanokomposite hergestellt durch Onium-Ionen interkalierten Ton und zähe mit Anhydrid gehärtete EpoxidharzeInfo
- Publication number
- DE60018316D1 DE60018316D1 DE60018316T DE60018316T DE60018316D1 DE 60018316 D1 DE60018316 D1 DE 60018316D1 DE 60018316 T DE60018316 T DE 60018316T DE 60018316 T DE60018316 T DE 60018316T DE 60018316 D1 DE60018316 D1 DE 60018316D1
- Authority
- DE
- Germany
- Prior art keywords
- onium
- tough
- anhydride
- epoxy resins
- cured epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B33/00—Silicon; Compounds thereof
- C01B33/20—Silicates
- C01B33/36—Silicates having base-exchange properties but not having molecular sieve properties
- C01B33/38—Layered base-exchange silicates, e.g. clays, micas or alkali metal silicates of kenyaite or magadiite type
- C01B33/44—Products obtained from layered base-exchange silicates by ion-exchange with organic compounds such as ammonium, phosphonium or sulfonium compounds or by intercalation of organic compounds, e.g. organoclay material
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K9/00—Use of pretreated ingredients
- C08K9/04—Ingredients treated with organic substances
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C1/00—Treatment of specific inorganic materials other than fibrous fillers; Preparation of carbon black
- C09C1/40—Compounds of aluminium
- C09C1/42—Clays
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C3/00—Treatment in general of inorganic materials, other than fibrous fillers, to enhance their pigmenting or filling properties
- C09C3/10—Treatment with macromolecular organic compounds
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2002/00—Crystal-structural characteristics
- C01P2002/08—Intercalated structures, i.e. with atoms or molecules intercalated in their structure
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2002/00—Crystal-structural characteristics
- C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
- C01P2002/72—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by d-values or two theta-values, e.g. as X-ray diagram
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2002/00—Crystal-structural characteristics
- C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
- C01P2002/77—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by unit-cell parameters, atom positions or structure diagrams
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2002/00—Crystal-structural characteristics
- C01P2002/80—Crystal-structural characteristics defined by measured data other than those specified in group C01P2002/70
- C01P2002/88—Crystal-structural characteristics defined by measured data other than those specified in group C01P2002/70 by thermal analysis data, e.g. TGA, DTA, DSC
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/54—Particles characterised by their aspect ratio, i.e. the ratio of sizes in the longest to the shortest dimension
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/32—Thermal properties
- C01P2006/33—Phase transition temperatures
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Inorganic Chemistry (AREA)
- Dispersion Chemistry (AREA)
- General Health & Medical Sciences (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Processes Of Treating Macromolecular Substances (AREA)
- Silicates, Zeolites, And Molecular Sieves (AREA)
- Epoxy Resins (AREA)
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US272277 | 1999-03-19 | ||
US09/272,277 US6251980B1 (en) | 1996-12-06 | 1999-03-19 | Nanocomposites formed by onium ion-intercalated clay and rigid anhydride-cured epoxy resins |
Publications (2)
Publication Number | Publication Date |
---|---|
DE60018316D1 true DE60018316D1 (de) | 2005-04-07 |
DE60018316T2 DE60018316T2 (de) | 2006-04-13 |
Family
ID=23039148
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
DE60018316T Expired - Fee Related DE60018316T2 (de) | 1999-03-19 | 2000-03-17 | Nanokomposite hergestellt durch Onium-Ionen interkalierten Ton und zähe mit Anhydrid gehärtete Epoxidharze |
Country Status (6)
Country | Link |
---|---|
US (1) | US6251980B1 (de) |
EP (1) | EP1038913B1 (de) |
JP (1) | JP2000297203A (de) |
CA (1) | CA2299705A1 (de) |
DE (1) | DE60018316T2 (de) |
MX (1) | MXPA00002760A (de) |
Families Citing this family (71)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6988305B1 (en) * | 1999-12-17 | 2006-01-24 | Magna International Of America, Inc. | Method and apparatus for blow molding large reinforced plastic parts |
US6414069B1 (en) * | 2000-03-03 | 2002-07-02 | Board Of Trustees Of Michigan University | Hybrid mixed ion clay structures for polymer nanocomposite formation |
US6737464B1 (en) | 2000-05-30 | 2004-05-18 | University Of South Carolina Research Foundation | Polymer nanocomposite comprising a matrix polymer and a layered clay material having a low quartz content |
WO2001092390A2 (en) | 2000-05-30 | 2001-12-06 | University Of South Carolina Research Foundation | A polymer nanocomposite comprising a matrix polymer and a layered clay material having an improved level of extractable material |
WO2002048270A1 (de) | 2000-12-15 | 2002-06-20 | Agrolinz Melamin Gmbh | Polymermodifizierte anorganische partikel |
PL202235B1 (pl) | 2000-12-15 | 2009-06-30 | Agrolinz Melamin Gmbh | Modyfikowane nieorganiczne cząstki o strukturze warstwowej, sposoby ich wytwarzania oraz zastosowanie |
AT410211B (de) | 2000-12-15 | 2003-03-25 | Agrolinz Melamin Gmbh | Halbzeuge und formstoffe aus aminoplasten |
JP3962271B2 (ja) * | 2001-05-11 | 2007-08-22 | 積水化学工業株式会社 | 難燃熱硬化性樹脂組成物 |
WO2003002243A2 (en) | 2001-06-27 | 2003-01-09 | Remon Medical Technologies Ltd. | Method and device for electrochemical formation of therapeutic species in vivo |
WO2003016394A1 (en) * | 2001-08-16 | 2003-02-27 | Henkel Loctite Corporation | Composition of bulk filler and epoxy-clay nanocomposite |
EP1448671B1 (de) | 2001-11-19 | 2007-09-12 | AMI Agrolinz Melamine International GmbH | Erzeugnisse, insbesondere formmassen aus triazinsegmente enthaltenden polymeren, verfahren zu deren herstellung und verwendungen |
KR100508907B1 (ko) * | 2001-12-27 | 2005-08-17 | 주식회사 엘지화학 | 차단성이 우수한 나노복합체 블렌드 조성물 |
KR100450232B1 (ko) * | 2002-01-24 | 2004-09-24 | 주식회사 엘지화학 | 유기점토 화합물, 및 이를 포함하는 고분자-점토나노복합체 조성물 |
US7163973B2 (en) * | 2002-08-08 | 2007-01-16 | Henkel Corporation | Composition of bulk filler and epoxy-clay nanocomposite |
US7220484B2 (en) * | 2002-11-22 | 2007-05-22 | National Research Council Of Canada | Polymeric nanocomposites comprising epoxy-functionalized graft polymer |
DE602004019050D1 (de) * | 2003-01-15 | 2009-03-05 | Ciba Holding Inc | Stabilisierung von thermoplastischen nanoverbundwerkstoffen |
CN1875056B (zh) * | 2003-11-04 | 2013-10-16 | 亨斯迈先进材料(瑞士)有限公司 | 双组分可固化组合物 |
US7013998B2 (en) * | 2003-11-20 | 2006-03-21 | Halliburton Energy Services, Inc. | Drill bit having an improved seal and lubrication method using same |
US20050109502A1 (en) * | 2003-11-20 | 2005-05-26 | Jeremy Buc Slay | Downhole seal element formed from a nanocomposite material |
EP1697460A4 (de) * | 2003-12-23 | 2007-05-23 | Valorbec Soc En Comandite | Verfahren und system zur herstellung von hochleistungsfähigen epoxidharzen und damit erhaltene hochleistungsfähige epoxidharze |
CA2562345C (en) * | 2004-04-07 | 2014-01-21 | Revcor, Inc. | Polymer nanocomposites for air movement devices |
US20070185248A1 (en) * | 2004-06-25 | 2007-08-09 | Polyone Corporation | Intumescent polylefin nanocomposites and their use |
EP1794085A1 (de) * | 2004-10-01 | 2007-06-13 | Imperial Chemical Industries Plc. | Dispersionen, filme, beschichtungen und verbundwerkstoffe |
KR100904939B1 (ko) * | 2004-11-22 | 2009-06-29 | 하르만 인터내셔날 인더스트리즈, 인코포레이티드 | 라우드스피커 플라스틱 콘 몸체 |
CA2594060A1 (en) * | 2004-12-23 | 2006-06-29 | Minh-Tan Ton-That | Compatibilization of polymer clay nanocomposites |
CN101454086B (zh) | 2005-07-15 | 2015-08-26 | 胶束技术股份有限公司 | 包含受控形态的药物粉末的聚合物涂层 |
WO2007011708A2 (en) | 2005-07-15 | 2007-01-25 | Micell Technologies, Inc. | Stent with polymer coating containing amorphous rapamycin |
US8840660B2 (en) | 2006-01-05 | 2014-09-23 | Boston Scientific Scimed, Inc. | Bioerodible endoprostheses and methods of making the same |
US8089029B2 (en) | 2006-02-01 | 2012-01-03 | Boston Scientific Scimed, Inc. | Bioabsorbable metal medical device and method of manufacture |
US8048150B2 (en) | 2006-04-12 | 2011-11-01 | Boston Scientific Scimed, Inc. | Endoprosthesis having a fiber meshwork disposed thereon |
ES2540059T3 (es) | 2006-04-26 | 2015-07-08 | Micell Technologies, Inc. | Recubrimientos que contienen múltiples fármacos |
US8545975B2 (en) * | 2006-06-26 | 2013-10-01 | Sabic Innovative Plastics Ip B.V. | Articles comprising a polyimide solvent cast film having a low coefficient of thermal expansion and method of manufacture thereof |
US7928154B2 (en) * | 2006-06-26 | 2011-04-19 | Sabic Innovative Plastics Ip B.V. | Methods of preparing polymer-organoclay composites and articles derived therefrom |
US9161440B2 (en) * | 2006-06-26 | 2015-10-13 | Sabic Global Technologies B.V. | Articles comprising a polyimide solvent cast film having a low coefficient of thermal expansion and method of manufacture thereof |
US8568867B2 (en) * | 2006-06-26 | 2013-10-29 | Sabic Innovative Plastics Ip B.V. | Polyimide solvent cast films having a low coefficient of thermal expansion and method of manufacture thereof |
EP2054537A2 (de) | 2006-08-02 | 2009-05-06 | Boston Scientific Scimed, Inc. | Endoprothese mit dreidimensionaler desintegrationssteuerung |
US8216267B2 (en) | 2006-09-12 | 2012-07-10 | Boston Scientific Scimed, Inc. | Multilayer balloon for bifurcated stent delivery and methods of making and using the same |
WO2008034048A2 (en) | 2006-09-15 | 2008-03-20 | Boston Scientific Limited | Bioerodible endoprosthesis with biostable inorganic layers |
WO2008034047A2 (en) | 2006-09-15 | 2008-03-20 | Boston Scientific Limited | Endoprosthesis with adjustable surface features |
CA2663250A1 (en) | 2006-09-15 | 2008-03-20 | Boston Scientific Limited | Bioerodible endoprostheses and methods of making the same |
US8057534B2 (en) | 2006-09-15 | 2011-11-15 | Boston Scientific Scimed, Inc. | Bioerodible endoprostheses and methods of making the same |
EP2068964B1 (de) | 2006-09-15 | 2017-11-01 | Boston Scientific Limited | Medizinische vorrichtungen und verfahren zu ihrer herstellung |
JP2010503482A (ja) | 2006-09-18 | 2010-02-04 | ボストン サイエンティフィック リミテッド | 内部人工器官 |
US9539593B2 (en) | 2006-10-23 | 2017-01-10 | Micell Technologies, Inc. | Holder for electrically charging a substrate during coating |
DE602007010669D1 (de) | 2006-12-28 | 2010-12-30 | Boston Scient Ltd | Hren dafür |
US8728170B1 (en) | 2006-12-28 | 2014-05-20 | Boston Scientific Scimed, Inc. | Bioerodible nano-fibrous and nano-porous conductive composites |
US11426494B2 (en) | 2007-01-08 | 2022-08-30 | MT Acquisition Holdings LLC | Stents having biodegradable layers |
JP5603598B2 (ja) | 2007-01-08 | 2014-10-08 | ミセル テクノロジーズ、インコーポレイテッド | 生物分解層を有するステント |
US8052745B2 (en) | 2007-09-13 | 2011-11-08 | Boston Scientific Scimed, Inc. | Endoprosthesis |
US20090152009A1 (en) * | 2007-12-18 | 2009-06-18 | Halliburton Energy Services, Inc., A Delaware Corporation | Nano particle reinforced polymer element for stator and rotor assembly |
SG192524A1 (en) | 2008-04-17 | 2013-08-30 | Micell Technologies Inc | Stents having bioabsorbable layers |
US7998192B2 (en) | 2008-05-09 | 2011-08-16 | Boston Scientific Scimed, Inc. | Endoprostheses |
US8236046B2 (en) | 2008-06-10 | 2012-08-07 | Boston Scientific Scimed, Inc. | Bioerodible endoprosthesis |
CN102159257B (zh) | 2008-07-17 | 2015-11-25 | 米歇尔技术公司 | 药物递送医疗设备 |
US7985252B2 (en) | 2008-07-30 | 2011-07-26 | Boston Scientific Scimed, Inc. | Bioerodible endoprosthesis |
JP2010056135A (ja) * | 2008-08-26 | 2010-03-11 | Japan Aviation Electronics Industry Ltd | 配線コーティング用フェノール樹脂組成物、これを用いる印刷回路基板およびその製造方法 |
US8382824B2 (en) | 2008-10-03 | 2013-02-26 | Boston Scientific Scimed, Inc. | Medical implant having NANO-crystal grains with barrier layers of metal nitrides or fluorides |
WO2010101901A2 (en) | 2009-03-02 | 2010-09-10 | Boston Scientific Scimed, Inc. | Self-buffering medical implants |
US9981072B2 (en) | 2009-04-01 | 2018-05-29 | Micell Technologies, Inc. | Coated stents |
EP2419058B1 (de) | 2009-04-17 | 2018-02-28 | Micell Technologies, Inc. | Stents mit gesteuerter elution |
EP2453834A4 (de) | 2009-07-16 | 2014-04-16 | Micell Technologies Inc | Medizinische wirkstofffreisetzungsvorrichtung |
EP2531140B1 (de) | 2010-02-02 | 2017-11-01 | Micell Technologies, Inc. | Stent und stenteinsatzsystem mit verbesserter einsetzbarkeit |
WO2011095208A1 (en) * | 2010-02-03 | 2011-08-11 | Abb Research Ltd | Electrical insulation system |
US8668732B2 (en) | 2010-03-23 | 2014-03-11 | Boston Scientific Scimed, Inc. | Surface treated bioerodible metal endoprostheses |
CA2797110C (en) | 2010-04-22 | 2020-07-21 | Micell Technologies, Inc. | Stents and other devices having extracellular matrix coating |
CA2805631C (en) | 2010-07-16 | 2018-07-31 | Micell Technologies, Inc. | Drug delivery medical device |
US10117972B2 (en) | 2011-07-15 | 2018-11-06 | Micell Technologies, Inc. | Drug delivery medical device |
US10188772B2 (en) | 2011-10-18 | 2019-01-29 | Micell Technologies, Inc. | Drug delivery medical device |
KR20150143476A (ko) | 2013-03-12 | 2015-12-23 | 미셀 테크놀로지즈, 인코포레이티드 | 생흡수성 생체의학적 임플란트 |
CN105377318A (zh) | 2013-05-15 | 2016-03-02 | 脉胜医疗技术公司 | 可生物吸收的生物医学植入物 |
CN111534260B (zh) * | 2020-04-24 | 2021-12-14 | 北京康美特科技股份有限公司 | 一种环氧树脂封装胶及其制备方法和应用 |
Family Cites Families (95)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2035546A (en) | 1932-05-14 | 1936-03-31 | Endowment Foundation | Insecticide composition |
US4125411A (en) | 1958-09-30 | 1978-11-14 | Yara Engineering Corporation | Kaolin product |
SE340695B (de) | 1963-05-31 | 1971-11-29 | Monsanto Co | |
US3515626A (en) | 1965-02-22 | 1970-06-02 | Ici Ltd | Thermoplastic laminates having improved surface properties |
US3419460A (en) | 1965-06-29 | 1968-12-31 | Fiber Industries Inc | Polyethylene terephthalate films containing surface protrusions |
GB1146668A (en) | 1965-07-12 | 1969-03-26 | Ici Ltd | Modified clay |
DE1642122B1 (de) | 1967-04-15 | 1970-07-30 | Riedel De Haen Ag | Verfahren zur Herstellung von Granulaten fuer die Schaedlungsbekaempfung |
GB1345475A (en) | 1971-02-01 | 1974-01-30 | Mitsubishi Petrochemical Co | Mthod of forming a filler and resin or rubber composition |
US3795650A (en) | 1972-10-16 | 1974-03-05 | Engelhard Min & Chem | Clay thixotrope for polyester resins and use thereof |
US3929849A (en) | 1973-10-01 | 1975-12-30 | Exxon Research Engineering Co | Tetraalkyl phosphonium aluminosilicates |
US4053493A (en) | 1973-10-01 | 1977-10-11 | Exxon Research & Engineering Co. | Layered tetraalkyl phosphonium clays |
US3912532A (en) | 1974-01-17 | 1975-10-14 | Nl Industries Inc | Urea-formaldehyde coated clay particles, as an opacifying agent |
US4221697A (en) | 1974-05-29 | 1980-09-09 | Imperial Chemical Industries Limited | Composite materials |
DE2437090A1 (de) | 1974-08-01 | 1976-02-19 | Hoechst Ag | Reinigungsmittel |
US4136103A (en) | 1975-12-29 | 1979-01-23 | Exxon Research & Engineering Co. | Substituted tetraalkyl phosphonium aluminosilicates |
GB1565362A (en) | 1976-01-28 | 1980-04-16 | Laporte Industries Ltd | Substained release of biologycally active organic compounds |
US4164487A (en) | 1976-12-23 | 1979-08-14 | The Dow Chemical Company | Water-thinnable mixtures of base-neutralized products of reaction of H3 PO4 with polyether epoxides and with other type epoxides |
US4210572A (en) | 1978-08-29 | 1980-07-01 | Nl Industries, Inc. | Coupling agents for thermosetting composites |
US4434075A (en) | 1981-10-19 | 1984-02-28 | Nl Industries, Inc. | Anionically modified organophilic clays and their preparation |
DE3145457A1 (de) | 1980-11-17 | 1982-09-09 | NL Industries, Inc., 10020 New York, N.Y. | Fluid auf oelbasis enthaltend kationische organophile tone |
JPS5790050A (en) | 1980-11-26 | 1982-06-04 | Toyota Central Res & Dev Lab Inc | Preparation of composite material consisting of clay mineral and organic polymer |
GB2090602B (en) | 1981-01-06 | 1984-08-15 | Mitsubishi Rayon Co | Polymer composition |
US4400485A (en) | 1981-08-28 | 1983-08-23 | Standard Oil Company (Indiana) | Rubber composition |
US4431755A (en) | 1982-07-16 | 1984-02-14 | Standard Oil Company (Indiana) | Rubber composition comprising phyllosilicate minerals, silanes, and quaternary ammonium salts |
US4500670B1 (en) | 1983-11-22 | 1994-12-27 | Dow Chemical Co | Composite mixtures for improving gel strength of water absorbent gels |
HU186325B (en) | 1984-08-06 | 1985-07-29 | Mta Termeszettudomanyai Kutato | Method for producing gels of reversible water-absorbing capacity and stabilized structure containing clay mineral |
US4789403A (en) | 1986-07-22 | 1988-12-06 | E.C.C. America Inc. | Surface modified layered lattice silicate pigments |
US4798766A (en) | 1985-02-08 | 1989-01-17 | E.C.C. America Inc. | Surface modified clays and process of manufacture |
US4851021A (en) | 1987-02-17 | 1989-07-25 | Armstrong World Industries, Inc. | Multi-ply composites and sheets of epoxy and flocced 2:1 layered silicates and methods for them |
US4624982A (en) | 1985-04-05 | 1986-11-25 | American Colloid Company | Method of temporarily inhibiting the swellability of water swellable clays and compositions |
US4613542A (en) | 1985-04-05 | 1986-09-23 | American Colloid Company | Method of impregnating a water-penetrable article with a swell-inhibited water swellable clay slurry |
US4676929A (en) | 1985-06-10 | 1987-06-30 | Corning Glass Works | Gels, gel products and methods |
US4739007A (en) | 1985-09-30 | 1988-04-19 | Kabushiki Kaisha Toyota Chou Kenkyusho | Composite material and process for manufacturing same |
JPS63251490A (ja) | 1987-04-08 | 1988-10-18 | Chuzo Kato | フオトクロミツク層間化合物及びエレクトロクロミツク層間化合物 |
US5229451A (en) | 1987-01-16 | 1993-07-20 | Imperial Chemical Industries Plc | Thermotropic polymer |
FR2610637B1 (fr) | 1987-02-11 | 1989-05-12 | Coatex Sa | Agent de pretraitement de materiaux mineraux grossiers en vue d'applications pigmentaires |
US4920171A (en) | 1987-02-24 | 1990-04-24 | Monadnock Paper Mills, Inc. | Water-resistant, water-flushable paper compositions |
DE3806548C2 (de) | 1987-03-04 | 1996-10-02 | Toyoda Chuo Kenkyusho Kk | Verbundmaterial und Verfahren zu dessen Herstellung |
US4894411A (en) | 1987-03-18 | 1990-01-16 | Kabushiki Kaisha Toyota Chuo Kenkyusho | Composite material and process for producing the same |
JPH0778089B2 (ja) | 1987-03-26 | 1995-08-23 | 株式会社豊田中央研究所 | 複合材料の製造方法 |
US4849006A (en) | 1987-08-07 | 1989-07-18 | E.C.C. America Inc. | Controlled release composition and method |
US5204078A (en) | 1988-01-21 | 1993-04-20 | Co-Op Chemical Co., Ltd. | Method for producing fluorine mica |
ES2059731T3 (es) | 1988-03-28 | 1994-11-16 | Altalanos Iparfejlesztesi Rt | Procedimiento de preparacion de geles capaces de absorber y soltar agua de modo reversible, a partir de minerales de arcilla y polimeros. |
DD281585A5 (de) | 1988-07-05 | 1990-08-15 | Akad Wissenschaften Ddr | Verfahren zur herstellung von aluminiumhydroxidchlorid-loesungen |
US5164440A (en) | 1988-07-20 | 1992-11-17 | Ube Industries, Ltd. | High rigidity and impact resistance resin composition |
US5248720A (en) | 1988-09-06 | 1993-09-28 | Ube Industries, Ltd. | Process for preparing a polyamide composite material |
EP0358415A1 (de) | 1988-09-06 | 1990-03-14 | Ube Industries, Ltd. | Material für Formteil und Film mit Flüssigkeits- oder Gasbarriereeigenschaft, Verfahren zu seiner Herstellung und seine Verwendung |
US4956121A (en) | 1989-01-17 | 1990-09-11 | Armstrong World Industries, Inc. | Dimethylacetamide mica and vermiculite suspensions |
US5091462A (en) | 1989-03-17 | 1992-02-25 | Ube Industries Limited | Thermoplastic resin composition |
US5206284A (en) | 1989-03-17 | 1993-04-27 | Ube Industries Ltd. | Thermoplastic resin composition |
JPH0747644B2 (ja) | 1989-05-19 | 1995-05-24 | 宇部興産株式会社 | ポリアミド複合材料及びその製造方法 |
US5391437A (en) | 1989-05-22 | 1995-02-21 | Nippon Kayaku Kabushiki Kaisha | High-strength composite material and process for producing the same |
JPH0621027B2 (ja) | 1989-09-28 | 1994-03-23 | 忠蔵 加藤 | 固体間反応による有機スメクタイトの製造方法 |
US5032546A (en) | 1990-02-28 | 1991-07-16 | Cornell Research Foundation, Inc. | Ion exchanged organic-inorganic composites |
US5032547A (en) | 1990-02-28 | 1991-07-16 | Cornell Research Foundation, Inc. | Organic-inorganic composites |
JP2872756B2 (ja) | 1990-05-30 | 1999-03-24 | 株式会社豊田中央研究所 | ポリイミド複合材料およびその製造方法 |
EP0479031B1 (de) | 1990-09-21 | 1996-12-11 | Kuraray Co., Ltd. | Harzmischung, ihre Herstellung und eine mehrschichtige Struktur |
ATE159270T1 (de) | 1991-08-12 | 1997-11-15 | Allied Signal Inc | Bildung polymerer nanokomposite aus blättrigem schichtmaterial durch ein schmelzverfahren |
WO1993004118A1 (en) | 1991-08-12 | 1993-03-04 | Allied-Signal Inc. | Melt process formation of polymer nanocomposite of exfoliated layered material |
AU653453B2 (en) | 1991-12-27 | 1994-09-29 | Sumitomo Chemical Company, Limited | Insecticidal compositions |
US5508072A (en) | 1992-08-11 | 1996-04-16 | E. Khashoggi Industries | Sheets having a highly inorganically filled organic polymer matrix |
US5506046A (en) | 1992-08-11 | 1996-04-09 | E. Khashoggi Industries | Articles of manufacture fashioned from sheets having a highly inorganically filled organic polymer matrix |
US5520998A (en) | 1992-10-12 | 1996-05-28 | Toray Industries, Inc. | Highly water-pressure-resistant and highly moisture-permeable waterproof sheet and method for producing same |
US5385776A (en) | 1992-11-16 | 1995-01-31 | Alliedsignal Inc. | Nanocomposites of gamma phase polymers containing inorganic particulate material |
US5414042A (en) | 1992-12-29 | 1995-05-09 | Unitika Ltd. | Reinforced polyamide resin composition and process for producing the same |
GB9309024D0 (en) | 1993-04-30 | 1993-06-16 | Ici Plc | Composite sheet |
US5340558A (en) | 1993-06-14 | 1994-08-23 | W.R. Grace & Co.-Conn. | Vermiculite composition with improved thermal expansion properties |
US5326500A (en) | 1993-06-14 | 1994-07-05 | W.R. Grace & Co.-Conn. | Vermiculite composition with improved chemical exfoliation |
WO1995006090A1 (en) | 1993-08-23 | 1995-03-02 | Alliedsignal Inc. | Polymer nanocomposites comprising a polymer and an exfoliated particulate material derivatized with organo silanes, organo titanates and organo zirconates dispersed therein and process of preparing same |
US5407879A (en) | 1993-09-29 | 1995-04-18 | American Colloid Company | Method of improving the contaminant resistance of a smectite clay by rewetting and impregnating the clay with a water-soluble polymer, and redrying the polymer-impregnated clay |
AU686305B2 (en) | 1994-01-24 | 1998-02-05 | Sumitomo Chemical Company, Limited | Laminate, laminated film and molding |
US5554670A (en) | 1994-09-12 | 1996-09-10 | Cornell Research Foundation, Inc. | Method of preparing layered silicate-epoxy nanocomposites |
US5587084A (en) | 1995-02-07 | 1996-12-24 | Board Of Trustees Operating Michigan State University | Method of removing organic contaminants from air and water with organophilic, quaternary phosphonium ion-exchanged smectite clays |
US5578672A (en) | 1995-06-07 | 1996-11-26 | Amcol International Corporation | Intercalates; exfoliates; process for manufacturing intercalates and exfoliates and composite materials containing same |
US5844032A (en) | 1995-06-07 | 1998-12-01 | Amcol International Corporation | Intercalates and exfoliates formed with non-EVOH monomers, oligomers and polymers; and EVOH composite materials containing same |
US5760121A (en) | 1995-06-07 | 1998-06-02 | Amcol International Corporation | Intercalates and exfoliates formed with oligomers and polymers and composite materials containing same |
US5698624A (en) | 1995-06-07 | 1997-12-16 | Amcol International Corporation | Exfoliated layered materials and nanocomposites comprising matrix polymers and said exfoliated layered materials formed with water-insoluble oligomers and polymers |
US5837763A (en) | 1995-06-07 | 1998-11-17 | Amcol International Corporation | Compositions and methods for manufacturing waxes filled with intercalates and exfoliates formed with oligomers and polymers |
US5849830A (en) | 1995-06-07 | 1998-12-15 | Amcol International Corporation | Intercalates and exfoliates formed with N-alkenyl amides and/or acrylate-functional pyrrolidone and allylic monomers, oligomers and copolymers and composite materials containing same |
US5552469A (en) | 1995-06-07 | 1996-09-03 | Amcol International Corporation | Intercalates and exfoliates formed with oligomers and polymers and composite materials containing same |
US5721306A (en) | 1995-06-07 | 1998-02-24 | Amcol International Corporation | Viscous carrier compositions, including gels, formed with an organic liquid carrier and a layered material:polymer complex |
US5659034A (en) | 1995-06-14 | 1997-08-19 | Nec Research Institute, Inc. | Layered vanadium oxide compositions |
US5760106A (en) | 1995-07-05 | 1998-06-02 | Board Of Trustees Operating Michigan State University | Sealant method of epoxy resin-clay composites |
AU6424296A (en) | 1995-08-29 | 1997-03-06 | Sumitomo Chemical Company, Limited | Gas barrier resin composition and process for producing the same |
US5830528A (en) | 1996-05-29 | 1998-11-03 | Amcol International Corporation | Intercalates and exfoliates formed with hydroxyl-functional; polyhydroxyl-functional; and aromatic compounds; composites materials containing same and methods of modifying rheology therewith |
US5804613A (en) | 1995-12-22 | 1998-09-08 | Amcol International Corporation | Intercalates and exfoliates formed with monomeric carbonyl-functional organic compounds, including carboxylic and polycarboxylic acids; aldehydes; and ketones; composite materials containing same and methods of modifying rheology therewith |
CA2182557A1 (en) | 1995-12-22 | 1997-06-23 | Gary W. Beall | Intercalates and exfoliates formed with functional monomeric organic compounds; composite materials containing same and methods of modifying rheology therewith |
US5880197A (en) | 1995-12-22 | 1999-03-09 | Amcol International Corporation | Intercalates and exfoliates formed with monomeric amines and amides: composite materials containing same and methods of modifying rheology therewith |
EP0805177B1 (de) | 1996-04-05 | 2003-09-03 | Toray Industries, Inc. | Gassperrfilm |
US5730996A (en) | 1996-05-23 | 1998-03-24 | Amcol International Corporation | Intercalates and expoliates formed with organic pesticide compounds and compositions containing the same |
US5853886A (en) | 1996-06-17 | 1998-12-29 | Claytec, Inc. | Hybrid nanocomposites comprising layered inorganic material and methods of preparation |
DK0818508T3 (da) | 1996-07-11 | 2001-11-19 | Wolff Walsrode Ag | Polyamidblandinger indeholdende faststofpartikler |
US6084019A (en) | 1996-12-31 | 2000-07-04 | Eastman Chemical Corporation | High I.V. polyester compositions containing platelet particles |
US6071988A (en) | 1996-12-31 | 2000-06-06 | Eastman Chemical Company | Polyester composite material and method for its manufacturing |
US5910523A (en) | 1997-12-01 | 1999-06-08 | Hudson; Steven David | Polyolefin nanocomposites |
-
1999
- 1999-03-19 US US09/272,277 patent/US6251980B1/en not_active Expired - Lifetime
-
2000
- 2000-02-28 CA CA002299705A patent/CA2299705A1/en not_active Abandoned
- 2000-03-17 DE DE60018316T patent/DE60018316T2/de not_active Expired - Fee Related
- 2000-03-17 MX MXPA00002760A patent/MXPA00002760A/es unknown
- 2000-03-17 EP EP00302202A patent/EP1038913B1/de not_active Expired - Lifetime
- 2000-03-21 JP JP2000078896A patent/JP2000297203A/ja active Pending
Also Published As
Publication number | Publication date |
---|---|
EP1038913A1 (de) | 2000-09-27 |
CA2299705A1 (en) | 2000-09-19 |
US6251980B1 (en) | 2001-06-26 |
DE60018316T2 (de) | 2006-04-13 |
JP2000297203A (ja) | 2000-10-24 |
EP1038913B1 (de) | 2005-03-02 |
MXPA00002760A (es) | 2002-04-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
DE60018316D1 (de) | Nanokomposite hergestellt durch Onium-Ionen interkalierten Ton und zähe mit Anhydrid gehärtete Epoxidharze | |
DE69922073D1 (de) | Epoxidharzzusammensetzung | |
DE69903256D1 (de) | Härtbare epoxyharzzusammensetzungen | |
DE60043697D1 (de) | Härtbare harzzusammensetzungen | |
DE69214220D1 (de) | Organophiler Ton | |
FI944679A0 (fi) | Saostuspiihappoja | |
DE69919221D1 (de) | Härtbare harzzusammensetzung | |
DE69229018D1 (de) | Mineralische Füllstoffe | |
GB0122195D0 (en) | Epoxy resin composition | |
DE60024795D1 (de) | Härtbare harzzusammensetzung | |
DE69827302D1 (de) | Stossfeste thermoplastische harzzusammensetzung | |
PL350298A1 (en) | Tamper evident closure | |
EP1434091A4 (de) | Positive strahlungsempfindliche harzzusammensetzung mit chemischer verstärkung | |
DE69913026D1 (de) | Epoxidharzzusammensetzung | |
FI980431A (fi) | Signaalin koodaus | |
FR2715418B1 (fr) | Barrière escamotable, notamment pour équiper les interruptions de la barrière centrale fixe d'une autoroute ou d'un équipement analogue. | |
NO934450L (no) | Epoksyharpiksmateriale | |
GB2350616B (en) | Novolak resins used as bonding agents | |
GB2337147B (en) | Improvements relating to security fencing | |
GB0006175D0 (en) | Modified clay minerals and polymer composites comprising the same | |
FR2578882B1 (fr) | Batiment collectif notamment pour court de tennis couvert, salle omnisport ou autre | |
HK1062021A1 (en) | One-pack moisture curable epoxy resin composition | |
HK1062022A1 (en) | One-pack moisture curable epoxy resin composition. | |
AU1986701A (en) | A novel polypeptide - human mariner transposase 19 and the polynucleotide encoding said polypeptide | |
NO905179L (no) | Herdbar epoksyharpiksblanding. |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
8364 | No opposition during term of opposition | ||
8339 | Ceased/non-payment of the annual fee |