DE3607950A1

DE3607950A1 - Process for producing ceramic plates or the like and ceramic plate produced by this process

Info

Publication number: DE3607950A1
Application number: DE19863607950
Authority: DE
Inventors: Michael Milbradt
Original assignee: Individual
Current assignee: Individual
Priority date: 1986-03-11
Filing date: 1986-03-11
Publication date: 1987-09-17

Abstract

Process for producing ceramic plates or the like, in which a clay slab is coated with a layer of ceramic material of a different colour and is subsequently baked; and that the graphic design of the baked, coated clay slab is performed by grinding away the appropriate parts of the differently coloured top layer.

Description

Die Erfindung betrifft ein Verfahren zum Herstellen von Keramikschildern od.dgl. sowie ein danach hergestelltes Keramikschild.The invention relates to a method for producing Ceramic signs or the like as well as a manufactured afterwards Ceramic shield.

Keramikschilder, z.B. als Namensschilder an Haus- oder Wohnungstüren, sind seit langem bekannt. Bei den her kömmlichen Herstellungsverfahren für derartige Schilder wurde der Namenszug, allein oder in Verbindung mit einem graphischen Motiv, in den frischen, noch weichen Ton ein geritzt, gedrückt oder gestanzt. Bei einem weiteren Ver fahren wird die getrocknete Tonplatte mit keramischen Farben bemalt.Ceramic signs, e.g. as name tags on house or Apartment doors have been known for a long time. With her conventional manufacturing process for such signs became the signature, alone or in connection with a graphic motif, in the fresh, yet soft tone scratched, pressed or punched. In another ver will drive the dried clay plate with ceramic Painted colors.

All diese Verfahren haben den Nachteil, daß die Schilder nach der Beschriftung trocknen und dann je nach Her stellungsverfahren bis zu zweimal gebrannt werden müssen.All these methods have the disadvantage that the signs dry after labeling and then depending on the manufacturer positioning procedures have to be fired up to twice.

Der Erfindung liegt daher die Aufgabe zugrunde, Keramik schilder ohne Verwendung irgendwelcher Farben schnell und dauerhaft zu beschriften und ein mehrmaliges Brennen nach dem Beschriften überflüssig zu machen.The invention is therefore based on the object of ceramics signs quickly and without using any colors to be permanently labeled and repeated burning to make labeling unnecessary.

Erfindungsgemäß wird diese Aufgabe durch ein Verfahren ge löst, bei dem eine Tonplatte mit einer Schicht aus andersfarbigem keramischen Material überzogen und anschließend gebrannt wird; und daß die graphische Gestaltung der gebrannten beschichteten Tonplatte durch Wegschleifen der entsprechenden Teile der andersfarbigen Deckschicht erfolgt.According to the invention, this object is achieved by a method triggers a clay plate with a layer of a different color ceramic material is coated and then fired; and that the graphic design of the fired coated Clay plate by grinding away the corresponding parts of the different colored top layer.

In einer besonderen Ausführungsform der Erfindung ist vor gesehen, daß die Tonplatte vor dem Beschichten getrocknet wird.In a special embodiment of the invention is before seen that the clay plate dried before coating becomes.

Eine weitere Ausführungsform der Erfindung sieht vor, daß die Tonplatte vor dem Beschichten einem Schrühbrand unter worfen wird.Another embodiment of the invention provides that the clay plate before being spray-coated will throw.

Erfindungsgemäß ist besonders bevorzugt, daß die Tonplatte durch Eintauchen in oder Besprühen, Übergießen oder Über rollen mit einer Engobe oder einem dünnen Schlicker eines andersfarbigen Tons beschichtet wird. According to the invention it is particularly preferred that the clay plate by immersing in or spraying, pouring over or over roll one with an engobe or a thin slip different colored clay is coated.

Es kann aber auch vorgesehen sein, daß die Tonplatte durch Eintauchen in oder Besprühen, Übergießen oder Überrollen mit einer anderfarbigen Glasur beschichtet wird.But it can also be provided that the clay plate through Immerse in or spray, pour or roll over is coated with a different colored glaze.

In einer weiteren Ausführungsform der Erfindung wird vor geschlagen, daß die Tonplatte aus hellem Ton hergestellt wird, die Beschichtung dagegen dunkel ist.In a further embodiment of the invention struck that the clay plate made of light clay the coating is dark.

Die Erfindung schlägt schließlich vor, daß die beschichtete Platte bei 950 bis 1100°C gebrannt wird.The invention finally proposes that the coated Plate is fired at 950 to 1100 ° C.

Besonders bevorzugt ist es dabei, daß die beschichtete Platte bei 1060°C gebrannt wird.It is particularly preferred that the coated Plate is fired at 1060 ° C.

Schließlich betrifft die Erfindung noch ein Keramikschild, das nach einer der obengenannten Ausführungsformen des er findungsgemäßen Verfahrens hergestellt worden ist.Finally, the invention also relates to a ceramic plate, that according to one of the above embodiments of the he inventive method has been produced.

Mit dem erfindungsgemäßen Verfahren gelingt es, ein reines Keramikschild mit besonders wetter fester Beschriftung zur Verfügung zu stellen. Die dabei verwendete Zweischicht-Technik läßt eine besonders deut liche Ausbildung von Schriftzügen und Motiven zu.With the method according to the invention it is possible to a pure ceramic sign with particularly good weather to provide fixed labeling. The one there The two-layer technique used makes one particularly clear training of lettering and motifs.

Das erfindungsgemäße Verfahren ermöglicht es, unbeschriftete Schilder herzustellen und zu bevorraten und ohne Zuhilfe nahme fremder Materialien, wie z.B. keramische Farben, die ein nochmaliges Brennen erforderlich machen würden, mit Hilfe der Schleiftechnik schnell und wirtschaftlich wetter fest zu beschriften.The method according to the invention enables unlabelled Manufacture and store signs and without any help foreign materials such as ceramic colors that would need to be fired again with With the help of grinding technology, weather is quick and economical to write firmly.

Nachstehend wird ein Ausführungsbeispiel der Erfindung ge nauer beschrieben.An embodiment of the invention is described below described in more detail.

Die Schilder werden aus einem hellen Ton geformt und ge trocknet. Dabei können die üblichen Trockentechniken und -einrichtungen verwendet werden. Bei besonders dünnen Ton platten kann es sinnvoll sein, diese vor dem nächsten Ver fahrensschritt einem kurzen Schrühbrand zu unterwerfen.The signs are formed from a light clay and ge dries. The usual drying techniques and devices are used. With particularly thin clay it may make sense to flatten these before the next ver subject to a short scrubbing fire.

Die so getrockneten oder kurz vorgebrannten Tonplatten wer den nun mit einer andersfarbigen Tonschicht, einer anders farbigen Glasur od.dgl. überzogen. Dies kann dadurch ge schehen, daß man die Teile in eine dunkle Engobe oder ei nen dünnen Schlicker eines dunklen Tones, in eine dunkle Glasur od.dgl. solange eintaucht, bis sich eine dünne, aber farblich deckende Schicht ergeben hat. Die Eintauchzeit hängt dabei von den verwendeten Tonsorten und der Beschaf fenheit des Beschichtungsmaterials ab.The so dried or briefly pre-fired clay plates who now with a different colored layer of clay, a different one colored glaze or the like. overdrawn. This can ge make sure you put the parts in a dark engobe or egg a thin slip of a dark tone, into a dark one Glaze or the like immersed until a thin, but color-opaque layer. The immersion time depends on the types of clay used and the supply of the coating material.

Zur Beschichtung der Tonplatte ist natürlich auch eines der üblichen Spritzverfahren anwendbar. Schließlich kann die Beschichtung auch durch Übergießen oder Überrollen auf die Platte aufgebracht werden.Of course, one of the is also for coating the clay plate usual spraying method applicable. Finally, the Coating also by pouring over or rolling over the Plate are applied.

Die so vorbehandelten Tonplatten werden nun bei Temperaturen zwischen 950 und 1100°C gebrannt, wobei bei beinahe allen Tonsorten, die für diese Zwecke verwendet werden, die Ideal temperatur bei etwa 1060°C liegt. Diese Brenntemperatur stellt den optimalen Kompromiß zwischen weitestgehender Frostsicher heit des Endproduktes und ausreichender Gravierfähigkeit der beschichteten Tonplatte dar. The clay plates pretreated in this way are now at temperatures fired between 950 and 1100 ° C, with almost all Types of clay used for these purposes, the ideal temperature is around 1060 ° C. This firing temperature provides the optimal compromise between as far as possible frost-proof of the end product and sufficient engraving ability coated clay plate.

Die Beschichtung oder Gravur erfolgt nun durch Wegschleifen der entsprechenden Teile der dünnen, dunklen Deckschicht mittels dafür üblichen Schleifgeräten, Graviermaschinen oder Handgravierern. Dadurch wird das verwendete helle Grundmaterial des Schildes wieder sichtbar. Auf diese Wei se wird eine kontrastreiche, besonders deutliche Ausbil dung von Namenszügen und Motiven ermöglicht.The coating or engraving is now done by grinding away the corresponding parts of the thin, dark top layer using conventional grinders, engraving machines or hand engravers. This will make the light used The base material of the sign is visible again. In this way It will be a high-contrast, particularly clear training names and motifs.

Das erfindungsgemäße Verfahren ist natürlich von den ver wendeten Einfärbungen unabhängig. Möglich wäre es daher auch, die Grundplatte aus dunklem Ton herzustellen und hell zu beschichten.The method according to the invention is of course ver applied coloring independently. It would therefore be possible also to make the base plate from dark clay and bright to coat.

Die in der vorstehenden Beschreibung sowie in den Ansprüchen offenbarten Merkmale der Erfindung können sowohl einzeln als auch in beliebigen Kombinationen für die Verwirklichung der Erfindung in ihren verschiedenen Ausführungsformen wesentlich sein.The in the above description as well as in the claims disclosed features of the invention can be used both individually and also in any combination for the realization of the Invention in its various embodiments essential be.

Claims

1. A process for the manufacture of ceramic plates or the like, characterized in that an audio disk is coated with a layer of a differently colored ceramic material and then fired. and that the graphical design of the fired coated clay plate is carried out by grinding away the corresponding parts of the different colored top layer.

2. The method according to claim 1, characterized in that the clay plate is dried before coating.

3. The method according to claim 1, characterized in that the clay plate before being spray-coated will throw.

4. The method according to any one of claims 1 to 3, characterized ge indicates that the clay plate by immersing in or Spray, pour over or roll over with an engobe or coated with a thin slip of a different color becomes.

5. The method according to any one of claims 1 to 3, characterized ge indicates that the clay plate by immersing in or Spray, pour or roll over with a different color beige glaze is coated.

6. The method according to any one of the preceding claims, since characterized in that the clay plate made of light clay is produced, but the coating is dark.

7. The method according to any one of the preceding claims, since characterized in that the coated plate at 950 to 1100 ° C is fired.

8. The method according to claim 7, characterized in that the coated plate is fired at 1060 ° C.

9. Ceramic shield, manufactured using a process according to any of the preceding claims.