DE2251535C3 - Verwendung einer Pulvermischung für die pulvermetallurgische Herstellung von verschleißfesten Gegenständen - Google Patents
Verwendung einer Pulvermischung für die pulvermetallurgische Herstellung von verschleißfesten GegenständenInfo
- Publication number
- DE2251535C3 DE2251535C3 DE2251535A DE2251535A DE2251535C3 DE 2251535 C3 DE2251535 C3 DE 2251535C3 DE 2251535 A DE2251535 A DE 2251535A DE 2251535 A DE2251535 A DE 2251535A DE 2251535 C3 DE2251535 C3 DE 2251535C3
- Authority
- DE
- Germany
- Prior art keywords
- percent
- powder
- weight
- wear
- metallurgical production
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
für die pulvermetallvtrgische Herstellung von Gegenständen
mit besonders guten Verschleißeigenschaften.
Die Erfindung betrifft die Verw endung einer Pulvermischung
für die pulvermetallurgisch^ Herstellung von Gegenständen.
Es ist eine Metallpulvermischung \>ekannt (deutsche
Auslegeschrift 1213 624), die aus 0' bis 6 Gewichtsprozent
Nickel, 0 bis 4 Gewichtsprozent Mangan, 0 bis 1,5 Gewichtsprozent Kohlenstoff in Form von
Graphit, 0,5 bis 5 Gewichtsprozent Kupfer, 0,01 bis 0,4 Gewichtsprozent Bor, Rest Eisen mit den üblichen
Verunreinigungen, besteht. Eine bevorzugte Mischung der bekannten Art besteht aus
2,4 Gewichtsprozent Nickel,
1 Gewichtsprozent Kupfer,
1,6 Gewichtsprozent Mangan,
0,8 Gewichtsprozent Kohlenstoff
1 Gewichtsprozent Kupfer,
1,6 Gewichtsprozent Mangan,
0,8 Gewichtsprozent Kohlenstoff
in Form von Graphit,
0,2 Gewichtsprozent Kupferborat,
Rest Elisen mit den üblichen Verunreinigungen.
0,2 Gewichtsprozent Kupferborat,
Rest Elisen mit den üblichen Verunreinigungen.
Mit diesen Metallpulvermischunjjen werden Eisenlegierungen
mit verbesserter Zugfestigkeit hergestellt.
Bei bestimmten gesinterten Gegenständen, wie beispielsweise Lagerflächen und Gleitbahnen, werden
jedoch besonders gute Verschleißeigenschaften gefordert, die unabhängig von der Zugfestigkeit sind.
Der Erfindung liegt daher die Aufgabe zugrunde, die Herstellung von Gegenständen mit den genannten Eigenschaften zu ermöglichen.
Der Erfindung liegt daher die Aufgabe zugrunde, die Herstellung von Gegenständen mit den genannten Eigenschaften zu ermöglichen.
Die Lösung dieser Aufgabe besteht in der erfindungsgemäßen
Verwendung einer Pulvermischung aus
1 bis 1,35 Gewichtsprozent Kohlenstoff
in Form von Graphit,
2 bis 2,4 Gewichtsprozent Mangan,
1,4 bis 1,7 Gewichtsprozent Nickel,
1 Gewichtsprozent Kupfer,
2 bis 2,4 Gewichtsprozent Mangan,
1,4 bis 1,7 Gewichtsprozent Nickel,
1 Gewichtsprozent Kupfer,
0,2 Gewichtsprozent Kupferborat,
Rest Eisen mit den üblichen Verunreinigungen,
für die pulvermetallurgische Herstellung von Gegenständen mit besonders guten Verschleißeigenschaften,
ao wobei der gesinterte Werkstoff ein ausgeprägtes
gleichmäßiges Karbidnetz aufweist.
Durch das Vorhandensein eines solchen gleichmäßigen Karbidnetzes in einem lamellaren perlitischen
Grundgefüge mit eingelagertem Restaustenit und Martensit werden die Verschleißeigenschaften sehr
wesentlich verbessert. Ermöglicht wird dies durch einen Kohlenstoffgehalt von 1 bis 1,35% in dem zu
verpressenden Pulver. Ein höherer Kohlenstoffgehalt würde eine unwirtschaftliche Verschlechterung der
Zerspanbarkeit der Werkstücke mit sich bringen. Die Pulvermischung wird auf eine Dichte von mindestens
ρ = 6,75 g/cm3 gepreßt und gesintert. Die Sinterung
erfolgt bei etwa H 50° C 25 Minuten lang in einer Atmosphäre aus dissoziiertem, mit Propan angereichertem
Ammoniak. Ein metallisches Stearat wird beim Tablettieren der Teile als Schmiermittel verwendet.
Die Ofenatmosphäre wird so eingestellt, daß alle Verbrennungsprodukte dieses Schmiermittels in die
Sinterzone gebracht werden und zusammen mit der beschriebenen Atmosphärenzusammensetzung einen
minimalen Kohlenstoff-Abbau garantieren.
Claims (1)
- Patentanspruch:Verwendung einer Pulvermischung aus1 bis 1,35 Gewichtsprozent Kohlenstoffin Form von Graphit,2 bis 2,4 Gewichtsprozent Mangan,
1,4 bis 1,7 Gewichtsprozent Nickel,1 Gewichtsprozent Kupfer,0,2 Gewichtsprozent Kupferborat,Rest Eisen mit üblichen Verunreinigungen,