DE102007023497B4 - Verfahren und Vorrichtung zur Herstellung von Gläsern, Glaskeramiken oder Keramiken sowie deren Verwendung - Google Patents

Verfahren und Vorrichtung zur Herstellung von Gläsern, Glaskeramiken oder Keramiken sowie deren Verwendung Download PDF

Info

Publication number
DE102007023497B4
DE102007023497B4 DE102007023497A DE102007023497A DE102007023497B4 DE 102007023497 B4 DE102007023497 B4 DE 102007023497B4 DE 102007023497 A DE102007023497 A DE 102007023497A DE 102007023497 A DE102007023497 A DE 102007023497A DE 102007023497 B4 DE102007023497 B4 DE 102007023497B4
Authority
DE
Germany
Prior art keywords
tubular outlet
glass
melt
vessel
iridium
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE102007023497A
Other languages
German (de)
English (en)
Other versions
DE102007023497A1 (de
Inventor
Uwe Dr. Kolberg
Thomas Kirsch
Paul Kissl
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Schott AG
Original Assignee
Schott AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Schott AG filed Critical Schott AG
Priority to DE102007023497A priority Critical patent/DE102007023497B4/de
Priority to GB0808466.7A priority patent/GB2450588B/en
Priority to US12/118,832 priority patent/US20080282734A1/en
Priority to JP2008128370A priority patent/JP4927027B2/ja
Priority to FR0853197A priority patent/FR2916197B1/fr
Publication of DE102007023497A1 publication Critical patent/DE102007023497A1/de
Application granted granted Critical
Publication of DE102007023497B4 publication Critical patent/DE102007023497B4/de
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B5/00—Melting in furnaces; Furnaces so far as specially adapted for glass manufacture
    • C03B5/16—Special features of the melting process; Auxiliary means specially adapted for glass-melting furnaces
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B5/00—Melting in furnaces; Furnaces so far as specially adapted for glass manufacture
    • C03B5/16—Special features of the melting process; Auxiliary means specially adapted for glass-melting furnaces
    • C03B5/167—Means for preventing damage to equipment, e.g. by molten glass, hot gases, batches
    • C03B5/1672—Use of materials therefor
    • C03B5/1675—Platinum group metals
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B5/00—Melting in furnaces; Furnaces so far as specially adapted for glass manufacture
    • C03B5/02—Melting in furnaces; Furnaces so far as specially adapted for glass manufacture in electric furnaces, e.g. by dielectric heating
    • C03B5/021—Melting in furnaces; Furnaces so far as specially adapted for glass manufacture in electric furnaces, e.g. by dielectric heating by induction heating
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
    • C03B5/00—Melting in furnaces; Furnaces so far as specially adapted for glass manufacture
    • C03B5/16—Special features of the melting process; Auxiliary means specially adapted for glass-melting furnaces
    • C03B5/26—Outlets, e.g. drains, siphons; Overflows, e.g. for supplying the float tank, tweels
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/062—Glass compositions containing silica with less than 40% silica by weight
    • C03C3/064—Glass compositions containing silica with less than 40% silica by weight containing boron
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/083—Glass compositions containing silica with 40% to 90% silica, by weight containing aluminium oxide or an iron compound
    • C—CHEMISTRY; METALLURGY
    • C03—GLASS; MINERAL OR SLAG WOOL
    • C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C3/00—Glass compositions
    • C03C3/04—Glass compositions containing silica
    • C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
    • C03C3/089—Glass compositions containing silica with 40% to 90% silica, by weight containing boron
    • C03C3/091—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Organic Chemistry (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Crucibles And Fluidized-Bed Furnaces (AREA)
  • Glass Compositions (AREA)
  • Liquid Crystal (AREA)
  • Glass Melting And Manufacturing (AREA)
DE102007023497A 2007-05-18 2007-05-18 Verfahren und Vorrichtung zur Herstellung von Gläsern, Glaskeramiken oder Keramiken sowie deren Verwendung Expired - Fee Related DE102007023497B4 (de)

Priority Applications (5)

Application Number Priority Date Filing Date Title
DE102007023497A DE102007023497B4 (de) 2007-05-18 2007-05-18 Verfahren und Vorrichtung zur Herstellung von Gläsern, Glaskeramiken oder Keramiken sowie deren Verwendung
GB0808466.7A GB2450588B (en) 2007-05-18 2008-05-09 Apparatus and method for the production of high-melting glass materials or glass ceramic materials
US12/118,832 US20080282734A1 (en) 2007-05-18 2008-05-12 Apparatus and method for the production of high-melting glass materials or glass ceramic materials
JP2008128370A JP4927027B2 (ja) 2007-05-18 2008-05-15 高融点ガラス材料あるいは高融点ガラスセラミック材料の製造装置及び方法
FR0853197A FR2916197B1 (fr) 2007-05-18 2008-05-16 Appareil et procede pour la production de materiaux de verre ou de materiaux de vitroceramique a haute temperature de fusion

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
DE102007023497A DE102007023497B4 (de) 2007-05-18 2007-05-18 Verfahren und Vorrichtung zur Herstellung von Gläsern, Glaskeramiken oder Keramiken sowie deren Verwendung

Publications (2)

Publication Number Publication Date
DE102007023497A1 DE102007023497A1 (de) 2008-11-20
DE102007023497B4 true DE102007023497B4 (de) 2010-08-05

Family

ID=39571089

Family Applications (1)

Application Number Title Priority Date Filing Date
DE102007023497A Expired - Fee Related DE102007023497B4 (de) 2007-05-18 2007-05-18 Verfahren und Vorrichtung zur Herstellung von Gläsern, Glaskeramiken oder Keramiken sowie deren Verwendung

Country Status (5)

Country Link
US (1) US20080282734A1 (https=)
JP (1) JP4927027B2 (https=)
DE (1) DE102007023497B4 (https=)
FR (1) FR2916197B1 (https=)
GB (1) GB2450588B (https=)

Families Citing this family (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
FR2938554B1 (fr) * 2008-11-19 2011-05-06 Areva Nc Procede de revetement d'un element de creuset metallique par un melange de verre et de ceramique
DE102010051664A1 (de) * 2010-11-17 2012-05-24 Liebherr-Hydraulikbagger Gmbh Arbeitsgerät
DE102010051663A1 (de) 2010-11-17 2012-05-24 Liebherr-Hydraulikbagger Gmbh Arbeitsgerät
JP5637626B2 (ja) * 2011-03-25 2014-12-10 日本山村硝子株式会社 温度計測器付きオリフィス、及びガラスびんの製造方法
CN102229465B (zh) * 2011-04-30 2013-04-10 浙江大学 铝锂硅微晶玻璃熔窑的膜法富氧燃烧装置及用法
DE102014206214A1 (de) * 2014-04-01 2015-10-01 Beiersdorf Ag Verfahren zum Schutz der Haut vor UV-Strahlung
RU2693152C2 (ru) * 2015-01-06 2019-07-01 Филипс Лайтинг Холдинг Б.В. Способ и печатающая головка для трехмерной печати стекла
DE102016105519A1 (de) * 2015-03-24 2016-09-29 Shin-Etsu Chemical Co., Ltd. Sintervorrichtung und Sinterverfahren
DE102015117422A1 (de) * 2015-10-13 2017-04-13 Schott Ag Wolfram-haltiger Formdorn zur Glasformung
US20180155231A1 (en) * 2016-12-07 2018-06-07 Corning Incorporated Flow stopper for a bottom delivery melter
KR102386231B1 (ko) * 2018-01-30 2022-04-14 코닝 인코포레이티드 용융 유리 교반 챔버
US11760678B2 (en) * 2018-04-20 2023-09-19 Corning Incorporated Apparatus and method for controlling an oxygen containing atmosphere in a glass manufacturing process
KR20210080595A (ko) 2018-11-21 2021-06-30 코닝 인코포레이티드 유리 멜트 표면 상의 버블 수명 감소 방법
WO2021202102A1 (en) * 2020-03-30 2021-10-07 Corning Incorporated Apparatus and method for reducing defects in glass melt systems
CN111811275B (zh) * 2020-06-24 2021-10-08 中国科学院金属研究所 利用三明治布料方式和电磁感应熔炼引熔高熔点混合物的方法

Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0222132A (ja) * 1988-07-07 1990-01-25 Furuya Kinzoku:Kk 高品位ガラスの溶解装置
EP0220333B1 (de) * 1985-10-26 1990-03-21 Schott Glaswerke Durchsichtige farbige Glaskeramik mit guter Temperaturbelastbarkeit und variabel einstellbarer Transmission im IR-Bereich
US4938198A (en) * 1988-08-30 1990-07-03 Toyota Jidosha Kabushiki Kaisha Internal combustion engine
DE4321373C2 (de) * 1993-06-26 1995-12-14 Schott Glaswerke Glaskeramik mit hoher Transmission im Wellenlängenbereich von 2700 bis 3300 nm, Verfahren zu deren Herstellung und deren Verwendung
DE19622522C1 (de) * 1996-06-05 1998-01-22 Schott Glaswerke Verfahren zur Herstellung von dichtgesinterten Glaskeramik-Formkörpern
DE19907038A1 (de) * 1999-02-19 2000-08-31 Schott Glas Transluzente oder opake Glaskeramik mit Hochquarz-Mischkristallen als vorherrschender Kristallphase und deren Verwendung
DE19939781A1 (de) * 1999-08-21 2001-02-22 Schott Glas Skulltiegel für das Erschmelzen oder das Läutern von anorganischen Substanzen, insbesondere von Gläsern und Glaskeramiken
DE19939787A1 (de) * 1999-08-21 2001-02-22 Schott Glas Transparente, mit Vanadiumoxid-Zusatz dunkel einfärbbare Glaskeramik mit Hochquarz-Mischkristallen als vorherrschende Kristallphase und Verfahren zu ihrer Herstellung
DE10017699A1 (de) * 2000-04-08 2001-11-29 Schott Glas Verglasung von Räumen, die einem extrem hohen Temperaturgradienten ausgesetzt sind
EP1160208A2 (en) * 2000-05-22 2001-12-05 General Electric Company Quartz fusion crucible
EP1170264A1 (de) * 2000-07-04 2002-01-09 Schott Glas Transluzente Glaskeramik, Verfahren zur Herstellung einer transluzenten Glaskeramik sowie deren Verwendung
DE10017701C2 (de) * 2000-04-08 2002-03-07 Schott Glas Gefloatetes Flachglas
WO2002044115A2 (de) * 2000-11-30 2002-06-06 Schott Glas Beschichtetes metallteil in der glasherstellung
US6482758B1 (en) * 1999-10-14 2002-11-19 Containerless Research, Inc. Single phase rare earth oxide-aluminum oxide glasses
DE10348466A1 (de) * 2003-10-14 2005-05-19 Schott Ag Vorrichtung und Verfahren zur Herstellung von hoch schmelzenden Gläsern oder Glaskeramiken sowie Glas oder Glaskeramik

Family Cites Families (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3867137A (en) * 1973-06-22 1975-02-18 Atomic Energy Commission Purification of iridium
EP0087409A1 (en) * 1981-08-24 1983-09-07 CARMAN, Justice N. Glass making furnace apparatus
WO1983004245A1 (en) * 1982-05-24 1983-12-08 Carman Justice N Homogenizing apparatus and glass making furnace
JPH01219028A (ja) * 1988-02-29 1989-09-01 Hoya Corp ガラスの溶融方法
GB8911441D0 (en) * 1989-05-18 1989-07-05 Tetronics Res & Dev Co Ltd A process for the treatment of molten materials
WO2002016279A1 (de) 2000-08-24 2002-02-28 Schott Glas Transparente, mit vanadiumoxid-zusatz dunkel einfärbbare glaskeramik
DE102006003521B4 (de) * 2006-01-24 2012-11-29 Schott Ag Vorrichtung und Verfahren zum kontinuierlichen Läutern von Gläsern mit hohen Reinheitsanforderungen

Patent Citations (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0220333B1 (de) * 1985-10-26 1990-03-21 Schott Glaswerke Durchsichtige farbige Glaskeramik mit guter Temperaturbelastbarkeit und variabel einstellbarer Transmission im IR-Bereich
JPH0222132A (ja) * 1988-07-07 1990-01-25 Furuya Kinzoku:Kk 高品位ガラスの溶解装置
US4938198A (en) * 1988-08-30 1990-07-03 Toyota Jidosha Kabushiki Kaisha Internal combustion engine
DE4321373C2 (de) * 1993-06-26 1995-12-14 Schott Glaswerke Glaskeramik mit hoher Transmission im Wellenlängenbereich von 2700 bis 3300 nm, Verfahren zu deren Herstellung und deren Verwendung
DE19622522C1 (de) * 1996-06-05 1998-01-22 Schott Glaswerke Verfahren zur Herstellung von dichtgesinterten Glaskeramik-Formkörpern
DE19907038A1 (de) * 1999-02-19 2000-08-31 Schott Glas Transluzente oder opake Glaskeramik mit Hochquarz-Mischkristallen als vorherrschender Kristallphase und deren Verwendung
DE19939781A1 (de) * 1999-08-21 2001-02-22 Schott Glas Skulltiegel für das Erschmelzen oder das Läutern von anorganischen Substanzen, insbesondere von Gläsern und Glaskeramiken
DE19939787A1 (de) * 1999-08-21 2001-02-22 Schott Glas Transparente, mit Vanadiumoxid-Zusatz dunkel einfärbbare Glaskeramik mit Hochquarz-Mischkristallen als vorherrschende Kristallphase und Verfahren zu ihrer Herstellung
US6482758B1 (en) * 1999-10-14 2002-11-19 Containerless Research, Inc. Single phase rare earth oxide-aluminum oxide glasses
DE10017699A1 (de) * 2000-04-08 2001-11-29 Schott Glas Verglasung von Räumen, die einem extrem hohen Temperaturgradienten ausgesetzt sind
DE10017701C2 (de) * 2000-04-08 2002-03-07 Schott Glas Gefloatetes Flachglas
EP1160208A2 (en) * 2000-05-22 2001-12-05 General Electric Company Quartz fusion crucible
EP1170264A1 (de) * 2000-07-04 2002-01-09 Schott Glas Transluzente Glaskeramik, Verfahren zur Herstellung einer transluzenten Glaskeramik sowie deren Verwendung
WO2002044115A2 (de) * 2000-11-30 2002-06-06 Schott Glas Beschichtetes metallteil in der glasherstellung
DE10348466A1 (de) * 2003-10-14 2005-05-19 Schott Ag Vorrichtung und Verfahren zur Herstellung von hoch schmelzenden Gläsern oder Glaskeramiken sowie Glas oder Glaskeramik

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
Platinum metals review 1965, 9(2), 51-56 *

Also Published As

Publication number Publication date
GB2450588A (en) 2008-12-31
GB0808466D0 (en) 2008-06-18
GB2450588B (en) 2013-02-20
US20080282734A1 (en) 2008-11-20
FR2916197A1 (fr) 2008-11-21
DE102007023497A1 (de) 2008-11-20
JP4927027B2 (ja) 2012-05-09
FR2916197B1 (fr) 2014-01-17
JP2008285402A (ja) 2008-11-27

Similar Documents

Publication Publication Date Title
DE102007023497B4 (de) Verfahren und Vorrichtung zur Herstellung von Gläsern, Glaskeramiken oder Keramiken sowie deren Verwendung
DE10348466B4 (de) Vorrichtung und Verfahren zur Herstellung von hoch schmelzenden Gläsern oder Glaskeramiken und Verwendung einer Vorrichtung
EP2184264B1 (de) Vorrichtung zum blasenfreien Transportieren, Homogenisieren und Konditionieren von geschmolzenem Glas
DE69807812T3 (de) Vakuumentgasungsvorrichtung für geschmolzenes Glas
DE102007008299B4 (de) Verfahren zur Herstellung von Gläsern, wobei die chemische Reduktion von Bestandteilen vermieden wird
DE102006003521B4 (de) Vorrichtung und Verfahren zum kontinuierlichen Läutern von Gläsern mit hohen Reinheitsanforderungen
DE10393837B4 (de) Verfahren und Vorrichtung zur Beheizung von Schmelzen
DE60128488T2 (de) Ofen und verfarhen zum schmelzen und formen von gegenständen aus quarzglas
DE60129376T2 (de) Verfahren und Vorrichtung zur Herstellung von Quarzglaskörpern
EP1618074B1 (de) Schmelzen und läutern in wannen mit gekühlten wänden
DE102007004242B4 (de) Verfahren zum Herstellen eines Formkörpers aus Quarzglas durch Sintern, Formkörper und Verwendung des Formkörpers
DE2729188A1 (de) Hochtemperatur-reaktor und verfahren zu seinem betrieb
EP2627609B1 (de) Reduzierung von pt und rh abdampfverlusten bei hohen temperaturen durch verwendung einer sperrschicht
DE102010037437B4 (de) Glasschmelzanlage sowie Verfahren zum Betreiben einer solchen Glasschmelzanlage
DE1206553B (de) Ofen zum Schmelzen von Glas oder aehnlichen Produkten und Verfahren zum Betrieb des Ofens
DE20321430U1 (de) Vorrichtung zur Herstellung von hoch schmelzenden Gläsern oder Glaskeramiken sowie Glas oder Glaskeramik
DE102006051049B4 (de) Oxidationsgeschützte Behältnisse aus Iridium zum Transportieren und/oder Konditionieren einer Glasschmelze, insbesondere für den kontinuierlichen Betrieb, sowie Verfahren
DE102011105145B4 (de) Vorrichtung zum Transportieren, Homogenisieren und/oder Konditionieren einer anorganischen nichtmetallischen Schmelze, Verfahren zur Herstellung eines Glases und/oder einer Glaskeramik sowie Verfahren zur Herstellung einer Sicke in Iridiumblech
DE102006019647B4 (de) Verfahren zum Dimensionieren einer drehbaren Vorrichtung zum Herstellen einer Schmelze sowie drehbare Vorrichtung
DE10236136A1 (de) Hochfrequenzbeheizter kalter Tiegel, insbesondere zum Einschmelzen von anorganischem Material
EP4590645A1 (de) Glasschmelzwanne
WO2003078337A1 (de) Verfahren zum behandeln eines metallischen bauteiles, das mit einer glasschmelze in berührung gelangt, sowie ein solches metallisches bauteil

Legal Events

Date Code Title Description
OP8 Request for examination as to paragraph 44 patent law
8364 No opposition during term of opposition
R119 Application deemed withdrawn, or ip right lapsed, due to non-payment of renewal fee