DE2932861C2 - Heißsiegelfähige Polyamidfolie mit zwei Beschichtungen - Google Patents

Heißsiegelfähige Polyamidfolie mit zwei Beschichtungen

Info

Publication number
DE2932861C2
DE2932861C2 DE2932861A DE2932861A DE2932861C2 DE 2932861 C2 DE2932861 C2 DE 2932861C2 DE 2932861 A DE2932861 A DE 2932861A DE 2932861 A DE2932861 A DE 2932861A DE 2932861 C2 DE2932861 C2 DE 2932861C2
Authority
DE
Germany
Prior art keywords
film
polyamide film
layer
heat
coatings
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE2932861A
Other languages
English (en)
Other versions
DE2932861A1 (de
Inventor
Rudolf Burgdorf Bern Hofer
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Amcor Flexibles Burgdorf GmbH
Original Assignee
Schuepbach AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority to CH738479A priority Critical patent/CH619644A5/de
Application filed by Schuepbach AG filed Critical Schuepbach AG
Priority to DE2932861A priority patent/DE2932861C2/de
Publication of DE2932861A1 publication Critical patent/DE2932861A1/de
Application granted granted Critical
Publication of DE2932861C2 publication Critical patent/DE2932861C2/de
Expired legal-status Critical Current

Description

Die Erfindung betrifft eine heißsiegelfähige Polyamidfolie der im Oberbegriff des Hauptancpruches genannten Art sowie ihre Verwendung bei aufreißbaren Verpackungen.
Durch die DE-OS 24 27 489 ist eine derartige Kunststoffolie bekannt. Sie besteht aus Polyamid mit einer Zwischenschicht aus Vinylidenchlorid und einer heißsiegelfähigen Deckschicht mit wenigstens 86% Vinylidenchloridanteil bekannt. Ihr liegt die Aufgabe zugrvnde, die Deckschicht mit ihrem hohen VÜC-Anteil einerseits heißsiegelfähig zu machen, andererseits die Feuchtwarmblock-Eigenschaft der Deckschicht nicht zu erhöhen. Dies wird durch Zugabe eines weichmachenden Polymeres in einem Anteil von 0,5—20% zu dem VDC-Anteil erreicht. — Eine solche Folie ist nur mit sich selbst gut siegelfähig, d. h. an Stellen an denen die Folie sich überlappt wie z. B. bei Umhüllungen von Zigarettenpackungen, für die die bekannte Folie in erster Linie gedacht ist wegen ihres geringen Feuchtwarmblockverhaltens und bei der das Aufreißen im allgemeinen mit einem Hilfsmittel, z. B. einem Aufreißfaden oder -streifen ausgeführt wird. Der hohe Anteil an VDC in der Deckschicht verhindert das Heißsiegeln mit fremden Kunststoffen und ein glattes Aufreißen an diesen.
Demgegenüber liegt der Erfindung die Aufgabe zu Grunde, eine beschichtete Polyamidfolie nach dem Oberbegriff des Hauptanspruches zu schaffen, die auch mit einem anderen Kunststoff, wie z. B. PVC gut heißsiefcelbar und ohne Hilfsmittel leicht von diesem abreißbar ist, so daß Verpackungen aus diesem anderen Kunststoff mit der Polyamidfolie durch Heißsiegeln sicher und dicht verschließbar sind und dennoch durch Erfassen an einem Folienabschnitt durch leichtes Aufreißen derselben geöffnet werden können, ohne daß die Folie selbst verletzt oder zerstört wird.
Zur Lösung dieser Aufgabe sieht die Erfindung die Merkmale des kennzeichnenden Teils des Hauptanspruches vor. Die Ansprüche 2 und 3 betreffen eine vorteilhafte Ausgestaltung des Gegenstandes des Hauplanspruches sowie die Verwendung der Polyamidfolie.
Gegenüber der Folie nach der DE-OS 24 27 489 mit
ihrem hohen PVDC-Anteil in der Deckschicht ist überraschend, daß der an sich bekannte Thermolack der erfindungsgemäßen Folie mit geringen Anteilen an PVDC oder VDC gute Heißsiegeleigenschaften zeigt
Der Vorteil der erfindungsgemäßen Folie besteht darin, daß sie außer der bekannten Wirkung einer Dampf- und Feuchtigkeitssperre bei Anwendung als Verpackungsverschluß ein Aufreißen in der Ebene oder an der Thermolackschicht ermöglicht, d. h. ein Kohäsionsbruch in der PVDC-Zwischenschicht erfolgt, ohne daß hierbei z. B. eine Deckfolie aus Aluminium, mit der die Folie kaschiert wird, einreißt, so daß Schnittverletzungen vermieden werden.
Bei einer vorzugsweisen Ausführungsform der Folie ist diese aus PA 6 oder 6,6 mit einer Aluminium-Deckfolie von 0,009 bis 0,030 mm Dicke oder mit einer Papierlage von 60 g/m2 Flächengewicht verSi?*Ten.
Unter Einhaltung der vorstehenden Vorteile bieten sich auch beim Kaschieren der Folie mit einer Papieroder Aluminium-Deckfolie herstellungsmäßige Vorteile. — Ein weiterer Vorteil der erfindungsgemäßen Schichtenkombination ergibt sich daraus, daß sie in einem weiten Temperaturbereich heißsiegelbar ist
Die Kombination von PA 6 oder 6,6/PVDC/Gemisch von mindestens einem Methacryl-Copolymer und mindestens einem Vinyl-Copolymer als Gesamtheit zeitigt eine besonders gute Versiegelung und Aufreißbarkeit einer verschlossenen Packung. Die Reihenfolge der drei Schichten, nämlich PA 6 oder 6,6 als eigentliche Verschlußfolie, PVDC als Haftschicht und der Thermolack, ist für die erfindungsgemäße Folie unerläßlich. Es wird angenommen, daß alle drei Schichten untereinander und mit dem anderen Kunststoff, z. B. einem Bechermaterial bei der Heißsiegelung eine Verschmelzung eingehen. Der genaue Mechanismus dieses Vorgangs ist jedoch noch nicht restlos abgeklärt.
Die Herstellung der Folie kann auf bekannte Art unter Einsatz der üblichen Lackier- und Kaschiermaschinen erfolgen. Mit PVDC beschichtetes PA 6 oder 6,6 ist im Handel, jedoch für andere Verwendungszwecke, erhältlich. Falls die Herstellung von Grund auf erfolgt, ist es zweckmäßig und empfehlenswert, die Beschichtung der Folie aus PA 6 oder 6,6 mit dem als Haftschicht wirkenden PVDC im Zuge der Folienherstellung vorzunehmen. Die Lackierung mit dem Thermolack kann dann zu einem späteren Zeitpunkt erfolgen, wobei der Thermolack auch partiell, d. h. nur in den heißzusiegelnden Zonen aufgetragen werden kann.
Das als; Thermolack zum Einsatz gelangende, an und für sich bekannte Gemisch, muß ein oder mehrere Copolymere von Methacrylat und Vinyl enthalten.
Nachstehend !.ind beispielsweise Ausführungsformen der erfindungsgemäßen Folie angeführt, wobei für Polyamidfolie sowohl PA 6 wie auch PA 6,6 verwendet werden kann, wovon jedoch PA 6 bevorzugt wird.
Beispiele
a) Außenlackierung / Alufolie 15μηι/ΡΑ
20 μιη /
20 μιη /
PVDC 4 g/m2 / Thermolack 4 g/m2
AußonlackierunR / Papier 60 g/m2 / PA
PVDC 4 g/m2 / Thermolack 4 g/m2
c) Außenlackierung/PA 40 μιη / PVDC 4 g/m2 / Thermolack 4 g/m2
d) Außenlackierung / Zellglas / PA 20 μιη / PVDC 4 g/m2 / Thermolack 4 g/m2

Claims (3)

Patentansprüche:
1. Heißsiegelfähige Polyamidfolie mit zwei Beschichtungen, von denen die der Polyamidfolie benachbarte Beschichtung eine Polyvinylidenchloridschicht ist, dadurch gekennzeichnet, daß die zweite, der Folie abgewandte Schicht eine Thermolackschicht aus einem Gemisch von mindestens einem Methacrylat-Copolyiner und mindestens einem Vinyl-Copolymer ist.
2. Heißsiegelfähige Polyamidfolie nach Anspruch 1, dadurch gekennzeichnet, daß die Folie auf ihrer freien, der Thermolackschicht abgewendeten Oberfläche mit einer Deckfolie aus Aluminium oder Papier kaschiert und/oder mit einer Außenlackierung versehen ist
3. Verwendung einer Siegelschichtkombination nach Anspruch 1 zum Verschließen von in der Siegelnaht aufreißbaren Packungen.
DE2932861A 1979-08-10 1979-08-14 Heißsiegelfähige Polyamidfolie mit zwei Beschichtungen Expired DE2932861C2 (de)